TY - JOUR A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Mix, Renate A1 - Unger, Wolfgang T1 - Formation of Plasma Polymer Layers with Functional Groups of Different Type and Density at Polymer Surfaces and their Interaction with Al Atoms N2 - Monotype functionalizations with different types of functional groups (OH, NH2, COOH) on polypropylene and poly(tetrafluoroethylene) surfaces were synthesized using pulsed plasma-initiated homo- or copolymerization of functional group-carrying monomers. The maximum concentrations of functional groups were 31 OH, 18 NH2 or 24 COOH groups per 100 C atoms using allyl alcohol, allylamine or acrylic acid respectively as the monomer. The measured peel strengths of aluminium deposits increased linearly with the concentration of functional groups. Near the maximum concentration of OH (>27 OH/100 C atoms) or at moderate concentrations of COOH groups (>10 COOH/100 C atoms), constant (maximum) peel strengths were measured due to the mechanical collapse of one component in the composite (cohesive failure). Interface failures in Al-PP composites were found with COOH, NH2 and OH groups and cohesive failures were seen when higher concentrations of COOH groups were applied (>10 COOH/100 C atoms). PY - 2004 DO - https://doi.org/10.1002/ppap.200400008 SN - 1612-8850 SN - 1612-8869 VL - 1 IS - 1 SP - 28 EP - 50 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-4707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Mix, Renate A1 - Kühn, Gerhard T1 - Contribution of chemical interactions to the adhesion between aluminium and functional groups of different (mono-) type and density at polymer surfaces T2 - 7th European Adhesion Conference (EURADH 2004) CY - Freiburg im Breisgau, Germany DA - 2004-09-07 PY - 2004 VL - 1 SP - 138 EP - 143 PB - DECHEMA CY - Frankfurt am Main AN - OPUS4-4680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Unger, Wolfgang A1 - Mix, Renate ED - Radusch, H.-J. ED - Fiedler, L. T1 - Plasma-initiated homo and copolymerisation for modifying polymer surfaces with funtional groups of different type and density T2 - Internationale Fachtagung Polymerwerkstoffe ; P-2002 CY - Halle (Saale), Germany DA - 2002-09-25 PY - 2002 SN - 3-86010-656-2 SP - 534 EP - 539 PB - Martin-Luther-Univ. Halle-Wittenberg CY - Halle (Saale) AN - OPUS4-6969 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Mix, Renate A1 - Kühn, Gerhard A1 - Unger, Wolfgang T1 - Functional groups bearing plasma homo and copolymer layers as adhesion promoters in metal-polymer composites T2 - 10. Neues Dresdner Vakuumtechnisches Kolloquium (NDVaK) CY - Dresden, Germany DA - 2002-10-17 PY - 2002 SP - 6 EP - 15 PB - DTVa CY - Dresden AN - OPUS4-6970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühn, Gerhard A1 - Retzko, Iris A1 - Lippitz, Andreas A1 - Unger, Wolfgang A1 - Friedrich, Jörg Florian T1 - Homofunctionalized polymer surfaces formed by selective plasma processes N2 - Several possibilities exist to produce a modified polymer surface with a high density of only one sort of functional group such as: (i) the plasma grafting of unfragmented monomer molecules and their polymerization forms OH, NH2, COOH groups, etc. in concentrations of approximately 25 groups per 100 C atoms; (ii) selective plasma bromination provides 10–25 CBr groups; (iii) the plasma oxidation of polymer surfaces in an O2 plasma followed by the chemical reduction of all O-containing groups to OH groups by diborane, vitride™ (Na complex) or LiAlH4 yields 9–14 OH groups per 100 carbon atoms; and (iv) the grafting of spacers with different endgroups onto OH or CBr groups produces 7–10 spacer molecules/100 C. This work was focused on the formation of thin plasma deposited polymer layers with a maximum of (homo)functional groups and with a minimum of chemical irregularities using the pulsed plasma technique. The monomers were allylalcohol, allylamine, acrylonitrile and acrylic acid. The further intent was to study the interactions of functional groups (OH, COOH, NH2) and deposited metals (Cr, Al, Ti). It was expected that more basic (NH2), weakly basic or neutral (OH) or more acidic (COOH) groups would show different interactions and chemical reactions with metal atoms. KW - Pulsed plasma polymerization KW - Functional groups KW - Long-term stability KW - Polymer-metal composites PY - 2001 DO - https://doi.org/10.1016/S0257-8972(01)01056-8 SN - 0257-8972 VL - 142-144 SP - 494 EP - 500 PB - Elsevier Science CY - Lausanne AN - OPUS4-6971 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Retzko, Iris A1 - Kühn, Gerhard A1 - Unger, Wolfgang A1 - Lippitz, Andreas T1 - Plasma polymers with chemically defined structures in contact with metals N2 - The retention of chemical structure and functional groups during plasma polymerization was investigated. Usually plasma polymer layers, prepared by a continuous wave radio-frequency plasma, are often chemically irregular in their structure and composition. To minimize these irregularities low wattages and the pulsed plasma technique were applied to avoid fragmentations. The first goal was to produce plasma polymers comprising double or triple bonds as precursors for electrically conducting polymers. Acetylene, ethylene, butadiene and polystyrene were used as monomers and deposited as thin polymer films by pulsed plasmas of low wattages. Styrene polymerization was strongly enhanced in the dark phase (plasma off) of a pulsed r.f. plasma caused by the reactivity of the vinyl-type double bond. This could be confirmed by a verification of a rather high chemical regularity of the film sample. The oxygen content of this film measured by X-ray photoelectron spectrometry (XPS) was in situ 0% and after 24 h exposure to air lower than 1%. Additionally, post-plasma oxidations of trapped radicals with air could be suppressed using NO gas as radical quencher. Such quenched plasma polymer layers were completely stable against oxidation for a number of weeks. During the low-wattage pulse plasma polymerization metal atoms were simultaneously or layer by layer evaporated into the growing layer and in situ measured by XPS. These metal atoms are acting as dopants. Here, Li, K, Mg and Cr were used at different concentrations providing electrical conductivity and magnetic properties for the film. KW - Pulsed plasma KW - Plasma polymerization KW - Doping with metal atoms KW - Encapsulation of nanoparticles PY - 2001 DO - https://doi.org/10.1016/S0257-8972(01)01051-9 SN - 0257-8972 VL - 142-144 SP - 460 EP - 467 PB - Elsevier Science CY - Lausanne AN - OPUS4-6972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Möller, B. A1 - Kühn, Gerhard A1 - Unger, Wolfgang A1 - Krüger, P. T1 - Improvement of adhesion properties of polymers by producing oxyfluorinated surfaces PY - 2001 SN - 0016-4232 VL - 92 IS - 5 SP - 1334 EP - 1444 PB - Leuze CY - Saulgau, Württ. AN - OPUS4-6973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Mix, Renate ED - D'Agostino, R. T1 - Polymer Surface Modification with Monofunctional Groups of Different Type and Density T2 - 16th International Symposium on Plasma Chemistry ; ISPC-16 CY - Taormina, Italy DA - 2003-06-22 PY - 2005 SN - 3-527-40487-2 SP - 3 EP - 21 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-7019 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Mix, Renate T1 - Tailoring of Polymer Surfaces with Different Monotype Functional Groups of Variable Density Using Chemical and Plasma Chemical Processes T2 - 10th Dresden Polymer Discussion: Characterization of Polymer Surfaces and Thin Films CY - Meißen, Germany DA - 2005-04-10 KW - Plasma modification KW - Introduction of functional groups KW - Reactions at polymer surfaces PY - 2005 SP - 34 EP - 49 PB - Leibniz-Institut für Polymerforschung Dresden CY - Meißen AN - OPUS4-7332 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Mix, Renate A1 - Kühn, Gerhard T1 - Adhesion of metals to plasma-induced functional groups at polymer surfaces N2 - The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 3–4 to 10–14 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral “monomers” like ethylene or butadiene the concentration of the functional groups was varied. A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2–CH2). KW - Peel strength KW - Aluminium KW - Polypropylene KW - Poly(tetrafluoroethylene) KW - Pulsed plasma KW - Allyl alcohol KW - Allylamine KW - Acrylic acid KW - Plasma surface treatment KW - Adhesion PY - 2005 SN - 0257-8972 VL - 200 IS - 1-4 SP - 565 EP - 568 PB - Elsevier Science CY - Lausanne AN - OPUS4-10897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Friedrich, Jörg Florian A1 - Mix, Renate A1 - Kühn, Gerhard ED - Possart, W. T1 - Contribution of chemical interactions to the adhesion between evaporated metals and functional groups of different types at polymer surfaces PY - 2005 SN - 3-527-31263-3 SP - 265 PB - Wiley-VCH CY - Weinheim AN - OPUS4-10898 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meyer-Plath, Asmus A1 - Mix, Renate A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian ED - d'Agostino, R. T1 - The Potential of Surface Radicals for Polymer Functionalization T2 - 16th International Symposium on Plasma Chemistry (ISPC-16) CY - Taormina, Italy DA - 2003-06-22 PY - 2003 IS - CD-ROM PB - Dep. of Chemistry, Univ. CY - Bari AN - OPUS4-2612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fritz, Andreas A1 - Schönhals, Andreas A1 - Mix, Renate A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian T1 - Dielectric spectroscopy of plasma copolymers of the system allyl alcohol/alkene N2 - Polymers synthesized with plasma techniques are very interesting materials for electronic, optic, and bio compatible applications. Thin films of plasma polymers shows a good adhesion to metals, glass, or other polymers. But the supramolecular structure, the durability, and the chemical and mechanical behavior of these polymers is poorly understood. Therefore dielectric investigations are carried out to study the dynamic behavior of the plasma polymers. As polymer system allyl alcohol/alkene is chosen to get polymers with a defined concentration of hydroxyl groups. The dielectric investigations shows several relaxation processes and a dependency of the dielectric parameters from the ratio of allyl alcohol in the polymer is observed. This results indicated that the alkene monomers were assembled continuous into the polymer matrix. T2 - Frühjahrstagung des Arbeitskreises Festkörperphysik bei der DPG CY - Regensburg, Deutschland DA - 2002-03-11 PY - 2002 UR - http://old.dpg-tagungen.de/archive/2002/cpp_4.html SN - 0420-0195 SN - 0372-5448 SN - 0343-9216 IS - CPP 4.7 SP - 424 CY - Bad Honnef AN - OPUS4-2057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fritz, Andreas A1 - Schönhals, Andreas A1 - Mix, Renate A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian T1 - Dielectric spectroscopy of plasma copolymers or the system allyl alcohol/alkene T2 - Frühjahrstagung des Arbeitskreises Festkörperphysik bei der DPG CY - Regensburg, Germany DA - 2002-03-11 PY - 2002 SN - 0420-0195 SN - 0372-5448 SN - 0343-9216 IS - CPP 4.7 SP - 424 CY - Bad Honnef AN - OPUS4-2058 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Mix, Renate T1 - Tayloring of polymer surfaces with different monotype functional groups of variable density using chemical and plasma chemical processes T2 - 10th Dresden Polymer Discussion: Characterization of Polymer Surfaces and Thin Films CY - Meißen, Germany DA - 2005-04-10 KW - Plasma modification KW - Introduction of functional groups KW - Reactions at polymer surfaces PY - 2005 SP - 34 EP - 49 PB - Leibniz-Institut für Polymerforschung Dresden CY - Meißen AN - OPUS4-11941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mach, Reinhard A1 - Maneck, Heinz-Eberhard A1 - Röhl-Kuhn, Barbara A1 - Peplinski, Burkhard A1 - Benemann, Sigrid A1 - Strauß, Birgid A1 - Schütz, W. A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian ED - Pershin, L. T1 - Modification of graphite powders in a thermal RF induction plasma T2 - 17th International Symposium on Plasma Chemistry (ISPC-17) CY - Toronto, Canada DA - 2005-08-07 PY - 2005 SP - 1(?) EP - 6(?) CY - Toronto AN - OPUS4-11942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard A1 - Mix, Renate ED - Pershin, L. T1 - Chemical synthesis at plasma modified polymer surfaces T2 - 17th International Symposium on Plasma Chemistry (ISPC-17) CY - Toronto, Canada DA - 2005-12-07 PY - 2005 SP - 1(?) EP - 6(?) CY - Toronto AN - OPUS4-11944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mix, Renate A1 - Friedrich, Jörg Florian A1 - Kühn, Gerhard ED - Mutlu, M. T1 - Adhesion between metal atoms and polymer surfaces fitted with different types and variable density of functional groups T2 - 3rd workshop COST 527 CY - Antalya, Turkey DA - 2004-10-07 KW - Peel strength KW - Aluminium KW - Pulsed plasma KW - Allyl alcohol KW - Allylamine KW - Acrylic acid PY - 2005 SN - 975-491194-0 SP - 106 EP - 114 PB - Hacettepe Univ. Press CY - Ankara AN - OPUS4-11042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mix, Renate A1 - Kühn, Gerhard A1 - Friedrich, Jörg Florian ED - Mittal, K. L. T1 - Contribution of chemical interactions between Al atoms and different types of functional groups to the adhesion of Al-polymer systems T2 - 2nd International Symposium on Adhesion Aspects of Thin Films CY - Orlando, FL, USA DA - 2003-12-15 KW - Al-functional group interactions KW - Adhesion-promoting plasma polymer layers KW - Pulsed plasma polymerization PY - 2005 SN - 90-6764-421-8 VL - 2 SP - 123 EP - 144 PB - VSP CY - Utrecht AN - OPUS4-11156 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wettmarshausen, Sascha A1 - Kühn, Gerhard A1 - Hidde, Gundula A1 - Mittmann, Hans-Ulrich A1 - Friedrich, Jörg Florian T1 - Plasmabromination - the Selective Way to Monotype Functionalized Polymer Surfaces N2 - In contrast to other plasma modification processes of polymer surfaces, the bromination is very selective and shows a high yield in C—Br groups. The most convenient bromination process was found using bromoform, which was thus preferred to elemental bromine, allyl bromide, vinyl bromide or tert-butylbromide. The bromoform process give yields in C—Br up to 40 C—Br or more, with only 2-3% co-introduction of O-functionalities whereas allyl bromide results in yields of about 20 C—Br and more, but in more than 10% oxygen-containing by-products. C—Br groups serve as anchoring points for grafting of molecules, oligomers and pre-polymers of diole or diamine character. KW - Functional groups KW - Grafting KW - Plasma bromination KW - Polymer surfaces KW - Selective plasma process KW - Spacer PY - 2007 DO - https://doi.org/10.1002/ppap.200700019 SN - 1612-8850 SN - 1612-8869 VL - 4 IS - 9 SP - 832 EP - 839 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-16209 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -