TY - JOUR A1 - Baláž, Matej A1 - Birinci, Mustafa A1 - Şentürk, Kader A1 - Achimovičová, Marcela A1 - Baláž, Peter A1 - Tampubolon, Imelda Octa A1 - Stolar, Tomislav A1 - Bienert, Ralf A1 - Emmerling, Franziska A1 - Erdemoğlu, Sema A1 - Sis, Hikmet A1 - Erdemoğlu, Murat T1 - Utilizing Taguchi method and in situ X-ray powder diffraction monitoring to determine the influence of mechanical activation conditions on the physico-chemical properties and Al leachability of K-feldspar N2 - K-feldspar represents an important natural resource of potassium and aluminum. Within the framework of this study, the K-feldspar was mechanically activated in a planetary ball mill under different conditions planned according to 43 Taguchi orthogonal array experimental design. As outputs, specific surface area (SBET), median particle size (d50), amorphization degree of mineral phases , and Al recovery were used. It was found that the initial d50 value of 293 μm could be reduced to 6.7 μm and the SBET value of 4.7 m2/g could be increased up to 32.5 m2/g upon milling. Both microcline KAl3SiO8, and albite NaAl3SiO8 could be almost completely amorphized, whereas quartz SiO2 still maintained some crystallinity even under the most intensive conditions. Increasing SBET and decreasing the d50 values did not lead to a significant improvement in Al leach recovery, whereas a clear relationship between the amorphization of microcline and the recovered aluminum was found. Analysis of Variance (ANOVA) showed that increasing ball-to-powder ratio is the most beneficial for the improvement in Al recovery. In situ powder X-ray diffraction monitoring performed in an oscillation ball mill under synchrotron irradiation has shown very rapid amorphization of microcline phase at the beginning. However, amorphization of microcline was only partial after two hours of the treatment in this mill, apart from almost complete process in the planetary ball mill. In the end, regressions for the calculation of Al recovery by knowing the values of input parameters were calculated. In general, by just using mechanical activation without the subsequent roasting process that is commonly used to boost metal recoveries, it was possible to quantitatively recover aluminum from K-feldspar. KW - Mechanochemistry KW - Mechanical activation KW - Design of experiments PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611059 DO - https://doi.org/10.1016/j.jmrt.2024.08.156 SN - 2238-7854 VL - 32 SP - 3886 EP - 3895 PB - Elsevier B.V. AN - OPUS4-61105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stawski, Tomasz A1 - Karafiludis, Stephanos A1 - Pimentel, Carlos A1 - Montes-Hernández, German A1 - Kochovski, Zdravko A1 - Bienert, Ralf A1 - Weimann, Karin A1 - Emmerling, Franziska A1 - Scoppola, Ernesto A1 - Van Driessche, Alexander E.S. T1 - Solution-driven processing of calcium sulfate: The mechanism of the reversible transformation of gypsum to bassanite in brines N2 - Here, we show that calcium sulfate dihydrate (gypsum) can be directly, rapidly and reversibly converted to calcium sulfate hemihydrate (bassanite) in high salinity solutions (brines). The optimum conditions for the efficient production of bassanite in a short time (<5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the better-known behaviour of the bassanite phase in low-salt environments. In low-salinity aqueous solutions, bassanite is considered to be metastable with respect to gypsum and anhydrite, and therefore gypsum-to-bassanite conversion does not occur in pure water. Interestingly, the high-salinity transformation of gypsum-to-bassanite has been reported by many authors and used in practice for several decades, although its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures was inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline phase for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios. KW - Industrial and Manufacturing Engineering KW - Strategy and Management KW - General Environmental Science KW - Renewable Energy, Sustainability and the Environment KW - Building and Construction KW - Calcium sulfate KW - Gypsum KW - Bassanite KW - Scattering KW - Raman KW - In situ KW - Synchrotron KW - BESSY KW - MySpot PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-594698 UR - https://www.sciencedirect.com/science/article/pii/S0959652624004591#appsec1 DO - https://doi.org/10.1016/j.jclepro.2024.141012 SN - 0959-6526 VL - 440 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-59469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -