TY - JOUR A1 - Zerbst, Uwe A1 - Ainsworth, R. A. A1 - Beier, H.T. A1 - Pisarski, H. A1 - Zhang, Z. L. A1 - Nikbin, K. A1 - Nitschke-Pagel, T. A1 - Münstermann, S. A1 - Kucharczyk, P. A1 - Klingbeil, Dietmar T1 - Review on fracture and crack propagation in weldments - A fracture mechanics perspective N2 - Welding is one of the most common methods in industrial practice for joining components. Its main advantages are high speed in manufacturing combined with low costs and, usually, a high degree of flexibility, integrity and reliability. Nevertheless, welding is a highly complex metallurgical process and, therefore, weldments are susceptible to material discontinuities, flaws and residual stresses which may lead to structural failure and life time reduction. As a consequence weldments are an important field of fracture mechanics methods although its application is more complex than for homogeneous or non-welded structures. The aim of the paper is to provide an overview on the current state of fracture mechanics application to weldments. It starts by discussing the specific features which any fracture mechanics analysis of weldments has to take into account. Then, the experimental determination of fracture toughness, fatigue crack propagation and tensile properties of weldments is addressed. Finally, the analytical determination of the crack driving force in components and structural integrity assessment approaches for weldments are presented. KW - Weldments KW - Fracture mechanics KW - Fracture toughness KW - Fatigue crack propagation KW - Residual stresses KW - Strength mismatch PY - 2014 U6 - https://doi.org/10.1016/j.engfracmech.2014.05.012 SN - 0013-7944 SN - 1873-7315 VL - 132 SP - 200 EP - 276 PB - Elsevier Science CY - Kidlington AN - OPUS4-32819 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Gerwien, Peter A1 - Kucharczyk, P. A1 - Münstermann, S. A1 - Schork, B. T1 - Fracture-mechanics-based prediction of the fatigue strength of weldments. Material aspects N2 - Any fracture mechanics based determination of the fatigue strength of weldments requires different input information such as the local weld geometry and material data of the areas the crack is passing through during its propagation. The latter is so far not a trivial task as the fatigue crack is usually initiated at the weld toe at the transition from the weld metal to the heat affected zone and it subsequently propagates through the different microstructures of the latter to eventually grow into the base material and to cause final fracture. This paper describes how the material input information has gained particularly for heat affected zone material by thermo-mechanically simulated material specimens for two steels of quite different static strength. The data comprise the cyclic stress-strain curve, the crack closure effect-corrected crack growth characteristics, long crack fatigue crack propagation thresholds, the dependency of the parameter on the crack length and monotonic fracture resistance. The substantial experimental effort was necessary for the validation exercises of the IBESS approach, however, within the scope of practical application more easily applicable estimating methods are required. For that purpose the paper provides a number of appropriate proposals in line with its check against the reference data from the elaborate analyses. KW - Heat affected zone KW - Cyclic stress-strain curve KW - Fatigue crack propagation KW - Fatigue crack propagation threshold KW - Fracture resistance PY - 2018 U6 - https://doi.org/10.1016/j.engfracmech.2017.09.010 SN - 0013-7944 SN - 1873-7315 VL - 198 SP - 79 EP - 102 PB - Elsevier AN - OPUS4-46854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - BOOK A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Schork, B. A1 - Hensel, J. A1 - Kucharczyk, P. A1 - Ngoula, D. A1 - Tchuindjang, D. A1 - Bernhard, J. A1 - Beckmann, C. T1 - The IBESS approach for the determination of the fatigue life and strength of weldments by fracture mechanics analysis N2 - This book provides a comprehensive and thorough guide to those readers who are lost in the often-confusing context of weld fatigue. It presents straightforward information on the fracture mechanics and material background of weld fatigue, starting with fatigue crack initiation and short cracks, before moving on to long cracks, crack closure, crack growth and threshold, residual stress, stress concentration, the stress intensity factor, J-integral, multiple cracks, weld geometries and defects, microstructural parameters including HAZ, and cyclic stress-strain behavior. The book treats all of these essential and mutually interacting parameters using a unique form of analysis. KW - Fatigue crack propagation KW - Cyclic J-integral KW - Cyclic R-curve analysis KW - Fatigue S-N curve KW - HAZ PY - 2019 SN - 978-3-030-04072-7 SN - 978-3-030-04073-4 U6 - https://doi.org/10.1007/978-3-030-04073-4 SP - 1 EP - 130 PB - Springer CY - Cham AN - OPUS4-47576 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -