TY - JOUR A1 - Gea, M. A1 - Bonetta, S. A1 - Iannarelli, L. A1 - Giovannozzi, A. M. A1 - Maurino, V. A1 - Bonetta, S. A1 - Hodoroaba, Vasile-Dan A1 - Armato, C. A1 - Rossi, A. M. A1 - Schilirò, T. T1 - Shape-engineered titanium dioxide nanoparticles (TiO2-NPs): cytotoxicity and genotoxicity in bronchial epithelial cells JF - Food and Chemical Toxicology N2 - The aim of this study was to evaluate cytotoxicity (WST-1 assay), LDH release (LDH assay) and genotoxicity (Comet assay) of three engineered TiO2-NPs with different shapes (bipyramids, rods, platelets) in comparison with two commercial TiO2-NPs (P25, food grade). After NPs characterization (SEM/T-SEM and DLS), biological effects of NPs were assessed on BEAS-2B cells in presence/absence of light. The cellular uptake of NPs was analyzed using Raman spectroscopy. The cytotoxic effects were mostly slight. After light exposure, the largest cytotoxicity (WST-1 assay) was observed for rods; P25, bipyramids and platelets showed a similar effect; no effect was induced by food grade. No LDH release was detected, confirming the low effect on plasma membrane. Food grade and platelets induced direct genotoxicity while P25, food grade and platelets caused oxidative DNA damage. No genotoxic or oxidative damage was induced by bipyramids and rods. Biological effects were overall lower in darkness than after light exposure. Considering that only food grade, P25 and platelets (more agglomerated) were internalized by cells, the uptake resulted correlated with genotoxicity. In conclusion, cytotoxicity of NPs was low and affected by shape and light exposure, while genotoxicity was influenced by cellular-uptake and aggregation tendency. KW - Nanoparticles KW - Shape-engineered KW - Raman spectroscopy KW - Genotoxic and oxidative damage KW - Cytotoxicity PY - 2019 UR - https://www.sciencedirect.com/science/article/pii/S0278691519301036?via%3Dihub DO - https://doi.org/10.1016/j.fct.2019.02.043 SN - 0278-6915 SN - 1873-6351 VL - 127 SP - 89 EP - 100 PB - Elsevier AN - OPUS4-47532 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Giovannozzi, A. A1 - Gradt, Thomas A1 - Häusler, Ines A1 - Rossi, A. A1 - Wetzel, B. A1 - Zhang, G. A1 - Dmitriev, A.I. T1 - Exploring the potential of Raman spectroscopy for the identification of silicone oil residue and wear scar characterization for the assessment of tribofilm functionality JF - Tribology International N2 - We applied a combination of Raman spectroscopy (RS) and cross-sectional transmission electron microscopy (X-TEM) to identify silicone oil residues and tribofilms at steel disc surfaces after tribological testing. Neither chemical cleaning nor mechanical removal of a 50 µm thick surface layer produced a surface without any silicone residue. Nevertheless, long-term tribological properties are not affected due to silicone degradation which has been proved by Raman spectroscopy. Excellent anti-wear and anti-friction properties of a nanocomposite at severe stressing conditions correlated with the formation of a silica-based tribofilm containing amorphous and graphite-like carbon nanoparticles. Since reliable carbon quantification by analytical TEM is difficult, RS is a useful complementary method for carbon identification at wear scars. KW - Raman spectroscopy KW - Cross-sectional TEM KW - Silicone oil residue KW - Tribofilm PY - 2015 DO - https://doi.org/10.1016/j.triboint.2015.04.046 SN - 0301-679X VL - 90 SP - 481 EP - 490 PB - Butterworth-Heinemann CY - Oxford AN - OPUS4-33421 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -