TY - CONF A1 - El-Batahgy, A. A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Effect of laser-beam and hybrid-laser-arc welding parameters and filler metal on microstructure and mechanical properties of thick heat-treated steel X8ni9+Qt640 for cryogenic service T2 - 4th International Conference on Welding and Failure Analysis of Engineering Materials N2 - The present research work encloses results of experimental investigations of the interaction between welding process parameters for laser-beam and hybrid-laser-arc as well as type of the filler metal and the achievable mechanical properties of the weld joints on steel grade X8Ni9+QT640 for cryogenic service containing 9% nickel. The results obtained contribute to the development and conversion in the industrial practice a new laser beam-based welding technology for the automated manufacturing of facilities for the liquefaction, storage and the transport of natural gases (LNG facilities). The results show, that the martensitic microstructure of the laser weld metal including low amount of retained austenite not exceeding 3.5% leads to the relatively low V-notch impact energy. The remarkable heterogeneity in the chemical composition of the weld metal through the weld thickness could be recognized in the case of hybrid-laser-arc welding with ERNiCrMo-3 austenitic filler metal, what also led to insufficient impact toughness of the weld metall. The most promising results could be achieved by using 11%Ni filler wire, which is similar to the base metal and provides a homogeneous microstructure with uniform distribution of Ni through the weld seam. It is remarkable, that a correlation between Charpy impact toughness and wire feeding speed and respectively process heat input exists. The highest toughness values were 134±58 J at -196C. The both laser as well as laser-hybrid welds passed the tensile test. The failure stress of 720±3 MPa with a fracture location in the base material was achieved for all samples tested. T2 - 4th International Conference on Welding and Failure Analysis of Engineering Materials CY - Aswan, Egypt DA - 19.11.2018 KW - Hybrid-laser-arc welding KW - Laser-beam welding, KW - Cryogenic steel KW - Microstructure KW - Tensile strength PY - 2018 SP - W-29, 1 EP - 10 AN - OPUS4-46738 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uhlmann, E. A1 - Meier, P. A1 - Hinzmann, D. A1 - Kropidlowski, K. A1 - Prasol, L. A1 - Woydt, Mathias T1 - Dry turning with niobium carbide based tools T2 - 2018 World Congress on Powder Metallurgy N2 - In the present work it was shown that Niobium carbide (NbC) offers a competitive profile compared to tungsten carbide (WC) as cutting material regarding ist wear resistance preferably in metal cutting processes. T2 - WORLDPM 2018 CY - Beijing, China DA - 16.09.2018 KW - Turning KW - Semi-finishing KW - Niobium carbide KW - Tungsten carbide KW - Iron-based alloys KW - Aluminum PY - 2018 SP - Part 5, 775 EP - 784 AN - OPUS4-46203 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Woydt, Mathias T1 - Dry turning with niobium carbide based tools T2 - POWDERMET 2018 N2 - Niobium carbide (NbC) has attracted recently some attention as a substitute for tungsten carbide in machining. In the present work it was shown that the metallurgical and mechanical aspects favoring long tool lifes of NbC. T2 - POWDERMET 2018 CY - San Antonio, TX, USA DA - 17.06.2018 KW - Niobium carbide KW - NbC KW - Cutting tool KW - Machining PY - 2018 SN - 978-1-943694-18-1 VL - 2 SP - 538 EP - 545 AN - OPUS4-45802 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pavlov, V.A. A1 - Zavialov, S.V. A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Development of a measuring technology of strain field in welds T2 - 20th International Conference Digital Signal Processing N2 - In the article considered the problem of hot cracks occurrence during laser welding process. The main reason of their appearance is strain. The optical method for measuring full field strain locally near the solidification front during laser welding process is proposed. The proposed method of optical measurement allows to determine the real values of the critical strain for various materials characterizing the occurrence of hot cracks in laser welding process. T2 - 20th international conference "Digital signal processing and applications DSPA-2018" CY - Moskau, Russia DA - 28.03.2018 KW - Solidification cracking KW - Critical strain KW - Strain rate KW - Optical measurement KW - Laser welding KW - In situ strain PY - 2018 SN - 978-5-905278-33-4 SP - 749 EP - 754 AN - OPUS4-44910 LA - rus AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Le Quilliec, G. A1 - Leroy, R. A1 - Richard, C. A1 - Woydt, Mathias A1 - Morandeau, A. T1 - Comparison of the life-span of NbC-Co and WC-Co inserts during different machining operations on 100Cr6 (SAE 52100) bearing steel T2 - Proceedings of the International Symposium on Wear Resistant Alloy for the Mining and Processing Industry N2 - The aim of the study presented in this paper is to highlight the potential of niobium carbide cutting tool inserts for machining and to compare their performance to commercially available tungsten carbide inserts. In this work, a comparison between a conventional Wc-Co insert and NbC-Co inserts was carried out under hard machining conditions on specimens made of 100Cr6 bearing steel grade (SAE 52100). T2 - International Symposium on Wear Resistant Alloys for the Mining and Processing Industry CY - Sao Paulo, Brazil DA - 04.05.2015 KW - Niobium carbide KW - Cobalt KW - Fe3Al KW - Inserts KW - Cutting tools KW - Wear KW - Turning PY - 2018 SN - 978-0-692-05382-9 SP - 535 EP - 545 AN - OPUS4-44207 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wägner, Yannick A1 - Binkowski, Sigrid A1 - Woydt, Mathias T1 - Charakterisierung von Hartstoffphasen in Gefüge T2 - Fortschritte in der Metallographie - Sonderbände der Praktischen Metallographie N2 - Der Beitrag handelt von der Verbesserung der Verschleißbeständigkeit von Hartstoffphasen in Metal Matrix Composites (MMC), Hartgusslegierungen, Hadfield-Stählen oder Werkzeugstählen. T2 - 15. International Metallographie-Tagung CY - Leoben, Asutria DA - 19.09.2018 KW - Verschleißbeständigkeit KW - Hartstoffphasen KW - NbC PY - 2018 SN - 978-3-88355-416-7 VL - 52 SP - 133 EP - 138 PB - DGM - INVENTUM GmbH CY - Sankt Augustin AN - OPUS4-46056 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, T. A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Build-up Strategies for Laser Metal Deposition in Additive Manufacturing T2 - Fraunhofer Direct Digital Manufacturing Conference - Konferenzband N2 - Laser Metal Deposition (LMD) as a technology for additive manufacturing allows the production of large components outside of closed working chambers. Industrial applications require a stable process as well as a constant deposition of the filler material in order to ensure uniform volume growth and reproducible mechanical properties. This paper deals with the influence of travel path strategies on temperature profile and material deposition. Meandering and spiral hatching strategies are used in the center as well as in the edge of a specimen. The temperature is measured with thermocouples attatched to the backside of the specimen. The tests are carried out on the materials S235JR and 316L. The results show a strong dependence of the maximum temperatures on the travel path strategy and the welding position on the component. T2 - Fraunhofer Direct Digital Manufacturing Conference (DDMC) CY - Berlin, Germany DA - 14.03.2018 KW - Additive Manufacturing KW - Temperature behavior KW - Laser Metal Deposition KW - Stainless Steel KW - 316L KW - Edge effects PY - 2018 SN - 978-3-8396-1320-7 VL - 1 SP - 1 EP - 6 PB - Fraunhofer-Gesellschaft CY - München AN - OPUS4-44719 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fabry, Çağtay A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Automatisierungs- und Regelkonzepte für das MSG-Engspaltschweißen - Pendel- und Füllgradregelung T2 - 37. Assistentenseminar Füge- und Schweißtechnik N2 - Das MSG-Engspaltschweißen eignet sich auf Grund der I-Nahtvorbereitung besonders für das wirtschaftliche Fügen bei hohen Blechdicken über 100 mm und bietet darüber hinaus zusätzliche technologische Vorteile. Für die automatisierte Anwendung des Verfahrens unter Produktionsbedingungen muss dabei die Prozesssicherheit auch für mitunter große Variationen der Spaltbreite entlang der Schweißnaht gesichert bleiben. In erster Linie betrifft dies bei mechanischer Auslenkung der Drahtelektrode die Adaption der Pendelbewegung auf die jeweilige Spaltbreite um eine ausreichende Flankenanbindung zu garantieren. Für die Online-Regelung der Pendelbewegung mittels Lichtbogensensorik wurde eine Methode implementiert die die notwendigen Pendelwinkel an jeder Nahtflanke unabhängig ermittelt und darüber hinaus Fehlstellungen des Brenners sowie Veränderungen des Kontaktrohrabstandes und der Prozessparameter eigenständig kompensiert. Eine Füllgradregelung auf Grundlage optischer Erfassung und Auswertung der Schweißnahtgeometrie wurde zusätzlich eingesetzt um bei veränderlichen Nahtquerschnittsflächen einen vorgegebenen, gleichbleibenden Lagenaufbau zu erzielen. T2 - WGF Assistentenseminar 2016 CY - Paewesin, Germany DA - 06.09.2016 KW - MSG-Engspaltschweißen KW - MAG Prozesssteuerung KW - Sensorik KW - Lichtbogensensorik KW - Profilvermessung PY - 2018 SN - 978-3-96144-025-2 VL - 339 SP - 1 EP - 7 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-44284 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spranger, Felix A1 - Hilgenberg, Kai A1 - Rethmeier, Michael T1 - Anwendung der Laserimplantation zur Strukturierung verschleißgefährdeter Werkzeuge T2 - 38. Assistentenseminar Fügetechnik / DVS Berichte N2 - In einer Vielzahl technischer Anwendungen spielt die Aufrechterhaltung eines definierten Reibungs- und Verschleißverhaltens zwischen bewegten Oberflächen für die Sicherheit und Funktionalität eine entscheidende Rolle. Die Oberflächentechnik versucht durch geeignete Verfahren die Randschichten zu ertüchtigen, um Reibung und Verschleiß zu kontrollieren. Eine Verbesserung der Materialeigenschaften kann durch flächige Beschichtungen erreicht werden. Zusätzlich ermöglichen Oberflächenstrukturierungen breite Möglichkeiten zur Beeinflussung des Schmierungszustandes bzw. der Kontaktbedingungen. Neben Negativstrukturen bieten ebenfalls erhabene Mikrostrukturen großes Potenzial zur Beeinflussung des tribologischen Verhaltens. Ihr Einsatz ist aber aufgrund der besonderen Verschleißproblematik erhabener Strukturen momentan limitiert, so dass in der Regel zusätzliche verschleißreduzierende Beschichtungen notwendig werden. In diesem Beitrag wurde das Verfahren der Laserimplantation angewandt, mit dem erhabene und separierte Oberflächenstrukturen hoher Verschleißfestigkeit in einem Fertigungsschritt erzeugbar sind. Das Verfahren basiert auf einem lokalisierten Dispergieren von Hartstoffpartikeln. Hierfür wurde erstmalig ein gepulster Faserlaser mit hoher Strahlqualität zur Erzeugung punkt- und linienförmiger Mikrostrukturen angewandt. Versuche wurden auf dem Kaltarbeitsstahl X153CrMoV12 unter Anwendung von Titandiborid als Hartstoff durchgeführt. Anhand von Härtemessungen konnte gezeigt werden, dass sowohl punkt- als auch linienförmige Strukturen mit Härten über 1000 HV1 und einer feinkörnigen Mikrostruktur mit feinverteilten Hartstoffpartikeln herstellbar sind. Des Weiteren war es möglich, die Implantgeometrien, welche an Querschliffen und durch Weißlichtinterferometeraufnahmen erfasst wurden, durch die Pulsleistung und Pulsdauer zu steuern. T2 - 38. Assistentenseminar der WGF CY - Rabenau, Germany DA - 06.09.2017 KW - Laserimplantation PY - 2018 SN - 978-3-96144-028-3 VL - 342 SP - 24 EP - 33 CY - Düsseldorf AN - OPUS4-47295 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiede, Tobias A1 - Cabeza, Sandra A1 - Mishurova, Tatiana A1 - Nadammal, Naresh A1 - Kromm, Arne A1 - Bode, Johannes A1 - Haberland, C. A1 - Bruno, Giovanni T1 - An assessment of bulk residual stress in selective laser melted Inconel 718 T2 - Proceedings ECNDT2018 N2 - Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing. The residual stress distribution in the bulk of IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate. The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction. T2 - ECNDT 2018 CY - Göteborg, Sweden DA - 11.06.2018 KW - Residual stress KW - Selective laser melting KW - Neutron diffraction KW - IN718 PY - 2018 UR - http://cdn.ecndt2018.com/wp-content/uploads/2018/05/ecndt-0315-2018-File001.pdf SP - 1 AN - OPUS4-45325 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -