TY - CONF A1 - Lay, Vera A1 - Baensch, Franziska A1 - Johann, Sergej A1 - Sturm, Patrick A1 - Mielentz, Frank A1 - Prabhakara, Prathik A1 - Hofmann, Detlef A1 - Niederleithinger, Ernst A1 - Kühne, Hans-Carsten T1 - SealWasteSafe: materials technology, monitoring techniques, and quality assurance for safe sealing structures in underground repositories N2 - Within the project SealWasteSafe, we advance construction materials and monitoring concepts of sealing structures applied for underground disposal of nuclear or toxic waste. As these engineered barriers have high demands concerning integrity, an innovative alkali-activated material (AAM) is improved and tested on various laboratory scales. This AAM has low reaction kinetics related to a preferential slow release of the heat of reaction in comparison to alternative salt concretes based on Portland cement or magnesium oxychloride cements. Hence, crack formation due to thermally induced strain is reduced. After successful laboratory scale analysis (Sturm et al., 2021), the AAM is characterised on a larger scale by manufacturing test specimens (100–300 L). Conventional salt concrete (DBE, 2004) and the newly developed AAM are compared using two specimen geometries, i.e. cylindrical and cuboid. A comprehensive multisensor monitoring scheme is developed to compare the setting process of AAM and salt concrete for these manufactured specimens. The analysed parameters include temperature and humidity of the material, acoustic emissions, and strain variations. Passive sensor systems based on radiofrequency identification technology (RFID) embedded in the concrete, enable wireless access to temperature and humidity measurements and are compared to conventional cabled systems. Additionally, fibre-optic sensors (FOS) are embedded to record strain, but also have potential to record temperature and moisture conditions. Part of this project aims at demonstrating the high reliability of sensors and also their resistance to highly alkaline environments and to water intrusion along cables or at sensor locations. Further technical improvements were implemented so that first results clearly show the scalability of the setting process from previous small-scale AAM experiments and particularly the high potential of the newly developed approaches. Furthermore, ultrasonic methods are used for quality assurance to detect obstacles, potential cracks and delamination. On the one hand, both active and passive ultrasonic measurements complement the results obtained from the multisensor monitoring scheme for the produced specimens. On the other hand, the unique large aperture ultrasonic system (LAUS) provides great depth penetration (up to nearly 10 m) and can thus be applied at in situ sealing structures built as a test site in Morsleben by the Federal Company for Radioactive Waste Disposal (Bundesgesellschaft für Endlagerung, BGE) as shown by Effner et al. (2021). An optimised field lay-out identified from forward modelling studies and advanced imaging techniques applied to the measured data will further improve the obtained results. To characterise the inside of the test engineered barrier and achieve a proof-of-concept, an ultrasonic borehole probe is developed to enable phased arrays that can further improve the detection of potential cracks. Modelling results and first analysis of semispherical specimens confirmed the reliability of the directional response caused by the phased arrays of the newly constructed ultrasonic borehole probe. Overall, the project SealWasteSafe improves the construction material, multisensor monitoring concepts and ultrasonics for quality assurance. This will help to develop safe sealing structures for nuclear waste disposal. The outcomes are particularly valuable for salt as a host rock but partly also transferrable to alternative conditions. T2 - Safe ND Interdisciplinary research symposium on the safety of nuclear disposal practices CY - Berlin, Germany DA - 10.11.2021 KW - Borehole probe KW - SealWasteSafe KW - Engineered barrier KW - Materials technology KW - Monitoring KW - AAM KW - Ultrasound PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-539172 DO - https://doi.org/10.5194/sand-1-127-2021 VL - 1 SP - 127 EP - 128 PB - Copernicus AN - OPUS4-53917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lay, Vera A1 - Baensch, Franziska A1 - Skłodowska, Anna A1 - Fritsch, Tobias A1 - Stamm, Michael A1 - Prabhakara, Prathik A1 - Johann, Sergej A1 - Sturm, Patrick A1 - Kühne, Hans-Carsten A1 - Niederleithinger, Ernst T1 - Multi–sensory Monitoring and Non–destructive Testing of New Materials for Concrete Engineered Barrier Systems N2 - The crucial part of nuclear waste storage is the construction of sealing structures made of reliable, safe and well–understood materials. We present an extended analysis of long-term multi–sensory monitoring and non–destructive testing (NDT) inspection of two laboratory specimens aiming at potential materials for sealing structures for nuclear waste repositories. Specimens with a volume of 340 litres made from newly developed alkali–activated materials (AAM) and established salt concrete (SC) were analysed using embedded acoustic emission and wireless radio-frequency identification (RFID) sensors, ultrasonic echo imaging, active thermography, and X–ray computed tomography. The monitoring analysis showed lower heat of reaction and 50% less acoustic emission events in AAM compared to SC. However, due to the surface effects of the AAM material, the number of acoustic emission events increased significantly after approximately two months of monitoring. Subsequently performed NDT inspections reliably located embedded sensors and confirmed the absence of major cracks or impurities. The presented laboratory results show the feasibility and potential of comprehensive NDT monitoring and inspection to characterise cementitious and alternative materials as well as the need for multi–parameter long–term monitoring. Thus, our study demonstrates that tailored NDT investigations will help to develop safe sealing structures for nuclear waste repositories. KW - Radioactive waste KW - Barrier KW - Concrete KW - AAM KW - Non-destructive testing PY - 2024 DO - https://doi.org/10.3151/jact.22.516 SN - 1347-3913 VL - 22 IS - 9 SP - 516 EP - 529 PB - Japan Concrete Institute AN - OPUS4-61461 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Skłodowska, Anna A1 - Baensch, Franziska A1 - Lay, Vera A1 - Niederleithinger, Ernst A1 - Kühne, Hans-Carsten T1 - Acoustic emission monitoring for engineered barriers in nuclear waste disposal N2 - To safely dispose of nuclear waste in underground facilities, engineered barrier systems are needed to seal shafts and galleries. The material used in these barriers must be adapted to the host rock parameters. Shrinking and cracking must be avoided to provide a barrier with almost zero permeability. For repositories in salt rock environments, several types of salt concrete (SC) are possible construction materials. Within the project SealWasteSafe, we compared the behavior of an innovative alkali-activated material (AAM) with standard SC in their hydration and hardening phase. To monitor the microstructural changes within the two materials SC and AAM, acoustic emission (AE) signals have been recorded for up to ~250 days on 340-litercubic specimens. The phenomenon of AE is defined as the emission of elastic waves in materials due to the release of localized internal energy. Such energy release can be caused by the nucleation of micro-fracture, e.g., in concrete while curing or when exposed to load. The occurrence of AE events gives first rough indications of microstructural changes and potentially occurring cracking and thus, provides insights for structural health monitoring (SHM). The results show, that for the first 28 days after casting, less AE activity was detected in the AAM compared to SC. After 61 days, in the AAM material, the number of AE events exceeded those observed in the SC. However, the majority of the AE detected and located in AAM was related to surface effects, and not to microstructural changes or occurring cracks within the bulk volume. Additionally, the source location analysis indicated, that despite lower activity in SC, we observed some clustering of the events. In contrast, in AAM, the activity inside the specimen is randomly distributed over the whole volume. The monitoring results help to estimate the material’s sealing properties which are crucial to assess their applicability as sealing material for engineered barriers. T2 - 11th European Workshop on Structural Health Monitoring (EWSHM 2024) CY - Potsdam, Germany DA - 11.06.2024 KW - Endlager KW - Barriere KW - AAM KW - Akustische Emission PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-604699 UR - https://www.ndt.net/article/ewshm2024/papers/768_manuscript.pdf DO - https://doi.org/10.58286/29834 SN - 1435-4934 SP - 1 EP - 7 PB - NDT.net AN - OPUS4-60469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -