TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Improving welding stresses by filler metal and heat control selection in component-related butt joints of high-strength steel N2 - The application of high-strength fine-grained structural steels with yield strengths greater than or equal to 690 MPa expands because of present light weight design trends. The requirements regarding the welded components safety increased due to high loading capacity. This determines a sustainable and economic application as well. However, high welding residual stresses could diminish the components safety, especially due to high restraint conditions in component or repair welds. Therefore, this work is concerned with global and local welding stresses, especially crack-critical welding stresses in the HAZ and while root welding due to the restraint conditions. Restraint intensities of real components were analysed and realised with two different weld tests, alongside two different plate dimensions and steel grades. A comparison of the test results showed several significant effects for heat control and restraint intensity regarding restraint forces and local welding stresses. Among these effects, substantial influences were found for the filler metal selection with partially altered results for root and filler beads. Local stresses of weld seam and HAZ were affected differently. KW - Residual stresses KW - MAG welding KW - Restraint KW - High-strength steels KW - Process parameters PY - 2015 DO - https://doi.org/10.1007/s40194-014-0219-7 SN - 0043-2288 SN - 1878-6669 VL - 59 IS - 3 SP - 455 EP - 464 PB - Springer CY - Oxford AN - OPUS4-32546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Characterising phase transformations of different LTT alloys and their effect on residual stresses and cold cracking N2 - Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were – for the first time – detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 µm. The residual stresses show significant distributions dependent on Ms temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent. KW - Austenite KW - Cold cracking KW - Martensite KW - Low themperature KW - Transformation PY - 2011 DO - https://doi.org/10.1007/BF03321286 SN - 0043-2288 VL - 55 IS - 3 SP - 48 EP - 56 PB - International Institute of Welding CY - France AN - OPUS4-38978 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Engineering approach to assess residual stresses in welded components N2 - Present trends to lightweight design lead to an expanding relevance of high-strength fine-grained structural steels especially in mobile crane constructions. With growing material strength, the challenge for welding fabrication increases, since high loading capacities and safety requirements have to be accomplished. The utilisation of the high strength potential often requires complex constructions associated with high restraint conditions while welding. Increased residual stresses may occur due to superimposing reaction and restraint stresses, which have to be quantified and evaluated to ensure the safety and integrity of high-strength steel constructions. Particularly, the scope of residual stresses has to be taken into account for different effects in the HAZ, notches, weld and base metal. Commonly, conservative assumptions of residual stresses lead to distinct underestimations of the load bearing capacity particularly for welded high-strength steel constructions. This study concludes results of recent works of the researchers regarding the complex interaction among heat control, material and restraint intensity on the residual stress state in welded components. These analyses are extended by further experiments. Based on the obtained major effects, an approach for a welding residual stress assessment regarding component design according to prevailing standards for crane construction, an important application for high-strength steels, is presented. KW - Process parameters KW - Residual stresses KW - MAG welding KW - Restraint KW - High-strength steels PY - 2017 DO - https://doi.org/10.1007/s40194-016-0394-9 SN - 0043-2288 SN - 1878-6669 VL - 91 IS - 1 SP - 91 EP - 106 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-39044 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Launert, B. A1 - Rhode, Michael A1 - Kromm, Arne A1 - Pasternak, H. A1 - Kannengießer, Thomas T1 - Measurement and numerical modeling of residual stresses in welded HSLA component-like I-girders N2 - The present contribution shows the residual stress results obtained from experiments with the sectioning method in comparison to global(structural) welding simulation models on component-like (i.e., large scale) I-girders made of structural steel grades S355 and S690QL. Plates were welded by conventional gas metal arc welding using two different heat inputs. In addition, the base material was assumed to be stress-free. Based on these results, conclusions and recommendations for the design of welded I-girders are drawn. T2 - IIW - Annual Assembly 2016 CY - Melbourne, Australia DA - 10.07.2016 KW - Residual Stresses KW - Microalloyed Steels KW - Girders KW - MAG Welding KW - Numerical Simulation PY - 2016 DO - https://doi.org/10.1007/s40194-016-0413-x SN - 1878-6669 SN - 0043-2288 VL - 61 IS - 2 SP - 223 EP - 229 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-38919 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Load analyses of welded high-strength steel structures using image correlation and diffraction techniques N2 - In an increasing number of modern steel applications, high-strength structural steel grades are demanded to meet specifications regarding a high load-bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for high-strength steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In this study, a stress-strain analysis was conducted at component-related structures from S960QL using digital image correlation while preheating, welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with global analyses using either a DIC system or a special testing facility, which allowed in situ measurements of welding loads. By analysing two different seam geometries, it could be shown that lower multi-axial stresses arise if a narrower weld groove is used. Comparative analyses revealed a direct correlation of the local residual stresses in the weld with transverse shrinkage restraint, whereas the residual stress level in the HAZ is significantly affected by the bending restraint of the weld construction and the occurring bending stresses, respectively. KW - Process parameters KW - Residual stresses KW - Restraint KW - GMAwelding KW - High-strength steels PY - 2018 DO - https://doi.org/10.1007/s40194-018-0566-x SN - 0043-2288 SN - 1878-6669 VL - 62 IS - 3 SP - 459 EP - 469 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-44270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Falkenreck, Thora E. A1 - Kromm, Arne A1 - Böllinghaus, Thomas T1 - Investigation of physically simulated weld HAZ and CCT diagram of HSLA armour steel N2 - The phase transformation under various cooling rates and in different HAZ regions for high-strength armour steel was analysed by dilatometry. To develop a continuous cooling transformation (CCT) diagram, the samples were heated up to a peak temperature of 1250 °C to achieve a coarse-grained microstructure and then cooled down with a cooling time t 8/5 varying from 3 to 240 s. Analysis of dilatation curves revealed the austenite decomposition process, during which transformation temperatures were determined. The results showed martensitic transformations for all welding-relevant cooling times. Furthermore, to analyse different heat-affected subzones of the weld, the peak temperature was varied between 550 and 1250 °C at a constant cooling time t 8/5 of 6 s. The simulated coarse-grained heat-affected zone (CGHAZ) and fine-grained-heat affected zone (FGHAZ) showed only martensitic transformations with transformation temperatures below 400 °C. The steel exhibited an inhomogeneous hardness with hardening in the CGHAZ and FGHAZ and softening in the intercritical and subcritical HAZ. The physically simulated microstructure was validated by a real hybrid laser-arc weld microstructure. KW - Dilatometry KW - High-strength steels KW - CCT diagrams KW - Heat-affected zone PY - 2018 DO - https://doi.org/10.1007/s40194-017-0511-4 SN - 0043-2288 SN - 1878-6669 VL - 62 IS - 1 SP - 47 EP - 54 PB - Springer AN - OPUS4-44716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mishurova, Tatiana A1 - Cabeza, Sandra A1 - Thiede, Tobias A1 - Nadammal, Naresh A1 - Kromm, Arne A1 - Klaus, Manuela A1 - Genzel, Christoph A1 - Haberland, Christoph A1 - Bruno, Giovanni T1 - The influence of the support structure on residual stress and distortion in SLM Inconel 718 parts N2 - The effect of support structure and of removal from the base plate on the residual stress state in selective laser melted IN718 parts was studied by means of synchrotron X-ray diffraction. The residual stresses in subsurface region of two elongated prisms in as-built condition and after removal from the base plate were determined. One sample was directly built on a base plate and another one on a support structure. Also, the distortion on the top surface due to stress release was measured by contact profilometry. High tensile residual stress values were found, with pronounced stress gradient along the hatching direction. In the sample on support, stress redistribution took place after removal from the base plate, as opposed to simple stress relaxation for the sample without support. The sample on support structure showed larger distortion compared to sample without support. We conclude that the use of a support decreases stress values but stress-relieving heat treatments are still needed. KW - Additive manufacturing KW - SLM KW - Residual stress KW - Synchrotron X-ray diffraction KW - IN718 PY - 2018 DO - https://doi.org/10.1007/s11661-018-4653-9 SN - 1073-5623 VL - 49A IS - 7 SP - 3038 EP - 3046 PB - Springer Sciences & Business Media CY - New York, NY AN - OPUS4-45100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hensel, J. A1 - Kromm, Arne A1 - Nitschke-Pagel, T. A1 - Dixneit, Jonny A1 - Dilger, K. T1 - Capability of martensitic low transformation temperature welding consumables for increasing the fatigue strength of high strength steel joints N2 - The use of low transformation temperature (LTT) filler materials represents a smart approach for increasing the fatigue strength of welded high strength steel structures apart from the usual procedures of post weld treatment. The main mechanism is based on the effect of the low start temperature of martensite formation on the stress already present during welding. Thus, compressive residual stress formed due to constrained volume expansion in connection with phase transformation become highly effective. Furthermore, the weld metal has a high hardness that can delay the formation of fatigue cracks but also leads to low toughness. Fundamental investigations on the weldability of an LTT filler material are presented in this work, including the characterization of the weld microstructure, its hardness, phase transformation temperature and mechanical properties. Special attention was applied to avoid imperfections in order to ensure a high weld quality for subsequent fatigue testing. Fatigue tests were conducted on the welded joints of the base materials S355J2 and S960QL using conventional filler materials as a comparison to the LTT filler. Butt joints were used with a variation in the weld type (DY-weld and V-weld). In addition, a component-like specimen (longitudinal stiffener) was investigated where the LTT filler material was applied as an additional layer. The joints were characterized with respect to residual stress, its stability during cyclic loading and microstructure. The results show that the application of LTT consumables leads to a significant increase in fatigue strength when basic design guidelines are followed. This enables a benefit from the lightweight design potential of high-strength steel grades. KW - Low transformation temperature KW - Welding KW - Fatigue strength KW - Residual stress PY - 2020 DO - https://doi.org/10.3139/120.111562 VL - 62 IS - 9 SP - 891 EP - 899 PB - Carl Hanser Verlag AN - OPUS4-51180 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vollert, F. A1 - Thomas, Maximilian A1 - Kromm, Arne A1 - Gibmeier, J. T1 - Solidification Cracking Assessment of LTT Filler Materials by Means of Varestraint Testing and μCT N2 - Investigations of the weldability of metals often deal with hot cracking, as one of the most dreaded imperfections during weld fabrication. The hot cracking investigations presented in this paper were carried out as part of a study on the development of low transformation temperature (LTT) weld filler materials. These alloys allow to mitigate tensile residual stresses that usually arise during welding using conventional weld filler materials. By this means, higher fatigue strength and higher lifetimes of the weld can be achieved. However, LTT weld filler materials are for example, high-alloyed Cr/Ni steels that are susceptible to the formation of hot cracks. To assess hot cracking, we applied the standardized modified varestraint transvarestraint hot cracking test (MVT), which is well appropriate to evaluate different base or filler materials with regard to their hot cracking susceptibility. In order to consider the complete material volume for the assessment of hot cracking, we additionally applied microfocus X-ray computer tomography (μCT). It is shown that by a suitable selection of welding and MVT parameter the analysis of the complete 3D hot crack network can provide additional information with regard to the hot cracking model following Prokhorov. It is now possible to determine easy accessible substitute values (e.g., maximum crack depth) for the extent of the Brittleness Temperature Range (BTR) and the minimum critical strain Pmin. KW - LTT weld filler materials KW - μCT-analysis KW - Hot cracking KW - Varestraint test PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-509126 DO - https://doi.org/10.3390/ma13122726 VL - 13 IS - 12 SP - 2726 PB - MDPI AN - OPUS4-50912 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schasse, R. A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Mente, Tobias T1 - Residual stresses in repair welds of high-strength low-alloy steels N2 - Residual stresses are often the cause for cracks in weld constructions. That is why the residual stress level, induced by manufacturing process, plays a crucial role. The present study aims on the effect of multiple repair weld procedures on a high-strength structural steel S690QL. The widespread technology of carbon arc-air gouging was applied. The weld zone and the heat-affected zone (HAZ) were subjected to multiple thermal cycles by gouging and subsequent repair welding. The investigations were focused on the change of the residuals stresses, the impact on the microstructure and the changes for the mechanical properties of the repair welded joint. The residual stresses were determined by X-ray diffraction. The results have shown a significant dependence for the residual stress levels from the repair cycle. In addition, distinctive changes in microstructures and hence mechanical properties occurred. The fusion line of the repair weld and the adjacent HAZ are the most critical areas. This is where the loss of ductility is most pronounced. KW - Residual stresses KW - High-strength steels KW - Brittle fracture PY - 2015 DO - https://doi.org/10.1007/s40194-015-0257-9 SN - 0043-2288 SN - 1878-6669 VL - 59 IS - 6 SP - 757 EP - 765 PB - Springer CY - Oxford AN - OPUS4-34974 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -