TY - JOUR A1 - Santandrea, A. A1 - Vignes, A. A1 - Krietsch, Arne A1 - Brunello, D. A1 - Perrin, L. A1 - Laurent, A. A1 - Dufaud, O. T1 - Evaluating the explosion severity of nanopowders: International standards versus reality N2 - The maximum explosion overpressure and the maximum rate of pressure rise, which characterize thedust explosion severity, are commonly measured in apparatuses and under specific conditions defined byinternational standards. However, those standards conditions, designed for micropowders, may not befully adapted to nanoparticles. Investigations were conducted on different nanopowders (nanocellulose,carbon black, aluminum) to illustrate their specific behaviors and highlight the potential inadequacyof the standards. The influence of the sample preparation was explored. Various testing procedureswere compared, focusing on the dust cloud turbulence and homogeneity. Dust dispersion experimentsevidenced the importance of the characterization of the dust cloud after dispersion, due to the frag-mentation of agglomerates, using metrics relevant with nanoparticles reactivity (e.g. surface diameterinstead of volume diameter). Moreover, the overdriving phenomenon (when the experimental resultsbecome dependent of the ignition energy), already identified for micropowders, can be exacerbated fornanoparticles due to their low minimum ignition energy and to the high energy used under standardconditions. It was evidenced that for highly sensitive nanopowders, pre-ignition phenomenon can occur.Finally, during severe explosions and due to a too long opening delay of the ‘fast acting valve’, the flamecan go back to the dust container. KW - Dust explosions KW - Gas explosions KW - Minimum ignition temperature KW - Hybrid mixtures PY - 2020 DO - https://doi.org/10.1016/j.psep.2020.04.011 VL - 138 SP - 279 EP - 291 PB - Elsevier B.V. AN - OPUS4-50944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krietsch, Arne T1 - Nanoskalig hergestellte Materialien - Neueste Erkenntnisse T2 - 12. Fachtagung Anlagen-, Arbeits- und Umweltsicherheit CY - Köthen DA - 2015-11-05 PY - 2015 AN - OPUS4-34788 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krietsch, Arne T1 - Brand- und Explosionsgefahren von nanoskaligen Metallstäuben T2 - Jahrestreffen der ProcessNet-Fachgruppe "Agglomerations- und Schüttguttechnik" mit Beteiligung der Fachgemeinschaft "Anlagen- und Prozesssicherheit" CY - Magdeburg, Germany DA - 2014-03-10 PY - 2014 AN - OPUS4-30445 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Dörfel, Ilona A1 - Steinborn, Gabriele A1 - Langner, Jeanette A1 - Krietsch, Arne A1 - Seeger, Stefan A1 - Österle, Werner A1 - Schmidt, Martin A1 - Bresch, Harald T1 - Dossier on titanium dioxide - Part 1/1 - NM 105 N2 - In November 2007, OECD’s Working Party on Manufactured Nanomaterials (WPMN) launched the Sponsorship Programme for the Testing of Manufactured Nanomaterials (hereafter the Testing Programme). The objective was to conduct specific tests, relevant to human health and environmental safety endpoints, on a variety of manufactured nanomaterials (MN). The outcomes of the Testing Programme were intended to assess the applicability of the existing test guidelines1 to nanomaterials, as well as to provide useful information on any intrinsic properties of MNs, which are different from the same bulk material with greater external dimensions. Understanding the properties of NMs is crucial to choose appropriate strategies for hazard identification, risk assessment or risk management measures. The Testing Programme involved delegations from OECD member countries, some non-member economies and other stakeholders. The broad international representation, from a range of delegations enabled the programme to pool expertise and resources without which this programme would not have been possible. KW - Nanomaterial KW - Nanoparticle KW - Sponsorship programme KW - Nano characterization PY - 2015 UR - http://www.oecd.org/env/ehs/nanosafety/dossier-on-silver-nanoparticles-part1-1.htm IS - 54 SP - 27 CY - Paris AN - OPUS4-35430 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhao, P. A1 - Schmidt, Martin A1 - Krause, U. A1 - Duan, Q. A1 - Krietsch, Arne A1 - Wu, Dejian T1 - Experimental study on the minimum explosion concentration of anthracite dust: The roles of O2 mole fraction, inert gas and CH4 addition N2 - The explosion characteristics of anthracite coal dust with/without small amount of CH4 (1.14 vol %) were investigated by using a 20 L spherical explosion apparatus with an emphasis on the roles of oxygen mole fraction and inert gas. Two methods based on overpressure and combustion duration time were used to determine the minimum explosion concentration (MEC) or the lower explosion limit (LEL) of the pure anthracite coal dust and the hybrid coal-methane mixtures, respectively. The experiment results showed that increasing oxygen mole fraction increases the explosion risk of coal dust: with increasing oxygen mole fraction, the explosion pressure (Pex) and the rate of explosion pressure rise ((dp/dt)ex)) increase, while MEC decreases. The explosion risk of anthracite dust was found to be lower after replacing N2 with CO2, suggesting that CO2 has a better inhibition effect on explosion mainly due to its higher specific heat. However, the addition of 1.14% CH4 moderates the inhibition effect of CO2 and the promotion effect of O2 on anthracite dust explosion for some extent, increasing explosion severity and reducing the MEC of anthracite dust. For hybrid anthracite/CH4 mixture explosions, Barknecht’s curve was found to be more accurate and conservative than Chatelier’s line, but neither are sufficient from the safety considerations. The experimental results provide a certain help for the explosion prevention and suppression in carbonaceous dust industries. KW - Lower explosion limit KW - Minimun explosion concentration KW - Explosion charasteristics KW - Hybrid mixture KW - Explosion regimes PY - 2021 DO - https://doi.org/10.1016/j.jlp.2021.104490 VL - 2021 SP - 1 EP - 10 PB - Elsevier Ltd. ET - 71 AN - OPUS4-54074 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krietsch, Arne A1 - Reyes Rodriguez, M. A1 - Kristen, A. A1 - Kadoke, D. A1 - Abbas, Z. A1 - Krause, U. T1 - Ignition temperatures and flame velocities of metallic nanomaterials N2 - The production of materials with dimensions in the nanometre range has continued to increase in recent years. In order to ensure safety when handling these products, the hazard potential of such innovative materials must be known. While several studies have already investigated the effects of explosions (such as maximum explosion pressure and maximum pressure rise) of powders with primary particles in the nanometre range, little is known about the ignition temperatures and flame velocities. Therefore, the minimum ignition temperature (MIT) of metallic nano powders (aluminium, iron, copper and zinc) was determined experimentally in a so called Godbert-Greenwald (GG) oven. Furthermore, the flame velocities were determined in a vertical tube. In order to better classify the test results, the tested samples were characterised in detail and the lower explosion limits of the tested dust samples were determined. Values for the burning velocity of aluminium nano powders are higher compared to values of micrometre powd ers (from literature). While MIT of nanometre aluminium powders is within the range of micrometre samples, MIT of zinc and copper nano powders is lower than values reported in literature for respective micrometre samples. KW - Dust explosions KW - Nanomaterial KW - Flame propagation KW - Minimum ignition temperature PY - 2021 DO - https://doi.org/10.1016/j.jlp.2021.104482 SN - 0950-4230 VL - 2021 IS - 71 SP - 1 EP - 9 PB - Elsevier Ltd. AN - OPUS4-54076 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Abbas, Z. A1 - Gabel, D. A1 - Krietsch, Arne A1 - Krause, U. T1 - Quasi-static dispersion of dusts for the determination of lower explosion limits of hybrid mixtures N2 - Knowledge of explosion limiting concentration of explosible materials is necessary forthe design of explosion protection measures. Currently employed methods of testing MEC of a dust cloud or LEL of a hybrid mixture are based on arbitrary assumptionsand possess technical limitations that often lead to values of MEC/LEL, which are unrealistically low or poorly reproducible. This contribution presents an improved method for experimental determination of MEC of a combustible dust cloud or LEL of a flammable gas or hybrid mixture. The new setup operates under laminar conditions and allows a uniform suspension of dust particles in an open top acrylic glass tube. Dust concentration is measured with the help of infrared sensors installed a few centimeters above and below the ignition source. In order to evaluate the dependence of MEC on flow front velocity, MEC of lycopodium was determined at four flow velocities. The results show that the flow field intensity does not significantly influence the MEC of lycopodium for the flow ranges tested in this work. Moreover, LEL of hybrid mixtures of lycopodium and methane was also tested at flow velocities of 4.7 cm/s, 5.8 cm/s, 7 cm/s and 11 cm/s and compared with the values obtained from other sources. The results suggest that the requirement of high energy pyrotechnical igniter may be relinquished, provided that a truly homogeneous suspension of dust particles could be achieved. Moreover, the effect of relative amount of dust and gas, on the course of ignition and flame propagation in hybrid mixtures at their LEL, was studied by the help of high speed videos. For hybrid mixtures of carbonaceous dusts (like lycopodium) at their LEL, ignition occurs in the gas phase, however, flame propagation is only possible through a two-way interaction of dust and gas during the course of combustion. KW - Dust explosions KW - Gas explosions KW - Lower explosion limit KW - Hybrid mixtures PY - 2022 DO - https://doi.org/10.1016/j.jlp.2021.104640 SN - 0950-4230 VL - 74 SP - 1 EP - 18 PB - Elsevier Ltd. AN - OPUS4-54077 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krietsch, Arne A1 - Reyes Rodriguez, M. A1 - Kristen, A. A1 - Kadoke, D. A1 - Abbas, Z. A1 - Krause, U. T1 - Ignition temperatures and flame velocities of metallic nanomaterials N2 - The production of materials with dimensions in the nanometre range has continued to increase in recent years. In order to ensure safety when handling these products, the hazard potential of such innovative materials must be known. While several studies have already investigated the effects of explosions (such as maximum explosion pressure and maximum pressure rise) of powders with primary particles in the nanometre range, little is known about the ignition temperatures and flame velocities. Therefore, the minimum ignition temperature (MIT) of metallic nano powders (aluminium, iron, copper and zinc) was determined experimentally in a so called Godbert-Greenwald (GG) oven. Furthermore, the flame velocities were determined in a vertical tube. In order to better classify the test results, the tested samples were characterised in detail and the lower explosion limits of the tested dust samples were determined. Values for the burning velocity of aluminium nano powders are higher compared to values of micrometre powders (from literature). While MIT of nanometre aluminium powders is within the range of micrometre samples, MIT of zinc and copper nano powders is lower than values reported in literature for respective micrometre samples. T2 - 13th Symposium International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions (ISHPMIE) CY - Online meeting DA - 27.07.2021 KW - Dust explosions KW - Nanomaterial KW - Flame propagation KW - Minimum ignition temperature PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-540930 DO - https://doi.org/10.7795/810.20200724 SP - 591 EP - 605 PB - Physikalisch-Technische Bundesanstalt AN - OPUS4-54093 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krietsch, Arne A1 - Krause, U. A1 - Gabel, D. A1 - Abbas, Z. A1 - Dufaud, O. T1 - Quasi-static dispersion of dusts for the determination of lower explosion limits of hybrid mixtures N2 - Knowledge of explosion limiting concentration of explosible materials is necessary for the design of explosion protection measures. Currently employed methods of testing MEC of a dust cloud or LEL of a hybrid mixture are based on arbitrary assumptions and possess technical limitations that often lead to values of MEC/LEL, which are unrealistically low or poorly reproducible. This contribution presents an improved method for experimental determination of MEC of a combustible dust cloud or LEL of a flammable gas or hybrid mixture. The new set-up operates under laminar conditions and allows a uniform suspension of dust particles in an open top acrylic glass tube. Dust concentration is measured with the help of infrared sensors installed a few centimeters above and below the ignition source. In order to evaluate the dependence of MEC on flow front velocity, MEC of lycopodium was determined at four flow velocities. The results show that the flow field intensity does not significantly influence the MEC of lycopodium for the flow ranges tested in this work. Moreover, LEL of hybrid mixtures of lycopodium and methane was also tested at flow velocities of 4.7 cm/s, 5.8 cm/s, 7 cm/s and 11 cm/s and compared with the values obtained from other sources. The results suggest that the requirement of high energy pyrotechnical igniter may be relinquished, provided that a truly homogeneous suspension of dust particles could be achieved. Moreover, the effect of relative amount of dust and gas, on the course of ignition and flame propagation in hybrid mixtures at their LEL, was studied by the help of high speed videos. For hybrid mixtures of carbonaceous dusts (like lycopodium) at their LEL, ignition occurs in the gas phase, however, flame propagation is only possible through a two-way interaction of dust and gas during the course of combustion. T2 - 13th Symposium International Symposium on Hazards, Prevention and Mitigation of Industrial Explosions (ISHPMIE) CY - Online meeting DA - 27.07.2020 KW - Dust explosions KW - Gas explosions KW - Lower explosion limit KW - Hybrid mixtures PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-540955 DO - https://doi.org/10.7795/810.20200724 SP - 750 EP - 764 PB - Physikalisch-Technische Bundesanstalt AN - OPUS4-54095 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Su, Bin A1 - Luo, Zhenmin A1 - Krietsch, Arne A1 - Wu, Dejian A1 - Wang, Tao A1 - Zhou, Shangyong A1 - Deng, Jun T1 - Quantitative investigation of explosion behavior and spectral radiant characteristics of free radicals for syngas/air mixtures N2 - The combustion characteristics and explosive hazard of syngas (H2/CO)/air mixtures are affected by its exact composition and equivalence ratios. In this paper, the explosion pressure and spectral radiant intensity of free radicals were quantitatively examined for syngas with different H2 proportions ([H2 in syngas] = 0, 30, 50, 70, 100 vol%) and equivalence ratios (φ = 0.8, 1.0, 1.2, 1.4, 1.6, 2.0, 2.5). The results show that the explosion process of syngas/air mixtures can be separated into the initial slow combustion stage, the violent deflagration stage and the deflagration ending stage. The peaks of explosion pressure, pressure rise rate, OH*spectral intensity and rise rate of spectral intensity first increase and then decrease with increasing the equivalence ratio, and they reduce gradually with the decrease of H2 proportion in syngas. The H2 content in syngas greatly affects the heat release and the concentration of excited state OH*, especially for the syngas/air mixtures with smaller proportion of H2. Additionally, the presence of H2 greatly increases the deflagration index and spectral radiant index of OH* for syngas/air mixtures. The average rise rates of explosion pressure and spectral intensity of free radicals are introduced and the coupling model between them is established based on the first law of thermodynamics and the principle of chain reaction. The established model is furthermore verified by the experimental results. It is indicated that there is a linear relationship between average rise rates of explosion pressure and spectral intensity (OH*). The results can be used to improve the combustion efficiency of syngas and to guide theoretically the prevention, mitigation and control of syngas explosions. KW - Syngas KW - Hydrogen KW - Explosion pressure KW - Free radicals KW - Spectral intensity PY - 2024 DO - https://doi.org/10.1016/j.ijhydene.2023.10.280 SN - 0360-3199 VL - 50 IS - Part A SP - 1359 EP - 1368 PB - Elsevier Ltd. AN - OPUS4-59482 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -