TY - JOUR A1 - Hilger, A. A1 - Kardjilov, N. A1 - Lange, A. A1 - Kupsch, Andreas A1 - Hentschel, M. P. A1 - Manke, I. T1 - Neutron darkfield imaging of fiber composites JF - Materials Testing N2 - While X-ray based darkfield imaging with grating interferometers is already widely used, darkfield imaging with neutrons has still a relatively small user community focused mostly on magnetic materials. Here, we demonstrate the application of neutron darkfield imaging byTalbot-Lau type grating interferometry to fiber reinforced plastics. Common carbon and glass fiber composites have been investigated including characteristic damage structures. The darkfield images show a strong signal response caused by fiber delamination, suitable fiber direction, particles, pores and cracks. The basic principles of neutron darkfield imaging applied to fiber composites are highlighted. KW - Neutron radiography KW - Darkfield imaging KW - Talbot-Lau interferometer KW - Fiber composites KW - Non-destructive testing PY - 2021 DO - https://doi.org/10.1515/mt-2020-0103 SN - 2195-8572 SN - 0025-5300 VL - 63 IS - 7 SP - 623 EP - 629 PB - De Gruyter CY - Berlin AN - OPUS4-53077 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Soares, A.P. A1 - Baum, D. A1 - Hesse, B. A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Zaslansky, P. T1 - Scattering and phase-contrast X-ray methods reveal damage to glass fibers in endodontic posts following dental bur trimming JF - Dental Materials N2 - Objectives. There is concern that the integrity of fiberglass dental posts may be affected by chairside trimming during treatment. We hypothesize that hard X-ray methods of phase contrast-enhanced micro-CT (PCE-CT) and synchrotron based X-ray refraction (SXRR) can reliably identify and help characterize the extent of damage. Methods. Fiberglass posts were imaged both as manufactured and following trimming with a diamond bur. Each of the posts was imaged by SXRR and by PCE-CT. Datasets from PCE-CT were used to visualize and quantify 2D and 3D morphological characteristics of intact and of damage-affected regions caused by trimming. Results. The SXRR images revealed fiber inhomogeneities from manufacturing with a significant increase in internal surfaces in sample regions corresponding to damage from trimming. PCE-CT volumes unveiled the micromorphology of single fibers in the posts and some damage in the trimmed area (e.g. fractures, splinters and cracks). Area, perimeter, circularity, roundness, volume and thickness of the glass fibers in the trimmed area were statistically different from the control (p < 0.01). Significance. The integrity of single fibers in the post is critical for bending resistance and for long-term adhesion to the cement in the root canals. Damage to the fibers causes substantial structural weakening across the post diameter. Glass fragments produced due to contact with the dental bur may separate from the post and may significantly reduce bond capacity. The above mentioned synchrotron-based imaging techniques can further facilitate assessment of the structural integrity and the appearance of defects in posts (e.g. after mechanical load). KW - Fiberglass composite KW - Fiber reinforced dental post KW - X-ray refraction KW - Phase contrast-enhanced micro-CT KW - Non-destructive testing PY - 2021 DO - https://doi.org/10.1016/j.dental.2020.10.018 SN - 0109-5641 VL - 37 IS - 2 SP - 201 EP - 211 PB - Elsevier Inc. AN - OPUS4-52071 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -