TY - JOUR A1 - Yevtushenko, Oleksandra A1 - Bettge, Dirk A1 - Bohraus, Stefan A1 - Bäßler, Ralph A1 - Pfennig, A. A1 - Kranzmann, Axel T1 - Corrosion behavior of steels for CO2 injection JF - Process safety and environmental protection N2 - The process chain for Carbon Capture and Sequestration (CCS) includes tubing for injection of CO2 into saline aquifers. The compressed CO2 is likely to contain specific impurities; small concentrations of SO2 and NO2 in combination with oxygen and humidity are most harmful. In addition, CO2 saturated brine is supposed to rise in the well when the injection process is interrupted. The material selection has to ensure that neither CO2 nor brine or a combination of both will leak out of the inner tubing. In this comprehensive paper the investigated materials range from low-alloy steels and 13% Cr steels up to high-alloy materials. Electrochemical tests as well as long term exposure tests were performed in CO2, in brine and combination of both; pressure was up to 100 bar, temperature up to 60 °C. Whereas the CO2 stream itself can be handled using low alloy steels, combinations of CO2 and brine require more resistant materials to control the strong tendency to pitting corrosion. The corrosion behavior of heat-treated steels depends on factors such as microstructure and carbon content. For different sections of the injection tube, appropriate materials should be used to guarantee safety and consider cost effectiveness. KW - CCS KW - Injection tubing KW - Corrosion KW - Safety KW - Carbon steel KW - High alloy steel KW - Saline fluid KW - Supercritical CO2 PY - 2014 DO - https://doi.org/10.1016/j.psep.2013.07.002 SN - 0957-5820 SN - 1744-3598 VL - 92 IS - 1 SP - 108 EP - 118 PB - Elsevier CY - Amsterdam AN - OPUS4-28966 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Ruhl, Aki Sebastian A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Kranzmann, Axel T1 - Corrosion aspects of materials selection for CO2 transport and storage T2 - 2nd ICEPE International conference on energy process engineering - Efficient carbon capture for coal power plants N2 - The geological storage of carbon dioxide (Carbon Capture and Storage, CCS) in depleted gas reservoirs or in saline aquifers is a widely discussed issue. Carbon dioxide may induce corrosion on the piping steels during compression, transportation and injection. Therefore, selection of appropriate piping steels is a key factor in order to increase the safety and reliability of the CCS technology, and to keep the processes cost-effective. The here described subproject of the COORAL project (German acronym for “C02 purity for capture and storage”) deals with the levels of impurities in the C02 stream that will be acceptable when using specific steels. Material exposure to carbon dioxide (C02) containing specific amounts of water vapor, oxygen (02) sulfur dioxide (S02), nitrogen dioxide (N02), carbon monoxide (CO) can be a challenge to steels. Within this subproject 13 different Steels are tested for suitability as materials used for compression, transportation and injection Units within the CCS chain. T2 - 2nd ICEPE International conference on energy process engineering - Efficient carbon capture for coal power plants CY - Frankfurt/M., Germany DA - 20.06.2011 KW - Carbon capture KW - CCS KW - Corrosion PY - 2011 SP - 76 EP - 78 AN - OPUS4-24250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Kranzmann, Axel A1 - Bäßler, Ralph T1 - Korrosion von Stählen in überkritischem CO2 unter realitätsnahen Bedingungen T2 - Kraftwerkstechnik 2015 N2 - Kohlendioxid (C02), das z.B. aus dem Abgas von fossilgefeuerten Kraftwerken, Stahlwerken oder Zementwerken abgetrennt wird, enthält Verunreinigungen. Dies sind beispielsweise Wasserdampf, 02, S0X, NOx und H2S. Derartige Gasmischungen sind instabil und ihre Komponenten können zu weiteren Produkten reagieren. Wenn Wassermoleküle zur Verfügung stehen, können saure Lösungen kondensieren. Die Korrosion von Werkstoffen und Bauteilen in Kontakt mit den transportierten Gasmischungen wird an der BAM in Laborversuchen untersucht, Das wichtigste Ziel ist, sichere und bezahlbare Kombinationen von zugelassenen Konstruktionswerkstoffen und Grenzwerten für Verunreinigungen im C02-Strom vorzuschlagen. In den bisherigen Arbeiten hat sich herausgestellt, dass für eine verlässliche Aussage die Experimente möglichst realitätsnah durchgeführt werden sollten. Hierfür müssen die Parameter: hoher Druck (um 100 bar), Temperatur (um 60 °C), Strömungsverhältnisse (laminar oder turbulent) sowie mechanische Spannung kombiniert werden. Für diese Anforderungen wurden Prüfstände entwickelt und Experimente durchgeführt. T2 - 47. Kraftwerktechnisches Kolloquium CY - Dresden, Germany DA - 13.10.2015 KW - Hochtemperaturkorrosion KW - CCS KW - Kraftwerkstechnik PY - 2015 SN - 978-3-934409-70-5 SP - 959 EP - 970 PB - SAXONIA CY - Freiberg AN - OPUS4-35038 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kratzig, Andreas A1 - Le, Quynh Hoa A1 - Bettge, Dirk A1 - Bäßler, Ralph A1 - Kranzmann, Axel ED - EUROCORR, T1 - Interaction of oxidizing and reductive components in CO2 fluids in transport pipelines at low and high pressure and low temperature T2 - EUROCORR 2017 N2 - Carbon Capture Utilization and Storage (CCUS) is a promising technology for the reduction of CO2 emissions, e.g. from fossil-fuel operated power plants or cement mills. Crucial points for a sustainable and future-proof CCUS procedure are reliability and cost efficiency of the pipeline transport network. Due to the absence of certified benchmarks for upper limits, systematic experiments with impurities in the CO2 stream were carried out. For oxidation processes SO2 and NO2 acted as corrosive components, and for reductive atmosphere H2S. Carbon steel L485MB (pipeline), martensitic steel 1.4313 (compression) and austenitic steel 1.4562 (injection) were selected as specimens. Experiments were performed at 0 bar or 100 bar and within a temperature range 278 K ≤ T ≤ 313 K. High-alloyed Cr-Ni steels revealed no corrosion (1.4562, 1.4313), while for carbon steel considerable corrosion was observed. The type and intensity of corrosion was strongly coupled with the applied corrosive species and the level of humidity in the CO2 stream, leading to different compositions of acidic condensates. Applying a reducing atmosphere results in very little corrosion rates, but provokes pitting corrosion. In contrast, oxidizing or mixed settings lead to a clearly increased growth of the corrosion layer, but exhibit shallow uniform corrosion. Exceptional nitric acid results in intergranular corrosion. Investigations on the specimens were carried out by optical microscopy, XRD, SEM/EDX, and AAS/IC. T2 - EUROCORR 2017 CY - Prague, Czech Republic DA - 03.09.2017 KW - CCS KW - Pipeline transport KW - CO2 corrosion KW - Carbon steels KW - Condensation PY - 2017 SP - Paper 80181, 1 EP - 4 AN - OPUS4-41918 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kratzig, Andreas A1 - Bettge, Dirk A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Kranzmann, Axel T1 - Interaction of Oxidizing and Reductive Components in CO2 Streams with Transport Pipeline Steel X70 at High Pressure and Low Temperature T2 - 14th Greenhouse Gas Control Technologies Conference Melbourne 21-26 October 2018 (GHGT-14) N2 - Specific amounts of oxidizing and reductive impurities as well as some moisture were added to dense phase CO2 to replicate CO2 streams from sources in a CCS pipeline network. Due to the moisture content being only 50 ppmV no visible acid condensation took place. To simulate stress conditions at the inside pipeline surface due to fluid pressure (10 MPa) specimens were preloaded using a load frame. Experiments conducted at 278 K and at 313 K revealed the highest corrosion rate at lower temperature. Corrosive effect of impurities was strongest applying mixed atmosphere, containing oxidizing and reductive components, closely followed by CO2 streams with pure oxidizing character. By far, the lowest corrosion rate (10x lower) resulted from reductive atmosphere. In general, at constant temperature and pressure the CO2 stream composition strongly influences the morphology, thickness and composition of the corrosion products. Applying oxidizing or mixed impurities, iron hydroxides or oxides (e.g. goethite, hematite) occur as dominating corrosion products, capable to incorporate different amounts of sulfur. In contrast, using reductive atmosphere very thin corrosion layers with low crystallinity were developed, and phase identification by XRD was unfeasible. SEM/EDX analysis revealed the formation of Fe-O compounds, most likely attributed to the oxygen partial pressure in the system induced by CO2 (≥0.985 volume fraction) and volatile H2O. In addition to the surface covering corrosion layer, secondary phases had grown locally distributed on top of the layer. These compounds are characteristic for the applied atmosphere and vary in number, shape and chemical composition. T2 - 14th Greenhouse Gas Control Technologies Conference (GHGT-14) CY - Melbourne, Australia DA - 21.10.2018 KW - CCS KW - CO2 Corrosion KW - Pipelines PY - 2019 UR - https://ssrn.com/abstract=3365756 VL - 2019 SP - 1 EP - 15 AN - OPUS4-49711 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bettge, Dirk A1 - Bäßler, Ralph A1 - Le, Quynh Hoa A1 - Kranzmann, Axel T1 - Abschlussbericht des Projektteils CLUSTER - BAM: Werkstoffauswahl und Festlegung von Obergrenzen für Verunreinigungen in variierenden CO2-Strömen auf Grund von realitätsnahen Korrosionsexperimenten - FKZ 03ET7031C - im Projektverbund CLUSTER: Auswirkungen der Begleitstoffe in den abgeschiedenen CO2‐Strömen unterschiedlicher Emittenten eines regionalen Clusters auf Transport, Injektion und Speicherung N2 - Nachdem im Verbundprojekt COORAL das Hauptaugenmerk auf überkritisches CO2 gelegt wurde, d. h. Transport über kurze Strecken bei erhöhter Temperatur, wurde in CLUSTER ein größeres lokales Transport-Netzwerk betrachtet, bei dem CO2 bei geringeren Temperaturen, also vorwiegend im flüssigen Zustand transportiert wird. Wurden in COORAL die CO2-Ströme von Kohlekraftwerken untersucht, ging es in CLUSTER zusätzlich um die Emissionen von relevanten Industrien, deren CO2-Emissionen nicht ohne Weiteres vermieden werden können. Aufgrund der Erfahrungen in COORAL konnte eine Auswahl von kommerziellen Werkstoffen getroffen werden, die für einen konkreten Einsatz für CCS zur Verfügung stünden. Die gemischten und fluktuierenden CO2-Zusammensetzungen sind bei geeigneten Begrenzungen der Begleit¬stoffe im CO2 bezüglich Korrosionsvorgänge beherrschbar. Die Machbarkeit eines lokalen CCS-Clusters erscheint daher gegeben, soweit dies die Anlagen für Kompression, Transport und Injektion betrifft. KW - CCS KW - Korrosion KW - CO2-Speicherung KW - Pipelines PY - 2019 SP - 1 EP - 67 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-50249 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -