TY - JOUR A1 - Blaeß, Carsten A1 - Müller, Ralf A1 - Boccaccini, A. R. T1 - Sintering and crystallization kinetics of bioactive glass 13-93 N2 - This study investigates the sintering and crystallization behavior and kinetic of the bioactive glass (BG) 13–93 with nominal composition (in mol%): 54.6 SiO2 - 1.7 P2O3 - 22.1 CaO - 6.0 Na2O - 7.9 K2O - 7.7 MgO. Sintering and crystallization were investigated non-isothermally for various particle size fractions smaller than 315 μm as well as for bulk samples. Densification was not hindered by the presence of crystalline phases across all particle size fractions. Afterwards, wollastonite was found as the dominant crystal phase at higher temperature which resorb primary surface precipitation-like quartz crystallites. The growth direction shifts into volume when the sample surface is nearly covered. The crystal growth rate of wollastonite was calculated from the crystalline surface layer thickness measured during heating. The findings of this study are relevant for the high temperature processing of BG 13–93. KW - Bioactive glass KW - Sintering KW - Crystallization PY - 2024 DO - https://doi.org/10.1016/j.jnoncrysol.2023.122790 SN - 0022-3093 VL - 627 SP - 1 EP - 7 PB - Elsevier AN - OPUS4-59337 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf T1 - GLAS DIGITAL - Datengetriebener Workflow für die beschleunigte Entwicklung von Glas N2 - Aktuelle Ergebnisse des Projektes GlasDigital werden kurz zusammenfassend und allgemein verständlich vorgestellt. T2 - MatFo 2022 CY - Cologne, Germany DA - 14.11.2022 KW - Oxidglas KW - robotische Glasschmelzanlage KW - Ontologie KW - ML KW - Digitaler Zwilling KW - Bildanalyse PY - 2022 AN - OPUS4-56492 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf T1 - GlasDigital - Datengetriebener Workflow für die beschleunigte Entwicklung von Glas N2 - Das Projekt GlasDigital im Rahmen der BMBF Initiative MaterialDigital wird vorgestellt. T2 - MatFo22 CY - Berlin, Germany DA - 14.11.2022 KW - Material Digital PY - 2022 AN - OPUS4-56282 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf T1 - Hochtemperaturlaserprofilometrie (HTLP) N2 - Der Vortrag stellt die an der BAM neu entwickelte Methode der Hochtemperatur-Laserprofilometrie (HTLP) vor und illustriert Anwendungsmöglichkeieten T2 - Seminar Instrumentelle Analytik, Fakultät III Prozesswissenschaften, Lehrstuhl Keramik TU Berlin CY - TU Berlin, Germany DA - 17.2.2017 KW - Sintern KW - Hochtemperaturformerkennung PY - 2017 AN - OPUS4-44210 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf T1 - VACUUM HOT EXTRACTION (VHE-MS): Concentration, diffusion and degassing of volatiles N2 - Der Vortrag gibt eine Einführung in die Methode der Vakuumheißextraktion und beschreibt die Anwendungsmöglichkeiten der an der BAMN betriebenen Anlage. T2 - Seminar Instrumentelle Analytik, Fakultät III Prozesswissenschaften, Lehrstuhl Keramik TU Berlin CY - TU Berlin, Germany DA - 26.1.2018 KW - Gasabgabe KW - Diffusion KW - Gasgehalt PY - 2018 AN - OPUS4-45665 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf T1 - Glass Sintering with Concurrent Crystallization and Foaming N2 - Glass powders are promising candidates for manufacturing a broad diversity of sintered materials like sintered glass-ceramics, glass matrix composites or glass bonded ceramics with tailored mechanical, thermal, electrical and optical properties and complex shape. Its wide and precise adjustability makes this class of materials a key component for advanced technologies. Processing of glass or composite powders often allow even more flexibility in materials design. At the same time, however, processing can have substantial effects on the glass powder surface and sinterability. Thus, mechanical damage and surface contamination can strongly enhance surface crystallization, which may retard or even fully prevent densification. Whereas sintering and concurrent crystallization have been widely studied, partially as cooperative effort of the TC7 of the ICG, and although glass powder sintering is predominantly applied for glasses of low crystallization tendency, sintering is also limited by gas bubble formation or foaming. The latter phenomenon is much less understood and can occur even for slow crystallizing glass powders. The lecture illustrates possible consequences of glass powder processing on glass sintering, crystallization and foaming. T2 - 7th Int Congress on Ceramics, Symposium Frontiers of Glass Science CY - Iguacu, Brazil DA - 17.06.2018 KW - Glass KW - Powder KW - Sintering KW - Foaming PY - 2018 AN - OPUS4-45670 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf T1 - Sintering and foaming of silicate N2 - Glass powders are promising candidates for manufacturing a broad diversity of sintered materials like sintered glass-ceramics, glass matrix composites or glass bonded ceramics with properties and complex shape. Powder processing, however, can substantially affect sinterability, e.g. by promoting surface crystallization. On the other hand, densification can be hindered by gas bubble formation for slow crystallizing glass powders. Against this background, we studied sintering and foaming of silicate glass powders with different crystallization tendency for wet milling and dry milling in air, Ar, N2, and CO2 by means of heating microscopy, DTA, Vacuum Hot Extraction (VHE), SEM, IR spectroscopy, XPS, and ToF-SIMS. In any case, foaming activity increased significantly with progressive milling. For moderately milled glass powders, subsequent storage in air could also promote foaming. Contrarily, foaming could be substantially reduced by milling in water and 10 wt% HCl. Although all powder compacts were uniaxially pressed and sintered in air, foaming was significantly affected by different milling atmosphere and was found most pronounced for milling in CO2 atmosphere. Conformingly, VHE studies revealed that foaming is mainly driven by carbonaceous species, even for powders milled in other gases. Current results of this study thus indicate that foaming is caused by carbonaceous species trapped on the glass powder surface. T2 - ICG Annual Meeting 2018 CY - Yokohama, Japan DA - 23.09.2018 KW - Foaming KW - Glass KW - Powder KW - Sintering PY - 2018 AN - OPUS4-46474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fest, Sarah Ute A1 - Reinsch, Stefan A1 - Müller, Ralf T1 - Milling, sintering and crystallization of 11BaO-25CaO-64SiO2 glass powder N2 - The crystallization of 11BaO-25CaO-64SiO2 mol% glass powders and related effects of glass powder milling have been studied by X-ray diffraction (XRD), light and scanning electron microscopy (SEM) and differential thermal analysis (DTA). Glass powders were made by ZrO2 crushing with subsequent sieving or sedimentation or alternatively made by milling with agate, corundum and tungsten carbide. Although surface crystallization was detectable during late sintering, all powders fully sintered. Wollastonite was found as primary crystal phase followed by cristobalite and sanbornite precipitation. The latter crystallization steps caused a second DTA-peak for fine powders. DTA-peak temperatures shifted to lower temperature with decreasing particle size in any case. No significant effects of milling materials on DTA-peak temperatures were evident. As an exception, however, milling in agate caused strongly decreased temperatures of the second DTA-peak. This observation can be explained by the progressive mechanical damaging, which results from the required prolonged milling time with agate due to its small materials density, and the fact that diamond made scratches did promote surface crystallization of cristobalite. The present study thus shows that even for glass powders with excellent sinterability, milling can affect microstructure evolution. KW - Glass KW - Crystallization KW - Powder preparation KW - SOFC PY - 2014 UR - http://onlinelibrary.wiley.com/doi/10.1111/ijag.12080/full DO - https://doi.org/10.1111/ijag.12080 SN - 2041-1286 SN - 2041-1294 VL - 5 IS - 3 SP - 236 EP - 247 PB - Wiley-Blackwell CY - Hoboken, NJ [u.a.] AN - OPUS4-30807 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schiller, Wolfgang Arno A1 - Eberstein, Markus A1 - Müller, Ralf T1 - Glas-Keramik-Komposite für Mikrosysteme und Sensoren PY - 2002 SN - 1618-8721 VL - 1 IS - 2 SP - 17 PB - Deutsche Glastechnische Gesellschaft CY - Offenbach AN - OPUS4-3115 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Altantsog, Pagvajav A1 - Ojunbileg, L. A1 - Palam, B. A1 - Tserenshimed, M. A1 - Chadraabal, Shgdariin A1 - Müller, Ralf A1 - Nofz, Marianne A1 - Gaber, Martin T1 - Some experimental results of glass melting by using sands from Buir nuur N2 - We have carried out some laboratory experiments to establish possibilities to melt 16Na2O*10CaO*74SiO2 glasses from consisting of mainly quarz sands of Buir nuur lake. When the sands used directly, the formed glasses had slight blue colour, the origin of which may be connected with aluminium and iron impurities in the sands. Presence of these impurities is confirmed by chemical analyse and ESR study data. Allso have been studied liquid gas extraction phenomena in the sands and melted glass samples and determined some physical properties of them. PY - 2002 VL - 17 SP - 107 EP - 115 AN - OPUS4-3118 LA - mon AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -