TY - JOUR A1 - Günther, Martin A1 - Levchik, S. V. A1 - Schartel, Bernhard T1 - Bubbles and collapses: Fire phenomena of flame-retarded flexible polyurethane foams N2 - Flexible polyurethane foams (FPUF) are easy to ignite and exhibit rapid flame spread. In this paper, the fire phenomena of two standard foam formulations containing tris (1,3-dichloro-2-propyl) phosphate (FR-2) and a halogen-freepoly (ethyl ethylene phosphate) (PNX), respectively, as flame retardants are compared. A multimethodological approach is proposed which combines standard fire tests as well as new investigatory approaches. The thermophysical properties of the foams were determined by thermogravimetric analysis (TG), reaction to small flames was studied by means of the limiting oxygen index (LOI) and UL 94 HBF test, and the burning behavior was investigated with the cone calorimeter. Further, temperature development in burning cone calorimeter samples was monitored using thermocouples, and rheological measurements were performed on pyrolyzed material, delivering insight into the dripping behavior of the foams. This paper gives comprehensive insight into the fire phenomena of flame-retarded FPUFs that are driven by the two-step decomposition behavior of the foams. LOI and UL 94 HBF tests showed a reduced flammability and reduced tendency to drip for the flame-retarded foams. TG and cone calorimeter measurements revealed that the two-step decomposition behavior causes two stages during combustion, namely structural collapse and pool fire. The flame-retardant mode of action was identified to take place primarily during the foam collapse and be based mainly on flame inhibition. However, some condensed-phase action was been measured, leading to significantly increased melt viscosity and improved dripping behavior for foams containing PNX. KW - Burning behavior KW - Flame retardant KW - Flexible PU foam PY - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-512145 SN - 1042-7147 SN - 1099-1581 VL - 31 IS - 10 SP - 2185 EP - 2198 PB - Wiley Online Libary AN - OPUS4-51214 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schartel, Bernhard A1 - Günther, Martin T1 - Flame retardancy of polyurethanes N2 - Polyurethanes (PU) represent one of the most versatile classes of plastics. They are processed and used as thermoplastic, elastomer, and thermoset. The requirements regarding flammability are correspondingly versatile. Depending on the material and the field of application, specific fire tests have to be fulfilled. This paper describes the different concepts used to fulfil these requirements by choosing the right raw materials and flame retardants. KW - Polyurethane KW - Flame retardant KW - Foam KW - Flammability KW - Pyrolysis KW - Cone calorimeter PY - 2020 VL - 17 IS - 1 SP - 44 EP - 48 PB - Dr. Gupta AN - OPUS4-50737 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schartel, Bernhard A1 - Günther, Martin T1 - Flammschutz von Polyurethanen N2 - Polyurethane (PU) bilden eine der vielseitigsten Klassen der Polymerwerkstoffe. Kein anderer Kunststoff wird sowohl als Thermoplast, als Elastomer wie auch als Duroplast verarbeitet und eingesetzt. Entsprechend vielfältig sind auch die Anforderungen an den Flammschutz. Je nach Material und Anwendung müssen spezifische Brandnormen erfüllt werden. Der vorliegende Aufsatz gibt einen Überblick über die verfügbaren Ansätze, um durch geeignete Auswahl der Rohstoffe und der Flammschutzmittel diese verschiedensten Anforderungen an das Brandverhalten zu erfüllen. KW - Polyurethan KW - Flammschutz KW - Pyrolyse KW - Schaum KW - Cone calorimeter PY - 2020 VL - 20 IS - 1 SP - 48 EP - 53 PB - Dr. Gupta AN - OPUS4-50736 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lenz, J. A1 - Pospiech, D. A1 - Paven, M. A1 - Albach, R. W. A1 - Günther, Martin A1 - Schartel, Bernhard A1 - Voit, B. T1 - Improving the Flame Retardance of Polyisocyanurate Foams by Dibenzo[d,f][1,3,2]dioxaphosphepine 6-Oxide-Containing Additives N2 - A series of new flame retardants (FR) based on dibenzo[d,f][1,3,2]dioxaphosphepine 6-oxide (BPPO) incorporating acrylates and benzoquinone were developed previously. In this study, we examine the fire behavior of the new flame retardants in polyisocyanurate (PIR) foams. The foam characteristics, thermal decomposition, and fire behavior are investigated. The fire properties of the foams containing BPPO-based derivatives were found to depend on the chemical structure of the substituents. We also compare our results to state-of-the-art non-halogenated FR such as triphenylphosphate and chemically similar phosphinate, i.e. 9,10-dihydro-9-oxa-10- phosphaphenanthrene-10-oxide (DOPO), based derivatives to discuss the role of the phosphorus oxidation state. KW - Polyisocyanurate KW - Dibenzo[d,f][1,3,2]dioxaphosphepine 6-oxide KW - Phospha-Michael addition KW - Flame retardant KW - Foams PY - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-485590 SN - 2073-4360 VL - 11 IS - 8 SP - Article 1242 PB - MDPI AN - OPUS4-48559 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günther, Martin A1 - Lorenzetti, A. A1 - Schartel, Bernhard T1 - Bubbles and Collapses: Fire Phenomena of Polyurethane Foams N2 - This work investigates the fire phenomena of rigid polyurethane foams (RPUFs) in detail. To elucidate structure-property relationships, systematically varied sets of materials were prepared covering polyurethane, polyisocyanurate-polyurethane and flame retarded polyurethane foams. Advanced cone calorimeter investigations provide insight into the fire behavior under forced flaming conditions. Thermocouples inside specimens give information about the temperature gradient during combustion. Furthermore, fire phenomena were characterized using cross sections of quenched samples and the scanning electron microscope. By using a Multi methodological approach and systematically varied sets of foam materials, new insights into the burning of RPUFs were won. For the flame retarded foams, the dominant flame retardant mode of action changed with density. PIR foams exhibited a cellular structure in the residue leading to the superior fire performance compared to polyurethane foams. The understanding of fire phenomena contributes to future development of tailored flame retardant strategies for RPUFs. T2 - AOFSM’3, 3rd Asia-Oceania Symposium for Fire Safety Materials Science and Engineering CY - Shanghai, China DA - 24.10.2019 KW - PU-Foam KW - Fire behaviour PY - 2019 AN - OPUS4-49457 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Günther, Martin A1 - Lorenzetti, A. A1 - Schartel, Bernhard T1 - From Cells to Residues: Flame-Retarded Rigid Polyurethane Foams N2 - Rigid polyurethane foams (RPUFs) exhibit short times to ignition as well as rapid flame spread and are therefore considered to be hazardous materials. This paper focuses on the fire phenomena of RPUFs, which were investigated through a multimethodological approach. Water-blown polyurethane (PUR) foams without flame retardants (FRs) as well as waterblown PUR foams containing triethyl phosphate as a gas phase-active FR were examined. The aim of this study is to clarify the influence of the FR on the fire phenomena during combustion of the foams. Additionally, materials’ densitieswere varied to range from 30 to 100 kg/m3. Thermophysical properties were studied bymeans of thermogravimetry; fire behavior and flammability were investigated via cone calorimeter and limiting Oxygen index, respectively. During the cone calorimeter test, the temperature development inside the burning specimens was monitored with thermocouples, and cross sections of quenched specimens were examined visually, giving insight into the morphological changes during combustion. The present paper delivers a comprehensive study, illuminating phenomena occurring during foam combustion and the influence of a FR active in the gas phase. The superior fire performance of flameretarded PUR foams was found to be based on flame inhibition, and on increased char yield leading to a more effective protective layer. It was proven that in-depth absorption of radiation is a significant factor for estimation of time to ignition. Cross sections investigated with the electron scanning microscope exhibited a pyrolysis front with an intact foam structure underneath. The measurement of temperature development inside burning specimens implied a shift of burning behavior towards that of non-cellular materials with rising foam density. KW - Polyurethane KW - Rigid foams KW - Fire behavior PY - 2020 U6 - https://doi.org/10.1080/00102202.2019.1634060 SN - 0010-2202 SN - 1563-521X VL - 192 IS - 12 SP - 2209 EP - 2237 PB - Taylor & Francis AN - OPUS4-51483 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trela, C. A1 - Kind, Thomas A1 - Günther, Martin T1 - Ground penetrating radar in reflection vs transmission mode for void detection in concrete structures N2 - The concreting of prefabricated concrete structures can lead to insufficient bonding or even to remaining cavities. Honeycombs (aggregate clusters without cement) represent potential weakening of the structure and need to be detected non-destructively. In our study we tested the capability of ground penetrating radar (GPR)techniques for this purpose. We applied GPR in reflection mode and zero-offset profiling (ZOP) Transmission mode on a precast concrete twin wall with built-in honeycombs. GPR measurements were performed as twochannel measurement with ground coupled antennas with centre frequencies of 1.5 GHz and 2.6 GHz mounted to an automated scanner system. Our findings show that ZOP transmission measurements are a more efficient method to detect voids in reinforced concrete structures compared to reflection mode measurements. This holds for both the effort needed for the measurement and the evaluation as well as the validity of the data. Honeycombs (basically representing voids) are usually characterized by strongly reduced amplitudes and earlier arrivals of the transmitted wave. T2 - NDT-CE 2015 - International symposium non-destructive testing in civil engineering CY - Berlin, Germany DA - 15.09.2015 KW - Ground penetrating radar KW - Reflection KW - Transmission KW - Reinforced concrete KW - Prefabricated wall KW - Void detection PY - 2015 SN - 1435-4934 SP - 324 EP - 344 PB - Technische Universität Berlin / Bundesanstalt für Materialforschung und -prüfung CY - Berlin, Germany AN - OPUS4-40006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günther, Martin A1 - Lorenzetti, Alessandra A1 - Schartel, Bernhard T1 - Fire phenomena of rigid polyurethane foams N2 - This work investigates the fire phenomena of rigid polyurethane foams (RPUF) in detail. To elucidate structure-property relationships systematically varied sets of foams were prepared. RPUF were synthesized with different densities using water and pentane as blowing agent. What is more, a flame retarded RPUF and rigid polyisocyanurate-polyurethane foams were examined. The comprehensive understanding of the processes taking place during combustion is the foundation of customized development of successful flame retardant approaches. Advanced cone calorimeter investigations provide insight into the fire behavior under forced flaming conditions. Thermocouples in the inside of specimens give information about the temperature gradient and temperature of the pyrolysis zone during combustion. Furthermore, fire phenomena were characterized using SEM, LOI and thermal analysis. By using a multi-methodological approach and systematically varied sets of foam materials, new insights into the burning of RPUF were won. The detailed knowledge of fire phenomena is essential for future development of tailored flame retardant strategies for RPUF. T2 - 15th International Conference on Advances in Foam Materials & Technology, FOAMS 2017 CY - Bayreuth, Germany DA - 11.10.2017 KW - Foam KW - Cone calorimeter KW - Flame retardancy KW - Fire behaviour KW - Polyurethane PY - 2017 AN - OPUS4-42755 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gómez-Fernández, S. A1 - Günther, Martin A1 - Schartel, Bernhard A1 - Corcuera, M. A. A1 - Eceiza, A. T1 - Impact of the combined use of layered double hydroxides, lignin and phosphorous polyol on the fire behavior of flexible polyurethane foams N2 - Flexible polyurethane foams with densities of 40 ± 2 kg m−3 were prepared by combining different ecofriendly fillers such as layered double hydroxides (LDH) and kraft lignin (a byproduct of the pulp and paper industry) with a phosphorous polyol (E560) in order to study their effect on the mechanical performance and fire behavior of the foams. Two series of foams were prepared, some containing lignin or LDH separately, and some with a combination of both: one of the series was prepared without E560 (0E foam series) and the other with 5 parts per hundred of E560 polyol (5E series). The use of fillers resulted in increased viscosity of the reactive mixture, requiring higher blowing agent content in order to hold the density of the foams constant. It was observed that urea phase segregation was favored in the series of 0E foams due to their lower viscosity than the 5E series. This had consequent effects on the resilience, compression force deflection and compression set of these foams. In terms of fire behavior it was observed that while the limiting oxygen index decreased, cone calorimeter results showed that the combination of lignin, LDH and E560 decreased the heat release of the foams. In addition, the combination of fillers and E560 contributed to increase the viscosity of the pyrolysis products, preventing the dripping of the molten polymer, which is a key factor in flame propagation towards adjacent objects in fire scenarios. KW - Ligning KW - Foam KW - Flexible polyurethane foam KW - Flame retardant PY - 2018 SN - 0926-6690 VL - 125 SP - 346 EP - 359 PB - Elsevier B.V. AN - OPUS4-45971 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Günther, Martin A1 - Lorenzetti, A. A1 - Schartel, Bernhard T1 - Fire Phenomena of Rigid Polyurethane Foams N2 - Rigid polyurethane foams (RPUFs) typically exhibit low thermal inertia, resulting in short ignition times and rapid flame spread. In this study, the fire phenomena of RPUFs were investigated using a multi-methodological approach to gain detailed insight into the fire behaviour of pentaneand water-blown polyurethane (PUR) as well as pentane-blown polyisocyanurate Polyurethane (PIR) foams with densities ranging from 30 to 100 kg/m3. Thermophysical properties were studied using thermogravimetry (TG); flammability and fire behaviour were investigated by means of the limiting oxygen index (LOI) and a cone calorimeter. Temperature development in burning cone calorimeter specimens was monitored with thermocouples inside the foam samples and visual investigation of quenched specimens’ cross sections gave insight into the morphological changes during burning. A comprehensive investigation is presented, illuminating the processes taking place during foam combustion. Cone calorimeter tests revealed that in-depth absorption of radiation is a significant factor in estimating the time to ignition. Cross sections examined with an electron scanning microscope (SEM) revealed a pyrolysis front with an intact foam structure underneath, and temperature measurement inside burning specimens indicated that, as foam density increased, their burning behaviour shifted towards that of solid materials. The superior fire performance of PIR foams was found to be based on the cellular structure, which is retained in the residue to some extent. KW - Foam KW - Polyurethane KW - Fire behaviour KW - Flammability PY - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-465577 SN - 2073-4360 VL - 10 IS - 10 SP - 1166-1 EP - 1166-22 PB - MDPI AN - OPUS4-46557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günther, Martin A1 - Lorenzetti, A. A1 - Schartel, Bernhard T1 - Bubbles And Collapses: Fire Phenomena Of Rigid Polyurethane Foams N2 - Rigid polyurethane foams (RPUF) are widely used in industry and daily life because of their outstanding mechanical and thermal insulating properties. While their convenient mechanical characteristics predestine these materials for shock absorption, their low thermal conductivity is responsible for their excellent thermal insulation properties. A principal characteristic affecting not only the use properties, but also the burning behaviour, is the density of RPUF. In case of fire, cellular polymers like RPUF behave differently from bulk materials. The reason for their comparatively high ignitability is the high rate of temperature rise on the surface when exposed to heat, which is due to their cellular structure and characterised as low thermal inertia. The heat build-up on the surface results in a short time to ignition. Therefore foams are able to develop fire and large amounts of smoke within a short period of time. Even though their fire load is quite low because of their low density, their heat release rate is high. These burning properties are not only a consequence of the chemical consistence of such materials, but also a result of their morphology. The aim of the work is to investigate the fire phenomena of RPUF. Characterised by simultaneous physical and chemical processes which interact, depend, and compete with each other, the combustion of RPUF is a highly complex occurrence. Therefore it is necessary to study all aspects in detail. The fire phenomena that were examined are gasification, liquefaction, charring and structural integrity as well as collapse. The melting of cellular polymers and dripping of pyrolysis products, together with the ability to form pool fires, are the main hazards in fires involving foams. Structural collapse via melting or decomposition, or the retention of the foam’s morphology through charring, are the main characteristics of their burning behaviour. Cellular structure is a further important factor influencing the materials’ response to fire, and deserves examination in greater depth. Since the cells in closed-cell foam are filled with the blowing agent used to produce the material, and this blowing agent can be inert (carbon dioxide) or highly flammable (pentane), this component also affects the burning properties and will be investigated. Examination of the influence of the macroscopic morphology, namely the cell size and thickness of cell walls, will contribute to the study. In order to provide comprehensive insight into the processes taking place during combustion, and to elucidate structure-property relationships, a set of foams with systematically varied properties was prepared. RPUF was obtained using water and pentane as a blowing agent. Besides RPUF, a flame-retarded RPUF and rigid polyisocyanurate-polyurethane foam were examined, since these foams are known for their higher stability from a thermodanymic point of view. As a flame retardant active in the gas phase, triethylphosphate was used. Using a multi-methodological approach, the complex interaction of fire phenomena was studied in detail. Cone calorimeter measurements provide insight into fire behaviour under forced-flaming conditions. They were carried out in an horizontal and a vertical orientation to account for the effects of melt flow and dripping. Sample-holders were equipped with glass windows to monitor the materials’ response to forced-flaming conditions with a video camera. Thermocouples were inserted into the specimens, giving information about the temperature gradient in the inside of the sample and the temperature of the pyrolysis zone during combustion. Changes in the morphology and thickness of the pyrolysis zone were examined using a hot-stage microscope, as well as SEM images of cross-sections of quenched foam specimens. The determination of the Oxygen Index and the use of thermogravimetry measurements rounded out the investigation. T2 - FRPM 2017, 16th European Meeting on Fire Retardant Polymeric Materials CY - Manchester, UK DA - 03.07.2017 KW - Foam KW - Polyurethane KW - Polyisocyanurate PY - 2017 AN - OPUS4-40950 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günther, Martin A1 - Lorenzetti, Alessandra A1 - Schartel, Bernhard T1 - Investigating the fire phenomena of rigid polyurethane foams N2 - This work investigates the fire phenomena of rigid polyurethane foams (RPUF) in detail. Rigid polyurethane foams (RPUF) are widely used in industry and daily life because of their outstanding mechanical and thermal insulating properties. In case of fire, cellular polymers like RPUF behave differently from bulk materials, the reason for this is their low thermal inertia. The aim of this study is to investigate the fire phenomena of RPUF in detail. Characterized by simultaneous physical and chemical processes which interact, depend, and compete with each other, the combustion of RPUF is a highly complex occurrence. Therefore it is necessary to study all aspects in detail. The fire phenomena that were examined are gasification, liquefaction, charring and structural integrity as well as collapse. The comprehensive understanding of the processes taking place during combustion is the foundation of customized development of successful flame retardant approaches. Advanced cone calorimeter investigations provide insight into the fire behavior under forced flaming conditions. Thermocouples in the inside of specimens give information about the temperature gradient and temperature of the pyrolysis zone during combustion. Changes in the morphology and thickness of the pyrolysis zone were examined using a hot-stage microscope, as well as SEM images of cross-sections of quenched foam specimens. Furthermore, fire phenomena were characterized using LOI and thermal analysis. By using a multimethodological approach and systematically varied sets of Polyurethane and Polyisocyanurate foams, new insights into the burning of RPUF were won. The detailed knowledge of fire phenomena is essential for future development of tailored flame retardant strategies for RPUF. T2 - AMI Fire Retardants in Plastics 2019 CY - Pittsburgh, PA, USA DA - 02.04.2019 KW - Fire behavior KW - Rigid polyurethane foam PY - 2019 AN - OPUS4-47835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lenz, J. U. A1 - Pospiech, D. A1 - Komber, H. A1 - Korwitz, A. A1 - Kobsch, O. A1 - Paven, M. A1 - Albach, R. W. A1 - Günther, Martin A1 - Schartel, Bernhard T1 - Effective halogen-free flame-retardant additives for crosslinked rigid polyisocyanurate foams: Comparison of chemical structures N2 - The impact of phosphorus-containing flame retardants (FR) on rigid polyisocyanurate (PIR) foams is studied by systematic variation of the chemical structure of the FR, including non-NCO-reactive and NCO-reactive dibenzo[d,f][1,3,2]dioxaphosphepine 6-oxide (BPPO)- and 9,10 dihydro-9-oxa-10 phosphaphenanthrene-10-oxide (DOPO)-containing compounds, among them a number of compounds not reported so far. These PIR foams are compared with PIR foams without FR and with standard FRs with respect to foam properties, thermal decomposition, and fire behavior. Although BPPO and DOPO differ by just one oxygen atom, the impact on the FR properties is very significant: when the FR is a filler or a dangling (dead) end in the PIR polymer network, DOPO is more effective than BPPO. When the FR is a subunit of a diol and it is fully incorporated in the PIR network, BPPO delivers superior results. KW - Flame retardant; KW - Dibenzo[d,f][1,3,2]dioxaphosphepine 6-oxide; BPPO KW - 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide; DOPO KW - Polyisocyanurate; PIR KW - Rigid foam KW - Cone calorimeter KW - Pudovik reaction PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-567712 SN - 1996-1944 VL - 16 IS - 1 SP - 1 EP - 22 PB - MDPI CY - Basel AN - OPUS4-56771 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -