TY - GEN A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas A1 - Czeskleba, Denis T1 - Simulation of hydrogen distribution in submerged arc welded heavy plates as tool for evaluating cold cracking sensitivity for offshore structures N2 - Foundation structures for offshore wind turbines are typically made of heavy plate struc-tural steels, such as S420ML, welded by submerged arc welding. Due to the welding process conditions, higher amounts of hydrogen can be introduced. In this context, large plate thicknesses result in long diffusion paths and a prolonged diffusion time for hydrogen at ambient temperature and possible delayed hydrogen-assisted cold cracking. As a result, hydrogen can accumulate in areas of high mechanical stress and strain. Due to the delayed diffusion, a minimum waiting time of up to 48 h must be observed before non-destructive testing can be performed. In addition, the assessment of possible cold crack locations is very complex. For this reason, a numerical model of a component-like weld test was developed to simulate the temperature field during welding and subsequent cooling. A hydrogen diffusion model based on the temporal-local temperature distribution was established. It was applied to simulate the change of hydrogen distribution as a function of temperature cycle during multi-layer welding and further for the entire waiting time interval ≤ 48 h. As a result, crack critical areas could be evaluated in terms of accu-mulated hydrogen. An advantage of the diffusion model is the simulation of a normalized concentration, i.e. between "0" (no hydrogen) and "1" (max. concentration), which can be scaled to experimentally determined hydrogen concentrations. Finally, selected results for increased real hydrogen ingress are presented, which confirm the relatively high crack resistance of the S420 submerged arc welded joint. KW - Hydrogen assisted cracking KW - Diffusion KW - Numerical simulation KW - Offshore steel PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632416 DO - https://doi.org/10.21268/20250507-6 SP - 1 EP - 12 PB - Technische Universität Clausthal CY - Clausthal-Zellerfeld, Deutschland AN - OPUS4-63241 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias T1 - Gasflaschenzerknall in einer Löschanlage: Ursachen – Schadensanalyse – Prävention N2 - Schadensanalyse an einer mit Inergen gefüllten Gasflasche aus einer Löschanlage aus dem vergütetem Stahl 34CrMo4. Die Durchführung der Schadensanalyse erfolgte nach VDI 3822. Schadensursache war Spannungsrisskorrosion durch Wasserreste in Verbindung mit dem Gasbestandteil Kohlendioxid des eingefüllten Inergen. Die Wasserreste verblieben nach der hydraulischen Druckprüfung unentdeckt in der 1996 hergestellten Gasflasche. Auch bei der Erstbefüllung mit Inergen im Jahr 2003 blieben die Wasserreste unentdeckt. Nach Installation der befüllten Gasflasche in der Löschanlage im Jahr 2004 verblieb diese dort bis zum Schadensereignis im Jahr 2021. T2 - 51. VDI-Jahrestagung Schadensanalyse - Produktverbesserung durch Schadensprävention CY - Würzburg, Germany DA - 21.10.2025 KW - Gasflasche KW - Inergen-Löschanlage KW - Schadensanalyse PY - 2025 AN - OPUS4-64652 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias A1 - Grimault de Freitas, Tomás A1 - Nietzke, Jonathan A1 - Konert, Florian A1 - Sobol, Oded A1 - Wackermann, Ken A1 - Ruchti, Peter A1 - Elsen-Humberg, Stefan A1 - Systermans, Thomas ED - Zimmermann, Martina T1 - Hohlzugprüfung als kostengünstige Methode zur Werkstoffcharakterisierung für die Wasserstoffwirtschaft N2 - Wasserstoff ist ein notwendiger Baustein zur Erreichung zukünftiger Klimaziele. Für eine schnell hochlaufende Wasserstoffwirtschaft ist es daher notwendig sowohl bestehende Infrastruktur als auch neue Werkstoffe für den sicheren und nachhaltigen Einsatz in Wasserstofftechnologien zu qualifizieren. Die akzeptierten und standardisierten Prüfverfahren zur Ermittlung des Einflusses gasförmigen Wasserstoffs auf die mechanischen Eigenschaften metallischer Werkstoffe sind meist sehr komplex, mit hohem technologischem und finanziellem Aufwand verbunden und stehen nur Wenigen Instituten weltweit zur Verfügung. Die Hohlzugprüftechnik bietet hier eine kostengünstige und einfach zu realisierende Alternative. Mit der im Jahr 2024 erstmals veröffentlichten ISO 7039 wurde diese Prüftechnik auch für die Wirtschaft anwendbar gemacht. Der Standard gilt allgemein für die Prüfung mit gasförmigen Medien, weist jedoch in Bezug auf die Prüfung mit gasförmigem Wasserstoff noch einige Wissenslücken auf. Im Teilvorhaben H2HohlZug des Leitprojekt TransHyDE werden die Lücken zum Einfluss der Geometrie, Oberflächenqualität sowie Gasreinheit in einzelnen Arbeitspaketen geschlossen und die Erkenntnisse in einen Standard überführt. T2 - 43. Vortrags- und Diskussionstagung Werkstoffprüfung 2025 - Werkstoffe und Bauteile auf dem Prüfstand CY - Dresden, Germany DA - 27.11.2025 KW - Hohlzugprüfung KW - Druckwasserstoff KW - ISO 7039 KW - H2HohlZug - TransHyDE PY - 2025 SN - 978-3-88355-454-9 SP - 11 EP - 17 PB - Deutsche Gesellschaft für Materialkunde e.V. (DGM) CY - Dresden AN - OPUS4-64937 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias T1 - Hohlzugprüfung - Kostengünstige Methode zur Werkstoffcharakterisierung für die Wasserstoffwirtschaft N2 - Wasserstoff ist ein notwendiger Baustein zur Erreichung zukünftiger Klimaziele. Für eine schnell hochlaufende Wasserstoffwirtschaft ist es daher notwendig sowohl bestehende Infrastruktur als auch neue Werkstoffe für den sicheren und nachhaltigen Einsatz in Wasserstofftechnologien zu qualifizieren. Die akzeptierten und standardisierten Prüfverfahren zur Ermittlung des Einflusses gasförmigen Wasserstoffs auf die mechanischen Eigenschaften metallischer Werkstoffe sind meist sehr komplex, mit hohem technologischem und finanziellem Aufwand verbunden und stehen nur Wenigen Instituten weltweit zur Verfügung. Die Hohlzugprüftechnik bietet hier eine kostengünstige und einfach zu realisierende Alternative. Mit der im Jahr 2024 erstmals veröf-fentlichten ISO 7039 wurde diese Prüftechnik auch für die Wirtschaft anwendbar gemacht. Der Standard gilt allgemein für die Prüfung mit gasförmigen Medien, weist jedoch in Bezug auf die Prüfung mit gasförmigem Wasserstoff noch einige Wissenslücken auf. Im Teilvorhaben H2HohlZug des Leitprojekt TransHyDE werden die Lücken zum Einfluss der Geometrie, Ober-flächenqualität sowie Gasreinheit in einzelnen Arbeitspaketen geschlossen und die Erkenntnisse in einen Standard überführt. T2 - 43. Vortrags- und Diskussionstagung Werkstoffprüfung 2025 - Werkstoffe und Bauteile auf dem Prüfstand CY - Dresden, Germany DA - 27.11.2025 KW - Hohlzugprüfung KW - Druckwasserstoff KW - ISO 7039 KW - H2HohlZug - TransHyDE PY - 2025 AN - OPUS4-64936 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Erxleben, Kjell A1 - Richter, Tim A1 - Schröpfer, Dirk A1 - Mente, Tobias A1 - Michael, Thomas T1 - Local mechanical properties of dissimilar metal TIG welded joints of CoCrFeMnNi high entropy alloy and AISI 304 austenitic steel N2 - Multiple principal element alloys encompass the well-known high entropy alloys (HEA). The alloy system represents a new class of materials consisting of at least three alloying elements, each containing 5 to 35 at.%. Thus, this alloying concept differs fundamentally from conventional materials such as steel or nickel alloys. For this purpose, the alloying elements are specifically selected, the microstructures are adjusted in a single-phase and, in some cases, multi-phase manner. In particular, conflicting goals, such as the trade-off between strength and ductility in conventional steels, are overcome. However, in the last 20 years, the focus has been on material synthesis. With the increase in available material quantities, the focus is now on processing issues such as joining and welding processes. The weldability of HEAs has received very little attention so far. The experience with dissimilar metal welds is completely lacking but is essential for the application of these materials in combination with conventional materials. The present study presents comprehensive experimental results on the weldability of an equimolar CoCrFeMnNi-HEA in cold-rolled and heat-treated condition, which was joined by tungsten inert gas welding to an austenitic steel AISI 304. The mechanical properties of the dissimilar metal welds were characterized by cross-weld tensile samples, whereas the local deformation in the weld of the different welding zones was measured by digital image correlation. In accordance with the respective initial HEA condition (cold-rolled vs. heat-treated), the local strain behavior was divergent and influenced the global mechanical properties of both DMW types. Nonetheless, the experiments provided proof in principle of the weldability for dissimilar joints of the CoCrFeMnNi-HEA welded to conventional materials like austenitic stainless steels ensuring a corresponding capability for mechanical loading. This allows further considerations on the application of these innovative materials. KW - TIG welding KW - High-entropy alloys KW - Mechanical properties KW - Dissimilar metal weld PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595775 DO - https://doi.org/10.1007/s40194-024-01718-4 SN - 0043-2288 SP - 1 EP - 11 PB - Springer Science and Business Media LLC AN - OPUS4-59577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas A1 - Schaupp, Thomas A1 - Zavdoveev, Anatoly T1 - Challenges for testing hydrogen-assisted cold cracking in weld seams of high-strength steel grades N2 - Hydrogen can cause weld cold cracking even days after fabrication. In this respect, higher strength steels present a challenge to established cold crack testing. In general, the tolerable hydrogen concentration for crack prevention decreases with increasing material strength. In addition, advanced welding processes require changes in weld geometry and heat input. This directly influences the formation of crack-critical microstructures, e.g. in hardened areas of the heat-affected zone. The limits of use and application of modern cold cracking tests are evaluated by (1) the externally loaded Implant-test and (2) the self-restraint Tekken-test. In particular, external mechanical stresses, which cause additional mechanical loads on the components during welding, must be considered due to the component-specific stiffness of high-strength steels. Accompanying test methods for determining hydrogen concentration and diffusion in welds are presented, such as carrier gas hot extraction for determining hydrogen concentration (ISO 3690) or temperature-dependent diffusion coefficients. These values are of great importance for a holistic approach to the evaluation of the cold cracking sensitivity of high strength steels. KW - Hydrogen KW - Welding KW - Cold cracking test KW - High-strength steel PY - 2024 DO - https://doi.org/10.37434/tpwj2024.08.01 SN - 0957-798X VL - 2024 IS - 8 SP - 3 EP - 9 PB - International Association "Welding" CY - Kyiv, Ukraine AN - OPUS4-60946 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas T1 - Parameters and challenges for reliable hydrogen determination in welded joints by carrier gas hot extraction N2 - For the hydrogen-based energy economy of tomorrow, the construction of the necessary infrastructure will play a central role. Most materials used to date, such as welded steels, can be prone to hydrogen embrittlement under certain conditions. This includes the classic delayed cold cracking during welding as well as degradation phenomena during service of components in hydrogen-containing environment. For the evaluation of any hydrogen effect, for example, on the mechanical properties of a welded metallic material, the hydrogen content must be precisely determined. In the case of weld seams, the carrier gas hot extraction (CGHE) according to ISO 3690 is meanwhile state-of-the-art. CGHE is based on accelerated hydrogen degassing due to the thermal activation of hydrogen at elevated temperatures. In addition to the quantification of hydrogen, thermal desorption analysis (TDA) with varying heating rates can be used to determine and evaluate the hydrogen trapping at microstructural defects in the material. For both techniques, experimental and metrological influences must be considered, which have a major effect on the result. For example, ISO 3690 suggests different sample geometries and minimum extraction times for CGHE. This study summarizes the results and experiences of numerous investigations at the Federal Institute for Materials Research and Testing (BAM) with different sample temperatures and geometries (ISO 3690 type B and cylindrical TDA samples) regarding the influence of the sample surface (polished/welded), measurement accuracy depending on the sample volume and the insufficient monitoring of the effect of PI control on the extraction temperature. A deviating extraction temperature from the target temperature can significantly falsify the measurement results. Based on the results, methods are shown which allow the desired extraction temperature to be reached quickly without physically interfering with the measuring equipment. This serves to significantly improve the reliability of the hydrogen measurement through increased signal stability and accelerated hydrogen desorption. In general, an independent temperature measurement with dummy samples is recommended for the heating procedure of choice to exclude possible undesired temperature influences before the measurement. The methods described can be transferred directly to industrial applications KW - Welding KW - Hydrogen measurement KW - ISO 3690 KW - Carrier gas hot extraction PY - 2024 DO - https://doi.org/10.37434/tpwj2024.04.01 SN - 0957-798X VL - 4 SP - 3 EP - 10 PB - International Association Welding AN - OPUS4-60071 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Mente, Tobias T1 - Trapping and diffusion in high-pressure hydrogen charged CoCrFeMnNi high entropy alloy compared to austenitic steel 316L N2 - High entropy alloys (HEAs) have attracted considerable research attention as potential substitute materials for austenitic steels in high-pressure hydrogen environments. The corresponding hydrogen absorption, diffusion and trapping has received less scientific attention. Therefore, the CoCrFeMnNi-HEA was investigated and compared to an austenitic steel AISI 316L. Both were subjected to high-pressure hydrogen charging at 200 bar and 1000 bar. Thermal Desorption Analysis (TDA) was used to clarify the specific desorption behavior and hydrogen trapping. For this purpose, the underlying TDA spectra were analyzed in terms of a reasonable peak deconvolution into a defined number of peaks and the activation energies for the respective and predominant hydrogen trapping sites were then calculated. Both materials show comparable hydrogen diffusivity. However, there were significant differences in the absorbed hydrogen concentrations at both charging pressures. The calculated activation energies suggest strong hydrogen trapping in the CoCrFeMnNi-HEA. KW - High-entropy alloy KW - Hydrogen diffusion KW - Trapping KW - High-pressure charging KW - Thermal desorption analysis PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611901 DO - https://doi.org/10.1016/j.ijhydene.2024.09.393 SN - 0360-3199 VL - 89 IS - 89 SP - 772 EP - 782 PB - Elsevier B.V. CY - Amsterdam, Netherlands AN - OPUS4-61190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias T1 - MatCom - Materialeigenschaften und Kompatibilität für Wasserstofftechnologien - MatCom 1 - Metallische Werkstoffe N2 - Aufbauend auf dem historischen Schadensfall von A. Martens im Jahr 1894 zur Explosion von H2-Gasflaschen auf dem Tempelhofer Feld und den dabei durchgeführten Untersuchungen wird im Hauptteil des Vortrages auf die Standardisierung der Hohlzugprüftechnik eingegangen. Dabei wird zunächst auf die Vor- und Nachteile unterschiedlicher Prüfmöglichkeiten zur Wasserstoffkompatibilität metallischer Werkstoffe und deren Schweißverbindungen eingegangen und im Weiteren die Umsetzung der Prüftechnik an der BAM beschrieben. Für die Standardisierung der Hohlzugprüftechnik wurden verschiedene Randbedingungen mit Einfluss auf die Ergebnisqualität überprüft. Dabei wurde der Pipelinestahl X65 als auch der additiv gefertigte Werkstoff 316L genutzt. Abschließend wird auf die Verwaltungspartnerschaft mit Namibia eingegangen und die umzusetzenden Projekte mit Bezug zur Schweißtechnik dargestellt. T2 - BAM-PTB Workshop CY - Magdeburg, Germany DA - 04.09.2024 KW - MatCom1 KW - H2Safety@BAM KW - Hohlzugprobe PY - 2024 AN - OPUS4-61036 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Kromm, Arne A1 - Mente, Tobias A1 - Brackrock, Daniel A1 - Czeskleba, Denis A1 - Kannengießer, Thomas T1 - Component test for the assessment of delayed hydrogen-assisted cracking in thick-walled SAW joints for offshore applications N2 - Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods, or jackets. These components are typically constructed using submerged arc welding (SAW) with high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen-assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicates the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam/layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with over 20 passes and a seam length of 1000 mm. Additional welded stiffeners simulated the effect of a high restraint, to achieve critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of up to 48 h after the completion welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modeling allowed the qualitative estimation of the hydrogen diffusion in the weld. No noticeable HAC occurrence was identified and confirms the high cracking resistance of the investigated material. Finally, the applicability of the MWT concept should be critically discussed. KW - Hydrogen KW - Cold cracking KW - Minimum Waiting Time KW - Offshore steel grade KW - Component test PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-591981 DO - https://doi.org/10.1007/s40194-023-01658-5 SP - 1 EP - 15 PB - Springer Science and Business Media LLC AN - OPUS4-59198 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -