TY - JOUR A1 - Malakhov, A. A1 - Epishin, A. A1 - Denisov, I. A1 - Saikov, I. A1 - Nolze, Gert T1 - Morphology and Structure of Brass–Invar Weld Interface after Explosive Welding JF - Materials N2 - This paper presents the results of a study of the morphology and structure at the weld interface in a brass–Invar bimetal, which belongs to the class of so-called thermostatic bimetals, or thermobimetals. The structure of the brass–Invar weld interface was analyzed using optical microscopy and scanning electron microscopy (SEM), with the use of energy-dispersive X-ray (EDX) spectrometry and back-scattered electron diffraction (BSE) to identify the phases. The distribution of the crystallographic orientation of the grains at the weld interface was obtained using an e-Flash HR electron back-scatter diffraction (EBSD) detector and a forward-scatter detector (FSD). The results of the study indicated that the weld interface had the wavy structure typical of explosive welding. The wave crests and troughs showed the presence of melted zones consisting of a disordered Cu–Zn–Fe–Ni solid solution and undissolved Invar particles. The pattern quality map showed that the structure of brass and Invar after explosive welding consisted of grains that were strongly elongated towards the area of the highest intensive plastic flow. In addition, numerous deformation twins, dislocation accumulations and shear bands were observed. Thus, based on the results of this study, the mechanism of Cu–Zn–Fe–Ni structure formation can be proposed. KW - Explosive welding KW - Thermobimetal KW - Grain structure KW - Brass KW - Invar PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-565964 DO - https://doi.org/10.3390/ma15238587 SN - 1996-1944 VL - 15 IS - 23 SP - 1 EP - 10 PB - MDPI AN - OPUS4-56596 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Epishin, A.I. A1 - Nolze, Gert A1 - Alymov, M.I. T1 - Pore Morphology in Single Crystals of a Nickel-Based Superalloy After Hot Isostatic Pressing JF - Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science N2 - The morphology of pores partially shrunk during a half-hour HIP at temperature of 1288 °C and pressure of 103 MPa has been investigated in nickel-based superalloy CMSX-4. The investigation resulted in the following findings: surrounding the shrinking pores by a c¢-shell (Ni3Al), faceting of the pores surface by {023} and {011} planes, and formation the submicroscopic satellite pores connected by channels with the neighboring larger pores. It is assumed that the formation of the c¢-shell around the pores and the faceting of the pore surface is due to diffusion processes occurring during pore shrinkage, and therefore these findings can be considered as arguments supporting the vacancy model of pore annihilation. The submicroscopic satellite pores are expected to be the result of dividing the casting pores of a complex initial shape during their shrinking. The connecting channels are probably required for the gas to escape from the rapidly shrinking small satellite pores into the slowly shrinking large pore. Thus, it is reasonable to assume that the casting pores may contain some amount of gas. KW - HIP KW - Superalloy KW - Porosity KW - Faceting KW - negative crystal growth PY - 2022 DO - https://doi.org/10.1007/s11661-022-06893-x SN - 1073-5623 SP - 1 EP - 9 PB - Springer Nature AN - OPUS4-56409 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Svetlov, I. L. A1 - Epishin, A. I. A1 - Petrushin, N. V. A1 - Gerstein, G. A1 - Nolze, Gert A1 - Maier, H. J. T1 - Creep of Directionally Solidified Eutectics Ni/Ni3 Al–NbC under Thermal Cycling JF - Inorganic Materials: Applied research N2 - A nickel-based eutectic alloy with a γ/γ'-NbC structure was directionally solidified with a planar front. The specimens were tested for creep under sawtooth thermal cycling in the temperature range from 600 to 1100°C. It has been established that the lifetime under the conditions of thermal cycling is about five times shorter than it is predicted by the linear damage accumulation rule on the basis of results of isothermal creep tests. Faster creep under thermal cycling is caused by the rapid coarsening of the γ/γ' microstructure due to the periodic partial dissolution and reprecipitation of the γ' phase in heating and cooling half-cycles. KW - High temperature nickel-based eutectic alloys KW - γ/γ' matrix KW - Carbide phase NbC KW - In-situ composites KW - Creep under thermal cycling PY - 2022 DO - https://doi.org/10.1134/S2075113322040347 SN - 2075-1133 VL - 13 IS - 4 SP - 1099 EP - 1108 PB - Springer Science + Business Media CY - Dordrecht AN - OPUS4-55163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Treninkov, I. A. A1 - Petrushin, N. V. A1 - Epishin, A. I. A1 - Svetlov, I. L. A1 - Nolze, Gert A1 - Elyutin, E. S. T1 - Experimental Determination of Temperature Dependence of Structural–Phase Parameters of Nickel-Based Superalloy JF - Inorganic Materials: Applied Research N2 - The temperature dependences of the periods of the crystal lattices of the γ and γ' phases, their dimensional mismatch (misfit), and volume fraction of the γ' phase of an experimental single-crystal hightemperature nickel-based alloy have been determined by X-ray diffraction analysis in the temperature range of 18–1150°C. The temperature ranges in which intense changes in the structural and phase characteristics of the alloy under study take place have been determined. KW - X-ray diffraction analysis KW - High temperatures KW - Nickel-based superalloys KW - Single crystal KW - Crystal lattice period PY - 2022 DO - https://doi.org/10.1134/s2075113322010373 SN - 2075-1133 VL - 13 IS - 1 SP - 171 EP - 178 PB - Springer Science + Business Media CY - Dordrecht AN - OPUS4-54466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Epishin, A. I. A1 - Petrushin, N. V. A1 - Svetlov, I. L. A1 - Nolze, Gert T1 - Model for Forecasting Temperature Dependence of γ/γ' Misfit in Heat-Resistant Nickel Alloys JF - Inorganic Materials: Applied Research N2 - An analytical model for forecasting the temperature dependence of γ/γ' misfit in heat-resistant nickel alloys is proposed. The model accounts for the concentration dependences of the periods of crystalline lattices of the γ and γ' phases (Vegard law), thermal expansion of the γ and γ' lattices, and dissolution of the γ' phase at high temperatures. Adequacy of calculations of misfit is confirmed by comparison with the results of measurements using methods of X-ray and neutron diffraction. The model is applied for development of a nickel alloy with positive misfit. KW - Heat-resistant nickel alloys KW - Dimensional mismatch of crystalline lattice periods (misfit) KW - Microstructure evolution PY - 2022 DO - https://doi.org/10.1134/S2075113322010105 SN - 2075-1133 VL - 13 IS - 1 SP - 7 EP - 16 PB - Springer AN - OPUS4-54379 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schneider, J. A1 - Farris, L. A1 - Nolze, Gert A1 - Reinsch, Stefan A1 - Cios, G. A1 - Tokarski, T. A1 - Thompson, S. T1 - Microstructure evolution in Inconel 718 produced by powder bed fusion additive manufacturing JF - Journal of manufacturing and materials processing N2 - Inconel 718 is a precipitation strengthened, nickel-based super alloy of interest for the Additive Manufacturing (AM) of low volume, complex parts to reduce production time and cost compared to conventional subtractive processes. The AM process involves repeated rapid melting, solidification and reheating, which exposes the material to non-equilibrium conditions that affect elemental segregation and the subsequent formation of solidification phases, either beneficial or detrimental. These variations are difficult to characterize due to the small length scale within the micron sized melt pool. To understand how the non-equilibrium conditions affect the initial solidification phases and their critical temperatures, a multi-length scale, multi modal approach has been taken to evaluate various methods for identifying the initial phases formed in the as-built Inconel 718 produced by laser-powder bed fusion (L-PBF) additive manufacturing (AM). Using a range of characterization tools from the bulk differential thermal analysis (DTA) and x-ray diffraction (XRD) to spatially resolved images using a variety of electron microscopy tools, a better understanding is obtained of how these minor phases can be properly identified regarding the amount and size, morphology and distribution. Using the most promising characterization techniques for investigation of the as-built specimens, those techniques were used to evaluate the specimens after various heat treatments. During the sequence of heat treatments, the initial as-built dendritic structures recrystallized into well-defined grains whose size was dependent on the temperature. Although the resulting strength was similar in all heat treated specimens, the elongation increased as the grain size was refined due to differences in the precipitated phase distribution and morphology. KW - Metal additive manufacturing KW - Inconel 718 KW - Heat treatment KW - Grain boundary precipitates KW - Laves phase PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542758 DO - https://doi.org/10.3390/jmmp6010020 SN - 2504-4494 VL - 6 IS - 1 SP - 1 EP - 20 PB - MDPI CY - Basel AN - OPUS4-54275 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -