TY - JOUR A1 - Guo, Y. A1 - Lippitz, Andreas A1 - Saftien, P. A1 - Unger, Wolfgang A1 - Kemnitz, E. T1 - Tuning the surface properties of novel ternary iron(III) fluoride-based catalysts using the template effect of the matrix N2 - Sol–gel prepared ternary FeF3–MgF2 materials have become promising heterogeneous catalysts due to their porosity and surface Lewis/Brønsted acidity (bi-acidity). Despite the good catalytic performance, nanoscopic characterisations of this type of material are still missing and the key factors controlling the surface properties have not yet been identified, impeding both a better understanding and further development of ternary fluoride catalysts. In this study, we characterised the interaction between the bi-acidic component (FeF3) and the matrix (MgF2) on the nano-scale. For the first time, the formation pathway of FeF3–MgF2 was profiled and the template effect of MgF2 during the synthesis process was discovered. Based on these new insights two novel materials, FeF3–CaF2 and FeF3–SrF2, were established, revealing that with decreasing the atomic numbers (from Sr to Mg), the ternary fluorides exhibited increasing surface acidity and surface area but decreasing pore size. These systematic changes gave rise to a panel of catalysts with tuneable surface and bulk properties either by changing the matrix alkaline earth metal fluoride or by adjusting their ratios to Fe or both. The template effect of the alkaline earth metal fluoride matrix was identified as the most probable key factor determining the surface properties and further influencing the catalytic performance in ternary fluoride based catalysts, and paves the way to targeted design of next-generation catalysts with tunable properties. KW - Catalysis KW - Surface analysis KW - XPS PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-327410 DO - https://doi.org/10.1039/c4dt03229b SN - 1477-9226 SN - 1477-9234 SN - 1364-5447 VL - 44 IS - 11 SP - 5076 EP - 5085 PB - RSC CY - Cambridge AN - OPUS4-32741 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meißner, G. A1 - Dirican, D. A1 - Jäger, Christian A1 - Braun, T. A1 - Kemnitz, E. T1 - Et3GeH versus Et3SiH: controlling reaction pathways in catalytic C–F bond activations at a nanoscopic aluminum chlorofluoride† N2 - Catalytic C–F bond activation reactions of mono- and polyfluoroalkanes at Lewis acidic amorphous aluminum chlorofluoride (ACF) are presented. The hydrogen sources Et3GeH or Et3SiH control the selectivity of the conversions. The immobilization of Et3GeH at ACF resulted in catalytic dehydrohalogenation reactions to yield olefins under very mild conditions. In contrast, if Et3SiH is immobilized at ACF, C–C coupling occured and the formation of Friedel–Crafts products was observed. MAS NMR spectroscopic studies revealed information about the surface binding of the substrates. KW - Vapor-phase hydrofluorination KW - Carbon-fluorine bonds KW - Vinyl fluoride KW - Phosphine-ligands KW - Room-temperature KW - Building-blocks KW - Etal-complexes KW - Germylium ions KW - Lewis-acids KW - Hydrodefluorination PY - 2017 DO - https://doi.org/10.1039/c7cy00845g SN - 2044-4753 SN - 2044-4761 VL - 7 IS - 15 SP - 3348 EP - 3354 PB - The Royal Society of Chemistry AN - OPUS4-41836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Hannes A1 - Kemnitz, E. A1 - Hertwig, Andreas A1 - Beck, Uwe T1 - Transparent MgF2-films by sol-gel coating: Synthesis and optical properties N2 - Dielectric, anti-reflective or high reflective systems consist of low and high refractive index layers. Common systems are oxides. The preparation of low refractive index MgF2-films of optical quality by means of an anhydrous low temperature sol–gel synthesis is presented. The MgF2-sol is prepared by spin-coating on silicon and glass substrates. Various film thicknesses between 20 nm and 435 nm have been deposited. It has been shown that the thickness increase is proportional to the number of coating steps. The deposited MgF2-films consist of 10 nm to 20 nm large nanoparticles and have smooth surfaces with an average roughness (Ra) of (1.7 ± 0.3) nm. The optical constants n and k of the films are in agreement with the literature data of bulk-MgF2. KW - Sol-gel KW - Nano-MgF2 KW - Spin coating KW - Optical properties KW - Nanoparticles PY - 2008 DO - https://doi.org/10.1016/j.tsf.2007.10.126 SN - 0040-6090 VL - 516 IS - 12 SP - 4175 EP - 4177 PB - Elsevier CY - Amsterdam AN - OPUS4-17375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Hannes A1 - Hertwig, Andreas A1 - Beck, Uwe A1 - Kemnitz, E. T1 - Low temperature sol-gel metal oxide and fluoride layer stacks for optical applications N2 - MgF2 and TiO2 single layers and layer stacks were produced by a spin-coating sol-gel process. The final temperature treatment was carried out at 100 °C. The layers were deposited onto silicon and fused silica substrates and were analysed by means of atomic force microscopy, X-ray photoelectron spectroscopy, transmission electron microscopy, ellipsometry, and UV-vis transmission spectroscopy. MgF2 and TiO2 single layers have morphological and optical properties comparable with physical vapour deposited layers. By using spectroscopic mapping ellipsometry, a good inter- and intra-sample homogeneity was confirmed. Multiple deposition steps result in a linear increase of layer thickness. Various films were deposited with thicknesses between 25 nm and 350 nm. It was shown that the low temperature sol-gel process results in films of optical quality. Anti-reflective and high reflective layer stacks consisting of MgF2 and TiO2 were designed and can be produced now by a sol-gel process, whereas the MgF2 layers in the layer stacks contains also traces of MgF2-2xOx. KW - Magnesium fluoride KW - Titanium oxide KW - Sol-gel KW - Spin-coating KW - Optical properties KW - Optical layer stacks KW - MgF2 KW - TiO2 PY - 2010 DO - https://doi.org/10.1016/j.tsf.2010.06.025 SN - 0040-6090 VL - 518 IS - 21 SP - 6080 EP - 6086 PB - Elsevier CY - Amsterdam AN - OPUS4-21516 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Hannes A1 - Kemnitz, E. A1 - Hertwig, Andreas A1 - Beck, Uwe T1 - Moderate temperature sol-gel deposition of magnesium fluoride films for optical UV-applications: A study on homogeneity using spectroscopic ellipsometry N2 - Thin films of MgF2 have been deposited on silicon wafers in optical quality with a novel sol-gel deposition process at temperatures as low as 100 °C. The properties of the fluoride layers are compared to bulk MgF2 with respect to the optical constants. By employing spectroscopic mapping ellipsometry, the uniformity of the thickness of fluoride layers is confirmed to be within acceptable limits for optical applications. The optical constants are close to the bulk data. High-quality low-index films of suitable and homogeneous thickness have already been produced on a laboratory scale. KW - 78.20.-e KW - 78.66.Li KW - 78.68.+m KW - 81.20.Fw PY - 2008 DO - https://doi.org/10.1002/pssa.200777856 SN - 1862-6300 SN - 0031-8965 VL - 205 IS - 4 SP - 821 EP - 824 PB - Wiley-VCH CY - Berlin AN - OPUS4-17330 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - König, R. A1 - Scholz, G. A1 - Scheurell, K. A1 - Heidemann, D. A1 - Buchem, I. A1 - Unger, Wolfgang A1 - Kemnitz, E. T1 - Spectroscopic characterization of crystalline AIF3 phases N2 - A comprehensive spectroscopic characterization of all known crystalline AlF3 phases (α-, β-, η-, κ-, θ-AlF3) is presented for the first time in this study. Beside their X-ray diffraction powder patterns, which were already published in the literature, 27Al and 19F MAS NMR, FT IR and XPS spectroscopic techniques were applied for all phases in a consistent manner. For all phases prepared the utilization of 27Al satellite transition (SATRAS) NMR allowed to determine the quadrupolar parameters of the aluminium sites including their distributions. In addition, η-AlF3 was isolated with high phase purity and characterized following a new preparation path different from those known so far in the literature. KW - Crystalline aluminium fluorides KW - Solid state NMR KW - FT IR KW - XPS PY - 2010 DO - https://doi.org/10.1016/j.jfluchem.2009.10.015 SN - 0022-1139 SN - 1873-3328 VL - 131 IS - 1 SP - 91 EP - 97 PB - Elsevier CY - Amsterdam AN - OPUS4-20991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scholz, G. A1 - Krahl, Thoralf A1 - Ahrens, M. A1 - Martineau, C. A1 - Buzaré, J.Y. A1 - Jäger, Christian A1 - Kemnitz, E. T1 - 115In and 19F MAS NMR study of (NH4)3InF6 phases N2 - This study presents for the first time an NMR spectroscopic characterization of the room and high temperature phases of (NH4)3InF6 using 19F and 115In as probe nuclei. The reversible phase transition to the cubic phase at 353 K was followed by MAS NMR in situ. Static NMR experiments of the room temperature phase and MAS NMR experiments of the high temperature phase allowed the determination of the NMR parameters of both nuclei. Finally, the scalar In–F coupling, rarely observed in solid state NMR, is evidenced in both room and high temperature phases of (NH4)3InF6, and measured in the high temperature phase. KW - (NH4)3InF6 KW - 115In and 19F solid state NMR KW - XRD PY - 2011 DO - https://doi.org/10.1016/j.jfluchem.2011.01.010 SN - 0022-1139 SN - 1873-3328 VL - 132 IS - 4 SP - 244 EP - 249 PB - Elsevier CY - Amsterdam AN - OPUS4-23475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - König, R. A1 - Scholz, G. A1 - Pawlik, Alf A1 - Jäger, Christian A1 - van Rossumm, B. A1 - Oschkinat, H. A1 - Kemnitz, E. T1 - Crystalline Aluminium Hydroxy Fluorides: Structural Insights Obtained by High Field Solid State NMR and Trend Analyses N2 - A series of crystalline aluminum hydroxy fluorides in cubic pyrochlore structure AlFx(OH)3-x·H2O with variable F-content x were investigated by solid-state NMR by applying different magnetic fields up to 21.1 T. Distinguishable octahedral species AlFx(OH)6-x (x = 1-6) were identified in the crystalline aluminum hydroxy fluorides. The subsequent analysis of the highfield 27Al MAS NMR data allows the derivation of the trend analysis graphs giving correlations between the 27Al chemical shifts and the quadrupolar frequencies and the F-content x in AlFx(OH)6-x. Clear trends were obtained for both, which are, along with the 19F MAS chemical-shift trend analysis presented earlier, valuable tools for the interpretation of MAS NMR spectra of amorphous AlFx(OX)3-x compounds (X = H, alkyl). Following the dehydration of the pyrochlores by solid-state NMR eventually reveals a remarkable influence of the incorporated solvent molecules (H2O) on the 19F chemical shift. On that basis, a new chemical-shift trend analysis for 19F chemical shifts in correlation with x in AlFx(OH)6-x units for proton-poor substances (in the Al, F, O, H system) was determined. By using this correlation, high-surface AlF3 has a mean bulk Al:F ratio similar to that found for ACF, namely, AlF2.8(O/OH)0.2. KW - Aluminium-27 KW - Crystalline aluminium hydroxy fluorides KW - Chemical shift trend analysis KW - High field solid state NMR KW - Quadrupolar nuclei PY - 2008 DO - https://doi.org/10.1021/jp804662f SN - 1932-7447 SN - 1089-5639 VL - 112 IS - 40 SP - 15708 EP - 15720 PB - Soc. CY - Washington, DC AN - OPUS4-18365 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - König, R. A1 - Scholz, G. A1 - Pawlik, Alf A1 - Jäger, Christian A1 - Rossum, B. van A1 - Kemnitz, E. T1 - Identification of AIFx(OR)y species in strongly disordered aluminium isopropoxide fluoride solids: a field-dependent MAS NMR study KW - Ultra high-field MAS NMR (21.1T) KW - 27 Al MAS solid state NMR KW - Fluoride xerogels KW - Sol-gel process KW - Fluorolysis KW - Quadrupolar nuclei PY - 2009 DO - https://doi.org/10.1021/jp9066795 SN - 1932-7447 SN - 1089-5639 VL - 113 IS - 35 SP - 15576 EP - 15585 PB - Soc. CY - Washington, DC AN - OPUS4-20461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pawlik, Alf A1 - König, R. A1 - Scholz, G. A1 - Kemnitz, E. A1 - Brunklaus, G. A1 - Bertmer, M. A1 - Jäger, Christian T1 - Access to local structures of HS-AIF3 and its precursor determined by high-resolution solid-state NMR KW - Aluminium fluoride KW - 27Al NMR KW - MQMAS KW - Amorphous materials KW - Catalysts PY - 2009 DO - https://doi.org/10.1021/jp904626k SN - 1932-7447 SN - 1089-5639 VL - 113 IS - 38 SP - 16674 EP - 16680 PB - Soc. CY - Washington, DC AN - OPUS4-20463 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Feist, M. A1 - Troyanov, S.I. A1 - Mehner, Hartmut A1 - Witke, Klaus A1 - Kemnitz, E. T1 - Zwei Oxidationsstufen und vier verschiedene Koordinationen von Eisen in einer Verbindung. Synthese, Kristallstruktur und spektroskopische Charakterisierung von 1,4-Dimethylpiperazinium-Chloroferrat(II, III), (dmpipzH2)6[FeIICl4]2[FeIIICl4]2[FeIICl5] [FeIIICl6] KW - 1,4-Dimethylpiperazinium chloroferrate(II,III) KW - Crystal Structure KW - Trigonal-bipyramidal pentachloroferrate(II) KW - Mössbauer, Raman spectroscopy PY - 1999 SN - 0044-2313 SN - 1521-3749 SN - 0372-7874 SN - 0863-1786 SN - 0863-1778 IS - 625 SP - 141 EP - 146 PB - Wiley-VCH CY - Weinheim AN - OPUS4-2305 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ünveren, Ercan A1 - Kemnitz, E. A1 - Hutton, S. A1 - Lippitz, Andreas A1 - Unger, Wolfgang T1 - Analysis of highly resolved x-ray photoelectron Cr 2p spectra obtained with a Cr2O3 powder sample prepared with adhesive tape KW - High-resolution XPS KW - Cr2O3 powder KW - Multiplet splitting PY - 2004 SN - 0142-2421 SN - 1096-9918 VL - 36 SP - 92 EP - 95 PB - Wiley CY - Chichester AN - OPUS4-3427 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ünveren, Ercan A1 - Kemnitz, E. A1 - Oran, Umut A1 - Unger, Wolfgang T1 - Static TOF-SIMS Surface Analysis of a CCl2F2 Activated Chromia Catalyst Used for a Cl/F Exchange Reaction N2 - Static TOF-SIMS results strongly underpin earlier conclusions from ESCA, XANES, and tracer studies that the accumulation of fluorine and chlorine at the surface of chromia by a heterogeneous reaction with a chlorofluorocarbon compound results in the formation of mixed chromium oxide halide species and not in the nucleation of CrCl3 and/or CrF3 phases. KW - Oberflächenanalytik KW - Katalyse PY - 2004 DO - https://doi.org/10.1021/jp046773h SN - 1520-6106 SN - 1520-5207 SN - 1089-5647 VL - 108 SP - 15454 EP - 15456 PB - Soc. CY - Washington, DC AN - OPUS4-4718 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Böse, Olaf A1 - Unger, Wolfgang A1 - Kemnitz, E. A1 - Schroeder, S. L. M. T1 - Active sites on an oxide catalyst for F/Cl-exchange reactions: X-ray spectroscopy of fluorinated y-Al2O3 N2 - The dismutation of CHClF2 to CHF3 and CHCl3 was used to probe the effect of γ-Al2O3 fluorination on fluorine-against-chlorine (Cl/F) exchange reactions. X-ray photoelectron spectroscopy (XPS), X-ray excited Auger electron spectroscopy (XAES) and X-ray absorption near edge structure (XANES) spectroscopy were employed to probe the modifications at the surface of γ-Al2O3 accompanying the initial stages of fluorination. The results suggest that fluorine uptake by γ-Al2O3 starts initially at the surface of the oxide particles, with the formation of a fluorine species that is characterised by a single bond and a high effective charge q. Catalytic Cl/F-exchange is only observed after accumulation of higher fluorine concentrations, for which insertion of fluorine into the sub-surface region of the oxide crystallites has commenced. Quantitative XPS shows that the fluorination level must exceed approximately 10 atom% of the anions to achieve catalytic activity. The spectroscopic evidence suggests that the formation of aluminium oxofluorides is sufficient to provide catalytic activity. The presence of an AlF3 phase is not a condition for the observation of catalytic activity, even though defect-rich AlF3 is ultimately the endpoint of the fluorination process and is itself a Cl/F exchange catalyst. PY - 2002 DO - https://doi.org/10.1039/b110792e SN - 1463-9076 SN - 1463-9084 VL - 4 IS - 12 SP - 2824 EP - 2832 PB - The Royal Soc. of Chemistry CY - Cambridge AN - OPUS4-6940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krishna Murthy, J. A1 - Gross, U. A1 - Rüdiger, St. A1 - Ünveren, Ercan A1 - Unger, Wolfgang A1 - Kemnitz, E. T1 - Synthesis and characterization of chromium(III)-doped magnesium fluoride catalysts N2 - Cr3+-doped MgF2 systems are synthesised by a novel non-aqueous soft chemistry route using different Cr precursors and varying Cr loading. These systems have been characterized by X-ray powder diffraction (XRD), BET surface area, TPD of ammonia, FT-IR pyridine adsorption analysis and X-ray photoelectron spectroscopy, and tested for their catalytic activity in dismutation of CCl2F2 and CF3–CHClF. Catalysts synthesised starting from CrO3 or (CH3CO2)7Cr3(OH)2 showed better catalytic activity than those prepared with CrCl3. FT-IR pyridine adsorption studies reveal that the catalytic activity is highly correlated with the Lewis acid strength. In TPD of NH3 catalysts prepared from CrO3 and (CH3CO2)7Cr3(OH)2, precursors showed a similar behaviour, different from that of catalysts prepared from CrCl3. KW - Lewis acid KW - Heterogeneous catalysis KW - Metal fluoride KW - Doped systems PY - 2005 UR - http://www.sciencedirect.com/science/journal/0926860X DO - https://doi.org/10.1016/j.apcata.2004.12.004 SN - 0947-8396 VL - 282 IS - 1-2 SP - 85 EP - 91 PB - Springer CY - Berlin AN - OPUS4-7442 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ünveren, Ercan A1 - Kemnitz, E. A1 - Lippitz, Andreas A1 - Unger, Wolfgang T1 - Surface Characterization of Chromia for Chlorine/Fluorine Exchange Reactions N2 - The dismutation of CCl2F2 was used to probe the effect of halogenation of chromia by Cl/F exchange reactions to find out the difference between the halogenated inactive and active catalysts. The heterogeneous reactions were performed in a continuous flow Ni reactor and also under simulated reaction conditions in a reactor where after the reaction X-ray photoelectron spectroscopy (XPS) and X-ray excited Auger electron spectroscopy (XAES) analyses are possible without air exposure of the catalyst, i.e., under so-called "in situ" conditions. The Cr(III) 2p XP spectra, which revealed multiplet splitting features and satellite emission, were used for chemical analysis by using a simple evaluation procedure which neglects this inherent complexity. Chemical analysis was also applied by using chemical state plots for Cr 3s in order to cross-check Cr 2p related results. Both ex and in situ XPS show that as soon as Cr2O3 is exposed to CCl2F2 at 390°C fluorination as well as chlorination takes place at the catalyst surface. When the XPS surface composition reaches approximately 4 at. % fluorination and 6 at. % chlorination, maximum catalytic activity was obtained. Application of longer reaction times did not change significantly the obtained surface composition of the activated chromia. The fluorination and chlorination of chromia was further investigated by various HF and HCl treatments. The activated chromia samples and the Cr2O3, Cr(OH)3, CrF2OH, CrF3·H2O, α-CrF3, β-CrF3, and CrCl3 reference samples with well-known chemical structures were also characterized by X-ray absorption near edge structure (XANES), time-of-flight secondary ion mass spectroscopy (TOF-SIMS), pyridine-FTIR, wet chemical (F and Cl) analysis, X-ray powder diffraction (XRD), and surface area (BET) analysis. The results suggest that the formation of chromium oxide chloride fluoride species, e.g., chromium oxide halides, at the surface is sufficient to provide catalytic activity. The presence of any CrF3 and/or CrCl3 phases on the activated chromia samples was not found. PY - 2005 DO - https://doi.org/10.1021/jp045902r SN - 1520-6106 SN - 1520-5207 SN - 1089-5647 VL - 109 IS - 5 SP - 1903 EP - 1913 PB - Soc. CY - Washington, DC AN - OPUS4-10531 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scheurell, K. A1 - Hoppe, E. A1 - Brzezinka, Klaus-Werner A1 - Kemnitz, E. T1 - Bulk and surface properties of highly dispersed VOx/ZrO2, VOx/SiO2 and VOx/TiO2/SiO2 systems and their relevance for propane oxidation N2 - Highly dispersed vanadium-doped metal oxides such as VOx/ZrO2, VOx/SiO2 and VOx/TiO2/SiO2 with vanadium contents between 0 and 25 mole% were prepared by special bulk preparation methods (coprecipitation and sol–gel, followed by freeze-drying). Bulk and surface properties of the obtained mixed oxide solid solutions were thoroughly investigated by different analytical methods (Raman and FTIR spectroscopy, TPD, H2-TPR, oxygen isotope measurements etc.). Moreover, the catalytic behaviour of the oxides was studied for the example of the oxidative dehydrogenation (ODH) of propane to propylene. Independent of the preparation method, the catalytic behaviour of vanadium-doped ZrO2 and TiO2 phases is very similar. Both metal oxide solid solutions are very active in propane ODH whereas the catalytic activity of VOx/SiO2 is relatively low. On the other hand, the reduction of the catalytic activity is accompanied by an improved selectivity for the formation of propylene. The correlation between the catalytic activity and the acidity of the oxide systems is discussed. Oxidation experiments with 18O2 clearly show that the ODH reaction occurs according to the Mars–van Krevelen mechanism. KW - Vanadium-doped metal oxides KW - Solid solutions KW - Coprecipation KW - Sol-gel-method KW - Propan oxidation KW - Catalytic activity KW - Oxygen mobility PY - 2004 DO - https://doi.org/10.1039/b402924k SN - 0959-9428 SN - 1364-5501 VL - 14 IS - 16 SP - 2560 EP - 2568 PB - Royal Society of Chemistry CY - Cambridge AN - OPUS4-4152 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Murthy, J.K. A1 - Gross, U. A1 - Rüdiger, S. A1 - Ünveren, Ercan A1 - Unger, Wolfgang A1 - Kemnitz, E. T1 - Synthesis and characterization of chromium(III)-doped magnesium fluoride catalysts N2 - Cr3+-doped MgF2 systems are synthesised by a novel non-aqueous soft chemistry route using different Cr precursors and varying Cr loading. These systems have been characterized by X-ray powder diffraction (XRD), BET surface area, TPD of ammonia, FT-IR pyridine adsorption analysis and X-ray photoelectron spectroscopy, and tested for their catalytic activity in dismutation of CCl2F2 and CF3–CHClF. Catalysts synthesised starting from CrO3 or (CH3CO2)7Cr3(OH)2 showed better catalytic activity than those prepared with CrCl3. FT-IR pyridine adsorption studies reveal that the catalytic activity is highly correlated with the Lewis acid strength. In TPD of NH3 catalysts prepared from CrO3 and (CH3CO2)7Cr3(OH)2, precursors showed a similar behaviour, different from that of catalysts prepared from CrCl3. KW - Lewis acid KW - Heterogeneous catalysis KW - Metal fluoride KW - Doped systems PY - 2005 SN - 0926-860X SN - 1873-3875 VL - 282 IS - 1-2 SP - 85 EP - 91 PB - Elsevier CY - Amsterdam AN - OPUS4-11953 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Noack, J. A1 - Emmerling, Franziska A1 - Kirmse, H. A1 - Kemnitz, E. T1 - Sols of nanosized magnesium fluoride: formation and stabilisation of nanoparticles N2 - The formation of magnesium fluoride sols and xerogels according to the fluorolytic sol–gel synthesis based on the reaction of Mg(OMe)2 with non-aqueous HF has been thoroughly investigated by X-ray scattering (WAXS/XRD), TEM, SAXS, DLS and 19F MAS NMR spectroscopy. Mechanistic insights were gained by following the reaction progress and formation of intermediate phases of the fluorination of magnesium alkoxides. For F:Mg ratios of 0.3 and 0.4 the formation of two crystalline phases was observed containing the recently obtained compound [Mg6F2(OCH3)10(CH3OH)14] hexanuclear dicubane units. The stoichiometric reaction yields magnesium fluoride nanoparticles with crystallite sizes below 5 nm, which show broad reflections in the X-ray diffraction pattern. Metal fluoride sols prepared by this way undergo tremendous changes over the first several weeks after synthesis. Immediately after the fluorination, particles of about 120 nm—probably agglomerates—are formed, which break apart in the course of about one month of ageing and low-viscous, transparent sols with particles of about 12 nm are obtained. At the same time structural re-organisation processes within the magnesium fluoride particles are observed by an increase of the (110) reflection in WAXS. KW - Surface modification KW - Colloidal particles KW - Gold nanoparticles KW - Gel synthesis KW - Small-angle scattering KW - Oxide KW - Polyelectrolytes KW - Aggregation KW - Dispersion PY - 2011 DO - https://doi.org/10.1039/c1jm11943e SN - 0959-9428 SN - 1364-5501 VL - 21 IS - 38 SP - 15015 EP - 15021 PB - Royal Society of Chemistry CY - Cambridge AN - OPUS4-26183 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - König, R. A1 - Scholz, G. A1 - Veiczi, M. A1 - Jäger, Christian A1 - Troyanov, S.I. A1 - Kemnitz, E. T1 - New crystalline aluminium alkoxide oxide fluorides: evidence of the mechanism of the fluorolytic sol-gel reaction N2 - This study reports three new crystalline aluminum isopropoxide oxide fluorides with molar ratios of Al:F equal to 1:1 and 1:1.25. These are the first three representatives isolated without the incorporation of external donor molecules. Compound 1 Al4F4(µ4-O)(µ-O'Pr)5[H(O'Pr)2] contains a tetranuclear unit consisting of two different five fold coordinated AlFO4-units, with F exclusively in the terminal position. Compound 2, Al4F4(µ4-O)(µ-O'Pr)5[H(O'Pr)2]·Al5F5(µ5-O)(µ-O'Pr)8, contains both a tetranuclear unit (as in 1) and a pentanuclear Al-unit. Al-atoms in the latter are five- and six fold coordinated. Compound 3, Al16F20(µ4-O)4(µ-O'Pr)20·2('PrOH), exhibits a slightly higher fluorination degree and contains an oligomeric chain of four F-linked tetranuclear Al-units. In addition to X-ray structure analysis, compound 1 was characterized by different solid state MAS NMR techniques, including 27Al triple quantum MAS NMR and 1H, 1H→13C CP, 19F and 27Al MAS NMR. On the basis of the collected data, a reliable decomposition of 27Al single pulse MAS NMR spectra and an unambiguous assignment of the resonances to the respective structural AlFO4-units are given. The new crystalline aluminum isopropoxide oxide fluorides are direct evidence of the fluorolytic sol–gel mechanism previously discussed. KW - Aluminium fluorine KW - MAS NMR KW - Qudrupolar nuclei KW - Crystalline aluminium isopropoxide fluoride PY - 2011 DO - https://doi.org/10.1039/c1dt10514k SN - 1477-9226 SN - 1477-9234 SN - 1364-5447 VL - 40 IS - 34 SP - 8701 EP - 8710 PB - RSC CY - Cambridge AN - OPUS4-26245 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -