TY - JOUR A1 - Häusler, Ines A1 - Darvishi Kamachali, Reza A1 - Hetaba, W. A1 - Skrotzki, Birgit T1 - Thickening of T-1 Precipitates during Aging of a High Purity Al–4Cu–1Li–0.25Mn Alloy N2 - The age hardening response of a high-purity Al–4Cu–1Li–0.25Mn alloy (wt. %) during isothermal aging without and with an applied external load was investigated. Plate shaped nanometer size T1 (Al2CuLi) and θ′ (Al2Cu) hardening phases were formed. The precipitates were analyzed with respect to the development of their structure, size, number density, volume fraction and associated transformation strains by conducting transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM) studies in combination with geometrical Phase analysis (GPA). Special attention was paid to the thickening of T1 phase. Two elementary types of single-layer T1 precipitate, one with a Li-rich (Type 1) and another with an Al-rich (Defect Type 1) central layer, were identified. The results show that the Defect Type 1 structure can act as a precursor for the Type 1 structure. The thickening of T1 precipitates occurs by alternative stacking of These two elementary structures. The thickening mechanism was analyzed based on the magnitude of strain associated with the precipitation transformation normal to its habit plane. Long-term aging and aging under load resulted in thicker and structurally defected T1 precipitates. Several types of defected precipitates were characterized and discussed. For θ′ precipitates, a ledge mechanism of thickening was observed. Compared to the normal aging, an external load applied to the peak aged state leads to small variations in the average sizes and volume fractions of the precipitates. KW - Al-Cu-Li-alloy KW - Precipitation KW - T1 precipitate KW - Microstructure evolution KW - Thickening KW - Creep KW - Volume fraction KW - Number density KW - Strain difference PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-471207 DO - https://doi.org/10.3390/ma12010030 SN - 1996-1944 VL - 12 IS - 1 SP - 30, 1 EP - 23 PB - MDPI AN - OPUS4-47120 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ikeda, Yuki A1 - Wallis, Theophilus A1 - Maaß, Robert A1 - Darvishi Kamachali, Reza T1 - Thermodynamics of grain boundary segregation transition and their relevance for liquid metal embrittlement in Fe-Zn system N2 - Grain boundaries (GBs) are common sites of failure in polycrystalline materials. Recently, a massive Zn segregation transition at Fe GBs was discovered and shown to act as a potent precursor of liquid metal embrittlement (LME) in the Fe-Zn system (Kamachali et al., Scripta Materialia 238 (2024) 115758). In this study, we elaborate on how temperature, GB type and the chemo-structurally coupled phase decomposition at the GB impact this segregation transition. CALPHAD and atomistic simulation data were utilized as inputs to conduct quantitative density-based thermodynamic modeling and phase-field simulations across various GBs, alloy compositions, and temperatures. We reveal that once the segregation transition becomes possible, the GB structural variation stabilizes spinodally formed Zn-rich phases within the GB region, with a higher tendency in disordered GBs. GB phase diagrams were constructed to identify and analyze the range of critical temperatures and alloy compositions associated with the segregation transition. The phase diagrams reveal that the miscibility gap for more disordered GB expands and, although the segregation transition is inevitable and occurs for all GBs, the barrier to triggering it is lower for more disordered GBs. Based on our thermodynamic analyses, potential processing modifications and GB engineering strategies for mitigating segregation-induced LME are thoroughly discussed. KW - Thermodynamics KW - Phase-Field Modelling KW - Steels PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-634145 DO - https://doi.org/10.1016/j.actamat.2025.121134 SN - 1359-6454 VL - 296 SP - 1 EP - 11 PB - Elsevier BV AN - OPUS4-63414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ferrari, Bruno A1 - Fantin, Andrea A1 - Said, D. A1 - Fitch, A. N. A1 - Suárez Ocano, Patricia A1 - Mishurova, Tatiana A1 - Roveda, Ilaria A1 - Kromm, Arne A1 - Darvishi Kamachali, Reza A1 - Bruno, Giovanni A1 - Evans, Alexander A1 - Requena, G. A1 - Agudo Jácome, Leonardo A1 - Serrano Munoz, Itziar T1 - The impact of scanning strategy on cell structures in PBF-LB/M/IN718: an in situ synchrotron x-ray diffraction study N2 - In additive manufacturing, any change of the process parameters, such as scanning strategy, directly affects the cooling rates, heat accumulation, and overall thermal history of the build. Consequently, parts built with different process parameters tend to have different levels of crystallographic texture, residual stress, and dislocation density. These features can influence the properties of the material and their development during post-processing operations. In this study, IN718 prisms were built by laser powder bed fusion (PBF-LB/M) using two different scanning strategies (continuous 67° rotations around the build direction, ROT, and alternating 0°/67° scans, ALT) to provide two different as-built conditions. In situ time-resolved synchrotron diffraction was performed during a solution heat treatment at 1027 °C for 1 h. Ex situ scanning electron microscopy was used to support and complement the in situ observations. An approach to quantify the effect of elemental microsegregation at the cell walls is developed based on the deconvolution of asymmetric γ-nickel matrix peaks. Following this approach, the scanning strategies are shown to affect the as-built fraction of cell walls in the material, resulting in a difference of approximately 5 %, in weight fraction, between ROT and ALT (19 % vs. 24 %, respectively). This microsegregation was observed to be rapidly homogenized during the heating ramp, and no significant changes to the peak shape in the γ peaks occurred during the isothermal part of the heat treatment, regardless of the scanning strategy. KW - Additive manufacturing KW - Inconel 718 KW - Synchrotron x-ray diffraction KW - Heat treatment KW - Laser powder bed fusion KW - Cellular microstructure PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-650958 DO - https://doi.org/10.1016/j.jmrt.2025.11.214 SN - 2238-7854 VL - 41 SP - 593 EP - 608 PB - Elsevier B.V. AN - OPUS4-65095 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Suárez Ocano, Patricia A1 - Fries, S. G. A1 - Lopez-Galilea, I. A1 - Darvishi Kamachali, Reza A1 - Roik, J. A1 - Agudo Jácome, Leonardo T1 - The AlMo0.5NbTa0.5TiZr refractory high entropy superalloy: Experimental findings and comparison with calculations using the CALPHAD method N2 - Detailed microstructural characterization of the AlMo0.5NbTa0.5TiZr refractory high entropy superalloy in the as-cast state is reported for first time and compared with the state annealed at 1400 oC for 24 h. The former shows a dendritic structure, with a mixture of A2/B2 phases < 20 nm in both the dendritic and interdendritic regions. A mostly amorphous phase, rich in Al and Zr, is found within the interdendritic region. The annealed state reproduced the combination of A2/B2/Al-Zr-rich phases reported previously. Calculations from two relevant ThermoCalc databases were compared with the experimental results. Equilibrium calculations were compared with results for the annealed alloy, whereas solidification paths calculated using Scheil-Gulliver model were used for comparison with the as-cast alloy. A previously hypothesized spinodal decomposition during cooling as the mechanism responsible for the patterned A2/B2 microstructure is confirmed via the CALPHAD calculations, pointing to its use as an efficient design tool for such alloys. Finally, the comparison between the experimental and computational findings allowed better understanding the solidification path and equilibrium stability of this alloy, giving a base to make better decisions on the field of new refractory superalloy design. KW - CALPHAD database analysis KW - Refractory superalloys KW - Chemically complex alloy KW - Characterization KW - Microstructure PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545906 DO - https://doi.org/10.1016/j.matdes.2022.110593 SN - 1873-4197 VL - 217 SP - 1 EP - 13 PB - Elsevier CY - Amsterdam AN - OPUS4-54590 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Jentzsch, Stefan A1 - Stock, Daniel A1 - Häcker, Ralf A1 - Skrotzki, Birgit A1 - Darvishi Kamachali, Reza A1 - Klingbeil, Dietmar A1 - Kindrachuk, Vitaliy T1 - Split Hopkinson Pressure Bar (SHPB) investigations of steel S355 specimens and complementary characterization methods N2 - The workbook SHPB_S355.xlsx contains in the main spreadsheet S355_TestOverview an overview on the S355 specimens, which were tested in Split Hopkinson Pressure Bar (SHPB) and complementary quasi-static (QS) tests. The tests were conducted with notched hat-shaped specimens without a notch offset (S355_TestOverview/column geometry: “no offset”) and a small notch offset of x=0.35 mm (S355_TestOverview/column geometry: “offset”), cf. Fig. 1 [1]. Furthermore, for selected specimens, links are provided to DIC and bar strain measurement files as well as to evaluations from further characterization methods (microhardness, EBSD). For the boundary conditions at the SHPB projectile impact, the pressures of the compressor p, driving the projectile, and the associated projectile impact velocities are provided in SHPB_S355.xlsx. The DIC displacement measurements are provided in FurtherMeasurements/DIC with frame output times in the file labels, which are associated with an imaginary trigger at the left end of the shortened incident bar (length 300 mm), which is considered within the SHPB simulation setup, see [1]. Furthermore, the DIC reference coordinate systems are provided as COS.jpg files in the respective DIC folders. Starting from the strain signals at the bars, captured by strain gauges at the incident (file name BC_Inc) and transmission bar (BC_Trans), displacement boundary conditions (which are provided for the tests in FurtherMeasurements/BarDisplBCs) are calculated by eq. (12) in [1], incorporating the acoustic velocity equal to 4639 m/s at the bars and a correction factor. Fig. 1 shows the shear specimen geometry (lengths in mm) with the offset of the notches x. For the quasi-static tests force(displacements)-values are directly provided in FurtherMeasurements/Fu_curves, which are considered from the relative displacements of the specimens, evaluated by DIC. The Vickers microhardness (HV 0.01) distribution across the shear localization zone was assessed by QNESS 60A+ EVO (DIN EN ISO 6507-1) for quasi-statically and dynamically tested specimens, applying the small notch offset, such that the specimens did not fail in the localization region. Therefore, raw data is provided in FurtherMeasurements/Microhardness. For fitting the microhardness distribution perpendicularly to the shear bands (as i.e. provided for the SHPB specimen in [1]), representative microhardness profiles were considered. Similarly for specimens with the small notch offset, EBSD data on dynamic and quasi-static tests is provided in FurtherMeasurements/EBSD. The grain size distributions for positions at the notch and the undeformed region are included in the subdirectory ./GrainLists_Shortened and EBSD images in the PowerPoint Presentations. Further information as the sizes and misorientations of the single grains, is incorporated in the subfolders ./GrainLists_FurtherInf. KW - Adiabatic shear bands KW - Split Hopkinson pressure bar KW - Digital image correlation PY - 2025 DO - https://doi.org/10.5281/zenodo.17591439 PB - Zenodo CY - Geneva AN - OPUS4-64842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhou, X. A1 - Darvishi Kamachali, Reza A1 - Boyce, B.L. A1 - Clark, B.G. A1 - Raabe, D. A1 - Thompson, G.B. T1 - Spinodal Decomposition in Nanocrystalline Alloys N2 - For more than half a century, spinodal decomposition has been a key phenomenon in considering the formation of secondary phases in alloys. The most prominent aspect of the spinodal phenomenon is the lack of an energy barrier on its transformation pathway, offering an alternative to the nucleation and growth mechanism. The classical description of spinodal decomposition often neglects the influence of defects, such as grain boundaries, on the transformation because the innate ability for like-atoms to cluster is assumed to lead the process. Nevertheless, in nanocrystalline alloys, with a high population of grain boundaries with diverse characters, the structurally heterogeneous landscape can greatly influence the chemical decomposition behavior. Combining atom-probe tomography, precession electron diffraction and density-based phase-field simulations, we address how grain boundaries contribute to the temporal evolution of chemical decomposition within the miscibility gap of a Pt-Au nanocrystalline system. We found that grain boundaries can actually have their own miscibility gaps profoundly altering the spinodal decomposition in nanocrystalline alloys. A complex realm of multiple interfacial states, ranging from competitive grain boundary segregation to barrier-free low-dimensional interfacial decomposition, occurs with a dependency upon the grain boundary character. KW - Density-based Thermodynamics KW - Nanocrystalline alloys KW - Spinodal decomposition KW - Defects engineering PY - 2021 DO - https://doi.org/10.1016/j.actamat.2021.117054 VL - 215 SP - 117054 PB - Elsevier Ltd. AN - OPUS4-52918 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ta, N. A1 - Bilal, M. U. A1 - Häusler, I. A1 - Saxena, A. A1 - Lin, Y.-Y. A1 - Schleifer, F. A1 - Fleck, M. A1 - Glatzel, U. A1 - Skrotzki, Birgit A1 - Darvishi Kamachali, Reza T1 - Simulation of the θ′ Precipitation Process with Interfacial Anisotropy Effects in Al-Cu Alloys N2 - The effects of anisotropic interfacial properties and heterogeneous elasticity on the growth and ripening of plate-like θ′-phase (Al2Cu) in Al-1.69 at.% Cu alloy are studied. Multi-phase-field simulations are conducted and discussed in comparison with aging experiments. The precipitate/matrix interface is considered to be anisotropic in terms of its energy and mobility. We find that the additional incorporation of an anisotropic interfacial mobility in conjunction with the elastic anisotropy result in substantially larger aspect ratios of the precipitates closer to the experimental observations. The anisotropy of the interfacial energy shows comparably small effect on the precipitate’s aspect ratio but changes the interface’s shape at the rim. The effect of the chemo-mechanical coupling, i.e., the composition dependence of the elastic constants, is studied as well. We show that the inverse ripening phenomenon, recently evidenced for δ’ precipitates in Al-Li alloys (Park et al. Sci. Rep. 2019, 9, 3981), does not establish for the θ′ precipitates. This is because of the anisotropic stress fields built around the θ′ precipitates, stemming from the precipitate’s shape and the interaction among different variants of the θ′ precipitate, that disturb the chemo-mechanical effects. These results show that the chemo-mechanical effects on the precipitation ripening strongly depend on the degree of sphericity and elastic isotropy of the precipitate and matrix phases. KW - Aging KW - Phase-field simulation KW - Interfacial anisotropy KW - Chemo-mechanical coupling KW - Precipitation KW - Elasticity KW - θ′-(Al2Cu) precipitate phase PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522672 DO - https://doi.org/10.3390/ma14051280 VL - 14 IS - 5 SP - 1280 PB - MDPI AN - OPUS4-52267 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jentzsch, Stefan A1 - Stock, Daniel A1 - Häcker, Ralf A1 - Skrotzki, Birgit A1 - Darvishi Kamachali, Reza A1 - Klingbeil, Dietmar A1 - Kindrachuk, Vitaliy T1 - Shear Band Formation with Split Hopkinson Bar Experiments N2 - The essence of dynamic failure is closely linked to dramatic shear deformations which often lead to the formation of adiabatic shear bands (ASB). Under high loading velocities and the subsequent rapid temperature increase, the localization of shear strain is crucial in view of safety issues of systems in mechanical and aircraft engineering, especially with respect to fast rotating components and diverse crash scenarios. In this research, we perform high speed impact tests at the split Hopkinson pressure bar (SHPB) setup and use particular hat-shaped specimen geometries that resemble the stresses and failure conditions at the component level. In the first step, we specify a notched specimen geometry using finite element (FE) simulations to ensure pure shear. Further, quasi-static compressive tests and a series of impact tests at high strain rates of 10^3-10^4 s^-1 are conducted on specimens manufactured from a fine-grain structural steel with the properties of S355. Optical microscopy and electron backscatter diffraction (EBSD) of the sheared zones unveil significant localization to maximal shear strains of about 0.9 accompanied by grain refinement by factors 5 to 14. The displacements across the surface of the specimens are captured with subset-based local digital image correlation (DIC) during the impact time, and serve as an objective to validate a viscoplastic constitutive relationship. More precisely, the deformation distribution is accurately reproduced by the widely recognized Johnson-Cook (JC) model, which features an enhanced description of damage evolution. Thus, combining experimental and characterization techniques, continuum mechanics and reasonable optimization strategies for the identification of model parameters provides an efficient approach for comprehensive insights into the strain localization behaviour and its impact on the mechanical performance of S355 under extreme strain rates and deformations. KW - Adiabatic shear bands KW - Finite element analysis KW - Viscoplastic material modelling KW - Split Hopkinson pressure bar KW - Hat-shaped specimen KW - Johnson–Cook parameter identification PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613339 DO - https://doi.org/10.1016/j.ijmecsci.2024.109749 VL - 284 SP - 1 EP - 14 PB - Elsevier BV AN - OPUS4-61333 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ikeda, Yuki A1 - Ni, H.C. A1 - Chakraborty, A. A1 - Ghassemi-Armaki, H. A1 - Zuo, J.M. A1 - Darvishi Kamachali, Reza A1 - Maaß, Robert T1 - Segregation-induced grain-boundary precipitation during early stages of liquid-metal embrittlement of an advanced high-strength steel N2 - Liquid-metal embrittlement (LME) of galvanized (Zn-coated) advanced high-strength steels is a long-known problem in materials science. Here we reveal the initial microstructural processes underneath the Zn-coating that lead to LME-microcrack initiation in the steel substrate. We track the microstructural evolution during the first tens of milliseconds and find pronounced signatures of Fe-Zn intermetallic precipitation in both ferrite grain boundaries and at internal ferrite-oxide phase boundaries. In concert with novel CALPHAD-integrated density-based thermodynamic modelling, we demonstrate that Zn-rich intermetallic phase-nucleation can occur at markedly low processing temperatures due to a segregation transition. We show that a small Znenrichment caused by Zn bulk-diffusion during the initial temperature rise in a joining process is sufficient to induce the segregation transition and subsequent nucleation of Fe-Zn intermetallic grain-boundary phases, which the experiments link to crack initiation sites. These findings direct focus onto LME-controlling microstructural and thermodynamic phenomena at temperatures below the ductility trough and the austenite formation temperature. KW - Resistance spot welding KW - Liquid-metal embrittlement KW - Steels KW - Grain boundaries PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-581067 DO - https://doi.org/10.1016/j.actamat.2023.119243 VL - 259 SP - 1 EP - 12 PB - Elsevier Ltd AN - OPUS4-58106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Darvishi Kamachali, Reza A1 - da Silva, A. A1 - McEniry, E. A1 - Gault, B. A1 - Neugebauer, J. A1 - Raabe, D. T1 - Segregation-assisted spinodal and transient spinodal phase separation at grain boundaries N2 - Segregation to grain boundaries affects their cohesion, corrosion, and embrittlement and plays a critical role in heterogeneous nucleation. In order to quantitatively study segregation and low-dimensional phase separation at grain boundaries, here, we apply a density-based phase-field model. The current model describes the grain-boundary thermodynamic properties based on available bulk thermodynamic data, while the grain-boundary-density profile is obtained using atomistic simulations. To benchmark the performance of the model, Mn grain-boundary segregation in the Fe–Mn system is studied. 3D simulation results are compared against atom probe tomography measurements conducted for three alloy compositions. We show that a continuous increase in the alloy composition results in a discontinuous jump in the segregation isotherm. The jump corresponds to a spinodal Phase separation at grain boundary. For alloy compositions above the jump, we reveal an interfacial transient spinodal phase separation. The transient spinodal phenomenon opens opportunities for knowledge-based microstructure design through the chemical manipulation of grain boundaries. The proposed density-based model provides a powerful tool to study thermodynamics and kinetics of segregation and phase changes at grain boundaries. KW - Grain Boundary Spinodal KW - Densty-based Thermodynamics KW - Microstrucrue Design PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519497 DO - https://doi.org/10.1038/s41524-020-00456-7 VL - 6 IS - 1 SP - 191 PB - Nature AN - OPUS4-51949 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -