TY - JOUR A1 - Mente, Tobias A1 - Böllinghaus, Thomas T1 - kModeling of hydrogen distribution in a duplex stainless steel N2 - Quite a number of models for hydrogen distribution in steels and welds have been developed in the past 20 years. They reach from simple analytical models to more complex two and three dimensional finite element simulations. So far, these models have been used to simulate hydrogen distribution in homogeneous microstructure. This paper contributes to numerical simulation of hydrogen distribution in heterogeneous microstructure, e. g. in a duplex stainless steel microstructure consisting of two phase fractions. Under appropriate conditions, such as cathodic protection, it is possible that hydrogen is absorbed leading to material embrittlement and possibly initiating hydrogen assisted cracking. In order to avoid hydrogen assisted cracking in duplex stainless steels, it is of great interest to know more about the diffusion behavior of the ferrite and austenite phase. A numerical model has been developed that operates on the mesoscale and enables simulation of hydrogen transport in the various phases of a metallic material. As a first application of this model, hydrogen distribution in a duplex stainless steel 1.4462, consisting of approximately equal portions of ferrite and austenite, was simulated using the finite element program package ANSYS. The results reflect the dependency of hydrogen distribution on the microstructural alignment of the ferrite and austenite phase fractions. Crack-critical areas can thus be identified, provided the critical strain-hydrogen combination is known for the respective microstructural phase. KW - Finite element KW - Simulation KW - Duplex stainless steel KW - Hydrogen KW - Diffusion KW - Weld metal KW - Microstructure PY - 2012 SN - 0043-2288 SN - 1878-6669 VL - 56 IS - 11/12 SP - 66 EP - 78 PB - Springer CY - Oxford AN - OPUS4-27483 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mente, Tobias A1 - Böllinghaus, Thomas T1 - Heat treatment effects on the reduction of hydrogen in multi-layer high-strength weld joints KW - Cold cracking KW - Heat treatment KW - High strength steels KW - Hydrogen KW - Numerical simulation KW - Structural steels PY - 2012 SN - 0043-2288 SN - 1878-6669 VL - 56 IS - 7/8 SP - 26 EP - 36 PB - Springer CY - Oxford AN - OPUS4-26055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mente, Tobias A1 - Böllinghaus, Thomas T1 - Mesoscale modeling of hydrogen-assisted cracking in duplex stainless steels N2 - Quite a number of numerical models for hydrogen-assisted cracking in different kind of steels are existing reaching from simple analytical models to more complex two- and three-dimensional finite element simulations. These numerical models have been used to simulate the processes of hydrogen-assisted cracking in homogeneous microstructure. This paper contributes to numerical simulation of hydrogen-assisted cracking in heterogeneous microstructure, e.g., in a duplex stainless steel microstructure consisting of two phase fractions. If hydrogen is absorbed during welding or during service, i.e., due to cathodic protection, hydrogen is leading to material embrittlement and leads to hydrogen-assisted cracking. In order to improve understanding of the mechanisms of hydrogen-assisted cracking in duplex stainless steels, a numerical model has been created that operates at the mesoscale and enables simulation of stress–strain distribution as well as cracking in the various phases of a metallic material. Stress–strain distribution and hydrogen-assisted cracking in the duplex stainless steel 1.4462, consisting of approximately equal portions of ferrite and austenite, was simulated using the finite element program ANSYS. It was shown by numerical simulation that higher local stresses and strains are present at ferrite and austenite than the global stresses and strains in the duplex stainless steel, while the highest plastic deformations occur at austenite and the highest stresses can be found in small ferrite bars surrounded by ductile austenitic islands. By analyzing the stress–strain distribution in the duplex microstructure, crack critical areas in the ferrite can be identified. Hydrogen-assisted cracking was modeled assuming high hydrogen concentrations and regarding the local mechanical load in each phase of the duplex stainless steel. The mesoscale model qualitatively reflects the crack initiation and propagation process in the ferritic and austenitic phase of the duplex stainless steel. KW - Finite element analysis KW - Simulating KW - Duplex stainless steels KW - Stress distribution KW - Strain KW - Mathematical models KW - Hydrogen-assisted cracking KW - Hydrogen PY - 2014 DO - https://doi.org/10.1007/s40194-013-0106-7 SN - 0043-2288 SN - 1878-6669 VL - 58 IS - 2 SP - 205 EP - 216 PB - Springer CY - Oxford AN - OPUS4-29442 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Mente, Tobias A1 - Böllinghaus, Thomas T1 - Modeling of hydrogen-assisted cracking (HAC) in duplex stainless steels (DSS) N2 - Modeling of Hydrogen-Assisted Cracking (HAC) in Duplex Stainless Steels (DSS): - Hydrogen causes significant degradation in DSS and consequently HAC - Mechanisms of HAC have not been fully understood in two-phase microstructures - Mesoscale numerical modeling for HAC in DSS was created, coupled to the macroscale, enabling simulation of HAC in both phases independent from predefined crack paths T2 - International Hydrogen Conference - Material Performance in Hydrogen Environments CY - Jackson Lake Lodge, Moran, Wyoming, USA DA - 11.09.2016 KW - Hydrogen KW - Numerical modeling KW - Duplex stainless steel KW - Hydrogen assisted cracking PY - 2016 AN - OPUS4-37404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Münster, C. A1 - Mente, Tobias A1 - Rhode, Michael A1 - Böllinghaus, Thomas ED - Sommitsch, C. ED - Enzinger, N. ED - Mayr, P. T1 - Modelling of hydrogen diffusion in power station steels and influence of experimental conditions on the determination of diffusion coefficients N2 - In the field of modelling hydrogen assisted cracking (HAC) phenomenon, hydrogen diffusivity is an important input parameter for numerical simulation. In terms of hydrogen diffusion coefficients, they have great impact on realistic assessment of the evolution of possible crack critical hydrogen concentrations. In addition, the chemical compositions of steels can have a strong effect on hydrogen diffusion. Unfortunately, literature provides a wide range of available hydrogen diffusion coefficients even for similar microstructures and equal temperatures. The scattering of the data can lead to significant deviations in the results of simulating the evolving hydrogen concentrations due to hydrogen uptake (by fabrication or service). Thus, the application of such data to crack-models or for component life tie predictions can be realized up to the present only by considering envelope curves of such value, corresponding to a work or bench case scenario, respectively. For improved reliability of numerical simulaitons, it is necessary to minimize the mentioned deviation of these data. Hence, this work focuses on the validation of hydrogen diffusion coefficients obtained from permeation experiments at room temperature. Two baintic steels with different alloying concepts were investigated, the creep-resistant 7CrMoVTiB10-10 and the reactor pressure vessel grade 20MnMoNi4-5. A numerical model is presented for simulation of the corresponding hydrogen diffusion during permeation experiments using the finite element software ANSYS. Three different diffusion coefficients (obtained from different common calculation methods) are considered and compared to numerical results. The vases of thes calculation methods are permeation transients which are a direct measure for hydrogen. The results of the simulated hydrogen diffusion coefficients show that only one procedure for calculation of diffusion coefficitnes is suitable in comparision to the experimental values. Thus, it is suggested to use this method for analysis of experimental results in case of hydrogen diffusion during permeation experiments. Furthermore, this work supplies validated values for the hydrogen diffusion coefficients of both steel grades. KW - Hydrogen KW - Diffusion Coefficient KW - Numerical Simulation KW - Permeation KW - Creep-resistant Steel KW - Pressure Vessel Steel PY - 2016 SN - 978-3-85125-490-7 SN - 2410-0544 SP - 435 EP - 457 PB - Technische Universität Graz CY - Graz AN - OPUS4-38917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias A1 - Böllinghaus, Thomas ED - Somerday, B. P. ED - Sofronis, P. T1 - Mesoscale Numerical Simulation of Hydrogen-Assisted Cracking in Duplex Stainless Steels N2 - A two-dimensional numerical mesoscale model has been created representing a microstructure of a typical 2205/1.4462 duplex stainless steel to further elucidate the mechanisms of hydrogen-assisted crack initiation and propagation in multiphase non-hydride forming metallic microstructures. Hydrogen-assisted cracking (HAC) was simulated by considering different stress and strain behavior as well as different diffusion behavior in both phases. For simulation of crack initiation and propagation, the element elimination technique has been applied. The model allows the simulation of path-free crack propagation which contributes to a better understanding of the HAC process in two-phase microstructures. As a particular result, the analyses revealed that a global macroscopic elastic deformation might already cause plastic deformation in both phases entailing respective HAC. T2 - International Hydrogen Conference CY - Jakson Lake Lodge, Wyoming, USA DA - 11.09.2016 KW - Computer simulation KW - Cracking (Materials) KW - Fracture (Process) KW - Hydrogen KW - Stainless steel PY - 2017 SN - 978-0-7918-6138-7 DO - https://doi.org/10.1115/1.861387_ch67 SP - 589 EP - 596 PB - The American Society of Mechanical Engineers (ASME) CY - New York AN - OPUS4-45680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Richter, Tim A1 - Mayr, P. A1 - Nitsche, A. A1 - Mente, Tobias A1 - Böllinghaus, Thomas T1 - Hydrogen diffusion in creep-resistant 9% Cr P91 multi-layer weld metal N2 - Welded components of P91 9% Cr steel demand for careful welding fabrication with necessary post weld heat treatment (PWHT). Before the PWHT, a hydrogen removal heat treatment is necessary for avoidance of hydrogen assisted cracking (HAC). In this context, the microstructure and temperature-dependent hydrogen diffusion is important, and reliable diffusion coefficients of P91 weld metal are rare. For that reason, the diffusion behavior of P91 multi-layer weld metal was investigated for as-welded (AW) and PWHT condition by electrochemical permeation experiments at room temperature and carrier gas hot extraction (CGHE) from 100 to 400 °C. Hydrogen diffusion coefficients were calculated, and the corresponding hydrogen concentration was measured. It was ascertained that both heat treatment conditions show significant differences. At room temperature the AW condition showed significant hydrogen trapping expressed by to seven times lower diffusion coefficients. A preferred diffusion direction was found in perpendicular direction expressed by high permeability. The CGHE experiments revealed lower diffusion coefficients for the AW condition up to 400 °C. In this context, a hydrogen concentration of approximately 21 ml/100 g was still trapped at 100 °C. For that reason, a certain HAC susceptibility of as-welded P91 weld metal cannot be excluded, and hydrogen removal should be done before PWHT. KW - Creep resisting materials KW - Diffusion KW - Hydrogen KW - Weld metal KW - Post weld heat treatment KW - Microstructure PY - 2020 DO - https://doi.org/10.1007/s40194-019-00828-8 SN - 0043-2288 VL - 64 IS - 2 SP - 267 EP - 281 PB - Springer AN - OPUS4-50471 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Schaupp, Thomas A1 - Münster, C. A1 - Mente, Tobias A1 - Kannengießer, Thomas A1 - Böllinghaus, Thomas T1 - Hydrogen determination in welded specimens by carrier gas hot extraction - a review on the main parameters and their effects on hydrogen measurement N2 - Carrier gas hot extraction (CGHE) is a commonly applied technique for determination of hydrogen in weld joints using a thermal conductivity detector (TCD) for hydrogen measurement. The CGHE is based on the accelerated hydrogen effusion due to thermal activation at elevated temperatures. The ISO 3690 standard suggests different specimen geometries as well as necessary minimum extraction time vs. temperature. They have the biggest influence on precise hydrogen determination. The present study summarizes the results and experience of numerous test runs with different specimen temperatures, geometries (ISO 3690 type B and small cylindrical samples), and factors that additionally influence hydrogen determination. They are namely specimen surface (polished/as-welded), limited TCD sensitivity vs. specimen volume, temperature measurement vs. effects of PI-furnace controller, as well as errors due to insufficient data assessment. Summarized, the temperature is the driving force of the CGHE. Two different methods are suggested to increase the heating rate up to the desired extraction temperature without changing the experimental equipment. Suggestions are made to improve the reliability of hydrogen determination depended on the hydrogen signal stability during extraction accompanied by Evaluation of the recorded data. Generally, independent temperature measurement with dummy specimens is useful for further data analysis, especially if this data is used for calculation of trapping kinetics by thermal desorption analysis (TDA). KW - Hydrogen KW - Carrier gas hot extraction KW - Experimental design KW - Thermal conductivity device PY - 2019 DO - https://doi.org/10.1007/s40194-018-0664-9 SN - 0043-2288 VL - 63 IS - 2 SP - 511 EP - 526 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-47603 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -