TY - JOUR A1 - Sonntag, Nadja A1 - Jürgens, Maria A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Creep-fatigue of P92 in service-like tests with combined stress- and strain-controlled dwell times N2 - Complex service-like relaxation- and creep-fatigue tests with strain- and stress-controlled dwells and fatigue cycle durations of approx. 2200 s were performed exemplarily on a grade P92 steel at 620 ◦C in this study. The results indicate deviations in the prevailing creep mechanisms of long-term relaxation and creep dwells, affecting subsequent dwells, load shifts, and the macroscopic softening behavior quite differently. In addition, fracture surfaces and longitudinal metallographic sections reveal intergranular crack growth for complex loading with stress-controlled dwells, whereas complex strain-controlled tests enhance oxidation and transgranular crack propagation. These findings substantiate the limited transferability of relaxation-fatigue to creep-fatigue conditions. KW - Tempered martensite-ferritic steel KW - P92 KW - Dwell periods KW - Creep-fatigue interaction KW - Stress relaxation PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-564239 SN - 0142-1123 VL - 168 SP - 1 EP - 12 PB - Elsevier Ltd. AN - OPUS4-56423 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit A1 - Fedelich, Bernard T1 - Ermüdungsverhalten, Lebensdauer und Schädigungsprozesse von P92 unter zyklischen Betriebsbedingungen N2 - Schnelle Lastwechsel mit hohen Temperaturgradienten führen zu thermischen und mechanischen Beanspruchungen v.a. in dickwandigen Bauteilen. Daraus ergibt sich ein komplexes Lastkollektiv, bei dem der Werkstoff sowohl durch Kriechermüdung als auch durch thermomechanische Ermüdung (TMF) geschädigt wird. Welche Auswirkungen hat eine gleichzeitige Änderung von Temperatur, mechanischer Beanspruchung und Arbeitsmedium auf die Schädigungsprozesse? T2 - KWT Dresden CY - Dresden, Germany DA - 18.10.2016 KW - LCF KW - P92 KW - TMF PY - 2016 AN - OPUS4-38587 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Olbricht, Jürgen A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - FLEXIKON - Teil 2: Ermüdungsverhalten, Schädigungsentwicklung und Lebensdauer von 9-12% Cr-Stählen im zyklischen Kraftwerksbetrieb N2 - Schnelle Lastwechsel führen v.a. in dickwandigen Kraftwerksbauteilen zu starken thermischen und mechanischen Beanspruchungen, da sich hohe Temperaturgradienten über der Wand des Bauteils einstellen. Es ergeben sich komplexe Lastkollektive aus zeitlich veränderlichen Spannungen/Dehnungen und Temperaturen, die formal einer Kombination aus Kriechbeanspruchung, Kriechermüdung und thermomechanischer Ermüdung (TMF) entsprechen. T2 - 47. Kraftwerkstechnisches Kolloquium CY - Dresden DA - 13.10.2015 KW - TMF KW - LCF KW - P91 KW - P92 PY - 2015 AN - OPUS4-35613 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Sonntag, Nadja A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - Cyclic operation performance of 9-12% Cr ferritic-martensitic steels part 1: Cyclic mechanical behavior under fatigue and creep-fatigue loading N2 - The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach, both of which are presented in “Part 2: Microstructural Evolution during Cyclic Loading and its Representation in a Physically-based Micromechanical Model“. T2 - 45. MPA-Seminar CY - Leinfelden-Echterdingen, Germany DA - 01.10.2019 KW - Tempered Martensite Ferritic Steels KW - P92 KW - Low Cycle Fatigue KW - Thermo-Mechanical Fatigue KW - Creep-Fatigue PY - 2019 SP - 75 EP - 79 PB - MPA (Materialprüfungsanstalt Universität Stuttgart) CY - Stuttgart AN - OPUS4-50051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Jürgens, Maria T1 - Verhalten des hochwarmfesten Stahles P92 unter zyklischen thermo-mechanischen Bedingungen in lastflexiblen Dampfkraftwerken N2 - Die Erzeugung von Erneuerbaren Energien unterliegt starken Schwankungen, die von konventionellen Kraftwerken ausgeglichen werden müssen, um das Stromnetz stabil zu halten. Für die konventionellen Kraftwerke bedeutet dies eine zunehmend zyklische Fahrweise, die zu häufigeren Last- und Temperaturwechseln führt. Von den eingesetzten Werkstoffen fehlen Daten zum Verhalten unter zyklischer Fahrweise. Ziel dieser Arbeit ist es daher, für P92, einen als Rohrleitungswerkstoff eingesetzten hochwarmfesten Stahl, zu untersuchen, welche Auswirkungen zyklische Fahrweisen auf die Schädigungsprozesse und Lebensdauern haben. Da durch den zyklischen Betrieb eine verstärkte Schädigung durch Ermüdungsprozesse zu erwarten ist, wurden dehnungskontrollierte isotherme (LCF) und nicht-isotherme (TMF) Ermüdungsversuche mit und ohne Haltezeit bei verschiedenen Temperaturen bzw. Temperaturintervallen durchgeführt. Mit den Haltezeitversuchen soll dabei das Kriech-Ermüdungs-Verhalten untersucht werden. Bei den TMF-Versuchen wurde zusätzlich die Temperaturrate variiert, um näher an den realen Lastwechselgeschwindigkeiten zu prüfen. Schließlich wurden auf Basis der durchgeführten LCF- und TMF-Versuche betriebsnahe Versuchsprozeduren entwickelt, um unterschiedliche Betriebsmodi in einem Versuch abzubilden. Die durchgeführten mechanischen Versuche stellen eine umfangreiche Basis zu Ermüdungsdaten an P92 dar. Neben der Abhängigkeit der Lebensdauer von Temperatur, Temperaturintervall und –rate, sowie Dehnung und Haltezeit, konnte auch das Entfestigungsverhalten genauer charakterisiert werden. Sowohl Haltezeiten als auch das Reduzieren der Temperaturrate können die Lebensdauer erheblich verringern. Dabei kommt es gerade bei vermeintlich kleinen Dehnungen, bei denen die Streckgrenze nur leicht überschritten wird, zu einer Lebensdauerreduzierung. Haltezeiten verstärken zudem die zyklische Entfestigung. Die fraktographische Analyse der Proben hat ergeben, dass es keinen direkten Zusammenhang zwischen der Entfestigung und der Bildung von Nebenrissen gibt. Stattdessen zeigen EBSD- und TEM-Untersuchungen, dass es zur Bildung einer Subkornstruktur kommt und die Entfestigung auf dem Verschwinden von Kleinwinkelkorngrenzen beruht. Während bei den LCF-Proben eine reine Ermüdungsschädigung vorliegt, konnte bei einigen TMF-Proben eine kriechdominierende Schädigung nachgewiesen werden. Die betriebsnahen Zyklen zeigen, dass sich mit den durchgeführten Versuchen das reale Betriebsverhalten gut abschätzen lässt. Da es jedoch auch Parameterkombinationen gibt, bei denen keine Änderung des Entfestigungs- und Lebensdauerverhaltens auftritt, sollte genau bekannt sein, welche Belastungen in einem Bauteil auftreten. KW - P92 KW - LCF KW - TMF KW - Energiewende KW - Kriechermüdung KW - Energy transition KW - Creep-fatigue PY - 2020 U6 - https://doi.org/10.14279/depositonce-10538 SP - 1 EP - 144 CY - Berlin AN - OPUS4-51571 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jürgens, Maria A1 - Sonntag, Nadja A1 - Olbricht, Jürgen A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - The effect of dwell times on the thermomechanical fatigue life performance of grade P92 steel at intermediate and low strain amplitudes N2 - Results of an extended TMF test program on grade P92 steel in the temperature range of 620 °C - 300 °C, comprising in-phase (IP) and out-of-phase (OP) tests, partly performed with symmetric dwells at Tmax/Tmin, are presented. In contrast to previous studies, the low-strain regime is also illuminated, which approaches flexible operation in a power plant with start/stop cycles. At all strain amplitudes, the material performance is characterized by continuous cyclic softening, which is retarded in tests at lower strains but reaches similar magnitudes in the course of testing. In the investigated temperature range, the phase angle does not affect fatigue life in continuous experiments, whereas the IP condition is more detrimental in tests with dwells. Fractographic analyses indicate creep-dominated and fatigue-dominated damage for IP and OP, respectively. Analyses of the (micro)hardness distribution in the tested specimens suggest an enhanced microstructural softening in tests with dwell times for the low- but not for the high-strain regime. To rationalize the obtained fatigue data, the fracture-mechanics-based D_TMF concept, which was developed for TMF life assessment of ductile alloys, was applied. It is found that the D_TMF parameter correlates well with the measured fatigue lives, suggesting that subcritical growth of cracks (with sizes from a few microns to a few millimeters) governs failure in the investigated range of strain amplitudes. KW - 9-12%Cr steel KW - Thermomechanical fatigue KW - Symmetric dwell periods KW - Low strain KW - Parametric modeling PY - 2021 U6 - https://doi.org/10.1016/j.msea.2020.140593 VL - 805 SP - 140593 PB - Elsevier B.V. AN - OPUS4-52374 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - Betriebsnahe LCF- und TMF-Untersuchungen an ferritsch-martensitischen Chromstählen N2 - Betriebsnahe LCF- und TMF-Untersuchungen an P92, Vorstellung erster Versuchsergebnisse T2 - DVM Arbeitskreis Bauteilverhalten bei thermomechanischer Ermüdung CY - Berlin, Germany DA - 06.04.2017 KW - P92 KW - TMF KW - LCF PY - 2017 AN - OPUS4-39831 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jürgens, Maria A1 - Olbricht, Jürgen A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - Low Cycle Fatigue and Relaxation Performance of Ferritic–Martensitic Grade P92 Steel N2 - Due to their excellent creep resistance and good oxidation resistance, 9–12% Cr ferritic–martensitic stainless steels are widely used as high temperature construction materials in power plants. However, the mutual combination of different loadings (e.g., creep and fatigue), due to a “flexible” operation of power plants, may seriously reduce the lifetimes of the respective components. In the present study, low cycle fatigue (LCF) and relaxation fatigue (RF) tests performed on grade P92 helped to understand the behavior of ferritic–martensitic steels under a combined loading. The softening and lifetime behavior strongly depend on the temperature and total strain range. Especially at small strain amplitudes, the lifetime is seriously reduced when adding a hold time which indicates the importance of considering technically relevant small strains. KW - Ferritic–martensitic steel KW - P92 KW - Low cycle fatigue KW - Relaxation fatigue KW - Cyclic softening PY - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-473905 VL - 9 IS - 1 SP - 99, 1 EP - 25 PB - MDPI AN - OPUS4-47390 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Skrotzki, Birgit T1 - Thermo-Mechanical Fatigue Behavior of P92 N2 - In the present contribution, the thermo-mechanical fatigue and creep-fatigue behavior of two different 9% Cr steel grades (P91 and P92) was investigated. Standard LCF/TMF-tests as well as near-service loading tests with different hold times have been carried out to study the material behavior of the new loading scenarios. Microstructural investigations help to identify the observed deformation characteristics (like e.g. pronounced softening) and the dominating damage mechanisms under different loads. The test programme is complemented by selected tests on service-aged material which demonstrate possible reactions of older components in existing plants to changes in operation profiles. In a next step, the experimental results will be used for parameter identification of a deformation and lifetime model to predict the material behavior. T2 - LCF08 CY - Dresden, Germany DA - 27.06.2017 KW - Near-service testing KW - Power plant KW - Ferritic-martensitic steels KW - P91 KW - P92 KW - Thermo-Mechanical Fatigue PY - 2017 AN - OPUS4-42267 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Fedelich, Bernard A1 - Olbricht, Jürgen A1 - Skrotzki, Birgit T1 - Thermo-mechanical fatigue behavior of P91/P92 N2 - 9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep resistance and good oxidation resistance. Creep resistance is considered as the primary parameter in material selection for base-load power plants, but the growing share of renewable energy sources in power generation forces many installations into more "flexible" operation with frequent load reductions and shutdowns. Under cyclic operation of power plants, temperature gradients occur especially in thick-walled components. Locally, these gradients lead to complex time- and temperature-dependent loading scenarios which may result in superimposed creep deformation/damage, creep-fatigue and thermo-mechanical fatigue. The combination of different damage processes may seriously reduce the lifetimes of respective components. A fundamental understanding of the damage evolution in ferritic-martensitic steels under combined static and cyclic loading is therefore required. In the present contribution, the thermo-mechanical fatigue and creep-fatigue behavior of two different 9% Cr steel grades (P91 and P92) was investigated. Standard LCF/TMF-tests as well as near-service loading tests with different hold times have been carried out to study the material behavior of the new loading scenarios. Microstructural investigations help to identify the observed deformation characteristics (like e.g. pronounced softening) and the dominating damage mechanisms under different loads. The test programme is complemented by selected tests on service-aged material which demonstrate possible reactions of older components in existing plants to changes in operation profiles. In a next step, the experimental results will be used for parameter identification of a deformation and lifetime model to predict the material behavior. T2 - LCF08 CY - Dresden, Germany DA - 27.06.2017 KW - Near-service testing KW - Power plant KW - Ferritic-martensitic steels KW - P91 KW - P92 KW - Thermo-Mechanical Fatigue PY - 2017 SN - 978-3-9814516-5-8 VL - 2017 SP - 101 EP - 105 PB - DVM CY - Berlin AN - OPUS4-42268 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Skrotzki, Birgit A1 - Jürgen, Olbricht T1 - Creep fatigue behavior of P91/P92 N2 - 9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep resistance and good oxidation resistance. Creep resistance is considered as the primary parameter in material selection for base-load power plants, but the growing share of renewable energy sources in power generation forces many installations into more "flexible" operation with frequent load reductions and shutdowns. Under cyclic operation of power plants, temperature gradients occur especially in thick-walled components. Locally, these gradients lead to complex time- and temperature-dependent loading scenarios which may result in superimposed creep deformation/damage, creep-fatigue and thermo-mechanical fatigue. The combination of different damage processes may seriously reduce the lifetimes of respective components. A fundamental understanding of the damage evolution in ferritic-martensitic steels under combined static and cyclic loading is therefore required. In the present contribution, the creep-fatigue behavior of two different 9% Cr steel grades (P91 and P92) was investigated. Standard creep-tests as well as LCF/TMF tests with hold time have been carried out to study the material behavior of the new loading scenarios. Microstructural investigations help to identify the observed deformation characteristics and the dominating damage mechanisms under different loads. The test programme is complemented by cyclic creep-tests (temperature change) and creep-tests under atmospheres. In a next step, the experimental results will be used for parameter identification of a deformation and lifetime model to predict the material behavior. T2 - ECCC 2017 CY - Düsseldorf, Germany DA - 10.09.2017 KW - Near-service testing KW - Power plant KW - Ferritic-martensitic steels KW - P91 KW - P92 KW - Creep-Fatigue PY - 2017 AN - OPUS4-42269 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria ED - Skrotzki, Birgit ED - Jürgen, Olbricht T1 - Creep fatigue behavior of P91/P92 N2 - 9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep resistance and good oxidation resistance. Creep resistance is considered as the primary parameter in material selection for base-load power plants, but the growing share of renewable energy sources in power generation forces many installations into more "flexible" operation with frequent load reductions and shutdowns. Under cyclic operation of power plants, temperature gradients occur especially in thick-walled components. Locally, these gradients lead to complex time- and temperature-dependent loading scenarios which may result in superimposed creep deformation/damage, creep-fatigue and thermo-mechanical fatigue. The combination of different damage processes may seriously reduce the lifetimes of respective components. A fundamental understanding of the damage evolution in ferritic-martensitic steels under combined static and cyclic loading is therefore required. In the present contribution, the creep-fatigue behavior of two different 9% Cr steel grades (P91 and P92) was investigated. Standard creep-tests as well as LCF/TMF tests with hold time have been carried out to study the material behavior of the new loading scenarios. Microstructural investigations help to identify the observed deformation characteristics and the dominating damage mechanisms under different loads. The test programme is complemented by cyclic creep-tests (temperature change) and creep-tests under atmospheres. In a next step, the experimental results will be used for parameter identification of a deformation and lifetime model to predict the material behavior. T2 - ECCC 2017 CY - Düsseldorf, Germany DA - 10.09.2017 KW - Near-service testing KW - Power plant KW - Ferritic-martensitic steels KW - P91 KW - P92 KW - Creep-Fatigue PY - 2017 SN - 978-3-514-00832-8 SP - 1 EP - 5 AN - OPUS4-42270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jürgens, Maria A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Ermüdungsverhalten des warmfesten Stahls P92 N2 - Hochwarmfeste ferritisch-martensitische Stähle mit 9-12 Gew.-% Chromgehalt werden wegen ihrer hohen Kriechfestigkeit und ihres gleichzeitig guten Oxidationswiderstands erfolgreich als Konstruktionswerkstoff für Hochtemperaturbauteile in Kraftwerken eingesetzt. Die zunehmend zyklische Fahrweise konventioneller Kraftwerke im lastflexiblen Betrieb führt zu häufigen Last- und Temperaturwechseln, die von den Bauteilen sicher ertragen werden müssen. Schnelle Lastwechsel verursachen vor allem in dickwandigen Bauteilen erhebliche thermische und mechanische Beanspruchungen. Während unter stationären Betriebs¬bedingungen der Lebensdauerverbrauch von der Werkstoffschädigung durch Kriechen dominiert wurde, verstärkt sich im zyklischen Betrieb die Schädigung durch Ermüdungsprozesse. In der hier vorgestellten Arbeit wird am Beispiel des ferritisch-martensitischen Stahls P92 untersucht, welche Auswirkungen zyklische Fahrweisen auf die Schädigungsprozesse und Lebensdauern dieser Stähle haben. Das Versuchsprogramm kombiniert deshalb Standardtests mit betriebsnahen mechanischen Versuchen unter überlagerter Kriech-, Ermüdungs- und Temperaturwechselbeanspruchung. Diese werden im vorliegenden Beitrag anhand erster Versuchsergebnisse vorgestellt. Ziel der Arbeiten ist, die auftretenden mechanischen Effekte darzustellen und die zugrunde liegenden Schadensmechanismen durch umfangreiche mikroanalytische/fraktographische Nachuntersuchungen des Probenmaterials zu identifizieren. T2 - DGM-AK-Sitzung Mechanisches Verhalten bei hoher Temperatur CY - Berlin, Germany DA - 20.09.2017 KW - P92 KW - LCF KW - RF PY - 2017 AN - OPUS4-42272 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sonntag, Nadja A1 - Jürgens, Maria A1 - Uhlemann, Patrick A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - Experimental data from service-like creep-fatigue experiments on grade P92 steel N2 - This article refers to the research article entitled “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times” [1]. It presents experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress. Such service-like (SL) tests with additional long-term stress- and strain-controlled dwell times are non-standard, rare, and expensive, making these data very valuable. They may be used to approximate cyclic softening in the technically relevant range, for the design of complex SL experiments, or for detailed analyses of stress-strain hystereses (e.g., for stress or strain partitioning methods, for the determination of hysteresis energies (work), inelastic strain components, etc.). In addition, the latter analyses may supply important input for advanced parametric lifetime modeling of components under creep-fatigue loading or model calibration parameters. KW - Tempered martensite-ferritic steel KW - Creep KW - Stress relaxation KW - Creep-fatigue KW - Dwell times PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-578407 SN - 2352-3409 VL - 49 SP - 1 EP - 9 PB - Elsevier Inc. AN - OPUS4-57840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Olbricht, Jürgen A1 - Agudo Jácome, Leonardo A1 - Jürgens, Maria A1 - Roohbakhshan, Farshad A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - Cyclic loading performance and related microstructure evolution of ferritic-martensitic 9-12% Cr steels N2 - The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach. T2 - 44th MPA-Seminar CY - Leinfelden/Stuttgart, Germany DA - 17.10.2018 KW - Ferritic-martensitic steels KW - Cyclic loading KW - Microstructure evolution PY - 2018 SP - 259 EP - 265 AN - OPUS4-47118 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Jürgens, Maria A1 - Olbricht, Jürgen A1 - Winkelmann, Aimo T1 - Improving the precision of orientation measurements from technical materials via EBSD pattern matching N2 - We use pattern matching of experimental and dynamically simulated backscattered Kikuchi diffraction (BKD) patterns to increase the orientation precision of electron backscatter diffraction (EBSD) measurements. In order to quantify the improvement in orientation precision, we analyze the experimental distribution of the kernel average misorientation (KAM) angles. We find that for the same raw data, i.e. the same EBSD data acquisition time budget, the pattern matching approach improves the KAM resolution by an order of magnitude compared to orientation data delivered from the conventional Hough-transform based data analysis. This quantitative improvement enables us to interpret small orientation changes in plastically deformed materials which are hidden in noisy orientation data delivered from the reference EBSD system. As an application example, we analyze a ferritic-martensitic steel (P92) sample before and after low-cycle fatigue (LCF) loading (±0.3% strain) at 620 °C. Whereas the low precision of the EBSD orientation data from the manufacturer software does not allow a reliable discrimination of the gradually changing microstructure, we find very clear systematic differences of the local microstructure after the pattern matching orientation refinement of the initial, raw pattern data. For the investigated P92 sample, the KAM-angle histograms are well described by two log-normal distributions indicating the already tempered and the remaining and mostly untempered martensite. KW - Misorientation KW - Thermo-mechanical loading KW - Martensite KW - Log-normal distribution KW - Bimodal distribution PY - 2018 U6 - https://doi.org/10.1016/j.actamat.2018.08.028 VL - 159 SP - 408 EP - 415 PB - Elsevier Ltd. AN - OPUS4-46454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -