TY - GEN A1 - Carraba, L. A1 - Gluth, Gregor A1 - Pirskawetz, Stephan A1 - Krüger, Simone A1 - Bignozzi, M.C. ED - Falikman, V. ED - Realfonzo, R. ED - Coppola, L. ED - Hajek, P. ED - Riva, R. T1 - Fly ash-based lightweight geopolymer mortars for fire protection T2 - Durability and Sustainability of Concrete Structures (DSCS-2018). ACI Special Publication, Vol. 326 N2 - The present study aims to investigate the use of geopolymer mortars as passive fire protection system for steel structures. Coal fly ashes were used as aluminosilicate source and perlite was employed as aggregate to obtain a lightweight system. In addition, a geopolymer mortar containing quartz aggregate was produced for comparison. The geopolymer mortars were applied on stainless steel plates and exposed to both, cellulosic and hydrocarbon standard fire curves, according to ISO 834-1 and EN 1363-2, respectively. Acoustic emission measurements were conducted to analyze cracking phenomena during the high temperature exposure. The resulting temperature-time curves showed that the investigated system is effective in retarding the temperature rise of the steel plates. When the cellulosic fire curve was applied, a 20 mm [0.79 in.] thick layer of lightweight geopolymer mortar protected the steel substrate from reaching the critical temperature of 500 °C [932 °F] for at least 30 minutes, avoiding the rapid decrease of its mechanical properties and thus representing an important safety measure against accidental fires. No spalling phenomena on heating were detected; however, significant cracking was observed on cooling. KW - Alkali-activated materials KW - Geopolymers KW - Fire protection KW - Fire proofing KW - Acoustic emission PY - 2018 SN - 978-1-64195-022-0 VL - 326 SP - 26.1 EP - 26.10 PB - American Concrete Institute CY - Farmington Hills AN - OPUS4-46154 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Carabba, L. A1 - Pirskawetz, Stephan A1 - Krüger, Simone A1 - Gluth, Gregor A1 - Bignozzi, M.C. T1 - Acoustic emission study of heat-induced cracking in fly ash-based alkali-activated pastes and lightweight mortars JF - Cement and Concrete Composites N2 - Alkali-activated fly ashes have been proposed for various applications where resistance against high temperatures is required, yet several details regarding the response of these materials to heat-exposure need to be clarified. In the present study, heat-induced cracking in fly ash-based alkali-activated pastes and lightweight mortars was analyzed by in-situ acoustic emission (AE) detection during complete heating-cooling cycles (up to ∼1100 °C), augmented by thermogravimetry and ex-situ SEM and XRD analyses. The applicability of the lightweight mortars as passive fire protection coatings was assessed by recording temperature-time curves of mortar-coated steel plates. Cracking during heating was limited and associated exclusively with the dehydration of the materials in the temperature range ∼90–360 °C. However, samples heated to temperatures above ∼600 °C exhibited intense cracking on cooling. This was attributed to differential deformations caused by local sintering and partial melting at the glass transition temperature, and subsequent quenching on cooling. KW - Alkali-activated materials KW - Acoustic emission KW - Fire proofing KW - Heat resistance KW - Cracking PY - 2019 DO - https://doi.org/10.1016/j.cemconcomp.2019.04.013 SN - 0958-9465 SN - 1873-393X VL - 102 SP - 145 EP - 156 PB - Elsevier AN - OPUS4-47904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -