TY - JOUR A1 - Gluth, Gregor A1 - Lehmann, Christian A1 - Rübner, Katrin A1 - Kühne, Hans-Carsten T1 - Geopolymerization of a silica residue from waste treatment of chlorosilane production N2 - A silica residue from waste treatment of chlorosilane production was used together with solid sodium aluminate to test its applicability for the production of one-part geopolymers. The blend was activated with water and cured at 70 °C. The degree of reaction and strength were determined after 1, 3, and 7 days. The reaction products were analyzed by XRD and SEM/EDX. Until the third day of curing the degree of reaction of the residue reached 51 % and the strength was 8.9 MPa. The reaction product was identified as geopolymer containing zeolite A. Thus, the results confirmed that the residue may be used in the production of geopolymers. However, after 3 days of curing no further progress of reaction was observed and the strength slightly decreased, which was attributed to changes in the structure of the geopolymeric gel. It was further observed that even harsh vacuum drying left some water (presumably zeolitic water and surface hydroxyl groups) in the geopolymer. KW - Geopolymers KW - One-part formulation KW - Silica KW - Zeolite A PY - 2013 UR - http://link.springer.com/article/10.1617/s11527-012-9972-5/fulltext.html DO - https://doi.org/10.1617/s11527-012-9972-5 SN - 1359-5997 SN - 1871-6873 VL - 46 IS - 8 SP - 1291 EP - 1298 PB - Springer CY - Dordrecht AN - OPUS4-28596 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vogler, Nico A1 - Gluth, Gregor A1 - Oppat, Klaus A1 - Kühne, Hans-Carsten T1 - Charakterisierung von Bauteiloberflächen – Rautiefebestimmung mittels konventioneller und laserbasierter Verfahren T1 - Surface characterization of building elements - roughness measurements by conventional and laser-based methods N2 - Die Bestimmung der Rauheit von Bauteiloberflächen stellt eine wichtige Messaufgabe im Bauwesen dar. Vor allem bei der Betoninstandsetzung, im Straßenbau und bei der Herstellung von Stahlbeton-Halbfertigteilen ist die Rauheit – gemessen als Rautiefe – eine wichtige Kenngröße. Zurzeit werden Messungen der Rautiefe mittels volumetrischer Verfahren (Sandflächenverfahren) durchgeführt. Diese bereits seit mehreren Jahrzehnten angewandten Verfahren sind jedoch auf horizontale bzw. wenig geneigte und trockene Oberflächen beschränkt. Darüber hinaus hängen die erzielten Ergebnisse sehr stark von der angewandten Prüfvorschrift, den darin vorgeschriebenen Prüfmitteln und Geräten und dem jeweiligen Anwender ab. Als Alternative zu den volumetrischen Verfahren wurde an der Bundesanstalt für Materialforschung und -prüfung (BAM) ein automatisiertes, laserbasiertes Messverfahren entwickelt, mit dem Rautiefen von Bauteiloberflächen in Anlehnung an bereits standardisierte Verfahren bestimmt werden können. Der vorliegende Beitrag befasst sich zunächst mit den konventionellen Prüfverfahren, beschreibt die wichtigsten Zusammenhänge und zeigt die Grenzen dieser Methoden auf. Im zweiten Teil wird das an der BAM entwickeltes Messsystem, als zielführendes Alternativverfahren für die konventionellen Methoden, vorgestellt und dessen Leistungsfähigkeit näher beschrieben. N2 - The measurement of surface roughness of building elements is an important task in civil engineering, particularly in the field of concrete repair, in road construction and in the production of precast concrete elements. At present, the surface roughness is generally determined by the so called sand-patch-test (volumetric method). This method which is used since several decades is only applicable on horizontal or only slightly sloped and dry surfaces. In addition, the results strongly depend on the utilised standards, the prescribed test equipment and the executing person. Therefore, a laser-based device for the determination of surface roughness has been developed at Bundesanstalt fur Materialforschung und -pru-fung (BAM). This contribution deals first with the different modifications of the sand-patch-test and other conventional methods, and describes the underlying formulae and the limitations of the methods. In the second part, the laser-based system which was developed at BAM is presented; its advantages and the capability of this alternative method will be described in detail. KW - Rautiefe KW - Instandsetzung KW - Laserbasierte Rautiefebestimmung KW - Shear PY - 2017 SN - 0005-6650 VL - 92 IS - März SP - 97 EP - 104 PB - Springer VDI CY - Düsseldorf AN - OPUS4-39299 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Lehmann, Christian A1 - Rübner, Katrin A1 - Kühne, Hans-Carsten T1 - Reaction products and strength development of wastepaper sludge ash and the influence of alkalis N2 - Wastepaper sludge ash (WSA) from a newsprint paper mill was investigated for its mineralogical composition and its reaction products and strength development after activation with water and sodium and potassium hydroxide solutions. The results showed the WSA to consist of calcite, free lime, gehlenite, tricalcium aluminate, belite, talc, quartz and probably a glassy phase. The principle reaction product was monocarboaluminate (CO3–AFm) for the water- as well as for the alkali-activated WSA. Formation of monocarboaluminate and strength gain was more rapid for the alkali-activated WSA until 1 day of curing. However, afterwards reactions proceeded much slower when alkali solutions were used, leading to an about twice as high compressive strength for water-activated WSA mortars after 28 days of curing. The observed behavior is tentatively ascribed to a less uniform microstructure of the alkali-activated WSA. Significant differences between NaOH- and the KOH-activated WSA were not observed. KW - Wastepaper sludge ash KW - Reaction products KW - Monocarboaluminate KW - Strength KW - Alkali-activation PY - 2014 DO - https://doi.org/10.1016/j.cemconcomp.2013.09.009 SN - 0958-9465 SN - 1873-393X VL - 45 SP - 82 EP - 88 PB - Elsevier CY - Barking, Essex AN - OPUS4-29930 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sturm, Patrick A1 - Moye, J. A1 - Gluth, Gregor A1 - Vogler, Nico A1 - Taffe, A. A1 - Kühne, Hans-Carsten ED - Rossignol, S. ED - Gluth, Gregor T1 - Properties of alkali-activated mortars with salt aggregate for sealing structures in evaporite rock N2 - Concrete structures for sealing of tunnels in the host rock are an essential part of systems for nuclear waste storage. However, concretes based on blended cements or magnesium oxychloride cements, which are commonly considered for this application, can deteriorate severely due to a significant heat of hydration and associated deformation and cracking. Alkali-activated materials (AAMs) offer a potential solution to this problem because of their low heat release during hardening. To explore their suitability for the construction of sealing structures in evaporite rock, various AAMs with salt aggregate were studied regarding fresh properties, heat release, mechanical properties and microstructure. The heat of reaction of the AAMs was up to 55% lower than that of a blended cement designed for sealing structures, indicating significant benefits for the intended application. Other relevant properties such as mechanical strength and permeability depended strongly on the mix-design of the AAMs and curing conditions. KW - Alkali-activated materials KW - Geopolymers KW - Nuclear waste storage KW - Sealing structures KW - Evaporite rock PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519422 DO - https://doi.org/10.1016/j.oceram.2020.100041 SN - 2666-5395 VL - 5 IS - Special issue: Alkali-activated materials and geopolymers in ceramics and beyond SP - 1 EP - 8 PB - Elsevier CY - Amsterdam AN - OPUS4-51942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Wolfram A1 - Wend, Dirk A1 - Kühne, Hans-Carsten A1 - Meng, Birgit T1 - The influence of superplasticiser modifications on early hydration processes N2 - Self-compacting concrete (SCC) differs substantially from normal concrete as regards the quantity of superplasticiser dosage. The functionality of superplasticisers, based on the polycarboxylate ether (PCE) superplasticiser customary with SCC, is nowadays very well understood at construction material research level. However, knowledge concerning pertinent correlations does not always permeate practice to an equal extent. PCEs are extremely polymorphic as opposed to earlier superplasticiser groups, which still possess a considerable proportion of the superplasticiser market. The geometry of polymers can be adjusted individually to performance characteristics required for certain uses. Yet, in selecting a superplasticiser for its specified rheological properties, a very strong influence can equally be exerted simultaneously on the subsequent hydration process. The charge density of the PCE employed also plays a key role in connection with both rheology and early hydration. KW - Rheology KW - Early cement hydration KW - Polycarboxylate ether vicat KW - Shrinkage PY - 2012 SN - 1437-9023 VL - 4 SP - 64 EP - 69 PB - ad-media-Verl. CY - Köln AN - OPUS4-26355 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Priebe, Nsesheye Susan A1 - Gluth, Gregor A1 - Sturm, Patrick A1 - Vogler, Nico A1 - Kühne, Hans-Carsten T1 - Comparison of calcined illitic clays (brick clays) and low-grade kaolinitic clays as supplementary cementitious materials N2 - The use of calcined clays as supplementary cementitious materials (SCMs) has been identified as a viable option to decrease the CO2 emissions related to cement production. However, while extensive data is available about kaolinitic clays in this context, other clays such as illitic clays appear to be under-studied. Therefore, in the present study, two illitic clays were compared to two low-grade kaolinitic clays in terms of transformations in the calcination temperature range 650–900 °C, and performance of the calcined clays in blended cement pastes as measured by strength evolution, heat release, hydrated phase formation and portlandite consumption. The illitic clays required a higher calcination temperature for complete dehydroxylation of their illite than what is necessary for dehydroxylation of kaolinite. These higher calcination temperatures also led to particle sintering, significantly decreasing the specific surface area of the illitic clays, particularly for the clay with the higher Fe2O3 content. Nevertheless, while the kaolinitic clays generally exhibited the best performance as SCM, the illitic clay with lower Fe2O3 content performed similar to the kaolinitic clays when calcined at optimum temperature and applied at a moderate substitution rate. These findings demonstrate that several different clays have the potential to be used as SCM and indicate possible routes to identify suitable deposits for this purpose. KW - Blended cement KW - Calcined clay KW - Brick clay KW - Illite KW - Kaolinite PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488195 DO - https://doi.org/10.1617/s11527-019-1393-2 SN - 1359-5997 SN - 1871-6873 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. VL - 52 IS - 5 SP - Article Number 94 PB - Springer Nature AN - OPUS4-48819 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -