TY - CONF A1 - Genga, R. M. A1 - Cornish, L. A. A1 - Woydt, Mathias A1 - van Vuuren, J. A1 - Polese, C. T1 - NbC: A machining alternative for dry and MQL face-milling of grey cast rion (GCI) N2 - NbC was studied as the major carbide phase with Ni and Co binders, produced by both spark plasma sintering (SPS) and liquid phase sintering (LPS), and tested as cutting inserts during dry and MQL (Minimum quantity lubrication) face-milling of grey cast iron (GCI) (BS 1452, Grade 17). T2 - World PM2016 CY - Hamburg, Germany DA - 09.10.2016 KW - Niobium carbide KW - NbC KW - Machining KW - Spark plasma sintering (SPS) KW - Liquid phase sintering (LPS) PY - 2016 SN - ISBN 978-1-899072-47-7 SP - 1 EP - 6 AN - OPUS4-37889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genga, R. A1 - Cornish, L. A1 - Woydt, Mathias A1 - van Vuuren, A. J. A1 - Polese, C. T1 - Face-milling of grey cast iron (BS 1452) using WC-based and NbC-based cutting tools N2 - NbC was studied as the major carbide phase with Ni and Co binders, produced by both spark plasma sintering (SPS) and liquid phase sintering (LPS), and tested as cutting inserts during dry and MQL (Minimum quantity lubrication) face-milling of gey cast iron (GCI) (BS 1452, Grade 17). T2 - 10th Tool Conference 2016 - TOOL 2016 CY - Bratislava, Slovakia DA - 04.10.2016 KW - NbC KW - Spark plasma sintering KW - Ni KW - Mechanical properties KW - Flank wear KW - Chemical stability PY - 2016 SN - ISBN 978-3-200-04786-0 SP - 336 EP - 342 AN - OPUS4-37869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genga, R. M. A1 - Cornish, L. A. A1 - Woydt, Mathias A1 - Sobiyi, K. A1 - Polese, C. T1 - Wear and Mechanical properties of spark plasma and liquid phase sintered WC and NbC based cemented carbide inserts N2 - The effects on the mechanical properties, thermal behavior, response to cutting forces and wear mechanisms have been investigated for different manufacturing processes and materials for cemented carbide inserts. T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - WC KW - NbC KW - SPS KW - Co KW - Fe3Al KW - Hard-turning KW - Interrupted milling KW - Flank KW - Wear KW - Coolant-free KW - Crater wear KW - Machinability PY - 2018 SN - 978-0-692-05382-9 SP - 547 EP - 567 AN - OPUS4-44208 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Genga, R. M. A1 - Cornish, L. A. A1 - Woydt, Mathias A1 - Janse van Vuuren, A. A1 - Polese, C. T1 - Microstructure, mechanical and machining properties of LPS and SPS NbC cemented carbides for face-milling of grey cast iron N2 - The effects of spark plasma sintering (SPS), NbC as a major carbide phase and Ni as a Co binder substitute on the microstructure, mechanical properties and cutting insert wear during face-milling of grey cast iron (GCI) BS1452, grade 17, were investigated. KW - Niobium carbide KW - NbC KW - Hardness KW - Wear PY - 2018 U6 - https://doi.org/10.1016/j.ijrmhm.2017.12.036 SN - 0263-4368 VL - 73 SP - 111 EP - 120 PB - Elsevier Ltd. AN - OPUS4-44083 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Genga, R. M. A1 - Rokebrand, P. A1 - Cornish, L. A. A1 - Nelwalani, N. A1 - Brandt, Guido A1 - Kelling, Norbert A1 - Woydt, Mathias A1 - Janse van Vuuren, A. A1 - Polese, C. T1 - High-temperature sliding wear, elastic modulus and transverse rupture strength of Ni bonded NbC and WC cermets N2 - The effects of rapid pulse electric current sintering (PECS), substitution of WC by NbC and Co by Ni, and carbide additives (TiC and Mo2C) on the microstructure, elastic modulus, B3B transverse rupture strength (TRS) and high temperature sliding wear on WC-Co, WC-Ni, NbC-Co and NbC-Ni cermets were studied. High temperature sliding wear tests were carried out using a ball-on-disk tribometer, with a 10 N force, at a sliding speed of 1.34 m/s for 0.8 km (10 min) and 2.4 km (30 min), using 100Cr6 (AISI 52100) steel balls at 400 °C and 0% humidity. Additions of TiC and Mo2C to NbC-12Ni improved the sliding wear resistance, with TiC having the greater effect, reducing the sample wear rate by over 30% from 15.1×10−6mm3/N·m to 9.4×10−6mm3/N·m after sliding distance of 2.4 km. Generally, the LPS samples had lower wear volumes than the corresponding SPS samples, due to higher K1c and TRS. KW - Pulse electric current sintering KW - Niobium carbide KW - Nickel KW - Molybdenum carbide KW - Titanium carbide PY - 2020 U6 - https://doi.org/10.1016/j.ijrmhm.2019.105143 SN - 0263-4368 VL - 87 SP - 105143 PB - Elsevier Ltd. AN - OPUS4-51473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Genga, R. M. A1 - Cornish, L. A. A1 - Polese, C. A1 - Woydt, Mathias A1 - Janse van Vuuren, A. T1 - Wear investigation of NbC inserts during face-milling of grey cast iron N2 - Tungsten carbide (WC) based cemented carbides have a good combination of hardness, strength and toughness, making them key materials for cutting tool industry. T2 - The 54th Annual Conference CY - Port Elizabeth, South Africa DA - 05.12.2016 KW - Tungsten carbide (WC) KW - Niobium carbide (NbC) KW - Wear KW - Machining PY - 2016 SN - 978-0-620-73767-8 SN - 0250-0418 SP - 1 AN - OPUS4-39388 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -