TY - GEN A1 - Durlo Tambara, Luís Urbano A1 - Dehn, F. A1 - Gluth, Gregor ED - D’Erme, C. ED - Paglia, C. ED - Cordero, E. G. T1 - The importance of leaching for the carbonation resistance of alkali-activated slag and calcined clay concretes N2 - This study investigates the impact of leaching on the carbonation resistance of alkali-activated materials with varying calcium content. Six binder compositions were tested, combining ground blast furnace slag and calcined clay, with CaO content ranging from ~0% to ~40%. Samples underwent three conditions: no leaching, two weeks of leaching (2Le), and five leaching-carbonation cycles (5LCC). Carbonation tests were performed under natural conditions and 1% CO2 for reference and 2Le samples, while 5LCC samples were exposed solely to accelerated carbonation. Under natural carbonation, the typical relationship between carbonation resistance and the water/(CaO+MgOeq+Na2Oeq+K2Oeq) ratio was observed for both the reference and 2Le samples, with an increase in carbonation rate in compositions containing more than 40% calcined clay. In accelerated carbonation conditions, 2Le and 5LCC conditions showed slightly improved carbonation resistance compared to the reference samples, except for the mixtures containing only calcined clay (C100) and the mix with 40% calcined clay (C40S60). The poor performance of C100 was attributed to its low reactivity after 28 days, which resulted in significant sodium leaching and reduced activation of the calcined clay. Although C40S60 outperformed non-leached samples, its carbonation resistance slightly decreased in leached and accelerated carbonation samples due to reduced gel phase formation; however, this reduction was significantly less than that of C100. These findings suggest that while leaching can enhance carbonation resistance by reducing excess alkalis, low-reactivity systems, e.g. based solely on calcined clay, are more susceptible to degradation. KW - Carbonation KW - Alkali-activated materials KW - Leaching KW - Durability KW - Calcined clay PY - 2026 SN - 978-3-032-14170-5 DO - https://doi.org/10.1007/978-3-032-14170-5_16 SP - 148 EP - 157 PB - Springer CY - Cham AN - OPUS4-65355 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute T1 - Utilization of recycling materials in Germany - Regulations, assessment framework and leaching tools N2 - Der Vortrag wurde im Rahmen des 9th Geoenvironmental Assessment Seminars gehalten der auf Leaching- und Adsorptionstests fokussiert war. Der Vortrag enthielt einen Überblick über die Standardisierung von Leachingverfahren in DIN, CEN und ISO. Die Vorgehensweise der Bewertung des Schadstofftransfers bei der Wiederverwertung von Bodenmaterialien und der Verwertung mineralischer Ersatzbaustoffe in Deutschland wurde hinsichtlich der neuen rechtlichen Rahmenbedingungen dargestellt. Spezielle Herausforderungen bei der Untersuchung von PFAS mit Elutionsverfahren wurden aufgezeigt. T2 - 9th Geoenvironmental Assessment Seminar AIST (National Institute of Advanced Industrial Science and Technology) CY - Tsukuba, Japan DA - 25.03.2024 KW - Recycling of mineral waste KW - Contaminant transfer KW - Leaching KW - Assessment KW - Legislation KW - PFAS PY - 2024 AN - OPUS4-62057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kalbe, Ute A1 - Piechotta, Christian A1 - Bandow, Nicole T1 - Comparing PFAS analysis in batch leaching and column leaching tests N2 - Laboratory leaching tests are tools to assess the mobility of environmental contaminants released from granular materials. Comparative leaching tests were performed using four PFAS-contaminated soils whose concentration patterns of 10 selected perfluoroalkyl and polyfluoroalkyl substances (PFAS) differed due to the two types of contamination sources. This study aimed to evaluate the equivalence of two usual laboratory-scale leaching test procedures, batch and column percolation tests, at liquid-to-solid ratios (L/S) of 2 l/kg, which is the current practice within the German assessment framework, and 10 l/kg (relevant for some EU regulations such as the landfill directive). The differences between the replicates of leaching tests investigating PFAS were smaller for column percolation tests than for batch tests, probably mainly due to the greater sample size and the better representativeness of the sample portion analyzed. It was observed that batch tests overestimate the release of shorter-chain PFAS, whereby the effect was greater with carboxylic than with sulfonic acids. Currently, the limits of detection of analyses given by the DIN standard with regard to PFCA and PFSA in soils are partly not sufficient to detect very low contents, whereas the detection of selected PFCA and PFSA in eluates is more sensitive, in accordance with the available standards. This results in limitations when calculating mass balances. KW - PFAS KW - Leaching KW - Column percolation test KW - Batch test KW - Soil PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-618187 DO - https://doi.org/10.1007/s11356-024-35510-0 SN - 1614-7499 VL - 31 IS - 57 SP - 65233 EP - 65251 PB - Springer Science and Business Media LLC AN - OPUS4-61818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Franz-Georg A1 - Scholz, Philipp T1 - Assessment of the Long-Term Leaching Behavior of Incineration Bottom Ash: A Study of Two Waste Incinerators in Germany N2 - The long-term leaching behavior of incineration bottom ash (IBA) was studied with large-scale samples from two German waste incinerators with grate technology. The observation period was up to 281 days. The aging processes proceeded faster in the outdoor storage of the samples. The dominant factor in the leaching behavior is the pH, which starts at values above 12 and decreases to values below 10 (outdoors, <11 indoors). Most heavy metals exhibit minimum solubility in this pH range. The solubility of Sb depends on the prevailing Ca concentration, due to the formation of low-soluble Ca antimonate. The very low sulfate concentrations observed in the leaching tests with fresh IBA could be explained by the presence of ettringite. In the course of the aging reaction, ettringite is transformed into gypsum. The results from batch tests were compared with those from column tests, showing reasonable agreement. Leaching dynamics can be better followed with column tests. All results confirm that the use of IBA is possible under German law. KW - Aging KW - Incineration bottom ash KW - Leaching KW - Secondary building materials PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-591599 DO - https://doi.org/10.3390/app132413228 SN - 2076-3417 VL - 13 IS - 24 SP - 1 EP - 15 PB - MDPI AG CY - Basel AN - OPUS4-59159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Franz-Georg A1 - Kalbe, Ute T1 - Case Study on Secondary Building Materials for a Greener Economy N2 - Half of global material consumption involves mineral material. The circularity is still low so that the enhanced use of secondary building material is required to close loops. Three different secondary building materials are discussed based on exemplary research results: construction and demolition waste (C&D waste), soil-like material, and incineration bottom ash (IBA). Focus was placed on the environmental compatibility of the materials examined mainly by standardized leaching tests. C&D waste was investigated after a wet treatment using a jigging machine, and soil-like material and IBA were characterized with respect to their material composition. Their environmental compatibilities in particular were studied using standard leaching tests (batch tests and column tests). It was concluded that soil-like material can mostly be utilized even when the precautionary limit values set are exceeded by a factor of less than two. For C&D waste, the fine fraction below 2 mm and the content of brick material is problematic. IBA fulfills quality level “HMVA-2” following German regulations. Improved levels of utilization might be achievable with better treatment technologies. KW - Incineration bottom ash KW - Soil-like material KW - Leaching KW - Circular economy PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-576343 DO - https://doi.org/10.3390/app13106010 SN - 2076-3417 VL - 13 IS - 10 SP - 1 EP - 13 PB - MDPI CY - Basel AN - OPUS4-57634 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heisterkamp, I. A1 - Gartiser, S. A1 - Schoknecht, Ute A1 - Happel, O. A1 - Kalbe, Ute A1 - Kretzschmar, M. A1 - Ilvonen, O. T1 - Investigating the ecotoxicity of construction product eluates as multicomponent mixtures N2 - The release of hazardous compounds from construction products can harm human health and the environment. To improve the sustainability of construction materials, the leaching of substances from construction products and their potential environmental impact should be assessed. Twenty-seven construction products from different product groups were examined with a combination of standardized leaching tests (dynamic surface leaching test and percolation test) and biotests (algae, daphnia, fish egg, luminescent bacteria, umu and Ames fluctuation tests). To identify the released substances, extensive qualitative and quantitative chemical analyses were performed, including gas chromatographic and liquid chromatographic screening techniques. Results: Many of the tested eluates caused signifcant ecotoxic efects. Particularly high ecotoxicities were observed for grouts (lowest ineffective dilution (LID) up to 16384) and cork granules (LID up to 24578). The results of ecotoxicity tests allow the prioritization of the eluates that should be subjected to detailed chemical analyses. Organic screening by different methods and ranking the identifed substances based on recorded hazard classification is a suitable approach to identify the relevant toxic substances. Conclusions: Determining the ecotoxicity of eluates from construction products records the summary effect of all leachable substances. This instrument is especially useful for construction products of complex and largely unknown composition. The ecotoxicological and the chemical–analytical approach complement each other in an ideal way to characterize the potential hazard of eluates from construction products and to identify the environmentally hazardous components in these eluates. Our results confirm that the proposed harmonized methods for testing eluate toxicity are an adequate and applicable procedure to move toward a more sustainable way of building and to reduce toxic effects of construction products in their use phase in the environment. KW - Construction products KW - Building materials KW - Ecotoxicity KW - Biotests KW - Leaching KW - Eluates KW - Chemical analysis KW - Analytical screening techniques KW - Mixture toxicity PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-568864 DO - https://doi.org/10.1186/s12302-023-00711-w VL - 35 IS - 1 SP - 1 EP - 20 PB - Springer AN - OPUS4-56886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN ED - Simon, Franz-Georg ED - Kalbe, Ute T1 - Measurement of the Environmental Impact of Materials N2 - Throughout their life cycles—from production, usage, through to disposal—materials and products interact with the environment (water, soil, and air). At the same time, they are exposed to environmental influences and, through their emissions, have an impact on the environment, people, and health. Accelerated experimental testing processes can be used to predict the long-term environmental consequences of innovative products before these actually enter the environment. We are living in a material world. Building materials, geosynthetics, wooden toys, soil, nanomaterials, composites, wastes and more are research subjects examined by the authors of this book. The interactions of materials with the environment are manifold. Therefore, it is important to assess the environmental impact of these interactions. Some answers to how this task can be achieved are given in this Special Issue. KW - Leaching KW - Recycling KW - Emissions PY - 2023 UR - https://www.mdpi.com/books/book/6546 SN - 978-3-0365-5983-4 SN - 978-3-0365-5984-1 DO - https://doi.org/10.3390/books978-3-0365-5983-4 SP - 1 EP - 264 PB - MDPI CY - Basel ET - 1 AN - OPUS4-56770 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schoknecht, Ute A1 - Kalbe, Ute A1 - Heisterkamp, I. A1 - Kretzschmar, M. A1 - Gartiser, S. A1 - Happel, O. A1 - Ilvonen, O. T1 - Release of substances from joint grouts based on various binder types and their ecotoxic effects N2 - Background: The leaching of substances and the ecotoxic effects of eluates were studied for joint grouts that are based on various types of binders. Eight products, two of them containing either epoxy resin, polybutadiene or polyurethane binders, or modifed cement, were investigated using harmonized leaching tests for construction products in combination with ecotoxicity tests on algae, daphnia, luminescent bacteria, fish eggs and mutagenicity in accordance with CEN/TR 17105. In addition to basic parameters, such as pH, TOC, and inorganic components, organic substances in the eluates were analysed by gas and liquid chromatography in combination with mass spectrometry. Quantitative analyses in combination with ecotoxicity data on selected substances were used to deduce which substances cause the observed ecotoxic effects. Results: Different patterns of ecotoxic effects were observed in joint grouts with different binder types. The most ecotoxic effects were observed in epoxy resin-based products, followed by polybutadiene-based products. Fewer ecotoxic effects were observed in polyurethane-based products and modifed cements. Some of these showed no ecotoxicity. Some of the substances in the eluates were identified and related to ecotoxic effects. 4-Tert-butylphenol and amines probably contributed to the ecotoxic effects of at least one of the epoxy resin-based renders, whereas cobalt is assumed to contribute to the toxic effect on algae of one of the polybutadiene-based products. However, only some of the leached substances could be identifed, and only some of the ecotoxic effects can be explained by the available information on the composition of eluates and known ecotoxic profiles of the identified substances. Conclusions: Ecotoxicity tests on eluates from leaching tests indicate whether environmentally hazardous substances can be leached from construction products. Combined ecotoxicity tests and chemical analysis of eluates from EU-wide harmonized leaching tests for construction products can provide information on substances that cause these effects. This supports the identifcation and development of environmentally friendly construction products. This study confirmed that ecotoxicity tests in accordance with CEN/TR 17105 are a tool well-suited to support the implementation of the European Commission’s zero pollution vision for 2050 and to reduce pollution to levels no longer considered harmful to health and natural ecosystems. KW - Joint grouts KW - Leaching KW - Ecotoxixity PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-562392 DO - https://doi.org/10.1186/s12302-022-00686-0 SN - 2190-4707 VL - 34 IS - 1 SP - 1 EP - 16 PB - Springer Nature CY - Berlin AN - OPUS4-56239 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gentzmann, Marie A1 - Paul, Andrea A1 - Serrano, Juan A1 - Adam, Christian T1 - Understanding scandium leaching from bauxite residues of different geological backgrounds using statistical design of experiments N2 - The leaching behavior of scandium (Sc) from bauxite residues can differ significantly when residues of different geological backgrounds are compared. The mineralogy of the source rock and the physicochemical environment during bauxitization affect the association of Sc in the bauxite i.e., how Sc is distributed amongst different mineral phases and whether it is incorporated in and/or adsorbed onto those phases. The Sc association in the bauxite is in turn crucial for the resulting Sc association in the bauxite residue. In this study systematic leaching experiments were performed on three different bauxite residues using a statistical design of experiments approach. The three bauxite residues compared originated from processing of lateritic and karstic bauxites from Germany, Hungary, and Russia. The recovery of Sc and Fe was determined by ICP-OES measurements. Mineralogical changes were analyzed by X-ray-diffraction and subsequent Rietveld refinement. The effects of various parameters including temperature, acid type, acid concentration, liquid-to-solid ratio and residence time were studied. A response surface model was calculated for the selected case of citric acid leaching of Hungarian bauxite residue. The investigations showed that the type of bauxite residue has a strong influence. The easily leachable fraction of Sc can vary considerably between the types, reaching ~20–25% in German Bauxite residue and ~50% in Russian bauxite residue. Mineralogical investigations revealed that a major part of this fraction was released from secondary phases such as cancrinite and katoite formed during Bayer processing of the bauxite. The effect of temperature on Sc and Fe recovery is strong especially when citric acid is used. Based on the exponential relationship between temperature and Fe-recovery it was found to be particularly important for the selectivity of Sc over Fe. Optimization of the model for a maximum Sc recovery combined with a minimum Fe recovery yielded results of ~28% Sc recovery at <2% Fe recovery at a temperature of 60 ◦C, a citric acid normality of 1.8, and a liquid-to-solid ratio of 16 ml/g. Our study has shown that detailed knowledge about the Sc association and distribution in bauxite and bauxite residue is key to an efficient and selective leaching of Sc from bauxite residues. KW - Bauxite residue KW - Scandium KW - Leaching KW - Design of experiments KW - Red mud PY - 2022 DO - https://doi.org/10.1016/j.gexplo.2022.107041 SN - 0375-6742 VL - 2022 IS - 240 SP - 1 EP - 13 PB - Elsevier Science CY - Amsterdam AN - OPUS4-55531 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute A1 - Kalbe, Ute A1 - Happel, O. T1 - Combination of leaching tests with ecotoxicity and chemical analysis – Lessons learnt N2 - The presentation describes analytical methods to characterize eluates from leaching tests and identify organic substances in leachates. Chances to obtain complementary information from ecotoxtests and chemical analysis are discussed. T2 - Workshop: Ecotoxicological evaluation of construction products – test results, implementation in Guidance, Technical Standards and Ecolabelling CY - Online meeting DA - 21.03.2022 KW - Leaching KW - Ecotoxicity KW - Construction products PY - 2022 AN - OPUS4-55276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weiler, L. A1 - Pfingsten, J. A1 - Eickhoff, H. A1 - Geist, I. A1 - Hilbig, H. A1 - Hornig, U. A1 - Kalbe, Ute A1 - Krause, K. A1 - Kautetzky, D. A1 - Linnemann, V. A1 - Gschwendtner, M. A1 - Lohmann, D. A1 - Overeem-Bos, E. A1 - Schwerd, R. A1 - Vollpracht, A. T1 - Improving consistency at testing cementitious materials in the Dynamic Surface Leaching Test on the basis of the European technical specification CENTS 16637–2 – Results of a round robin test N2 - The environmental impact assessment of materials is usually based on laboratory tests, mostly in combination with models describing the longterm fate of the substances of interest in the targeted environmental compartment. Thus, laboratory tests are the fundamental link to achieve appropriate assessment conclusions which makes it essential to generate consistent results. This just as applies to the leaching of cementitious materials. In Europe, the leaching behavior of monolithic building materials is tested in the Dynamic Surface Leaching Test following the specification CEN/TS 16637–2. An interlaboratory comparison on European level regarding this technical specification showed relatively high intra- and interlaboratory variations for the tested materials (monolithic copper slag and cement stabilized coal fly ash). Therefore the German Committee for Structural Concrete (DAfStb) framed a guideline to specify additional testing conditions for cementitious materials. To assess the possible improvement by this guidelines measures, a round robin test with 11 participants from Germany and the Netherlands was conducted. This work aims to provide insight into the factors to be considered in the testing of alkaline materials, including sample preparation, and highlights crucial procedures and their manifestation in the results. All evaluated parameters showed improved results compared to the earlier round robin test. The relative standard deviations for repeatability (RSDr) and reproducibility (RSDR) of the elements calcium, barium, antimony, chromium, molybdenum and vanadium, which are the parameters evaluated in both round robin tests, were RSDr = 4%, 4%, 2%, 5%, 5%, and 5% respectively (4% in average) for this work, in comparison to the European round robin test with an average RSDr of 29% (17%, 17%, 20%, 40%, 36%, and 42%). The RSDR improved from 41% (30%, 36%, 29%, 57%, 40%, and 56%) to 14% (12%, 8%, 6%, 28%, 15%, and 12%). CO2 ingress during testing and the inaccuracy of eluate analytics for concentrations close to the determination limits were identified as the main sources of error. KW - Environmental assessment KW - Leaching KW - Heavy metals KW - Round robin test KW - Building Material PY - 2022 DO - https://doi.org/10.1016/j.jenvman.2022.114959 SN - 0301-4797 VL - 314 SP - 1 EP - 9 PB - Elsevier CY - Amsterdam AN - OPUS4-54647 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Franz-Georg A1 - Kalbe, Ute T1 - Measurement of the Environmental Impact of Materials N2 - This Special Issue, ‘Measurement of the Environmental Impact of Materials’, is focused on the impact that materials have on the environmental compartments of soil, water and air. Leaching and emission processes, including underlying mechanisms, are a recurring topic in most published articles in the present Special Issue. Contributions have come from three continents and numerous countries (USA, Germany, France, Latvia, Poland, Russia, Japan, Korea and Thailand) indicating the global dimension of the subject. KW - Leaching KW - Recycling KW - Nano-materials PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545099 DO - https://doi.org/10.3390/ma15062208 SN - 1996-1944 VL - 15 IS - 6 SP - 1 EP - 3 PB - MDPI CY - Basel AN - OPUS4-54509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Söftje, M. A1 - Weingartz, T. A1 - Plarre, Rüdiger A1 - Gjikaj, M. A1 - Namysko, J. C. A1 - Kaufmann, D. E. T1 - Surface Tuning of Wood via Covalent Modification of Its Lignocellulosic Biopolymers with Substituted BenzoatesA Study on Reactivity, Efficiency, and Durability N2 - Chemical modification of wood applying benzotriazolyl-activated carboxylic acids has proven to be a versatile method for the durable functionalization of its lignocellulosic biopolymers. Through this process, the material properties of Wood can be influenced and specifically optimized. To check the scope and limitations of this modification method, various benzamide derivatives with electron-withdrawing (EWG) or electron-donating (EDG) functional groups in different positions of the aromatic ring were synthesized and applied for covalent modification of Scots pine (Pinus sylvestris L.) sapwood in this study. The bonded amounts of substances (up to 2.20 mmol) were compared with the reactivity constants of the Hammett equation, revealing a significant correlation between the modification efficiency and the theoretical reactivity constants of the corresponding aromatic substitution pattern. The successful covalent attachment of the respective substituted benzamides was proven by attenuated total reflection infrared (ATR-IR) spectroscopy, while the stability of the newly formed ester bond was proven in a standardized leaching test. KW - Leaching KW - Wood Protection KW - Wood Modification PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-538932 DO - https://doi.org/10.1021/acsomega.1c04353 VL - 6 IS - 49 SP - 33542 EP - 33553 AN - OPUS4-53893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute A1 - Vogel, Christian A1 - Simon, Franz-Georg T1 - Antimony in incineration bottom ash – Leaching behavior and conclusions for treatment processes N2 - Antimony (Sb) is used in industrial products mainly as flame retardant in plastic material. Due to such additives in plastics, about a half of Sb ends up in municipal solid waste incineration at the end-of-life and consequently in relevant amounts in the generated bottom ash. In contact with water, the initial leachability is low, as antimonates form sparingly soluble compounds with Ca2+. Following the carbonation of the incineration bottom ash (IBA) during the proceeding ageing the pH in the leachates decreases. With decreasing concentration of Ca in the eluate the solution equilibrium changes and antimonates dissolve. In Germany it is intended to regulate Sb in IBA with the planned implementation of the so called Mantelverordnung (MantelVO, containing provisions on the utilisation of mineral waste) in the near future. The limit values set in the draft might be critical for IBA and therefore pose a risk for the utilisation of the mineral fraction of IBA in the well-established recycling routes. T2 - SUM 2020 – 5th Symposium on Urban Mining and Circular Economy CY - Online meeting DA - 18.11.2020 KW - Bottom ash KW - Leaching KW - Antimony PY - 2020 SP - 1 EP - 4 AN - OPUS4-51622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bandow, N. A1 - Aitken, M. D. A1 - Geburtig, Anja A1 - Kalbe, Ute A1 - Piechotta, Christian A1 - Schoknecht, Ute A1 - Simon, Franz-Georg A1 - Stephan, Ina T1 - Using Environmental Simulations to Test the Release of Hazardous Substances from Polymer-Based Products: Are Realism and Pragmatism Mutually Exclusive Objectives? N2 - The potential release of hazardous substances from polymer-based products is currently in the focus of environmental policy. Environmental simulations are applied to expose such products to selected aging conditions and to investigate release processes. Commonly applied aging exposure types such as solar and UV radiation in combination with water contact, corrosive gases, and soil contact as well as expected general effects on polymers and additional ingredients of polymer-based products are described. The release of substances is based on mass-transfer processes to the material surfaces. Experimental approaches to investigate transport processes that are caused by water contact are presented. For tailoring the tests, relevant aging exposure types and release quantification methods must be combined appropriately. Several studies on the release of hazardous substances such as metals, polyaromatic hydrocarbons, flame retardants, antioxidants, and carbon nanotubes from polymers are summarized exemplarily. Differences between natural and artificial exposure tests are discussed and demonstrated for the release of flame retardants from several polymers and for biocides from paints. Requirements and limitations to apply results from short-term artificial environmental exposure tests to predict long-term environmental behavior of polymers are presented. KW - Environmental simulations KW - Polymer-based products KW - Artificial weathering KW - Degradation KW - Leaching KW - Soil contact PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-509310 DO - https://doi.org/10.3390/ma13122709 SN - 1996-1944 VL - 13 IS - 12 SP - Paper 2709, 22 PB - MDPI CY - Basel, Switzerland AN - OPUS4-50931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kalbe, Ute A1 - Simon, Franz-Georg T1 - Potential use of incineration bottom ash in construction – Evaluation of the environmental impact N2 - Knowledge of the long-term leaching behavior of potentially harmful substances is crucial for the assessment of the environmental compatibility of reusing municipal solid-waste incineration bottom ash (MSWI BA) in construction, i.e., as a road base layer. BA fractions obtained from wet-processing aiming at the improvement of environmental quality were used to investigate the mobility of relevant substances. Eluates from laboratory-scaled leaching procedures (column percolation and lysimeters) were analyzed to learn about the long-term release of substances. Unsaturated conditions and artificial rainwater (AR) were used in the lysimeter tests to simulate field conditions. In addition, batch test eluates were generated at usual liquid-to-solid ratios (L/S) for compliance testing purposes. A variety of cations and anions was measured in the eluates. The wet treatment reduces the leaching of chloride and particularly sulfate by more than 60%. The release of typical contaminants for the treated MSWI BA such as the heavy metals Cu and Cr was well below 1% in the conducted leaching tests. An increase in the Sb concentration observed in the lysimeter experiments starting at L/S 0.75 L/kg and in the column experiment at L/S 4 L/kg is assumed to be related to decreasing concentrations of Ca and thus to the dissolution of sparingly soluble calcium antimonate. The same leaching mechanism applies with V, but the concentration levels observed are less critical regarding relevant limit values. However, on the long term the behavior of Sb could be problematic for the application of MSWI BA in construction. KW - MSWI bottom ash KW - Leaching KW - Batch tests KW - Lysimeter KW - Antimony PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-508421 DO - https://doi.org/10.1007/s12649-020-01086-2 SN - 1877-2641 VL - 11 IS - 12 SP - 7055 EP - 7065 PB - Springer AN - OPUS4-50842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vogel, Christian T1 - Leaching behavior of Antimony in MSWI bottom ash N2 - Bottom ash (BA) from municipal solid waste incineration (MSWI) contains harmful substances such as heavy metals, chloride and sulfate which are mobilized in contact with water. Standardized leaching tests are used to measure the extent of mobilization. It is known that fresh bottom ash displays elevated concentrations of various heavy metals such as lead or zinc due to the formation of hydroxo complexes as a result of high pH values of 12 and above. Storage of BA is accompanied by ageing processes, mainly the reaction of CaO and Ca(OH)2 with CO2 leading to lower pH values in contact with water around 11. Usually heavy metals concentrations are minimum at these conditions. Knowledge of the long-term leaching behavior of potentially harmful substances is crucial for the assessment of the environmental compatibility of reusing municipal solid-waste incineration bottom ash (MSWI BA) in construction, i.e., as a road base layer. BA fractions obtained from wet-processing aiming at the improvement of environmental quality were used to investigate the mobility of relevant substances. Eluates from laboratory-scaled leaching procedures (column percolation and lysimeters) were analyzed to learn about the long-term release of substances. Unsaturated conditions and artificial rainwater were used in the lysimeter tests to simulate field conditions. In addition, batch test eluates were generated at usual liquid-to-solid ratios (L/S) for compliance testing purposes. A variety of cations and anions was measured in the eluates. The wet treatment reduces the leaching of chloride and particularly sulfate by more than 60%. The release of typical contaminants for the treated MSWI BA such as the heavy metals Cu and Cr was well below 1% in the conducted leaching tests. An increase in the Sb concentration was observed in the lysimeter experiments starting at L/S 0.75 L/kg and in the column experiment at L/S 4 L/kg is assumed to be related to decreasing concentrations of Ca and thus to the dissolution of sparingly soluble calcium antimonate. The same leaching mechanism applies with V, but the concentration levels observed are less critical regarding relevant limit values. However, on the long term the behavior of Sb could be problematic for the application of MSWI BA as secondary building material. T2 - MINEA Final Conference CY - Bologna, Italy DA - 20.02.2020 KW - Antimony KW - Bottom ash KW - Leaching KW - Solubility PY - 2020 AN - OPUS4-50450 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Uhlig, S. A1 - Colson, B. A1 - Schoknecht, Ute T1 - A mathematical approach for the analysis of data obtained from the monitoring of biocides leached from treated materials exposed to outdoor conditions N2 - Leaching processes are responsible for the release of biocides from treated materials into the environment. Adequate modeling of emission processes is required in order to predict emission values in the framework of the risk assessment of biocidal products intended for long-term service life. Regression approaches have been applied to data obtained from the long-term monitoring of biocide emissions in experiments involving semi-field conditions. Due to the complex interaction of different underlying mechanisms such as water and biocide diffusion and desorption, however, these attempts have proven to be of limited usefulness e at least, for the available biocide emission data. It seems that the behavior of the biocide emission curve depends to a considerable extent on whichever underlying mechanism is slowest at a given point in time, thus limiting the amount of biocide available for release. Building on results obtained in the past few years, the authors propose a criterion for determining which mechanism controls the leaching process at a given point in time based on the slope of the log-log emission curve. In addition, a first-order approximation of this slope value is presented which displays advantages both in terms of computability and interpretability. Finally, an algorithm for the determination of breakpoints in the slope of the log-log emission curve is presented for the demarcation of phases within which one mechanism acts as a limiting factor. KW - Biocides KW - Leaching KW - Weathering KW - Mathematical analysis PY - 2019 DO - https://doi.org/10.1016/j.chemosphere.2019.04.102 SN - 0045-6535 SN - 1879-1298 VL - 228 SP - 271 EP - 277 PB - Elsevier AN - OPUS4-47886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heisterkamp, I. A1 - Gartiser, S. A1 - Kalbe, Ute A1 - Bandow, N. A1 - Gloßmann, A. T1 - Assessment of leachates from reactive fire-retardant coatings by chemical analysis and ecotoxicity testing N2 - The environmental compatibility of reactive fire-retardant coatings (intumescent paints) was investigated by a combination of leaching and ecotoxicological tests. Three representative fire-retardant coating systems were tested using two leaching procedures: “Horizontal Dynamic Surface Leaching Test” (DSLT) and the “Intermittent Immersion Test” (IIT). All eluate fractions (8 for DSLT and 9 for IIT) were analyzed for pH, conductivity, concentration of total organic carbon and selected anions und cations. Additionally, a GC-MS screening of selected fractions was conducted for identification of organic compounds. Eluate fractions 1 + 2 and fraction 7 of the DSLT were analyzed in four ecotoxicological tests (algae, daphnia, fish egg, luminescent bacteria) and in one genotoxicity test (umu). Concentration of most analytes was rather low or below limit of detection for many eluates. Analytes detected in eluates of all three products are Zn, Ba, SO4(2−) and PO4(3−). Release patterns do not indicate a general trend: some compounds show maximum release in the first fractions while for others the maximum was observed in later test stages. Ecotoxic effects in eluates were found, which were higher in the eluate fraction 7 (maximum lowest ineffective dilution for luminescent bacteria (LIDL) 256) than in the eluate fraction 1 + 2 (maximum LIDL = 24). The sensitivity of the test systems was very different with highest effects for luminescent bacteria, followed by algae and daphnia and without effects in the fish egg test and umu test. A biotest battery for the comprehensive assessment is therefore advisable. KW - Construction products regulation (CPR) KW - Intumescent coating KW - Fire-retardant paint KW - Leaching KW - Ecotoxicity PY - 2019 DO - https://doi.org/10.1016/j.chemosphere.2019.03.044 SN - 0045-6535 SN - 1879-1298 VL - 226 SP - 85 EP - 93 PB - Elsevier AN - OPUS4-47696 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hlavacek, Petr T1 - Behaviour of reinforced alkali-activated fly ash mortars under leaching conditions N2 - Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet. One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solu¬tion composition were monitored. Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for pro¬tec¬tion of steel reinforcement in alkali-activated fly ash mortars and concretes. T2 - International Conference on Sustainable Materials, Systems and Structures (SMSS 2019) CY - Rovinj, Croatia DA - 20.03.2019 KW - Alkali-activated materials KW - Leaching KW - Steel corrosion PY - 2019 AN - OPUS4-47621 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hlavacek, Petr A1 - Reinemann, Steffi A1 - Gluth, Gregor A1 - Ebell, Gino A1 - Mietz, Jürgen ED - Serdar, M. ED - Stirmer, N. ED - Provis, J. T1 - Behaviour of reinforced alkali-activated fly ash mortars under leaching conditions N2 - Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet. One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solution composition were monitored. Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for protection of steel reinforcement in alkali-activated fly ash mortars and concretes. T2 - International Conference on Sustainable Materials, Systems and Structures (SMSS 2019) CY - Rovinj, Croatia DA - 20.03.2019 KW - Alkali-activated materials KW - Steel corrosion KW - Leaching PY - 2019 SN - 978-2-35158-223-7 VL - 1 SP - 118 EP - 124 PB - RILEM Publications CY - Paris AN - OPUS4-47585 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hlavacek, Petr T1 - Steel reinforcement corrosion in alkali-activated fly ash mortars N2 - Corrosion of steel rebars in concrete presents one of the main deterioration mechanisms limiting service life of the reinforced structures. The corrosion is accompanied by an expansion of the corrosion products causing high pressures, concrete cracking and finally spalling of a cover layer. Critical chloride concentration, loss of alkalinity and modeling of the steel corrosion are in researchers' spotlight for decades, however reinforcement corrosion in alkali activated materials is insufficiently described and understood yet. In this work, the steel reinforcement corrosion in alkali-activated fly ash mortars is investigated in terms of electrochemical behaviour of the reinforced mortars exposed to aggressive environments such as leaching, carbonation and chloride ingress. A selected geopolymer mixture based on hard coal fly ash activated with sodium hydroxide and sodium silicate solutions is used for the steel reinforcement-corrosion experiments. The formation of passive layer on the steel rebars is observed after approx. two weeks of hardening at laboratory temperature. However, alternative heat-treatment at 80°C for several hours leads to immediate formation of the passive layer as well as to a faster strength gain (80 MPa after 24h at 80°C). Chloride-induced corrosion, leaching and carbonation resistance of the alkali activated fly ash-based concrete is studied, where leaching in deionized water or carbonation under natural conditions (~0.04 % CO2) for 300 days did not lead to corrosion of the embedded steel. On the other hand, accelerated carbonation under 100 % CO2 atmosphere lead to depassivation within two weeks. T2 - Alkali Activated Materials and Geopolymers CY - Tomar, Portugal DA - 27.05.2018 KW - Alkali-activation KW - Reinforcement corrosion KW - Carbonation KW - Chloride attack KW - Leaching PY - 2018 AN - OPUS4-47446 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bandow, Nicole A1 - Finkel, M. A1 - Grathwohl, P. A1 - Kalbe, Ute T1 - Influence of flow rate and particle size on local equilibrium in column percolation tests using crushed masonry N2 - Column leaching tests are frequently used and accepted for investigation of release of hazardous substances from solid materials. Independent of differences due to the field of application or national regulations, column tests assume that local equilibrium is established in the experiment which facilitates transfer of results to field conditions. In the process of harmonization and standardization within Europe the question on the influence of flow rate and grain size distribution on the local equilibrium was raised. Thus, a set of experiments using two different masonry materials with varying grain size distribution and flow rate were conducted including stop/flow experiments. Results are compared to a numerical model which takes intraparticle pore diffusion-controlled release of Mo and V into the percolating water into account. Due to the relatively high intraparticle porosity of the materials (24–29%) data and model indicate that initially equilibrium-state conditions prevail followed by rapidly decreasing concentrations. The model fits data for Mo and V reasonably well; however, after the initial decline of concentrations (at L/S > 2) extended tailing is observed especially of elements occurring as oxides, which is not captured by the model. KW - Leaching KW - Porosity KW - Stop/flow experiments model KW - Intraparticle diffusion KW - Vanadium KW - Molybdenum PY - 2019 DO - https://doi.org/10.1007/s10163-019-00827-3 SN - 1438-4957 SN - 1611-8227 VL - 21 IS - 3 SP - 642 EP - 651 PB - Springer Japan AN - OPUS4-47265 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maresca, A. A1 - Krüger, O. A1 - Herzel, Hannes A1 - Adam, Christian A1 - Kalbe, Ute A1 - Astrup, T. F. T1 - Influence of wood ash pre-treatment on leaching behaviour, liming and fertilising potential N2 - In Denmark, increasing amounts of woody biomass are being used for the production of renewable energy, resulting in more wood ashes being generated. While these materials have been mainly landfilled, wood ashes may also be utilised for fertilizing and liming purposes on top of soils. Pre-treatments involving hardening or granulation may be carried out prior to soil application. In this study, two Danish wood ash samples were hardened and/or granulated. Lab-hardening induced rapid changes in the shape of the acid neutralisation capacity curve of the ashes. Up-flow column tests, assuming local equilibrium conditions, were employed to investigate the leaching from pre-treated ashes. Granules and loose ashes demonstrated similar leaching behaviours, indicating that similar geochemical processes were governing their leaching. In comparison with untreated fresh ashes, the hardened ashes demonstrated reduced leaching of Ca, Ba, Pb and Zn with concentration levels generally below or close to the analytical limits of quantification; to the contrary, the leaching of As, P, Sb, Si, V and Mg was enhanced in the hardened ashes. The release of alkalinity was reduced by hardening. In general, all granules were barely breakable by finger-pinching and they could withstand one month of continuous leaching, preserving their overall shape. The solubility of phosphorous in neutral ammonium citrate indicated that about 30–51% of the total P content in the ash samples was released, suggesting that the ashes could be potentially valuable as P-fertiliser if applied onto soil. KW - Wood ash KW - Phoshpor availability KW - Leaching KW - Forest soils PY - 2019 DO - https://doi.org/10.1016/j.wasman.2018.11.003 SN - 0956-053X VL - 83 SP - 113 EP - 122 PB - Elsevier AN - OPUS4-46583 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gluth, Gregor A1 - Hlavacek, Petr A1 - Reinemann, Steffi A1 - Ebell, Gino A1 - Mietz, Jürgen ED - Alexander, M.G. ED - Beushausen, H. ED - Dehn, F. ED - Moyo, P. T1 - Leaching, carbonation and chloride ingress in reinforced alkali-activated fly ash mortars N2 - Alkali-activated fly ash mortars were studied with regard to durability-relevant transport coefficients and the electrochemical behaviour of embedded carbon steel bars on exposure of the mortars to leaching, carbonation and chloride penetration environments. The transport coefficients differed considerably between different formulations, being lowest for a mortar with BFS addition, but still acceptable for one of the purely fly ash-based mortars. Leaching over a period of ~300 days in de-ionized water did not lead to observable corrosion of the embedded steel, as shown by the electrochemical data and visual inspection of the steel. Exposure to 100 % CO2 atmosphere caused steel depassivation within approx. two weeks; in addition, indications of a deterioration of the mortar were observed. The results are discussed in the context of the different reaction products expected in high- and low-Ca alkali-activated binders, and the alterations caused by leaching and carbonation. T2 - International Conference on Concrete Repair, Rehabilitation and Retrofitting (ICCRRR 2018) CY - Cape Town, South Africa DA - 19.11.2018 KW - Alkali-activated materials KW - Steel corrosion KW - Leaching KW - Carbonation PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-464381 DO - https://doi.org/10.1051/matecconf/201819902025 VL - 199 SP - Article Number 02025 PB - EDP Sciences AN - OPUS4-46438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg A1 - Kalbe, Ute A1 - Bandow, Nicole T1 - Potential use of incineration bottom ash in construction – Evaluation of environmental impact N2 - The results from a long-term lysimeter experiment with incineration bottom ash irrigated with artificial rain are reported. Whereas chloride concentration dropped significantly, the release of antimony increased during the course of the experiment as a result of aging processes. T2 - 10th International Conference on the Environmental and Technical Implications of Construction with Alternative Materials, WASCON 2018 CY - Tampere, Finland DA - 06.06.2018 KW - Leaching KW - MSWI Bottom Ash KW - Lysimeter KW - Antimony PY - 2018 SN - 978-951-758-631-3 SN - 0356-9403 SP - 108 EP - 110 AN - OPUS4-45416 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute T1 - Potential use of incineration bottom ash in construction – Evaluation of environmental impact N2 - Around 5 million tonnes of MSWI bottom ash (BA) are generated per year in Germany. The incineration itself serves for metals as a concentrating and cleaning process. However, due to the almost exclusive wet extraction out of the furnace chamber the various metals are integrated in a heterogeneous and instable matrix. The metal recovery is therefore still a challenge relating the recovery rate and the purity, respectively. With state of the art treatment trains in Germany around 7.7% of ferrous metals and 1.3% of non-ferrous metals can be recovered out of MSWI BA. Large quantities of the mineral fraction are reused for sub-base material in road construction. A three month ageing period has been established as the common practice of further treatment of bottom ash before reuse applications. In the course of this aging the pH value of bottom ash decreases and contaminants are immobilized by processes like carbonation, hydration and oxidation. In particular leaching of heavy metals may be reduced to environmentally acceptable levels. However, the aging results in fixing of other valuable resources such as metals. Two laboratory scale lysimeters (30 cm in diameter) are being operated for more than three years aiming at the investigation of the long-term leaching behavior of a 0.25/45 mm mineral material obtained by treatment of MSWI bottom ash directly after incineration by a wet processing technology. Artificial rainwater is used as leachant (pH ≈ 6, ingredients NO32-, Cl-, SO42-, Na+, K+, Ca2+, Mg2+). The lysimeters are irrigated related to an average annual precipitation rate of 600 mm/a leading to a liquid to solid ratio (L/S) of about 0.7 per year of operation. Lysimeter tests are more adequate to simulate field scenarios and long-term leaching behavior in contrast to laboratory column tests particularly due to the unsaturated conditions and realistic contact time with the leachant. In comparison to the leaching of bottom ash (aged for 3 month and non-treated) in column tests the chloride and sulfate leaching in the lysimeters was reduced as a consequence of the previous wet processing. The sulfate release kept almost constant limited by CaSO4 solubility up to an L/S of about 0.7 l/kg. The chloride concentrations dropped quickly, starting from 7300 mg/l, and are now at an almost constant level of 50 mg/l which is significantly above the chloride concentration in the leachant. After an initial decrease of the pH from about 10.4 to 8 at L/S of 0.2 l/kg, the pH increased again and leveled out around 9.8 up to L/S 2.2 l/kg. At an L/S of about 2.5 l/kg now, Cr, Cu are still released. The Cu and Cr concentrations in the leachates were about 760 µg/l and 90 µg/l respectively at the beginning. For both metals the concentration decreased to about 35 µg/l now. The Mo concentrations dropped steadily from 1300 to 250 µg/l, whereas V and Sb concentrations increased in the course of the tests. Fe and Mn are not detectable anymore. More results of this experimental study will be presented and discussed with a special focus on elements forming oxyanions. T2 - 10th International Conference on the Environmental and Technical Implications of Construction with Alternative Materials, WASCON 2018 CY - Tampere, Finland DA - 06.06.2018 KW - Lysimeter, Antimony KW - MSWI bottom ash KW - Leaching PY - 2018 AN - OPUS4-45263 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bandow, Nicole T1 - Leachiing tests - a useful tool for the environmental impact assessment of construction products? N2 - Construction products and waste materials used for construction can be in contact with the environment and may release potential harmful compounds. Information on the total content of these substances in the product is not sufficient to assess its envrionmental impact since it does not consider realistic exposure conditions.The impact of these compounds is often assessed by using the total content in the product. This estimation lacks realistic exposure conditions. Concerning the pathway to soil and groundwater by contact with rain or seepage water leaching tests, which were developed and standardized by the European Committee for Standardization, are available. While for secondary construction products and waste this investigation of the leaching behaviour is standard procedure and is already part of regulation in Germany (draft ordinance on reuse of mineral waste) and within Europe (landfill directive) the release from primary construction products got in the focus more recently. Several monitoring studies found unexpected high concentrations of substances used as herbicides and fungicides in surface water and stormwater originating from urban areas. As some of these compounds are even banned for the use in agricultural applications in Europe alternative sources as roof materials and façade coatings exposed to rain were suggested. Further field and laboratory tests confirmed construction products as sources of these substances in water. The aim of this presentation is to show exemplary results of existing leaching methods and underline the strength and weaknesses of the test system with selected examples from our work. We especially draw the attention to the research which is still needed to close the gap between the results of leaching experiments and the subsequent risk assessment of the products. T2 - SETAC Europe CY - Rome, Italy DA - 13.05.2018 KW - Leaching KW - DSLT KW - Construction products PY - 2018 AN - OPUS4-44949 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute T1 - Tools for the characterization of secondary raw materials - status of leaching test application N2 - Leaching tests are used as tools for the assessment of environmental compatibility of granular waste materials with potential for reuse. The presentation gives an overview on available leaching tests, their field of application and relation to legislation. Furthermore robustness testing to elaborate optimized test conditions as well as performance characteristics from validation studies by BAM are addressed. T2 - Travelling Conference CY - Ho-Chi-Ming City, Vietnam DA - 01.02.2018 KW - Leaching KW - Risk assessment KW - Robustness studies PY - 2018 AN - OPUS4-44724 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute T1 - Tools for the characterization of secondary raw materials - status of leaching test application N2 - Leaching tests are used as tools for the assessment of environmental compatibility of granular waste materials with potential for reuse. The presentation gives an overview on available leaching tests, their field of application and relation to legislation. Furthermore robustness testing to elaborate optimized test conditions as well as performance characteristics from validation studies by BAM are addressed. T2 - Travelling Conference CY - Perth, Australia DA - 06.02.2018 KW - Leaching KW - Risk assessment KW - Robustness studies PY - 2018 AN - OPUS4-44723 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute T1 - Leaching behavior of soil-like materials, granular waste and construction products - Selected research results N2 - The presentation will summarize German regulations on the reuse of contaminated soil-like materials (excavated soil, dredged sediments, mining residues, urban soils etc.). Leaching tests as available tools for the assessment of environmental compatibility are discussed. First results of a currently running project on the monitoring of such materials with a focus on PAH are presented. A study on the leaching behavior of MSWI bottom ash fractions produced by an innovative wet processing technology using laboratory scale lysimeters will be presented in a second part. The application of scrap tire granules as infill for synthetic turf and within elastic support layers of outdoor sports surfaces leads to the release of contaminants and transfer to soil and groundwater. The development of a special leaching procedure for synthetic sports surfaces and subsequent modelling of contaminant transfer to groundwater is presented in a third part of the presentation. T2 - The International Workshop for Environmental Hazardous Impact Assessment of Recycling Resources CY - Seoul, Korea DA - 31.03.2017 KW - Contaminant transfer KW - Leaching KW - Waste KW - Construction products PY - 2017 AN - OPUS4-43012 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute T1 - Leaching and ecotoxicity tests as tools for the assessment of environmental compatibility of granular materials N2 - Leaching and ecotoxicity tests are used as tools for the assessment of environmental compatibility of granular waste materials with potential for reuse. The contribution gives an overview on the development of test conditions of leaching tests as well as research results on their robustness and performance. Examples of research results include the investigation of MSWI bottom ash, steel slag, contaminated soil, mining waste and other waste materials reused as construction products. The background of application of ecotoxicological tests in Germany is given comprising the selection of tests, advantages and limitations and available guidelines. T2 - The International Seminar for Technical Issues of Recycling CY - Nier, Incheon, Korea DA - 30.03.2017 KW - Ecotoxicological tests KW - Leaching KW - Waste recyling KW - Environmental compatibility PY - 2017 AN - OPUS4-43008 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute T1 - Leaching of PFC from soils contaminated with PFC of different origin N2 - Leaching tests are fundamental tools for the assessment of groundwater impact by contaminated soils concerning the soil-groundwater pathway. Such procedures are supposed to serve as the basis for a reliable leachate prognosis. They can be applied to determine the short and long term leaching behaviour as well as the source term of contaminated soils. For this purpose two types of leaching procedures have been validated in Germany for the examination of the leaching behaviour of frequently occurring organic substances (DIN 19528 - column test and DIN 19529 - batch test). A liquid-to-solid ratio (L/S) of 2 L/kg and 10 L/kg) is the basis for the risk assessment which is implemented in different German regulations. The equivalence of test results for both tests for the same material under investigation has been investigated for a variety of pollutants in order to assess their reliability in compliance testing. However, for emerging pollutants there is hardly data available on this issue. Leaching tests on soils contaminated with emerging pollutants such as PFC (Perfluorinated Surfactants) are currently coming more into consideration due to the increasing detection of contaminated sites. Therefore, two soils were investigated in this study from different contamination source (paper sludge containing compost and fire distinguishing foam) using both leaching tests and both liquid-to-solid ratios. The leachability of the various perfluorinated compounds in relation to their content in solid matter was considered. Furthermore the eluate pre-treatment prior analysis (in particular liquid/solid separation step needed for batch tests) has been taken into account. The comparability of the results from batch and column is dependent on the solubility of the various compounds, on the L/S and on the turbidity in the eluates. T2 - EGU General Assembly 2017 CY - Vienna, Austria DA - 23.04.2017 KW - Soil KW - PFC KW - Leaching PY - 2017 AN - OPUS4-43000 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalbe, Ute T1 - Comparison of column and batch tests for assessing leachability of PFC from soils N2 - Leaching tests are fundamental tools for the assessment of groundwater impact by contaminated soils concerning the soil-groundwater pathway. Such procedures are supposed to serve as the basis for a reliable leachate prognosis. They can be applied to determine the short and long term leaching behaviour as well as the source term of contaminated soils. For this purpose two types of leaching procedures have been validated in Germany for the examination of the leaching behaviour of frequently occurring organic substances (DIN 19528 - column test and DIN 19529 - batch test). A liquid-to-solid ratio (L/S) of 2 L/kg and 10 L/kg) is the basis for the risk assessment which is implemented in different German regulations. The equivalence of test results for both tests for the same material under investigation has been investigated for a variety of pollutants in order to assess their reliability in compliance testing. However, for emerging pollutants there is hardly data available on this issue. Leaching tests on soils contaminated with emerging pollutants such as PFC (Perfluorinated Surfactants) are currently coming more into consideration due to the increasing detection of contaminated sites. Therefore, two soils were investigated in this study from different contamination source (paper sludge containing compost and fire distinguishing foam) using both leaching tests and both liquid-to-solid ratios. The leachability of the various perfluorinated compounds in relation to their content in solid matter was considered. Furthermore the eluate pre-treatment prior analysis (in particular liquid/solid separation step needed for batch tests) has been taken into account. The comparability of the results from batch and column is dependent on the solubility of the various compounds, on the L/S and on the turbidity in the eluates. T2 - AquaConSoil 2017 CY - Lyon, France DA - 26.06.2017 KW - Soil KW - PFC KW - Leaching PY - 2017 AN - OPUS4-42997 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yasutaka, T. A1 - Imoto, Y. A1 - Kurosawa, A. A1 - Someya, M. A1 - Higashino, K. A1 - Kalbe, Ute A1 - Sakanakura, H. T1 - Effects of colloidal particles on the results and reproducibility of batch leaching tests for heavy metal-contaminated soil N2 - A simple batch test leaching procedure is used in many countries, as a compliance test, to evaluate the leaching of mainly inorganic substances from soil. However, agitating certain types of soil and then passing the solution through a membrane filter with 0.45-µm pores yields filtrates that have been colored by the colloidal particles. These colloids might affect the results of the inorganic substances obtained in the batch tests. In this study, we evaluated the effects of colloidal particles on the results and the reproducibility of batch tests on contaminated soil using different agitation methods and membrane filters with different pore sizes. The leaching behaviors of As, Pb, Se, F and Cl from three types of soil were studied. The As and Pb concentrations in the leachates of some types of soil were clearly affected by the amount of colloidal particles with a diameter of 0.10–0.45 µm and by the agitation method used. This was probably because As and Pb were present mainly in the particulate form in the leachate that had been passed through a membrane filter with 0.45-µm pores. This is not the case for every type of soil. The results of batch leaching tests showed that not only dissolved but also colloidal forms with a diameter of 0.10–0.45 µm might be included and that the existence of colloidal particles in the leachate decreases the batch leaching test reproducibility. KW - Leaching KW - Contaminated soil KW - Heavy metals KW - Colloids PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-429940 UR - https://www.sciencedirect.com/science/article/pii/S0038080617301166#! DO - https://doi.org/10.1016/j.sandf.2017.08.014 SN - 0038-0806 VL - 57 IS - 5 SP - 861 EP - 871 PB - Elsevier B.V. AN - OPUS4-42994 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wachtendorf, Volker A1 - Kalbe, Ute A1 - Krüger, O. A1 - Bandow, Nicole ED - Brown, R. ED - Gedde, U.W. ED - Hedenqvist, M.S. T1 - Influence of weathering on the leaching behaviour of zinc and PAH from synthetic sports surfaces N2 - Synthetic materials used for outdoor sports grounds consist of a mix of inorganic, organic and polymeric compounds that show ageing due to weathering and a complex leaching behaviour by percolation of rainwater, which can limit its lifetime. Additionally, weathering exposure induces degradation processes in the polymers, which leads to the formation of new surfaces allowing water to access additional reservoirs of leachable compounds. A laboratory test comprising artificial weathering, ozonisation and subsequent leaching was developed to investigate this behaviour in a reproducible and controllable way. The experiments showed a general decline of Zn, polycyclic aromatic hydrocarbons (PAH) and total organic carbon (TOC) concentrations after an initial increase. Within this general trend, the course of concentration over exposure duration is very specific for individual sample materials and the analyte under investigation. The results indicate that weathering and degradation behaviour cannot be predicted from initial material conditions. Thus, weathering experiments are recommended to fill this gap of knowledge. KW - Athletic tracks KW - Artificial turf KW - Ageing KW - Artificial weathering KW - Polymer degradation KW - Rubber granules KW - Leaching KW - Contamination PY - 2017 DO - https://doi.org/10.1016/j.polymertesting.2017.09.021 SN - 0142-9418 SN - 1873-2348 VL - 63 IS - October SP - 621 EP - 631 PB - Elsevier Ltd. CY - Amsterdam, The Netherlands AN - OPUS4-42205 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Neuhold, S. T1 - Effect of Leaching on the Surface Mineralogy of Steel Slags N2 - Electric arc furnace (EAF)slag is a complex multi-Phase system comparable to natural rock mineralogy, which can be used as a secondary rawmaterial. To ensure the environmental safety of EAF slags,regarding the mobility of contaminants,it is necessary to understand the Controlling mechanisms for the leaching of heavy metals such as chromium and Vanadium in this complex system. T2 - Goldschmidt Conference 2017 CY - Paris, France DA - 13.08.2017 KW - EAF slag KW - Leaching PY - 2017 AN - OPUS4-41853 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bandow, Nicole T1 - How to consider bioavailability in the assessment of construction products N2 - Construction products are complex materials and contain a large number of different chemicals, which might be released to the environment during usage. Depending on the compound and on the matrix only a small portion is transferred to environment and therefore a risk assessment should be based on the available portion. Concerning the pathway to soil and groundwater by contact with rain or seepage water leaching tests were developed and standardized by CEN to determine the release potential of construction products. Chemical analysis in the eluates can be combined with eco-toxicological testing. In this presentation an overview about existing leaching methods is given using selected examples of our work. We especially draw the attention to research which is still needed to close the gap between the results of leaching experiments and the subsequent risk assessment of the products. The eluates of 15 paints for outdoor use were used for a screening of organic compounds and the concentration of cations and anions were determined. Concerning the inorganic constituents only a small number of elements were present with concentrations higher than the limit of detection. Thus, leaching of potential hazardous chemicals is probably of higher concern. Several glycol ethers, polyalkylene glycols and some surfactants and coalescing agents have been identified. Among these only the latter are classified as hazardous to aquatic organisms. The identification of the organic compounds is a time consuming and labor-intensive step due to the high number of chemicals produced and used. Using eco-toxicity tests provides information on the environmental risk without the need for of chemical identification of all compounds. The screening of a set of construction products shows that only a part of eluates causes adverse effects in the test and that such screening can be used as a first step in the assessment of construction products. If this kind of testing is included in the evaluation concept an in depth chemical analysis is only needed for products showing adverse effects. Determination of the eluate concentration after leaching enables to determine the potential release to the environment and to focus on the available fraction. However, limit values or other concepts to use this information in risk assessment are still missing. T2 - SETAC Europe CY - Brussels, Belgium DA - 07.05.2017 KW - Bioavailability KW - Leaching KW - Ecotoxicity KW - Standardization KW - Construction products PY - 2017 AN - OPUS4-40210 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schoknecht, Ute A1 - Mathies, Helena A1 - Wegner, R. A1 - Uhlig, S A1 - Baldauf, H. A1 - Colson, B T1 - Leaching of biocides from organic coatings N2 - Biocide leaching was investigated for acrylate and vinyl acetate based coatings containing biocides either as liquid formulations or microcapsules. Laboratory and field tests indicate similar relations of results on carbendazim, diuron, terbutryn and OIT from different coatings in laboratory and field experiments. Emissions were higher in EN 16105 laboratory tests than from vertically installed test specimens exposed to weathering, and slower for microencapsulated biocides. Competing processes that cause losses of active substances can occur in both tests, but to a higher degree in field experiments. Emission curves related to runoff water were similar in repeated field experiments. Relative humidity, temperature and global radiation were identified as meteorological factors that affect leaching by complex interaction besides the amount of driving rain. KW - Leaching KW - Biozid KW - Beschichtung PY - 2016 SN - 1230-3321 IS - 4 SP - 3 EP - 9 AN - OPUS4-38909 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute A1 - Mathies, Helena A1 - Wegner, R. A1 - Uhlig, S. A1 - Baldauf, H. A1 - Colson, B. T1 - Leaching of biocides from organic coatings N2 - Biocide leaching was investigated for acrylate and vinyl acetate based coatings containing biocides either as liquid formulations or microcapsules. Laboratory and field tests indicate similar relations of results on carbendazim, diuron, terbutryn and OIT from different coatings in laboratory and field experiments. Emissions were higher in EN 16105 laboratory tests than from vertically installed test specimens exposed to weathering, and slower for microencapsulated biocides. Competing processes that cause losses of active substances can occur in both tests, but to a higher degree in field experiments. Emission curves related to runoff water were similar in repeated field experiments. Relative humidity, temperature and global radiation were identified as meteorological factors that affect leaching by complex interaction besides the amount of driving rain. T2 - 12th International Conference 'Advances in Coatings Technology ACT´16' CY - Sosnowiec, Poland DA - 08.11.2016 KW - Biocide KW - Leaching KW - Coating PY - 2016 SN - 978‒83‒63555‒50‒4 SP - Paper 51, 1 EP - 10 AN - OPUS4-38236 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute T1 - Leaching of biocides from organic coatings N2 - Biocide leaching was investigated for acrylate and polymer based coatings containing biocides either as liquid formulations or microcapsules. Laboratory and field tests indicate similar relations of results on carbendazim, diuron, terbutryn and OIT from different coatings in laboratory and field experiments. Emissions were higher in EN 16105 laboratory tests than from vertically installed test specimens exposed to weathering, and slower for microencapsulated biocides. Competing processes that cause losses of active substances can occur in both tests, but to a higher degree in field experiments. Emission curves related to runoff water were similar in repeated field experiments. Relative humidity, temperature and global radiation were identified as meteorological factors that affect leaching by complex interaction besides the amount of driving rain. T2 - Advances in Coatings Technology CY - Sosnowiec, Poland DA - 08.11.2016 KW - Biocide KW - Coating KW - Leaching PY - 2016 AN - OPUS4-38234 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schoknecht, Ute A1 - Mathies, Helena A1 - Wegner, R. T1 - Biocide leaching during field experiments on treated articles N2 - Background: Biocidal products can be sources of active substances in surface waters caused by weathering of treated articles. Marketing and use of biocidal products can be limited according to the European Biocidal Products Regulation if unacceptable risks to the environment are expected. Leaching of active substances from treated articles was observed in field experiments to obtain information on leaching processes and investigate the suitability of a proposed test method. Results: Leaching under weathering conditions proceeds discontinuously and tends to decrease with duration of exposure. It mainly depends on the availability of water, but is also controlled by transport processes within the materials and stability of the observed substances. Runoff amount proved to be a suitable basis to compare results from different experiments. Concentrations of substances are higher in runoff collected from vertical surfaces compared to horizontal ones, whereas the leached amounts per surface area are higher from horizontal surfaces. Gaps in mass balances indicate that additional processes such as degradation and evaporation may be relevant to the fate of active substances in treated articles. Leached amounts of substances were considerably higher when the materials were exposed to intermittent water contact under laboratory conditions as compared to weathering of vertically exposed surfaces. Conclusions: Experiences from the field experiments were used to define parameters of a procedure that is now provided to fulfil requirements of the Biocidal Products Regulation. The experiments confirmed that the amount of water which is in contact with exposed surfaces is the crucial parameter determining leaching of substances. KW - Biozidprodukte KW - Farben KW - Textil KW - Auswaschung KW - Freilandtest KW - Biocidal products KW - Paints KW - Textile KW - Leaching KW - Field test PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-354090 DO - https://doi.org/10.1186/s12302-016-0074-9 VL - 28 IS - 6 SP - 1 EP - 10 PB - Springer CY - SpringerOpen AN - OPUS4-35409 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schoknecht, Ute A1 - Kalbe, Ute A1 - Van Zomeren, A. A1 - Hjelmar, O. T1 - Laboratory leaching tests on treated wood according to different harmonised test procedures N2 - -Background- Laboratory leaching tests on treated wood were performed during a European robustness study in the framework of the validation of a tank leaching test procedure that has been proposed for construction products in order to determine the potential release of dangerous substances which can be transferred to soil and groundwater. The release of substances has to be determined also for materials treated with biocidal products according to the requirements of the European Biocidal Products Regulation. A similar leaching test procedure was already harmonised for treated wood for this purpose. Both test procedures were applied in parallel to wood treated with the same preservative to investigate whether the results of these tests can replace each other. Additional experiments were performed to further investigate unexpected effects of L/A ratio on leaching of copper and duration of storage of treated test specimens. -Results- Both procedures generate similar results concerning cumulative emissions of tebuconazole, copper, dissolved organic carbon and total nitrogen. The emission rates with time are in comparable ranges for both leaching protocols. Emissions of copper increased with decreasing L/A ratios. Strong correlation of copper concentrations and dissolved organic carbon as well as total nitrogen concentrations in eluates indicates that this observation is caused by co-elution of copper with organic substances. Duration of storage of treated test specimens affected emissions for the investigated wood preservative. -Conclusions- Based on these findings, results from both test procedures can be used to describe leaching characteristics and avoid double testing of treated wood to fulfil the requirements of the European regulations for either biocides or construction products. Leaching of substances from treated wood is a complex process that depends on its chemical composition and ageing processes. KW - Construction products KW - Biocidal product KW - Emission KW - Leaching KW - Tank leaching test KW - Treated wood KW - European regulation PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-317320 UR - http://www.enveurope.com/content/26/1/25 SN - 2190-4715 SN - 2190-4707 VL - 26 SP - 25, 1 EP - 10 PB - Springer CY - Berlin ; Heidelberg AN - OPUS4-31732 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kalbe, Ute A1 - Krüger, Oliver A1 - Wachtendorf, Volker A1 - Berger, Wolfgang A1 - Hally, S. T1 - Development of leaching procedures for synthetic turf systems containing scrap tyre granules N2 - Scrap tyres are widely reused in the form of granules as infill materials or component of sub-base layers in construction of sporting grounds such as synthetic turf areas and athletic track surfaces. The recycled rubber may contain organic and inorganic pollutants due to the presence of vulcanisation catalysts, stabilisers and other additives which can be released into soil and groundwater in the case of outdoor sports facilities. In order to evaluate the amount of potentially mobile pollutants, leaching tests can be employed. This study aimed particularly at the investigation of the feasibility of column tests using complete synthetic surface flooring or turf system assemblies. The release of zinc and polycyclic aromatic hydrocarbons (PAH) leached from components of sports surfaces containing recycled rubber granules was considered. Additionally, batch tests on coated and uncoated styrene butadiene rubber (SBR) granules aged by artificial weathering were performed to indicate its possible influence on the leaching behaviour of zinc and PAH. The chosen approach of column tests simulating typical complete synthetic sports surface installations has been proven to be feasible and robust. The time-dependent leaching behaviour and interactions between single components can be evaluated by column tests. Zinc was the most relevant contaminant in the eluates and its leachability was enhanced after accelerated ageing by artificial weathering. Leachable PAH were found in relatively low but well detectable amounts which increase by ageing as well. KW - Waste rubber KW - SBR KW - Artificial turf KW - Leaching KW - behaviour KW - Column test KW - Batch test KW - Weathering PY - 2013 DO - https://doi.org/10.1007/s12649-013-9248-5 SN - 1877-2641 SN - 1877-265X VL - 4 IS - 4 SP - 745 EP - 757 PB - Springer Science + Business Media CY - Dordrecht AN - OPUS4-29454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maszkowska, J. A1 - Kolodziejska, M. A1 - Bialk-Bielinska, A. A1 - Mrozik, W. A1 - Kumirska, J. A1 - Stepnowski, P. A1 - Palavinskas, R. A1 - Krüger, Oliver A1 - Kalbe, Ute T1 - Column and batch tests of sulfonamide leaching from different types of soil N2 - Sulfonamides (SAs) and their metabolites present severe hazards to human health and the environment, mainly because of antibiotic resistance. Knowledge of their bioavailability, including their sorption to soils and their impact on the soil-groundwater pathway, is crucial to their risk assessment. Laboratory batch and column leaching tests are important tools for determining the release potential of contaminants from soil or waste materials. Batch and column tests were carried out with soils differing in particle size distribution, organic matter content and pH, each spiked with sulfonamides (sulfadimethoxine (SDM), sulfaguanidine (SGD), sulfisoxazole (SX)). In order to test the applicability of leaching tests to polar contaminants batch and column tests were also compared. In the column tests, release was found to depend on the properties of both soil and sulfonamides. The fastest release was observed for coarse-grained soil with the smallest organic matter content (MS soil; 100% decrease in concentration until liquid-to-solid ratio (L/S) of 0.9 L kg-1 for all SAs). The slowest release was established for sulfadimethoxine (24.5% decrease in concentration until L/S 1.22 L kg-1). The results of the batch and column tests were comparable to a large extent, with slightly higher concentrations being obtained in the column test experiments of fine-grained soils with a high organic matter content. KW - Sulfonamides KW - Leaching KW - Column test KW - Batch test KW - Soil PY - 2013 DO - https://doi.org/10.1016/j.jhazmat.2013.05.053 SN - 0304-3894 VL - 260 SP - 468 EP - 474 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-28855 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Schoknecht, Ute A1 - Töpfer, Antje A1 - Uhlig, S. A1 - Baldauf, H. T1 - Characterisation of leaching of biocidal active substances of main group 2 'preservatives' from different materials under weathering conditions (Project No. (FKZ) 3708 65 404, Report No. (UBA-FB) 001641/E) N2 - Anwendungen von Bioziden in Materialien für Außenanwendungen sind mögliche Quellen für Biozide in Umweltkompartimenten infolge von witterungsbedingten Auswaschprozessen. Im Bericht werden Leachingprozesse und -parameter als auch Methoden zu deren Untersuchung unter Labor- und Freilandversuchsbedingungen beschrieben. Vorteile und Grenzen der verschiedenen Herangehensweisen zur Untersuchung von Leachingprozessen werden diskutiert. Standardisierte Auswaschtests sowie in der Fachliteratur publizierte Auswaschexperimente werden zusammenfassend dargestellt. Es wird beschrieben, wie Leachingdaten gemäß Technischem Leitfaden zur Biozidprodukten-Richtlinie 98/8/EG für eine Risikobewertung genutzt werden. Ein alternativer Ansatz zur mathematischen Modellierung von Leachingtest-Daten wurde erprobt und wird im Bericht erläutert. Potentiell lassen sich mit dem vorgeschlagenen Ansatz bestimmte gegenwärtig auftretende Schwierigkeiten bei der Risikobewertung umgehen. Applications of biocides in outdoor materials are potential sources of biocides in environmental compartments due to leaching processes under weathering conditions. Leaching processes and parameters as well as methods to investigate leaching processes under laboratory and semi-field conditons are described in the report. Benefits and limitations of different test approaches are discussed. Standardised leaching tests as well as leaching experiments reported in scientific literature are listed. The application of leaching data for risk assessments according to the Technical Guidance Documents for the Biocidal Products Directive (98/8/EC) is described. An alternative approach for mathematical modelling of leaching data was tested and is Explained in the report. Certain difficulties that currently appear during risk assessments may be circumvented by the proposed approach. KW - Test procedures KW - Biocide KW - EU biocidal products directive 98/8/EC KW - Material preservatives KW - In-can preservatives KW - Film preservatives KW - Fibre KW - Leather KW - Rubber and polymerised materials preservatives KW - Masonry preservatives KW - Weathering KW - Leaching KW - Mathematical modelling KW - Risk assessment KW - Biozid KW - EU Biozidproduktenrichtlinie 98/8/EG KW - Materialschutzmittel KW - Topf-Konservierungsmittel KW - Beschichtungsschutzmittel KW - Schutzmittel für Fasern KW - Leder KW - Gummi und polymerisierte Materialien KW - Schutzmittel für Mauerwerk KW - Bewitterung KW - Auswaschung KW - Testverfahren KW - Laborversuche KW - Freilandversuche KW - Mathematische Modellierung KW - Risikobewertung PY - 2012 UR - http://www.umweltbundesamt.de/publikationen/characterisation-of-leaching-of-biocidal-active SN - 1862-4804 SN - 0722-186X IS - 62 SP - 1 EP - 118 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-26520 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lupsea, M.O. A1 - Mathies, Helena A1 - Schoknecht, Ute A1 - Tiruta-Barna, L. A1 - Schiopu, N. T1 - Leaching from new generation treated wood: a chemical approach N2 - Leaching of biocides from construction products is currently a research topic receiving attention from the European regulation authorities (CEN/TC 351). In this paper we have focused on the leaching behaviour of CBA (copper-borateazoles) treated Pinus sylvestris. To better define the chemistry of the leaching phenomena, two leaching tests (a static equilibrium test and a dynamic surface leaching test) have been carried out on untreated and treated wood, which offered more information about how the leaching of biocides interferes with other substances released from the wood structure. Eluates, in liquid and lyophilised form, were further analyzed by analytical methods. Organic (tebuconazole) and inorganic (Cu, B) biocides were quantified and several organic compounds have been identified (e.g. carboxylic acids, phenols, amines, etc.). Also, the total amount of phenols and of carboxylic groups was determined. Results on inorganic compounds are in accordance with previous studies made on treated wood. Furthermore, organic carbon, tebuconazole and other organic compounds’ behaviour was extensively investigated. This study aims to complete existing leaching data and to help developing a chemical model for several biocides in wood, including Cu, B and tebuconazole. Keywords: leaching, CBA treated wood, biocide, organic compounds. T2 - 1st International conference on environmental and economic impact on sustainable development, incorporating envrionmental economics, toxikology and brownfields CY - New Forest, UK DA - 02.07.2012 KW - Leaching KW - CBA treated wood KW - Biocide KW - Organic compounds PY - 2012 DO - https://doi.org/10.2495/EID120461 SN - 1743-3541 SN - 1746-448X VL - 162 IS - Environmental Impact SP - 529 EP - 540 PB - WIT Press CY - Southampton [u.a.] AN - OPUS4-26262 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Oliver A1 - Christoph, Gabriele A1 - Kalbe, Ute A1 - Berger, Wolfgang T1 - Comparison of stir bar sorptive extraction (SBSE) and liquid-liquid extraction (LLE) for the analysis of polycyclic aromatic hydrocarbons (PAH) in complex aqueous matrices N2 - Stir bar sorptive extraction (SBSE) is an equilibrium extraction method used amongst others for the analysis of polycyclic aromatic hydrocarbons (PAH) in aqueous samples. We compared SBSE to liquid–liquid extraction (LLE) for aqueous eluates obtained from batch and column tests of PAH contaminated soils to check whether SBSE might be considered as an alternative sample preparation method. We used soils with different particle size distribution, organic matter content, and resulting eluate turbidity to test the sample preparation methods on eluates with matrices of varying complexity. Furthermore, we studied the influence of diluted organic matter (DOM) on the PAH sorption process to the polymer coating of the stir bar during SBSE. In the majority of cases, we found higher PAH concentrations (up to 288%) with SBSE than with LLE. The turbidity correlates with the difference in PAH results, i.e. the greater the turbidity in the eluate, the more PAH we found with SBSE compared to LLE. We observed no similar trend regarding the amount of total organic carbon (TOC). The presence of DOM in the eluate seems to hamper the SBSE slightly, the PAH recovery varied between 82 and 104%. KW - Stir bar sorptive extraction KW - Liquid-liquid extraction KW - Leaching KW - Batch test KW - Column test KW - Complex aqueous matrix PY - 2011 DO - https://doi.org/10.1016/j.talanta.2011.06.035 SN - 0039-9140 VL - 85 IS - 3 SP - 1428 EP - 1434 PB - Elsevier CY - Amsterdam AN - OPUS4-24031 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krüger, Oliver A1 - Kalbe, Ute A1 - Berger, Wolfgang A1 - Simon, Franz-Georg A1 - Lopez Meza, Sarynna T1 - Leaching experiments on the release of heavy metals and PAH from soil and waste materials N2 - Leaching tests are fundamental tools for the assessment of long-term impact of contaminated waste materials on the soil-groundwater pathway. Experiments were carried out in the framework of standardization and validation of column percolation and batch test procedures, in particular concerning the stipulation of the experimental setup. The colloid release of column and batch experiments was compared and the influence of different column filling heights (12.5–50 cm) on the release of polycyclic aromatic hydrocarbons (PAH) from soil was studied, as well as the effect of varying contact times (2.5–16 h) on the release of chromium from construction and demolition (C&D) waste and municipal solid waste incineration (MSWI) bottom ash. The results indicate that filtration of the eluate, which is required for batch tests, does not always allow the simulation of the actual colloid amount in soil pore water. Medium column heights four times the inner diameter of the column seemed to provide reasonable equilibrium adjustment conditions and avoid major biodegradation. The release of chromium was only marginally affected by the contact time, varied between 0.115 and 0.150 mg/kg for demolition waste eluate at a liquid-to-solid ratio of approximately 5 L/kg. KW - Column tests KW - Batch tests KW - Waste materials KW - Leaching KW - Standardization PY - 2012 DO - https://doi.org/10.1016/j.jhazmat.2011.02.016 SN - 0304-3894 VL - 207-208 SP - 51 EP - 55 PB - Elsevier CY - Amsterdam AN - OPUS4-24030 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bagda, E. A1 - Borho, N. A1 - Schoknecht, Ute T1 - Measuring the release - Leaching of biocides from facade coatings N2 - Facades are attacked by algae and fungi during weathering, impairing the surfaces visually and leading to long-term damage. To prevent this, appropriate biocides are used in facade coatings. These can be washed out during weathering, especially when it rains. A standardized laboratory procedure to determine the amount of biocides released under practical conditions has been developed and is accessible as European Standard FprEN 16105. KW - Leaching KW - Fassadenbeschichtungen KW - prEN 16105 KW - Testparameter KW - INS-Projekt PY - 2011 SN - 0930-3847 VL - 06 SP - 33 EP - 37 PB - Vincentz CY - Hannover AN - OPUS4-23829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -