TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen A1 - Meyer, A. T1 - About Polycondensation, Disproportionation, and Cyclization of Acetylated Poly(L-Lactide) Esters N2 - L-lactide (LA) is polymerized with ethyl L-lactate or trifluoroethanol as initiators (LA/In = 30/1), and the resulting poly(L-lactide) esters are acetylated with acetic anhydride. The acetylated PLA esters are mixed with SnOct2, dibutyltin bis(4-chlorophenoxide), or dibutyltin bis(pentafluorophenoxide) in solution and crystallized at 120 °C. The doped crystals are annealed at 140 °C or at 160 °C for 7, 14, and 28 days, and the chemical modifications that occurred in the solid state are monitored by matrix-assisted laser desorption/ionization time-of-flight (MALDI TOF) mass spectrometry, gel permeation chromatography (GPC), and differential scanning calorimetry (DSC) measurements. All catalysts promoted polycondensation, while no significant formation of cycles is observed. However, in the presence of SnOct2, disproportionation of chains occurred upon annealing at 120 or 140 °C, and crystallites consisting of extended chains with Mn values ≈3500 – 3600 and low dispersities (Ð < 1.5) are formed. KW - MALDI-TOF MS KW - Polycondensation KW - Polylactides KW - Transesterifcation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630349 DO - https://doi.org/10.1002/macp.202400175 SN - 1521-3935 VL - 225 IS - 19 PB - Wiley VHC-Verlag AN - OPUS4-63034 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen T1 - Ring-ring equilibration (RRE) of cyclic poly(L-lactide)s by means of cyclic tin catalysts N2 - With 2,2-dibutyl-2-stanna-1,3-dithiolane (DSTL) and 2-stanna-1,3-dioxa-4,5,6,7-dibenzoxepane (SnBiPh) as catalysts ring-expansion polymerizations (REP) were performed either in 2 M solution using three different solvents and two different temperatures or in bulk at 140 and 120 ◦C. A kinetically controlled rapid REP up to weight average molecular masses (Mẃs) above 300 000 was followed by a slower degradation of the molecular masses at 140 ◦C, but not at 120 ◦C Furthermore, a low molecular mass cyclic poly(L-lactide) (cPLA) with a Mn around 16 000 was prepared by polymerization in dilute solution and used as starting material for ring-ring equilibration at 140 ◦C in 2 M solutions. Again, a decrease of the molecular mass was detectable, suggesting that the equilibrium Mn is below 5 000. The degradation of the molecular masses via RRE was surprisingly more effective in solid cyclic PLA than in solution, and a specific transesterification mechanism involving loops on the surface of crystallites is proposed. This degradation favored the formation of extended-ring crystallites, which were detectable by a “saw-tooth pattern” in their MALDI mass spectra. KW - Organic Chemistry KW - Polymers and Plastics KW - MALDI-TOF MS KW - Materials Chemistry PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-593819 DO - https://doi.org/10.1016/j.eurpolymj.2024.112765 SN - 0014-3057 VL - 206 SP - 1 EP - 8 PB - Elsevier B.V. AN - OPUS4-59381 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -