TY - JOUR A1 - Schartel, Bernhard A1 - Kühn, Gerhard A1 - Mix, Renate A1 - Friedrich, Jörg Florian T1 - Surface Controlled Fire Retardancy of Polymers Using Plasma Polymerisation JF - Macromolecular materials and engineering N2 - Communication: Fire retardant coatings are deposited on polyamide-66 using plasma polymerisation. Chemical composition and thickness of deposits are adjusted varying the plasma treatment based on hexamethydisiloxane mixed with oxygen. The fire retardancy performances are evaluated using a cone calorimeter. The correlation between fire retardancy and thickness as well as chemical composition is discussed. KW - Cone calorimeter KW - Flame retardance KW - Heat release KW - Plasma polymerization KW - Polyamides PY - 2002 DO - https://doi.org/10.1002/1439-2054(20020901)287:9<579::AID-MAME579>3.0.CO;2-6 SN - 1438-7492 SN - 1439-2054 VL - 287 IS - 9 SP - 579 EP - 582 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-1537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühn, Gerhard A1 - Weidner, Steffen A1 - Decker, Renate A1 - Ghode, Archana A1 - Friedrich, Jörg Florian T1 - Selective surface functionalization of polyolefins by plasma treatment followed by chemical reduction JF - Surface and coatings technology N2 - Polymer surfaces can be finished with functional groups upon exposure to a plasma. Species of the plasma gas are attached at surface carbon atoms, forming functional groups of different composition. To produce a modified polymer surface with a high density and homogeneity of hydroxyl groups only, the oxygen-plasma-formed oxygen functional groups were chemically reduced by diborane and LiAlH4 with yields of 10 to 11 OH groups per 100 carbon atoms in the 3 to 5 nm near-surface layer as detected by X-ray photoelectron spectroscopy (XPS). The identification of hydroxyl groups was performed by means of attenuated total reflectance–Fourier transform infrared spectroscopy and XPS. KW - Attenuated total reflectance-Fourier transorm infrared spectroscopy KW - Chemical reduction of functional groups KW - Plasma modification KW - X-ray photoelectron spectroscopy PY - 1999 DO - https://doi.org/10.1016/S0257-8972(99)00232-7 SN - 0257-8972 VL - 116-119 SP - 796 EP - 801 PB - Elsevier Science CY - Lausanne AN - OPUS4-6983 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Mix, Renate A1 - Fritz, Andreas A1 - Schönhals, Andreas T1 - Polymer surface modification with monofunctional groups of variable types and densities JF - Journal of adhesion science and technology N2 - The retention of chemical structure and functional groups during pulsed plasma polymerization was used for producing adhesion-promoting plasma polymer layers with high concentrations of exclusively one kind of functional groups, such as OH, NH2, or COOH. The maximum content of functional groups was 31 OH using allyl alcohol, 18 NH2 using allylamine, or 24 COOH per 100 C atoms using acrylic acid. To vary the density of functional groups, chemical co-polymerization with ethylene as 'chain-extending' co-monomer, or butadiene as 'chemical crosslinker' was initiated in the pulsed plasma. The composition of these co-polymers was investigated by XPS and IR spectroscopy. The concentrations of functional groups were measured by derivatizing with fluorine-containing reagents and using XPS. A set of plasma parameters was found to be a good compromise between a high number of functional groups and complete insolubility in water, ethanol or THF,which is needed for further chemical processing. Here, these monotype-functionalized surfaces were used in metal-polymer systems as adhesion-promoting interlayers to examine the influence of type and density of functional groups on adhesion. As expected, COOH- and OH-group-terminated interlayers showed maximum peel strengths to evaporated aluminium layers. The adhesion increased linearly with the number of OH groups to a maximum at about 27 OH per 100 C atoms. Higher concentrations of OH groups did not increase the peel strength further. KW - Co-polymers KW - Adhesion-promoting interlayers KW - Metal-polymer systems PY - 2003 DO - https://doi.org/10.1163/156856103322396695 SN - 0169-4243 SN - 1568-5616 VL - 17 IS - 12 SP - 1591 EP - 1617 PB - VNU Science Press CY - Utrecht AN - OPUS4-2704 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian A1 - Unger, Wolfgang A1 - Lippitz, Andreas T1 - Plasmaoxidative Degradation of Polymers Studied by Matrix-assisted Laser Desorption/Ionization Mass Spectrometry JF - Rapid communications in mass spectrometry PY - 1996 SN - 0951-4198 SN - 1097-0231 VL - 10 SP - 727 EP - 732 PB - Wiley CY - Chichester AN - OPUS4-7004 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wettmarshausen, Sascha A1 - Kühn, Gerhard A1 - Hidde, Gundula A1 - Mittmann, Hans-Ulrich A1 - Friedrich, Jörg Florian T1 - Plasmabromination - the Selective Way to Monotype Functionalized Polymer Surfaces JF - Plasma processes and polymers N2 - In contrast to other plasma modification processes of polymer surfaces, the bromination is very selective and shows a high yield in C—Br groups. The most convenient bromination process was found using bromoform, which was thus preferred to elemental bromine, allyl bromide, vinyl bromide or tert-butylbromide. The bromoform process give yields in C—Br up to 40 C—Br or more, with only 2-3% co-introduction of O-functionalities whereas allyl bromide results in yields of about 20 C—Br and more, but in more than 10% oxygen-containing by-products. C—Br groups serve as anchoring points for grafting of molecules, oligomers and pre-polymers of diole or diamine character. KW - Functional groups KW - Grafting KW - Plasma bromination KW - Polymer surfaces KW - Selective plasma process KW - Spacer PY - 2007 DO - https://doi.org/10.1002/ppap.200700019 SN - 1612-8850 SN - 1612-8869 VL - 4 IS - 9 SP - 832 EP - 839 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-16209 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Retzko, Iris A1 - Kühn, Gerhard A1 - Unger, Wolfgang A1 - Lippitz, Andreas T1 - Plasma polymers with chemically defined structures in contact with metals JF - Surface and coatings technology N2 - The retention of chemical structure and functional groups during plasma polymerization was investigated. Usually plasma polymer layers, prepared by a continuous wave radio-frequency plasma, are often chemically irregular in their structure and composition. To minimize these irregularities low wattages and the pulsed plasma technique were applied to avoid fragmentations. The first goal was to produce plasma polymers comprising double or triple bonds as precursors for electrically conducting polymers. Acetylene, ethylene, butadiene and polystyrene were used as monomers and deposited as thin polymer films by pulsed plasmas of low wattages. Styrene polymerization was strongly enhanced in the dark phase (plasma off) of a pulsed r.f. plasma caused by the reactivity of the vinyl-type double bond. This could be confirmed by a verification of a rather high chemical regularity of the film sample. The oxygen content of this film measured by X-ray photoelectron spectrometry (XPS) was in situ 0% and after 24 h exposure to air lower than 1%. Additionally, post-plasma oxidations of trapped radicals with air could be suppressed using NO gas as radical quencher. Such quenched plasma polymer layers were completely stable against oxidation for a number of weeks. During the low-wattage pulse plasma polymerization metal atoms were simultaneously or layer by layer evaporated into the growing layer and in situ measured by XPS. These metal atoms are acting as dopants. Here, Li, K, Mg and Cr were used at different concentrations providing electrical conductivity and magnetic properties for the film. KW - Pulsed plasma KW - Plasma polymerization KW - Doping with metal atoms KW - Encapsulation of nanoparticles PY - 2001 DO - https://doi.org/10.1016/S0257-8972(01)01051-9 SN - 0257-8972 VL - 142-144 SP - 460 EP - 467 PB - Elsevier Science CY - Lausanne AN - OPUS4-6972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gross, Thomas A1 - Kühn, Gerhard A1 - Unger, Wolfgang T1 - Photoelectron spectroscopy on organic surfaces: X-ray degradation of oxygen-plasma-treated and chemically reduced poly(propylene) surfaces in comparison to conventional polymers JF - Surface and interface analysis N2 - The X-ray-induced sample damage during mono XPS analysis of an oxygen-plasma-oxidized and subsequently wet-chemically reduced poly(propylene) film was investigated as a showcase for plasma-modified or plasma-deposited samples. By doing this, the degradation index approach as introduced by Beamson and Briggs in the Scienta ESCA300 high-resolution XPS database of organic polymers has been adopted. As to be expected, the sample degrades by loosing oxygen as revealed by observation of decreasing O/C and COR/Csum ratios. However, the X-ray degradation indices are definitely higher than those of conventional reference polymers. Moreover, the COR/Csum degradation index is significantly higher in comparison with one obtained for the O/C ratio. In that context, there is no difference between the plasma sample and a conventional poly(vinyl alcohol) polymer. It is concluded that for reliable quantitative surface chemical analysis, the quality of spectra in terms of acquisition times must be optimized aimed to a minimization of X-ray degradation. Finally, it is proposed to describe the photon flux of an X-ray gun in an XPS experiment, which defines the degradation rate at the end, by using the sample current simply measured with a carefully grounded sputter-cleaned reference silver sample. KW - Photoelectron spectroscopy KW - ESCA/XPS KW - Surfaces KW - Surface modification KW - Poly(propylene) (PP) KW - Plasma treatment KW - X-ray KW - Degradation PY - 2009 DO - https://doi.org/10.1002/sia.3024 SN - 0142-2421 SN - 1096-9918 VL - 41 IS - 5 SP - 445 EP - 448 PB - Wiley CY - Chichester AN - OPUS4-19252 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Unger, Wolfgang A1 - Lippitz, Andreas A1 - Geng, Sh. A1 - Koprinarov, Ivaylo A1 - Kühn, Gerhard A1 - Weidner, Steffen T1 - Modelling plasma-induced reactions on polymer surfaces using aliphatic self-assembling and LB layers JF - Surface and coatings technology PY - 1998 SN - 0257-8972 VL - 98 SP - 1132 EP - 1141 PB - Elsevier Science CY - Lausanne AN - OPUS4-6999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Holländer, A. A1 - Kühn, Gerhard T1 - Matrix-assisted Laser Desorption/Ionization Mass Spectrometry of C36- Alkane degradated by Vacuum Ultraviolet Radiation JF - Rapid communications in mass spectrometry PY - 1997 SN - 0951-4198 SN - 1097-0231 VL - 11 SP - 447 EP - 450 PB - Wiley CY - Chichester AN - OPUS4-11095 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian T1 - Infrared-Matrix-assisted Laser Desorption/Ionization and Infrared-Laser Desorption/Ionization Investigations of Synthetic Polymers JF - Rapid communications in mass spectrometry PY - 1998 SN - 0951-4198 SN - 1097-0231 VL - 12 SP - 1373 EP - 1381 PB - Wiley CY - Chichester AN - OPUS4-6988 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -