TY - JOUR A1 - Nagamine, K. A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Honma, T. A1 - Komatsu, T. T1 - Crystallization behavior of lithium iron phosphate glass powders in different atmospheres N2 - Crystallization behavior in different atmospheres (air, Ar, and 7% H2/Ar) of lithium iron phosphate glass (33Li2O–33Fe2O3–1Nb2O5–33P2O5 (LFNP)) powders with different sizes of 2–1000 µm was examined. The crystallization peak temperature (Tp) in Ar and 7% H2/Ar decreased with decreasing the particle size of glass powders, but the value of Tp in air was independent of particle size. The crystallized glass obtained by heating to Tp showed the formation of the α-Li3Fe2(PO4)3 and LiFePO4 crystalline phases. Fe2O3 crystals were formed only in the inside of crystallized glass plates in the heating in air. The crystallization of LiFePO4 was largely enhanced in the particle size of <2 µm during the heating in Ar and 7% H2/Ar atmospheres. The main crystallization mechanism in LFNP glass was found to be surface crystallization. Significant shrinkages were observed for glass compacts (pellets) in the heating in 7% H2/Ar. These results suggest that controlling particle sizes and atmospheres enables the design the morphology of LiFePO4 crystals in LFNP glass. KW - DTA KW - Kristallisation KW - Phasenentwicklung KW - Unterschiedliche Atmosphären KW - Lithiumionen-Batterie PY - 2011 U6 - https://doi.org/10.1111/j.1551-2916.2011.04579.x SN - 0002-7820 SN - 1551-2916 VL - 94 IS - 9 SP - 2890 EP - 2895 PB - Blackwell Publishing CY - Malden AN - OPUS4-24914 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -