TY - CONF A1 - Girod, Matthias T1 - Online characterization of silver nanoparticles from continuous synthesis with scattering methods T2 - HZB User Meeting 2012 CY - Berlin, Germany DA - 2012-12-12 PY - 2012 AN - OPUS4-27606 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Girod, Matthias A1 - Vogel, Stefanie A1 - Szczerba, Wojciech A1 - Thünemann, Andreas T1 - How temperature determines formation of maghemite nanoparticles N2 - We report on the formation of polymer-stabilized superparamagnetic single-core and multi-core maghemite nanoparticles. The particle formation was carried out by coprecipitation of Fe(II) and Fe(III) sulfate in a continuous aqueous process using a micromixer system. Aggregates containing 50 primary particles with sizes of 2 nm were formed at a reaction temperature of 30 °C. These particles aggregated further with time and were not stable. In contrast, stable single-core particles with a diameter of 7 nm were formed at 80 °C as revealed by small-angle X-ray scattering (SAXS) coupled in-line with the micromixer for particle characterization. X-ray diffraction and TEM confirmed the SAXS results. X-ray absorption near-edge structure spectroscopy (XANES) identified the iron oxide phase as maghemite. KW - Iron Oxide Nanoparticles KW - Micromixer KW - SAXS KW - XANES KW - Carboxydextran KW - Nanotechnology PY - 2015 DO - https://doi.org/10.1016/j.jmmm.2014.09.057 SN - 0304-8853 VL - 380 SP - 163 EP - 167 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-32564 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Orts Gil, Guillermo A1 - Natte, Kishore A1 - Thiermann, Raphael A1 - Girod, Matthias A1 - Rades, Steffi A1 - Kalbe, Henryk A1 - Thünemann, Andreas A1 - Maskos, M. A1 - Österle, Werner T1 - On the role of surface composition and curvature on biointerface formation and colloidal stability of nanoparticles in a protein-rich model system N2 - The need for a better understanding of nanoparticle–protein interactions and the mechanisms governing the resulting colloidal stability has been emphasised in recent years. In the present contribution, the short and long term colloidal stability of silica nanoparticles (SNPs) and silica–poly(ethylene glycol) nanohybrids (Sil–PEG) have been scrutinised in a protein model system. Well-defined silica nanoparticles are rapidly covered by bovine serum albumin (BSA) and form small clusters after 20 min while large agglomerates are detected after 10 h depending on both particle size and nanoparticle–protein ratio. Oppositely, Sil–PEG hybrids present suppressive protein adsorption and enhanced short and long term colloidal stability in protein solution. No critical agglomeration was found for either system in the absence of protein, proving that instability found for SNPs must arise as a consequence of protein adsorption and not to high ionic environment. Analysis of the small angle X-ray scattering (SAXS) structure factor indicates a short-range attractive potential between particles in the silica-BSA system, which is in good agreement with a protein bridging agglomeration mechanism. The results presented here point out the importance of the nanoparticle surface properties on the ability to adsorb proteins and how the induced or depressed adsorption may potentially drive the resulting colloidal stability. KW - Nanoparticles KW - Protein corona KW - Biointerface KW - BSA KW - PEG KW - Colloidal stability PY - 2013 DO - https://doi.org/10.1016/j.colsurfb.2013.02.027 SN - 0927-7765 SN - 1873-4367 VL - 108 SP - 110 EP - 119 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-30100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Böhmert, L. A1 - Girod, Matthias A1 - Hansen, Ulf A1 - Maul, Ronald A1 - Knappe, Patrick A1 - Niemann, B. A1 - Weidner, Steffen A1 - Thünemann, Andreas A1 - Lampen, A. T1 - Analytically monitored digestion of silver nanoparticles and their toxicity on human intestinal cells N2 - Orally ingested nanoparticles may overcome the gastrointestinal barrier, reach the circulatory system, be distributed in the organism and cause adverse health effects. However, ingested nanoparticles have to pass through different physicochemical environments, which may alter their properties before they reach the intestinal cells. In this study, silver nanoparticles are characterised physicochemically during the course of artificial digestion to simulate the biochemical processes occurring during digestion. Their cytotoxicity on intestinal cells was investigated using the Caco-2 cell model. Using field-flow fractionation combined with dynamic light scattering and small-angle X-ray scattering, the authors found that particles only partially aggregate as a result of the digestive process. Cell viabilities were determined by means of CellTiter-Blue® assay, 4',6-diamidino-2-phenylindole-staining and real-time impedance. These measurements reveal small differences between digested and undigested particles (1–100 µg/ml or 1–69 particles/cell). The findings suggest that silver nanoparticles may indeed overcome the gastrointestinal juices in their particulate form without forming large quantities of aggregates. Consequently, the authors presume that the particles can reach the intestinal epithelial cells after ingestion with only a slight reduction in their cytotoxic potential. The study indicates that it is important to determine the impact of body fluids on the nanoparticles of interest to provide a reliable interpretation of their nano-specific cytotoxicity testing in vivo and in vitro. KW - Silver nanoparticles KW - In vitro digestion KW - Field-flow fractionation KW - Small-angle X-ray scattering KW - Dynamic light scattering KW - Caco-2 cells PY - 2014 DO - https://doi.org/10.3109/17435390.2013.815284 SN - 1743-5390 SN - 1743-5404 VL - 8 IS - 6 SP - 631 EP - 642 PB - Informa Healthcare CY - London AN - OPUS4-29926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sobisch, T. A1 - Emmerling, Franziska A1 - Girod, Matthias A1 - Menzel, Michael A1 - Lerche, D. T1 - Advantages of dual wavelength detection for size determination of nanoparticles with analytical centrifugation KW - Particle size distributions KW - Dual wavelength detection KW - Analytical centrifugation KW - Nanoparticle separation PY - 2013 SN - 978-3-944261-28-7 SN - 978-3-944261-36-2 SN - 978-3-944261-52-2 VL - 4 SP - 9 EP - 11 AN - OPUS4-30802 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Girod, Matthias T1 - Analysis of Aggregation of Silver nanoparticles by Small-angle X-ray Scattering T2 - 16. Tagung für Festkörperanalytik CY - Vienna, Austria DA - 2011-07-04 PY - 2011 AN - OPUS4-24224 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mandel, K. A1 - Szczerba, Wojciech A1 - Thünemann, Andreas A1 - Riesemeier, Heinrich A1 - Girod, Matthias A1 - Sextl, G. T1 - Nitric acid-stabilized superparamagnetic iron oxide nanoparticles studied with X-rays N2 - Agglomerated superparamagnetic iron oxide nanoparticles can easily and in large scale be precipitated from iron salt solutions. Although the process is well known, it is ambiguously either assumed that magnetite or maghemite is obtained. The first part of our study clarifies this question using X-ray absorption spectroscopy. For further processing of the nanoparticles, i.e., for giving them a surface functionality or incorporating them into composites, it is important to break the agglomerates and individualize the particles at first. This can effectively be done with nitric acid treatment. The influence of this process on the particles chemistry and structure was analyzed in great detail using X-ray diffraction, X-ray absorption, and smallangle X-ray scattering. In contrast to our expectation, no oxidation from magnetite (Fe3O4) to maghemite (γ- Fe2O3) was found; the formal valence of the particles in any case is magnetite (Fe3O4). Instead, an increase in the particles' surface disorder was discovered from X-ray absorption analyses and high-resolution transmission electron microscopy. The acid treatment roughens and distorts the surface of the nanoparticles which is connected with an increased spin disorder. KW - XANES KW - EXAFS KW - SAXS KW - Coprecipitation KW - Iron oxide spectra KW - Ferrofluid PY - 2012 DO - https://doi.org/10.1007/s11051-012-1066-3 SN - 1388-0764 SN - 1572-896X VL - 14 IS - 8 SP - 1066/1 EP - 9 PB - Kluwer CY - Dordrecht AN - OPUS4-26357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Girod, Matthias T1 - The impact of digestion on the physicochemical properties of silver nanoparticles and their toxicity for intestinal cells T2 - SAS2012 CY - Sydney, Australia DA - 2012-11-19 PY - 2012 AN - OPUS4-27183 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Girod, Matthias T1 - Online characterization of silver nanoparticles from continuous synthesis with scattering methods T2 - SAS2012 CY - Sydney, Australia DA - 2012-11-19 PY - 2012 AN - OPUS4-27187 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -