TY - JOUR A1 - Grehn, M. A1 - Seuthe, T. A1 - Reinhardt, F. A1 - Höfner, M. A1 - Griga, N. A1 - Eberstein, M. A1 - Bonse, Jörn T1 - Debris of potassium-magnesium silicate glass generated by femtosecond laser-induced ablation in air: An analysis by near edge X-ray absorption spectroscopy, micro Raman and energy dispersive X-ray spectroscopy N2 - The redeposited material (debris) resulting from ablation of a potassium–magnesium silicate glass upon scanning femtosecond laser pulse irradiation (130 fs, 800 nm) in air environment is investigated by means of three complementary surface analytical methods. Changes in the electronic band structure of the glass constituent Magnesium (Mg) were identified by X-ray Absorption Near Edge Structure spectroscopy (XANES) using synchrotron radiation. An up-shift of ≈0.8 eV of a specific Magnesium Κ-edge absorption peak in the spectrum of the redeposited material along with a significant change in its leading edge position was detected. In contrast, the surface left after laser ablation exhibits a downshift of the peak position by ≈0.9 eV. Both observations may be related to a change of the Mg coordinative state of the laser modified/redeposited glass material. The presence of carbon in the debris is revealed by micro Raman spectroscopy (µ-RS) and was confirmed by energy dispersive X-ray spectroscopy (EDX). These observations are attributed to structural changes and chemical reactions taking place during the ablation process. KW - Femtosecond laser ablation KW - Potassium-magnesium silicate glass KW - Debris KW - XANES KW - EDX KW - Raman spectroscopy PY - 2014 U6 - https://doi.org/10.1016/j.apsusc.2013.10.028 SN - 0169-4332 SN - 1873-5584 VL - 302 SP - 286 EP - 290 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-30454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grehn, M. A1 - Seuthe, T. A1 - Höfner, M. A1 - Griga, N. A1 - Theiss, C. A1 - Mermillod-Blondin, A. A1 - Eberstein, Markus A1 - Eichler, H. A1 - Bonse, Jörn T1 - Femtosecond-laser induced ablation of silicate glasses and the intrinsic dissociation energy N2 - The relation between ablation threshold fluence upon femtosecond laser pulse irradiation and the average dissociation energy density of silicate based multicomponent glass is studied. A simple model based on multiphoton absorption quantifies the absorbed energy density at the ablation threshold fluence. This energy density is compared to a calculated energy density which is necessary to decompose the glass compound into its atomic constituents. The results confirm that this energy density is a crucial intrinsic material parameter for the description of the femtosecond laser ablation threshold fluence of dielectrics. PY - 2014 U6 - https://doi.org/10.1364/OME.4.000689 SN - 2159-3930 VL - 4 IS - 4 SP - 689 EP - 700 PB - OSA CY - Washington, DC AN - OPUS4-30475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -