TY - JOUR A1 - Vogler, Nico A1 - Drabetzki, Philipp A1 - Lindemann, Mathias A1 - Kühne, Hans-Carsten T1 - Description of the concrete carbonation process with adjusted depth resolved thermogravimetric analysis N2 - The thermal gravimetric analysis (TG) is a common method for the examination of the carbonation progress of cement-based materials. Unfortunately, the thermal properties of some components complicate the evaluation of TG results. Various hydrate phases, like ettringite (AFt), C-S-H and AFm decompose almost simultaneously in the temperature range up to 200 °C. Additionally, physical bound water is released in the same temperature range. In the temperature range between 450 °C and 600 °C the decomposition of calcium hydroxide and amorphous or weakly bound carbonates takes place simultaneously. Carbonates, like calcite, from limestone powder or other additives may be already contained in the noncarbonated sample material. For this research an attempt was made to minimise the influence of these effects. Therefore, differential curves from DTG-results of non-carbonated areas and areas with various states of carbonation of the same sample material were calculated and evaluated. Concretes based on three different types of cement were produced and stored under accelerated carbonation conditions (1 % CO2 in air). The required sample material was obtained by cutting slices from various depth of previously CO2-treated specimen and subsequent grinding. During the sample preparation, a special attention was paid that no additional carbonation processes took place. As reference method for the determination of the carbonation depth the sprayed application of phenolphthalein solution was carried out. Microscopic analysis where examined to confirm the assumptions made previously. Furthermore, the observed effect of encapsulation of calcium hydroxide by carbonates caused by the accelerated carbonation conditions was examined more closely. KW - Microscopy KW - Accelerated carbonation KW - Carbonation behaviour KW - Concrete KW - Thermal Analysis PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-530571 DO - https://doi.org/10.1007/s10973-021-10966-1 VL - 147 IS - 11 SP - 1 EP - 14 PB - Springer AN - OPUS4-53057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grunewald, Thomas A1 - Grätz, Rainer A1 - Kühne, Hans-Carsten T1 - Werkzeuge zur Verwendung in explosionsgefährdeten Bereichen - Erkenntnisse zur Zündwahrscheinlichkeit von Edelstahl und NE-Metallen gegen Baustahl und Estrichbeton in Wasserstoff und Acetylen N2 - Üblicherweise werden Werkzeuge für den industriellen Einsatz aus hochlegierten Chromstählen hergestellt. Für den Einsatz in explosionsgefährdeten Bereichen werden oft Werkzeuge aus speziellen Nichteisen-Metalllegierungen (NE-Metall) verwendet. Für diese sogenannten funkenarmen Werkstoffe und deren mögliche Schlagpartner gibt es bisher keine umfassenden Untersuchungen mit Aussagen zur Zündwahrscheinlichkeit. Die TRGS 723, Abschn. 5.15, fordert den Nachweis der Funkenfreiheit der verwendeten Werkstoffpaarung. Jedoch sind Werkzeuge keine Geräte oder Schutzsysteme im Sinne der Richtlinie 2014/34/EU. Deshalb ist es nicht möglich, Werkzeuge in Übereinstimmung mit dieser Richtlinie zu zertifizieren. Der Nachweis der Erfüllung dieser Anforderungen ist durch Zertifizierungen im sogenannten "gesetzlich nicht geregelten" Bereich möglich. Die BAM bietet diese Zertifizierung für "Funkenarme Werkzeuge" im Rahmen ihres Zertifizierungsprogrammes an. Die bisherigen Ergebnisse der hier vorgestellten Untersuchung haben gezeigt, dass es keine funkenfreien, metallischen Werkzeuge (non-sparking Tools) gibt. Entscheidend ist im Hinblick auf die TRGS 723, ob zündfähige Funken entstehen oder nicht. Es ist immer die Frage, worauf die Werkzeuge im praktischen Anwendungsfall schlagen oder fallen gelassen werden können, d.h. aus welchem Material der mögliche Schlagpartner besteht. Dies können metallische Schlagpartner, aber auch Betonoberflächen sein. Unterschiedliche Kombinationen von Werkstoffen ergeben bei Schlagbeanspruchung im explosionsgefährdeten Bereich jeweils unterschiedliche Zündwahrscheinlichkeiten. Aber auch die Höhe der beim Einsatz der Werkzeuge möglichen kinetischen Schlagenergie und der Brenngas/Luft-Atmosphäre im betreffenden explosionsgefährdeten Bereich sind wichtige Einflussgrößen. KW - Mechanisch erzeugte Funken KW - Nichtelektrische Funken KW - Schlagfunken KW - Schleiffunken KW - Reibfunken KW - Funkenarmes Werkzeug KW - Funkenfreies Werkzeug KW - Nichtelektrischer Explosionsschutz KW - Non sparking tools PY - 2021 DO - https://doi.org/10.37544/2191-0073-2021-11-12-33 SN - 2191-0073 VL - 11 IS - 11-12 SP - 33 EP - 37 PB - VDI Fachmedien CY - Düsseldorf AN - OPUS4-53936 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rogge, Andreas A1 - Meng, Birgit A1 - Kühne, Hans-Carsten T1 - 63. DAfStb-Forschungskolloquium in der BAM - Green Intelligent Building N2 - Das jährlich im Herbst an wechselnden Forschungsstandorten stattfindende DAfStb-Forschungskolloquium wurde im Jahr 2024 von der BAM Bundesanstalt für Materialforschung und -prüfung in Berlin ausgerichtet. Unter der Überschrift „Green Intelligent Building“ referierten rd. 35 Vortragende in fünf Sitzungen unterschiedlicher Thematik über verschiedene betonbezogene Forschungsschwerpunkte in der BAM. Anhand der überwiegend von Doktoranden und Post-Docs dargebotenen Vorträge konnten sich die Teilnehmerinnen und Teilnehmer ein aktuelles Bild von der Qualität der wissenschaftlichen Arbeit und der hervorragenden Forschungsmöglichkeiten in der BAM machen. Durch die Vernetzung unterschiedlich ausgerichteter Fachbereiche innerhalb der BAM werden Synergie-Effekte genutzt. Analytische, baustoffliche, konstruktive, umweltorientierte und auf die Verfahrensentwicklung ausgerichtete Bereiche der BAM forschen gemeinsam zum Thema Stahlbetonbau. Es folgen ausführliche Zusammenfassungen der Tagungsinhalte. T2 - 11. Jahrestagung des DAfStb mit 63. Forschungskolloquium der BAM Green Intelligent Building CY - Berlin, Germany DA - 16.10.2024 KW - Bauteile KW - Bauwerke KW - Beton KW - Chemie der Bindemittel KW - Digitalisierung im Bauwesen KW - Green Intelligent Building KW - Innovative Technologien KW - Klimafreundliche Bindemittel KW - Ressourcenschonung PY - 2025 SN - 0005-9846 VL - 75 IS - 4 SP - 128 EP - 129 PB - concrete content UG CY - Schermbeck AN - OPUS4-63109 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Barthel, Maria A1 - Rübner, Katrin A1 - Kühne, Hans-Carsten A1 - Rogge, Andreas A1 - Dehn, F. T1 - From waste materials to products for use in the cement industry N2 - Industrial wastes (bottom ash, crushed concrete fines, filter residue, paper ash and lignite fly ash) have potential for use in building materials, for instance as raw materials for clinker production, as supplementary cementitious materials (SCMs) or mineral additions in concrete. The properties of the products are dependent on the reactivity of the waste materials used, which can be classified as inert, latent hydraulic or pozzolanic. In this study, waste materials were first characterised. This was followed by theoretical considerations of the mentioned application options. Experiments were limited to evaluation of potential as SCMs and, for this purpose, activity index measurements and calorimetric and thermogravimetric analyses were performed. Finally, the synergetic effects of various waste materials were considered. Paper ash (calcium oxide source) and filter residue (amorphous silicon dioxide source) showed the best prospects for use as cementitious material components. KW - thermal methods KW - blended cements KW - recycled material KW - analysis PY - 2016 DO - https://doi.org/10.1680/jadcr.15.00149 SN - 0951-7197 SP - 1 EP - 11 PB - ICE publishing CY - London, UK AN - OPUS4-36277 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vogler, Nico A1 - Lindemann, Mathias A1 - Drabetzki, Philipp A1 - Kühne, Hans-Carsten T1 - Alternative pH-indicators for determination of carbonation depth on cement-based concretes N2 - The most common method for determination of the carbonation depth is the sprayed application of indicator solutions, Phenolphthalein in particular. Since the aerosols of Phenolphthalein are suspected to be carcinogenic, efforts have been intensified to use alternative indicators for the determination of carbonation depth. The subject and aim of this research paper are to examine indicator solutions from Alizarin Yellow R, Thymol Blue and a Mixed Indicator. These indicator solutions are commercially available and are not suspected to be carcinogenic. For the purpose of this research, samples previously stored under accelerated carbonation conditions (1% CO2) were examined by thermogravimetric analysis (TGA) and examination of the pH value. Additionally, the electrolytic back-titration for determination of total CO2 amount was carried out comparatively to TGA. KW - Thermal analysis KW - Accelerated carbonation KW - pH-indicators KW - Concrete PY - 2020 DO - https://doi.org/10.1016/j.cemconcomp.2020.103565 VL - 109 SP - 1 EP - 9 PB - Elsevier Ltd. AN - OPUS4-50458 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühne, Hans-Carsten A1 - Raupach, M. A1 - Bastert, H. A1 - Eßer, A. A1 - Gehlen, Ch. A1 - Hintzen, W. A1 - Hohberg, I. A1 - Reichling, K. A1 - Westendarp, A. A1 - Wiens, U. A1 - Wolff, L. T1 - Neue Regeln braucht das Land - Die neue Instandhaltungs-Richtlinie des Deutschen Ausschuss für Stahlbeton (DAfStb), Teil 1 N2 - Mit Veröffentlichung der europäischen Normenreihe EN 1504 in den Jahren 2004 bis 2008 mussten in Deutschland die bisherigen nationalen Regelungen für die Instandsetzung von standsicherheitsrelevanten Betonbauteilen angepasst werden. Im vorliegenden Entwurf der neuen Instandhaltungs-Richtlinie wurden die Hinweise zur Planung und Durchführung von Instandsetzungsmaßnahmen aus der Instandsetzungsrichtlinie des DAfStb von 2001 entsprechend überarbeitet und aufgrund neuer Erkenntnisse ergänzt. Außerdem wurde das Regelwerk um Gesichtspunkte der Instandhaltung erweitert, sodass die Aspekte Wartung, Inspektion und Verbesserung nun in Anlehnung an DIN 31051 berücksichtigt werden. Zudem wurden Regelungen aus der ZTV-ING sowie der ZTV-W übernommen. Im ersten Teil dieses Artikels geben wir einen Überblick über die Gliederung und wesentliche neue Inhalte wie die Ausweitung der Instandsetzungsprinzipien. KW - Betoninstandsetzung PY - 2016 SN - 2190-9504 VL - 39. Jahrgang IS - 2.2016 SP - 16 EP - 23 PB - Verlagsgesellschaft Rudolf Müller GmbH & Co. KG CY - Köln AN - OPUS4-37167 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühne, Hans-Carsten A1 - Raupach, M. A1 - Bastert, H. A1 - Eßer, A. A1 - Gehlen, Ch. A1 - Hintzen, W. A1 - Hohberg, I. A1 - Reichling, K A1 - Westendarp, A. A1 - Wiens, U. A1 - Wolff, L. T1 - Das Bauwerk stellt die Anforderungen - Die neue Instandhaltungs-Richtlinie des Deutschen Ausschusses für Stahlbeton (DAfStb), Teil 2 N2 - In einer Artikelserie stellen wir die neue Instandhaltungs-Richtlinie des Deutschen Ausschusses für Stahlbeton (DAfStb) vor. Im zweiten Teil geht es um Betonersatz- und Oberflächenschutzsysteme sowie Rissfüllstoffe. Es werden als Folge des EuGH-Urteils vom Oktober 2014 zukünftig keine Anforderungen an Bauprodukte mit dem Nachweis über allgemeine bauaufsichtliche Prüfzeugnisse gestellt. Stattdessen werden auf Basis der Anforderungen individueller Bauwerke notwendige Merkmale von Bauprodukten für die Instandsetzung definiert. Außerdem wird Teil 3 der neuen Instandhaltungs-Richtlinie "Ausführung der Instandsetzung und Überwachung" vorgestellt. Neu ist hier die Einführung von Überwachungsklassen, die sich aus der Art des instand zu setzenden Betonbauteils (standsicherheitsrelevant oder nicht) und der auszuführenden Arbeiten ergeben, zum Beispiel Instandsetzung oder Verstärkung. Am Ende dieses Artikels wird kurz der 4. Teil der neuen Instandhaltungs-Richtlinie erläutert. KW - Betoninstandsetzung PY - 2016 SN - 2190-9504 VL - 39. Jahrgang IS - 3.2016 SP - 51 EP - 55 PB - Verlagsgesellschaft Rudolf Müller GmbH & Co. KG CY - Köln AN - OPUS4-37168 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sander, C. A1 - Kühne, Hans-Carsten A1 - Ünal, Murat A1 - Kleine, M. A1 - Köhler, A. A1 - Kriesten, V. T1 - Betondickglasfenster - Schadensmechanismen und Instandsetzungsprinzipien zur Erhaltung N2 - Errichtet aus Glas und Beton prägen heute unzählige Sakralbauten der 1950er- und 60er-Jahre unsere Stadtbilder. Nicht selten sind in diesen Kirchen erhebliche Schäden an den Betonglasfenstern zu verzeichnen. Diese fachgemäß zu erhalten, erfordert spezielles technisches und denkmalpflegerisches Know-how. An der Entwicklung geeigneter Instandsetzungsstrategien arbeitet derzeit ein interdisziplinäres Projektteam. KW - Betonglasrestaurierung KW - Schadensmechanismen KW - Instandsetzungsprinzipien KW - Glass KW - (Reinforced) concrete KW - Church windows KW - Churches KW - Structural analysis KW - Concrete block technique KW - Reinforcement KW - Dalle de verre PY - 2011 SN - 0933-4017 VL - 7 SP - 48 EP - 53 PB - Callwey CY - München AN - OPUS4-24834 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ramge, Peter A1 - Kühne, Hans-Carsten A1 - Meng, Birgit T1 - Development of a modular system for the protection and repair of concrete structures KW - Repair mortar KW - Repair systems KW - Polymer cement concrete (PCC) KW - Sprayed polymer cement concrete (SPCC) PY - 2010 SN - 1864-7251 SN - 0947-4498 VL - 16 IS - 4/5 SP - 387 EP - 400 PB - Aedificatio Publ. CY - Freiburg AN - OPUS4-22773 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ramge, Peter A1 - Kühne, Hans-Carsten A1 - Meng, Birgit T1 - Einfluss ausgewählter Modifikationen der Mischungszusammensetzung auf die Eigenschaften von Instandsetzungsmörteln N2 - Trotz der zahlreichen Möglichkeiten zur Beeinflussung der Mörteleigenschaften durch Mischungsmodifikationen ist es nahezu unmöglich, einzelne Eigenschaften unabhängig von anderen zu verändern. Bei einer Mischungsoptimierung muss im Einzelfall immer entschieden werden, welcher der gewünschten Eigenschaften die höchste Priorität zukommt. Anhand von Parameterstudien wird im vorliegenden Artikel verdeutlicht, wie es für bestimmte Anwendungen sinnvoll sein kann, die Verschlechterung einzelner Eigenschaften zu akzeptieren, wenn dadurch eine für den speziellen Einsatzfall essenzielle Eigenschaft verbessert werden kann. Die komplexen Wechselwirkungen der einzelnen Bestandteile fuhren dazu, dass auch scheinbar widersprüchliche Kombinationen von Zusatzmitteln im Einzelfall erforderlich werden können. Zur Anpassung der meisten Mörteleigenschaften gibt es verschiedene Möglichkeiten der Zielerreichung mit jeweils unterschiedlichen Nebeneffekten. Frisch- und Festmörteleigenschaften sind dabei gleichermaßen zu beachten. KW - Instandsetzungsmörtel KW - Betoninstandsetzung KW - Instandsetzungssysteme KW - Polymer-Zement Beton (PCC) KW - Polymer-Zement Spritzbeton (SPCC) KW - Repair mortar KW - Concrete rehabilitation KW - Repair systems KW - Polymer cement concrete (PCC) KW - Sprayed polymer cement concrete (SPCC) PY - 2011 SN - 1864-7251 SN - 0947-4498 VL - 17 IS - 3/4 SP - 169 EP - 180 PB - Aedificatio Publ. CY - Freiburg AN - OPUS4-24479 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hüsken, Götz A1 - Shamsuddoha, Md A1 - Pirskawetz, Stephan A1 - Hofmann, Detlef A1 - Baeßler, Matthias A1 - Kühne, Hans-Carsten T1 - Potential of a Repair System for Grouted Connections in Offshore Structures: Development and Experimental Verification N2 - Grouted connections are intensively used in offshore rigs, platforms as well as jacket and monopile offshore wind turbine structures. Being located in remote offshore conditions, these connections can experience considerable adverse loading during their lifetimes. Degradation was reported inside similar connections, which were installed in the last three decades. Grouting in the offshore sites may often be proven difficult, which eventually leads to reduced load-bearing capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs. In this study, scaled grouted connections were manufactured using a novel mould, whose integrity were monitored using digital image correlation (DIC). The connections were loaded under static load to visualize the main failure pattern using distributed fibre optic sensors and acoustic emission (AE) analysis. Grouted connections were then repaired using a cementitious injectable grout. The effectiveness of the grout injection was monitored using dye penetration technique. Finally, specimens are reloaded to identify the potential of such repair for grouted connections. KW - Offshore KW - Grouted connection KW - Fibre optic sensors KW - Acoustic emission analysis KW - Cracks KW - Repair KW - Rehabilitation KW - Static loading PY - 2021 DO - https://doi.org/10.1016/j.marstruc.2021.102934 VL - 77 SP - 102934 PB - Elsevier Ltd. AN - OPUS4-52059 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühne, Hans-Carsten T1 - Handlungshilfe zur Betoninstandsetzung N2 - Die TR Instandhaltung des Deutschen Instituts für Bautechnik wird als maßgebliches Bezugswerk der Betoninstandsetzung ür die Fachöffentlichkeit hinsichtlich ihrer Inhalte und Zielrichtung vorgestellt KW - Beton KW - Instandsetzung KW - Technische Regel KW - Planung KW - Ausführung KW - DIBt PY - 2021 UR - https://www.ingenieur.de/fachmedien/bauingenieur/ PB - VDI Fachmedien GmbH & Co. KG Unternehmen für Fachinformationen CY - Düsseldorf AN - OPUS4-52117 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lay, Vera A1 - Baensch, Franziska A1 - Skłodowska, Anna A1 - Fritsch, Tobias A1 - Stamm, Michael A1 - Prabhakara, Prathik A1 - Johann, Sergej A1 - Sturm, Patrick A1 - Kühne, Hans-Carsten A1 - Niederleithinger, Ernst T1 - Multi–sensory Monitoring and Non–destructive Testing of New Materials for Concrete Engineered Barrier Systems N2 - The crucial part of nuclear waste storage is the construction of sealing structures made of reliable, safe and well–understood materials. We present an extended analysis of long-term multi–sensory monitoring and non–destructive testing (NDT) inspection of two laboratory specimens aiming at potential materials for sealing structures for nuclear waste repositories. Specimens with a volume of 340 litres made from newly developed alkali–activated materials (AAM) and established salt concrete (SC) were analysed using embedded acoustic emission and wireless radio-frequency identification (RFID) sensors, ultrasonic echo imaging, active thermography, and X–ray computed tomography. The monitoring analysis showed lower heat of reaction and 50% less acoustic emission events in AAM compared to SC. However, due to the surface effects of the AAM material, the number of acoustic emission events increased significantly after approximately two months of monitoring. Subsequently performed NDT inspections reliably located embedded sensors and confirmed the absence of major cracks or impurities. The presented laboratory results show the feasibility and potential of comprehensive NDT monitoring and inspection to characterise cementitious and alternative materials as well as the need for multi–parameter long–term monitoring. Thus, our study demonstrates that tailored NDT investigations will help to develop safe sealing structures for nuclear waste repositories. KW - Radioactive waste KW - Barrier KW - Concrete KW - AAM KW - Non-destructive testing PY - 2024 DO - https://doi.org/10.3151/jact.22.516 SN - 1347-3913 VL - 22 IS - 9 SP - 516 EP - 529 PB - Japan Concrete Institute AN - OPUS4-61461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ramge, P. A1 - Kühne, Hans-Carsten T1 - Die Mischung macht's, Modulare Ersatzmassen zur Reprofilierung von Natursteinbauwerken N2 - Die Herausforderung einer anspruchsvollen Natursteininstandsetzung liegt in der richtigen Zusammensatzung der Steinersatzmassen. Dabei müssen vielerlei, teilweise gegenläufige Interessen miteinander vereinbart werden: Mechanische und bauphysikalische Belange müssen genauso beachtet werden wie denkmalpflegerische und gestalterische Aspekte. Auf die konkreten Anforderungen und Voraussetzungen einer Restaurierungsaufgabe reagieren zu können, ist die Grundvoraussetzung für ein gutes Gelingen. Hilfreich sind hier Mischungen, die modular aufgebaut sind und sich individuell und flexibel an die Erfordernisse anpassen lassen. PY - 2015 SN - 2190-9504 VL - 38 IS - 2 SP - 38 EP - 43 PB - Müller CY - Köln AN - OPUS4-34607 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bastert, H. A1 - Dickhaut, D. A1 - Eßer, A. A1 - Hintzen, W. A1 - Hohberg, I. A1 - Kühne, Hans-Carsten A1 - Kühner, S. A1 - Meyer, L. A1 - Raupach, M. A1 - Westendarp, A. A1 - Wiens, U. T1 - Überarbeitung der DAfStb-Richtlinie Instandsetzung - Statusbericht N2 - Derzeit erfolgt in mehreren Arbeitsgruppen unter Einbindung interessierter Kreise die Überarbeitung der 2001 erschienenen Richtlinie 'Schutz und Instandsetzung von Betonbauteilen' (Instandsetzungsrichtlinie) des Deutschen Ausschusses für Stahlbeton e.V. (DAfStb). Hierüber wird in dem nachfolgenden Beitrag berichtet, um der Fachwelt frühzeitig darzustellen, in welche Richtung die Fortschreibung des Regelwerkes geplant ist. Die geplante neue Richtlinie wird nach derzeitigem Beratungsstand eine deutliche inhaltliche Erweiterung erfahren. Daher wird sie in 'Richtlinie für die Instandhaltung von Betonbauteilen' (Instandhaltungsrichtlinie) umbenannt und wird Festlegungen zu der grundsätzlichen Vorgehensweise bei der Instandhaltung unter Berücksichtigung der Komponenten Wartung, Inspektion, Instandsetzung und Verbesserung in Anlehnung an DIN 31051 enthalten. Da diese umfassenderen Aufgaben deutlich präziser beschrieben werden, konkretisieren sich auch die Anforderungen an die erforderliche Qualifikation des sachkundigen Planers, der zukünftig verstärkt die 'Restnutzungsdauer' bei seiner Planung beachten und in entsprechende Maßnahmen umsetzen muss. Mit den Ergänzungen und Änderungen wird die Richtlinie an die aktuellen Entwicklungen und Regelungen im Betonbau angepasst. Gleichzeitig gewinnt die Planungsleistung erheblich an Bedeutung. Für Instandsetzungsprodukte gemäß DIN EN 1504 werden, die Beseitigung derzeit noch enthaltener Unklarheiten und technischer Defizite auf europäischer Ebene vorausgesetzt, Verwendbarkeitsmöglichkeiten aufgezeigt. Die Ausführung von Instandhaltungsmaßnahmen wird durch die Einführung von Überwachungsklassen mit zugehörigen Anforderungen an die durchzuführenden Prüfungen spezifiziert und damit konkretisiert. KW - Betoninstandsetzung KW - DIN EN 1504 KW - Europäische Normungsarbeit KW - Instandsetzungsmörtel KW - Oberflächenschutzsysteme PY - 2011 DO - https://doi.org/10.1002/best.201008258 SN - 0005-9900 SN - 1437-1006 VL - 106 IS - 7 SP - 501 EP - 510 PB - Ernst CY - Berlin AN - OPUS4-24342 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hüsken, Götz A1 - Pirskawetz, Stephan A1 - Meinel, Dietmar A1 - Babski, Veronika A1 - Kühne, Hans-Carsten T1 - Methoden zur Analyse des Bruchverhaltens hochfester Stahlfaserbetone N2 - Hochfeste und ultrahochfeste Stahlfaserbetone eignen sich aufgrund ihrer Eigenschaften für den Einsatz bei extremen mechanischen Beanspruchungen. Das für diesen Einsatz erforderliche duktile Bruchverhalten unter Zugbeanspruchung wird ausschließlich durch die Zugabe von geeigneten Stahlfasern und deren Wirkung in der Zementsteinmatrix erreicht. Für eine gezielte stoffliche Optimierung des Systems sind fundierte Kenntnisse zur Wirkungsweise der Stahlfasern notwendig, die bei bisherigen Untersuchungen lediglich auf Basis von klassischen Messverfahren zerstörender Prüfungen gewonnen wurden. Durch das Einbeziehen von Methoden der zerstörungsfreien Materialcharakterisierung können das Bruchverhalten hochfester und ultrahochfester Stahlfaserbetone orts- und zeitaufgelöst untersucht und die einzelnen Phasen des Schädigungsprozesses identifiziert werden. Anhand der vorliegenden Ergebnisse von Zugversuchen eines ultrahochfesten Stahlfaserbetons wird der kombinierte Einsatz von Methoden der zerstörungsfreien Materialprüfung gezeigt und deren Anwendbarkeit in der Analyse des Bruchverhaltens diskutiert. Das Hauptaugenmerk liegt dabei auf der Charakterisierung der ausschlaggebenden Versagensmodi unter Zugbelastung durch die einzelnen Verfahren und dem Vergleich zu klassischen Messmethoden (z. B. Extensometer). Die Zugversuche wurden dazu parallel durch optische Verformungsanalyse mittels Bildkorrelation (DIC), Schallemissionsanalyse (SEA) und 3-D-Computertomografie (CT) begleitet. KW - Stahlfaserbeton KW - Zugbeanspruchung KW - Optische Verformungsanalyse KW - Schallemission KW - Computertomografie PY - 2016 DO - https://doi.org/10.1002/bate.201600056 SN - 1437-0999 VL - 93 IS - 10 SP - 711 EP - 716 PB - Ernst & Sohn CY - Berlin AN - OPUS4-37767 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Westendarp, A. A1 - Reschke, T. A1 - Kühne, Hans-Carsten A1 - Maultzsch, Matthias A1 - Dauberschmidt, C. A1 - Rößler, G. T1 - Instandsetzung von Wasserbauwerken aus Beton; Teil 2 KW - Instandsetzung KW - Beton KW - Wasserbau KW - Spritzmörtel KW - Geringer fester Beton KW - ZTV-LB 219 PY - 2006 SN - 0005-9846 VL - 55 IS - 3 SP - 94 EP - 100 PB - Verlag Bau + Technik CY - Erkrath AN - OPUS4-12347 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Westendarp, A. A1 - Reschke, T. A1 - Kühne, Hans-Carsten A1 - Maultzsch, Matthias A1 - Dauberschmidt, C. A1 - Rößler, G. T1 - Instandsetzung von Wasserbauwerken aus Beton; Teil 1 KW - Instandsetzung KW - Beton KW - Wasserbau KW - Spritzmörtel KW - Geringer fester Beton KW - ZTV-LB 219 PY - 2006 SN - 0005-9846 VL - 56 IS - 1+2 SP - 22 EP - 29 PB - Verlag Bau + Technik CY - Erkrath AN - OPUS4-12348 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fontana, Patrick A1 - Lehmann, Christian A1 - Müller, Urs A1 - Kühne, Hans-Carsten A1 - Meng, Birgit A1 - Rogge, Andreas T1 - Wärmebehandlung und Autoklavierung von UHPC - Neue Perspektiven für die Betonfertigteilindustrie T1 - Heat curing and autoclaving of UHPC - New perspectives for the precast concrete industry N2 - Das Gefüge von UHPC ist durch eine dicht gepackte und fehlstellenarme Matrix gekennzeichnet. Eine zusätzliche Optimierung ist durch eine Wärmebehandlung bzw. hydrothermale Nachbehandlung (Autoklavierung) unter einem Wasserdampfsättigungsdruck möglich. Die Wärmebehandlung von Beton ist ein in der Betonfertigteilindustrie geläufiges Verfahren, um die Erstarrungszeit zu verkürzen und höhere Frühfestigkeiten zu erreichen. N2 - The structure of UHPC is characterized by a densely packed matrix with only a small number of voids; it can be enhanced further by heat curing or hydrothermal Treatment (autoclaving) subject to water vapor pressure. Heat curing of concrete is commonly applied in the precast industry in Order to shorten its setting time and achieve higher early strengths. KW - Ultrahochleistungsbeton KW - Stahlfasern KW - Nachbehandlung KW - Mikrostruktur KW - Festigkeit PY - 2011 SN - 0373-4331 SN - 1865-6528 N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 77 IS - 10 SP - 46 EP - 47 PB - Bauverl. CY - Gütersloh AN - OPUS4-24838 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vasilic, Ksenija A1 - Meng, Birgit A1 - Kühne, Hans-Carsten A1 - Roussel, N. T1 - Flow of fresh concrete through steel bars: a porous medium analogy N2 - Although being a very promising area of concrete technology, computational modeling of fresh concrete flow is a comprehensive and time consuming task. The complexity and required computation time are additionally increased when simulating casting of heavily reinforced sections, where each single reinforcement bar has to be modeled. In order to improve the computation speed and to get closer to a practical tool for simulation of casting processes, an innovative approach to model reinforced sections is proposed here. The basic idea of this approach is to treat the reinforcement zone as a porous medium in which a concrete is propagating. In the present paper, the numerical implementation of this concept is described. A methodology allowing for the computation of the equivalent permeability of the steel bars network is suggested. Finally, this numerical technique efficiency is evaluated by a comparison with experimental results of model fluids casting in model formworks. KW - Fresh concrete (A) KW - Rheology (A) KW - Modeling (E) KW - Permeability (C) KW - Yield stress KW - Simulation KW - Flow of mortar KW - Flow of concrete PY - 2011 DO - https://doi.org/10.1016/j.cemconres.2011.01.013 SN - 0008-8846 SN - 1873-3948 VL - 41 IS - 5 SP - 496 EP - 503 PB - Pergamon Press CY - New York, NY AN - OPUS4-25532 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -