TY - CONF A1 - Bäßler, Ralph A1 - Aristia, G. T1 - A Coating System for Corrosion Protection of Carbon Steel as an Alternative for High Alloyed Materials N2 - The screening of coatings shows that the modification by adding individual pigment was not sufficient to protect carbon steel even during a short-term exposure, indicated by the discoloration after only seven days of exposure. Electrochemical tests indicated that the coating cathodically protects carbon steel or slows down the corrosion reaction. A long-term exposure test confirmed that the PANI/SiO2 modified coating successfully protects the carbon steel in the Sibayak artificial geothermal water at 150 °C for 6 months. T2 - European Geothermal Congress CY - Berlin, Germany DA - 17.10.22 KW - Corrosion KW - Geothermal KW - Coatings KW - Polyaniniline KW - Silicate PY - 2022 AN - OPUS4-56084 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aristia, Gabriela A1 - Bäßler, Ralph T1 - A Coating System for Corrosion Protection of Carbon Steel as an Alternative for High Alloyed Materials T2 - Proceedings EGC 2022 N2 - Corrosive geothermal brines are a major challenge to geothermal power-plants. For cost reasons, plant designers favorize low alloyed steels, e.g., carbon steel, which are susceptible to uniform and localized corrosion when exposed to geothermal brines having acidic and saline properties. To solve such problem, coatings or inhibitors would be a protective solution as an alternative to the use of high alloyed materials. This study investigated a coating system consisting of polyaniline/silicon dioxide basing on locally available resources. Protection against corrosion of carbon steel is shown by long-term exposure and electrochemical tests of coated carbon steels, performed in an artificial acidic and saline geothermal brine, comparable to real conditions at a site in Indonesia. Therefore, an integrated coating system is presented for corrosion protection, combining the electro-chemical functionality of polyaniline and the physical advantages of silica. T2 - European Geothermal Congress CY - Berlin, Germany DA - 17.10.22 KW - Corrosion KW - Geothermal KW - Coatings KW - Polyaniniline KW - Silicate PY - 2022 SP - 1 EP - 7 CY - Berlin AN - OPUS4-56085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Additive manufacturing of metals – From fundamental technology to rocket nozzles, medical implants, and custom jewelry (Book review) T2 - Materials and Corrosion N2 - This book fulfills its intention to provide a comprehensive overview on 3D-printing of metals. The interested reader can get a lot of information about the topics one should deal with when working with additively manufactured metallic parts. It gives a general roadmap where to start, what to learn and how it fits together. KW - Additive manufacturing KW - Alloys KW - Cladding KW - 3D-Metal-Printing PY - 2018 DO - https://doi.org/10.1002/maco.201870124 SN - 0947-5117 VL - 69 IS - 12 SP - 1881 PB - WILEY-VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-46902 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Advanced ceramic and metallic coating and thin film materials for energy and environmental applications (Book review) T2 - Materials and Corrosion N2 - This book provides a state‐of‐the‐art overview on the processing, characterization, and modelling of metallic and ceramic materials used for energy and environmental applications. 17 scientists show a collection of current knowledge in 8 chapters. This book fulfills its intention to provide a reference book containing a collection of publications on thin films and coatings made of ceramic and metals used for energy and environmental applications. It covers a broad range of this topic and provides a comprehensive insight. Graduate and undergraduate students of materials science and mechanical engineering can find an overview on this topic to step in this interesting field of engineering. KW - Ceramic KW - Coating KW - Thin film KW - Energy PY - 2019 DO - https://doi.org/10.1002/maco.201970034 SN - 0947-5117 SN - 1521-4176 VL - 70 IS - 03 SP - 567 EP - 568 PB - WILEY-VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-47517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lee, Jun-Seob A1 - Bäßler, Ralph T1 - Aging of passive film on UNS N08031 in a Green-Death solution JF - Corrosion Engineering, Science and Technology N2 - Aging of passive film formed on UNS N08031 was investigated as a function of passivation time in Green-Death solution at 40°C. The specimen surface was in a stable passive state in the solution. The passive current density increased with an increase in the passivation potential. Electrochemical Impedance Spectroscopy and Mott–Schottky (M–S) analyses revealed that a more defective n-type semiconductive passive film formed as the potential increased while the film became stable as the defects in the film decreased at potential lower than 1.0 VSSE. The increase of the applied potential and the polarisation time are likely reasons for the change in passive film stability. KW - Iron–chromium–nickel alloy KW - Passivity KW - Green-Death solution KW - Flue gas desulphurisation facilities KW - Alloy 31 KW - Semiconductive layer PY - 2018 DO - https://doi.org/10.1080/1478422X.2018.1459077 SN - 1743-2782 SN - 1478-422X VL - 53 IS - 4 SP - 302 EP - 308 PB - Taylor & Francis AN - OPUS4-44923 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Werner, H. A1 - Behrens, R. T1 - Assessment of the corrosion resistance of high-alloyed metallic tank materials in the BAM-list-requirements for tanks for the transport of dangerous goods T2 - EUROCORR 2003 - Bridge between academia and industry T2 - EUROCORR 2003 CY - Budapest, Hungary DA - 2003-09-28 KW - BAM-List KW - Dangerous goods KW - Compatibility evaluations KW - High-alloyed metallic tank materials KW - Corrosion tests PY - 2003 N1 - Serientitel: EFC-Event – Series title: EFC-Event IS - 261 SP - 1 EP - 12 PB - European Federation of Corrosion CY - Budapest AN - OPUS4-2683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph T1 - Challenges for corrosion resistance of metallic materials in geothermal applications N2 - Corrosion aspects for use of metallic materials in geothermal applications are presented and discussed. T2 - Corrosion Workshop beim Geothermie Kongress 2018 CY - Essen, Germany DA - 27.11.2018 KW - Corrosion KW - Geothermal KW - Steel PY - 2018 AN - OPUS4-46744 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Challenges in corrosion (Book review) T2 - Materials and Corrosion N2 - Finally it can be concluded that this book fulfills its aim of being an attempt to present the subject of corrosion in a simple form. It introduces students into the world of corrosion making them familiar with general knowledge and certain kinds of approaches of assessing corrosion. KW - Corrosion KW - Material KW - Cost PY - 2017 DO - https://doi.org/10.1002/maco.201770044 SN - 1521-4176 VL - 68 IS - 4 SP - 484 EP - 484 PB - WILEY-VCH Verlag GmbH & Co. KgaA CY - Weinheim AN - OPUS4-43697 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Comparison of the corrosion resistance to dangerous goods of austenitic CrNiMo and duplex steels T2 - Corrosion 2014 N2 - The “BAM-List - Requirements for Tanks for the Transport of Dangerous Goods” is the basis in Germany for substance-related prototype approvals for tank Containers in Germany. Compatibility evaluations of selected metallic materials and polymeric materials under the influence of approximately 7200 dangerous goods have been published in the BAM-List since 1989. The austenitic CrNi- and CrNiMo-steels - UNS S30403, UNS S31600, UNSS31603 and UNS S31635 - are the materials mostly used worldwide for transport tanks. The duplex Steel UNS S31803 has been put on the BAMList due to the great interest of tank producers and transport Companies. Using UNS S31803 instead of 316L, the weight of the tanks can be reduced, and the list of transportable goods can be extended. The objective of these investigations was to compare the corrosion resistance of duplex Steel UNS S31803 and austenitic Steel UNS S31603. Therefore, test specimens of both steels were exposed to selected corrosive substances, such as formic acid, acetic acid, phosphoric acid, sulfuric acid, nitrating acid, monochloroacetic acid and trichloroacetone at 55 °C (30 °C, 70 °C). The test results have shown that the duplex Steel UNSS31803 is a good alternative to austenitic CrNiMo-steel UNS S31603 for tanks carrying corrosive dangerous goods. T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - Austenitic CrNiMo steel KW - Duplex steel KW - Corrosion resistance KW - Dangerous goods KW - BAM-list PY - 2014 SP - Paper 3786, 1 EP - 11 AN - OPUS4-30412 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Pötzsch, Sina A1 - Weltschev, Margit T1 - Compatibility of polymers exposed to heating oil blends with 10 % and 20 % biodiesel (FAME) N2 - Biodiesel (FAME) from rapeseed is an environmentally friendly alternative to common fossil fuels. It is also suitable to serve as blending component to fuels like heating oil. If the fuel composition is changed, materials compatibility must be guaranteed. Adding polar biodiesel to nonpolar heating oil, changes the blend’s solvency and might cause swelling, extraction and solvation of polymers. The objective of this research was to investigate the compatibility of polymeric materials, which are commonly used for components in middle distillate facilities, along with blends of heating oil and 20 % biodiesel (B20). For this propose, ACM, HNBR, FKM, PE, PA 6, POM, PUR and PVC were exposed to heating oil and B20 for 42 and 84 days at 40 °C. In addition, the polymers HNBR, FKM, PA, POM and PVC were also exposed at 70 °C. Furthermore, the resistance of polymers in eight-year aged B10 at 40 °C was evaluated. Ageing of biodiesel increases acidity which might propagate polymer corrosion. The materials were evaluated as resistant, if the loss in tensile properties (tensile strength and elongation at break) and Shore hardness remained under 15 % compared to the initial unexposed material values. For investigations under compressed conditions, the compression set was determined for specimens of ACM, FKM and HNBR after exposure in heating oil B0 and B20 for 3,7,14, 28, 56 and 90 days at 40 °C according to ISO 815-1. It was found that the resistance in B20 at 40 °C was given for all tested polymers except PUR. In the 8 years aged B10, PUR and POM were not compatible and ACM just conditionally compatible. At 70 °C, FKM and PVC were resistant in B20, whereas HNBR and PA 6 were not compatible. Swelling occurred for the elastomers ACM, HNBR and PUR. T2 - AMPP Annual International Corrosion Conference CY - Online Meeting DA - 19.04.2021 KW - Biodiesel KW - FAME KW - RME KW - Polymer in fuels KW - Corrosion PY - 2021 AN - OPUS4-52498 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pötzsch, Sina A1 - Weltschev, Margit A1 - Bäßler, Ralph T1 - Compatibility of polymers exposed to heating oil blends with 10 % and 20 % biodiesel (FAME) T2 - Proceedings Annual AMPP International Corrosion Conference 2021 N2 - Biodiesel (FAME) from rapeseed is an environmentally friendly alternative to common fossil fuels. It is also suitable to serve as blending component to fuels like heating oil. If the fuel composition is changed, materials compatibility must be guaranteed. Adding polar biodiesel to nonpolar heating oil, changes the blend’s solvency and might cause swelling, extraction and solvation of polymers. The objective of this research was to investigate the compatibility of polymeric materials, which are commonly used for components in middle distillate facilities, along with blends of heating oil and 20 % biodiesel (B20). For this propose, ACM, HNBR, FKM, PE, PA 6, POM, PUR and PVC were exposed to heating oil and B20 for 42 and 84 days at 40 °C. In addition, the polymers HNBR, FKM, PA, POM and PVC were also exposed at 70 °C. Furthermore, the resistance of polymers in eight-year aged B10 at 40 °C was evaluated. Ageing of biodiesel increases acidity which might propagate polymer corrosion. The materials were evaluated as resistant, if the loss in tensile properties (tensile strength and elongation at break) and Shore hardness remained under 15 % compared to the initial unexposed material values. For investigations under compressed conditions, the compression set was determined for specimens of ACM, FKM and HNBR after exposure in heating oil B0 and B20 for 3,7,14, 28, 56 and 90 days at 40 °C according to ISO 815-1. It was found that the resistance in B20 at 40 °C was given for all tested polymers except PUR. In the 8 years aged B10, PUR and POM were not compatible and ACM just conditionally compatible. At 70 °C, FKM and PVC were resistant in B20, whereas HNBR and PA 6 were not compatible. Swelling occurred for the elastomers ACM, HNBR and PUR. T2 - AMPP Annual International Corrosion Conference 2021 CY - Online Meeting DA - 19.04.2021 KW - Biodiesel KW - FAME KW - RME KW - Polymer in fuels PY - 2021 SP - 16222-01 EP - 16222-12 CY - Houston AN - OPUS4-52499 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Le, Quynh Hoa A1 - Bettge, Dirk T1 - Components in CO2-stream, corrosive to Materials to be Used in CC(U)S Applications N2 - CO2 quality specifications are not only a matter of CO2 purity (i.e. CO2 content). The “rest” also matters, in particular contents of reactive impurities affecting material corrosion (and rock alteration). Also chemical reactions in CO2 stream needs to be considered, in particular when combining CO2 streams of different compositions. T2 - WCO Forum at AMPP Annual International Corrosion Conference 2021 CY - Online Meeting DA - 26.04.2021 KW - Carbon capture storage KW - Corrosion PY - 2021 AN - OPUS4-52502 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Conducting polymers, fundamentals and applications – including carbon nanotubes and graphene (Book review) T2 - Materials and Corrosion N2 - Finally, it can be summarized that the second edition of this popular textbook provides a comprehensive overview on the practical basics and applications of conducting polymers. It fulfills its intension of assisting various researchers from diverse fields to become familiar with fundamentals and applications of conducting polymers. KW - Polymer KW - Degradation KW - Nanotubes PY - 2018 DO - https://doi.org/10.1002maco.201870055 SN - 1521-4176 VL - 69 IS - 5 SP - 662 PB - WILEY-VCH Verlag GmbH & Co. KgaA CY - Weinheim AN - OPUS4-44931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Conjugated polymers: Perspective, theory, and new materials (Book review) T2 - Materials and Corrosion N2 - In this also completely rewritten and reorganized second part of the two‐volume set 45 international experts comprise the current knowledge of conjugated polymers. In addition to part one on properties, processing characterization and morphology, 16 chapters cover perspectives, theory and new materials. Finally, it can be concluded that this 4th edition of this handbook fulfills, like the first part, its intention, to be the definitive resource on the topic of conducting polymers. This is assured by the updated and added contributions of all authors, which consider the significant developments both in fundamental understanding, progress and applications since publication of the previous edition. So, it can be recommended to everyone, who wants to get a comprehensive overview on conjugated polymers, not just to researchers, advanced students, and industry professionals working in materials science and engineering. KW - Polymer KW - Testing PY - 2019 DO - https://doi.org/10.1002/maco.201970094 SN - 1521-4176 SN - 0947-5117 VL - 70 IS - 9 SP - 1727 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-48886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Knauer, S A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Jaeger, P T1 - Contact angle and corrosion of a Water – CO2 system on X70 and S41500 at 278 K and pressures up to 20 MPa JF - International Journal of Greenhouse Gas Control N2 - Interfacial properties related to wettability and corrosion in CO2 transport pipelines are experimentally determined by the sessile and the pendant drop methods. The contact angle of a water drop in a compressed CO2 atmosphere is analyzed on an X70 pipeline carbon steel and compared to that on a martensitic steel S41500 to elucidate the effect of corrosion process on active wetting behaviour. The measurements are performed with liquid CO2 at 278 K and pressures ranging from 5 to 20 MPa. The results show that the contact angle (CA) increases with pressure from 132 ° to 143 ° for S41500 and from 117 ° to 137 ° for X70 and decreases with drop age by 20 ° to 24 ° regardless of the pressure and of the fact that corrosion only occurs on X70, which is confirmed by scanning electron microscopy, element mapping and energy dispersive x-ray spectrometry (EDS) analysis. At higher pressure, the contact angles on both materials converge. Further, related properties like density and interfacial tension were determined. CO2 - saturated water has a higher density than pure water: At 5 MPa saturated water reaches a density of 1017 kg⋅m^(-3) and at 20 MPa 1026 kg⋅m^(-3) compared to pure water with a density of 1002 kg⋅m^(-3) and 1009 kg⋅m^(-3), respectively. In this pressure range the IFT drops from 33 mN⋅m^(-1)at 5 MPa to 23 mN⋅m^(-1) at 20 MPa. KW - Carbon capture KW - Utilization, and storage (CCUS) technology KW - Contact angle KW - Wetting KW - Corrosion KW - Condensate KW - Impurities KW - Carbon steel PY - 2019 UR - https://www.sciencedirect.com/science/article/pii/S1750583618309472?dgcid=author DO - https://doi.org/10.1016/j.ijggc.2019.06.021 SN - 1750-5836 SN - 1878-0148 VL - 89 SP - 33 EP - 39 PB - Elsevier, ScienceDirect AN - OPUS4-48601 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Le, Quynh Hoa A1 - Yevtushenko, Oleksandra A1 - Bettge, Dirk T1 - Corrosion Aspects for Materials to be Used in CC(U)S Applications T2 - Proceedings of 1st International Conference on Corrosion Protection and Application N2 - This contribution provides current findings regarding materials susceptibility for carbon capture, utilization and storage (CCUS) applications. Basing on results gathered in 2 German long-term projects (COORAL and CLUSTER) suitable materials are introduced as well as dominating impurities of the CO2-stream and corrosion mechanisms. Investigations cover the whole CCUS process chain and provide material recommendations for certain parts. T2 - 1st International Conference on Corrosion Protection and Application CY - Chongqing, China DA - 09.10.2019 KW - Carbon KW - Capture KW - Storage KW - Utilization KW - CCS KW - CCU KW - CO2 KW - Corrosion KW - Steel PY - 2019 SP - Paper 31 PB - Chinese Society for Corrosion and Protection CY - Chongqing/China AN - OPUS4-49301 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Le, Quynh Hoa A1 - Yevtushenko, Oleksandra A1 - Bettge, Dirk T1 - Corrosion Aspects for Materials to be Used in CC(U)S Applications N2 - This contribution provides current findings regarding materials susceptibility for carbon capture, utilization and storage (CCUS) applications. Basing on results gathered in 2 German long-term projects (COORAL and CLUSTER) suitable materials are introduced as well as dominating impurities of the CO2-stream and corrosion mechanisms. Investigations cover the whole CCUS process chain and provide material recommendations for certain parts. T2 - 1st International Conference on Corrosion Protection and Application CY - Chongqing, China DA - 09.09.2019 KW - Carbon KW - Capture KW - Storage KW - Utilization KW - CCS KW - CCU KW - CO2 KW - Corrosion PY - 2019 AN - OPUS4-49302 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Ruhl, Aki Sebastian A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Kranzmann, Axel T1 - Corrosion aspects of materials selection for CO2 transport and storage T2 - 2nd ICEPE International conference on energy process engineering - Efficient carbon capture for coal power plants N2 - The geological storage of carbon dioxide (Carbon Capture and Storage, CCS) in depleted gas reservoirs or in saline aquifers is a widely discussed issue. Carbon dioxide may induce corrosion on the piping steels during compression, transportation and injection. Therefore, selection of appropriate piping steels is a key factor in order to increase the safety and reliability of the CCS technology, and to keep the processes cost-effective. The here described subproject of the COORAL project (German acronym for “C02 purity for capture and storage”) deals with the levels of impurities in the C02 stream that will be acceptable when using specific steels. Material exposure to carbon dioxide (C02) containing specific amounts of water vapor, oxygen (02) sulfur dioxide (S02), nitrogen dioxide (N02), carbon monoxide (CO) can be a challenge to steels. Within this subproject 13 different Steels are tested for suitability as materials used for compression, transportation and injection Units within the CCS chain. T2 - 2nd ICEPE International conference on energy process engineering - Efficient carbon capture for coal power plants CY - Frankfurt/M., Germany DA - 20.06.2011 KW - Carbon capture KW - CCS KW - Corrosion PY - 2011 SP - 76 EP - 78 AN - OPUS4-24250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sobetzki, Joana A1 - Bäßler, Ralph T1 - Corrosion behavior and limitations of duplex steel 1.4462 in artificial fluids of different geothermal wells in Germany T2 - EUROCORR 2013 - The European corrosion congress (Proceedings) N2 - Within the last years the use of geothermal energy as feasible energy source has risen and is going to replace fossil fuel supply more and more. Nevertheless, Service conditions in geothermal facilities are due to the Chemical composition of hydrothermal fluids and temperatures, in many cases, extreme in terms of corrosion. Since the construction of geothermal power plants shall be economical with maximum life Service, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable Operation ofthose facilities. The materials selection depends on the location of a power plant respectively on the Chemical composition of the produced aquifer fluid. The duplex Steel is often used as allround solution not only for the construction of geothermal power plants, because of its combination of good mechanical and corrosion properties and its lower costs compared to other highly alloyed materials. But there are limits for the use of the duplex-steel 1.4462 regarding its corrosion behavior, with which this contribution deals. The limitations of suitability of duplex steel 1.4462 in the geothermal fluids of Molasse Basin and Upper Rhine Graben obtained by means of electrochemical measurements and exposure tests are presented below. While 1.4462 in the artificial Molasse Basin Fluid shows an excellent corrosion resistance against pitting and uniform corrosion it presents low corrosion resistance in the artificial Upper Rhine Graben Fluid due to the difference in salinity. Besides it shows a limited corrosion resistance concerning crevice corrosion. T2 - EUROCORR 2013 - The European corrosion congress CY - Estoril, Portugal DA - 01.09.2013 KW - Localized corrosion KW - Duplex steel KW - Geothermal energy PY - 2013 SN - 978-989-8601-31-5 SP - 1 (Paper 1243) AN - OPUS4-29477 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Sarmiento Klapper, Helmuth A1 - Dimper, Matthias A1 - Keserović, Amela A1 - Sobetzki, Joana A1 - Zimmer, Sebastian T1 - Corrosion behavior of duplex stainless steel S31803 in artificial geothermal waters T2 - Proceedings of NACE International Corrosion Conference 2016 N2 - Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are due to the chemical composition of hydrothermal fluids and temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. This contribution deals with the evaluation of the corrosion behavior of duplex steel S31803 (318LN, X2CrNiMoN22-5-3, 1.4462) conducted by electrochemical measurements and exposure tests in artificial geothermal waters simulating the conditions in different locations with geothermal potential in Germany. The duplex steel S31803 shows limited suitability for applications in artificial geothermal waters due to its susceptibility to pitting and crevice corrosion. For low saline geothermal waters it can be considered suitable at moderate temperatures. Slight crevice corrosion susceptibility needs to be considered. Results are being incorporated into a materials catalogue for geothermal applications which shall provide basic information for designers and users of geothermal facilities. T2 - NACE International Corrosion Conference 2016 CY - Vancouver, BC, Canada DA - 6.3.2016 KW - S31803 KW - Crevice corrosion KW - Duplex steel KW - Geothermal energy PY - 2016 SP - 7361-1 EP - 7361-8 PB - NACE International CY - Houston TX, USA AN - OPUS4-36986 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Sarmiento Klapper, Helmuth A1 - Dimper, Matthias A1 - Keserović, Amela A1 - Sobetzki, Joana A1 - Zimmer, Sebastian T1 - Corrosion behavior of duplex stainless steel S31803 in artificial geothermal waters N2 - Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are due to the chemical composition of hydrothermal fluids and temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. This contribution deals with the evaluation of the corrosion behavior of duplex steel S31803 (318LN, X2CrNiMoN22-5-3, 1.4462) conducted by electrochemical measurements and exposure tests in artificial geothermal waters simulating the conditions in different locations with geothermal potential in Germany. The duplex steel S31803 shows limited suitability for applications in artificial geothermal waters due to its susceptibility to pitting and crevice corrosion. For low saline geothermal waters it can be considered suitable at moderate temperatures. Slight crevice corrosion susceptibility needs to be considered. Results are being incorporated into a materials catalogue for geothermal applications which shall provide basic information for designers and users of geothermal facilities. T2 - NACE International Annual Corrosion Conference CY - Vancouver, BC, Canada DA - 06.03.2016 KW - S31803 KW - Crevice corrosion KW - Duplex steel KW - Geothermal energy PY - 2016 AN - OPUS4-36987 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Carrillo Salgado, I. T1 - Corrosion behavior of highly alloyed steels in artificial saline aquifer fluids containing carbon dioxide JF - Physicochemical mechanics of materials KW - Highly alloyed steels KW - Carbon dioxide KW - Pitting corrosion PY - 2012 SN - 0430-6252 VL - 9 IS - 2 SP - 393 EP - 396 CY - L'viv, Ukrainian national academy of science AN - OPUS4-26056 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Carillo Salgado, I. T1 - Corrosion behavior of highly alloyed steels in artificial saline aquifer fluids containing carbon dioxide T2 - Latincorr 2014 - IX Latin American congress of corrosion (Proceedings) N2 - C02-corrosion on piping steels might cause problems during injection of flue gases for their storage in deep geological aquifer fluids. Therefore, the selection of appropriate piping steels is a key factor to increase safety and reliability of the Carbon Capture and Storage (CCS) technology, and to keep the process cost-efficient. Within the project COORAL (German acronym for “C02 purity for capture and storage”) corrosion studies on injection piping steels exposed to C02 and artificial brine with high Chloride concentration have been carried out. Corrosion of the injection pipe in C02-rich aquifer fluid may occur within the aquifer brine or when at injection interruptions the aquifer fluid may flow back into the injection pipe. Because of high salinity of aquifer brine and C02-corrosion an appropriate material ranking of injection piping steels should be made. Corrosion resistance of steels 1.4034, 1.4021, 1.4542, 1.4162 and 1.4562 was investigated in a corrosive environment using electrochemical and metallographic techniques. Electrochemical experiments in order to investigate the surface corrosion kinetics and polarization measurements in order to investigate localized corrosion phenomena have been carried out. Critical pitting potentials and repassivation potentials were determined by polarization curves of investigated materials and compared with measured corrosion potentials. Measured values were used in order to determine the suitability and performance of tested steels in C02-injection conditions. T2 - Latincorr 2014 - IX Latin American congress of corrosion CY - Medellín, Colombia DA - 28.10.2014 KW - Highly alloyed steels KW - Carbon dioxide KW - Pitting corrosion PY - 2014 SP - Paper 2445981, 1 EP - 5 AN - OPUS4-32746 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yevtushenko, Oleksandra A1 - Bettge, Dirk A1 - Bohraus, Stefan A1 - Bäßler, Ralph A1 - Pfennig, A. A1 - Kranzmann, Axel T1 - Corrosion behavior of steels for CO2 injection JF - Process safety and environmental protection N2 - The process chain for Carbon Capture and Sequestration (CCS) includes tubing for injection of CO2 into saline aquifers. The compressed CO2 is likely to contain specific impurities; small concentrations of SO2 and NO2 in combination with oxygen and humidity are most harmful. In addition, CO2 saturated brine is supposed to rise in the well when the injection process is interrupted. The material selection has to ensure that neither CO2 nor brine or a combination of both will leak out of the inner tubing. In this comprehensive paper the investigated materials range from low-alloy steels and 13% Cr steels up to high-alloy materials. Electrochemical tests as well as long term exposure tests were performed in CO2, in brine and combination of both; pressure was up to 100 bar, temperature up to 60 °C. Whereas the CO2 stream itself can be handled using low alloy steels, combinations of CO2 and brine require more resistant materials to control the strong tendency to pitting corrosion. The corrosion behavior of heat-treated steels depends on factors such as microstructure and carbon content. For different sections of the injection tube, appropriate materials should be used to guarantee safety and consider cost effectiveness. KW - CCS KW - Injection tubing KW - Corrosion KW - Safety KW - Carbon steel KW - High alloy steel KW - Saline fluid KW - Supercritical CO2 PY - 2014 DO - https://doi.org/10.1016/j.psep.2013.07.002 SN - 0957-5820 SN - 1744-3598 VL - 92 IS - 1 SP - 108 EP - 118 PB - Elsevier CY - Amsterdam AN - OPUS4-28966 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yevtushenko, Oleksandra A1 - Bäßler, Ralph A1 - Pfennig, A. T1 - Corrosion behaviour of Cr13 steel in CO2 saturated brine with high chloride concentration JF - Materials and corrosion N2 - The corrosion behaviour of martensitic stainless injection-pipeline steel X46Cr13 exposed to CO2 saturated artificial saline brine with high chloride concentration similar to onshore CCS-site at Ketzin, Germany has been investigated by means of electrochemical technique and microscopic observations at short exposure times (up to 24?h) and by mass loss and metallographic observations at exposure times up to 17520?h. Pitting corrosion kinetics has been characterised and the predictions about the corrosion mechanism are made. KW - Stainless steel KW - Pitting corrosion KW - Electrochemistry KW - Carbon dioxide PY - 2010 DO - https://doi.org/10.1002/maco.201005932 SN - 0947-5117 SN - 1521-4176 VL - 61 IS - 9999 SP - 1 EP - 5 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-23057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Faes, W. A1 - Lecompte, S. A1 - van Bael, J. A1 - Salenbien, R. A1 - Bäßler, Ralph A1 - Bellemans, I. A1 - Cools, P. A1 - de Geyter, N. A1 - Morent, R. A1 - Verbeken, K. A1 - de Paepe, M. T1 - Corrosion behaviour of different steel types in artificial geothermal fluids JF - Geothermics N2 - Geothermal energy is an interesting alternative to polluting fossil energy sources. Therefore, in Belgium, two wells have been drilled for a deep geothermal power plant. However, the environment to which the installations are exposed is challenging. The geothermal brine has 165 g/l total dissolved solids (of which 90% are sodium and chlorine) and the production temperature can be up to 130 °C. To assess their suitability to be used in a geothermal power plant, the corrosivity of the artificial brine to three common construction materials was investigated with exposure and electrochemical tests. The metals under consideration are a low-alloyed carbon steel (S235JR), an austenitic stainless steel (UNS S31603) and a duplex stainless steel (UNS S31803). The carbon steel, that was found to corrode uniformly, could be considered as a constructional material if a sufficient wall thickness is chosen. The austenitic stainless steel and the duplex stainless steel demonstrate very low uniform corrosion rates. They are however susceptible to pitting and crevice corrosion. To guarantee safe operation of the geothermal power plant, the susceptibility of the alloys to stress corrosion cracking should be tested and in situ experiments should be performed. KW - Geothermal energy KW - Corrosion KW - Carbon dioxide KW - Carbon steel KW - Stainless steel PY - 2019 DO - https://doi.org/10.1016/j.geothermics.2019.05.018 SN - 0375-6505 VL - 82 IS - 11 SP - 182 EP - 189 PB - Elsevier Ltd. AN - OPUS4-48759 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bender, R. A1 - Féron, D. A1 - Mills, D. A1 - Ritter, S. A1 - Bäßler, Ralph A1 - Bettge, Dirk A1 - de Graeve, I. A1 - Dugstad, A. A1 - Grassini, S. A1 - Hack, T. A1 - Halama, M. A1 - Han, E.-H. A1 - Harder, T. A1 - Hinds, G. A1 - Kittel, J. A1 - Krieg, R. A1 - Leygraf, C. A1 - Martinelli, L. A1 - Mol, A. A1 - Neff, D. A1 - Nilsson, J.-O. A1 - Odnevall, I. A1 - Paterson, S. A1 - Paul, S. A1 - Prošek, T. A1 - Raupach, M. A1 - Revilla, R. I. A1 - Ropital, F. A1 - Schweigart, H. A1 - Szala, E. A1 - Terryn, H. A1 - Tidblad, J. A1 - Virtanen, S. A1 - Volovitch, P. A1 - Watkinson, D. A1 - Wilms, M. A1 - Winning, G. A1 - Zheludkevich, M. T1 - Corrosion challenges towards a sustainable society JF - Materials and corrosion N2 - A global transition towards more sustainable, affordable and reliable energy systems is being stimulated by the Paris Agreement and the United Nation's 2030 Agenda for Sustainable Development. This poses a challenge for the corrosion industry, as building climate‐resilient energy systems and infrastructures brings with it a long‐term direction, so as a result the long‐term behaviour of structural materials (mainly metals and alloys) becomes a major prospect. With this in mind “Corrosion Challenges Towards a Sustainable Society” presents a series of cases showing the importance of corrosion protection of metals and alloys in the development of energy production to further understand the science of corrosion, and bring the need for research and the consequences of corrosion into public and political focus. This includes emphasis on the limitation of greenhouse gas emissions, on the lifetime of infrastructures, implants, cultural heritage artefacts, and a variety of other topics. KW - Corrosion KW - Corrosion costs KW - Corrosion protection KW - Preventive strategies PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-554801 DO - https://doi.org/10.1002/maco.202213140 SN - 1521-4176 VL - 73 IS - 11 SP - 1730 EP - 1751 PB - Wiley-VCH CY - Weinheim AN - OPUS4-55480 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Corrosion control through organic coatings (Book review) T2 - Materials and Corrosion N2 - Finally it can be summarized that this book fulfills its intention of providing theoretical background and examples for practical applications of coatings used for corrosion protection. It can be recommended to those being interested in coatings, serving as an overview on aspects which needs to be considered when working with such systems. KW - Coating KW - Corrosion KW - Pipeline PY - 2017 DO - https://doi.org/10.1002/maco.201770094 SN - 1521-4176 VL - 68 IS - 9 SP - 1014 EP - 1014 PB - WILEY-VCH Verlag GmbH & Co. KgaA CY - Weinheim AN - OPUS4-43706 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Le, Quynh Hoa A1 - Bettge, Dirk T1 - Corrosion Effects on Materials Considered for CC(U)S Applications N2 - Commercially available carbon steels are suitable for compression and pipelines as long as moisture content and impurities are limited. (water 50 to 100 ppmv, SO2 and NO2 ca. 100 ppmv) Corrosion rates increase with increasing water content. (0.2 – 20 mm/a) Condensation of acids and therefore droplet formation is always possible, even at low water contents. A low SO2 content within the CO2-stream might be more important than a low water content. Cr13-steels showed a general susceptibility to shallow pitting and pitting. So, they seem to be not suitable for CCUS applications. Low alloyed steels showed better corrosion behavior (predictable uniform corrosion). For direct contact with saline aquifer fluids only high alloyed steels shall be used. T2 - EFC Webinar CY - Online Meeting (Chongqing, China) DA - 18.05.2022 KW - Corrosion KW - CO2 quality KW - CO2 KW - CCS KW - CCU KW - Pipeline PY - 2022 AN - OPUS4-54854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Aristia, Gabriela A1 - Le, Quynh Hoa A1 - Bäßler, Ralph T1 - Corrosion of Carbon Steel in Artificial Geothermal Brine: Influence of Carbon Dioxide at 70 °C and 150 °C JF - Materials N2 - This study focuses on the corrosion mechanism of carbon steel exposed to an artificial geothermal brine influenced by carbon dioxide (CO2) gas. The tested brine simulates a geothermal source in Sibayak, Indonesia, containing 1500 mg/L of Cl-, 20 mg/L of SO4 2-, and 15 mg/L of HCO3-with pH 4. To reveal the temperature effect on the corrosion behavior of carbon steel, exposure and electrochemical tests were carried out at 70 °C and 150 °C. Surface analysis of corroded specimens showed localized corrosion at both temperatures, despite the formation of corrosion products on the surface. After 7 days at 150 °C, SEM images showed the formation of an adherent, dense, and crystalline FeCO3 layer. Whereas at 70 °C, the corrosion products consisted of chukanovite (Fe2(OH)2CO3) and siderite (FeCO3), which are less dense and less protective than that at 150 °C. Control experiments under Ar-environment were used to investigate the corrosive effect of CO2. Free corrosion potential (Ecorr) and electrochemical impedance spectroscopy (EIS) confirm that at both temperatures, the corrosive effect of CO2 was more significant compared to that measured in the Ar-containing solution. In terms of temperature effect, carbon steel remained active at 70 °C, while at 150 °C, it became passive due to the FeCO3 formation. These results suggest that carbon steel is more susceptible to corrosion at the near ground surface of a geothermal well, whereas at a deeper well with a higher temperature, there is a possible risk of scaling (FeCO3 layer). A longer exposure test at 150 °C with a stagnant solution for 28 days, however, showed the unstable FeCO3 layer and therefore a deeper localized corrosion compared to that of seven-day exposed specimens. KW - Carbon steel KW - CO2 KW - Corrosion KW - Electrochemical impedance spectroscopy KW - Geothermal PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-498168 DO - https://doi.org/10.3390/ma12223801 SN - 1996-1944 VL - 12 IS - 22 SP - 3801-1 EP - 20 PB - MDPI CY - Basel AN - OPUS4-49816 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yevtushenko, Oleksandra A1 - Bettge, Dirk A1 - Bäßler, Ralph A1 - Bohraus, Stefan T1 - Corrosion of CO2 transport and injection pipeline steels due to the condensation effects caused by SO2 and NO2 impurities JF - Materials and corrosion N2 - Condensates from the gas stream in simulated CO2 transport pipelines have been identified during the experiments in the laboratory. Because of their acidic origin the corrosion resistance of pipeline steels used for CCS (carbon capture and storage) technology might be limited. Over the last years it has become clear that the amount of water and acid building constituents in the CO2 stream has to be controlled very well. In this work, condensates formed in experiments using gaseous CO2 containing high amounts of water, NO2 and SO2 were analyzed, replicated, and used for extensive electrochemical experiments. These highly acidic condensates were enriched with CO2 and then applied to characteristic steels planned to use in the CCS transport chain. Even high alloy steels are susceptible to localized corrosion under these conditions. The results implicate that condensation of aggressive acid droplets has to be avoided or the locations where condensation takes place have to be controlled extensively. KW - Carbon dioxide KW - Carbon steel KW - Corrosion KW - High alloy steel PY - 2015 DO - https://doi.org/10.1002/maco.201307368 SN - 0947-5117 SN - 1521-4176 VL - 66 IS - 4 SP - 334 EP - 341 PB - Wiley-VCH CY - Weinheim AN - OPUS4-30036 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Munasir, A1 - Triwikantoro, A1 - Zainuri, M. A1 - Bäßler, Ralph A1 - Darminto, T1 - Corrosion Polarization Behavior of Al-SiO2 Composites in 1M NaCl and Related Microstructural Analysis JF - International Journal of Engineering N2 - The composites combining aluminum and silica nanoparticles with the addition of tetramethylammonium hydroxide (Al-SiO2(T)) and butanol (Al-SiO2(B)) as mixing media have been successfully fabricated. Corrosion behavior of Al-SiO2 composites before and after exposure in 1M NaCl solution was examined using potentiodynamic polarization (Tafel curve analysis). The study was also equipped with scanning electron microscopy (SEM), energy dispersive X-ray (EDX), and X-ray diffraction (XRD) investigations. Before exposure, Al-SiO2(T) exhibited the best corrosion resistance. Performance improvement was indicated by Al-SiO2(B) up to 10 times better than Al-SiO2(T) after exposure. The increased SiO2 content did not significantly enhance the corrosion resistance of the composites. The Al-SiO2 composites with 5% SiO2 content showed very high corrosion resistance (as the optimum composition). Furthermore, pitting corrosion was observed in the Al-SiO2 composites, indicated by the formation of corrosion products at grain boundaries. The product was affected by the presence of SiO2 in the Al matrix and the NaCl environment at 90 °C (approach to synthetic geothermal media: Na+, Cl, H+, OH-). Our study revealed the presence of γ-Al2O3, γ-Al(OH)3, and Al(OH)2Cl as the dominant corrosion products. KW - Al-Composite KW - Corrosion KW - Corrosion rate KW - SiO2 Nanoparticle KW - Tafel Plot PY - 2019 DO - https://doi.org/10.5829/ije.2019.32.07a.11 SN - 1025-2495 SN - 1735-9244 VL - 7 IS - 32 SP - 982 EP - 990 PB - Materials and Energy Research Center AN - OPUS4-48742 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Sarmiento Klapper, Helmuth A1 - Feigl, Michael A1 - Hilker, Nico T1 - Corrosion resistance of high-alloyed and alternative materials in an artificial geothermal water T2 - Corrosion 2014 N2 - Many technologies have been developed to take advantage of geothermal energy, which became a feasible energy source to replace fossil fuel supply. Nevertheless, service conditions in geothermal facilities are due to the chemical composition of hydrothermal fluids and involved high temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. This contribution deals with the evaluation of the corrosion behavior of two high-alloyed metallic materials and α-Al2O3 in an artificial geothermal fluid simulating the conditions in the Northern German Basin, a location with high geothermal potential. The suitability of the super austenitic stainless steel UNS N08031 and the nickel base alloy UNS N06059 in this geothermal fluid obtained by electrochemical measurements and exposure tests is addressed. As an alternative to the suitable but costly UNS N06059 that showed excellent corrosion resistance against pitting corrosion, ceramic made of α-Al2O3 represents an interesting possibility for selected components to be used in the construction of geothermal facilities T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - Localized corrosion KW - Stainless steel KW - Ni-based alloy KW - Ceramic KW - Geothermal energy PY - 2014 SP - Paper 3826, 1 EP - 8 AN - OPUS4-30632 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Sobetzki, Joana A1 - Sarmiento Klapper, Helmuth T1 - Corrosion resistance of high-alloyed materials in artificial geothermal fluids T2 - NACE International corrosion conference 2013 (Proceedings) T2 - NACE International Corrosion Conference 2013 CY - Orlando, FL, USA DA - 2013-03-17 KW - Steel KW - Geothermal KW - Brine KW - Salt solution PY - 2013 SN - 978-1-627-48145-8 SP - 1 EP - 8 (Paper 2327) PB - Curran CY - Red Hook, NY AN - OPUS4-29402 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Boduch, Alicja A1 - Sobetzki, Joana T1 - Corrosion resistance of high-alloyed materials in flowing artificial geothermal water T2 - Corrosion 2014 N2 - Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are due to the chemical composition of hydrothermal waters and temperatures, in many cases, extreme in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. This contribution deals with the evaluation of the corrosion behavior of different steels in flowing low saline, slightly alkaline, artificial geothermal water simulating the conditions in the Molasse-Basin, a location with geothermal potential in Germany. Test results for steels UNS S31603 and UNS S31803 exposed to this geothermal water obtained by electrochemical measurements and exposure tests are presented. Results obtained in static and flowing water condition show good performance of both alloys with a possible onset of localized corrosion at UNS S31603 in static conditions. T2 - Corrosion 2014 CY - San Antonio, TX, USA DA - 09.03.2014 KW - Localized corrosion KW - Steel KW - Duplex steel KW - Flow KW - Sulfide KW - Geothermal energy PY - 2014 SP - Paper 3825, 1 EP - 8 AN - OPUS4-30631 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sobetzki, Joana A1 - Le Manchet, S. A1 - Bäßler, Ralph T1 - Corrosion Resistance of the Super-Austenitic Stainless Steel UNS S31266 for Geothermal Applications T2 - Proceedings NACE International Corrosion Conference N2 - Super-austenitic stainless steels cover grades with high chromium (20 to 27 %), high nickel (18 to 31 %) and high molybdenum (4 to 6 %) contents. Within this family, the 6%Mo high nitrogen grade S31266 was developed to combine the beneficial influence of chromium, tungsten, molybdenum and nitrogen on its mechanical and corrosion properties. Due to 22 % nickel, 24 % chromium and 0.4 % nitrogen additions, this alloy exhibits a very stable microstructure, being less prone to intermetallic phase precipitation than the other highly alloyed super-austenitic stainless steels. This paper deals with the corrosion resistance of S31266 in artificial geothermal water with moderate salinity and low pH. Long-term static exposures and electrochemical tests were conducted at various temperatures to evaluate the pitting, crevice and stress corrosion cracking resistance of this material. The results show that S31266 is resistant up to 220 °C. As a consequence, it can be a good candidate material for geothermal applications involving a highly corrosive environment, especially salinity and low pH. T2 - NACE International Corrosion Conference 2107 CY - New Orleans LA, USA DA - 26.03.2017 KW - Geothermal energy KW - S31266 KW - Crevice corrosion KW - Super-austenitic stainless steel PY - 2017 SP - Paper 8825, 1 EP - 11 PB - NACE CY - Houston TX, USA AN - OPUS4-39830 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Sobetzki, Joana A1 - Le Manchet, S. T1 - Corrosion Resistance of the Super-Austenitic Stainless Steel UNS S31266 for Geothermal Applications N2 - Super-austenitic stainless steels cover grades with high chromium (20 to 27 %), high nickel (18 to 31 %) and high molybdenum (4 to 6 %) contents. Within this family, the 6%Mo high nitrogen grade S31266 was developed to combine the beneficial influence of chromium, tungsten, molybdenum and nitrogen on its mechanical and corrosion properties. Due to 22 % nickel, 24 % chromium and 0.4 % nitrogen additions, this alloy exhibits a very stable microstructure, being less prone to intermetallic phase precipitation than the other highly alloyed super-austenitic stainless steels. This paper deals with the corrosion resistance of S31266 in artificial geothermal water with moderate salinity and low pH. Long-term static exposures and electrochemical tests were conducted at various temperatures to evaluate the pitting, crevice and stress corrosion cracking resistance of this material. The results show that S31266 is resistant up to 220 °C. As a consequence, it can be a good candidate material for geothermal applications involving a highly corrosive environment, especially salinity and low pH. T2 - NACE International Corrosion Conference 2107 CY - New Orleans LA, USA DA - 26.03.2017 KW - Geothermal energy KW - Crevice corrosion KW - S31266 KW - Super-austenitic stainless steel PY - 2017 AN - OPUS4-39832 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Corrosion science and Technology (Book review) T2 - Materials and Corrosion N2 - It can be concluded, that this book fulfills its intention to be a relevant practical guide for students and professionals. The interested reader can get an insight into of all kinds of aspects one should consider when dealing with corrosion. KW - Corrosion PY - 2018 DO - https://doi.org/10.1002 maco.201870114 SN - 0947-5117 VL - 69 IS - 11 SP - 1677 EP - 1678 PB - Wiley‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-46748 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yevtushenko, Oleksandra A1 - Bäßler, Ralph A1 - Carrillo-Salgado, I. T1 - Corrosion stability of piping steels in a circulating supercritical impure CO2 environment T2 - NACE International corrosion conference 2013 (Proceedings) N2 - Within the project COORAL (German acronym for ''C02 purity for capture and storage") studies on pipeline steels exposed to circulating supercritical impure C02 have been carried out. For this purpose, a loop consisting of compressors, flow meter and two autoclaves was constructed. In order to simulate the real conditions in pipelines, impurities such as H20, CO, S02, N02 and 02 were added to the C02 stream before compression. Exposure experiments were carried out with Steel specimens placed in the autoclaves. Carbon Steel L360NB, pure iron X20Cr13, X46Cr13, X2CrMnNiN22-5-2 and alloy 31 have been exposed to circulating (flow rate 4 L/min) supercritical impure C02 for one week at 60 °C and 10 MPa Surface analysis and weight loss experiments in order to determine the corrosion products and the corrosion rates showed that the impurities cause corrosion problems. Slight general corrosion by L360NB and soft iron was observed. The initiation of pitting corrosion was observed at the surfaces of the materials X20Cr13, X46Cr13, X2CrMnNiN22-5-2. No visible signs of corrosion have been observed on alloy 31. T2 - NACE International Corrosion Conference 2013 CY - Orlando, FL, USA DA - 17.03.2013 KW - Supercritical circulating CO2 KW - Impurities KW - Exposure test KW - Corrosion PY - 2013 SN - 978-1-627-48145-8 SP - 1 EP - 11 (Paper 2372) PB - Curran CY - Red Hook, NY AN - OPUS4-28965 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Carrillo Salgado, Irene A1 - Le, Quynh Hoa T1 - Corrosion stability of piping steels in a circulating supercritical impure CO2 environment N2 - In supercritical impure CO2 (worst case scenario) highly alloyed Steels tend to pitting corrosion; iron and carbon steel tend to General corrosion, however, with low corrosion rates (< 0.1 mm/a) T2 - Kolloquium Uni Potsdam CY - Potsdam, Germany DA - 18.3.2016 KW - CCS KW - CO2 KW - Corrosion PY - 2016 AN - OPUS4-36990 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Bettge, Dirk A1 - Buggisch, E. A1 - Schiller, Bernadette Nicole A1 - Beck, M. T1 - Corrosion Study on Wellbore Materials for the CO2 Injection Process JF - Processes N2 - For reliability and safety issues of injection wells, corrosion resistance of materials used needs to be determined. Herein, representative low-cost materials, including carbon steel X70/1.8977 and low alloyed steel 1.7225, were embedded in mortar to mimic the realistic casing-mortar interface. Two types of cement were investigated: (1) Dyckerhoff Variodur commercial Portland cement, representing a highly acidic resistant cement and (2) Wollastonite, which can react with CO2 and become stable under a CO2 stream due to the carbonation process. Exposure tests were performed under 10 MPa and at 333 K in artificial aquifer fluid for up to 20 weeks, revealing crevice corrosion and uniform corrosion instead of expected pitting corrosion. To clarify the role of cement, simulated pore water was made by dispersing cement powder in aquifer fluid and used as a solution to expose steels. Surface analysis, accompanied by element mapping on exposed specimens and their crosssections, was carried out to trace the chloride intrusion and corrosion process that followed. KW - Carbon capture storage KW - CCS KW - Carbon dioxide KW - Corrosion KW - Carbon steel KW - Aquifer fluid KW - Cement KW - Casing KW - Pitting PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519774 DO - https://doi.org/10.3390/pr9010115 SN - 2227-9717 VL - 9 IS - 1 SP - 115 PB - MDPI CY - Basel AN - OPUS4-51977 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yevtushenko, Oleksandra A1 - Bäßler, Ralph A1 - Bettge, Dirk T1 - Corrosion susceptibility of steels under transport and injection exploitation conditions possible in CCS process chain T2 - EUROCORR 2014 - European corrosion congress N2 - Once sequestrated, C02 will be transported and injected in its gaseous, liquid or supercritical state. The presence of impurities significantly influences the corrosion behavior of pipeline steels even with small concentrations of water below its Saturation limit. T2 - EUROCORR 2014 - European corrosion congress CY - Pisa, Italy DA - 08.09.2014 KW - Corrosion KW - Stainless steel KW - CCS KW - COORAL PY - 2014 SN - 978-3-89746-159-8 SP - 1 AN - OPUS4-32745 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Bäßler, Ralph A1 - Werner, H. A1 - Alves, H. A1 - Behrens, R. T1 - Corrosion-resistant higher-alloyed metallic materials for the transport of corrosive dangerous goods in tanks T2 - Proceedings of CORROSION 2006 T2 - CORROSION 2006 CY - San Diego, CA, USA DA - 2006-03-12 KW - BAM-List KW - Dangerous goods KW - High-alloyed metallic tank materials KW - Corrosion tests KW - Korrosionsbeständigkeit KW - Tankwerkstoffe KW - Korrosionsuntersuchungen KW - Höherlegierte metallische Werkstoffe KW - BAM-Liste PY - 2006 SP - 06688/1 EP - 06688/12 PB - NACE CY - San Diego AN - OPUS4-12281 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, O. A1 - Le, Quynh Hoa A1 - Bettge, Dirk T1 - Corrosive CO2-stream components, challenging for materials to be used in CC(U)S applications N2 - This contribution provides current findings regarding materials susceptibility for CCUS applications. Basing on results gathered in 2 German long-term projects (COORAL and CLUSTER) suitable materials are introduced as well as dominating impurities of the CO2 stream and corrosion mechanisms. Investigations cover the whole CCUS process chain and provide the following recommendations for certain parts. Commercially available carbon steels are suitable for compression and pipelines as long as moisture content and impurities are limited (water 50 to 100 ppmv, SO2 and NO2 ca. 100 ppmv). Corrosion rates increase with increasing water content (0.2 – 20 mm/a). Condensation of acids and therefore droplet formation is always possible, even at low water contents. A low SO2 content within the CO2-stream might be more important than a low water content. Cr13-steels showed a general susceptibility to shallow pitting and pitting. So, they seem to be not suitable for CCUS applications. Low alloyed steels showed better corrosion behavior (predictable uniform corrosion). For direct contact with saline aquifer fluids only high alloyed steels shall be used. T2 - WCO Webinar on the occasion of Corrosion Awareness Day - Corrosion and Low-Carbon Energies CY - Frankfurt, Germany DA - 24.04.2020 KW - CO2-corrosion KW - CCUS KW - Pipeline KW - Carbon Capture PY - 2020 AN - OPUS4-50699 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bäßler, Ralph A1 - Eberle, Arno T1 - Damage investigation on the explosive destruction of a tank at a chlorine liquefaction plant JF - Engineering failure analysis N2 - This paper summarizes the investigation of a serious explosion, which shattered the chemical facility of a chlorine/alkaline plant in Northern Germany in 1981. A pressure tank made from HSB 50 S steel and used as storage of liquid residues from a chlorine liquefaction process violently ruptured and the explosion threw parts of the tank approximately 100 m through the air. The local county government ordered an investigation to determine the root cause of this incident. The main objective of the investigation was to determine whether a nitrogen overpressure or a chemical reaction of residuals inside the so-called 'Taffy' receiver caused the explosion. A fracture mechanics based analyses evaluated the conditions the material was exposed to during the damage. Metallographic and mechanical tests confirmed that the material specifications were within the values specified by the guidelines but corrosion had reduced the wall thickness considerably. Analytical calculations to determine the minimum required pressure for the rupture and to cause plastic deformation to the tank confirmed that the failure did not occur due to nitrogen overpressure and therefore, a chemical reaction must have occurred. A detailed chemical analysis confirmed that the explosive disintegration of methylnitrate, which is highly sensitive to heat and impact, and its halogenated derivatives likely caused the incident. Due to the design and operational mode of the plant, impurities could accumulate and form explosive compounds in the Taffy receivers without control. KW - Chlorine liquefaction process KW - 'Taffy' pressure tank failure KW - Explosion by chemical reaction of residues of methylnitrate KW - Fracture of HSB 50 S (StE 36) PY - 2014 DO - https://doi.org/10.1016/j.engfailanal.2014.02.007 SN - 1350-6307 SN - 1873-1961 VL - 43 IS - Special Issue 'A Tribute to Prof. A. Martens' SP - 120 EP - 132 PB - Elsevier Science Publ. CY - Oxford AN - OPUS4-30635 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Stoljarova, A. A1 - Regenspurg, S. T1 - Deposition of Brine Components on Materials in Geothermal Conditions T1 - ОСАЖДЕНИЕ КОМПОНЕНТОВ ГЕОТЕРМИЧЕСКИХ ВОД НА МАТЕРИАЛЫ В ГЕОТЕРМАЛЬНЫХ УСЛОВИЯХ N2 - Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are in many cases extreme in terms of corrosion due to the chemical composition of hydrothermal fluids and temperatures. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. During operation of a geothermal research facility in Groß Schönebeck copper and lead effects have been found downhole. Occurring mechanisms and measures to prevent precipitation or scaling needed to be investigated as well as potential influences of such precipitates on corrosion resistance of metallic materials used for equipment. This contribution deals with the evaluation of the corrosion behavior of carbon steel and corrosion resistant alloys in copper and/or lead containing artificial geothermal water, simulating the conditions in the Northern German Basin. The behavior of these materials in an artificial geothermal water obtained by electrochemical measurements and exposure tests are presented. While carbon steel exhibits precipitation and deposition, higher alloyed material shows different response to such species and a higher resistance in saline geothermal water. Basing on these results the suitability of the investigated corrosion resistant alloy is given for use in such conditions, whereas carbon steel creates difficulties due to its susceptibility to Cu- and Pb-precipitation. N2 - Поскольку геотермальные скважины являются реальным источником энергии для замены поставок ископаемого топлива, было разработано множество технологий для использования преимуществ геотермальной энергии. Тем не менее, условия эксплуатации на геотермальных установках во многих случаях являются экстремальными с точки зрения коррозии из-за химического состава гидротермальных жидкостей и температур. Таким образом, выбор материалов на основе предварительной квалификации имеет важное значение для обеспечения безопасной и надежной работы геотермальных объектов. Во время работы исследовательской установки в Грос Шёнебек (Groß Schönebeck) в скважине было обнаружено воздействие меди и свинца. Необходимо изучить возникшие механизмы и меры для предотвращения депозиции или образования коррозии, а также потенциальное влияние таких осаждений на коррозионную стойкость металлов, используемых для оборудования. Этот доклад посвящен оценке коррозионного поведения углеродистой стали и коррозионно-стойких сплавов в геотермальной воде, содержащей медь и / или свинец, моделирующей условия в Северогерманском бассейне (North German basin). Представлено поведение этих металлических материалов в геотермальной воде, полученной путем электрохимических измерений и испытаний на воздействие. В то время как углеродистая сталь демонстрирует коррозию и отложения, высоколегированный материал демонстрирует более высокую стойкость в соленой геотермальной воде. На основании этих результатов пригодность исследуемого коррозионно-стойкого сплава дана для использования в данных условиях, тогда как углеродистая сталь создает трудности из-за ее восприимчивости к депозиции солей меди и свинца. T2 - ХV International Conference Problems of Corrosion and Corrosion Protection of Materials “CORROSION-2020” CY - Online meeting DA - 15.10.2020 KW - Copper KW - Lead KW - Corrosion KW - Steel KW - Geothermal PY - 2020 UR - http://www.ipm.lviv.ua/corrosion2020/ AN - OPUS4-51438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph T1 - Determination of Corrosivity: Approach according to UN Regulations N2 - “Corrosive to Metals” (H290) describes the general potential danger of a substance to metallic materials. Uniform and localized attack is considered. It has nothing to do with containment material. Corrosion resistance of materials is determined similarly, but with much lower threshold values. Manual shall provide a simple test to easily determine the aggressivity potential to cause corrosion on metallic materials. Even a simple test requires experienced personnel. There seems to be a need of awareness and understanding training for both officials and applicants. T2 - ECHA GHS Training CY - Online meeting DA - 16.03.2021 KW - Corrosivity KW - Dangerous good KW - Corrosion PY - 2021 AN - OPUS4-52295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Dictionary of Metallurgy and Metal Processing - English-German – German-English (Book review) T2 - Materials and Corrosion N2 - The first issue of this classic dictionary contains highly specialized terms, not only of the area of metallurgy but also of welding, soldering and corrosion. Special attention was paid by the author to a correct reference of each term according to the field of application. Finally, this book fulfills the intension of its author, to collect relevant terms with the correct pendant from a huge variety of sources and applications. It provides the user a foundation for correct terminology and communication for international contacts. KW - Metallurgy KW - Processing PY - 2019 DO - https://doi.org/10.1002/maco.201970104 SN - 1521-4176 SN - 0947-5117 VL - 70 IS - 11 SP - 1919 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-49304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Knauer, S A1 - Kratzig, Andreas A1 - Bettge, Dirk A1 - Kranzmann, Axel T1 - Droplet corrosion of CO2 transport pipeline steels T2 - CORROSION 2018 N2 - This work examined the droplet corrosion of CO2 pipeline steels caused by impurities in CO2 supercritical/dense phase at 278 K, simulating the underground transport condition. The wetting properties of carbon steels (X52 and X70) as well as martensitic steel UNS S41500, and superaustenite UNS N08031 were studied by contact angle measurement, revealing reactive wetting behavior of carbon steels. Exposure tests with CO2 saturated water droplet on steel surface showed that the impurities (220 ppmv SO2 and 6700 ppmv O2) diffused into the droplet and then reacted with metal coupons in supercritical/dense phase condition, forming the corrosion product instantly during pumping process. Due to the active wetting behavior, the carbon steels suffered from heavily attack, while negligible corrosion product was observed in cases of martensitic steel UNS S41500 and superaustenite UNS 08031 coupons. Condensation experiments that were carried out on fresh polished coupons in CO2 with 1200 ppmv H2O showed that the formation and aggregation of droplet is dependent on the presence of impurities. Without SO2 and O2, the same concentration of H2O did not cause observable corrosion process after a week of exposure. With 220 ppmv SO2 and 6700 ppmv O2 even low water concentration (5-30 ppmv) still resulted in heterogeneous nucleation and subsequent growth of droplets, leading to corrosive process on carbon steel surface albeit to a lesser extent. T2 - CORROSION 2018 CY - Phoenix, AZ, USA DA - 15.04.2018 KW - CCUS KW - Supercritical/dense phase CO2 KW - Carbon steels KW - Martensitic steel KW - Superaustenite steel KW - Droplet corrosion PY - 2018 SP - Paper 10845, 1 EP - 11 PB - NACE International Publications Division CY - Houston, Texas, USA AN - OPUS4-44798 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le, Quynh Hoa A1 - Bäßler, Ralph A1 - Kratzig, Andreas A1 - Bettge, Dirk A1 - Kranzmann, Axel A1 - Knauer, S. T1 - Droplet corrosion of CO2 transport pipeline steels T2 - Conference Proceedings NACE International Corrosion Conference 2018 N2 - In this work, the focus was set on the corrosion process of condensate as drops on the surface of carbon steels (X52, X70), martensitic steel UNS S41500, and superaustenite UNS N08031 in CO2 atmosphere with impurities at 278 K (to simulate the transportation condition in a buried pipeline). Exposure tests were performed at both normal pressure and high pressure where CO2 is supercritical or in dense phase. The drop, 1 ‑ 10 μL in volume, was prepared by dropping CO2 saturated ultra-pure water onto the surface of steel coupons in a one-liter-autoclave. The CO2 gas stream, simulating the oxyfuel flue gas with varying concentration of impurities (SO2 and O2 ), was then pumped into the autoclave to observe the condensation and corrosion impacts of impurities. Comparable exposure tests were carried out with the same gas mixture and the same volume of water as vapor to observe the drop formation and the corrosion process that follows. The wettability and stability of drops on the surface of steel coupons in CO2 supercritical/dense phase environment was evaluated additionally by contact angle measurement. T2 - NACE International Annual Corrosion Conference CY - Phoenix, AZ, USA DA - 15.04.2018 KW - Geothermal KW - Coating KW - SiO2 KW - Polyaniline KW - Corrosion PY - 2018 SP - 10845, 1 EP - 11 PB - Omnipress CY - Houston AN - OPUS4-44917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -