TY - JOUR A1 - Österle, Werner A1 - Giovannozzi, A. A1 - Gradt, Thomas A1 - Häusler, Ines A1 - Rossi, A. A1 - Wetzel, B. A1 - Zhang, G. A1 - Dmitriev, A.I. T1 - Exploring the potential of Raman spectroscopy for the identification of silicone oil residue and wear scar characterization for the assessment of tribofilm functionality JF - Tribology International N2 - We applied a combination of Raman spectroscopy (RS) and cross-sectional transmission electron microscopy (X-TEM) to identify silicone oil residues and tribofilms at steel disc surfaces after tribological testing. Neither chemical cleaning nor mechanical removal of a 50 µm thick surface layer produced a surface without any silicone residue. Nevertheless, long-term tribological properties are not affected due to silicone degradation which has been proved by Raman spectroscopy. Excellent anti-wear and anti-friction properties of a nanocomposite at severe stressing conditions correlated with the formation of a silica-based tribofilm containing amorphous and graphite-like carbon nanoparticles. Since reliable carbon quantification by analytical TEM is difficult, RS is a useful complementary method for carbon identification at wear scars. KW - Raman spectroscopy KW - Cross-sectional TEM KW - Silicone oil residue KW - Tribofilm PY - 2015 DO - https://doi.org/10.1016/j.triboint.2015.04.046 SN - 0301-679X VL - 90 SP - 481 EP - 490 PB - Butterworth-Heinemann CY - Oxford AN - OPUS4-33421 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, G. A1 - Wetzel, B. A1 - Jim, B. A1 - Österle, Werner T1 - Impact of counterface topography on the formation mechanisms of nanostructured tribofilm of PEEK hybrid nanocomposites JF - Tribology International N2 - The effect of steel counterface topography on the formation mechanisms of nanostructured tribofilms of polyetheretherketone (PEEK) hybrid nanocomposites was studied. Three types of surface finishes with mean roughness Ra ranging from nano- to micro-scale were investigated. Tribo-sintering of nanopartides, oxidation of counterface steel and compaction of wear debris are identified to be competing factors dominating the formation and function of the tribofilms. Counterface topography played an important role on the competing factors, and thereby influenced significantly the final structure, the load-carrying capability and the lubrication performance of the tribofilms. It was disclosed that a thin tribofilm, which mainly consists of silica nanoparticles and which forms on the counterface with a submicron roughness, benefits best the tribological performance of the composites KW - Surface topography KW - Nanocomposite KW - Tribology KW - Tribofilm PY - 2015 DO - https://doi.org/10.1016/j.triboint.2014.11.015 SN - 0301-679X VL - 83 SP - 156 EP - 165 PB - Butterworth-Heinemann CY - Oxford AN - OPUS4-34612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pontes Rodrigues, A. C. A1 - Nunes Ribeiro, P. J. A1 - Österle, Werner A1 - de Farias Azevedo, C. R. T1 - Failure analysis as a tool to optimize the design of a ring on disc tribotest investigating the role of surface roughness JF - Engineering failure analysis N2 - The influence of the surface roughness of pearlitic grey cast iron discs on the formation of tribofilms and the evolution of the friction coefficient during a ring on disc tribotest with the addition of magnetite and magnetite–graphite nanopowders as interfacial media was investigated. The roughness parameters of the cast iron discs were varied by electro discharge machining (EDM) and grinding processes, producing four distinct surface roughness conditions. The evolution of the friction coefficient, however, did not reach the steady state for most of the samples and the role of the surface roughness on the friction coefficient could not be identified. Focused ion beam (FIB) microscopy on the cast iron discs was carried out to investigate the microstructure of the discs near the tribosurface. These results showed that the EDM process not only varied the surface roughness, but also changed the microstructure of the cast iron discs, promoting the incipient fusion of the cast iron surface, with the formation of ridges and casting defects (pores). As a result, a layer of rapidly solidified metal with a dendritic microstructure was formed near to the surface of the EDMed discs. KW - Ring-on disc tribotest KW - Surface roughness KW - EDM-processing KW - Rapid solification PY - 2015 DO - https://doi.org/10.1016/j.engfailanal.2015.03.011 SN - 1350-6307 SN - 1873-1961 VL - 56 SP - 131 EP - 141 PB - Elsevier Science Publ. CY - Oxford AN - OPUS4-34623 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Deutsch, Cornelius A1 - Dörfel, Ilona A1 - Gradt, Thomas A1 - Häusler, Ines A1 - Orts-Gil, G. A1 - Prietzel, C. A1 - Schneider, Thomas T1 - Final outcome of a fundamental research project on tribofilms formed during automotive braking, Part 1: Experimental studies T2 - EuroBrake 2014 (Proceedings) N2 - In order to obtain a better understanding of the role of tribofilms during automotive braking, their structures were investigated and the essential features identified. Next, different ingredient combinations were studied by preparing some model materials with simpler compositions than real tribofilms. A test method was developed for verifying the tribological properties of the model materials and for comparison with results obtained with numerical sliding simulations of such structures. Prerequisites of good brake Performance properties were identified. Although the coefficient of friction could be varied in a wide ränge, smooth sliding conditions could only be achieved with values smaller than 0.4. Tests with artificial third body powders turned out to be useful as screening method for the selection of raw materials for brake pad formulations. T2 - EuroBrake 2014 CY - Lille, France DA - 13.05.2014 KW - Tribofilm KW - Third body KW - Pad ingredients KW - Ball milling KW - Pin-on-disc test PY - 2014 SN - 978-0-9572076-4-6 SP - 1 EP - 8 PB - FISITA CY - London AN - OPUS4-35039 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dmitriev, A.I. A1 - Kloß, Heinz A1 - Österle, Werner T1 - Final outcome of a fundamental research project on tribofilms formed during automotive braking, Part 2: Numerical simulation T2 - EuroBrake 2014 (Proceedings) N2 - In part 1 it was shown that tribofilms usually are 100 nm thick and exhibit a multiphase nanocrystalline structure. The objective of our modelling efforts was to obtain a better understanding of the sliding behaviour and associated friction properties and to study the impact of internal and external parameters on these properties. The method of movable cellular automata (MCA) was used. The third bodies were considered as aggregates of linked nanoparticles which may decompose and form a layer of granulär material, the so-called mechanically mixed layer (MML), if certain fracture criteria are fulfilled. The basic model structure which consists of Fe3Ü4 nanoparticles with 13 % graphite inclusions was used. In order to assess the robustness of the model the following parameter studies were performed. The pressure ränge at an asperity contact was varied between 15 and 50 MPa. The mechanical properties of the oxide were varied between brittle and ductile behaviour corresponding to room temperature and high temperature behaviour. The mechanical properties of the soft ingredient were varied + 50 % of the properties of graphite. The influence T2 - EuroBrake 2014 CY - Lille, France DA - 13.05.2014 KW - Tribofilm KW - Third body KW - Dry friction KW - Modelling KW - Movable cellular automata PY - 2014 SN - 978-0-9572076-4-6 SP - 1 EP - 9 PB - FISITA CY - London AN - OPUS4-35040 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dmitriev, A. I. A1 - Österle, Werner T1 - Sliding simulation of automotive brake primary contact with variable amounts of copper and graphite nanoparticles T2 - ADVANCED MATERIALS WITH HIERARCHICAL STRUCTURE FOR NEW TECHNOLOGIES AND RELIABLE STRUCTURES 2016 N2 - Copper is one of the most important components in brake pads and its amount can reach up to 14%. In spite of a number of positive features copper usage in brake pad formulations has recently become the subject of considerable discussions, primarily due to concerns about potential risks related to environmental impacts of copper particles. So, for developing new pad formulations with possible replacements of copper content, it is very important to understand the functionality of copper additions to brake friction materials. In the paper theoretical investigation of the role of copper as a pad ingredient was carried out on the basis of modelling by the method of movable cellular automata (MCA). In the study the concentration of copper particles in a Fe3O4-matrix was varied. The sliding simulations were performed while assuming material properties at 500 degrees C in order to assess the beneficial role of copper during severe braking conditions corresponding to fading cycles during dynamometer testing. T2 - International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures CY - Tomsk, Russia DA - 19.09.2016 KW - Polymer matrix composite KW - Silica nanoparticles KW - Friction KW - Wear PY - 2016 DO - https://doi.org/10.1063/1.4966337 VL - 1783 SP - 020044-1 EP - 020044-4 AN - OPUS4-38933 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Österle, Werner A1 - Gesatzke, W. T1 - Dislocation particle interaction during secondary hardening and yielding of HSLA steel T2 - Proceedings 4th Riso International Symposium on Metallurgy and Material Science T2 - Riso International Symposium on Metallurgy and Material Science CY - Roskilde, Denmark DA - 05.09.1983 PY - 1983 SP - 473 EP - 478 AN - OPUS4-36051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Wever, H. A1 - Bunge, H. T1 - Development of microstructure and texture of cold rolling α iron JF - Metal Science PY - 1983 SN - 0026-0681 IS - 17 SP - 333 EP - 340 PB - Maney Publ. CY - London, UK AN - OPUS4-36056 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner T1 - Berechnung des Streckengrenzbeitrages plättchenförmiger Teilchen auf der Grundlage einer quantitativen Gefügeanalyse mit dem TEM JF - Practical metallography : preparation, imaging and analysis of microstructures = Praktische Metallographie PY - 1984 SN - 0032-678X VL - 21 SP - 377 EP - 389 PB - Hanser CY - München AN - OPUS4-36601 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ressel, P. A1 - Österle, Werner A1 - Urban, Ingrid A1 - Klein, A. A1 - Vogel, K. A1 - Kräutle, H. T1 - Transmission electron microscopy study of rapid thermally annealed Pd/Ge contacts on In0.53Ga0.47As JF - Journal of Applied Physics N2 - Phase formation in rapid thermally annealed Pd/Ge contacts on In0.53Ga0.47As has been investigated by means of cross-sectional transmission electron microscopy, convergent-beam electron diffraction, and energy-dispersive x-ray analysis. Solid-phase regrowth is observed to occur similarly as in Pd/Ge contacts on GaAs or InP. The reaction starts at low temperatures with the formation of an amorphous Pd–In–Ga–As layer, which crystallizes at elevated temperatures yielding hexagonal Pd4In0.53Ga0.47As being first described in this work. At temperatures .250 °C, this phase decomposes due to epitaxial solid-phase regrowth of In0.53Ga0.47As and formation of Pd–Ge phases. The stable composition is reached at temperatures .350 °C with excess Ge diffused through top Pd–Ge to the contact interface and growing epitaxially on the semiconductor. KW - Semiconductor KW - Thin film contact layer KW - Electron microscopy KW - Intermetallic phases PY - 1996 DO - https://doi.org/10.1063/1.363348 SN - 0021-8979 VL - 80 IS - 7 SP - 3910 EP - 3914 AN - OPUS4-38537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Reier, T. A1 - Schultze, J. W. A1 - Österle, Werner A1 - Buchal, C. T1 - Nucleation and growth of AlN nanocrystallites prepared by N+2 implantation JF - Surface and Coatings Technology N2 - The formation of AlN films prepared by N+2 ion implantation into aluminium was investigated using X-ray and Auger photoelectron spectroscopy ( XPS, AES) as well as cross-sectional transmission electron microscopy (XTEM). After 100-keV N+2 implantation of low doses (1×1017 cm−2), the formation of hexagonal AlN nanocrystals (crystal size <5 nm, Ncrystal=1017 cm−3) was observed. Their orientation is strongly correlated with the aluminium matrix. With the dose increasing to 3×1017 cm−2, crystal growth follows, finally forming a homogeneous AlN-layer. Furthermore, the diffraction patterns show an increasing amount of misorientation with increasing dose. From the crystal size distribution, we conclude that continuous nucleation takes place. Samples implanted with an energy of 3 keV exhibit analogous behaviour. Nitride growth was further investigated using microstructured AlN formed by 3-keV implantation through movable TEM-masks (structure size: 15–150 mm). In the case of high N+2 doses (D&5×1017 cm−2), AlN is detected by AES in the shielded area at a distance of up to 10 mm from the exposed region. The Diffusion coefficient was calculated to be 10−10 cm2 s−1. The formation of AlN proceeds in two steps. After a continuous nucleation, diffusion-assisted Crystal growth takes place until a homogeneous AlN layer results. KW - Aluminium nitride KW - Ion implantation KW - Nanocrystallites KW - Surface analysis KW - XTEM PY - 1998 SN - 0257-8972 VL - 103-104 SP - 415 EP - 420 PB - Elsevier AN - OPUS4-38539 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuhmann, J. F. A1 - Chiang, C. H. A1 - Harde, P. A1 - Reier, F. A1 - Österle, Werner A1 - Urban, Ingrid A1 - Klein, A. T1 - Pt thin-film metallization for FC-bonding using SnPb60/40 solder bump metallurgy JF - Materials Science and Engineering N2 - Platinum does not form any adherent oxides and can be easily wetted by tin-based solders. Platinum is also an available metallization in semiconductor laboratories. Therefore we investigated the diffusion of platinum thin-film metallizations into eutectic tin–lead solder by using a high-resolution secondary ion mass spectroscopy (SIMS) profiling from the back side. It is shown that an intermetallic phase (PtSn4) is formed during soldering, which controls the consumption of platinum during soldering and in operation. The consumption of platinum follows the well-known parabolic diffusion law. The activation energy of this process is 0.63 eV. Even at extended heating cycles of 2 min at 250°C, 190 nm from the original 300 nm of the platinum film remain undissolved. This high stability makes platinum a very attractive thin-film metallization for flip-chip (FC) bonding of new microsystems. KW - Pt thin film metallization KW - FC solder bonding KW - Diffusion KW - SIMS PY - 1998 SN - 0921-5093 VL - A242 SP - 22 EP - 25 PB - Elsevier AN - OPUS4-38540 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Würfl, J. A1 - Hilsenbeck, J. A1 - Nebauer, E. A1 - Tränkle, G. A1 - Obloh, H. A1 - Österle, Werner T1 - Reliability of AIGaN/GaN HFETs comprising refractory ohmic and Schottky contacts JF - Microelectronics Reliability N2 - Recent progress in the development of A1GaN/GaN heterostructure field effect transistors (HFETs) Shows the great potential towards high temperature / high power electronics. Nevertheless investigations on reliability properties of GaN-based devices are still at the beginning. The frequently used Ti/A1 based ohmic and Pt based Schottky contacts suffer from strong Degradation after aging at elevated temperatures. Therefore new contact systems have to be employed. Concerning the source and drain metallization we used an amorphous WSiN barrier layer as applied for GaAs on top of the Ti/Al-based ohmic contact. This technique significantly reduces the in-diffusion of the Au-containing overlayer, furthermore the barrier layer guaranties smooth contact morphology after RTA and aging, respectively. For the Schottky metallization the Ir/Au system was used. Reliability studies performed on HFET devices containing refractory Ti/A1/Ti/Au/WSiN ohmic and Ir/Au Schottky contacts demonstrate stable conditions during 120h aging at 500°C. KW - Semiconductor KW - Reliability KW - Contact resistance KW - Heterostructure field effect transistor PY - 2000 SN - 0026-2714 VL - 40 SP - 1689 EP - 1693 PB - Elsevier AN - OPUS4-38541 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Urban, Ingrid A1 - Severin, D. A1 - Trepte, S. T1 - Analyse von Reibschichten auf Bremsbelägen JF - Materialwissenschaft und Werkstofftechnik N2 - Die volle Leistung einer auf Reibung basierenden Bremse wird erst nach einem Einlaufvorgang erreicht. Dieser ist notwendig, um auf Belag und Scheibe eine sogenannte Reibschicht aufzubauen. Da diese Zwischenschicht das Reibungsverhalten des Systems maßgeblich bestimmt, ist es wichtig, sich Klarheit über ihre chemische Zusammensetzung, Mikrostruktur und die daraus resultierenden Eigenschaften zu verschaffen. Als Basismaterial diente ein phenolharzgebundener Belag Jurid 57-62, der mit verschiedenen Parametern (Flächenpressung und Umdrehungsgeschwindigkeit) gegen eine Stahlscheibe getestet wurde. Es wurden Dauerbremsungen von jeweils einer Stunde bzw. bis zu einem maximalen Belagverschleiß von 1 mm simuliert, wobei die Entwicklung der Reibzahl und die Oberflächentemperatur der Scheibe registriert wurde. Zur Analyse der Reibschichten auf dem Bremsbelag wurden mehrere Methoden parallel angewandt. So wurden Verschleißpartikel, die aus der Reibschicht stammen, gesammelt bzw. abgekratzt und nach Dispergieren auf Kohlefolien direkt im Transmissionselektronenmikros-kop (TEM) untersucht. Ferner wurden von einigen ausgesuchten Belagproben Mikrotom-schnitte sowie dünne Querschnittsfolien für die TEM-Untersuchung präpariert, um den Verbund Reibschicht-Grundmaterial darstellen zu können. Als Ergänzung wurden ferner oberflächenmorphologische und –analytische Verfahren wie REM/EDX und ESCA eingesetzt. Die Ergebnisse deuten darauf hin, dass die Reibschicht nanokristallin ist, und dass fast alle anorganischen Bestandteile des Bremsbelags sowie Eisenoxid von der Bremsscheibe in sehr fein verteilter Form vorliegen. Bei Belägen ohne Metallanteil bildet eine Barium-Eisen-Sulfatphase offenbar die Grundstruktur der Reibschicht, während auf eisenhaltigen Belägen Eisenoxid dominierend ist. Die nanokristalline Mikrostruktur entsteht, ähnlich wie beim mechanischen Legieren, durch einen Mahlvorgang von Verschleißpartikeln zwischen den Reibpartnern. Bei Überlastung des Belags tritt Zersetzung der Polymer-Bindephase ein, was zu einem raschen Anstieg der Verschleißrate führt. KW - Bremsbelag KW - Reibschicht KW - Reibungskoeffizient KW - Oberflächenanalyse KW - Transmissionselektronenmikroskopie PY - 2000 SN - 0933-5137 VL - 31 SP - 708 EP - 711 PB - Whiley VCH CY - Weinheim AN - OPUS4-38542 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nebauer, E. A1 - Österle, Werner A1 - Hilsenbeck, J. A1 - Würfl, J. A1 - Klein, A. T1 - XTEM and TFXRD investigations of ohmic Ti/Al/Ti/Au/WSiN contacts on AlGaN/GaN HFET layer systems JF - Semiconductor Science and Technology N2 - The microstructural features of the high-temperature-stable ohmic contact system Ti/Al/Ti/Au/WSiN on AlGaN/GaN were investigated using analytical transmission electron microscopy and thin film x-ray diffraction. For two typical rapid thermal annealing steps at 750 ◦C (non-ohmic behaviour) and 850 ◦C (ohmic behaviour) the intermetallic phases at the metal–semiconductor interface are presented. Increased annealing leads to the transformation of an Al2Au-AlAuTi phase mixture to a mixture of Al2Au-Al3Au8 phases and the formation of Ti-Al-nitride layers at the interfaces. In light of these results the electrical contact properties are discussed. KW - Ohmic contact KW - WSiN diffusion barrier KW - Rapid thermal annealing KW - Intermetallic phases KW - AlGaN/GaN heterostructure PY - 2002 SN - 0268-1242 VL - 17 SP - 249 EP - 254 PB - IOP Publishing Ltd AN - OPUS4-38543 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dmitriev, A. I. A1 - Österle, Werner A1 - Kloß, Heinz A1 - Orts-Gil, Guillermo T1 - A study of third body behaviour under dry sliding conditions. Comparison of nanoscale modelling with experiment JF - Estonian Journal of Engineering N2 - Automotive brake pads consist of many components but it is still not entirely clear which role each of the elements of this complex composition plays to provide the specified regimes of sliding. This is due to the mutual interaction of multiscale mechanisms, realized during the friction. In this work we have attempted to partly answer this question using computer simulations. Since the simulation allows us to consider various combinations of the structure of the system being simulated ceteris paribus, it becomes possible to understand the role of each constituent sequentially. The main attention is paid to the structure and composition of the thin film that forms on the surface of both bodies as a result of compaction of the wear product, its chemical composition and oxidation. This layer, also named a third body or friction film, differs in composition and microstructure from the two first bodies. We considered a single contact for the steady state sliding when the structure and composition of friction films already are formed. As a modelling tool we used the method of movable cellular automata, which has well proven itself in solving of such tasks. We investigated the influence of modification of the structure and composition of the third body on the features of system behaviour at friction. To assess the adequacy of the numerical model, experimental studies with an artificial third body were also carried out. The Simulation results are in good agreement with experimental data. KW - Third body KW - Dry sliding KW - Mechanically mixed layer KW - Computer simulation PY - 2012 DO - https://doi.org/10.3176/eng.2012.3.12 SN - 1736-6038 SN - 1736-7522 VL - 18 IS - 3 SP - 270 EP - 278 AN - OPUS4-38545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Natte, Kishore A1 - Friedrich, Jörg Florian A1 - Wohlrab, Sebastian A1 - Lutzki, J. A1 - von Klitzing, R. A1 - Österle, Werner A1 - Orts-Gil, Guillermo T1 - Impact of polymer shell on the formation and time evolution of nanoparticle-protein corona JF - Colloids and Surfaces B: Biointerfaces N2 - The study of protein corona formation on nanoparticles (NPs) represents an actual main issue in colloidal, biomedical and toxicological sciences. However, little is known about the influence of polymer shells on the formation and time evolution of protein corona onto functionalized NPs. Therefore, silicapoly(ethylene glycol) core–shell nanohybrids (SNPs@PEG) with different polymer molecular weights (MW) were synthesized and exhaustively characterized. Bovine serum albumin (BSA) at different concentrations (0.1–6 wt%) was used as model protein to study protein corona formation and time evolution. For pristine SNPs and SNPs@PEG (MW = 350 g/mol), zeta potential at different incubation times show a dynamical evolution of the nanoparticle–protein corona. Oppositely, for SNPs@PEG with MW ≥2000 g/mol a significant suppression of corona formation and time evolution was observed. Furthermore, AFM investigations suggest a different orientation (side-chain or perpendicular) and Penetration depth of BSA toward PEGylated surfaces depending on the polymer length which may explain differences in protein corona evolution. KW - Nanoparticles KW - Silica KW - PEGylation KW - Protein corona KW - BSA KW - Biointerface PY - 2013 DO - https://doi.org/10.1016/j.colsurfb.2012.11.019 SN - 0927-7765 VL - 104 SP - 213 EP - 220 PB - Elsevier AN - OPUS4-38547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dmitriev, A. I. A1 - Österle, Werner T1 - Modelling the sliding behaviour of tribofilms forming during automotive braking: impact of loading parameters and property range of constituents JF - Tribology Letters N2 - The impact of pressure, sliding velocity and property variation of constituents on the sliding behaviour of a model tribofilm was studied with the method of movable cellular automata (MCA). Whereas a clear pressure dependency of the coefficient of friction (COF) was always observed and could be correlated with the structure formation in terms of varying thickness of a mechanically mixed layer, the impact of the other parameters was either negligible or rather weak. Only if a brittle-to-ductile Transition of the oxide-based tribofilm was assumed, a significant decrease in the COF level was predicted. Temperature-dependent property changes can be neglected during MCA modelling, unless this transition takes place. For magnetite-based tribofilms, the transition temperature is beyond 800 °C, i.e. a temperature leading to fading effects during braking anyway. Thus, it could be concluded that, except for very severe braking conditions, sliding simulations with the MCA method yield meaningful results without considering temperature-dependent mechanical properties. KW - Tribofilm KW - Sliding behaviour KW - Friction KW - Movable cellular automata KW - Mechanically mixed layer PY - 2014 DO - https://doi.org/10.1007/s11249-013-0274-z SN - 1023-8883 SN - 1573-2711 VL - 53 IS - 1 SP - 337 EP - 351 PB - Springer AN - OPUS4-38548 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Natte, Kishore A1 - Österle, Werner A1 - Friedrich, Jörg Florian A1 - von Klitzing, R. A1 - Orts-Gil, Guillermo T1 - Tuning interfacial properties and colloidal behavior of hybrid nanoparticles by controlling the polymer precursor JF - Macromolecular Chemistry and Physics N2 - A facile and versatile synthetic route for controlling the size and surface potential of organic–inorganic hybrid silica nanoparticles (NPs) is introduced in this paper. For polymer-grafted NPs, the density of polymer chains on the surface is strongly affected by the concentration of precursor. Nevertheless, for condensed NPs, the precursor concentration determines the particle size but not the density of polymer chains on the surface or the adsorption of bovine serum albumin (BSA). Results presented here may have Major implications in biomedical and colloidal chemistry since interfacial and colloidal properties are known to drive several processes associated with nanoparticles in biological media. KW - BSA KW - Bio-interface KW - Nanosilica hybrids KW - PEG KW - Protein corona PY - 2012 DO - https://doi.org/10.1002/macp.201200148 SN - 0025-116X SN - 1022-1352 SN - 1521-3935 VL - 213 IS - 22 SP - 2412 EP - 2419 PB - Whiley-VCH CY - Weinheim AN - OPUS4-38549 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nikonov, A. Y.. A1 - Dmitriev, A. I. A1 - Österle, Werner T1 - Molecular dynamics study of slip mechanisms of nickel with amorphous-like Ni-P coating T2 - ADVANCED MATERIALS WITH HIERARCHICAL STRUCTURE FOR NEW TECHNOLOGIES AND RELIABLE STRUCTURES 2016 N2 - In the paper by using molecular dynamics method we investigate behavior of nickel-phosphorus compound in amorphous-like state under conditions of shear loading at the constant velocity. Samples with an amorphous layer of pure nickel and nickel-phosphorus compound were considered. The analysis showed that forces of shear resistance in the sample with an amorphous layer containing phosphorus in about 3 times less than the sample with a layer of pure nickel. Thus, it was shown that nickel-phosphorous coating in amorphous-like state may exhibit low friction properties, and, therefore, serve as the solid lubricant material. T2 - International Conference on Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures CY - Tomsk, Russia DA - 19.09.2016 KW - Local structural transformations KW - Lattice PY - 2016 DO - https://doi.org/10.1063/1.4966457 VL - 1783 SP - 020164-1 EP - 020164-4 AN - OPUS4-38932 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yilmaz, M. A1 - Wollschläger, Nicole A1 - Esfahani, M. N. A1 - Österle, Werner A1 - Leblebici, Y. A1 - Alaca, B. E. T1 - Superplastic behavior of silica nanowires obtained by direct patterning of silsesquioxane-based precursors JF - Nanotechnology N2 - Silica nanowires spanning 10 μm-deep trenches are fabricated from different types of silsesquioxane-based precursors by direct e-beam patterning on silicon followed by release through deep reactive ion etching. Nanowire aspect ratios as large as 150 are achieved with a critical dimension of about 50 nm and nearly rectangular cross-sections. In situ bending tests are carried out inside a scanning electron microscope, where the etch depth of 10 mm provides sufficient space for deformation. Silica NWs are indeed observed to exhibit superplastic behavior without fracture with deflections reaching the full etch depth, about two orders of magnitude larger than the nanowire thickness. A large-deformation elastic bending model is utilized for predicting the deviation from the elastic behavior. The results of forty different tests indicate a critical stress level of 0.1–0.4 GPa for the onset of plasticity. The study hints at the possibility of fabricating silica nanowires in a monolithic Fashion through direct e-beam patterning of silsesquioxane-based resins. The fabrication technology is compatible with semiconductor manufacturing and provides silica nanowires with a very good structural integrity. KW - Silica nanowires KW - HSQ KW - Superplasticity KW - In situ bending tests PY - 2017 DO - https://doi.org/10.1088/1361-6528/aa5b80 SN - 0957-4484 SN - 1361-6528 VL - 28 IS - 11 SP - Article 115302, 1 EP - 10 AN - OPUS4-39166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Dörfel, Ilona A1 - Wollenschläger, Nicole A1 - Gradt, Thomas A1 - Wolter, Christian A1 - Reinstädt, Philipp A1 - Zeigmeister, U. A1 - Dmitriev, A. I. A1 - Nikonov, A. Y. T1 - Potential of different nickel coatings for optimizing the sliding behavior of electrical connectors JF - Tribology International N2 - The potential of several nickel coatings was investigated by reciprocating sliding tests against copper thus simulating the plug-socket system of an electrical connector. KW - Electrical connectors KW - Electro-plated nickel coatings KW - Electroless Ni-P KW - Cold-welding KW - Tribooxidation PY - 2018 DO - https://doi.org/10.1016/j.triboint.2018.01.006 SN - 0301-679X SN - 1879-2464 VL - 120 SP - 491 EP - 501 PB - Elsevier Ltd. AN - OPUS4-44468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dmitriev, A. I. A1 - Häusler, Ines A1 - Wetzel, B. A1 - Zhang, G. A1 - Österle, Werner T1 - Modeling of the stress-strain behavior of an epoxy-based nanocomposite filled with silica nanoparticles JF - Materials and Design N2 - The method of movable cellular automata (MCA) was applied to simulate the stress-strain behavior of a nano composite consisting of an epoxy matrix and 6 vol. % silica nano particles. The size of the elements used for modelling was fixed at 10 nm, corresponding approximately to the diameter of the filler particles. Since not only the stress-strain response of the two constituents but also debonding of neighboring particles and granular flow was taken into account, plastic deformation as well as crack initiation and propagation could be simulated with the model. Modelling results were compared with tensile test results of both, pure epoxy as well as the epoxy-6 vol. % SiO2 composite. Since assuming bulk properties of the two constituents did not yield satisfactory results, slight modifications of the nanoparticle response functions and nanostructures were tested numerically. Finally, it was observed that only the assumption of slightly increased strength properties of the epoxy yielded good correlation between experimental and modelling results. This was attributed to an increased cross linking of the epoxy caused by the presence of silica nano particles. KW - Nanocomposite KW - Polymer matrix composite KW - Stress-strain behavior KW - Modeling KW - Computational mechanics PY - 2016 DO - https://doi.org/http://dx.doi.org/10.1016/j.matdes.2015.10.038 SN - 0264-1275 VL - 89 SP - 950 EP - 956 PB - Elsevier AN - OPUS4-35596 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dmitriev, A. I. A1 - Österle, Werner ED - Österle, Werner ED - Zhang, G. T1 - The role of solid lubricants for brake friction materials JF - Lubricants special issue "tribofilms and solid lubrication" N2 - This review article comprises of three parts. Firstly, reports of brake manufacturers on the beneficial impact of solid lubricants for pad formulations are surveyed. Secondly, since tribofilms were identified to play a crucial role in friction stabilization and wear reduction, the knowledge about tribofilm structures formed during automotive braking was reviewed comprehensively. Finally, a model for simulating the sliding behavior of tribofilms is suggested and a review on modelling efforts with different model structures related to real tribofilms will be presented. Although the variety of friction composites involved in commercial brake systems is very broad, striking similarities were observed in respect to tribofilm nanostructures. Thus a generalization of the tribofilm nanostructure is suggested and prerequisites for smooth sliding performance and minimal wear rates have been identified. A minimum of 13 vol.% of soft inclusions embedded in an iron oxide based tribofilm is crucial for obtaining the desired properties. As long as the solid lubricants or their reaction products are softer than magnetite, the main constituent of the tribofilm, the model predicts smooth sliding and a minimum of wear. KW - Solid lubricant KW - Friction KW - Automotive braking KW - Tribofilm KW - Sliding simulation KW - MCA-modeling PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-355973 UR - www.mdpi.com/journal/lubricants DO - https://doi.org/10.3390/lubricants4010005 SN - 2075-4442 VL - 4 IS - 1 SP - 5 EP - 26 PB - MDPI CY - Basel, Switzerland AN - OPUS4-35597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Dmitriev, A. I. A1 - Wetzel, B. A1 - Zhang, G. A1 - Häusler, Ines A1 - Jim, B.C. T1 - The role of carbon fibers and silica nanoparticles on friction and wear reduction of an advanced polymer matrix composite JF - Materials and design N2 - Excellent tribological properties of an advanced polymer matrix composite were obtained by a combination of micro- and nano-sized fillers. Surface features and the nanostructure of tribofilms were characterized by advanced microscopic techniques, and correlated with the macroscopic behavior in terms of wear rate and friction evolution. A model based on movable cellular automata was applied for obtaining a better understanding of the sliding behavior of the nanostructured tribofilms. The failure of the conventional composite without silica nanoparticles could be attributed to severe oxidational wear after degradation of an initially formed polymer transfer film. The hybrid composite preserves its antiwear and antifriction properties because flash temperatures at micron-sized carbon fibers, lead to polymer degradation and subsequent release of nanoparticles. It has been shown that the released particles are mixed with other wear products and form stable films at the disc surface thus preventing further severe oxidational wear. Furthermore, the released wear product also is embedding carbon fibers at the composite surface thus preventing fiber fragmentation and subsequent third body abrasion. With nanoscale modelling we were able to show that low friction and wear can be expected if the nanostructured silica films contain at least 10 vol.% of a soft ingredient. KW - Carbon fibers KW - Silica nanoparticles KW - Hybrid composite KW - Tribological properties KW - Tribofilm KW - Sliding simulation PY - 2016 DO - https://doi.org/10.1016/j.matdes.2015.12.175 SN - 0264-1275 VL - 93 SP - 474 EP - 484 PB - Elsevier AN - OPUS4-35598 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tasdemir, Z. A1 - Wollschläger, Nicole A1 - Österle, Werner A1 - Leblebici, Y. A1 - Alaca, B. E. T1 - A deep etching mechanism for trench-bridging silicon nanowires JF - Nanotechnology N2 - Introducing a single silicon nanowire with a known orientation and dimensions to a specific layout location constitutes a major challenge. The challenge becomes even more formidable, if one chooses to realize the task in a monolithic fashion with an extreme topography, a characteristic of microsystems. The need for such a monolithic integration is fueled by the recent surge in the use of silicon nanowires as functional building blocks in various electromechanical and optoelectronic applications. This challenge is addressed in this work by introducing a top-down, silicon-on-insulator technology. The technology provides a pathway for obtaining well-controlled silicon nanowires along with microstructures up to a three-order-of-magnitude scale difference. A two-step etching process is developed, where the first shallow etch defines a nanoscale protrusion on the wafer surface. After applying a conformal protection on the protrusion, a deep etch step is carried out forming the surrounding microscale features. A minimum nanowire cross-section of 35 nm by 168 nm is demonstrated in the presence of an etch depth of 10 m. All cross-sectional features are characterized via transmission electron microscopy and linked to specific process steps. The technology allows control on all dimensional aspects along with the exact location and orientation of the silicon nanowire. KW - Silicon nanowire KW - Deep reactive ion etching KW - Transmission electron microscopy PY - 2016 DO - https://doi.org/10.1088/0957-4484/27/9/095303 SN - 0957-4484 SN - 1361-6528 VL - 27 IS - 9 SP - 095303-1 EP - 095303-8 PB - IOP Publishing AN - OPUS4-35789 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Häusler, Ines A1 - Dörfel, Ilona A1 - Peplinski, Burkhard A1 - Dietrich, Paul A1 - Unger, Wolfgang A1 - Österle, Werner T1 - Comprehensive characterization of ball-milled powders simulating a tribofilm system JF - Materials characterization N2 - A model system was used to simulate the properties of tribofilms which form during automotive braking. The model system was prepared by ball milling of a blend of 70 vol.% iron oxides, 15 vol.% molybdenum disulfide and 15 vol.% graphite. The resulting mixture was characterized by X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and various transmission electron microscopic (TEM) methods, including energy dispersive X-ray spectroscopy (EDXS), high resolution investigations (HRTEM) with corresponding simulation of the HRTEM images, diffraction methods such as scanning nano-beam electron diffraction (SNBED) and selected area electron diffraction (SAED). It could be shown that the ball milling caused a reduction of the grain size of the initial components to the nanometer range. Sometimes even amorphization or partial break-down of the crystal structure was observed for MoS2 and graphite. Moreover, chemical reactions lead to a formation of surface coverings of the nanoparticles by amorphous material, molybdenum oxides, and iron sulfates as derived from XPS. KW - Tribofilm model system KW - Ball milling KW - X-ray powder diffraction KW - Transmission electron microscopy PY - 2016 DO - https://doi.org/10.1016/j.matchar.2015.11.024 SN - 1044-5803 SN - 1873-4189 VL - 111 SP - 183 EP - 192 PB - Elsevier CY - New York, NY AN - OPUS4-35051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dmitriev, A.I. A1 - Österle, Werner A1 - Wetzel, B. A1 - Zhang, G. T1 - Mesoscale modeling of the mechanical and tribological behavior of a polymer matrix composite based on epoxy and 6 vol.% silica nanoparticles JF - Computational materials science N2 - A model based on movable cellular automata (MCA) is described and applied for simulating the stress–strain and sliding behavior of a nanocomposite consisting of an epoxy matrix and 6 vol.% of homogeneously distributed silica nanoparticles. Tensile tests were used for verification of the model. It was realized that a slight modification of epoxy properties due to the addition of silica nanoparticles had to be taken into account in order to obtain good correlation between experimental and modeling results. On the other hand, sliding simulations revealed no susceptibility of results to slight modifications of matrix properties, but a significant impact of nanoparticles on the interface structure and smoothness of sliding mechanism. Furthermore, assuming both possibilities, bond breaking and rebinding of automata pairs, can explain different friction levels of polymer materials. KW - Nanocomposite KW - Stress–strain behavior KW - Movable cellular automata KW - Sliding simulation KW - Mechanically mixed layer KW - Coefficient of friction PY - 2015 DO - https://doi.org/10.1016/j.commatsci.2015.08.029 SN - 0927-0256 VL - 110 SP - 204 EP - 214 PB - Elsevier CY - Amsterdam AN - OPUS4-34013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, G. A1 - Häusler, Ines A1 - Österle, Werner A1 - Wetzel, B. A1 - Jim, B. T1 - Formation and function mechanisms of nanostructured tribofilms of epoxy-based hybrid nanocomposites JF - Wear N2 - The nanostructures and properties of the tribofilms of epoxy (EP) composites filled with short carbon fibers (SCF) and different volume fractions of monodisperse silica nanoparticles were investigated. When the conventional composite filled only with SCF was considered under a high pv condition, an iron oxide layer is formed on the steel counterface. The addition of even only 0.05 vol% nano-silica leads to a significant change of the tribofilm's structure and the tribological behavior of the composite. With increasing silica content, the oxidation layer on the steel surface is gradually replaced by a silica-based tribofilm. A close relationship between the tribofilms’ structure and the tribological behavior of the composites was identified. Mixing, possible reactions and tribo-sintering of silica nanoparticles with other wear products are deemed to be main mechanisms inducing the formation and the lubricity of the silica-based tribofilm. KW - Polymer-matrix composite KW - Sliding wear KW - Tribofilm KW - Nanoparticles KW - Tribo-sintering PY - 2015 DO - https://doi.org/10.1016/j.wear.2015.08.025 SN - 0043-1648 VL - 342-343 SP - 181 EP - 188 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-34442 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kloß, Heinz A1 - Österle, Werner A1 - Dmitriev, A.I. ED - Bartz, Wilfried J. T1 - Modelling mechanical friction and wear behaviour using numerical results of the movable cellular automata (MCA) method T2 - 19th International colloquium tribology - Industrial and automotive lubrication N2 - In the mechanical friction and wear process, normal and tangential (shear) forces cause elastic and plastic deformations, generate cracks and form loose wear particles through fracture processes. Depending on the working conditions, the material properties and the real contact Situation (topography), a third body is formed as a mechanical ly mixed layer, which determines different running-in and steady-state behaviours. Two dimensional (2D) MCA Simulation results will be described via empirical equations, which are related to the incubation time (period without wear) and the following running-in wear rate (kinetic concept of strength, fatigue wear model). In order to understand the running-in and steady-state wear, kinetic model equations for mass balance of the third body are useful and are therefore to be included in the investigation. For a more complex material behaviour, numerical Simulation results are also presented for friction at the pad-disk interface of automotive brakes. T2 - 19th International colloquium Tribology - Industrial and automotive lubrication CY - Stuttgart/Ostfildern, Germany DA - 21.01.2014 PY - 2014 SN - 978-3-943563-10-8 SP - Paper 8.10, 1 EP - 7 CY - Stuttgart/Ostfildern AN - OPUS4-30437 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schempp, Philipp A1 - Cross, C.E. A1 - Pittner, Andreas A1 - Oder, Gabriele A1 - Neumann, R.S. A1 - Rooch, Heidemarie A1 - Dörfel, Ilona A1 - Österle, Werner A1 - Rethmeier, Michael T1 - Solidification of GTA aluminium weld metal: Part I - Grain morphology dependent upon alloy composition and grain refiner content JF - Welding journal KW - Aluminium KW - Gas tungsten arc welding (GTAW) KW - Grain refinement KW - Columnar to equiaxed transition (CET) KW - Epitaxial nucleation KW - Duplex nucleation theory PY - 2014 SN - 0043-2296 SN - 0096-7629 VL - 93 SP - 53-s - 59-s PB - American Welding Society CY - New York, NY AN - OPUS4-30413 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rodrigues, A.C.P. A1 - Österle, Werner A1 - Gradt, Thomas A1 - Azevedo, César Roberto de Farias T1 - Impact of copper nanoparticles on tribofilm formation determined by pin-on-disc tests with powder supply: Addition of artificial third body consisting of Fe3O4, Cu and graphite JF - Tribology International N2 - Copper, magnetite and graphite particles were mixed in order to observe their impact on the coefficient of friction (CoF) during pin-on-disc tests and on the tribofilm formation after testing. Pure magnetite powder provided a value of CoF of 0.4. Magnetite-copper mixtures tested at 400 °C revealed lower CoF values (~0.4) than those at room temperature (~0.6). Magnetite-graphite and magnetite-graphite-copper mixtures presented lower CoF values (~0.3). All systems formed a magnetite-based tribofilm and patches of metallic copper were found on the tribosurfaces of the mixtures containing copper. Carbon layers and graphite nanoinclusions were observed in the graphite mixtures. The incorporation of zirconia particles, a by-product of ball milling mixing, prevented the selective transfer of graphite and copper to the tribosurfaces of some of the samples. KW - Brake pad materials KW - Sliding friction KW - Transfer layer KW - Surface analysis KW - Model friction tests PY - 2017 DO - https://doi.org/10.1016/j.triboint.2017.02.014 SN - 0301-679X VL - 110 SP - 103 EP - 112 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-40104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grulke, E. A. A1 - Yamamoto, K. A1 - Kumagai, K. A1 - Häusler, Ines A1 - Österle, Werner A1 - Ortel, Erik A1 - Hodoroaba, Vasile-Dan A1 - Brown, S. C. A1 - Chan, C. A1 - Zheng, J. A1 - Yamamoto, K. A1 - Yashiki, K. A1 - Song, N. W. A1 - Kim, Y. H. A1 - Stefaniak, A. B. A1 - Schwegler-Berry, D. A1 - Coleman, V. A. A1 - Jämting, Å. K. A1 - Herrmann, J. A1 - Arakawa, T. A1 - Burchett, W. W. A1 - Lambert, J. W. A1 - Stromberg, A. J. T1 - Size and shape distributions of primary crystallites in titania aggregates JF - Advanced Powder Technology N2 - The primary crystallite size of titania powder relates to its properties in a number of applications. Transmission electron microscopy was used in this interlaboratory comparison (ILC) to measure primary crystallite size and shape distributions for a commercial aggregated titania powder. Data of four size descriptors and two shape descriptors were evaluated across nine laboratories. Data repeatability and reproducibility was evaluated by analysis of variance. One-third of the laboratory pairs had similar size descriptor data, but 83% of the pairs had similar aspect ratio data. Scale descriptor distributions were generally unimodal and were well-described by lognormal reference models. Shape descriptor distributions were multi-modal but data visualization plots demonstrated that the Weibull distribution was preferred to the normal distribution. For the equivalent circular diameter size descriptor, measurement uncertainties of the lognormal distribution scale and width parameters were 9.5% and 22%, respectively. For the aspect ratio shape descriptor, the measurement uncertainties of the Weibull distribution scale and width parameters were 7.0% and 26%, respectively. Both measurement uncertainty estimates and data visualizations should be used to analyze size and shape distributions of particles on the nanoscale. KW - Measurement uncertainty KW - Size distribution KW - Shape distribution KW - TEM KW - Titania PY - 2017 DO - https://doi.org/10.1016/j.apt.2017.03.027 SN - 0921-8831 VL - 28 IS - 7 SP - 1647 EP - 1659 PB - Elsevier B.V. AN - OPUS4-40478 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yilmaz, M. A1 - Kilinc, Y. A1 - Nadar, G. A1 - Tasdemir, Z. A1 - Wollschläger, Nicole A1 - Österle, Werner A1 - Leblebici, Y. A1 - Alaca, B. E. T1 - Top-down technique for scaling to nano in silicon MEMS JF - Journal of Vacuum Science & Technology B, Nanotechnology and Microelectronics: Materials, Processing, Measurement, and Phenomena N2 - Nanoscale building blocks impart added functionalities to microelectromechanical systems (MEMS). The integration of silicon nanowires with MEMS-based sensors leading to miniaturization with improved sensitivity and higher noise immunity is one example highlighting the advantages of this multiscale approach. The accelerated pace of research in this area gives rise to an urgent need for batch-compatible solutions for scaling to nano. To address this challenge, a monolithic fabrication approach of silicon nanowires with 10-lm-thick silicon-on-insulator (SOI) MEMS is developed in this work. A two-step Si etching approach is adopted, where the first step creates a shallow surface protrusion and the second step releases it in the form of a nanowire. It is during this second deep etching step that MEMS—with at least a 2-order-of-magnitude scale difference - is formed as well. The technique provides a pathway for preserving the lithographic resolution and transforming it into a very high mechanical precision in the assembly of micro- and nanoscales with an extreme topography. Validation of the success of integration is carried out via in situ actuation of MEMS inside an electron microscope loading the nanowire up to its fracture. The technique yields nanowires on the top surface of MEMS, thereby providing ease of access for the purposes of carrying out surface processes such as doping and contact formation as well as in situ observation. As the first study demonstrating such monolithic integration in thick SOI, the work presents a pathway for scaling down to nano for future MEMS combining multiple scales. KW - Nanowires KW - Silicon KW - Top-down KW - MEMS PY - 2017 DO - https://doi.org/10.1116/1.4978047 SN - 1071-1023 VL - 35 IS - 2 SP - 022001-1 EP - 022001-7 PB - America Vacuum Society AN - OPUS4-39370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Jiao, Feng A1 - Österle, Werner A1 - Portella, Pedro Dolabella A1 - Ziebs, Josef T1 - Cyclic hardening of alloy 800h under biaxial loading T2 - Stainless steels '96 T2 - International Congress Stainless Steels '96 ; 2nd European congress CY - Düsseldorf and Neuss, Germany DA - 1996-06-03 KW - Hochtemperaturtechnik KW - Beanspruchung, zyklisch KW - Stahl, austenitisch KW - Legierung 800 H PY - 1996 SN - 3-514-00601-6 SP - 292 EP - 293 PB - Verl. Stahleisen CY - Düsseldorf AN - OPUS4-695 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Gesatzke, Wolfgang A1 - Österle, Werner A1 - Rooch, Heidemarie A1 - Urban, Ingrid ED - Portella, Pedro Dolabella T1 - Präparation von Mikro-Querschnitten mit dem fokussierten Ionenstrahl (FIB) T2 - Fortschritte in der Metallographie - Vortragstexte der 37. Metallographie-Tagung T2 - 37. Metallographie-Tagung CY - Berlin, Deutschland DA - 2003-09-17 PY - 2004 SN - 3-88355-322-0 SN - 0343-3579 N1 - Serientitel: Sonderbände der praktischen Metallographie – Series title: Sonderbände der praktischen Metallographie IS - 35 SP - 145 EP - 149 PB - Werkstoff-Informationsges. CY - Frankfurt AN - OPUS4-7641 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Portella, Pedro Dolabella A1 - Österle, Werner A1 - Jiao, F. A1 - Ziebs, Josef ED - Aldinger, F. T1 - Mechanisches Verhalten der Legierung 800H unter zyklischer zweiachsiger Beanspruchung T2 - Materialwissenschaftliche Grundlagen T2 - Werkstoffwoche '96 (WW) CY - Stuttgart, Deutschland DA - 1996-05-28 PY - 1997 SN - 3-88355-235-6 N1 - Serientitel: Werkstoffwoche '96 Symposium – Series title: Werkstoffwoche '96 Symposium IS - 7 SP - 361 EP - 366 PB - DGM Informationsges. CY - Frankfurt AN - OPUS4-2637 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bauer, Gisela A1 - Frenz, Holger A1 - Österle, Werner A1 - Wedell, Wolfgang ED - Aldinger, F. T1 - Ermüdungsverhalten kugelgestrahlter Proben aus IN 738 LC bei 650°C T2 - Materialwissenschaftliche Grundlagen T2 - Werkstoffwoche '96 (WW) CY - Stuttgart, Deutschland DA - 1996-05-28 PY - 1997 SN - 3-88355-235-6 N1 - Serientitel: Werkstoffwoche '96 Symposium – Series title: Werkstoffwoche '96 Symposium IS - 7 SP - 403 EP - 408 PB - DGM Informationsges. CY - Frankfurt AN - OPUS4-2636 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kinder, Joachim A1 - Klinger, Christian A1 - Österle, Werner A1 - Klingbeil, Dietmar ED - Portella, Pedro Dolabella T1 - Mechanisch induzierte Zwillingsbildung in Blechen aus Baustahl T2 - Fortschritte in der Metallographie - Vortragstexte der 35. Metallographie-Tagung T2 - 35. Metallographie-Tagung CY - Neu-Ulm, Deutschland DA - 2001-09-19 PY - 2002 SN - 3-88355-303-4 SN - 0343-3579 SP - 47 EP - 52 PB - Werkstoff-Informationsges. CY - Frankfurt AN - OPUS4-1364 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Aurich, Dietmar A1 - Helms, Rolf A1 - Österle, Werner A1 - Portella, Pedro Dolabella A1 - Ziebs, Josef T1 - Untersuchungen an einkristallinen Superlegierungen für Turbinenschaufeln T2 - Stähle für den Stahlbau T2 - VDEh-Vortragsveranstaltung "Stähle für den Stahlbau" CY - Düsseldorf, Deutschland DA - 1988-04-26 PY - 1988 SN - 3-514-00407-2 SP - 140 EP - 150 PB - Verl. Stahleisen CY - Düsseldorf AN - OPUS4-2456 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bettge, Dirk A1 - Österle, Werner A1 - Ziebs, Josef T1 - Temperature dependence of yield strength and elongation of the nickel-base superalloy IN 738 LC and the corresponding microstructural evolution JF - Zeitschrift für Metallkunde PY - 1995 SN - 0179-4841 SN - 0044-3093 VL - 86 SP - 190 EP - 197 PB - Hanser CY - München AN - OPUS4-2481 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jiao, Feng A1 - Österle, Werner A1 - Portella, Pedro Dolabella A1 - Ziebs, Josef T1 - Biaxial path-dependence of low-cycle fatigue behaviour and microstructure of alloy 800 H at room temperature JF - Materials science and engineering A N2 - Low-cycle fatigue experiments under combined axial-torsional loading have been carried out on alloy 800 H tubular specimens at room temperature. In comparison with proportional loading, an extra cyclic hardening effect produced by nonproportional loading was observed. The microstructure study highlights the fact that the dislocation arrangement under proportional loading is significantly different from that under nonproportional loading. Mechanical twinning was found in specimens cycled under axial loading and nonproportional loading. It is suggested that mechanical twinning depends not only on shear stress but also on normal stress on the plane of maximum shearing. The extra hardening can be interpreted in terms of the deformation microstructure. Fatigue cracking was initiated generally at the specimen surfaces along the plane of maximum shearing, but under nonproportional loading cracks were found also in the bulk of the specimens. Transcrystalline crack propagation was observed in the specimens after proportional and nonproportional LCF tests. PY - 1995 DO - https://doi.org/10.1016/0921-5093(94)09690-2 SN - 0921-5093 SN - 1873-4936 VL - 196 IS - 1 SP - 19 EP - 24 PB - Elsevier CY - Amsterdam AN - OPUS4-2503 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jiao, F. A1 - Bettge, Dirk A1 - Österle, Werner A1 - Ziebs, Josef T1 - Tension-compression asymmetry of the [001] single crystal nickel-base superalloy SC16 under cyclic loading at elevated temperatures JF - Acta materialia PY - 1996 SN - 1359-6454 SN - 1873-2453 VL - 44 SP - 3933 EP - 3942 PB - Elsevier Science CY - Kidlington AN - OPUS4-2509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fedelich, Bernard A1 - Frenz, Holger A1 - Österle, Werner A1 - Ohm, Katrin ED - Lütjering, G. T1 - A stochastic model for LCF small crack growth in a nickel-base superalloy T2 - Fatigue '96 T2 - 6th International Fatigue Congress CY - Berlin, Germany DA - 1996-05-06 PY - 1996 SN - 0-08-042268-3 VL - 96 IS - 2 SP - 1263 EP - 1268 PB - Pergamon CY - Oxford AN - OPUS4-2511 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Dörfel, Ilona A1 - Effner, Ute A1 - Glaubitz, Steffen A1 - Österle, Werner A1 - Rudolph, Edith ED - Ziegler, G. T1 - Charakterisierung hochfester ZrO2-Werkstoffe T2 - Werkstoff- und Verfahrenstechnik (Werkstoffwoche '96 Symposium 6) T2 - Werkstoffwoche '96 (WW) CY - Stuttgart, Deutschland DA - 1996-05-28 PY - 1997 SN - 3-88355-234-8 VL - 6 SP - 691 EP - 702 PB - DGM Informationsges. CY - Frankfurt AN - OPUS4-2635 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Binkowski, Sigrid A1 - Hübner, Wolfgang A1 - Aßmus, Kristin A1 - Benemann, Sigrid A1 - Österle, Werner ED - Portella, Pedro Dolabella T1 - Charakterisierung des Gefüges der austenitischen FeCrNi-Legierung 1.4876 nach Reibbeanspruchung bei 37 K T2 - Fortschritte in der Metallographie - Vortragstexte der 37. Metallographie-Tagung T2 - 37. Metallographie-Tagung CY - Berlin, Deutschland DA - 2003-09-17 PY - 2004 SN - 3-88355-322-0 SN - 0343-3579 N1 - Serientitel: Sonderbände der praktischen Metallographie – Series title: Sonderbände der praktischen Metallographie IS - 35 SP - 213 EP - 218 PB - Werkstoff-Informationsges. CY - Frankfurt AN - OPUS4-3420 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Österle, Werner A1 - Portella, Pedro Dolabella A1 - Ziebs, Josef A1 - Jiao, Feng ED - Lütjering, G. T1 - Mechanical behaviour of alloy 800h under cyclic biaxial loading T2 - Fatigue '96 T2 - 6th International Fatigue Congress CY - Berlin, Germany DA - 1996-05-06 KW - Legierung KW - Belastung, zyklisch KW - Beanspruchung, mechanisch PY - 1996 SN - 0-08-042268-3 VL - 2 IS - 2 SP - 989 EP - 994 PB - Pergamon CY - Oxford AN - OPUS4-669 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sievert, Rainer A1 - Österle, Werner A1 - Olschewski, Jürgen A1 - Ziebs, Josef T1 - Physical interpretation of a viscoplastic model applied to high temperature performance of a nickel-base superalloy T2 - Proceedings of the 7th International Conference on Mechanical Behaviour of Materials T2 - 7th International Conference on Mechanical Behaviour of Materials CY - The Hague, Netherlands DA - 1995-01-01 PY - 1995 SP - 557 EP - 558 CY - Den Haag AN - OPUS4-2507 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Oder, Gabriele A1 - Österle, Werner ED - Portella, Pedro Dolabella T1 - Anwendungsbeispiele für die Elektronenstrahl-Mikrosonde T2 - Fortschritte in der Metallographie - Vortragstexte der 37. Metallographie-Tagung T2 - 37. Metallographie-Tagung CY - Berlin, Deutschland DA - 2003-09-17 PY - 2004 SN - 3-88355-322-0 SN - 0343-3579 N1 - Serientitel: Sonderbände der praktischen Metallographie – Series title: Sonderbände der praktischen Metallographie IS - 35 SP - 141 EP - 144 PB - Werkstoff-Informationsges. CY - Frankfurt AN - OPUS4-7690 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Orts Gil, Guillermo A1 - Natte, Kishore A1 - Thiermann, Raphael A1 - Girod, Matthias A1 - Rades, Steffi A1 - Kalbe, Henryk A1 - Thünemann, Andreas A1 - Maskos, M. A1 - Österle, Werner T1 - On the role of surface composition and curvature on biointerface formation and colloidal stability of nanoparticles in a protein-rich model system JF - Colloids and surfaces B: Biointerfaces N2 - The need for a better understanding of nanoparticle–protein interactions and the mechanisms governing the resulting colloidal stability has been emphasised in recent years. In the present contribution, the short and long term colloidal stability of silica nanoparticles (SNPs) and silica–poly(ethylene glycol) nanohybrids (Sil–PEG) have been scrutinised in a protein model system. Well-defined silica nanoparticles are rapidly covered by bovine serum albumin (BSA) and form small clusters after 20 min while large agglomerates are detected after 10 h depending on both particle size and nanoparticle–protein ratio. Oppositely, Sil–PEG hybrids present suppressive protein adsorption and enhanced short and long term colloidal stability in protein solution. No critical agglomeration was found for either system in the absence of protein, proving that instability found for SNPs must arise as a consequence of protein adsorption and not to high ionic environment. Analysis of the small angle X-ray scattering (SAXS) structure factor indicates a short-range attractive potential between particles in the silica-BSA system, which is in good agreement with a protein bridging agglomeration mechanism. The results presented here point out the importance of the nanoparticle surface properties on the ability to adsorb proteins and how the induced or depressed adsorption may potentially drive the resulting colloidal stability. KW - Nanoparticles KW - Protein corona KW - Biointerface KW - BSA KW - PEG KW - Colloidal stability PY - 2013 DO - https://doi.org/10.1016/j.colsurfb.2013.02.027 SN - 0927-7765 SN - 1873-4367 VL - 108 SP - 110 EP - 119 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-30100 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -