TY - JOUR A1 - Habibimarkani, Heydar A1 - Abram, Sarah-Luise A1 - de Oliveira Guilherme Buzanich, Ana A1 - Prinz, Carsten A1 - Sahre, Mario A1 - Hodoroaba, Vasile-Dan A1 - Radnik, Jörg T1 - In-depth analysis of FeNi-based nanoparticles for the oxygen evolution reaction N2 - This study investigates the effect of varying iron-to-nickel ratios on the catalytic performance of Fe-Ni oxide nanoparticles (NPs) for the oxygen evolution reaction (OER). Addressing the issue of high energy wastage due to large overpotentials in OER, we synthesized and characterized different NP catalysts with different Fe: Ni oxide ratios. Transmission Electron Microscopy (TEM), Energy Dispersive X-ray Spectroscopy (EDS), and X-ray Diffraction (XRD) were employed to determine the morphology, elemental and phase composition of the NPs. Furthermore, in-depth profiling with X-ray Photoelectron Spectroscopy (XPS) and Hard X-ray Photoelectron Spectroscopy (HAXPES) revealed that iron predominantly exists as oxide, while nickel exhibits both metallic and oxidic forms depending on the Fe content. XPS indicated an enrichment of iron at the NP surface, whereas HAXPES and EDS data agreed on the bulk stoichiometry. The assessment of the catalytic activity via cyclic voltammetry (CV) showed that the Fe: Ni ratio of 2:3 exhibited superior performance, characterized by lower overpotential and a smaller Tafel slope. KW - Fe-Ni oxide KW - Nanoparticles KW - OER KW - Catalytic performance KW - Cyclic voltammetry PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-626932 UR - https://www.nature.com/articles/s41598-025-92720-3 DO - https://doi.org/10.1038/s41598-025-92720-3 VL - 15 IS - 1 SP - 1 EP - 17 PB - Springer Nature AN - OPUS4-62693 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fagan, Jeffrey A1 - Hodoroaba, Vasile-Dan T1 - VAMAS TWA Nanoparticle Populations Projects 15 and 16 N2 - The progress in the VAMAS Project #15 "Measurement of particle size and shape distribution of bipyramidal titania including deposition from liquid suspension" within TWA 34 Nanoparticle Populations is presented with highlight of the following points: - Determine and compare particle size and shape distribution by means of electron microscopy (SEM, TEM, STEM-in-SEM), atomic force microscopy (AFM) and small angle X-ray scattering (SAXS). - Determine uncertainty induced by deposition protocol from liquid suspension with comparison to known values from a prior ILC with already deposited nanoparticles on TEM grids. - Provide comparative validation of protocols for the techniques other than TEM. Further, the VAMAS/TWA 34 Project #16 "Measurement of (relative) number concentration of bimodal silica nanoparticles including deposition from liquid suspension" is presented. Follwowing points are discusssed: - Validate the performance of imaging methods to measure the relative number concentration by electron microscopy (SEM, TEM) and atomic force microscopy (AFM) and two modes of bimodal (30 and 60 nm) silica nanoparticles - Validate the performance of small angle X-ray scattering (SAXS) for the traceable measurement of the number concentration of the two modes. T2 - Versailles Project on Advanced Materials and Standards (VAMAS) 49th Steering Committee Meeting CY - Rio de Janeiro, Brazil DA - 23.09.2024 KW - VAMAS KW - Nanoparticles KW - Nanoparticle size and shape distribution KW - Particle number concentration KW - Interlaboratory comparison KW - Standardisation PY - 2024 UR - http://www.vamas.org/twa34/index.html AN - OPUS4-61422 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Salzmann, Christoph A1 - Pellegrino, Francesco A1 - Hodoroaba, Vasile-Dan T1 - STEM-in-SEM versus SE-InLens-type-SEM as a Reliable Analytical Pair-Tool for Measurement of Nanoparticle Size and Shape Distribution N2 - Following points are addressed in this contribution: Advantages of correlative analysis in electron microscopy; Measurement principle of the different electron microscopy modes used; Presentation of the nanomaterials used for this study; Role of sample preparation; and, with particular description, the Sequence kV-variation with InLens SE & transmission SEM detection of the same field-of-view. KW - Nanoparticles KW - Electron microscopy KW - Metrology KW - Particle size distribution PY - 2024 DO - https://doi.org/10.1093/mam/ozae044.308 VL - 30 IS - Supplement_1 SP - 650 EP - 651 PB - Oxford University Press (OUP) AN - OPUS4-61042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mrkwitschka, Paul A1 - Abram, Sarah-Luise A1 - Rühle, Bastian A1 - Hodoroaba, Vasile-Dan T1 - Understanding Correlative Electron Microscopy Imaging with SEM, STEM-in-SEM and TEM for the Accurate Characterization of Size and Shape of Iron Oxide Nanoparticles N2 - The recently certified reference material (CRM) BAM-N012 as cubical iron oxide FeOx nanoparticles (NPs) of 8 nm area equivalent square edge length (ESL) and the RM candidate BAM-N013 as nearly spherical NPs of 22 nm size were analyzed in detail by electron microscopy (EM). For the metrological characterization with SEM, STEM in SEM and TEM, the understanding of the imaging contrasts and sensitivities, and the correct interpretation of the (art)effects which are inherent to each detection mode is necessary. The same sample areas with NPs deposited on a TEM grid were analyzed by two SEM acquisition modes, i. e. SE InLens and STEM in SEM using a dedicated transmission sample holder, and further, correlatively, analyzed with TEM. With increasing kV, SE InLens shows increasing particle size (unless overcharging at the particle boundaries is filtered), as a known effect. For STEM-in-SEM the particle size decreases significantly and individual particles are identified easier (at 2 kV only a few single particles can be detected automatically). ❑ Documentation of the sample preparation and measurement conditions (including optimization process) is important for reproducibility. ❑ Plasma cleaning, analysis in the transmission mode at SEM is recommended for FeOx NPs. ❑ Selection of the threshold algorithm can significantly alter the reported ECD. KW - Nanoparticles KW - Iron oxide KW - Electron microscopy KW - Reference materials KW - Particle size distribution KW - Imaging PY - 2024 DO - https://doi.org/10.1093/mam/ozae044.339 VL - 30 IS - Supplement_1 SP - 710 EP - 711 PB - Oxford University Press (OUP) AN - OPUS4-61007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Ongoing International Interlaboratory Comparisons on Size, Shape and (Relative) Concentration of Complex Nanoparticles under the Pre-Standardization Platform of VAMAS N2 - Traceable morphological and chemical characterization of nanomaterials with respect to the various possible sizes, size distributions, shapes, and concentrations of real-world nanoparticles (NPs) is a challenging task. Particularly for the nonspherical, non-monodisperse nanoparticles – as typically for most of the commercial particles, including their strong tendency to agglomerate, there is a lack of standard operation procedures providing accurate nanoparticle characterisation. In the framework of the pre-standardisation framework of VAMAS (Versailles Project on Advanced Materials and Standards, www.vamas.org) two interlaboratory comparison (ILC) studies are being carried out under the Technical Working Area (TWA) 34 “Nanoparticle Populations”:i) Project #15 addresses the analysis of the size and shape distribution of TiO2 bipyramidal NPs by traceable imaging methods such as TEM, SEM, STEM-in-SEM, AFM as well as with SAXS as an ensemble method. This ILC is thought as the next level development of the case studies exemplified in the published ISO standards ISO 21363 and ISO 19749. It was agreed to complete the first ILC with the NPs already prepared according to the same procedure on a TEM grid, and, at a later stage, to carry out second ILCs with the same NPs distributed to the participants as liquid suspensions together with protocols for the uniform NP deposition on suited substrates - as developed and optimized within the European project nPSize. Once having good deposition protocols available, the door for automated image analysis gets opened. Corresponding image analysis protocols and reporting templates have been distributed to the ILC participants, too. ii) Project #16: two spherical SiO2 NP samples with bi-modal size distributions in two nominal relative number concentrations were prepared and distributed also as liquid suspensions accompanied by sample preparation, measurement, and image analysis protocols and reporting templates. Here, the NP concentration is the primary parameter to be measured. For the imaging methods it is targeted to measure the relative nanoparticle concentrations (relative populations of the two modes). The results of all the participating laboratories, in both ILCs, compiled in comparative representations will be shown and discussed for the first time. The reduction of the measurement uncertainties associated to the size, shape and number-concentration results induced by the significant improvement of the sample preparation on substrates (as single particles with a high-density coverage), combined with well-defined image analysis procedures will be highlighted. Finally, a very recent 3rd ILC an the determination of lateral size of Graphene Oxide flakes by SEM is presented as project P13 under VAMAS TWA41 Graphene and Related 2D. T2 - Microscopy and Microanalysis 2024 CY - Cleveland, OH, USA DA - 28.07.2024 KW - VAMAS KW - Interlaboratory comparison KW - Imaging KW - Nanoparticles KW - Electron microscopy KW - Graphene oxide KW - Particle size distribution PY - 2024 AN - OPUS4-60875 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mrkwitschka, Paul A1 - Hodoroaba, Vasile-Dan T1 - Understanding Correlative Electron Microscopy Imaging with SEM, STEM in SEM and TEM for the Accurate Characterization of Size and Shape of FeOx Nanoparticles N2 - The recently certified reference material (CRM) BAM-N012 as cubical iron oxide FeOx nanoparticles (NPs) of 8 nm area equivalent square edge length (ESL) and the RM candidate BAM-N013 as nearly spherical NPs of 22 nm size were analyzed in detail by electron microscopy (EM). For the metrological characterization with SEM, STEM in SEM and TEM, the understanding of the imaging contrasts and sensitivities, and the correct interpretation of the (art)effects which are inherent to each detection mode is necessary. The same sample areas with NPs deposited on a TEM grid were analyzed by two SEM acquisition modes, i. e. SE InLens and STEM in SEM using a dedicated transmission sample holder, and further, correlatively, analyzed with TEM. With increasing kV, SE InLens shows increasing particle size (unless overcharging at the particle boundaries is filtered), as a known effect. For STEM-in-SEM the particle size decreases significantly and individual particles are identified easier (at 2 kV only a few single particles can be detected automatically). ❑ Documentation of the sample preparation and measurement conditions (including optimization process) is important for reproducibility. ❑ Plasma cleaning, analysis in the transmission mode at SEM is recommended for FeOx NPs. ❑ Selection of the threshold algorithm can significantly alter the reported ECD. T2 - Microscopy and Microanalysis 2024 CY - Cleveland, OH, USA DA - 28.07.2024 KW - Nanoparticles KW - Electron microscopy KW - Iron oxide KW - Reference materials KW - Correlative microscopy KW - Size and shape distribution PY - 2024 AN - OPUS4-60806 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - STEM in SEM vs SE InLens type SEM as a Reliable Analytical Pair Tool for Measurement of Nanoparticle Size and Shape Distribution N2 - In this lecture, following points are addressed: – Advantages of correlative analysis in electron microscopy – Measurement principle of the different electron microscopy modes used – Presentation of the nanomaterials used for this study – Role of sample preparation – Sequence kV variation with InLens & transmission detection of the same field-of-view – Conclusive remarks including Monte Carlo simulations T2 - Microscopy and Microanalysis 2024 CY - Cleveland, OH, USA DA - 28.07.2024 KW - Correlative analysis KW - Electron microscopy KW - Nanoparticles KW - SEM KW - STEM-in-SEM KW - Particle size distribution KW - Titanium dioxide PY - 2024 AN - OPUS4-60804 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Measurement of Lateral Dimensions of Particles & Flakes (2D) by Imaging Methods N2 - An overview with the basics of size and shape measurement of particles and 2D structures according to established methodologies (and popular imaging processing software packages) with imaging techniques is given. Main descriptors are explained based on practical cases are determined interactively at the flipchart. T2 - MaterialsWeek 2024 CY - Limassol, Cyprus DA - 17.06.2024 KW - Nanoparticles KW - 2D materials KW - Lateral dimensions KW - ISO KW - Imaging PY - 2024 AN - OPUS4-60454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Role of Sample Preparation for Accurate and Automated Morphological Analysis of Nanoparticles proven in Interlaboratory Comparison Exercises N2 - Traceable morphological and chemical characterization of nanomaterials with respect to the various possible sizes, size distributions, shapes, and concentrations of real-world nanoparticles (NPs) is a challenging task. Particularly for the nonspherical, non-monodisperse nanoparticles – as typically for most of the commercial particles, including their strong tendency to agglomerate, there is a lack of standard operation procedures providing accurate nanoparticle characterisation. In the framework of the pre-standardisation framework of VAMAS (Versailles Project on Advanced Materials and Standards, www.vamas.org) two interlaboratory comparison (ILC) studies are being carried out under the Technical Working Area (TWA) 34 “Nanoparticle Populations”:i) Project #15 addresses the analysis of the size and shape distribution of TiO2 bipyramidal NPs by traceable imaging methods such as TEM, SEM, STEM-in-SEM, AFM as well as with SAXS as an ensemble method. This ILC is thought as the next level development of the case studies exemplified in the published ISO standards ISO 21363 and ISO 19749. It was agreed to complete the first ILC with the NPs already prepared according to the same procedure on a TEM grid, and, at a later stage, to carry out second ILCs with the same NPs distributed to the participants as liquid suspensions together with protocols for the uniform NP deposition on suited substrates - as developed and optimized within the European project nPSize. Once having good deposition protocols available, the door for automated image analysis gets opened. Corresponding image analysis protocols and reporting templates have been distributed to the ILC participants, too. ii) Project #16: two spherical SiO2 NP samples with bi-modal size distributions in two nominal relative number concentrations were prepared and distributed also as liquid suspensions accompanied by sample preparation, measurement, and image analysis protocols and reporting templates. Here, the NP concentration is the primary parameter to be measured. For the imaging methods it is targeted to measure the relative nanoparticle concentrations (relative populations of the two modes). The results of all the participating laboratories, in both ILCs, compiled in comparative representations will be shown and discussed for the first time. The reduction of the measurement uncertainties associated to the size, shape and number-concentration results induced by the significant improvement of the sample preparation on substrates (as single particles with a high-density coverage), combined with welldefined image analysis procedures will be highlighted. T2 - MaterialsWeek 2024 CY - Limassol, Cyprus DA - 17.06.2024 KW - Nanoparticles KW - VAMAS KW - Interlaboratory comparison KW - Sample preparation KW - Nanoparticle concentration PY - 2024 AN - OPUS4-60453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Ongoing VAMAS ILC s on Nanoparticles and Graphene Oxide N2 - This contributions shows the first results of the ongoing interlaboratory comparisons under VAMAS/TWA 34 Nanoparticle populations related on the determination of pasrticle size distribution and relative concentration of nanoparticles and an example of an ILC running under VAMAS/TWA 41 Graphene and Related 2D Materials on the determination of the lateral diemsnions of graphene oxide flakes by Scanning Electron Microscopy. The link to related standardisation projects at ISO/TC Nanotechnologies are explained. T2 - Webinar Building the Foundation: Interlaboratory Comparisons and Reference Products for Advanced Materials CY - Berlin, Germany DA - 16.05.2024 KW - Nanoparticles KW - VAMAS KW - Interlaboratory comparison KW - Standardisation KW - Electron microscopy KW - AFM KW - SAXS PY - 2024 AN - OPUS4-60097 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -