TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Gibmeier, J. A1 - Genzel, C. A1 - Van der Mee, V. T1 - Determination of residual stresses in low transformation temperature (LTT -) welds metals using X-rayand high energy synchrotron radiation N2 - Crack and fatigue resistance are relevant evaluation criteria for welded joints and are decreased by tensile residual stresses resulting from the welding and cooling process, while compressive residual stresses can have a positive influence on the characteristics mentioned. In order to generate compressive residual stresses, a set of post weld treatment procedures is available, like shot peening, hammering, etc. These procedures have the disadvantage that they are time and cost extensive and have to be applied after welding. As another point, such technologies can only produce compressive stresses at the top surface, i.e. can only contribute to the reduction of the risk of cracks initiated at the surface, like fatigue cracks. A chance to generate compressive stresses over the complete weld joint during the welding procedure is offered by the so-called Low Transformation Temperature (LTT -) filler wires. Compared to conventional wires, these materials show lower phase transformation temperatures, which can work against coolingrelated tensile stresses, resulting from respective shrinkage restraint. In consequence, distinct compressive residual stresses can be observed within the weld and adjacent areas. The strength of these fillers makes them potentially applicable to high-strength steel welding. Welds produced with different LTT – filler wires have shown different levels and distributions of the resulting residual stresses depending on the specific transformation temperature. The transformation temperatures are determined by temperature measurement. Classical X-ray diffraction as well as diffraction methods using high energy synchrotron radiation have been used for residual stress analysis. By means of high energy synchrotron diffraction in reflection mode residual stress depth gradients can be determined nondestructively. The phase selective nature of the diffraction measurements enables the simultaneous determination of the phase specific residual stresses of all contributing crystalline phases within one experiment. The application of white beam diffraction implies recording of a multitude of diffraction lines within the energy range of the provided energy spectrum of the white beam. By this means phase specific residual stress depth distributions up to distances of 150 ìm below the surface can be analysed for steel using the energy dispersive set-up of the HMI-beamline EDDI at the Bessy site, Berlin, providing an energy range between 20-150 keV. As a side effect quantitative phase analysis can be carried out using white energy dispersive diffraction e.g. the determination of the content of retained austenite in the weld. KW - Filler materials KW - Low temperature KW - Reference lists KW - Residual stresses KW - Temperature KW - Transformation KW - Synchrotron radiation KW - Phase specific residual stresses KW - Energy dispersive diffraction PY - 2009 SN - 0043-2288 SN - 1878-6669 VL - 53 IS - 1/2 SP - 3 EP - 16 PB - Springer CY - Oxford AN - OPUS4-19214 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Rethmeier, Michael A1 - Gibmeier, J. A1 - Genzel, C. T1 - Residual stresses and in-situ measurement of phase transformation in low transformation temperature (LTT) welding materials PY - 2009 SN - 1097-0002 SN - 0069-8490 SN - 0376-0308 VL - 52 SP - 755 EP - 762 CY - Newtown Square, Pa., USA AN - OPUS4-19817 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Formation of welding residual stresses in low transformation temperature (LTT) materials N2 - For the safety and cost efficiency of welded high-strength steel structures, precise knowledge of the level and distribution of welding- and cooling-specific stresses and residual stresses is essential, since they exert a decisive influence on strength, crack resistance, and finally on the bearable service load. This paper presents innovative filler materials, of which the phase transformation temperature was deliberately adjusted via the chemical composition. The transformation behaviour of these martensitic Low Transformation Temperature (LTT-) filler materials shows direct effects on the local residual stresses in the weld and the HAZ. These effects can purposefully be exploited to counteract the thermally induced shrinkage of the material and to produce significant compressive residual stresses in the weld. Comparative welding experiments were carried out on 690 MPa high-strength base materials using various LTT-filler materials. High energy synchrotron radiation was used for residual stress measurement. Particularly the use of high energy synchrotron radiation makes it possible to detect the residual stress condition fast without destruction of material. Thereby, residual stress depth gradients can be determined simultaneously without removing material. In steel, gradients of up to 150 µm can be resolved in such a way. Furthermore, the application of high energy radiation permits determination of residual stresses of any available residual austenite contents. Results show significant dependence of transformation temperatures on the resulting residual stress level and distribution. KW - Phase specific residual stresses KW - Phase transformation KW - Low transformation temperature filler wire KW - Energy dispersive diffraction KW - High strength steel PY - 2009 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-205909 DO - https://doi.org/10.1590/S0104-92242009000100009 SN - 0104-9224 SN - 1980-6973 VL - 14 IS - 1 SP - 74 EP - 81 PB - Associação Brasileira de Soldagem, ABS CY - Rio de Janeiro AN - OPUS4-20590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - In-situ-phase analysis using synchrotron radiation of low transformation temperature (LTT) welding material N2 - Cold cracking resistance is a relevant evaluation criterion for welded joints and affected by residual stresses which result from the welding procedure. Compressive residual stresses can thereby have a positive influence on preventing cracking. A unique possibility of generating compressive residual stresses already during the welding procedure is offered by the so-called Low Transformation Temperature (LTT) filler wires. Compared to conventional wires, these materials show decreased phase transformation temperatures which can work against the cooling-specific contraction. In consequence, distinct compressive residual stresses can be observed within the weld and adjacent areas. The strength of these fillers makes them potentially applicable to high-strength steel welding. Investigations were carried out to determine the phase transformation behaviour of different LTT-filler materials. Transformation temperatures were identified using Single Sensor Differential Thermal Analysis (SS-DTA). Additionally Synchrotron radiation was used to measure the transformation kinetics of all involved crystalline phases during heating and cooling of a simulated weld thermal cycle. KW - In-situ phase analysis KW - Energy dispersive diffraction KW - Phase transformation KW - Low Transformation Temperature filler wire PY - 2009 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-205922 DO - https://doi.org/10.1590/S0104-92242009000100010 SN - 0104-9224 SN - 1980-6973 VL - 14 IS - 1 SP - 82 EP - 88 PB - Associação Brasileira de Soldagem, ABS CY - Rio de Janeiro AN - OPUS4-20592 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - In situ phase characterization of low transformation temperature (LTT) alloy by means of synchrotron diffraction N2 - Cold cracking resistance is a relevant evaluation criterion for welded joints and affected by residual stresses which result from the welding procedure. Compressive residual stresses can thereby have a positive influence on preventing cracking. A unique possibility of generating compressive residual stresses already during the welding procedure is offered by the socalled Low Transformation Temperature (LTT) filler wires. Compared to conventional wires, these materials show decreased phase transformation temperatures which can work against the cooling-specific contraction. In consequence, distinct compressive residual stresses can be observed within the weld and adjacent areas. The strength of these fillers makes them potentially applicable to high-strength steel welding. Investigations were carried out to determine the phase transformation behaviour of different LTT-filler materials. Transformation temperatures were identified using Single Sensor Differential Thermal Analysis (SS-DTA). Additionally Synchrotron radiation was used to measure the transformation kinetics of all involved crystalline phases during heating and cooling of a simulated weld thermal cycle. KW - In-situ phase analysis KW - Energy dispersive diffraction KW - Phase transformation PY - 2010 SN - 1684-579X VL - 5 IS - 158 SP - 17 EP - 23 PB - Izdat. Masinostroenie CY - Moskva, Russia AN - OPUS4-21829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Gibmeier, J. T1 - In-situ observation of phase transformations during welding of low transformation temperature filler material KW - LTT filler material KW - In-situ observation KW - Energy dispersive diffraction KW - Transformation temperature KW - Residual stress PY - 2010 DO - https://doi.org/10.4028/www.scientific.net/MSF.638-642.3769 SN - 0255-5476 VL - 638-642 SP - 3769 EP - 3774 PB - Trans Tech Publications CY - Aedermannsdorf, Switzerland AN - OPUS4-20725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Gibmeier, J. A1 - Rethmeier, Michael T1 - In-situ-Analyse der Phasenumwandlungskinetik während des Schweißens N2 - Zugeigenspannungen, wie sie beim Schweißprozess durch inhomogene Temperaturverteilungen und Schrumpfungen hervorgerufen werden, können die Lebensdauer geschweißter Verbindungen signifikant herabsetzen. Eine neue und außerordentlich attraktive Methode, um Druckeigenspannungen bereits während des Schweißens gezielt einzustellen, gelingt mit sogenannten LTT (Low Transformation Temperature)-Legierungen. LTT-Legierungen weisen eine martensitische Phasenumwandlung bei relativ niedrigen Temperaturen auf, wobei die damit verbundene Volumenexpansion zu einer Reduktion der Schrumpfeigenspannungen bzw. Erzeugung von Druckeigenspannungen führt. Zum direkten Nachweis der Phasenumwandlungen und der damit verbundenen resultierenden Schweißeigenspannungen wurden erstmals In-situ-Schweißexperimente unter Nutzung hoch energetischer, polychromatischer Synchrotronstrahlung (Weißstrahl) realisiert, um die Umwandlungskinetik während eines realen Schweißprozesses und die daraus resultierenden Schweißeigenspannungen zu analysieren. Es wird gezeigt, dass mit LTT-Legierungen signifikante Druckeigenspannungen in der Schweißnaht erreicht werden. PY - 2010 SN - 0025-5300 VL - 52 IS - 4 SP - 204 EP - 210 PB - Hanser CY - München AN - OPUS4-21219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brauser, Stephan A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Rethmeier, Michael T1 - In-situ synchrotron diffraction and digital image correlation technique for characterizations of retained austenite stability in low-alloyed transformation induced plasticity steel N2 - Direct measurement and quantification of phase transformation in a low-alloyed transformation induced plasticity steels depending on the tensile load as well as determination of the real true stress and true strain values were carried out in-situ using high energy synchrotron radiation. Digital image correlation technique was used to quantify more precisely the true strain values. The aim of the work was to obtain a better understanding of the phase transformation of commercial low-alloyed transformation induced plasticity steel depending on the true strain and true stress values. KW - Transformation induced plasticity KW - In-situ synchrotron diffraction KW - Austenite stability KW - Digital image correlation PY - 2010 DO - https://doi.org/10.1016/j.scriptamat.2010.08.007 SN - 1359-6462 SN - 1872-8456 VL - 63 IS - 12 SP - 1149 EP - 1152 PB - Elsevier CY - Oxford AN - OPUS4-22164 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Altenkirch, J. A1 - Gibmeier, J. A1 - Kostov, V. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Doyle, S. A1 - Wanner, A. T1 - Time- and temperature-resolved synchrotron X-ray diffraction: observation of phase transformation and strain evolution in novel low temperature transformation weld filler materials N2 - Solid-state phase transformations and the evolution of thermal and elastic strains in novel low temperature transformation (LTT) weld filler materials in the near surface region are monitored in real time by means of an innovative experimental set-up at the PDIFF (powder diffraction) beamline at the synchrotron light source ANKA (Angströmquelle Karlsruhe) at the KIT (Karlsruhe Institute for Technology). The key components of the diffraction set-up are two fast microstrip line detectors, which enables the strain evolution to be followed as a function of time and temperature for a 0.5?s counting time. During controlled heating and cooling cycles, as well as during near welding cycles, the martensite–austenite–martensite phase transitions are analysed. The transformation kinetics are monitored during resistance heating of small chips of the pure LTT alloys and during gas tungsten arc welding of simplified LTT welds using a specially designed welding rig for in-situ studies on the diffraction instruments. Under the mechanically unconstrained condition allowing free thermal expansion and shrinkage, the LTT alloys are found to exhibit decreasing transformation temperatures Ac and MS and increasing phase fraction of retained austenite for increasing Ni content. The strain evolution during welding reveals increased compressive stresses upon welding, which is attributed to the martensite formation upon cooling, which counteracts the thermal contraction strains. Comparison of the transformation temperatures reveals higher values than in the pure LTT alloys, but no variation between the different alloys. On the one hand, this is attributed to preferred grain orientation affecting the diffraction measurements and the determination of the transformation temperatures. On the other hand, it is possible that with the different chemical compositions of the LTT alloys and the mechanical constraints during welding, the evolution of the residual strain and stress may vary and result in counteracting affects with respect to lowered martensite start temperatures. KW - In-situ synchrotron X-ray diffraction KW - Low temperature transformation KW - Welding PY - 2011 DO - https://doi.org/10.1177/0309324711413190 SN - 0309-3247 SN - 2041-3130 VL - 46 IS - 7 SP - 563 EP - 579 PB - Sage CY - London AN - OPUS4-24683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brauser, Stephan A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Rethmeier, Michael T1 - In-situ analysis of solid state phase transformation in TRIP-aided steels by synchrotron diffraction N2 - Energy dispersive synchrotron diffraction (EDXRD) analysis and 3 dimensional digital image correlations were conducted to investigate the stress and strain effected transformation behavior during tensile loading of low alloyed TRansformation Induced Plasticity (TRIP) steel. This technique allowed for phase specific stress measurement during certain tensile load steps in the elastic and also plastic regime. Additionally the simultaneous determination of the load dependent phase content was realized. The results show that the martensite transformation starts only after exceeding the overall yield point and is finished before reaching the uniform elongation, whereas a large portion of the austenite remains unchanged in the structure. Furthermore, the martensite transformation related to the stress in the γ-phase and α-phase was analyzed and quantified. KW - Synchrotron KW - EDXRD KW - Phase transformation KW - TRIP steel KW - Digital image correlation KW - Residual stress PY - 2011 UR - https://www.jstage.jst.go.jp/article/qjjws/29/3/29_3_81s/_pdf DO - https://doi.org/10.2207/qjjws.29.81s SN - 0288-4771 VL - 29 IS - 3 SP - 81 EP - 85 CY - Tokyo, Japan AN - OPUS4-24693 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -