TY - CONF A1 - Rethmeier, Michael A1 - Gumenyuk, Andrey A1 - Gook, S. T1 - Laser-hybrid welding for pipe production and pipe laying of thick large diameter pipes T2 - IIW 2013 - 7th Asia Pacific IIW International congress 2013 CY - Singapore DA - 2013-07-08 PY - 2013 SP - 417 EP - 423 AN - OPUS4-28935 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey A1 - Petrovskiy, V.N. A1 - Rethmeier, Michael A1 - Shcheglov, Pavel A1 - Uspenskiy, S.A. T1 - Condensed metal particles influence during the high power fiber laser welding N2 - Different types of lasers are used nowadays for a number of technological Solutions, Modem high power solid-state lasers with high brightness of Radiation like Fiber or disc lasers find ever more applications in welding technology. Apart from the replacement of the CC>2-iasers traditionaHy used fcr these purposes, they provide new technological possibilities of metal treatment, such as using industrial robots and remote welding with high power laser radiation. The possibility of flexible optical fiber delivery of the radiation to any point gives a great technological advantage and permits welding processes to be realized with complicated weld seam geomelries and different positions using a minimum of additional fixtures. The short wavelength of the high power solid state lasers (1.07 ’m) causes another advantage. The coefflcient of inverse 170 Bremsstrahlung absorption from free electrons in plasma for such radiation is about 100 times lower than for the COi-iaser radiation. Owing to this fact, using the solid state lasers allows it to avoid a negative influence of the welding plume. However, a short wavelength can lead to another kind of laser Radiation attenuation, which is connected with the formation of a cloud consisting of small metal particles that absorb and scatter laser radiation. This cloud arises due to the condensation of hot metal vapor by flying out from the deep Penetration channel and broadening in relatively cold atmosphere over the metal Surface. Some theoretical and experimental approaches were made in advance in Order to estimate the influence of the Condensed particles on laser radiation and welding quality. In this paper a systematic study including the determination of the Cloud size and its dynamical characteristics is presented. The results were obtained within the scope of the first stage of the metal vapor condensation process Investigation during welding with high power fiber lasers. T2 - International Conference 'Lasers in Science, Technology, Medicine' CY - Moscow, Russia DA - 19.09.2011 PY - 2011 VL - 22 SP - 170 EP - 177 AN - OPUS4-29166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Uspenskiy, S.A. A1 - Shcheglov, Pavel A1 - Petrovskiy, V.N. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Spectral diagnostics of a vapor-plasma plume produced during welding with a high-power ytterbium fiber laser N2 - We have conducted spectroscopic studies of the welding plasma formed in the process of welding with an ytterbium fiber laser delivering output power of up to 20 kW. The influence of shielding gases (Ar, He) on different parts of the welding plume is investigated. The absorption coefficient of the laser radiation by the welding-plume plasma is estimated. Scattering of 532-nm probe radiation from particles of the condensed metal vapor within the caustic of a high-power fiber laser beam is measured. Based on the obtained results, conclusions are made on the influence of the plasma formation and metal vapor condensation on the radiation of the high-power fiber laser and the stability of the welding process. PY - 2013 DO - https://doi.org/10.1134/S0030400X13070205 SN - 0030-400X SN - 1562-6911 VL - 115 IS - 1 SP - 140 EP - 146 PB - MAIK Nauka/Interperiodica Publ. / Pleiades Publishing, Ltd. CY - Moscow AN - OPUS4-28983 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Avilov, Vjaceslav A1 - Graf, J. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Anwendung von AC-Magnetfeldern zur Verbesserung der Nahtqualität laserstrahlgeschweißter Aluminiumverbindungen N2 - Im Rahmen eines AiF-Forschungsvorhabens wurde die Beeinflussung des Schweißprozesses mittels generierter Wechselstrom-Magnetfelder (ACMagnetfelder) beim Laserstrahlschweißen von Aluminiumlegierungen untersucht. Das vorrangige Augenmerk galt hierbei der Entfernung von Poren sowie der Stabilisierung der Schweißnahtoberfläche zur Vermeidung von rauen Schweißnähten. Das Schweißen mit Einsatz des AC-Magneten erzeugte im Vergleich zu den Referenznähten deutlich flachere Schweißnähte mit reduzierter Porenanzahl, die typische Schuppenstruktur wurde unterdrückt. Das Magnetfeld bewirkte bei entsprechenden Parametern der magnetischen Flussdichte und der Frequenz eine Halbierung der Rauigkeit der Schweißnahtoberfläche. Neben der Oberflächenberuhigung wurde auch die Verteilung von Poren in der Schmelze beeinflusst. Es konnte nachgewiesen werden, dass bei einer geeigneten Auswahl der Parameter von AC-Magnetfeldern die Porositätsanteile in der Schweißnaht auf ein Zehntel gegenüber den Referenzschweißnähten reduziert werden können.----------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------- Within the framework of an AiF research project, investigations were conducted into the influences exerted on the welding process using generated alternating current (AC) magnetic fields during the laser beam welding of aluminium alloys. In this respect, attention was principally paid to removing pores and to stabilising the weld surface in order to avoid rough welds. In comparison with the reference welds, welding utilising the AC magnet produced considerably flatter welds with a reduced number of pores and the typical ripple structure was suppressed. With corresponding parameters for the magnetic flux density and the frequency, the roughness of the weld surface was halved using the magnetic field. In addition to the surface stabilisation, influences were also exerted on the distribution of pores in the molten metal. It was possible to prove that, by selecting suitable parameters for AC magnetic fields, the porosity proportions in the weld can be reduced to one tenth of those in the reference welds. KW - Aluminium KW - Laserstrahlschweißen KW - Magnetfelder KW - Poren KW - Schweißnahtimperfektionen KW - Werkstofffragen PY - 2014 SN - 0036-7184 VL - 66 IS - 9 SP - 524 EP - 529 PB - Verl. für Schweißen u. Verwandte Verfahren, DVS-Verl. CY - Düsseldorf AN - OPUS4-31441 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, André A1 - Gumenyuk, Andrey A1 - Lammers, Marco A1 - Malletschek, A. A1 - Rethmeier, Michael T1 - Laser beam welding of thick titanium sheets in the field of marine technology N2 - The ever larger requirements of the material selection in the range of maritime industry necessitate the application of high-tech materials. Titanium because of its excellent mechanical properties at low weight is an attractive alternative for the construction of ships. The goal of this investigation was to design a welding method for joining samples of 16 mm thick Ti3Al2.5 V. The welding experiments with a 20 kW Yb-fiber laser source and varying combinations of parameters were intended to qualify the laser beam welding process. The welding results were analyzed by non-destructive and destructive testing. In addition, the welding tests were recorded with two high-speed cameras to observe the weld pool and the vapor plume. The evaluation of the high-speed images in correlation with the results of non-destructive testing shows, that a significant improvement of process stability and weld quality can be achieved by the suppression of the vapor plume. KW - Titanium alloy KW - Maritime industry KW - Vapor plume KW - Laser beam welding KW - Ti3Al2.5V PY - 2014 DO - https://doi.org/10.1016/j.phpro.2014.08.046 SN - 1875-3892 VL - 56 SP - 582 EP - 590 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-31439 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, André A1 - Avilov, Vjaceslav A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser beam welding of aluminium alloys under the influence of an electromagnetic field N2 - During laser beam welding of aluminum alloys an electromagnetic field may favour pore outgassing through the top oxide layer. High frequencies cause a small penetration depth and thus exert a stabilizing effect on the weld surface. The point at which the laser beam between the two magnetic poles hits the workpiece surface is crucial to the influence of the magnetic field on the weld surface roughness. Using analyzed parameters for different laser points of application cause a change in weld surface roughness could be observed. The weld surface roughness could be reduced by 50%. The outgassing effect in terms of a reduction of pores could be observed for all parameter sets investigated. T2 - Lasers in manufacturing conference 2013 CY - Munich, Germany DA - 13.05.2013 KW - Electromagnetically controlled laser beam welding KW - Surface roughness KW - Porosity prevention KW - Aluminium alloys PY - 2013 DO - https://doi.org/10.1016/j.phpro.2013.03.045 SN - 1875-3892 VL - 41 SP - 4 EP - 11 PB - Elsevier B.V. CY - Amsterdam [u.a.] AN - OPUS4-28147 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sohail, M. A1 - Han, S.-W. A1 - Na, S.-J. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Characteristics of weld pool behavior in laser welding with various power inputs N2 - This paper investigates the numerical simulations of multi-kilowatt disk laser and fiber laser welding, ranging from 6 to 18 kW to study the behavior of molten pool in 20-mm-thick steel plate by using Volume-Of-Fluid (VOF) method and several mathematical models like Gaussian heat source, recoil pressure, Marangoni flow, buoyancy force, and additional shear stress and heat source due to the metallic vapor. Vortex flow pattern is observed for higher laser power except for 6-kW case, and the higher the laser power, the bigger the vortex flow pattern. Welding speed has an influence on molten pool in terms of depth of penetration and size of molten pool, but overall shape of molten pool remains the same. The reasons for the vortex flow pattern in high-power laser welding are the absorption of more energy at the bottom of keyhole, which promotes more liquid metal at the bottom, while for lower power with lower speed, the melt formation is more uniform in the thickness direction and most of the molten metal in the lower part of keyhole reaches the top of molten pool, and consequently, no vortex flow pattern is observed in the keyhole bottom. KW - Laser welding KW - Mathematical models KW - Simulating KW - Molten pool KW - Flow PY - 2014 DO - https://doi.org/10.1007/s40194-014-0112-4 SN - 0043-2288 SN - 1878-6669 VL - 58 IS - 3 SP - 269 EP - 277 PB - Springer CY - Oxford AN - OPUS4-30644 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Graf, Benjamin A1 - Schuch, M. A1 - Kersting, R. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Additive process chain using selective laser melting and laser metal deposition N2 - Selective Laser Melting (SLM) and Laser Metal Deposition (LMD) are prominent methods in the field of additive manufacturing technology. While the powder-bed based SLM allows the manufacturing of complex structures, buildrate and part volumes are limited. In contrast, LMD is able to operate with high deposition rates on existing parts, however shape complexity is limited. Utilizing their respective strengths, a combination of these two additive technologies has the potential to produce complex parts with high deposition rates. In this paper, a process chain consisting of additive technologies SLM and LMD is described. The experiments are conducted using the alloys Ti-6Al-4V and Inconel 718. A cylindrical test specimen is produced and the microstructure along the SLM-LMD zone is described. In addition, this process chain was tested in the manufacturing of a turbine blade. The feasibility of implementing this process chain for small batch production is discussed. The results are evaluated to show advantages and limitations of the SLM-LMD process chain. This paper is relevant for industrial or scientific users of additive manufacturing technologies, who are interested in the feasibility of a SLM-LMD process chain and its potential for increased deposition rates. T2 - LiM 2015 - Lasers in manufacturing conference 2015 CY - Munich, Germany DA - 22.06.2015 KW - Macro processing KW - Additive manufacturing KW - Laser metal deposition KW - Ti-6Al-4V KW - Inconel 718 KW - Process chain KW - Deposition rate PY - 2015 SP - 1 EP - 6 AN - OPUS4-33778 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey T1 - Mobile vacuum device for laser beam welding of thick materials T2 - 3rd International Conference in Africa and Asia "Welding and Failure Analysis of Engineering Materials", WAFA 2015 CY - Luxor, Egypt DA - 2015-11-02 PY - 2015 AN - OPUS4-34785 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, André A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Impiego di un dispositivo per il vuoto locale di tipo mobile nell'applicazione del processo laser. T1 - Deployment of mobile vacuum device in the application of laser beam welding N2 - Lo sviluppo del pennacchio di vapore durante la saldatura laser di metalli con direzioni di propagazione lungo l'asse del fascio laser comporta una riduzione della potenza del laser assorbita nel keyhole. Questi effetti negativi possono essere notevolmente attenuati mediante l'applicazione di una ridotta pressione ambientale, diminuendo così l'interazione tra il fascio laser ed i prodotti dell'evaporazione, condizione che favorisce la stabilità del processo di saldatura e si traduce in una maggiore profondità di penetrazione. Una tecnica convenzionale utilizza il principio della camera a vuoto, simile a quello utilizzato per la saldatura a fascio elettronico. L'applicazione di questa tecnica è limitata dalle dimensioni della camera e riduce quindi i vantaggi di questo approccio, particolarmente per componenti di grandi dimensioni. Abbiamo dimostrato la possibilità di applicazione del vuoto in forma localizzata con apparecchiature mobili, che consentono di generare una pressione ridotta solo in una piccola zona attorno al keyhole. Utilizzando un dispositivo di chiusura appositamente progettato per la pressione, di tipo mobile, che può essere spostato lungo l'asse del giunto è possibile ottenere una pressione assoluta di circa 200 mbar. Questo è sufficiente per aumentare la profondità di penetrazione di circa il 50%. I campioni di acciaio grado S355 sono stati saldati con una potenza laser incrementale da 5 kW a 12 kW a pressione atmosferica e confrontati con quelli saldati a pressione ambiente di 200 mbar. La valutazione della sezione longitudinale ha rivelato un aumento della profondità di penetrazione dei giunti di circa il 35%. Inoltre, sono stati eseguiti test di saldatura in configurazione di giunti testa a testa con lamiere di 15 mm di spessore con diverse potenze associate al fascio laser eseguiti a pressione atmosferica ed a pressione ambiente ridotta di circa 200 mbar. L'aumento nella profondità di penetrazione fino al 40% è relativo alla pressione ridotta. In particolare, basse velocità di saldatura con pressione ridotta si sono rivelate particolarmente vantaggiose in termini di aumento della penetrazione. N2 - The development of the vapour plume during the laser beam welding of metals with propagation directions along the laser beam axis leads to a reduction of the absorbed laser power in the keyhole. These unfavourable effects can be significantly mitigated by the application of a reduced ambient pressure thus decreasing the interaction between the laser beam and evaporation products, which leads to more stable welding process and results in increased penetration depth. A conventional technique use a vacuum chamber principle, similar to that, used for electron beam welding. Application of this technique is restricted by the chamber size and reduces thus the advantages of this approach especially for large components. We demonstrate a possibility of mobile local vacuum application, which allows to generate a reduced pressure only in small region around the keyhole. By using of specially designed mobile pressure lock which can be moved along the welding direction absolute pressure of around 200 mbar could be obtained. This is sufficient to increase the welding depth by around 50%. Samples from S355 were welded with an incremental laser power from 5 kW to 12 kW at atmospheric pressure and compared to those welded at ambient pressure of 200 mbar. The evaluation of the longitudinal section revealed an increase of the welding depth by about 35%. Furthermore, the welding trials in butt joint configuration on 15 mm thick plates at various laser beam power performed for atmospheric and reduced ambient pressure of around 200 mbar. The increase in welding depth up to 40% was established for reduced pressure. Particularly, low welding speeds under reduced pressure were especially advantageous in terms of increasing the welding depth. KW - laser welding KW - Laserstrahlschweißen KW - vacuum KW - local effects KW - Vakuum KW - Lokale Effekte PY - 2016 SN - 0035-6794 VL - 04 IS - 04 SP - 1 EP - 8 AN - OPUS4-35619 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Avilov, Vjaceslav A1 - Fritzsche, André A1 - Bachmann, Marcel A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Full penetration laser beam welding of thick duplex steel plates with electromagnetic weld pool support N2 - Full penetration high power bead-on-plate laser beam welding tests of up to 20 mm thick 2205 duplex steel plates were performed in PA position. A contactless inductive electromagnetic (EM) weld pool support system was used to prevent gravity drop-out of the melt. Welding experiments with 15 mm thick plates were carried out using IPG fiber laser YLR 20000 and Yb:YAG thin disk laser TruDisk 16002. The laser power needed to achieve a full penetration was found to be 10.9 and 8.56 kW for welding velocity of 1.0 and 0.5 m min−1, respectively. Reference welds without weld pool support demonstrate excessive root sag. The optimal value of the alternating current(AC) power needed to completely compensate the sagging on the root side was found to be ≈1.6 kW for both values of the welding velocity. The same EM weld pool support system was used in welding tests with 20 mm thick plates. The laser beam power (TRUMPF Yb:YAG thin disk laser TruDisk 16002) needed to reach a full penetration for 0.5 m min−1 was found to be 13.9 kW. Full penetration welding without EM weld pool support is not possible—the surface tension cannot stop the gravity drop-out of the melt. The AC power needed to completely compensate the gravity was found to be 2 kW. KW - Electromagnetic weld pool control KW - Duplex stainless steel KW - Laser beam welding KW - Full penetration welding PY - 2016 DO - https://doi.org/10.2351/1.4944103 SN - 1042-346X SN - 1938-1387 VL - 28 IS - 2 SP - 022420-1 EP - 022420-7 PB - American institute of physics CY - Woodbury, NY, USA AN - OPUS4-35668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey T1 - Laser beam welding of thick materials under the influence of local reduced ambient pressure T2 - 8. International Conference "Beam Technologies and Laser Application" CY - St. Petersburg, Russia DA - 2015-09-21 PY - 2015 AN - OPUS4-34403 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sohail, M. A1 - Han, S.-W. A1 - Na, S.-J. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Numerical investigation of energy input characteristics for high-power fiber laser welding at different positions N2 - Partial penetration welding with a fiber laser at a 9-kW laser power was carried out on 20-mm-thick plates at different positions and analyzed by both experimental and numerical methods. Experiments were carried out for four different angular positions at 1.5 m/min welding speed. All four cases showed a tail-like structure of molten pool on the top surface. The in-depth mechanisms of the energy input characteristics in fiber laser position welding for eight different positions were studied by numerical simulation using the volume-of-fluid (VOF) method. Experimental and numerical results were compared for four cases and showed fair agreement. Observation of flow pattern and bead shape revealed that gravity had little influence on bead shape and flow structure, but changed the pore structure considerably. Flow structure showed a periodic behavior which probably nullified the effect of gravity in position welding. Most of the laser rays reached the bottom of the keyhole without interruption and then multiple reflections started within the keyhole. The first five reflections inside the keyhole delivered around 70 % of the total energy. KW - Laser keyhole welding KW - Fiber laser KW - Partial penetration KW - Position welding KW - Pipe welding PY - 2015 DO - https://doi.org/10.1007/s00170-015-7066-6 SN - 0268-3768 SN - 1433-3015 VL - 80 IS - 5 SP - 931 EP - 946 PB - Springer CY - London AN - OPUS4-35121 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, André A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Mobile vacuum device for laser beam welding of thick materials N2 - The development of the vapour plume during the laser beam welding of metals with propagation directions along the laser beam axis leads to a reduction of the absorbed laser power in the keyhole. These unfavourable effects can be significantly mitigated by the application of a reduced ambient pressure thus decreasing the interaction between the laser beam and evaporation products, which leads to more stable welding process and results in increased penetration depth. A conventional technique use a vacuum chamber principle, similar to that, used for electron beam welding. Application of this technique is restricted by the camera size and reduces thus the advantages of this approach especially for large components. We demonstrate a possibility of mobile local vacuum application, which allows to generate a reduced pressure only in small region around the keyhole. By using of specially designed mobile pressure lock which can be moved along the welding direction absolute pressure of around 200 mbar could be obtained. This is sufficient to increase the welding depth by around 50%. Coupons from S355 were welded with an incremental laser power from 5 kW to 12 kW at atmospheric pressure and compared to those welded at ambient pressure of 200 mbar. The evaluation of the longitudinal section revealed an increase of the welding depth by about 35%. Furthermore, the welding trials in butt joint configuration on 15 mm thick plates at various laser beam power performed for atmospheric and reduced ambient pressure of around 200 mbar. The increase in welding depth up to 40% was established for reduced pressure. Particularly, low welding speeds under reduced pressure were especially advantageous in terms of increasing the welding depth. T2 - 3rd International conference in Africa and Asia "Welding and failure analysis of engineering materials" CY - Luxor, Egypt DA - 02.11.2015 KW - High power laser beam welding KW - Mobile vacuum KW - Local reduced pressure KW - Vapour plume KW - Keyhole PY - 2015 SP - 1 EP - 7 AN - OPUS4-35094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Using the optical measuring techniques to investigate the hot cracking susceptibility laser welded joints N2 - The safety of components or constructions is of great importance in the manufacturing and processing of metallic materials. Solidification cracking as well as the weldability of materials remain still for many years a highly contentious issues, particularly with regard to the causes of the hot crack formation. Many of studies have been conducted to determine the critical condition of occurrence of the solidification cracking. In this study different digital image correlation measuring techniques in conjunction with laser diodes as the illuminating source have been employed to measure the arising strain field during the laser welding process at the surface of the workpiece directed to the laser beam in the close vicinity of the weld pool. The Controlled Tensile Weldability test (CTW) was used to apply an external tensile load during the laser beam welding in order to generate the solidification cracks. The results showed that by means of those techniques it is possible to measure the strain field without any disturbances from the intense welding light or the smoke. Additionally, the strain and the strain rate as a critical factor determining solidification crack formation can be measured and analyzed. T2 - LiM 2015 - Lasers in manufacturing conference 2015 CY - Munich, Germany DA - 22.06.2015 KW - Solidification cracking KW - Laser beam wlding KW - Optical measuring technique KW - Hot cracking test PY - 2015 SP - 1 EP - 7 AN - OPUS4-35100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, André A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser beam welding of thick materials under the influence of local reduced ambient pressure N2 - The development of the vapour plume during the laser beam welding of metals with propagation directions along the laser beam axis leads to a reduction of the absorbed laser power in the keyhole. The main reasons are the scattering of the laser radiation on the condensed phase of metallic vapour as well as the defocusing of the laser beam due to the density gradient in the vapour plume. These unfavourable effects can be significantly mitigated by the application of a reduced ambient pressure thus decreasing the interaction between the laser beam and evaporation products, which leads to more stable welding process and results in increased penetration depth, as known from previous studies. A conventional technique use a vacuum chamber principle, similar to that, used for electron beam welding. Application of this technique is restricted by the chamber size and reduces thus the advantages of this approach especially for large components. We demonstrate a possibility of mobile local vacuum application, which allows to generate a reduced pressure only in small region around the keyhole. By using of specially designed mobile pressure lock which can be moved along the welding direction absolute pressure of around 200 mbar could be obtained. This is sufficient to increase the welding depth by around 50%. Coupons from S355 were welded with an incremental laser power from 5 kW to 12 kW at atmospheric pressure and compared to those welded at ambient pressure of 200 mbar. The evaluation of the longitudinal section revealed an increase of the welding depth by about 35%. Furthermore, the welding trials in butt joint configuration on 15 mm thick plates at various laser beam power performed for atmospheric and reduced ambient pressure of around 200 mbar. The increase in welding depth up to 40% was established for reduced pressure. Particularly, low welding speeds under reduced pressure were especially advantageous in terms of increasing the welding depth. T2 - VIII BTLA 2015 - 8th International conference "Beam technologies & laser application" CY - St. Petersburg, Russia DA - 21.09.2015 KW - High power laser beam welding KW - Mobile vacuum KW - Local reduced pressure KW - Vapour plume KW - Keyhole PY - 2015 SP - 45 EP - 46 AN - OPUS4-34973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of hot crack susceptibility of laser welded joints of four austenitic steels N2 - Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack is for most fusion welding processes a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding standardization and research. In this study a new investigation programme has been developed to qualify the hot cracking susceptibility of a variety of austenitic stainless steels. The results show the possibility of using this technique to determinate the critical values that occur with initiation of solidification cracking during laser beam welding T2 - The METEC and 2nd European Steel Technology and Application Days CY - Düsseldorf, Germany DA - 15.06.2015 KW - Laser beam welding KW - Hot cracking KW - Solidification cracking KW - Hot cracking test PY - 2015 SP - 1 EP - 5 AN - OPUS4-36525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Experimental study and numerical simulation of hot crack formation for novel laser weldability test. N2 - Laser beam welding is a widely established manufacturing process in several industries. The solidification cracking seriously effecting the safety of welded joints could arise during the beam welding of stainless steels caused by high solidification rates. In this study the controlled tensile weldability test (CTW) was used to investigate the solidification cracking susceptibility the fully austenitic stainless steels CrMnNi (1.4376), CrNi (1.4301), CrNiMo (1.4404) and CrNiSi (1.4828) during laser beam welding. The test facility allows welding of specimens with simultaneous application of tensile load along or cross to the welding direction while the speed of tensile force application is either constant or increases linearly. The tensile force increment and/or the displacement are set by means of a CNC controller. Trials were conducted by varying the ultimate tensile strain and cross-head speed while keeping the welding parameters constant. By observing the crack-no crack behaviour and estimating the generated crack length for each trail using a new optimized experimental procedure the influence of the two important conditions (the strain and the strain rate) for the formation of solidification cracks can be investigated, the critical values of strain and strain rate that are responsible for solidification cracking formation have been determined. In the present study a three-dimensional FEM using the contact element technique was developed to simulate the solidification cracking during laser full penetration welding under external load conditions for the steel 1.4376 in order to get a better understanding of the mechanisms of hot crack initiation and the theoretical results were compared to the experimental ones. By comparing the resulting solidification crack with simulated crack, it is possible to determine the critical condition of solidification crack formation in the region where the strains and the strain rates cannot be measured due to the high temperature. The results show a good agreement between numerical calculation and experiment. It is proposed that the solidification cracking susceptibility may be predicted by FEM analysis by using the correct mechanical and thermo-physical constants of the materials. T2 - BEAM TECHNOLOGIES & LASER APPLICATION CY - St. Petersburg, Russia DA - 21.09.2015 KW - Solidification cracking KW - Hot cracking test KW - FEM KW - Laser beam welding PY - 2015 SN - 978-5-7422-5150-7 SP - 55 EP - 68 AN - OPUS4-36615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - El-Batahgy, A.M. T1 - Laser and hybrid laser-arc welding of cryogenic 9 % NI Steel N2 - Heat treated 9%Ni steel is considered the most suitable and economic material for construction of large-size liquefied natural gas (LNG) storage tanks which operate at cryogenic temperatures (-196°C). Strength above 700 MPa as well as a minimum impact value of 60 J are required to ensure reliable operation of the LNG tanks at operating temperature. Conventional arc welding processes, including shielded metal arc welding, gas metal arc welding, gas tungsten arc welding and submerged arc welding, are currently used in construction of LNG tanks. Ni based filler wire is the preferred filler metal of choice in LNG tank construction. The main problem with this choice is the lower mechanical properties, particularly tensile strength of the weld metal. To compensate, the wall thickness needs to be excessively thick to ensure the strength of the welded structures. Ni based filler material is expensive and a large quantity is needed to fill the multi-pass weld grooves. These factors significantly add to the cost in the fabrication of LNG storage tanks. For these reasons, exploration of new welding technologies is a priority. A big potential can be seen in laser based welding techniques. Laser beam welding results in much smaller fusion zone with chemical composition and mechanical properties similar to that of the base material. Laser welding is a much faster process and allows for a joint geometry which requires less filler material and fewer welding passes. The advantages of laser welding can help to overcome the problems pointed out above. Trials of autogenous laser welding, laser cold-wire welding and hybrid laser-arc welding conducted on the 9%Ni steel are presented in this paper. Chemical composition of the weld metal as well as effects of welding parameters on the weld formation, microstructure and tensile strength is discussed. Filler wire penetration depth as well as character of its distribution in the narrow laser welds was examined using EPMA - electron probe microanalysis. KW - hardness KW - cryogenic steel KW - laser welding KW - microstructure KW - tensile strength PY - 2016 UR - http://gns.mephi.ru/sites/default/files/journal/file/en.2016.1-4.pdf SN - 2499-9733 VL - 1 IS - 18 SP - 34 EP - 45 PB - Research Nuclear University MEPHl CY - Moskau, Russia AN - OPUS4-36553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frei, J. A1 - Suwala, H. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Bestimmung der Rissanfälligkeit von hochfesten Stählen beim Widerstandspunktschweißen N2 - Die stetig zunehmenden Anforderungen an Kraftstoffverbrauch, Schadstoffemission, sowie passive Sicherheit haben die Automobilindustrie vor Herausforderungen gestellt, die nur durch einen konsequenten Einsatz moderner hochfester Stahlwerkstoffe zu bewältigen sind. Obgleich eine generelle Eignung dieser Stähle für das Widerstandspunktschweißen (WPS) gegeben ist, kann es durch verschiedene externe Einflüsse im betrieblichen Umfeld zur Rissbildung in der Schweißverbindung kommen. Der Einfluss dieser Risse auf die mechanischen Eigenschaften ist derzeit nicht hinreichend genau erfasst, so dass häufig die Vorgabe einer rissfreien Schweißverbindung besteht. Die Kenntnis der Rissanfälligkeit der verarbeiteten Materialkombinationen sowie von ungünstigen Schweißparametern ist daher für viele Unternehmen von erheblicher wirtschaftlicher Bedeutung. Im Rahmen des FOSTA Projekts P921 „Entwicklung eines Verfahrens zur Bestimmung der Rissanfälligkeit von hochfesten Stählen beim Widerstandspunktschweißen“ wurde ein Ansatz zur Bestimmung der Rissanfälligkeit von WPS-Verbindungen hochfester Stähle entwickelt. Mittels einer hydraulischen Vorrichtung unter Zugbelastung wurden geschweißte, rissbehaftete Proben optisch ausgewertet. Das Verfahren ist geeignet, um ein Werkstoffranking bezüglich der Rissanfälligkeit beim Widerstandspunktschweißen für Werkstoffe aufzustellen. KW - Widerstandspunktschweißen KW - Werkstoffranking KW - Rissanfälligkeit KW - hochfeste Stähle KW - Liquid Metal Embrittlement KW - Lötrissigkeit PY - 2016 DO - https://doi.org/10.3139/120.110904 VL - 58 IS - 7-8 SP - 612 EP - 616 PB - Carl Hanser Verlag CY - München AN - OPUS4-37161 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -