TY - JOUR A1 - Eberstein, Markus A1 - Mann, Guido A1 - Vogel, Jens A1 - Zoheidi, M. A1 - Krüger, Jörg T1 - Influence of Technological Parameters on Nanosecond Laser-induced Surface Damage of Optical Multimode Fibers JF - Advanced materials research N2 - High-power optical multimode fibers are essential components for materials processing and surgery and can limit the reliability of expensive systems due to breakdown at the end faces. The breakdown threshold of fibers is determined by intrinsic materials properties and parameters of the technology applied. The aim of this paper is the identification of technological parameters that are crucial for the fiber quality. Fibers were drawn from preforms of Heraeus SWU with core material F300 and a low amount of OH-. Both, the cladding (fluorine doped SiO2) to core diameter ratio (CCDR) and the drawing speed were varied. CCDR values between 1.05 and 1.4 were used. Afterwards, the laser-induced damage thresholds (LIDT) of the fibers were determined. For comparison, also samples from preforms, which underwent different thermal treatments above the transition temperature, were tested with respect to their damage resistivity. Single and multi pulse LIDT measurements were done in accordance with the relevant ISO standards. Nd:YAG laser pulses with durations of 15 ns (1064 nm wavelength) and 8.5 ns (532 nm) at a repetition rate of 10 Hz were utilized. For the fibers, LIDT values (1-on-1, 1064 nm and 532 nm) increased with growing CCDR and with decreasing drawing velocities. KW - Silica glass KW - Multimode fiber KW - Nanosecond laser KW - Damage threshold PY - 2005 SN - 1022-6680 SN - 1662-8985 VL - 39-40 SP - 225 EP - 230 PB - Trans Tech Publ. CY - Zurich AN - OPUS4-17339 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mann, Guido A1 - Zoheidi, M. A1 - Eberstein, Markus A1 - Krüger, Jörg T1 - Influence of core diameter and coating material on nanosecond laser-induced damage threshold of optical multimode fibers T2 - European Materials Research Society (EMRS) Spring Meeting 2009, Symposium Q "Laser and Plasma Processing for Advanced Materials" T2 - European Materials Research Society (EMRS) Spring Meeting 2009, Symposium Q "Laser and Plasma Processing for Advanced Materials" CY - Strasbourg, France DA - 2009-06-08 PY - 2009 AN - OPUS4-19218 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mann, Guido A1 - Jurke, Mathias A1 - Zoheidi, M. A1 - Eberstein, M. A1 - Krüger, Jörg T1 - Influence of core diameter and coating material on nanosecond laser-induced damage threshold of optical multicode fibers T2 - 10. Konferenz der ESG und 84. Glastechnische Tagung T2 - 10. Konferenz der ESG und 84. Glastechnische Tagung CY - Magdeburg, Germany DA - 2010-05-30 PY - 2010 AN - OPUS4-20891 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mann, Guido A1 - Zoheidi, M. A1 - Krüger, Jörg T1 - Hochleistungsfasern am Limit - Laserinduzierte Zerstörung als Einsatzgrenze bei Lichtwellenleitern JF - Laser + Photonik N2 - Aufgrund der steigenden Anforderungen an Fasern für Hochleistungsanwendungen hat die Business Unit Fiber Optics der Leoni Gruppe gemeinsam mit der BAM Bundesanstalt für Materialforschung und -prüfung die Herausforderung angenommen, erstmalig die Zerstörschwellen eigener “large core” Spezialfasern zu untersuchen. KW - Laserinduzierte Zerstörschwelle KW - Optische Multimodefaser KW - Lichtwellenleiter KW - Nanosekundenlaser PY - 2012 UR - http://www.leoni-fiber-optics.com/fileadmin/bu/fo/news/pdf/fachpresse/I-PDF_LP110166_leoni_LP4-12_kleiner_.pdf SN - 1610-3521 VL - 4 SP - 18 EP - 21 PB - Hanser CY - München AN - OPUS4-26424 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bonse, Jörn A1 - Mann, Guido A1 - Krüger, Jörg A1 - Marcinkowski, M. A1 - Eberstein, M. T1 - Femtosecond laser-induced removal of silicon nitride layers from doped and textured silicon wafers used in photovoltaics JF - Thin solid films N2 - The removal of a 75- to 90-nm-thick passivating silicon nitride antireflection coating from standard textured multicrystalline silicon photovoltaic wafers with a typical diffused 90-Ω/sq-emitter upon irradiation with near-infrared femtosecond laser pulses (790 nm central wavelength, 30 fs pulse duration) is studied experimentally. The laser irradiation areas are subsequently characterized by complementary optical microscopy, scanning electron microscopy and depth profiling chemical analyses using secondary ion mass spectrometry. The results clarify the thin-film femtosecond laser ablation scenario and outline the process windows for selective antireflection coating removal. KW - Photovoltaics KW - Solar cell KW - Laser processing KW - FS-laser ablation KW - Silicon nitride PY - 2013 DO - https://doi.org/10.1016/j.tsf.2013.07.005 SN - 0040-6090 VL - 542 SP - 420 EP - 425 PB - Elsevier CY - Amsterdam AN - OPUS4-28874 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mann, Guido A1 - Krüger, Jörg ED - Jitsuno, T. ED - Shao, J. ED - Rudolph, W. T1 - Nanosecond laser damage of optical multimode fibers T2 - Proceedings of SPIE N2 - For pulse laser materials processing often optical step index and gradient index multimode fibers with core diameters ranging from 100 to 600 μm are used. The design of a high power fiber transmission system must take into account limitations resulting from both surface and volume damage effects. Especially, breakdown at the fiber end faces and self-focusing in the fiber volume critically influence the fiber performance. At least operation charts are desirable to select the appropriate fiber type for given laser parameters. In industry-relevant studies the influence of fiber core diameter and end face preparation on laser-induced (surface) damage thresholds (LIDT) was investigated for frequently used all-silica fiber types (manufacturer LEONI). Experiments on preform material (initial fiber material) and compact specimens (models of the cladding and coating material) accompanied the tests performed in accordance with the relevant LIDT standards ISO 21254-1 and ISO 21254 2 for 1-on-1 and S-on-1 irradiation conditions, respectively. The relation beam diameter vs. LIDT was investigated for fused silica fibers. Additionally, laser-induced (bulk) damage thresholds of fused silica preform material F300 (manufacturer Heraeus) in dependence on external mechanical stress simulating fiber bending were measured. All experiments were performed with 10-ns laser pulses at 1064 and 532 nm wavelength with a Gaussian beam profile. T2 - Pacific Rim Laser Damage 2016 CY - Yokohama, Japan DA - 18.05.2016 KW - laser damage KW - optical fiber KW - nanosecond laser KW - fused silica PY - 2016 DO - https://doi.org/10.1117/12.2238515 VL - 9983 SP - 99830T AN - OPUS4-37140 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mann, Guido A1 - Vogel, Jens A1 - Zoheidi, M. A1 - Eberstein, Markus A1 - Krüger, Jörg T1 - Breakdown limits of optical multimode fibers for the application of nanosecond laser pulses at 532 nm and 1064 nm wavelength JF - Applied surface science N2 - For many applications, optical multimode fibers are used for the transmission of powerful laser radiation. High light throughput and damage resistance are desirable. Laser-induced breakdown at the end faces of fibers can limit their performance. Therefore, the determination of laser-induced damage thresholds (LIDT) at the surface of fibers is essential. Nanosecond (1064 nm and 532 nm wavelength) single-shot LIDT were measured according to the relevant standard on SiO2 glass preforms (Suprasil F300) as basic materials of the corresponding fibers. For 10 kinds of fused silica fibers (FiberTech) with core diameters between 180 µm and 600 µm, an illumination approach utilizing a stepwise increase of the laser fluence on a single spot was used. For both wavelengths, the LIDT values (0% damage probability) obtained by means of the two methods were compared. The influence of surface preparation (polishing) on damage resistance was investigated. For equal surface finishing, a correlation between drawing speed of the fibers and their surface LIDT values was found. In addition to the surface measurements, bulk LIDT were determined for the preform material. KW - Fiber waveguides KW - Physical radiation damage KW - Laser-beam impact phenomena KW - Glasses KW - Radiation treatment PY - 2009 DO - https://doi.org/10.1016/j.apsusc.2008.07.157 SN - 0169-4332 SN - 1873-5584 VL - 255 IS - 10 SP - 5519 EP - 5522 PB - North-Holland CY - Amsterdam AN - OPUS4-19036 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mann, Guido A1 - Jurke, Mathias A1 - Zoheidi, M. A1 - Eberstein, Markus A1 - Krüger, Jörg T1 - Influence of core diameter and coating material on nanosecond laser-induced damage threshold of optical multimode fibers JF - Journal of optoelectronics and advanced materials N2 - Single and multi pulse laser-induced damage thresholds (LIDT) of core, cladding, and coating materials of high-power optical multimode fibers were determined in accordance with ISO 11254 for 532 nm and 1064 nm wavelength in the 10-ns pulse duration regime with spatial Gaussian beam shape. For all-silica fibers, LIDT increases with rising core diameter in a range between 100-600 µm for a constant cladding-core ratio of 1.2. The damage resistance of the low refracting cladding (0.3 % fluorine doped fused silica) is comparable to the undoped SiO2 core. Coating materials show significantly lower LIDT than light-guiding parts of the fibers. KW - Fiber waveguides (42.81.Qb) KW - Physical radiation damage (61.80.-x) KW - Laser-beam impact phenomena (79.20.Ds) KW - Glasses (81.05.Kf) PY - 2010 SN - 1454-4164 VL - 12 IS - 3 SP - 711 EP - 714 PB - INOE & INFM CY - Bucharest AN - OPUS4-21083 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -