TY - JOUR A1 - Dabah, Eitan A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Kardjilov, N. A1 - Manke, I. A1 - Boin, M. A1 - Woracek, R. A1 - Griesche, Axel T1 - Time-resolved Bragg-edge neutron radiography for observing martensitic phase transformation from austenitized super martensitic steel N2 - Neutron Bragg-edge imaging was applied for the visualization of a γ-Austenite to α'-martensite phase transformation. In the present study, a super martensitic stainless steel sample was heated until complete austenitization and was subsequently cooled down to room temperature. The martensitic phase Transformation started at Ms = 190 °C. Using a monochromatic neutron beam with λ = 0.390 nm, the transmitted intensity was significantly reduced during cooling below Ms, since the emerging martensitic phase has a higher attenuation coefficient than the austenitic phase at this wavelength. The phase Transformation process was visualized by filming the transmission images from a scintillator screen with a CCD camera with a temporal resolution of 30 s and a spatial resolution of 100 µm. KW - Neutron imaging KW - Bragg-edge imaging KW - Phase transformation PY - 2017 U6 - https://doi.org/10.1007/s10853-016-0642-9 SN - 0022-2461 SN - 1573-4803 VL - 52 IS - 6 SP - 3490 EP - 3496 AN - OPUS4-38574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -