TY - JOUR A1 - Eberstein, Markus A1 - Glitzky, Carsten A1 - Gemeinert, Marion A1 - Rabe, Torsten A1 - Schiller, Wolfgang Arno A1 - Modes, C. T1 - Design of LTCC with high thermal expansion JF - International Journal of Applied Ceramic Technology N2 - New applications of low-temperature co-fired ceramics (LTCC), such as pressure sensors or integrated functional layers, require materials that possess higher coefficients of thermal expansion (CTE). To fabricate LTCC with elevated CTE, two methods of material design are examined: firstly, glass ceramic composites (GCC), which consist of >50 vol% glass in the starting powder, and, secondly, glass-bonded ceramics (GBC), where glass is added as a sintering aid only. The CTE of GBC is mainly determined by the crystalline component. For GCC, the CTE can be well predicted, if CTE and elastic data of each phase in the microstructure are known. A nonlinear characteristic of the CTE versus phase composition was found with increasing Ecrystals/Eglass ratio and absolute CTE difference between the components. The glass composition and glass amount can be used to compensate the fixed properties of a crystalline material in a desired way. However, because the CTE and permittivity of a glass cannot be chosen independently, an optimum glass composition has to be found. For a given LTCC, it is possible to control the devitrification by shifting the glass composition. In this way, the resulting CTE values can be predicted more exactly and tailoring becomes possible. Different LTCC materials, based on the crystalline compounds Ba(La,Nd)2Ti4O12, ZrO2 (Y-TZP), SiO2 (quartz), and specially developed glasses, possessing an elevated CTE of around 10 × 10-6 K-1 while showing permittivity εr between 6 and 63, are introduced. KW - LTCC KW - Glass ceramic composites KW - Coefficient of thermal expansion CTE KW - Design PY - 2009 DO - https://doi.org/10.1111/j.1744-7402.2008.02316.x SN - 1546-542X SN - 1744-7402 VL - 6 IS - 1 SP - 1 EP - 8 PB - American Ceramic Soc. CY - Westerville, Ohio AN - OPUS4-18675 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rabe, Torsten A1 - Naghib Zadeh, Hamid A1 - Glitzky, Carsten A1 - Töpfer, J. T1 - Integration of Ni-Cu-Zn ferrite in low temperature Co-fired ceramics (LTCC) modules JF - International Journal of Applied Ceramic Technology N2 - Integration of magnetic functional components in LTCC circuit boards calls for co-firing of dielectric and ferrite tapes. Ni-Cu-Zn ferrites with permeability of µ = 900 were fully densified at the standard LTCC sintering temperature of 900°C. Co-firing of this ferrite with dielectric tapes requires the adaptation of the shrinkage behavior of the materials as well as the thermal contraction during the cooling period – especially in the temperature range below the transformation point of the glass phase of the dielectric tape. To match these preconditions, a new dielectric LTCC material with steep sintering curve and high thermal expansion coefficient was designed. Sintered multilayer laminates composed of Ni-Cu-Zn ferrite and tailored dielectric tapes are free of cracks and possess no open porosity. No significant interdiffusion between the ferrite and dielectric tapes was found using microprobe analysis. Pure ferrite laminates show homogeneous microstructure with large grains up to 50 µm in diameter. However, growth of ferrite grains does not take place near the interface between ferrite and release or dielectric tapes. There is a strong correlation between permeability and volume fraction of large ferrite grains. Compared to pure ferrite laminates the permeability of co-sintered Ni-Cu-Zn ferrite layers is drastically reduced to 400, that is a decrease of more than 50%. PY - 2012 DO - https://doi.org/10.1111/j.1744-7402.2011.00712.x SN - 1546-542X SN - 1744-7402 VL - 9 IS - 1 SP - 18 EP - 28 PB - American Ceramic Soc. CY - Westerville, Ohio AN - OPUS4-25544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Naghib Zadeh, Hamid A1 - Glitzky, Carsten A1 - Österle, Werner A1 - Rabe, Torsten T1 - Low temperature sintering of barium titanate based ceramics with high dielectric constant for LTCC applications JF - Journal of the European Ceramic Society N2 - The sintering temperature of BaTiO3 powder was reduced to 900 °C due to the ZnO-B2O3-Li2O-Nb2O5-Co2O3 addition. Excellent densification was achieved after sintering at 900 °C for 2 h. The low sintering temperature of newly developed capacitor materials allows a co-firing with pure silver electrodes. The dielectric constant and the temperature stability of the dielectric constant are strongly correlated with the composition of the ZnO-B2O3-Li2O additives. A high dielectric constant up to 3000 and a dielectric loss less than 0.024 were measured on multilayer capacitors sintered at 900 °C with silver inner electrodes. KW - BaTiO3 and titanates KW - Capacitors KW - Dielectric properties KW - LTCC PY - 2011 DO - https://doi.org/10.1016/j.jeurceramsoc.2010.10.003 SN - 0955-2219 SN - 1873-619X VL - 31 IS - 4 SP - 589 EP - 596 PB - Elsevier Ltd. CY - Oxford AN - OPUS4-22886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Naghib Zadeh, Hamid A1 - Glitzky, Carsten A1 - Dörfel, Ilona A1 - Rabe, Torsten T1 - Low temperature sintering of barium titanate ceramics assisted by addition of lithium fluoride-containing sintering additives JF - Journal of the European Ceramic Society N2 - By addition of LiF-containing sintering additives to commercial BaTiO3 powder, more than 98% of the theoretical density was reached at a sintering temperature of 900 °C both on powder compacts and laminates. Dielectric measurements were performed on ceramic samples in the temperature and frequency ranges from -20 °C to 125 °C and from 103 to 106 Hz, respectively. High relative permittivity (εr ~ 3160) and low dielectric loss (tan δ ~ 0.014) were measured for tapes of the favoured material. The breakdown strength for tapes with a thickness of about 80 µm is 30 kV/mm. The microprobe analysis showed, that no interfacial reaction between the dielectric layer and the Ag-electrode had occurred. The newly developed barium titanate ceramics completely densifying at 900 °C turned out to be promising for integration of buried capacitors in LTCC multilayers. KW - LTCC KW - BaTiO3 KW - LiF KW - Capacitors PY - 2010 DO - https://doi.org/10.1016/j.jeurceramsoc.2009.07.005 SN - 0955-2219 SN - 1873-619X VL - 30 IS - 1 SP - 81 EP - 86 PB - Elsevier CY - Oxford AN - OPUS4-20133 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -