TY - JOUR A1 - Müller, Ralf A1 - Eberstein, Markus A1 - Reinsch, Stefan A1 - Schiller, Wolfgang Arno A1 - Deubener, J. A1 - Thiel, A. T1 - Effect of rigid inclusions on sintering of low temperature co-fired ceramics KW - Sintering KW - Glass Matrix Composites KW - Rigid Inclusion KW - Effective Viscosity KW - Kinetic Modelling KW - LTCC PY - 2007 SN - 1753-3562 SN - 0017-1050 SN - 0031-9090 SN - 1750-6697 VL - 48 IS - 4 SP - 259 EP - 266 PB - Society of Glass Technology CY - Sheffield AN - OPUS4-16211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Ralf A1 - Reinsch, Stefan A1 - Eberstein, Markus A1 - Deubener, J. A1 - Thiel, A. A1 - Schiller, Wolfgang Arno T1 - Effects of dispersed Al2O3 particles on sintering of LTCC N2 - The sintering of Low Temperature Co-fired Ceramics prepared from alumoborosilicate glass- and Al2O3 powders of similar small particle size was studied by dilatometry, heating microscopy, microstructure analysis, glass- and effective viscosity measurements. The steric effect of Al3O3 inclusions was studied using a gnon-reactiveh model composite. With increasing Al3O3 volume fraction (Φ ≤ 0.45), sintering decelerates and its final stage shifts to higher temperature. The attainable shrinkage is reduced as Al2O3 particle clusters bearing residual pores become more frequent. The kinetics of sintering could be described formally superposing the weighed contributions of differentially sized and randomly composed glass-crystal particle clusters and assuming a sintering rate controlled by the effective matrix viscosity, which increases with Φ and with progressive wetting of Al2O3 particles during densification. The "reactive" model composite shows significant dissolution of Al2O3 into the glass, which has two opposed effects on sintering: reducing Φ and increasing glass viscosity. For the present case (Φ = 0.25), the latter effect dominates and sintering is retarded by Al2O3 dissolution. Crystallization of wollastonite starts after full densification. Dissolution of Al2O3 was found to promote the subsequent growth of anorthite. KW - LTCC KW - Glass matrix composites KW - Al2O3-inclusions KW - Sintering kinetics PY - 2005 SN - 1022-6680 SN - 1662-8985 VL - 39-40 SP - 375 EP - 380 PB - Trans Tech Publ. CY - Zurich AN - OPUS4-18441 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Unger, Brita A1 - Rurack, Knut A1 - Müller, Ralf A1 - Resch-Genger, Ute A1 - Buttke, K. T1 - Effects of the Sol-Gel Processing on the Fluorescence Properties of Laser Dyes in Tetraethoxysilane Derived Matrices N2 - Two fluorescent dyes were incorporated into sol-gel derived SiO2 matrices. The dye was added to SiO2 precursors of different degrees of pre-condensation and the spectroscopic properties of the immobilized dye were measured at various aging and drying stages of the resulting gels. The significant influence of the processing parameters on the spectroscopic properties is manifested in the relative intensity of a second red shifted emission band (550–560 nm), which was observed besides the typical coumarin emission band (495 nm). The appearance of this long wavelength emission might be attributed to dye aggregation or to other reactions with the ambient matrix forced by micro porosity phenomena. KW - Sol-gel KW - Precursor chemistry KW - Fluorescence properties KW - Optical solids PY - 2000 DO - https://doi.org/10.1023/A:1008768318418 SN - 0928-0707 SN - 1573-4846 VL - 19 SP - 799 EP - 802 PB - Kluwer Academic Publ. CY - Dordrecht AN - OPUS4-1080 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peplinski, Burkhard A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Müller, Ralf A1 - Schadrack, Reinhard A1 - Michaelis, Matthias A1 - Emmerling, Franziska A1 - Reuther, H. A1 - Menzel, Michael T1 - Evidence of formation of the tridymite form of AlPO4 in some municipal sewage sludge ashes N2 - Evidence is provided that the tridymite component observed in the X-ray diffraction patterns of some sewage sludge ashes (SSAs) should not be interpreted as the tridymite modification of SiO2 but as the tridymite form of AlPO4. This proof is based on a combined X-ray Powder Diffraction (XRD), X-ray fluorescence (XRF) and Mossbauer spectroscopy investigation of two SSAs produced at two fluidized bed incineration facilities, located in different municipalities and operated differently. The structural and chemical characterization was carried out on the 'as received' SSA samples as well as on the residues of these two SSAs pretreated by leaching in citric acid. In addition, direct proof is presented that the tridymite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850 °C) typical for fluidized bed incinerators. KW - Aluminium phosphate KW - Ash KW - Fly ash KW - Incinerator ash KW - Sewage sludge ash KW - Tridymite form PY - 2013 DO - https://doi.org/10.1017/S0885715613000869 SN - 0885-7156 VL - 28 IS - S2 SP - S425 EP - S435 PB - JCPDS CY - Swarthmore, Pa. AN - OPUS4-29703 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Ralf A1 - Behrens, Harald A1 - Ageo-Blanco, Boris A1 - Reinsch, Stefan A1 - Wirth, Thomas T1 - Foaming Species and Trapping Mechanisms in Barium Silicate Glass Sealants N2 - Barium silicate glass powders 4 h milled in CO2 and Ar and sintered in air are studied with microscopy, total carbon analysis, differential thermal Analysis (DTA), vacuum hot extraction mass spectroscopy (VHE-MS), Fourier-transformed infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), and time-of-flight secondary-ion mass spectrometry (TOF-SIMS). Intensive foaming of powder compacts is evident, and VHE studies prove that foaming is predominantly caused by carbonaceous species for both milling gases. DTA Shows that the decomposition of BaCO3 particles mix-milled with glass powders occurs at similar temperatures as foaming of compacts. However, no carbonate at the glass surface could be detected by FTIR spectroscopy, XPS, and TOF-SIMS after heating to the temperature of sintering. Instead, CO2 molecules unable to rotate identified by FTIR spectroscopy after milling, probably trapped by mechanical dissolution into the glass bulk. Such a mechanism or microencapsulation in cracks and particle aggregates can explain the contribution of Ar to foaming after intense milling in Ar atmosphere. The amount of CO2 molecules and Ar, however, cannot fully explain the extent of foaming. Carbonates mechanically dissolved beneath the surface or encapsulated in cracks and micropores of particle aggregates are therefore probably the major foaming source. KW - Milling KW - Foaming KW - Glass powder KW - Sintering PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-531227 DO - https://doi.org/10.1002/adem.202100445 SN - 1438-1656 VL - 24 IS - 6 SP - 2100445-1 EP - 2100445-13 AN - OPUS4-53122 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zietka, S. A1 - Deubener, J. A1 - Behrens, H. A1 - Müller, Ralf T1 - Glass transition and viscosity of hydrated silica glasses N2 - The viscosity of silica glasses with different water contents was measured by penetration of sapphire microspheres in the range from 1012-1014·7 Pas at ambient pressure. Commercial silica glasses were used together with hydrous silica glasses, which were prepared by melting glass powder plus water in an internally heated pressure vessel at 2-3 kbar and 1350-1450°C. The temperature dependence of the viscosity of silica glasses with total water contents Cw of 5·4×10-4, 7·0×10-4, 1·00×10-2, and 1·55×10-2(Cw in mass fractions) can be described by Arrhenius equations. From the results, the linear dependence of the T12 isokom (K) with the logarithm of the water content was determined as T12=192-409 logCw. The analysis of the compositional dependence of the T12 isokom in the H2O-Na2O-SiO2 system reveals a temperature depression of up to 200 K for mixed water- and sodium-bearing glasses compared to H2O-SiO2 and Na2O-SiO2 glasses with same molar silica content. From these findings we conclude that protons may contribute significantly to the mixed alkali effect in glasses. KW - Wassergehalt KW - Silicatgläser KW - Viskosität PY - 2007 SN - 1753-3562 SN - 0017-1050 SN - 0031-9090 SN - 1750-6697 VL - 48 IS - 6 SP - 380 EP - 387 PB - Society of Glass Technology CY - Sheffield AN - OPUS4-18396 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eichelbaum, M. A1 - Rademann, K. A1 - Weigel, W. A1 - Löchel, B. A1 - Radtke, Martin A1 - Müller, Ralf T1 - Gold-Ruby Glass in a New Light: On the Microstructuring of Optical Glasses with Synchrotron Radiation KW - Nanoparticles KW - Glasses KW - Synchrotron radiation KW - X-ray lithography KW - Surface plasmon resonance KW - Luminescence PY - 2007 SN - 0017-1557 VL - 40 IS - 4 SP - 1 EP - 5 CY - London AN - OPUS4-16432 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marzok, Ulrich A1 - Müller, Ralf A1 - Schadrack, Reinhard A1 - Krauhausen, M. A1 - Burgstedt, F. A1 - Brode, W. A1 - Reetz, R. T1 - High-temperature laser profilometry for ceramic tapes N2 - Advanced ceramics are promising key components for microsystems engineering, communication Technology and medical engineering. Driven by steadiiy increasing demands on dimensional accuracy of components and Integration density, sintering has to be controlled at an unprecedented degree of precision. Being most crucial for components of complex shape, graded or heterogeneous-composed parts like LTCC multilayers for microsystems, precise control of sintering has a decisive influence on the dimensional accuracy, mechanical integrity and reliability of sintered components. Thus, permanent or temporary shape distortions or warping during sintering may result from spatially heterogeneous microstructure and temperature distribution, e.g. during the co-firing process of green multilayer Stacks printed with metallization and other functional pastes. Whereas permanent warping can be easily measured after sintering, temporary warping during firing is more difficult to measure. Nonetheless, this effect may cause latent failures later, which often limit the applicability of ceramic components. PY - 2013 SN - 0173-9913 SN - 0196-6219 VL - 90 IS - 4 SP - E35 EP - E40 PB - Göller CY - Baden-Baden AN - OPUS4-28500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marzok, Ulrich A1 - Müller, Ralf A1 - Schadrack, Reinhard A1 - Krauhausen, M. A1 - Burgstedt, F. A1 - Brode, W. A1 - Reetz, R. T1 - Hochtemperatur-Laserprofilometrie an keramischen Bauteilen N2 - Hochleistungssinterwerkstoffe spielen eine wachsende Rolle in derzeitigen Schlüsseltechnologien wie der Mikrosystem-, Informations-, Kommunikations- und Medizintechnik. Dabei steigen die Anforderungen an die präzise Steuerung der Sinterung. Besonders für komplexe, gradierte oder heterogen zusammengesetzte Formkörper wie zum Beispiel keramische LTCC-Multilayer für die Mikrosystemtechnik hat die exakte Beherrschung dieses Prozessschrittes wesentlichen Einfluss auf die Maßhaltigkeit, mechanische Integrität und Zuverlässigkeit der gesinterten Bauteile. Bedingt durch die Heterogenität der mehrlagigen und mit Leit- und anderen Funktionspasten bedruckten Sinterkörper hinsichtlich ihrer sinterphysikalischen oder thermischen Eigenschaften können bleibende oder temporäre Verwerfungen beim Schrumpfungsprozess auftreten, wobei letztere unter Umständen Ursache latenter Fehler im späteren Bauteil sind. PY - 2013 SN - 0173-9913 SN - 0196-6219 VL - 90 IS - 3 SP - D19 EP - D24 PB - Göller CY - Baden-Baden AN - OPUS4-28013 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Welter, T. A1 - Marzok, Ulrich A1 - Deubener, J. A1 - Reinsch, Stefan A1 - Müller, Ralf T1 - Hydrogen diffusivity in sodium aluminosilicate glasses N2 - Hydrogen gas diffusivity of fourteen glasses of the Na2O-Al2O3-SiO2 system are studied along the joins quartzalbite-jadeite-nepheline (Qz-Ab-Jd-Np, fully polymerized) and albite-sodium disilicate (Ab-Ds, depolymerized). Density measurements show that ionic porosity decreases from 54.4% (Qz) to 51.5% (Np) and from 52.4% (Ab) to 50.2% (Ds). Hydrogen diffusivity D follows similar trends but at another scale. D at 523 K decreases from 4×10−12 to 3×10−14m2 s−1 (Qz-Np) and from 4×10−13 to 3×10−15m2 s−1 (Ab-Ds). Charge compensating Na+ acting as a filling agent in fully polymerized network structures leads to up to one order of Magnitude higher diffusivities as depolymerized glass structures of the same SiO2 content where Na+ takes the role of a modifier ion. Temperature dependence of the diffusivity indicates that both the activation energy involved with the moving H2 molecule as well as the accessible volume in the structure contribute to this compositional trend. KW - Aluminosilicate glasses KW - Hydrogen diffusivity KW - Ionic porosity PY - 2019 DO - https://doi.org/10.1016/j.jnoncrysol.2019.119502 VL - 521 SP - 119502 PB - Elsevier B.V. AN - OPUS4-50392 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ried, Peter A1 - Gaber, Martin A1 - Müller, Ralf A1 - Deubener, J. T1 - Hydrogen permeability of a barium-aluminoborosilicate glass - A methodical approach N2 - The H2 effusion from H2 saturated glass powders, H2 permeation through the wall of blown glass bulbs, and H2 permeation through the wall of glass capillaries were applied to evaluate the permeability of hydrogen gas in a barium-aluminoborosilicate (BABS) glass. To validate these methods, two commercial glasses (vitreous silica and borosilicate) were used as a reference. Permeation values obtained from the different experiments agreed within a factor of 3 or less. The H2 permeability of BABS glass at temperatures close to ambient was found to be at least 3 orders of magnitude below that of borosilicate and silica glasses. The powder method, which requires minimal sample preparation efforts, turned out to provide easy access to the measurement of H2 permeability of glasses down to P = 3.9 × 10- 21 mol s- 1 Pa- 1 m- 1. KW - Hydrogen gas KW - Permeability KW - Solubility KW - Diffusivity KW - Aluminoborosilicate glass PY - 2014 DO - https://doi.org/10.1016/j.jnoncrysol.2014.04.006 SN - 0022-3093 VL - 394-395 SP - 43 EP - 49 PB - North-Holland Publ. Co. CY - Amsterdam AN - OPUS4-30720 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Deubener, J. A1 - Behrens, H. T1 - Internal friction of hydrated soda-lime-silicate glasses N2 - The internal friction of hydrated soda-lime-silica glasses with total water content (CW ) up to 1.9 wt. % was studied by dynamic mechanical analysis (DMA) using temperature-frequency sweeps from 723 K to 273 K and from 1 s-1 to 50 s-1. Total water content and concentrations of H2O molecules (CH2O ) and OH groups (COH) in the DMA specimens were determined by infrared spectroscopy. For low water contents (CW ≈ COH < 0.25 wt. %) two discrete internal friction peaks below the glass transition (α relaxation) were assigned to the low-temperature motion of alkali ions (γ relaxation) and cooperative movements of dissimilar mobile species under participation of OH at higher temperature (βOH relaxation). For large water contents (CW > 1 wt. %), where significant amounts of molecular water are evident (CH2O > 0.15 wt. %), however, internal friction spectra change unexpectedly: the βOH peak heights saturate and a low temperature shoulder appears on the β-relaxation peak. This emerging relaxation mode (βH2O relaxation) was assigned to the motions of H2O molecules. βH2O relaxation was found to be faster than βOH but slower than γ relaxation. Activation energy of the different relaxation modes increased in the order γ < βH2O < βOH < α. KW - Internal friction KW - Glass KW - Water content PY - 2013 DO - https://doi.org/10.1063/1.4828740 SN - 0021-9606 SN - 1089-7690 VL - 139 SP - 174506-1 EP - 174506-6 PB - American Institute of Physics CY - Melville, NY AN - OPUS4-29698 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deubener, J. A1 - Behrens, H. A1 - Müller, Ralf A1 - Zietka, S. A1 - Reinsch, Stefan T1 - Kinetic fragility of hydrous soda-lime-silica glasses N2 - The effect of hydration on the kinetic fragility of soda-lime-silica glasses was investigated by viscometry in the glass transition range. Water-bearing glasses were prepared from industrial float glass (FG) and a ternary model glass (NCS = 16Na2O 10CaO 74SiO2 in mol%) by bubbling steam through the melt at 1480 °C and up to 7 bar. Additionally, a sodium borosilicate glass (NBS = 16Na2O 10B2O3 74SiO2 in mol%) was hydrated under equal conditions. As detected by infrared spectroscopy water dissolves in the glasses exclusively as OH-groups. The hydration resulted in a total water content CW up to ~ 0.2 wt% for FG, NCS and NBS glasses. Kinetic fragility, expressed by the steepness index m, was determined from the temperature dependence of η at the glass transition. Viscosity data from previous studies on hydrous float glasses (CW > 1 wt%) were surveyed together with literature data on the (H2O)–Na2O–CaO–SiO2, (H2O)–Na2O–SiO2 and (H2O)–SiO2 systems to expand the range of water concentration and bulk composition. We could demonstrate that m decreases for all glasses although water is dissolved as OH and should depolymerize the network. An empirical equation of the general type m = a - b logCW where a, b are fitting parameters, enables m to be predicted, for each glass series as function of the water content CW. The enlarged data base shows that the parameter B of the Arrhenius viscosity-temperature relation decreases much stronger than the isokom temperature at the glass transition. KW - Soda-lime-silica KW - Fragility KW - Viscosity KW - Water in glass PY - 2008 DO - https://doi.org/10.1016/j.jnoncrysol.2008.04.021 SN - 0022-3093 VL - 354 IS - 42-44 SP - 4713 EP - 4718 PB - North-Holland Publ. Co. CY - Amsterdam AN - OPUS4-18187 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zocca, Andrea A1 - Wirth, Cynthia A1 - Bernardo, E. A1 - Müller, Ralf A1 - Günster, Jens A1 - Colombo, P. T1 - LAS glass-ceramic scaffolds by three-dimensional printing N2 - Highly porous (>60% open porosity) glass–ceramic scaffolds with remarkable mechanical properties (compression strength of ~15 MPa) were produced by indirect 3D printing. Precursor glass powders were printed into 3D ordered structures and then heat treated to sinter and develop crystalline phases. The final glass–ceramic contained a β-spodumene solid solution together with a secondary phase of lithium disilicate. The precision of the printed geometry and the density of the struts in the scaffold depended on several processing parameters (e.g. powder size and flowability, layer thickness) and were improved by increasing the binder saturation and drying time. Two types of powders with different particle size distribution (PSD) and flowability were used. Powders with a larger PSD, could be processed within a wider range of printing parameters due to their good flowability; however, the printing precision and the struts density were lower compared to the scaffolds printed using the powder in a smaller average PSD. KW - Glass ceramics KW - Porosity KW - Shaping KW - Strength KW - Additive manufacturing PY - 2013 DO - https://doi.org/10.1016/j.jeurceramsoc.2012.12.012 SN - 0955-2219 SN - 1873-619X N1 - Geburtsname von Wirth, Cynthia: Gomes, C. M. - Birth name of Wirth, Cynthia: Gomes, C. M. VL - 33 IS - 9 SP - 1525 EP - 1533 PB - Elsevier CY - Oxford AN - OPUS4-28284 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blaeß, Carsten A1 - Müller, Ralf T1 - Master curve for viscous crack healing N2 - A novel method to generalize kinetic data of viscous crack healing in glasses is proposed. The method assumes that crack healing progress is proportional to the healing time, t, and indirect proportional to viscosity, n. This way, crack length and crack width data, normalized to the initial crack length and plotted versus t/n, allow to compare crack healing progress for different cracks and healing temperatures in a master curve. Crack healing experiments conducted in this study demonstrate the applicability of this method for a commercial microscope slide glass. KW - Crack healing KW - Glass KW - Master curve KW - Vickers indentation PY - 2018 DO - https://doi.org/10.1016/j.matlet.2017.12.082 SN - 0167-577X SN - 1873-4979 VL - 216 SP - 110 EP - 112 PB - Elsevier AN - OPUS4-44300 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Unger, Brita A1 - Rurack, Knut A1 - Müller, Ralf A1 - Jancke, Harald A1 - Resch-Genger, Ute T1 - Microscopic vs. macroscopic structural evolution of SiO2 sols and gels employing a tailor-made fluorescent reporter dye N2 - The short- and long-term structural evolution and aging of sol–gel materials prepared under mild conditions are studied by fluorometry, dynamic light scattering (DLS), 29Si NMR and gravimetry. In combination with the first, a newly developed donor–acceptor-substituted fluorescent probe with two acidophilic sites of different strength and topology is introduced. Its performance in detecting changes in parameters such as polarity, proticity, and pore volume on the microscopic scale is compared to two other dyes and to the macroscopic changes revealed by DLS, NMR and gravimetry. At early stages of the sol–gel process, fluorometry, DLS and NMR reveal similar changes which are typical of the structural evolution of SiO2 sols having different synthesis parameters. During later times of sol aging, DLS and NMR reflect the growth of the network and indicate that all sols approach similar structural equilibria. Fluorometry supports these findings by signalling a gradual decrease in mobile species with high proton activity. The formation of the spanning cluster upon gelation is strongly evident only from DLS results while the local environment of the fluorophore remains largely unchanged. However, the fluorescent dye is able to report microscopic changes even during long-term aging. Drying of the gels with a pronounced contraction of solvated pores is readily observable by fluorometry and gravimetry. During the late reaction stages, the fluorescence properties of the tailor-made dye are still sensitive toward the environment. PY - 2005 DO - https://doi.org/10.1039/b501622c SN - 0959-9428 SN - 1364-5501 VL - 15 IS - 30 SP - 3069 EP - 3083 PB - Royal Society of Chemistry CY - Cambridge AN - OPUS4-10378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fest, Sarah Ute A1 - Reinsch, Stefan A1 - Müller, Ralf T1 - Milling, sintering and crystallization of 11BaO-25CaO-64SiO2 glass powder N2 - The crystallization of 11BaO-25CaO-64SiO2 mol% glass powders and related effects of glass powder milling have been studied by X-ray diffraction (XRD), light and scanning electron microscopy (SEM) and differential thermal analysis (DTA). Glass powders were made by ZrO2 crushing with subsequent sieving or sedimentation or alternatively made by milling with agate, corundum and tungsten carbide. Although surface crystallization was detectable during late sintering, all powders fully sintered. Wollastonite was found as primary crystal phase followed by cristobalite and sanbornite precipitation. The latter crystallization steps caused a second DTA-peak for fine powders. DTA-peak temperatures shifted to lower temperature with decreasing particle size in any case. No significant effects of milling materials on DTA-peak temperatures were evident. As an exception, however, milling in agate caused strongly decreased temperatures of the second DTA-peak. This observation can be explained by the progressive mechanical damaging, which results from the required prolonged milling time with agate due to its small materials density, and the fact that diamond made scratches did promote surface crystallization of cristobalite. The present study thus shows that even for glass powders with excellent sinterability, milling can affect microstructure evolution. KW - Glass KW - Crystallization KW - Powder preparation KW - SOFC PY - 2014 UR - http://onlinelibrary.wiley.com/doi/10.1111/ijag.12080/full DO - https://doi.org/10.1111/ijag.12080 SN - 2041-1286 SN - 2041-1294 VL - 5 IS - 3 SP - 236 EP - 247 PB - Wiley-Blackwell CY - Hoboken, NJ [u.a.] AN - OPUS4-30807 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Ralf A1 - Prado, M. O. A1 - Zanotto, E. D. T1 - Model for sintering polydispersed glass particles N2 - We propose a model to describe the sintering kinetics of polydispersed glass particles, having no adjustable parameter. The model is based on three sintering stages: a pure ‘Frenkel' (F) first step, a mixed ‘Frenkel/Mackenzie–Shuttleworth' stage, and a third, pure ‘Mackenzie–Shuttleworth' (MS) step. The model considers sample shrinkage as the sum of the partial shrinkage of several clusters, each consisting of equally sized particles and each showing independent F or MS behavior. The overall set of clusters mimics the specimen's real particle size distribution. We then introduce the concept of neck forming ability, which allows the formation of necks among particles of different sizes, relaxing the clustering condition. Using experimental physical parameters: particle size distribution, viscosity, surface energy, and the theoretical neck forming ability, the model describes well the sintering kinetics of an alumino-borosilicate glass powder having polydispersed, irregular shaped particles in a variety of temperatures. The sintering kinetics of the real powder is slower, but not far from the calculated kinetics of a monodispersed distribution containing only particles of average size. Thus the model provides a tool for estimating the sintering kinetics of real glass powders, for any size distribution and temperature, thus minimizing the number of laboratory experiments. PY - 2001 DO - https://doi.org/10.1016/S0022-3093(00)00399-9 SN - 0022-3093 VL - 279 IS - 2-3 SP - 169 EP - 178 PB - North-Holland Publ. Co. CY - Amsterdam AN - OPUS4-935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peplinski, Burkhard A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Müller, Ralf A1 - Michaelis, Matthias A1 - Krahl, T. A1 - Emmerling, Franziska T1 - Nanocrystalline and stacking-disordered beta-cristobalite AlPO4: the now deciphered main constituent of a municipal sewage sludge ash from a full-scale incineration facility N2 - For the first time evidence is provided that a nanocrystalline and stacking-disordered, chemically stabilized β-cristobalite form of AlPO4 occurs in a sewage sludge ash (SSA). This proof is based on a combined X-ray powder diffraction and X-ray fluorescence investigation of an SSA produced at a large-scale fluidized bed incineration facility serving a catching area with a population of 2 million. The structural and chemical characterization was carried out on 'as received' SSA samples as well as on solid residues remaining after leaching this SSA in sodium hydroxide solution. Thus, it was ascertained that the observed nanocrystalline and stacking-disordered cristobalite-like component belongs to the aluminum phosphate component of this SSA, rather than to its silicon dioxide component. In addition, a direct proof is presented that the chemically stabilized β-cristobalite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850°C), typical for fluidized bed incinerators. KW - Aluminum phosphate KW - Chemical stabilization of high-temperature forms KW - Cristobalite form KW - Stacking disorder KW - Incinerator ash KW - Sewage sludge ash PY - 2015 DO - https://doi.org/10.1017/S0885715614001213 SN - 0885-7156 VL - 30 IS - Supplement S 1 SP - S31 EP - S35 PB - JCPDS CY - Swarthmore, Pa. AN - OPUS4-33435 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wisniewski, W. A1 - Thieme, C. A1 - Müller, Ralf A1 - Reinsch, Stefan A1 - Groß-Barsnick, S.-M. A1 - Rüssel, C. T1 - Oriented surface nucleation and crystal growth in a 18BaO·22CaO·60SiO2 mol% glass used for SOFC seals N2 - A glass of the composition 37BaO·16CaO·47SiO2 wt% produced on an industrial scale is crystallized at 970 °C for times ranging from 15 min to 2 h. The crystallization at the immediate surface as well as the crystal growth into the bulk are analyzed using scanning electron microscopy (SEM) including energy dispersive X-ray spectroscopy (EDXS) and electron backscatter diffraction (EBSD) as well as X-ray diffraction in the Θ–2Θ setup (XRD). The immediate surface shows the oriented nucleation of walstromite as well as the formation of wollastonite and an unknown phase of the composition BaCaSi3O8. All three phases also grow into the bulk where walstromite ultimately dominates the kinetic selection and grows throughout the bulk due to a lack of bulk nucleation. Walstromite shows systematic orientation changes as well as twinning during growth. A critical analysis of the XRD-patterns acquired from various crystallized samples indicates that their evaluation is problematic and that phases detected by XRD in this system should be verified by another method such as EDXS. KW - Glass KW - Surface nucleation KW - Orientation KW - EBSD PY - 2018 DO - https://doi.org/10.1039/c7ce02008b VL - 20 IS - 6 SP - 787 EP - 795 PB - Royal Society of Chemistry AN - OPUS4-44405 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -