TY - JOUR A1 - Kannengießer, Thomas A1 - Kromm, Arne T1 - Characterising phase transformations of different LTT alloys and their effect on residual stresses and cold cracking N2 - Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were – for the first time – detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 µm. The residual stresses show significant distributions dependent on Ms temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent. KW - Austenite KW - Cold cracking KW - Martensite KW - Low themperature KW - Transformation PY - 2011 DO - https://doi.org/10.1007/BF03321286 SN - 0043-2288 VL - 55 IS - 3 SP - 48 EP - 56 PB - International Institute of Welding CY - France AN - OPUS4-38978 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heinze, Christoph A1 - Kromm, Arne A1 - Schwenk, Christopher A1 - Kannengießer, Thomas A1 - Rethmeier, Michael T1 - Welding residual stresses depending on solid-state transformation behaviour studied by numerical and experimental methods N2 - The development of high-strength structural steels with yield strengths up to 1000 MPa results in the requirement of suitable filler materials for welding. Recently designed low transformation temperature (LTT) alloys offer appropriate strength. The martensitic phase transformation during welding induces compressive residual stress in the weld zone. Therefore, the mechanical properties of welded joints can be improved. The present paper illustrates numerical simulation of the residual stresses in LTT-welds taking into account the effect of varying Ms/Mf-temperatures, and therefore different retained austenite contents, on the residual stresses. Residual stress distributions measured by synchrotron diffraction are taken as evaluation basis. A numerical model for the simulation of transformation affected welds is established and can be used for identification of appropriate Ms-temperatures considering the content of retained austenite. KW - Welding simulation KW - Residual stress KW - Low transformation temperature filler material KW - Martensitic transformation KW - Retained austenite PY - 2011 DO - https://doi.org/10.4028/www.scientific.net/MSF.681.85 SN - 0255-5476 VL - 681 SP - 85 EP - 90 PB - Trans Tech Publications CY - Aedermannsdorf, Switzerland AN - OPUS4-23357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brauser, Stephan A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Rethmeier, Michael T1 - In-situ analysis of solid state phase transformation in TRIP-aided steels by synchrotron diffraction N2 - Energy dispersive synchrotron diffraction (EDXRD) analysis and 3 dimensional digital image correlations were conducted to investigate the stress and strain effected transformation behavior during tensile loading of low alloyed TRansformation Induced Plasticity (TRIP) steel. This technique allowed for phase specific stress measurement during certain tensile load steps in the elastic and also plastic regime. Additionally the simultaneous determination of the load dependent phase content was realized. The results show that the martensite transformation starts only after exceeding the overall yield point and is finished before reaching the uniform elongation, whereas a large portion of the austenite remains unchanged in the structure. Furthermore, the martensite transformation related to the stress in the γ-phase and α-phase was analyzed and quantified. KW - Synchrotron KW - EDXRD KW - Phase transformation KW - TRIP steel KW - Digital image correlation KW - Residual stress PY - 2011 UR - https://www.jstage.jst.go.jp/article/qjjws/29/3/29_3_81s/_pdf DO - https://doi.org/10.2207/qjjws.29.81s SN - 0288-4771 VL - 29 IS - 3 SP - 81 EP - 85 CY - Tokyo, Japan AN - OPUS4-24693 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Brauser, Stephan A1 - Kannengießer, Thomas A1 - Rethmeier, Michael T1 - High-energy synchrotron diffraction study of a transformation induced plasticity steel during tensile deformation N2 - Energy-dispersive x-ray diffraction offers the possibility for measurement and evaluation of diffraction spectra containing information of various diffraction lines of all contributing crystalline phases of a material. Combined strain imaging and diffraction analysis was conducted during the tensile test of a low alloyed transformation-induced plasticity (TRIP) steel in order to investigate the transformation induced plasticity, strain hardening, and load partitioning effects. Optical strain imaging allowed for determination of localized true strains from three-dimensional deformations measured in situ. High-energy synchrotron radiation has permitted diffraction analysis in transmission mode to gather information from the material interior. Phase-specific stress evolution during loading could be observed applying the sin2ψ technique during certain load steps. The strains of the individual lattice planes were determined in different locations under varying angles between loading and perpendicular direction. Using energy-dispersive methods it was also possible to determine the transformation behaviour during elastic and plastic regime taking into account a large number of diffraction lines. The results show that the approach practised here enables one to pull together macroscopic and phase-specific microscopic material behaviour in order to improve existing models for prediction of complex load situations. KW - EDXRD KW - Transformation-induced plasticity (TRIP) KW - Residual stress KW - Synchrotron KW - Martensite transformation PY - 2011 DO - https://doi.org/10.1177/0309324711403969 SN - 0309-3247 SN - 2041-3130 VL - 46 IS - 7 SP - 581 EP - 591 PB - Sage CY - London AN - OPUS4-24604 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Altenkirch, J. A1 - Gibmeier, J. T1 - Residual stresses in multilayer welds with different martensitic transformation temperatures analyzed by high-energy synchrotron diffraction N2 - Low Transformation Temperature (LTT) alloys were developed in order to control the residual stress development by the martensitic phase transformation already during cooling of the weld metal. The positive effect of such LTT alloys on the mitigation of detrimental tensile residual stresses during welding has already been confirmed on the basis of individual laboratory tests. Within the current project it was experimentally investigated whether the phase transformation mechanisms are effective under increased restraint due to multi-pass welding of thicker specimens. The local residual stress depth distribution was analyzed non-destructively for V-type welds processed by arc welding using energy dispersive synchrotron X-ray diffraction (EDXRD). The use of high energy (20 keV to 150 keV) EDXRD allowed for the evaluation of diffraction spectra containing information of all contributing phases. As the investigated LTT alloy contains retained austenite after welding, this phase was also considered for stress analysis. The results show in particular how the constraining effect of increased thickness of the welded plates and additional deposited weld metal influences the level of the residual stresses in near weld surface areas. While the longitudinal residual stresses were reduced in general, in the transition zone from the weld to the heat-affected zone (HAZ) compressive residual stresses were found. KW - Low Transformation Temperature KW - Phase Transformation KW - Residual Stress KW - Synchrotron Diffraction PY - 2011 DO - https://doi.org/10.4028/www.scientific.net/MSF.681.37 SN - 0255-5476 VL - 681 SP - 37 EP - 42 PB - Trans Tech Publications CY - Aedermannsdorf, Switzerland AN - OPUS4-23470 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Altenkirch, J. A1 - Gibmeier, J. A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Nitschke-Pagel, T. A1 - Hofmann, M. T1 - In situ study of structural integrity of low transformation temperature (LTT)-welds N2 - We discuss the stability of weld residual strain under static and quasi cyclic transverse tensile loading in the elastic and elastic–plastic region. The test welds were joined with low transformation temperature weld filler materials with 10 wt% Cr and varying Ni-content from 8 to 12 wt%. Using neutron diffraction the residual lattice strain in the martensitic α'- and austenitic γ-phase in the fusion zone as well as the ferritic α-phase in the heat affected zone and base metal as induced by welding, superimposed by stepwise tensile loading and after unloading was measured. The amount of retained austenite in the fusion zone increases with increasing Ni-content, but it decreases with increasing load level due to stress induced martensite formation. In the as-welded condition the transverse macroscopic residual lattice strain was found to be in low compression in the fusion zone in each weld, while the heat affected zone was in tension. Local plastic deformation of the γ-phase as a result of yielding during tensile loading in combination with the change in phase fraction resulted in increased macroscopic compression in the fusion zone. The reduced yield strength in the heat affected zone resulted in plastic deformation and a considerable shift into compression. Comparison with the cross weld distribution of the hardness and FWHM of the neutron diffraction interference lines supported the assumption of plastic deformation of the γ- and α-phase in the fusion and heat affected zone, respectively, while the α'-phase in the fusion zone was stressed within the elastic regime only. Microstructural observations as well as measurement of the local γ-phase fraction by means of laboratory X-ray diffraction in the fusion zone strengthen these observations. KW - Low transformation temperature KW - Residual stress KW - Neutron diffraction PY - 2011 DO - https://doi.org/10.1016/j.msea.2011.03.091 SN - 0921-5093 SN - 1873-4936 VL - 528 IS - 16-17 SP - 5566 EP - 5575 PB - Elsevier CY - Amsterdam AN - OPUS4-24359 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kannengießer, Thomas A1 - Rethmeier, Michael A1 - Portella, Pedro Dolabella A1 - Ewert, Uwe A1 - Redmer, Bernhard T1 - Assessment of hot cracking behaviour in welds N2 - Hot crack assessment during production and processing of metallic materials is an essential prerequisite for the safety of welded structures. The hot cracking investigations presented here were carried out as part of a study aimed at the development of Cr/Ni low transformation temperature filler materials. Low transformation temperature alloys open up the possibility for welding high strength steels. The externally loaded Modified Varestraint Transvarestraint hot cracking test was employed in the experiments described. The hot cracking resistance was evaluated with the help of light microscopy applied at the specimen surface. The proportionality between hot cracking susceptibility and Cr/Ni alloy content was explained by the altered solidification kinetics and by the enlarged solidification interval. The internal crack paths and the three-dimensional structure of the crack net in the material volume were examined using X-ray computer tomography. The total crack lengths for different material depths and circumjacent rectangular volumes, respectively, were be determined. An increasing hot cracking susceptibility with increasing Cr/Ni alloy content was also be established for the specimen volume. KW - Hot cracking KW - Low transformation temperature (LTT) alloy KW - Modified varestraint transvarestraint (MVT) hot cracking test KW - X-ray computer tomography PY - 2011 DO - https://doi.org/10.3139/146.110545 SN - 1862-5282 VL - 102 IS - 8 SP - 1001 EP - 1006 PB - Carl Hanser CY - München AN - OPUS4-24400 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beyer, Katrin A1 - Kannengießer, Thomas A1 - Griesche, Axel A1 - Schillinger, B. T1 - Neutron radiography study of hydrogen desorption in technical iron N2 - The purpose of the present study is to show the feasibility of examining hydrogen desorption in technical iron samples using neutron radiography at the ANTARES facility of the FRM II research reactor, Technische Universität München. It has been shown that this method is appropriate for in situ determination of hydrogen Desorption for concentrations as low as 20 ppmH. Experiments were carried out in the temperature range from room temperature up to 260 °C. Measurement was based on direct comparison between electrochemically hydrogen-loaded iron samples and hydrogen-free reference samples at the same temperature. This enables the determination of hydrogen concentration as a function of time and temperature. Ex situ carrier gas hot extraction experiments using the same temperature–time profiles as the neutron radiography experiments have been used to calibrate the greyscale values of the radiographs to defined hydrogen concentrations. It can be stated that hydrogen desorption correlates with sample temperature. KW - Neutron radiography KW - Hydrogen PY - 2011 DO - https://doi.org/10.1007/s10853-011-5450-7 SN - 0022-2461 SN - 1573-4803 VL - 46 IS - 15 SP - 5171 EP - 5175 PB - Springer Science + Business Media B.V. CY - Norwell, Mass. AN - OPUS4-25150 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brauser, Stephan A1 - Kannengießer, Thomas T1 - Hydrogen absorption and diffusion in different welded duplex steels N2 - In this study, hydrogen absorption and diffusion were investigated for various high-alloyed ferritic-austenitic duplex steels. On account of the specific transformation and solidification behaviour, respectively, of duplex steels as compared to single-phase ferritic and austenitic steels, special conditions have to be considered concerning hydrogen absorption which may ultimately lead to microstructure-dependent hydrogen-assisted weld metal cracking. Hydrogen absorption during welding may occur via the shielding gas, moisture from the surroundings or via the welding filler material. As a contribution to the interpretation and prediction of hydrogen-induced cracking in welded duplex steels, the actual hydrogen absorption via the arc as well as the weld metal hydrogen diffusion was investigated for the first time in a duplex steel DS (1.4462), a super duplex steel SDS (1.4501) and in a lean duplex steel LDS (1.4162). Isothermal heat treatment using carrier gas hot extraction enabled quantification of the amounts of hydrogen trapped in the respective microstructure areas. The hydrogen diffusion coefficients were determined by analytical and numerical calculation. The total hydrogen concentrations and the diffusion coefficients were found to be nearly identical. Trapped hydrogen was however observed to be dependent on the material and on the microstructure condition. The influence of hydrogen on the mechano-technological properties of the weld metal was characterized with the help of tensile tests. In addition, the hydrogen embrittlement effect was detected in scanning electron microscopic analyses. KW - Absorption KW - Diffusion KW - Embrittlement KW - Duplex stainless steels KW - Hydrogen PY - 2011 SN - 0043-2288 SN - 1878-6669 VL - 55 IS - 5-6 SP - 26 EP - 36 PB - Springer CY - Oxford AN - OPUS4-23721 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lorenz, Stephan A1 - Kannengießer, Thomas A1 - Posch, G. T1 - Eignung hochlegierter Fülldrahtelektroden zum Laserstrahl-MSG-Hybridschweißen N2 - Gegenstand dieses Forschungsprojekts waren Untersuchungen zur Qualifikation von Fülldrahtelektroden für das Laserstrahl-MSG-Hybridschweißen hochlegierter Stähle. Dieser Typ Drahtelektrode ermöglicht aufgrund seines ringförmigen Metallmantels und der pulverartigen Füllung insbesondere im oberen Bereich der erzielbaren Abschmelzleistungen einen stabilen, spritzerarmen Werkstoffübergang vergleichbar dem im Sprühlichtbogen. Im Gegensatz dazu wird beim Abschmelzen von Massivdrahtelektroden ein kontrollierter Werkstoffübergang durch die Impulslichtbogentechnik erreicht. Die Werkstoff- und prozessspezifischen Eigenschaften beim Schweißen dieser Zusatzwerkstoffe haben einen signifikanten Einfluss auf die Schweißnahtmetallurgie sowie die Prozessstabilität. Zur Untersuchung der Übertragbarkeit der erzielbaren Werkstoffeigenschaften vom MSG-Schweißen auf das Laserstrahl-MSG-Hybridschweißen wurden Versuche am hochlegierten Grundwerkstoff AISI403L (X2CrNil911) durchgeführt. Als Zusatzwerkstoffe gemäß DIN EN 12 072 und DIN EN ISO 17 633 kamen vier Drahtelektroden, ein eigens für das Positionsschweißen konzipierter Rutilfülldraht 19 9 L P M1, ein zum Schweißen in Wannenposition geeigneter Rutilfülldraht T 19 9 L R M (C) 3, ein Metallpulverfülldraht T199LMM1 sowie ein Massivdraht G19 9 L Si zum Einsatz. KW - Fülldrahtelektroden KW - Laserstrahlschweißen KW - Metall-Schutzgasschweißen KW - Hybridschweißen KW - Werkstofffragen KW - Zusatzwerkstoffe PY - 2011 SN - 0036-7184 VL - 63 IS - 5 SP - 222 EP - 228 PB - Verl. für Schweißen u. Verwandte Verfahren, DVS-Verl. CY - Düsseldorf AN - OPUS4-23850 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -