TY - THES A1 - Artinov, Antoni T1 - On the mathematical analysis of the relationship between the bulging region and the centerline solidification cracking in laser beam welding N2 - The present Ph.D. thesis provides a comprehensive experimental and theoretical study of the bulging-cracking relationship in laser beam welding of thick unalloyed steel sheets. It focuses on experimentally proving the existence of the bulging region and on developing a coupled multiphysics mathematical framework to analyze its influence on the three critical factors controlling the susceptibility to solidification cracking, namely the thermal, metallurgical, and mechanical factors. The research employs a novel experimental setup, utilizing a combination of transparent quartz glass and thick unalloyed steel sheet, enabling real-time visualization of the weld pool geometry and confirming the existence of a distinctive bulging region. To deepen the understanding of these experimental insights, an extensive multiphysics mathematical framework was developed and rigorously verified and validated. This framework introduces an innovative approach using Lamé curves for accurately describing complex three-dimensional weld pool geometries, including the bulging region's characteristics. Through analytical solutions and numerical procedures, it facilitates the computation of solidification parameters, which are crucial for understanding the metallurgical aspects of crack formation. The framework also incorporates a mechanical model to assess and evaluate the local stress distribution within the bulging region. The findings indicate that an elongated, sharply shaped bulging region significantly increases the susceptibility to solidification cracking. This is attributed to its adverse impact on the distribution and local dwell time of liquid metal residing at grain boundaries during solidification, combined with the localized tensile stresses identified in the bulging region. In essence, this research contributes to the broader understanding of solidification cracking in laser beam welding of thick unalloyed steel sheets, with a particular focus on the bulging region. The insights and methodologies developed in this thesis are valuable for future research and advancements in the application of the laser beam welding technology for joining high-thickness unalloyed steel components. KW - Bulging effect KW - Centerline solidification cracking KW - Mathematical modeling KW - Structural steel KW - High power laser beam welding PY - 2024 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-599010 SP - 1 EP - 152 CY - Berlin AN - OPUS4-59901 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Ávila Calderón, Luis Alexander T1 - Mechanisches Verhalten von additiv gefertigtem nichtrostendem Stahl X2CrNiMo17-12-2 (AISI 316L) und Vergleich zur konventionell gefertigten Variante T1 - Mechanical behavior of additively manufactured stainless steel X2CrNiMo17-12-2 (AISI 316L) and comparison with a conventionally manufactured variant N2 - Die additive Fertigung (AM) metallischer Werkstoffe ist eine Technologie, die zunehmend Gegenstand von Forschungsaktivitäten und industrieller Anwendung ist. Dennoch steht sie noch vor Herausforderungen, um eine breite Nutzung in sicherheitsrelevanten Anwendungen zu erreichen. Die Hauptgründe für die Verzögerung des technologischen Durchbruchs zugunsten von AM-Metallen gegenüber konventionell hergestellten Varianten sind das Fehlen eines tieferen Verständnisses der Prozess-Struktur-Eigenschafts-Beziehungen und die begrenzte Verfügbarkeit von Daten zu den Materialeigenschaften. In diesem Kontext stellt diese Arbeit einen Beitrag sowohl zum Verständnis der Prozess-Struktur-Eigenschafts-Beziehungen als auch zur Verbesserung der Datenlage von 316L dar, einem häufig als Konstruktionswerkstoff in verschiedenen Hochtemperaturbauteilen verwendeten Werkstoff. Die Arbeit legt den Fokus auf die mittels Laser-Pulverbettschmelzen hergestellte Werkstoffvariante, PBF-LB/M/316L. Eine konventionell hergestellte Variante, HR/316L, wurde auch untersucht. Bei PBF-LB/M/316L wurde zusätzlich der Effekt ausgewählter Wärmebehandlungen ausgewertet. Die Untersuchung umfasste die Charakterisierung der mechanischen Eigenschaften und der Verformungs- und Schädigungsmechanismen bei erhöhten Prüftemperaturen bei LCF und Kriechen, wo die Daten und Wissenslage am spärlichsten ist. Außerdem hat die untersuchte PBF-LB/M/316L-Wersktoffvariante einen geringen Porositätsgrad. Somit hat diese Arbeit die Mikrostruktur stärker in den Fokus genommen als die meisten bisher in der Literatur verfügbaren Studien. Die mechanische Prüfkampagne umfasste Zugversuche zwischen Raumtemperatur und 650 °C, LCF-Versuche zwischen Raumtemperatur und 600 °C sowie Kriechversuche bei 600 °C und 650 °C. In Ermangelung konkreter Richtlinien und Normen wurde die Charakterisierung zumeist anhand der bestehenden internationalen Prüfnormen und Probengeometrien durchgeführt. Aus jedem dieser Prüfverfahren wurden die entsprechenden Festigkeits- und Verformungskennwerte ermittelt. Darüber hinaus wurde mit Hilfe gezielter mikrostruktureller Untersuchungen ein Beitrag zum Verständnis des Zusammenhangs zwischen der Mikrostruktur und den mechanischen Eigenschaften in Bezug auf die Verformungs- und Schädigungsmechanismen geleistet. Die Dehngrenze von PBF-LB/M/316L ist etwa doppelt so hoch wie die von HR/316L und dieser Trend setzt sich mit ansteigender Prüftemperatur fort. Die Bruchdehnung ist bei allen Prüftemperaturen geringer. PBF-LB/M/316L weist über den größten Teil der Ermüdungslebensdauer vor allem bei Raumtemperatur höhere zyklische Spannungen als HR/316L auf. Ausschließlich bei den kleinsten Dehnungs-schwingbreiten sind die Ermüdungslebensdauer ausgeprägt kürzer. Das Wechselverformungsverhalten von PBF-LB/M/316L ist durch eine Anfangsverfestigung gefolgt von einer kontinuierlichen Entfestigung charakterisiert, welche bis zum Auftreten der zum Versagen führenden Entfestigung stattfindet. Die Kriechbruchzeiten und die Dauer jeder Kriechphase sind bei allen Kombinationen von Prüfparametern bei PBF-LB/M/316 kürzer als bei HR/316L. Die Spannungsabhängigkeit von PBF-LB/M/316L ist im Vergleich zu HR/316L geringer und die Duktilität beim Kriechen kleiner. Die minimale Kriechrate wird bei allen geprüften Parameterkombinationen bei deutlich geringeren Kriechdehnungen erreicht. Eine Wärmebehandlung bei 450 °C / 4 h bewirkt keine wesentliche Änderungen der Mikrostruktur und Zugversuchseigenschaften. Eine zusätzliche Wärmebehandlung bei 900 °C / 1 h verursacht eine Abnahme der Dehngrenze des PBF-LB/M/316L. Diese blieb aber immer noch um den Faktor 1,5x höher als bei HR/316L. Die Verformungsmerkmale wurden kaum davon beeinflusst. Bezüglich des Kriechverhaltens hat die Wärmebehandlung bei 900 °C / 1 h längere sekundäre und tertiäre Kriechstadien bewirkt und die Kriechdehnung hat sich signifikant erhöht. Die Bruchbilder unterscheiden sich generell nicht nur aber vor allem mit ansteigender Prüftemperatur, bei der bei PBF-LB/M/316L oft interkristalline Rissbildung beobachtet wurde. Die Zellstruktur trägt als der Hauptfaktor zu den unterschiedlichen mechanischen Eigenschaften im Vergleich zur HR/316L-Variante bei. Darüber hinaus spielen mutmaßlich die Kornmorphologie, die Stapelfehlerenergie und der Stickstoffgehalt eine Rolle. N2 - Metal additive manufacturing (AM) is a technology that is increasingly the subject of research activities and industrial applications. However, it still faces challenges to achieve widespread use in safety-relevant applications. The main reasons for the delay of this technological breakthrough in favor of AM metals over conventionally manufactured variants are the lack of a deeper understanding of process-structure-property relationships and the limited availability of data on material properties. In this context, this work contributes to both achieving a better understanding of process-structure-property relationships and the improvement of data for 316L, an alloy frequently used as a structural material in various high-temperature components. The work focuses on a material variant produced by laser pow-der bed fusion, PBF-LB/M/316L. A conventionally produced variant, HR/316L, was also investigated. For PBF-LB/M/316L, the effect of selected heat treatments was also evaluated. The investigation included the characterization of the mechanical properties and the related deformation and damage mechanisms at elevated test temperatures in LCF and creep, where data and knowledge are scarce. The PBF-LB/M/316L variant studied has a low degree of porosity. Thus, this work is more focused on the microstructure than most studies available in the literature. The mechanical test campaign included tensile tests between room temperature and 650 °C, LCF tests between room temperature and 600 °C, and creep tests at 600 °C and 650 °C. In the absence of concrete guidelines and standards for testing of AM metals, the characterization mostly took place using existing international test standards and specimen geometries. From each of the test methods, corresponding strength, and deformation characteristic values were determined. In addition, targeted microstructural investigations contributed to understanding the relationship between the microstructure and the mechanical properties in terms of deformation and damage mechanisms. The proof stress of PBF-LB/M/316L is about twice that of HR/316L. This trend remains with increasing test temperature. The elongation after fracture is lower at all test temperatures. Regarding LCF, PBF-LB/M/316L exhibits higher cyclic stresses than HR/316L for most of the fatigue life, especially at room temperature. Exclusively at the smallest strain amplitudes, the fatigue lives of PBF-LB/M/316L are markedly shorter than in HR/316L. The cyclic stress-strain deformation behavior of PBF-LB/M/316L features an initial strain hardening followed by a continuous softening, which occurs until the softening leading to failure takes place. The creep rupture times and the duration of each creep stage are shorter for PBF-LB/M/316 than for HR/316L for all combinations of test parameters. The stress dependence of PBF-LB/M/316L is lower, and the creep ductility is smaller compared to HR/316L. The minimum creep rate is reached at significantly lower creep extensions for all parameter combinations tested. A heat treatment at 450 °C / 4 h did not cause significant changes in the microstructure and tensile behavior. An additional heat treatment at 900 °C / 1 h caused a decrease in the proof stress of PBF-LB/M/316L. However, it still remained higher than the one of HR/316L by a factor of 1.5x. The deformation characteristics were hardly affected. Regarding the creep behavior, this latter heat treatment at 900 °C / 1 h caused longer secondary and tertiary creep stages, and the creep strain increased significantly. The fracture characteristics generally differed, which happened not only but especially with increasing test temperature, where intergranular cracking often took place in PBF-LB/M/316L. The cellular structure is considered the main factor contributing to the different mechanical properties compared to the HR/316L variant. In addition, grain morphology, stacking fault energy, and nitrogen content might play a role. KW - AGIL KW - Additive Fertigung KW - Laser-Pulverbettschmelzen KW - Mikrostrukturentwicklung KW - 316L KW - LCF KW - Kriechen KW - Additive Manufacturing KW - Microstructure KW - Mechanical Properties KW - Mechanische Eigenschaften PY - 2024 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-597143 SP - 1 EP - 190 CY - Berlin AN - OPUS4-59714 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Charmi, Amir T1 - A multiscale numerical framework for the simulation of anistropic material response of additively manufactured stainless steel 316L undergoing large plastic deformation N2 - Additive manufacturing (AM) offers significantly greater freedom of design compared to conventional manufacturing processes since the final parts are built layer by layer. This enables metal AM, also known as metal 3D printing, to be utilized for improving efficiency and functionality, for the production of parts with very complex geometries, and rapid prototyping. However, despite many technological advancements made in recent years, several challenges hinder the mass adoption of metal AM. One of these challenges is mechanical anisotropy which describes the dependency of material properties on the material orientation. Therefore, in this work, stainless steel 316L parts produced by laser-based powder bed fusion are used to isolate and understand the root cause of anisotropy in AM parts. Furthermore, an efficient and accurate multiscale numerical framework is presented for predicting the deformation behavior of actual AM parts on the macroscale undergoing large plastic deformations. Finally, a novel constitutive model for the plastic spin is formulated to capture the influence of the microstructure evolution on the material behavior on the macroscale. KW - Additive Fertigung KW - Austenitischer Stahl KW - Finite-Elemente-Methode KW - Mehrskalenmodell KW - Simulation PY - 2024 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20240207-173356-002 SP - 1 EP - 163 PB - Bauhaus-Universität Weimar CY - Weimar AN - OPUS4-59511 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Ecke, Alexander T1 - Integrated Diagnostics of Pharmaceutical Contaminants in Water Supply and Management Systems N2 - The contamination of drinking water with pharmaceuticals represents a severe health risk. In order to monitor the drinking water quality continuously and enable quick countermeasures in case of contamination, novel sensors are required. Here, immunoanalytical methods based on the binding of the analyte to highly selective antibodies can be helpful. In this work, magnetic bead-based immunoassays (MBBAs) have been developed for the detection of two relevant contaminants of drinking water: diclofenac (DCF) and amoxicillin (AMX). In case of the latter, not only the parent drug is of interest in the risk assessment but also its hydrolysis products (HPs). In a comprehensive study, the influence of external factors and intrinsic properties of the water on the rate of hydrolysis was investigated. As the hydrolysis of AMX further impacts the recognition by the antibody, a strategy to analyze samples with unknown hydrolysis degree of AMX was established employing the enzyme β-lactamase in sample preparation. For both analytes, the MBBAs enable the fast quantification with results obtained in less than one hour which represents a major improvement over conventional immunoassays like the enzyme-linked immunosorbent assay (ELISA). Compared to the respective ELISAs with the same antibodies, the MBBAs further exhibit improved analytical parameters such as a broader measurement range and lower limits of detection. Due to the magnetic properties of the beads that serve as a platform for the assays, they are suitable for the mobile and automated detection at the point-of-care. An integrated diagnostic system was designed in which electrochemical detection with chronoamperometry on a microfluidic chip allows for further miniaturization of the system to enable monitoring of the drinking water quality online in water supply pipes at waterworks. N2 - Die Kontamination von Trinkwasser mit Arzneimitteln stellt eine ernste Gesundheitsgefahr dar. Um die Trinkwasserqualität kontinuierlich überwachen und im Falle einer Verunreinigung zeitnah reagieren zu können, sind neuartige Sensoren erforderlich. Hier können immunanalytische Methoden, die auf der Bindung des Analyten an hochselektive Antikörper beruhen, hilfreich sein. In dieser Arbeit wurden magnetpartikelbasierte Immunoassays (MBBAs) für zwei relevante Kontaminanten des Trinkwassers entwickelt: Diclofenac (DCF) und Amoxicillin (AMX). Bei letzterem erwiesen sich neben der Ausgangsverbindung auch dessen Hydrolyseprodukte (HPs) als relevant für die Gefährdungsbeurteilung. In einer umfassenden Studie wurde der Einfluss von externen Faktoren und intrinsischen Eigenschaften des Wassers auf die Hydrolysegeschwindigkeit untersucht. Da die Hydrolyse von AMX auch die Erkennung durch den Antikörper beeinflusst, wurde eine Strategie zur Analyse von Proben mit unbekanntem Hydrolysegrad von AMX unter Verwendung des Enzyms β-Lactamase in der Probenvorbereitung entwickelt. Für beide Analyten ermöglichen die MBBAs eine schnelle Quantifizierung mit Ergebnissen in weniger als einer Stunde, was eine wesentliche Verbesserung gegenüber herkömmlichen Immunoassays wie dem Enzyme-linked Immunosorbent Assay (ELISA) darstellt. Im Vergleich zu den entsprechenden ELISAs mit denselben Antikörpern weisen die MBBAs zudem verbesserte analytische Parameter auf, wie einen breiteren Messbereich und niedrigere Nachweisgrenzen. Aufgrund der magnetischen Eigenschaften der Partikel, die als Plattform für die Assays dienen, eignen sie sich für den mobilen und automatisierten Einsatz vor Ort. Ein integriertes Diagnosesystem, bei dem die elektrochemische Detektion mittels Chronoamperometrie auf einem mikrofluidischen Chip eine weitere Miniaturisierung des Systems ermöglicht, wurde entworfen, um die Überwachung der Trinkwasserqualität online in Wasserwerken zu ermöglichen. KW - Antibiotics KW - Immunoassay KW - Amoxicillin KW - Diclofenac KW - Biosensor KW - Antibodies PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-591901 SP - 1 EP - 129 CY - Berlin AN - OPUS4-59190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Riedel, Soraya T1 - Development of electrochemical antibody-based and enzymatic assays for mycotoxin analysis in food N2 - Electrochemical methods are promising to meet the demand for easy-to-use devices monitoring key parameters in the food industry. Many companies run own lab procedures for mycotoxin analysis, but it is a major goal to simplify the analysis. The enzyme-linked immunosorbent assay using horseradish peroxidase as enzymatic label, together with 3,3',5,5' tetramethylbenzidine (TMB)/H2O2 as substrates allows sensitive mycotoxin detection with optical detection methods. For the miniaturization of the detection step, an electrochemical system for mycotoxin analysis was developed. To this end, the electrochemical detection of TMB was studied by cyclic voltammetry on different screen-printed electrodes (carbon and gold) and at different pH values (pH 1 and pH 4). A stable electrode reaction, which is the basis for the further construction of the electrochemical detection system, could be achieved at pH 1 on gold electrodes. An amperometric detection method for oxidized TMB, using a custom-made flow cell for screen-printed electrodes, was established and applied for a competitive magnetic bead-based immunoassay for the mycotoxin ochratoxin A. A limit of detection of 150 pM (60 ng/L) could be obtained and the results were verified with optical detection. The applicability of the magnetic bead-based immunoassay was tested in spiked beer using a handheld potentiostat connected via Bluetooth to a smartphone for amperometric detection allowing to quantify ochratoxin A down to 1.2 nM (0.5 µg/L). Based on the developed electrochemical detection system for TMB, the applicability of the approach was demonstrated with a magnetic bead-based immunoassay for the ergot alkaloid, ergometrine. Under optimized assay conditions a limit of detection of 3 nM (1 µg/L) was achieved and in spiked rye flour samples ergometrine levels in a range from 25 to 250 µg/kg could be quantified. All results were verified with optical detection. The developed electrochemical detection method for TMB gives great promise for the detection of TMB in many other HRP-based assays. A new sensing approach, based on an enzymatic electrochemical detection system for the mycotoxin fumonisin B1 was established using an Aspergillus niger fumonisin amine oxidase (AnFAO). AnFAO was produced recombinantly in E. coli as maltose-binding protein fusion protein and catalyzes the oxidative deamination of fumonisins, producing hydrogen peroxide. It was found that AnFAO has a high storage and temperature stability. The enzyme was coupled covalently to magnetic particles, and the enzymatically produced H2O2 in the reaction with fumonisin B1 was detected amperometrically in a flow injection system using Prussian blue/carbon electrodes and the custom-made wall-jet flow cell. Fumonisin B1 could be quantified down to 1.5 µM (≈ 1 mg/L). The developed system represents a new approach to detect mycotoxins using enzymes and electrochemical methods. N2 - Zur Entwicklung von einfach zu bedienenden Vor-Ort-Geräten, welche für die Analytik von wichtigen Parametern in der Lebensmittelindustrie eingesetzt werden können, sind elektrochemische Methoden besonders vielversprechend. Viele Unternehmen führen bereits Mykotoxinanalytik in eigenen Laboren am Produktionsstandort durch, dennoch gibt es große Bestrebungen Analysenmethoden weiter zu vereinfachen. Der Enzyme-linked Immunosorbent Assay (ELISA), welcher häufig mit der Meerrettichperoxidase als enzymatischem Label und 3,3',5,5'-Tetramethylbenzidine (TMB)/H2O2 als Enzymsubstraten arbeitet, ermöglicht den sensitiven Mykotoxinnachweis mithilfe optischer Detektionsmethoden. Zur Miniaturisierung des Detektionsschrittes wurde in dieser Arbeit der Aufbau von elektrochemischen Detektionssystemen für die Mykotoxinanalytik untersucht. Dazu wurde zunächst die elektrochemische Reaktion von TMB an verschiedenen Materialien siebgedruckter Elektroden (Kohlenstoff und Gold) sowie bei verschiedenen pH-Werten (pH 1 und pH 4) untersucht. Eine stabile Elektrodenreaktion, welche die Grundlage für den weiteren Aufbau des elektrochemischen Detektionssystems darstellt, konnte bei pH 1 an Goldelektroden erzielt werden. Basierend darauf wurde eine amperometrische Detektionsmethode für oxidiertes TMB entwickelt, wofür eine maßgefertigte Durchflusszelle verwendet wurde. Die amperometrische TMB-Detektion wurde für einen kompetitiven Magnetpartikel-basierten Immunoassay für Ochratoxin A eingesetzt. Mit diesem Assay wurde eine Nachweisgrenze von 150 pM (60 ng L-1) erreicht und die Ergebnisse konnten durch optische Detektion verifiziert werden. Die Anwendbarkeit des Assays konnte in Ochratoxin A dotiertem Bier demonstriert werden, wobei für die Detektion ein tragbarer Potentiostat verwendet wurde, welcher über Bluetooth mit einem Smartphone verbunden war. Hiermit konnten niedrige Ochratoxin A Konzentration von bis zu 1.2 nM (0.5 µg L-1) bestimmt werden. Aufbauend auf dem entwickelten elektrochemischen Detektionssystem für TMB wurde die Anwendbarkeit des Ansatzes auf einen Magnetpartikel-basierten Immunoassay für das Ergotalkaloid Ergometrine, evaluiert. Unter optimierten Bedingungen konnte mit dem Assay eine Nachweisgrenze von 3 nM (1 µg L-1) erreicht werden. In mit Ergometrin versetztem Roggenmehl konnten Konzentrationen von 25 bis 250 µg kg-1 nachgewiesen werden. Die entwickelte elektrochemische Nachweismethode für TMB bietet einen vielversprechenden Ansatz für den Einsatz in vielen anderen Meerrettichperoxidase-basierten Assays. Für das Mykotoxin Fumonisin B1, wurde ein neues sensorisches System entwickelt, welches auf einem enzymatischen elektrochemischen Nachweis basiert. Hierfür wurde eine Aspergillus niger Fumonisin Aminoxidase (AnFAO) rekombinant als Fusionsprotein mit dem Maltose-bindenden Protein exprimiert. AnFAO katalysiert die oxidative Deaminierung von Fumonisinen, wobei H2O2 gebildet wird. Es konnte gezeigt werden, dass AnFAO eine hohe Lagerungs- und Temperaturstabilität hat. Für den Nachweis von Fumonisin B1 wurde das Enzym kovalent an Magnetpartikel gekoppelt. Das enzymatisch produzierte H2O2 konnte anschließend amperometrisch mithilfe von Preußisch Blau/Kohlenstoff-Elektroden in der maßgefertigten Durchflusszelle detektiert werden. Fumonisin B1 konnte bis zu einer Konzentration von 1,5 µM (≈ 1 mg L-1) quantifiziert werden. Das entwickelte System stellt einen neuen Ansatz dar, um Mykotoxine unter Nutzung von Enzymen und elektrochemischen Methoden zu detektieren. KW - Mycotoxins KW - Biosensor KW - Antibodies KW - Electrochemical detection PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:517-opus4-607477 SP - 1 EP - 96 PB - Universität Potsdam CY - Potsdam AN - OPUS4-59189 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Kazlagic, Anera T1 - Provenancing of cement by the means of isotope techniques N2 - Concrete is the most important human-made material because it serves as the basis of our built environment. Since the properties of concretes are dominated by their key compound, cement, devising a way to determine the cement’s origin, known as provenancing, is of great importance for answering different provenance-related questions. These questions range from liability issues when damage occurs to concrete-made structures, to forensic investigations where cement particles are found at crime scenes. This thesis showcases the use of isotope techniques to answer these provenance-related questions. Conventional 87Sr/86Sr and 143Nd/144Nd isotope and elemental ratios consisting of Ca, Sr, K, Mn, Mg, and Ti are used as fingerprints for ordinary Portland cement (OPC) provenancing. The first part of this thesis describes research previously conducted in fingerprinting cementitious materials, providing an overview of provenance studies of cement and the main approaches commonly used. In several studies, the origin of clinker for certain locations was determined via different approaches. However, clinker is an intermediate product, which is available only at the production site and therefore, the practical relevance is rather limited. Furthermore, the use of Sr and Nd isotope systems, together with elemental fingerprints are presented as state of the art in the field. Therein, the principal approach for the overall study is sketched. For the second part of the study, a sample preparation technique for Sr isotopes in Portland cement was developed. The aim was to find the most appropriate sample preparation procedure for cement provenancing and selection was realised by comparing the 87Sr/86Sr isotope ratios of differently treated OPCs with those of the corresponding clinkers. Based on these findings, the third part of the study focused on the measurements of Sr and Nd isotope ratios, together with elemental ratios, to establish a reliable technique for OPC provenancing. The outcomes of this final stage are then used to establish a procedure for fingerprinting cements. This becomes possible with the use of Sr and Nd isotope ratios and geochemical profiles. To perform isotope ratio measurements and obtain reliable data, it was necessary to establish a quality control procedure. Thus, an interlaboratory comparison (ILC) was organised to characterise 87Sr/86Sr isotope ratios in geological and industrial reference materials by applying the conventional method for 87Sr/86Sr isotope ratios. As reference material, four cements (VDZ 100a, VDZ 200a, VDZ 300a, IAG OPC-1), one limestone (IAG/CGL ML-3) and one slate (IAG OU-6) were selected, thus covering a wide range of Sr isotope signatures. KW - Isotope ratio KW - Strontium KW - Neodymium KW - Ordinary Portland cement PY - 2023 SP - 1 EP - 148 CY - Berlin AN - OPUS4-59172 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Klewe, Tim T1 - Non-destructive classification of moisture deterioration in layered building floors using ground penetrating radar N2 - In the event of moisture deterioration, rapid detection and localization is particularly important to prevent further deterioration and costs. For building floors, the layered structure poses a challenging obstacle for most moisture measurement methods. But especially here, layer-specific information on the depth of the water is crucial for efficient and effective repairs. Ground Penetrating Radar (GPR) shows the potential to generate such depth information. Therefore, the present work investigates the suitability of GPR in combination with machine learning methods for the automated classification of the typical deterioration cases (i) dry, (ii) wet insulation, and (iii) wet screed. First, a literature review was conducted to identify the most common methods for detecting moisture in building materials using GPR. Here, it especially became clear that all publications only investigated individual time-, amplitude- or frequency features separately, without combining them. This was seen as a potential aspect for innovation, as the multivariate application of several signal features can help to overcome individual weaknesses and limitations. Preliminary investigations carried out on drying screed samples confirmed the profitable use of multivariate evaluations. In addition to the general suitability and dependencies of various features, first limitations due to possible interference between the direct wave and the reflection wave could be identified. This is particularly evident with thin or dry materials, for which the two-way travel times of the reflected radar signals become shorter. An extensive laboratory experiment was carried out, for which a modular test specimen was designed to enable the variation of the material type and thickness of screed and insulation, as well as the simulation of moisture deteriorations. The data collected revealed clear differences between dry and deteriored structures within measured B-scans. These deviations were to be detected with the newly introduced B-scan features, which evaluate the statistical deviation of A-scan features within a survey line. In this way, deteriorations to unknown floor structures are recognized, regardless of the material parameters present. In a subsequent training and cross-validation process of different classifiers, accuracies of over 88 \% of the 504 recorded measurements (252 different experimental setups) were achieved. For that, the combination of amplitude and frequency features, which covered all relevant reflections of the radar signals, was particularly beneficial. Furthermore, the data set showed only small differences between dry floors and deteriored screeds for the B-scan features, which could be attributed to a homogeneous distribution of the added water in the screeds. The successfully separation of these similar feature distributions raised the suspicion of overfitting, which was examined in more detail by means of a validation with on-site data. For this purpose, investigations were carried out at five different locations in Germany, using the identical measurement method like in the laboratory. By extracting drilling cores, it was possible to determine the deterioration case for each measurement point and thus generate a corresponding reference. However, numerous data had to be sorted out before classification, since disturbances due to underfloor heating, screed reinforcements, steel beams or missing insulation prevented comparability with the laboratory experiments. Validation of the remaining data (72 B-scans) achieved only low accuracy with 53 \% correctly classified deterioration cases. Here, the previously suspected overfitting of the small decision boundary between dry setups and deteriored screeds within the laboratory proved to be a problem. The generally larger deviations within (also dry) on-site B-scans were thus frequently misclassified as screed deterioration. In addition, there were sometimes strongly varying layer thicknesses or changing cases of deterioration within a survey line, which caused additional errors due to the local limitation of the drilling core reference. Nevertheless, individual on-site examples also showed the promising potential of the applied signal features and the GPR method in general, which partly allowed a profound interpretation of the measurements. However, this interpretation still requires the experience of trained personnel and could not be automated using machine learning with the available database. Nevertheless, such experience and knowledge can be enriched by the findings of this work, which provide the basis for further research. Future work should aim at building an open GPR data base of on-site moisture measurements on floors to provide a meaningful basis for applying machine learning. Here, referencing is a crucial point, whose limitations with respect to the moisture present and its distribution can easily reduce the potential of such efforts. The combination of several reference methods might help to overcome such limitations. Similarly, a focus on monitoring approaches can also help to reduce numerous unknown variables in moisture measurements and increase confidence in the detection of different deterioration cases. KW - NDT KW - Moisture measurement KW - Ground penetrating radar KW - Building floor PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-591044 SP - 1 EP - 146 PB - Technische Universität Berlin CY - Berlin AN - OPUS4-59104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Spitzer, Stefan T1 - Influence of the ignition source on the Safety Characteristics of hybrid dust-gas mixtures N2 - Safety characteristics like the lower explosion limit, the highest concentration for a given substance mixed with air that does not result in a self-propagating flame, or the maximum explosion pressure, the highest pressure that can be reached after ignition for a given combustible substance mixed with air at any concentration, are widely used in the industry to either prevent an explosion or to mitigate the effects of it. Safety characteristics are not physical constants, are determined experimentally and depend on the chosen experimental parameters such as the ignition energy or turbulence. For the determination of the safety characteristics lower explosion limit (LEL), limiting oxygen concentration (LOC), maximum explosion pressure (pmax) and maximum rate of pressure rise ((dp/dt)max) of gases and vapors the gas is filled via partial pressures into a test vessel and then ignited under quiescent conditions with a weak (2 J - 20 J) ignition source. For dusts, the same safety characteristics are determined under turbulent conditions to elevate the dust homogeneously and it is ignited with two chemical igniters with an ignition energy of 1000 J each (LEL and LOC) or 5000 J each (pmax and (dp/dt)max). For the determination of safety characteristics of hybrid mixtures (a mixture containing a combustible dust and a flammable gas) there is no existing standard. In the last 40 years most of the research on their safety characteristics was performed with dust testing equipment that was modified for the addition of flammable gas. Because of the different mixing procedures of gases and dusts with air and because of different ignition energies and sources that are normally used for the standard tests of gases or dusts, the results were hardly reproducible. Statements about the different safety characteristics were contradictory and left the reader or the person responsible for designing safety measures for a process plant or a facility behind with no clear suggestion about the behavior of hybrid mixtures. This thesis is aimed on determining the influence of the different ignition sources and energies on the safety characteristics pmax, (dp/dt)max, lower explosion limit, and limiting oxygen concentration of hybrid mixtures. Several test series were conducted to characterize different standardized ignition sources, that are already in use for the determination of safety characteristics of single-phase substances (gases, liquids, dusts). The burning duration, the igniting volume and the net energy were investigated. It was shown, that the chemical igniters and the exploding wire are suitable ignition sources for the determination of safety characteristics of hybrid mixtures in general. Their burning duration was long enough to ignite dusts and quick enough, that the decay of the turbulence or sedimentation of the dusts did not occur. Both ignition sources produced comparable results for the determination of pmax, LEL and (dp/dt)max of dusts when they had the same ignition energy. A reduced ignition energy of the exploding wire and the chemical igniters did not affect the pmax and (dp/dt)max. The LEL changed with lower energies. However, for the determination of the LOC of hybrid mixtures the exploding wires with an overall energy of 2 kJ produced the best results. The influence of the different mixing procedures that have already been used for hybrid mixtures and the requirements for them were also investigated experimentally for the gas concentration and the determined safety characteristics and compared to each other. It was shown, that the partial pressure method works for mixing hybrid mixtures but the pressures should be measured very accurately and the gas concentration should be validated. Furthermore, the influence of the turbulence that is inevitable when testing dusts, on the safety characteristics of gases was determined. It was found that the chemical igniters and exploding wires produced comparable results for the determination of pmax, LEL and (dp/dt)max under turbulence. For the LOC only exploding wires with two times 1 kJ worked. Finally, the safety characteristics of hybrid mixtures were determined with different ignition energies and sources and the data were compared. It was discovered, that the pmax of hybrid mixtures was the same value than the higher determined one of the single substances while (dp/dt)max of hybrid mixtures was about 10 % to 25 % higher than the value of the stoichiometric gas mixture under turbulence. The point was found at the stoichiometric gas concentration with very little amounts of dust. To prove the key findings of this work and for the establishment of a standardized procedure for the determination of safety characteristics of hybrid mixtures, an international round robin test was conducted with eleven participating facilities in seven countries. The results were comparable within a reasonable range and are presented in this dissertation in an extra chapter. Based upon the observations in this work a reliable solution for a new standardizable ignition source to determine the safety characteristics of hybrid dust-gas-mixtures is proposed. KW - Ignition Sources KW - Hybrid Mixtures KW - Explosions PY - 2023 SP - 1 EP - 132 AN - OPUS4-58905 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Lecompagnon, Julien T1 - Nondestructive defect characterization using full-frame spatially structured super resolution laser thermography N2 - Laser-based active thermography is a contactless non-destructive testing method to detect material defects by heating the object and measuring its temperature increase with an infrared camera. Systematic deviations from predicted behavior provide insight into the inner structure of the object. However, its resolution in resolving internal structures is limited due to the diffusive nature of heat diffusion. Thermographic super resolution (SR) methods aim to overcome this limitation by combining multiple thermographic measurements and mathematical optimization algorithms to improve the defect reconstruction. Thermographic SR reconstruction methods involve measuring the temperature change in an object under test (OuT) heated with multiple different spatially structured illuminations. Subsequently, these measurements are inputted into a severely ill-posed and heavily regularized inverse problem, producing a sparse map of the OuT’s internal defect structure. Solving this inverse problem relies on limited priors, such as defect-sparsity, and iterative numerical minimization techniques. Previously mostly experimentally limited to one-dimensional regions of interest (ROIs), this thesis aims to extend the method to the reconstruction of two-dimensionalROIs with arbitrary defect distributions while maintaining reasonable experimental complexity. Ultimately, the goal of this thesis is to make the method suitable for a technology transfer to industrial applications by advancing its technology readiness level (TRL). In order to achieve the aforementioned goal, this thesis discusses the numerical expansion of a thermographic SR reconstruction method and introduces two novel algorithms to invert the underlying inverse problem. Furthermore, a forward solution to the inverse problem in terms of the applied SR reconstruction model is set up. In conjunction with an additionally proposed algorithm for the automated determination of a set of (optimal) regularization parameters, both create the possibility to conduct analytical simulations to characterize the influence of the experimental parameters on the achievable reconstruction quality. On the experimental side, the method is upgraded to deal with two-dimensional ROIs, and multiple measurement campaigns are performed to validate the proposed inversion algorithms, forward solution and two exemplary analytical studies. For the experimental implementation of the method, the use of a laser-coupled DLP-projector is introduced, which allows projecting binary pixel patterns that cover the whole ROI, reducing the number of necessary measurements per ROI significantly (up to 20x). Finally, the achieved reconstruction of the internal defect structure of a purpose-made OuT is qualitatively and qualitatively benchmarked against well-established thermographic testing methods based on homogeneous illumination of the ROI. Here, the background-noise-free two-dimensional photothermal SR reconstruction results show to outclass all defect reconstructions by the considered reference methods. N2 - Die laserbasierte aktive thermografische Prüfung als berührungslose Methode der zerstörungsfreien Werkstoffprüfung (NDT) basiert auf der aktiven Erwärmung des Testobjekts (OuT) und Messung des resultierenden Temperaturanstiegs mit einer Infrarotkamera. Dadurch bedingt können systematische Abweichungen vom vorhergesagten Erwärmungsverhalten Aufschluss über dessen innere Struktur geben. Jedoch ist das Auflösungsvermögen für innenliegende Defekte durch die diffusive Natur der Wärmeleitung in Festkörpern begrenzt. Thermografische Super-Resolution (SR)-Methoden zielen darauf ab, diese Limitation durch die Kombination mehrerer Messungen mit jeweils unterschiedlicher strukturierter Erwärmung und mathematischer Optimierungsmethoden zu überwinden. Zur Rekonstruktion innerer Defekte mithilfe thermografischer SR-Rekonstruktionsmethodik wird für die Gesamtheit mehrerer Messungen ein schlecht gestelltes und stark regularisiertes inverses mathematisches Problem gelöst, was in einer dünnbesetzten Karte der internen Defektstruktur des OuTs resultiert. Die Inversion mittels iterativer numerischer Minimierungsverfahren profitiert dabei von einzelnen Annahmen wie der vergleichsweisen Seltenheit von Materialdefekten. Nachdem die Methode bisher experimentell fast ausschließlich auf eindimensionale Messbereiche (ROIs) beschränkt war, zielt diese Arbeit auf eine Erweiterung zur Prüfung zweidimensionaler ROIs mit arbiträren Defektverteilungen bei erträglicher experimenteller Komplexität ab. Ziel ist es, durch die Weiterentwicklung des Technologie-Reifegrades (TRL) den Technologietransfer zur industriellen Anwendung zu ermöglichen. Hierzu werden erst die numerische Erweiterung der SR-Rekonstruktionsmethodik für zweidimensionale ROIs erörtert und zwei neue Algorithmen zur Invertierung des zugrunde liegenden inversen Problems vorgestellt, sowie eine Vorwärtslösung des inversen Problems entwickelt. In Verbindung mit einem neuartigen Algorithmus zur automatisierten Bestimmung der (optimalen) Regularisierungsparameter wird erstmals die Möglichkeit geschaffen, analytische Simulationen zum Einfluss einzelner Parameter auf die erreichbare Rekonstruktionsqualität durchzuführen. Weiterhin wird der experimentelle Ansatz zur Prüfung zweidimensionaler ROIs erweitert. Mehrere Messkampagnen validieren die eingeführten Inversionsalgorithmen, die Vorwärtslösung und zwei exemplarische analytische Studien. Für die experimentelle Umsetzung wird erstmals die Verwendung lasergekoppelter DLP-Technologie für die makroskopische thermografische Prüfung nutzbar gemacht, welche die Projektion großflächiger binärer Pixelmuster ermöglicht. Dadurch kann die Anzahl der erforderlichen Messungen pro ROI ohne Qualitätseinbußen erheblich reduziert werden (bis zu 20x). Abschließend werden die erzielten Rekonstruktionsergebnisse der internen Defektstruktur eines speziell angefertigten OuTs qualitativ und quantitativ mit auf homogener Erwärmung basierenden etablierten Methoden der thermografischen Prüfung verglichen. Hier zeigt sich, dass die weitgehend rauschfreien SR-Rekonstruktionsergebnisse alle Defektrekonstruktionen der betrachteten Referenzmethoden deutlich übertreffen. KW - Nondestructive testing KW - Zerstörungsfreie Prüfung KW - Thermography KW - Thermografie KW - Super resolution KW - Structured illumination KW - Strukturierte Beleuchtung KW - Defect characterization KW - Defektcharakterisierung KW - DMD KW - DLP PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-588296 SP - 1 EP - 154 PB - Technische Universität Berlin CY - Berlin AN - OPUS4-58829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Sprengel, Maximilian Franz-Arthur T1 - Study on the determination and the assessment of the residual stress in laser powder bed fused stainless steel structures N2 - Additive manufacturing processes offer extensive advantages for the design freedom of structures through layer-by-layer production. This enables high weight savings as well as the integration of functions such as cooling channels. This technology thus offers great potential to contribute to a sustainable future. The pioneer among these manufacturing processes is the powder bed fusion of metals with laser beams (PBF-LB/M). This process is characterised by high laser scanning speeds and highly localised heat input, which have a strong effect on the microstructure and thus also on the mechanical properties. For example, the austenitic steel 316L exhibits a cellular structure at the subgrain level. This microstructure feature leads to higher yield strengths and comparable ductility to conventionally processed 316L. In addition to the traditional applications of 316L steel in the petrochemical and nuclear industries, this enables new applications such as medical stents or bipolar plates for fuel cells with proton exchange membranes. However, the layer-by-layer production with high scanning speeds and localised heat input induces cooling rates in the order of 106 K.s-1. The large temperature gradients and the shrinkage restraints of each weld bead and layer lead to the development of complex residual stress fields. These reduce the material performance and can even lead to premature failure. Thus, the fatigue properties are severely affected by rapid crack growth or prematurely developing cracks. Furthermore, specimens may warp during PBF-LB/M or immediately when the components are separated from the build plate. Therefore, residual stress is one of the main disadvantages of PBF-LB/M, making it difficult for this technology to be more widely accepted in the industry. Based on the current state of the literature, the procedure for determining residual stress employing diffraction methods, the influence of the component geometry, as well as the inter-layertime (ILT) on residual stress and, lastly, suitable heat treatment strategies for relaxing residual stress in PBF-LB/M/316L, were identified as insufficiently researched areas. Determining residual stress is a major challenge. X-ray and neutron diffraction are particularly suitable for filigree structures, which can preferably be produced using PBF-LB/M. Here, the microscopic strain of the lattice planes is used to calculate the macroscopic residual stress. These methods are nondestructive and allow the spatial resolution of the bi-axial and tri-axial residual stress. In the present work, in-situ neutron diffraction tensile tests were performed to analyse the micromechanical behaviour of PBF-LB/M/316L. The suitability of the lattice planes for calculating the macroscopic residual stress was investigated. The (311) lattice plane was found to be the best option for determining the macroscopic residual stress in PBF-LB/M/316L. Furthermore, it was shown that the Kröner model can be used to calculate the X-ray diffraction constants despite the texture. Currently, both aspects are common practices in the determination of residual stress. The results presented here support the validity of this approach and increase the confidence in the experimentally determined residual stress, which has a positive effect on the assessment of quality concerning the safety of a component manufactured by PBF-LB/M. The geometry of a structure manufactured by PBF-LB/M determines the component stiffness and influences the thermal gradients during manufacture and ultimately the residual stress. The effect of smaller or larger dimensions (larger than 10 mm) on the residual stress is rarely considered. To investigate this aspect, representative test specimens with different thicknesses and lengths were produced. Hence, the influence of the geometry i.e., component stiffness on the residual stress was evaluated. The residual stress was determined using X-ray and neutron diffraction. The analysis of the residual stress showed that an increase in thickness leads to overall higher residual stress. In addition, it was shown that increasing the sample dimension leads to smaller residual stress gradients. Above a threshold value of a few millimetres, no significant change in the residual stress was observed. The ILT is inherent in every PBF-LB/M construction job and influences the thermal gradients during production and thus the residual stress. A change in wall thickness in a geometrically complex structure or a variation in the number of specimens in the construction process leads directly to a change in the ILT. To simulate this, specimens with different ILT were produced. The residual stress was determined by X-ray and neutron diffraction. The use of a short ILT resulted in higher surface residual stress, but lower volume residual stress. Here, the surface residual stress and the residual stress in the volume showed contrary behaviour. This was attributed to the complex heat conduction during the process, as shown by the thermographic measurements. To avoid distortion of the specimens or real components upon separation from the build plate or during post-processing steps, stress relief annealing is usually performed after the PBF-LB/M process. Based on standards for heat treatment of welded austenitic steels, heat treatments were performed at low (450 °C for four hours) and high (800 °C and 900 °C for one hour) temperatures. The results show that the heat treatment at 450 °C relaxed the residual stress by only 5 %. This low relaxation is due to the stability of the cell structures. The high-temperature heat treatment showed that 900 °C is required to dissolve the cell structure and achieve a relaxation of about 85 %. This result is in good agreement with the standards for stress relief annealing of welded austenitic steels. N2 - Additive Fertigungsverfahren bieten durch die schichtweise Herstellung weitreichende Vorteile für die Gestaltungsfreiheit von Strukturen und ermöglichen somit hohe Gewichtseinsparungen. Auch die Integration von Funktionen, beispielsweise Kühlkanäle, können unmittelbar während der Herstellung eingebracht werden. Damit bietet diese Technologie ein hohes Potential zu einer nachhaltigen Zukunft beizutragen. Der Vorreiter unter diesen Fertigungsprozessen ist das Pulverbettbasierte Schmelzen von Metallen mittels Laserstrahlen (PBF-LB/M). Dieser Prozess zeichnet sich durch hohe Laserscangeschwindigkeiten und eine stark lokalisierte Wärmeeinbringung aus, welche sich auf die Mikrostruktur und damit auch auf die mechanischen Eigenschaften auswirken. So weist der austenitische Stahl 316L eine zelluläre Struktur auf Subkornniveau auf, welche zu höheren Streckgrenzen jedoch nicht verringerter Duktilität im Vergleich zu konventionell verarbeitetem 316L führt. Dies ermöglicht, neben den traditionellen Einsatzgebieten des Stahls 316L in der petrochemischen und nuklearen Industrie, neue Anwendungen wie medizinische Stents oder Bipolarplatten für Brennstoffzellen mit Protonenaustauschmembran. Die schichtweise Fertigung mit hohen Scangeschwindigkeiten und lokaler Wärmeeinbringung bedingt jedoch Abkühlraten in der Größenordnung von 106 K.s-1. Die hohen Temperaturgradienten im Zusammenspiel mit den Schrumpfbehinderungen jeder Schweißraupe und Lage sorgen für die Entstehung komplexer Eigenspannungsfelder. Diese verringern die Beanspruchbarkeit des Materials und können sogar zu einem vorläufigen Versagen führen. So sind die Ermüdungseigenschaften durch ein rapides Risswachstum bzw. ein vorzeitig entstehender Riss durch Eigenspannungen stark beeinträchtigt. Des Weiteren kommt es vor, dass sich die Proben während des PBF-LB/M oder unmittelbar bei der Trennung der Bauteile von der Bauplatte verziehen. Daher sind die Eigenspannungen eines der Hauptnachteile des PBF-LB/M, die eine breitere Akzeptanz dieses Verfahrens in der Industrie erschweren. Ausgehend vom aktuellen Literaturstand, wurde die Vorgehensweise bei der Bestimmung der Eigenspannungen mittels Beugungsmethoden, der Einfluss der Bauteilgeometrie bzw. Bauteilsteifigkeit sowie der Zwischenlagenzeit auf die Eigenspannungen und zuletzt geeignete Wärmebehandlungsstrategien zur Relaxation der Eigenspannungen in PBF-LB/M/316L als unzureichend erforschte Bereiche identifiziert. Die Bestimmung der Eigenspannung ist eine große Herausforderung. Insbesondere bei filigranen Strukturen, welche vorzugsweise mittels PBF-LB/M hergestellt werden können, eignen sich die Röntgen- und Neutronenbeugung. Hierbei wird die mikroskopische Dehnung der Gitterebenen zur Berechnung der makroskopischen Eigenspannung verwendet. Diese Methoden sind zerstörungsfrei und ermöglichen die räumliche Auflösung der bi-axialen und tri-axialen Eigenspannungen. In der vorliegenden Arbeit wurden in-situ Neutronenbeugungszugversuche durchgeführt, um das mikromechanische Verhalten des PBF-LB/M/316L zu analysieren. Die Eignung der Gitterebenen zur Berechnung der makroskopischen Eigenspannung wurde untersucht. Die (311) Gitterebene erwies sich als die beste Option für die Bestimmung der makroskopischen Eigenspannung in PBF-LB/M/316L. Darüber hinaus wurde gezeigt, dass das Kröner-Modell trotz Textur zur Berechnung der Röntgenbeugungskonstanten verwendet werden kann. Derzeit werden beide Aspekte in der Bestimmung der Eigenspannungen standardmäßig angewandt. Die hier präsentierten Ergebnisse untermauern die Gültigkeit dieses Vorgehens und erhöhen das Vertrauen in den experimentell bestimmten Eigenspannungen, welches sich positiv auf die Beurteilung der Qualität hinsichtlich der Sicherheit eines durch PBF-LB/M gefertigten Bauteils auswirkt. Die Geometrie einer durch PBF-LB/M hergestellten Struktur bestimmt maßgeblich die Bauteilsteifigkeit und beeinflusst die thermischen Gradienten während der Herstellung und letztendlich die Eigenspannungen. Die Auswirkung kleinerer oder größerer Abmessungen (größer 10 mm) auf die Eigenspannungen wird derzeit oft nicht berücksichtigt. Um diesen Aspekt zu untersuchen, wurden repräsentative Probekörper mit unterschiedlichen Dicken und Längen hergestellt. Damit konnte der Einfluss der Geometrie bzw. Bauteilsteifigkeit auf die Eigenspannungen gezielt bewertet werden. Die Eigenspannungen wurden mittels Röntgen- als auch Neutronenbeugung bestimmt. Die Analyse der Eigenspannungen ergab, dass eine Erhöhung der Dicke zu insgesamt höheren Eigenspannungen führt. Zusätzlich wurde gezeigt, dass eine Vergrößerung der Probenabmessung zu kleineren Eigenspannungsgradienten führt. Oberhalb eines Schwellenwerts von wenigen Millimetern ändern sich die Eigenspannungen nicht mehr signifikant. Die sogenannte Zwischenlagenzeit (ILT) ist jedem PBF-LB/M-Bauauftrag inhärent und beeinflusst die thermischen Gradienten während der Herstellung und damit maßgeblich die Eigenspannungen. Ein Wanddickensprung in einer geometrisch komplexen Struktur bzw. einer Variation der Probenanzahl im Bauprozess führt unmittelbar zu einer Änderung der ILT. Um dies nachzubilden, wurden Proben mit unterschiedlichen ILT hergestellt. Die Eigenspannungen wurden mittels Röntgen- und Neutronenbeugung bestimmt. Die Verwendung einer kurzen ILT hat zu höheren Oberflächeneigenspannungen geführt, jedoch zu geringeren Volumeneigenspannungen. Hierbei zeigten die Oberflächeneigenspannungen und die Eigenspannungen im Volumen ein konträres Verhalten. Dies wurde auf die komplexe Wärmeleitung während des Prozesses zurückgeführt, wie die thermografischen Messungen zeigten. Um den Verzug der hergestellten Probekörper oder realen Bauteile bei der Abtrennung der Bauplatte oder in Nachbearbeitungsschritten zu vermeiden, wird in der Regel ein Spannungsarmglühen nach dem PBF-LB/M Prozess durchgeführt. Basierend auf Standards für die Wärmebehandlung von geschweißten austenitischen Stählen, wurden Wärmebehandlungen bei niedrigen (450 °C für vier Stunden) und hohen (800 °C bzw. 900 °C für eine Stunde) Temperaturen durchgeführt. Die Ergebnisse zeigen, dass die Wärmebehandlung bei 450 °C die Eigenspannungen um lediglich 5 % relaxierte. Diese geringe Relaxation ist auf die Stabilität der Zellstrukturen zurückzuführen. Die Hochtemperatur-Wärmebehandlung zeigte, dass 900 °C erforderlich sind, um die Zellstruktur aufzulösen und eine Relaxation von etwa 85 % zu erreichen. Dieses Ergebnis steht in guter Übereinstimmung mit den Standards für das Spannungsarmglühen geschweißter austenitischer Stähle. T3 - BAM Dissertationsreihe - 173 KW - Residual Stress KW - Powder Bed Fusion of Metals with Laser Beams KW - Austenitic Stainless Steel KW - Diffraction KW - Heat Treatment KW - Eigenspannungen KW - Pulverbettbasiertes Laserstrahlschmelzen KW - Austenitischer Rostfreier Stahl KW - Beugung KW - Wärmbehandlung PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-579802 SN - 1613-4249 VL - 173 SP - 1 EP - 256 PB - Eigenverlag CY - Berlin AN - OPUS4-57980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -