TY - JOUR A1 - Neubert, S. A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Strain-rate controlled Gleeble experiments to determine the stress-strain behavior of HSLA steel S960QL N2 - In order to generate a material data base for computational welding mechanics, temperature and strain-rate dependent stress-strain experiments were performed by using a Gleeble®3500 testing system. The object of the investigation was HSLA transformable steel S960QL and related solid phases as bainite, martensite and austenite. For the production of these solid phases, the base material was heat treated according to an average weld temperature cycle which was extracted within the heat affected zone of a thermal numerical weld simulation of a GMA weld. The hot tensile tests were carried out via cost-saving flat specimen geometries. Two experimental series with different strain-rates were conducted, where the longitudinal strain-rate was controlled by specification of the transversal strain-rate applying Poisson’s-ratio. Subsequently, the resulting stress-strain curves were approximated in accordance with the Ramberg-Osgood-materials law. Consequently, it is shown that the temperature and strain-rate dependent stress-strain behavior of metals can be successfully characterized by means of a Gleeble®-system. However, this requires a control of the longitudinal strain-rate by specification of the transversal strain-rate. The related experimental procedure and the method of evaluation are explained in detail. With regard to all tested solid phases, a significant strain-rate dependency can only be observed upwards from temperatures of 400 °C. Based on experimental results, Ramberg-Osgood-parameters will be presented to describe the stress-strain behavior of steel S960QL and related solid phases for temperatures between 25 °C and 1200 °C. Furthermore, the use of costsaving flat specimen-geometry appears reasonable. N2 - Für die Generierung einer Materialdatenbank zur Schweißstruktursimulation wurden temperatur- und dehnratenabhängige Spannungs-Dehnungsexperimente unter Einsatz einer Gleeble® 3500-Anlage durchgeführt. Als Untersuchungsgegenstand diente der hochfeste niedriglegierte Feinkornbaustahl S960QL und seine zugehörigen Festphasen Bainit, Martensit und Austenit. Zur Herstellung dieser Festphasen wurde der Grundwerkstoff Wärmebehandlungen ausgesetzt, welche die charakteristischen Merkmale eines durchschnittlichen Schweißzeittemperaturzyklus aufweisen. Dieser Temperaturzyklus wurde aus der Wärmeeinflusszone eines numerisch nachgebildeten Temperaturfeldes einer MAG-Schweißverbindung extrahiert. Die Zugversuche wurden an einer kostengünstig herzustellenden Flachprobengeometrie durchgeführt, wobei zwei Experimentalreihen mit jeweils unterschiedlichen Dehnraten realisiert wurden. Die resultierenden Spannungs-Dehnungskurven wurden durch die Ramberg-Osgood-Beziehung approximiert. Es konnte gezeigt werden, dass das temperatur- und dehnratenabhängige Spannungs-Dehnungsverhalten von Metallen durch die Anwendung eines Gleeble®-Systems erfolgreich charakterisiert werden kann. Die Einstellung der Längsdehnrate muss dabei durch die Kontrolle der Querdehnrate unter Berücksichtigung des Poisson-Verhältnisses erfolgen. Die experimentellen Prozeduren und die zugehörigen Auswertemethodiken wurden detailliert erläutert. Für alle getesteten Festphasen wurde ein signifikanter Dehnrateneinfluss erst für Temperaturen ab 400 °C aufwärts beobachtet. Die anhand der Messergebnisse abgeleiteten Ramberg-Osgood-Parameter zur Beschreibung des Verfestigungsverhaltens für den Temperaturbereich zwischen 25 °C und 1200 °C werden vollständig präsentiert. KW - Stress-strain behavior KW - Gleeble testing KW - HSLA KW - Strain-rate KW - Numerical welding simulation KW - Transformable steels PY - 2018 U6 - https://doi.org/10.3139/120.111208 SN - 0025-5300 VL - 60 IS - 7-8 SP - 733 EP - 748 PB - Carl Hanser CY - München AN - OPUS4-45791 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neubert, S. A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Numerical Sensitivity Analysis of TRIP-Parameter K on Weld Residual Stresses and Weld Distortion N2 - A combined experimental numerical approach is applied for a sensitivity analysis of the transformation induced plasticity (TRIP)-parameter K on welding residual stresses and welding distortion for the welding of the low-alloyed high-strength S960QOL with the high-alloyed hig-strength filler material CN13-4-IG. A thermo-mechanical FE model of a real GMA welding process was experimentally validated against termperature field, X-Ray stress measurments and optical distortion measurement. Within the sensititvity analysis K was varied and the influence on the calculated welding residual stresses and welding distortion is evaluated by performing corresponding FEA. The correct order of K magnitude is necessary in order to reproduce the residual stresses qualitatively and quantitatively. For the sufficient reproducing of the welding distortion the transformation induced plasticity can be neglected. T2 - 11th International Seminar - Numerical Analysis of Weldability CY - Graz, Austria DA - 27.09.2015 KW - TRIP PY - 2016 SN - 978-3-85125-490-7 SN - 2410-0544 SP - 361 EP - 383 PB - Verlag der Technischen Universität Graz CY - Graz AN - OPUS4-38904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neubert, S. A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Experimentelle Bestimmung der umwandlungsplastischen Konstante K und deren Einfluss auf Schweißeigenspannungen N2 - Die in dieser Studie vorgestellte einfache Probengeometrie zeigt sich in Verbindung mit der angewandten Versuchs- und Auswertemethodik geeignet, um den umwandlungsplastischen (TRIP)-Parameter K unter Verwendung des thermomechanischen Simulators Gleeble® 3500 experimentell zu bestimmen. Der TRIP-Parameter K wurde für die Grundwerkstoffe S355J2+N und S960QL, sowie für den hochlegierten Zusatzwerkstoff CN13-4 -IG bestimmt. Die numerische Einflussanalyse zeigt, dass bei der Berechnung von (Oberflächen-)Schweiß­eigen-spannungen die Vernachlässigung des TRIP-Effektes kaum einen Einfluss auf die Längseigenspannungen hat. Im Gegensatz da­ zu resultieren gegenüber dem Referenzfall sig­nifikante Abweichungen der Quereigenspannungen im und um den Schweißnahtbereich. Die Verdopplung des TRIP-Parameters K ge­genüber dem Referenzfall hat nur einen ver­nachlässigbaren Einfluss auf die Längs- sowie Quereigenspannungen auf der Oberfläche. Für eine qualitative und quantitative numerische Nachbildung der experimentell bestimmten Längs- und Quereigenspannungen ist die Be­rücksichtigung der Größenordnung des materi­al-abhängigen TRIP-Parameters K notwendig. T2 - 35. Assistentenseminar Füge- und Schweißtechnik CY - Institut für Werkstoff- und Fügetechnik der Otto-von­ Guericke-Universität Magdeburg DA - 01.12.2014 KW - Umwandlungsplastischen Konstante K KW - Einfluss auf Schweißeigenspannungen PY - 2016 SN - 978-3-945023-55-6 VL - 2016/314 SP - 15 EP - 21 PB - DVS Media Düsseldorf CY - Düsseldorf AN - OPUS4-38057 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neubert, S. A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Influence of non-uniform martensitic transformation on residual stresses and distortion of GMA-welding N2 - A combined experimental and numerical approach is applied for a numerical analysis of the non-uniform martensitic transformation kinetic on welding residual stresses and distortion of a single pass weld. The (γ → α)-transformation kinetic within the weld pool region is governed by a non-uniform distribution of the elements chromium and nickel. The single-pass weld was performed by use of the low-alloyed high-strength steel S960QL with the high-alloyed high-strength filler wire CN 13/4-IG®. A thermo-mechanical FE model of the welding process was experimentally validated against temperature field, solid phase distribution, transformation behaviour, X-Ray stress measurements and transient optical distortion measurements. The experimentally determined and calculated weld residual stresses and transient distortion are in good agreement. It can be shown that the change on the (γ → α)-transformation kinetic driven by the inhomogeneous distribution of the chemical contents causes a strong influence on the weld residual stresses within the volume of the weld pool, which could promote crack propagation within the solidified weld pool by use of high-alloyed filler materials. Furthermore, a significant influence on the development of the transient welding distortion is visible. This influence should be respected during numerically calculation of welding distortion in case of multi-pass welding using interpass temperatures and high-alloyed filler materials. KW - Welding residual stresses KW - FEA KW - Welding simulation KW - Dissimilar welding KW - Transformable steels PY - 2017 U6 - https://doi.org/10.1016/j.jcsr.2016.08.020 SN - 0143-974X SN - 1873-5983 VL - 128 SP - 193 EP - 200 PB - Elsevier Ltd. AN - OPUS4-37276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -