TY - CONF A1 - Blaeß, Carsten A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Groh, D. A1 - Döhler, F. A1 - Brauer, D. S. T1 - Sintering and crystallization of new bioactive glasses N2 - Bioglass® 45S5 is mainly used clinically as powders, granules or pastes instead of sintered compacts. This is due to the inherent problem of crystallization during the sintering, which results in poor mechanical properties and reduced bioactivity. Recently, new bioactive glasses with improved crystallization stability have been developed as promising candidates for manufacturing of sintered powder compacts for bone regeneration, which combine improved sintering behavior with bioactivity. Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkali oxide ratio was increased, sodium oxide was partially replaced by potassium oxide and up to 3 mol% calcium fluoride were added, in order to stabilize the glass against crystallization. The aim of this study was to investigate the sintering and crystallization behavior of these new bioactive glasses. Sintering and crystallization were characterized by heating microscopy, XRD, FTIR, SEM, and DTA. The results show that a sintered density of 88-99 % is achieved in contrast to only 57-67% for Bioglass® 45S5. In addition, FTIR and XRD analyses show that Bioglass® 45S5 crystallized during sintering while for the new glasses no crystalline phases are detected. The thermal properties of all glasses were studied by DTA measurements, and the influence of grain size was characterized. These studies showed that full densification can be attained for particle size < 32 µm, whereas coarser particles progressively increase residual porosity. Observed foaming phenomena, are strongly retarded by crystallization of beta-HAp. T2 - ICG 2016 CY - Shanghai, China DA - 07.04.2016 KW - Bioactive KW - Glass KW - Crystallization KW - Sintering PY - 2015 AN - OPUS4-38304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blaeß, Carsten A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Groh, D. A1 - Döhler, F. A1 - Brauer, D. S. T1 - New bioactive glasses with improved sintering behavior N2 - Nowadays, the use of bioactive glasses is established for bone regeneration; however glasses are used mostly as powders, granules or in a paste. Sintered scaffolds are not used clinically, because of the in inherent problem of crystallization during the sintering process, resulting in poor mechanical properties and reduced bioactivity. The aim of this study was therefore to design new bioactive glasses, which combine improved processing and sintering with bioactivity. Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkalioxide ratio was increased, sodiumoxide was partially replaced by potassiumoxide and up to 8 mol% calciumflorid were added, in order to stabilize the glass against crystallization. The sintering behavior of the new glasses was characterized by heating microscopy and compared to Bioglass® 45S5. The results showed that the new glasses achieved a sintered density of 88-99 % in contrast to only 57-67% for Bioglass® 45S5. In addition FTIR and XRD analyses showed that Bioglass® 45S5 crystallized during sintering while for the new glasses no crystalline phases were detected. The thermal properties of all glasses were studied by DTA and DSC measures, and the influence of grain size and heating rate were characterized. These studies showed a shift of start and end temperature of sintering process as well as the final density. The structure of sintered specimens during and after sintering was examined using light and electron microscopy (REM). T2 - Crystallization 2015 CY - Nagaoka, Japan DA - 11.10.2015 KW - Bioactive KW - Glass KW - Crystallization KW - Sintering PY - 2015 AN - OPUS4-38308 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blaeß, Carsten A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Agea Blanco, Boris A1 - Brauer, D. S. T1 - Blähen, Mechanismus, Ursachen und Vermeidung N2 - Phänominilogische Studien des Blähens von bioactiven Gläsern verschiedener Zusammensetzung und Unteruschung des Einflusses einer Kristallisation. Die ausgasenden Komponenten wurden mittels Vakuumheißextraktion(VHE) und Infrarotspektroskopie identifiziert sowie der Einfluss von Korngröße, Mahldauer und -atmosphäre auf das Blähen unterucht. T2 - Glashüttentag 2015 CY - Freiberg, Germany DA - 29.09.2015 KW - Blähen KW - Glas KW - Bioaktiv KW - Kristallisation PY - 2015 AN - OPUS4-38309 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blaeß, Carsten T1 - Blähen: Mechanismus, Ursachen und Vermeidung T2 - 4. Glashüttentag der Jungen DGG CY - Freiberg, Deutschland DA - 2015-09-20 PY - 2015 AN - OPUS4-35201 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blaeß, Carsten A1 - Müller, Ralf A1 - Reinsch, Stefan A1 - Groh, D. A1 - Döhler, F. A1 - Brauer, D. S. T1 - New bioactive glasses with improved sintering behavior T2 - Crystallization 2015 CY - Nagaoka, Japan DA - 2015-10-11 PY - 2015 AN - OPUS4-35202 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -