TY - JOUR A1 - Thomsen-Schmidt, P. A1 - Hasche, K. A1 - Ulm, G. A1 - Herrmann, K. A1 - Krumrey, M. A1 - Ade, G. A1 - Stümpel, J. A1 - Busch, I. A1 - Schädlich, S. A1 - Schindler, A. A1 - Frank, W. A1 - Hirsch, D. A1 - Procop, Mathias A1 - Beck, Uwe T1 - Realisation and metrological characterisation of thickness standards below 100 nm N2 - High-accuracy film thickness measurements in the range below 100 nm can be made by various complex methods like spectral ellipsometry (SE), scanning force microscopy (SFM), grazing incidence X-ray reflectometry (GIXR), or X-ray fluorescence analysis (XRF). The measurement results achieved with these methods are based on different interactions between the film and the probe. A key question in nanotechnology is how to achieve consistent results on a level of uncertainty below one nanometre with different techniques. Two different types of thickness standards are realised. Metal film standards for X-ray techniques in the thickness range 10 to 50 nm are calibrated by GIXR with monochromatised synchrotron radiation of 8048 eV. The results obtained at four different facilities show excellent agreement. SiO2 on Si standards for SE and SFM in the thickness range 6 to 1000 nm are calibrated by GIXR with monochromatised synchrotron radiation of 1841 eV and with a metrological SFM. Consistent results within the combined uncertainties are obtained with the two methods. Surfaces and interfaces of both types of standards are additionally investigated by transmission electron microscopy (TEM). PY - 2004 U6 - https://doi.org/10.1007/s00339-003-2273-7 SN - 0947-8396 VL - 78 IS - 5 SP - 645 EP - 649 PB - Springer CY - Berlin AN - OPUS4-17195 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Seah, M.P. A1 - Spencer, S.J. A1 - Bensebaa, F. A1 - Vickridge, I. A1 - Danzebrink, H. A1 - Krumrey, M. A1 - Gross, Thomas A1 - Österle, Werner A1 - Wendler, E. A1 - Rheinländer, B. A1 - Azuma, Y. A1 - Kojima, I. A1 - Suzuki, N. A1 - Suzuki, M. A1 - Tanuma, S. A1 - Moon, D.W. A1 - Lee, H.J. A1 - Cho, H.M. A1 - Chen, H.Y. A1 - Wee, A. T. S. A1 - Osipowicz, T. A1 - Pan, J.S. A1 - Jordaan, W.A. A1 - Hauert, R. A1 - Klotz, U. A1 - van der Marel, C. A1 - Verheijen, M. A1 - Tamminga, Y. A1 - Jeynes, C. A1 - Bailey, P. A1 - Biswas, S. A1 - Falke, U. A1 - Nguyen, N.V. A1 - Chandler-Horowitz, D. A1 - Ehrstein, J.R. A1 - Muller, D. A1 - Dura, J.A. T1 - Ultra-thin SiO2 on Si, Part V: Results of a CCQM Pilot Study of Thickness Measurements KW - SiO2 KW - Thin films KW - Thickness KW - XPS KW - Ellipsometry KW - TEM PY - 2003 SN - 1473-2734 SP - 57 pages AN - OPUS4-4118 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seah, M.P. A1 - Unger, Wolfgang A1 - Wang, H. A1 - Jordaan, W. A1 - Gross, Thomas A1 - Dura, J.A. A1 - Moon, D.W. A1 - Totarong, P. A1 - Krumrey, M. A1 - Hauert, R. A1 - Zhiqiang, M. T1 - Ultra-thin SiO2 on Si IX: absolute measurements of the amount of silicon oxide as a thickness of SiO2 on Si N2 - Results from a study conducted between National Metrology Institutes (NMIs) for the measurements of the absolute thicknesses of ultra-thin layers of SiO2 on Si are reported. These results are from a key comparison and associated pilot study under the auspices of the Consultative Committee for Amount of Substance. ´Amount of substance´ may be expressed in many ways, and here the measurand is the thickness of the silicon oxide layers with nominal thicknesses in the range 1.5-8 nm on Si substrates, expressed as the thickness of SiO2. Separate samples were provided to each institute in containers that limited the carbonaceous contamination to approximately < 0.3 nm. The SiO2 samples were of ultra-thin on (100) and (111) orientated wafers of Si. The measurements from the laboratories which participated in the study were conducted using ellipsometry, neutron reflectivity, X-ray photoelectron spectroscopy or X-ray reflectivity, guided by the protocol developed in an earlier pilot study. A very minor correction was made in the different samples that each laboratory received. Where appropriate, method offset values attributed to the effects of contaminations, from the earlier pilot study, were subtracted. Values for the key comparison reference values (agreed best values from a Consultative Committee study) and their associated uncertainties for these samples are then made from the weighted means and the expanded weighted standard deviations of the means of these data. These results show a dramatic improvement on previous comparisons, leading to 95% uncertainties in the range 0.09-0.27 nm, equivalent to 0.4-1.0 monolayers over the 1.5-8.0 nm nominal thickness range studied. If the sample-to-sample uncertainty is reduced from its maximum estimate to the most likely value, these uncertainties reduce to 0.05-0.25 nm or ~1.4% relative standard uncertainties. The best results achieve ~1% relative standard uncertainty. It is concluded that XPS has now been made fully traceable to the SI, for ultra-thin thermal SiO2 on Si layers, by calibration using wavelength methods in an approach that may be extended to other material systems. KW - Attenuation length KW - Calibration KW - Silicon dioxide KW - Thickness KW - Ultra-thin oxide PY - 2009 U6 - https://doi.org/10.1002/sia.3045 SN - 0142-2421 SN - 1096-9918 VL - 41 IS - 5 SP - 430 EP - 439 PB - Wiley CY - Chichester AN - OPUS4-19246 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kim, K.J. A1 - Kim, C.S. A1 - Ruh, S. W. A1 - Unger, Wolfgang A1 - Radnik, Jörg A1 - Mata-Salazar, J. A1 - Juarez-Garcia, J.M. A1 - Cortazar-Martinez, O. A1 - Herrera-Gomez, A. A1 - Hansen, P.E. A1 - Madesen, J.S. A1 - Senna, C.A. A1 - Archanjo, B.S. A1 - Damasceno, J.C. A1 - Achete, C.A. A1 - Wang, H. A1 - Wang, M. A1 - Windover, D. A1 - Steel, E. A1 - Kurokawa, A. A1 - Fujimoto, T. A1 - Azuma, Y. A1 - Terauchi, S. A1 - Zhang, L. A1 - Jordaan, W.A. A1 - Spencer, S.J. A1 - Shard, A.G. A1 - Koenders, L. A1 - Krumrey, M. A1 - Busch, I. A1 - Jeynes, C. T1 - Thickness measurement of nm HfO2 films N2 - A pilot study for the thickness measurement of HfO2 films was performed by the Surface Analysis Working Group (SAWG) of the Consultative Committee for Amount of Substance (CCQM). The aim of this pilot study was to ensure the equivalency in the measurement capability of national metrology institutes for the thickness measurement of HfO2 films. In this pilot study, the thicknesses of six HfO2 films with nominal thickness from 1 nm to 4 nm were measured by X-ray Photoelectron Spectroscopy (XPS), X-ray Reflectometry(XRR), X-ray Fluorescence Analysis (XRF), Transmission Electron Spectroscopy (TEM), Spectroscopic Ellipsometry (SE) and Rutherford Backscattering Spectrometry (RBS). The reference thicknesses were determined by mutual calibration of a zero-offset method (Medium Energy Ion Scattering Spectroscopy (MEIS) of KRISS) and a method traceable to the length unit (the average thicknesses of three XRR data except the thinnest film). These reference thicknesses are traceable to the length unit because they are based on the traceability of XRR. For the thickness measurement by XPS, the effective attenuation length of Hf 4f electrons was determined. In the cases of XRR and TEM, the offset values were determined from a linear fitting between the reference thicknesses and the individual data by XRR and TEM. The amount of substance of HfO2, expressed as thickness of HfO2 films (in both linear and areal density units), was found to be a good subject for a CCQM key comparison. To reach the main text of this paper, click on Final Report. The final report has been peer-reviewed and approved for publication by the CCQM. KW - Thickness measurements KW - nm films KW - X-ray Photoelectron Spectroscopy KW - Mutual calibration PY - 2021 U6 - https://doi.org/10.1088/0026-1394/58/1A/08016 SN - 0026-1394 VL - 58 IS - 1a SP - 08016 PB - IOP Publishing Lt. CY - Bristol AN - OPUS4-54175 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deumer, J. A1 - Pauw, Brian Richard A1 - Marguet, S. A1 - Skroblin, D. A1 - Taché, O. A1 - Krumrey, M. A1 - Gollwitzer, C. T1 - Small-angle X-ray scattering: characterization of cubic Au nanoparticles using Debye’s scattering formula N2 - A versatile software package in the form of a Python extension, named CDEF (computing Debye’s scattering formula for extraordinary form factors), is proposed to calculate approximate scattering profiles of arbitrarily shaped nanoparticles for small-angle X-ray scattering (SAXS). CDEF generates a quasi-randomly distributed point cloud in the desired particle shape and then applies the open-source software DEBYER for efficient evaluation of Debye’s scattering formula to calculate the SAXS pattern (https://github.com/j-from-b/CDEF). If self-correlation of the scattering signal is not omitted, the quasi-random distribution provides faster convergence compared with a true-random distribution of the scatterers, especially at higher momentum transfer. The usage of the software is demonstrated for the evaluation of scattering data of Au nanocubes with rounded edges, which were measured at the four-crystal monochromator beamline of PTB at the synchrotron radiation facility BESSY II in Berlin. The implementation is fast enough to run on a single desktop computer and perform model fits within minutes. The accuracy of the method was analyzed by comparison with analytically known form factors and verified with another implementation, the SPONGE, based on a similar principle with fewer approximations. Additionally, the SPONGE coupled to McSAS3 allows one to retrieve information on the uncertainty of the size distribution using a Monte Carlo uncertainty estimation algorithm. KW - X-ray scattering KW - SAXS KW - Non-spherical nanoparticles KW - Nanoparticles KW - Nanomaterials KW - Debye scattering equation KW - Simulation KW - Data fitting PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-557652 VL - 55 IS - Pt 4 SP - 993 EP - 1001 PB - International Union of Crystallography CY - Chester, England AN - OPUS4-55765 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rackwitz, Vanessa A1 - Krumrey, M. A1 - Laubis, C. A1 - Scholze, F. A1 - Hodoroaba, Vasile-Dan T1 - New reference and test materials for the characterization of energy dispersive X-ray spectrometers at scanning electron microscopes N2 - Checking the performance of energy dispersive X-ray spectrometers as well as validation of the results obtained with energy dispersive X-ray spectrometry (EDX) at a scanning electron microscope (SEM) involve the use of (certified) reference and dedicated test materials. This paper gives an overview on the test materials mostly employed by SEM/EDX users and accredited laboratories as well as on those recommended in international standards. The new BAM reference material EDS-CRM, which is currently in the process of certification, is specifically designed for the characterization of EDS systems at a SEM through calibration of the spectrometer efficiency in analytical laboratories in a simple manner. The certification of the spectra by means of a reference EDS is described. The focus is on the traceability of EDS efficiency which is ensured by measurements of the absolute detection efficiency of silicon drift detectors (SDD) and Si(Li) detectors at the laboratory of the PTB using the electron storage ring BESSY II as a primary X-ray source standard. A new test material in development at BAM for testing the performance of an EDS in the energy range below 1 keV is also briefly presented. KW - EDX KW - EDS KW - Performance check KW - SEM KW - Test materials KW - Spectrometer efficiency PY - 2015 U6 - https://doi.org/10.1007/s00216-014-8242-5 SN - 1618-2642 SN - 1618-2650 VL - 407 IS - 11 SP - 3045 EP - 3053 PB - Springer CY - Berlin AN - OPUS4-33025 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Roebben, G. A1 - Kestens, V. A1 - Varga, Z. A1 - Charoud-Got, J. A1 - Ramaye, Y. A1 - Gollwitzer, Christian A1 - Bartczak, D. A1 - Geißler, Daniel A1 - Noble, J.E. A1 - Mazoua, S. A1 - Meeus, N. A1 - Corbisier, P. A1 - Palmai, M. A1 - Mihály, J. A1 - Krumrey, M. A1 - Davies, J. A1 - Resch-Genger, Ute A1 - Kumarswami, N. A1 - Minelli, C. A1 - Sikora, A. A1 - Goenaga-Infante, H. T1 - Reference materials and representative test materials to develop nanoparticle characterization methods: the NanoChOp project case N2 - This paper describes the production and characteristics of the nanoparticle test materials prepared for common use in the collaborative research project NanoChOp (Chemical and optical characterization of nanomaterials in biological systems), in casu suspensions of silica nanoparticles and CdSe/CdS/ZnS quantum dots (QDs). This paper is the first to illustrate how to assess whether nanoparticle test materials meet the requirements of a "reference material" (ISO Guide 30, 2015) or rather those of the recently defined category of "representative test material (RTM)" (ISO/TS 16195, 2013). The NanoChOp test materials were investigated with small-angle X-ray scattering (SAXS), dynamic light scattering (DLS), and centrifugal liquid sedimentation (CLS) to establish whether they complied with the required monomodal particle size distribution. The presence of impurities, aggregates, agglomerates, and viable microorganisms in the suspensions was investigated with DLS, CLS, optical and electron microscopy and via plating on nutrient agar. Suitability of surface functionalization was investigated with attenuated total reflection Fourier transform infrared spectrometry (ATR-FTIR) and via the capacity of the nanoparticles to be fluorescently labeled or to bind antibodies. Between-unit homogeneity and stability were investigated in terms of particle size and zeta potential. This paper shows that only based on the outcome of a detailed characterization process one can raise the status of a test material to RTM or reference material, and how this status depends on its intended use. KW - Nanoparticle KW - Materials characterization KW - Reference material KW - Analytical quality assurance KW - Metrology PY - 2015 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-349644 SN - 2296-2646 VL - 3 SP - Article 56, 1 EP - 16 PB - Frontiers Media CY - Lausanne AN - OPUS4-34964 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Geißler, Daniel A1 - Gollwitzer, C. A1 - Sikora, A. A1 - Minelli, C. A1 - Krumrey, M. A1 - Resch-Genger, Ute T1 - Effect of fluorescent staining on size measurements of polymeric nanoparticles using DLS and SAXS N2 - The influence of fluorescence on nanoparticle size measurements using dynamic light scattering (DLS) and small angle X-ray scattering (SAXS) was investigated. For this purpose, two series of 100 nm-sized polymer nanoparticles stained with different concentrations of the fluorescent dyes DY555 and DY680 were prepared, absorbing/emitting at around 560 nm/590 nm and 695 nm/715 nm, respectively. SAXS measurements of these particle series and a corresponding blank control (without dye) revealed similar sizes of all particles within an uncertainty of 1 nm. DLS measurements carried out at three different laboratories using four different DLS instruments and two different laser wavelengths, i.e., 532 nm and 633 nm, revealed also no significant changes in size (intensity-weighted harmonic mean diameter, ZAverage) and size distribution (polydispersity index, PI) within and between the two dye-stained particle series and the blank sample. Nevertheless, a significant decrease of the detected correlation coefficients was observed with increasing dye concentration, due to the increased absorption of the incident light and thus, less coherent light scattering. This effect was wavelength dependent, i.e. only measurable for the dye-stained particles that absorb at the laser wavelength used for the DLS measurements. PY - 2015 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-349684 SN - 1759-9660 SN - 1759-9679 VL - 7 IS - 23 SP - 9785 EP - 9790 PB - RSC Publ. CY - Cambridge AN - OPUS4-34968 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dietrich, Paul A1 - Treu, Dieter A1 - Kalbe, Henryk A1 - Krumrey, M. A1 - Gross, Thomas A1 - Marti, K. A1 - Unger, Wolfgang T1 - Experimental determination of the effective attenuation length of palladium 3d 5/2 photoelectrons in a magnetron sputtered Pd nanolayer N2 - An electron effective attenuation length (EAL) of 1.68nm for Al Kα excited Pd 3d 5/2 photoelectrons with a kinetic energy of 1.152 keV has been determined experimentally using a sputtered Pd film deposited on an ultra flat fused quartz substrate. The film thickness was reduced by Ar ion sputtering several times in order to obtain different Pd film thicknesses which are used to determine experimental EAL values. These results are compared to data generated by using a Simulation of Electron Spectra for Surface Analysis (SESSA) simulation using an inelastic mean free path (IMFP) calculated with the Tanuma–Powell–Penn (TPP)-2M formula and with ‘elastic scattering on and off’. Contributions to the uncertainty budget related to the experimental approach are discussed in detail. Proposals on how to further improve the approach are suggested. KW - Pd 3d KW - Electron effective attenuation length KW - XPS PY - 2017 UR - http://onlinelibrary.wiley.com/doi/10.1002/sia.6141/abstract?campaign=woletoc U6 - https://doi.org/10.1002/sia.6141 SN - 0142-2421 SN - 1096-9918 VL - 49 IS - 5 SP - 464 EP - 468 PB - John Wiley & Sons, Ltd AN - OPUS4-39682 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Radunz, Sebastian A1 - Schavkan, A. A1 - Wahl, Sebastian A1 - Würth, Christian A1 - Tschiche, H. R. A1 - Krumrey, M. A1 - Resch-Genger, Ute T1 - Evolution of Size and Optical Properties of Upconverting Nanoparticles during High-Temperature Synthesis N2 - We investigated the growth of β-phase NaYF4:Yb3+,Er3+ upconversion nanoparticles synthesized by the thermal decomposition method using a combination of in situ and offline analytical methods for determining the application-relevant optical properties, size, crystal phase, and chemical composition. This included in situ steady state luminescence in combination with offline time-resolved luminescence spectroscopy as well as small-angle X-ray scattering (SAXS) transmission electron microscopy (TEM), X-ray diffraction analysis (XRD), and inductively coupled Plasma optical emission spectrometry (ICP-OES). For assessing the suitability of our optical monitoring approach, the in situ-collected spectroscopic data, which reveal the luminescence evolution during nanocrystal synthesis, were compared to measurements done after cooling of the reaction mixture of the as-synthesized particles. The excellent correlation of the in situ and time-resolved upconversion luminescence with the nanoparticle sizes determined during the course of the reaction provides important insights into the various stages of nanoparticle growth. This study highlights the capability of in situ luminescence monitoring to control the efficiency of UCNP synthesis, particularly the reaction times at elevated temperatures and the particle quality in terms of size, shape, and crystal structure, as well as luminescence lifetime and upconversion quantum yield. KW - Rare earth nanoparticles KW - Upconversion KW - TEM KW - SAXS PY - 2018 UR - https://pubs.acs.org/doi/pdf/10.1021/acs.jpcc.8b09819 U6 - https://doi.org/10.1021/acs.jpcc.8b09819 VL - 50 IS - 122 SP - 28958 EP - 28967 PB - American Chemical Society CY - Washington, DC AN - OPUS4-47169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -