TY - CONF A1 - Giese, Marcel A1 - Schröder, Nina A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Kadoke, Daniel A1 - Kruse, Julius T1 - Local strain behaviour in cross weld tensile specimens of microalloyed high strength steels using digital image correlation N2 - This study specifically examines the role of the microalloying element titanium (Ti) in achieving the desired mechanical properties of quenched and tempered high-strength fine-grain structural steels, with a nominal yield strength of ≥ 690 MPa. Current specifications limit chemical composition only by defining upper thresholds, but even minor variations in Ti content can substantially alter mechanical properties. Consequently, accurate prediction of weldability and welded joint integrity becomes challenging, as variations in Ti lead to distinct microstructural characteristics, potentially causing undesirable softening or hardening effects in the heat-affected zone (HAZ). To address these complexities, two distinct titanium concentrations were systematically investigated for the first time using specially developed laboratory-cast alloys. Both alloying configurations were based on the standard S690QL grade, with consistent chemical composition and heat treatment parameters maintained across the samples. For the weldability analysis, three-layer welds were executed using gas metal arc welding (GMAW), allowing for the identification of critical microstructural zones within the HAZ that exhibit significant softening or hardening. The influence of the softened HAZ region on failure mechanisms was assessed through transverse tensile tests. Digital image correlation (DIC) was employed to capture local strain variations across different HAZ regions in situ. With a custom-developed mirror system, local strains in microstructural zones on both the top and bottom surfaces of the weld were recorded simultaneously. This setup enabled a detailed analysis of how weld seam geometry (e.g., V-groove configuration) influences strain gradients. Additionally, the investigation of localized deformation provided insights into how variations in Ti content within the HAZ affect global strain, fracture constriction, fracture location, and overall fracture behavior. T2 - MPA Seminar 2024 Materials Processes Applications CY - Stuttgart, Germany DA - 08.10.2024 KW - HAZ-Softening KW - Digital Image Correlation KW - Cross weld tensile test PY - 2024 AN - OPUS4-61488 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Dittmann, Florian A1 - Kromm, Arne A1 - Varfolomeev, Igor A1 - Kannengiesser, Thomas T1 - Improvement of Fatigue Resistance through the Application of a Low-Transformation-Temperature Welding Consumable N2 - Low transformation temperature (LTT) welding consumables are an innovative approach to reduce tensile residual stress in weld seams and the surrounding heat affected zone (HAZ). The reduced tensile stress can lead to an improvement in fatigue strength of welded components. LTT alloys are characterized by a chemical composition which reduce the martensite start temperature (Ms) close to room temperature. This article focuses on a hybrid use of LTT filler metals, where the LTT filler is applied as an additional layer to conventional welds on fatigue-critical spots. Conventional gas metal arc welded longitudinal stiffeners are used as specimens. At the face ends of the stiffeners, a second LTT layer was added with various modifications in weld shapes. These different shapes were achieved by changing the welding parameters such as welding speed and offset to the first layer. These samples were used to analyze shape, dilution, resulting Ms, residual stress and fatigue strength. The dilatometer verified Ms and dilution did not change significant, although the area of the 2nd LTT weld seam was varying clear with each modification. However, the weld modification had a significant effect on the residual stress state and the fatigue strength. The X-ray determined residual stress in the HAZ became lower when the weld toe of the LTT layer was further away from the stiffener. All samples with LTT weld exhibit significantly higher fatigue strength values than conventionally single and double-layer welded samples. The lower the residual stress at weld toe, the higher the fatigue strength. The results show that on the one hand LTT filler metals increase the fatigue strength, and on the other hand the impact of LTT fillers materials is not restricted to the dilution and Ms, the shape of the weld seam must also be considered. T2 - 4th international Conference on Advanced Joining Processes AJP CY - Combria, Portugal DA - 16.10.2025 KW - Low transformation temperature (LTT) KW - Residual stress reduction KW - Fatigue strength KW - Longitudenal stiffener PY - 2025 AN - OPUS4-65090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Influence of the weld geometry on the residual stress reduction using low transformation temperature welding consumables N2 - Low transformation temperature (LTT) welding consumables offer an innovative approach to increase the fatigue strength of welded high-strength steel structures. LTT welding consumables are characterized by a martensitic phase transformation near ambient temperature, which generates compressive residual stresses in the weld and heat affected zone (HAZ). The aim is to achieve a weld geometry, which generate high compressive residual stresses at the fatigue crack critical weld toe. Longitudinal stiffeners were gas metal arc welded using a conventional welding consumable; the base material was a high strength steel S700M. A chromium-nickel alloyed LTT consumable was deposit subsequently just on front sides of the stiffeners. Different welding parameters led to varying cross sections of the weld. The residual stresses were determined using X-ray diffraction (XRD) in the crack critical HAZ. When using only the conventional, the HAZ is characterized by high tensile residual stresses. The additional application of the LTT alloy leads to a significant reduction of the tensile residual stresses. Depending on the weld geometry, even compressive residual stresses can be observed at the weld toe T2 - ECRS 2024 CY - Prague, Czech Republic DA - 03.06.2024 KW - LTT (Low Transformation Temperature) KW - Residual stress reduction KW - Fatigue PY - 2024 AN - OPUS4-60305 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Eigenspannungsabbau mittels LTT – Schweißzusätzen unter Berücksichtigung der Nahtgeometrie N2 - Low Transformation Temperature (LTT)-Schweißzusätze sind ein innovativer Ansatz, um Eigenspannungen in Schweißnähten zu reduzieren. Dieser Vortrag behandelt neben den Einfluss der LTT-Schweißzusätze auch deren Naht-Ausführungen. Die unterschiedlichen LTT-Nahtgeometrien haben einen signifikanten Einfluss auf den Eigenspannungsabbau in der Schweißnaht und der Wärmeeinflusszone (WEZ). T2 - SFB 1120 Summer School CY - Steinfeld, Germany DA - 11.06.2024 KW - LTT (Low Transformation Temperature) KW - Eigenspannungen KW - Ermüdungsfestigkeit KW - Aufmischung PY - 2024 AN - OPUS4-60306 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Dittmann, Florian A1 - Varfolomeev, Igor T1 - Untersuchung der Ermüdungsfestigkeit von LTT-geschweißten Längssteifen mit variierender Nahtausführungen N2 - Low Transformation Temperature (LTT) Schweißzusätze erzeugen während der Abkühlung Druckeigenspannungen in die Schweißnaht und Wärmeeinflusszone durch eine Volumenexpansion, wodurch die Ermüdungsfestigkeit erhöht werden kann. Um das Potential dieser neuartigen Schweißzusätze besser zu quantifizieren, wurden konventionelle Längssteifen als Probenkörper verwendet, welche an den Stirnseiten mit einer LTT-Zusatznaht geschweißt wurden. Durch Variation der Schweißparameter konnten unterschiedliche Nahtformen realisiert werden. Es konnte, je nach Nahtausführung, eine Erhöhung der Ermüdungsfestigkeit bei 2 Millionen Lastwechsel von 64 MPa bis 100 MPa in Gegensatz zu konventionellen Proben festgestellt werden. Somit sind LTT-Zusätze grundsätzlich geeignet, um die Ermüdungsfestigkeit zu erhöhen. T2 - Frühjahrssitzung 2025 des Fachausschusses Eigenspannungen der AWT CY - Karlsruhe, Germany DA - 07.04.2025 KW - LTT (Low Transformation Temperature) KW - Eigenspannungen KW - Ermüdungsfestigkeit KW - Aufmischung PY - 2025 AN - OPUS4-62930 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Dittmann, Florian A1 - Varfolomeev, Igor T1 - Wechselwirkung zwischen Nahtgestaltung und Ermüdungsfestigkeit in LTT-geschweißten Längssteifen N2 - Schweißzusätze mit niedriger Martensitstarttemperatur (Low Transformation Temperature, LTT) induzieren während der Abkühlphase infolge einer volumeninduzierten Martensitumwandlung Druckeigenspannungen in der Schweißnaht sowie in der angrenzenden Wärmeeinflusszone (WEZ). Diese Spannungen können zu einer signifikanten Erhöhung der Ermüdungsfestigkeit führen. Zur quantitativen Bewertung des Potenzials dieser innovativen Werkstoffe wurden konventionelle Längssteifen als Versuchsproben herangezogen, bei denen an den Stirnseiten Schweißnähte unter Verwendung von LTT-Zusatzwerkstoffen appliziert wurden. Durch gezielte Variation der Schweißparameter konnten unterschiedliche Nahtgeometrien realisiert werden. In Abhängigkeit von der Nahtausführung zeigte sich bei einer Belastungszahl von 2 Millionen Zyklen eine Steigerung der Ermüdungsfestigkeit im Bereich von 64 MPa bis 100 MPa im Vergleich zu Referenzproben mit herkömmlichen Schweißzusätzen. Die Ergebnisse belegen, dass der Einsatz von LTT-Schweißzusätzen grundsätzlich geeignet ist, die Ermüdungsfestigkeit geschweißter Strukturen zu verbessern. T2 - Din Sitzung: Gemeinschaftsarbeitsausschuss NAS/NMP, Zerstörende Prüfung von Schweißverbindungen CY - Online meeting DA - 20.03.2025 KW - LTT (Low Transformation Temperature) KW - Eigenspannungen KW - Ermüdungsfestigkeit KW - high-strength steels PY - 2025 AN - OPUS4-62929 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Dittmann, Florian A1 - Varfolomeev, Igor T1 - Effect of weld design on fatigue strength of welded components using LTT filler materials N2 - Low transformation temperature (LTT) filler metals are an innovative approach to reduce tensile residual stress in weld seams and the surrounding heat affected zone (HAZ). The reduced tensile stress leads to an improvement in the fatigue strength of welded components. LTT filler metals are characterized by a reduced martensite start temperature (Ms), which is close to room temperature because of their chemical composition. This paper focuses on the hybrid use of LTT filler metals, where the LTT filler is applied as an additional layer to conventional welds on fatigue-critical spots. Conventional gas metal arc welded longitudinal stiffeners are used as specimens and at the face ends of the stiffeners, a second LTT layer was added with various weld modifications. These modifications were achieved by changing the welding parameters such as welding speed and offset to the first layer. These samples were used to analyze shape, dilution and resulting Ms, residual stress and fatigue strength. The dilution and dilatometer verified Ms did not change significant, although the surface of the 2nd LTT weld seam was varying clear with each modification. However, the weld modification had a significant effect on the residual stress state and the fatigue strength. The X-ray determined residual stress in the HAZ became lower when the weld toe of the LTT layer was further away from the stiffener. The Fatigue strength is clearly dependent on the residual stress state. The lower the residual stress at weld toe, the higher the fatigue strength. All samples with LTT weld exhibit significantly higher fatigue strength values than conventionally single and double-layer welded samples. The results show that on the one hand LTT filler metals increase the fatigue strength, and on the other hand the impact of LTT fillers materials is not restricted to the dilution and Ms, the shape of the weld seam must also be considered. T2 - IIW Intermediate Meeting CII CY - Trollhättan, Sweden DA - 10.03.2025 KW - LTT (Low Transformation Temperature) KW - Residual stress reduction KW - Fatigue strength KW - High-strength steels KW - Welding PY - 2025 AN - OPUS4-62708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Reichel, Levin A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Modern welding processes for optimising repair welds on high strength offshore steels N2 - The successful energy transition in Germany will require offshore wind turbines with outputs >10 MW in the future. To achieve these high outputs, turbines far from coast are required with large subsea jacket structures (30 m up to 50 m) and tall towers (up to 200 m). High-strength steels with a yield strength up to 500 MPa and wall thicknesses up to 150 mm are increasingly being used for these structures. This plac-es high demands on welding manufacturing, especially for high-strength offshore steels. During the manu-facturing process detected defects by NDT require localized repair of welds by gouging and rewelding. Due to a lack of investigations, there are no repair concepts and information in standards and guidelines, par-ticularly for high-strength thick plate joints made of high-strength offshore steels. However, these are ur-gently needed to enable manufacturers, especially SMEs, to carry out safe and economical repairs. There-fore, BAM started the FOSTA project P1629 (IGF 01IF22746N) to investigate the stress-optimized repair (local gouging and welding) of high-strength thick plate joints made of offshore grades in the yield strength range off 355 to 460 MPa and similar weld metal with controlled high-performance GMAW pro-cesses and optimized narrow gouging grooves. The experimental analyses take into account the complex interaction of process, material, and design-related influences on the formation of weld induced stresses and the special microstructure of high-strength fine-grain structural steels. Welding-related material degra-dation and crack-critical residual tensile stresses need to be avoided to ensure high component safety and performance. A reduction in residual stress in the presence of high restraint conditions can be achieved by adapted heat control (if no disassembly measures are possible). The repair process involves manual thermal gouging, which allows the groove configuration to be modi-fied. Modern welding processes using high frequency arc control provide deep root penetration and focused energy input capable of welding narrow seams. A comparison was made between the traditional weld con-figuration with a wide 45° groove and transition arc welding and a narrow 30° groove with modern welding process. Even in the case of free shrinkage specimens, the narrow groove weld exhibits a significant reduc-tion of residual stresses, cf. Figure 1, especially in the HAZ and toward the adjacent base material. This can be attributed to the lower weld metal volume needed and the reduction of heat input per layer due to the controlled arc process. For the purposes of this comparison, the same weld seam build-up (but different number of layers) has been applied to both seam configurations. Note that in industrial application (manu-al welding), the wider groove would be welded with several off-center weld beads with conventional weld-ing process. In this analysis this would cause asymmetric effects regarding the residual stress state, diffi-cult to compare to each other. Component-related welding experiments on special testing equipment, adapted process and heat control concepts along with variable groove configurations will be developed and recommendations for guidelines elaborated. This is the prerequisite for fully utilizing the strength potential of high-strength steels and making a valuable contribution to the energy transition in Germany, especially for steel-processing SMEs. T2 - IIW Intermediate Meeting CII CY - Trollhättan, Sweden DA - 10.03.2025 KW - Repair welding KW - Gouging KW - Residual stress KW - Offshore wind turbines KW - High-strength steels PY - 2025 AN - OPUS4-62743 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Spannungen beim Schweißen von Bauteilen N2 - Der Vortrag gibt einen Überblick über das Phänomen der Schweißeigenspannungen. Es wird auf die Bedeutung und Entstehungsursachen eingegangen. Mit besonderem Fokus auf die Eigenspannungen beim Schweißen von Komponenten werden Messmöglichkeiten und Anwendungsbeispiele vorgestellt. T2 - Jahresmitgliederversammlung DVS Bezirksverbandes Berlin CY - Berlin, Germany DA - 24.04.2024 KW - Eigenspannungen PY - 2024 AN - OPUS4-59944 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Möglichkeiten zur Optimierung von schweißbedingten Beanspruchungen durch Einsatz von LTT-Zusatzwerkstoffen N2 - Der Vortrag gibt einen Überblick zum Thema Low Transformation Temperature (LTT) Zusatzwerkstoffe. Es wird gezeigt, wie mit einem Experiment unter Nutzung von Sychrotronstrahlung das Phänomen der Umwandlungsplastizität untersucht werden kann. T2 - 12. Vollversammlung des SFB 1120: Summer School 2024 CY - Steinfeld (Kall), Germany DA - 11.06.2024 KW - Eigenspannungen KW - LTT-Zusatzwerkstoffe KW - Hochfester Stahl PY - 2024 AN - OPUS4-60259 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Best practice: How to work with a mobile diffractometer N2 - Beginning with a general overview about resdiual stress determination by X-ray diffraction, the presentation is focussing on some does and dont's when working with a portable diffractometer. T2 - European Conference on Residual Stresses 11 - Tutorial 1: Residual stresses in additive manufacturing CY - Prague, Czech Republic DA - 03.06.2024 KW - Residual stress KW - X-ray diffraction PY - 2024 AN - OPUS4-60287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Bewertung von Zusatzwerkstoffen zur Eigenspannungskontrolle in Schweißnähten mittels Röntgen- und Neutronenbeugung T2 - Frühjahrssitzung 2014 des AWT Fachausschusses Eigenspannungen CY - Herzogenaurach, Germany DA - 2014-04-29 PY - 2014 AN - OPUS4-30699 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Residual stress of repair welds in high strength low alloy steel T2 - IIW Annual Assembly - SC II-A CY - Seoul, South Korea DA - 2014-07-14 PY - 2014 AN - OPUS4-31094 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Evaluation of weld filler alloying concepts for residual stress engineering by means of Neutron and X-ray diffraction T2 - European Conference on Residual Stresses ECRS 9 CY - Troyes, France DA - 2014-07-07 PY - 2014 AN - OPUS4-31095 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Möglichkeiten zur Optimierung von Schweißeigenspannungen durch Einsatz tieftemperaturumwandelnder Schweißzusatzwerkstoffe N2 - Die Erkenntnis, dass die Phasenumwandlung bei der Schweißeigenspannungsentstehung hochfester Stähle eine bedeutende Rolle spielt, gibt es bereits seit langer Zeit. Bisher existierten jedoch keine Ansätze, diesen Effekt praktisch zur Schweißeigenspannungskontrolle zu nutzen. Neuartige Low Transformation Temperature (LTT) Legierungen bieten aufgrund ihrer charakteristischen chemischen Zusammensetzung die Möglichkeit, hochfeste Stähle auf deren Festigkeitsniveau zu fügen. Die martensitische Phasenumwandlung soll zudem eine gezielte Einstellung der Schweißeigenspannungen erlauben. Die bisher vorliegenden Untersuchungen zu diesem Thema sind zwar zahlreich, bieten jedoch nur wenige Erkenntnisse zur Wechselwirkung zwischen der Phasenumwandlung und den resultierenden Schweißeigenspannungen. Der Vortrag gibt anhand ausgewählter Beispiele einen Einblick in Möglichkeiten und Grenzen der LTT-Schweißzusatzwerkstoffe. T2 - 2. Kolloquium Eigenspannungsseminar anlässlich des 80. Geburtstags von Herrn Prof. a.D. Dr.-Ing. Helmut Wohlfahrt CY - Braunschweig, Germany DA - 14.04.2016 KW - Schweißeigenspannungen KW - Martensitumwandlung KW - Schweißzusatzwerkstoff PY - 2016 AN - OPUS4-38966 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Alloying Elements for Residual Stress Control during Welding of High Strength Steels T2 - 4. DFG Nachwuchsakademie Materials Science and Materials Engineering "Analysis and assessment of residual stresses on different length-scales" CY - Bad Arolsen, Germany DA - 2010-05-26 PY - 2010 AN - OPUS4-21385 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Controlling Welding Residual Stresses by means of Alloy Design T2 - 2nd World Materials Research Institutes Forum, Workshop for Young Scientists CY - Berlin, Germany DA - 2010-08-31 PY - 2010 AN - OPUS4-21940 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Exploring the Interaction of Phase Transformation and Residual Stress during Welding by Synchrotron Diffraction T2 - 64th IIW Annual Assembly CY - Chennai, India DA - 2011-07-17 PY - 2011 AN - OPUS4-24150 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Bewertung von Legierungen zur Eigenspannungskontrolle beim Schweißen unter besonderer Berücksichtigung der Umwandlungsplastizität T2 - 4. DFG Nachwuchsakademie "Analyse und Bewertung von Eigenspannungen auf unterschiedlichen Längenskalen" CY - Kassel, Germany DA - 2012-04-23 PY - 2012 AN - OPUS4-25779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Innovatives Konzept zum Schweißen moderner Werkstoffe T2 - Sonderkolloquium des Adolf-Martens-Fonds e. V. aus Anlass der Verleihung des Promotionspreises 2011 CY - Berlin, Germany DA - 2012-10-04 PY - 2012 AN - OPUS4-26627 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - LTT-Zusatzwerkstoffe zur Optimierung von Schweißeigenspannungen N2 - Der Vortrag gibt eine Einführung zum Thema LTT-Zusatzwerkstoffe. Anhand experimenteller Befunde werden die Mechanismen erläutert und die Auswirkungen auf die Schweißeigenspannungen verdeutlicht. T2 - 1. LTT-Workshop des ISF RWTH Aachen CY - Aachen, Germany DA - 11.05.2022 KW - LTT-Zusatzwerkstoff KW - Hochfester Stahl KW - Eigenspannungen KW - Martensit KW - Phasenumwandlung PY - 2022 AN - OPUS4-56267 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Eigenspannungsabbau mittels LTT - Schweißzusätzen unter Berücksichtigung der Nahtgeometrie N2 - Der Vortrag befasst sich mit der gezielten Einbringung zusätzlicher LTT-Lagen zur Erzeugung von Druckeigenspannungen in ermüdungskritischen Bereichen von konventionellen Schweißverbindungen. Dies ermöglicht eine wirtschaftliche Lösung, ohne die Integrität der Schweißverbindungen zu beeinträchtigen. Dazu wurden Längssteifen aus hochfestem Stahl in der ersten Lage mit konventionellem Schweißzusatzwerkstoff mittels Metall-Lichtbogenschweißen geschweißt. Anschließend wurde ein Chrom-Nickel-legierter LTT-Schweißzusatz auf die Stirnseiten der Steifen aufgebracht. Durch Variation der Schweißparameter konnten verschiedene Schweißnahtgeometrien des LTT-Zusatzwerkstoffs analysiert werden. T2 - NA 092-00-05 GA "Gemeinschaftsarbeitsausschuss NAS/NMP: Zerstörende Prüfung von Schweißverbindungen (DVS AG Q 4/Q 4.1) CY - Berlin, Germany DA - 20.03.2024 KW - LTT KW - Eigenspannungen KW - hochfester Stahl PY - 2024 AN - OPUS4-59752 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Investigation of hot cracking susceptibility via Modified Varestraint Transvarestraint testing of high-strength filler material N2 - MVT testing was conducted in Transvarestraint mode in multiple welding conditions and under a range of bending speeds. The materials observed were high strength filler metals used in GTAW namely DIN EN ISO 16834-A G 69 4 M21 Mn3Ni1CrMo (G69), 16834-A G 89 6 M21 Mn4Ni2CrMo (G89 6), 16834-A G 89 5 M21 Mn4Ni2,5CrMo (G89 5) and a filler wire 18276-A T 89 4 ZMn2NiCrMo M M21 1 H5 (T89). For evaluation light optical microscope pictures were used. Pixels containing cracks were manually segmented using a self-written program. Out of the segmented images data including crack length, position and area can be calculated for every crack. The results show dependencies of solidification cracking on the test parameters. T2 - IIW Intermediate Meeting Comission II-C CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Solidification cracking KW - High strength steel KW - Varestraint test PY - 2024 AN - OPUS4-59749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Increasing the Significance of Varestraint Tests through Improved Crack Evaluation N2 - The contribution describes a newly developed software tool for crack identification and selection in Modified Varestraint Transvarestraint (MVT) testing. From the digital crack information, in addition to the classical results, such as Total Crack Length (TCL) and Maximum Crack Length (MCL), advanced evaluations can be applied, taking into account the loading and welding parameters. A numerical parameter study is conducted to demonstrate how the isolated variation of individual welding and loading parameters, affects the crack lengths that can potentially be expected based on the machine specifics. An alternative crack criterion is presented that evaluates the crack formation in relation to the machine behavior. Some examples demonstrate the possibilities and limitations of the approach. The criterion can be used to compare and transfer the results of different varestraint test variants. T2 - IIW Annual Assembly, Comission II-C CY - Singapore DA - 17.07.2023 KW - Solidification cracking KW - Varestraint-Test PY - 2023 AN - OPUS4-57984 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Characterising Phase Transformations of Different LTT Alloys and their Effect on Residual Stresses an Cold Cracking T2 - IIW Annual Assembly CY - Singapore DA - 2009-07-12 PY - 2009 AN - OPUS4-19734 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Residual stress Formation in component related stress relief cracking Tests of a welded creep resistant steel N2 - Submerged arc welded (SAW) components of creep-resistant low-alloyed Cr-Mo-V steels are used for thick-walled heavy petrochemical reactors (wall-thickness up to 475 mm) as well as employed in construction of modern high-efficient fossil fired power plants. These large components are accompanied by significant restraints during welding fabrication, especially at positions of different thicknesses like welding of nozzles. As a result, residual stresses occur, playing a dominant role concerning so-called stress relief cracking (SRC) typically during post weld heat treatment (PWHT). Besides specific metallurgical factors (like secondary hardening due to reprecipitation), high tensile residual stresses are a considerable influence factor on SRC. For the assessment of SRC susceptibility of certain materials mostly mechanical tests are applied which are isolated from the welding process. Conclusions regarding the influence of mechanical factors are rare so far. The present research follows an approach to reproduce loads, which occur during welding of real thick-walled components scaled to laboratory conditions by using Tests designed on different measures. A large-scale slit specimen giving a high restraint in 3 dimensions by high stiffness was compared to a medium-scale multi-pass welding U-Profile specimen showing a high degree of restraint in longitudinal direction and a small-scale TIG-remelted specimen. The small-scale specimens were additionally subjected to mechanical bending to induce loads that are found during fabrication on the real-scale in heavy components. Results show for all three cases comparable high tensile residual stresses up to yield strength with high gradients in the weld metal and the heat affected zone. Those high tensile stresses can be significant for cracking during further PWHT. T2 - European Conference on Residual Stresses - ECRS10 CY - Leuven, Belgium DA - 11.09.2018 KW - Welding KW - Residual stress KW - Creep resistant steel KW - Post weld heat treatment KW - Stress relief cracking KW - 13CrMoV9-10 PY - 2018 AN - OPUS4-45983 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Residual stress reduction using LTT welding consumables with focus on the weld geometry N2 - This article focuses on the selective placement of additional LTT layers to generate compressive residual stresses in fatigue-critical areas of conventional weld joints. This enables an economical solution without effecting the integrity of welded joints. For this, longitudinal stiffeners made of high-strength steel were gas metal arc welded using conventional welding consumable in the first layer. Afterwards, a chromium-nickel alloyed LTT welding consumable was deposit on front sides of the stiffeners. By varying the welding parameters, different weld geometries of the LTT filler metal could be analyzed. The effects of additional LTT layers were investigated with regards to residual stresses, microstructure and strength. X-ray residual stresses measurements show that the residual stresses at the failure critical weld toe are significantly reduced by using additional LTT layers. While the conventional weld is characterized by tensile residual stresses, compressive residual stresses can be detected at the LTT weld. The level of residual stresses is influenced by the geometry of the LTT layer. Additional LTT layers with a high offset to the conventional weld generate more compressive residual stress in the HAZ than with a low offset. Therefore, the weld geometry has a considerable impact on the residual stress profile. T2 - IIW Intermediate Meeting Comission II-A CY - Incheon, Republic of Korea DA - 12.03.2024 KW - LTT KW - Residual stress KW - High strength steel PY - 2024 AN - OPUS4-59747 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Projektkurzvorstellung: Bewertung konstruktiv bedingter Erstarrungsrisse beim Schweißen hochfester Feinkornbaustähle N2 - Die Integrität von Leichtbaustrukturen aus hochfesten Stählen ist zunehmend durch die Bildung von Heißrissen gefährdet. Aktuell treten Erstarrungsrisse an Konstruktionsmerkmalen auf, obwohl heißrisssichere niedriglegierte Grund- und Zusatzwerkstoffe als auch Schweißprozessbedingungen eingesetzt wurden. Werkstoff- und prozessseitig wurden diese Rissursachen bereits eingehend erforscht. Untersuchungen zum Aspekt der konstruktiv bedingten Heißrissvermeidung, aus denen sich Empfehlungen für ein beanspruchungsgerechtes Gestalten für KMU ableiten lassen, liegen bislang lückenhaft vor bzw. sind veraltet und für hochfeste Leichtbauten kaum zielführend. Konstruktive Gegenmaßnahmen zur Vermeidung von Erstarrungsrissen liegen oft nicht vor. Das Design und die konstruktiven Randbedingungen beeinflussen die Erstarrungsrisse entscheidend. Um eine schnelle Umsetzbarkeit der Resultate für KMU zu ermöglichen, soll eine einfache und kostengünstige Methodik zur Heißrissbewertung entwickelt werden. Gerade KMU haben einen hohen Nachholbedarf an heißrisssicheren und wirtschaftlichen Leichtbaulösungen. Konstrukteure und Anwender aus KMU würden durch fundierte Kenntnisse über mögliche erstarrungsrisskritische Beanspruchungszustände kostenintensive Qualitätsmängel vermeiden. Das Ziel ist es, Kenngrößen zu identifizieren, die während des Schweißens unter realitätsnahen Bedingungen erfasst werden können. Diese Parameter werden als Transfergrößen genutzt, um eine Heißrissbewertung eines geschweißten Bauteils zu ermöglichen. Anliegen des Vorhabens wird die Prüfung und Bewertung von typischen Beanspruchungszuständen beim Schweißen von Leichtbaustrukturen hinsichtlich ihrer Erstarrungsrissneigung sein. Durch Ableitung klassifizierter Gestaltungshinweise wird ein signifikanter Beitrag zur Steigerung der Wettbewerbsfähigkeit insbesondere für KMU geliefert. Die Ergebnisse werden in Normen zur sicheren schweißtechnischen Fertigung von Leichtbaustrukturen aus hochfesten Stählen direkt einfließen. T2 - Sitzung des NA 092-00-05 GA "Gemeinschaftsarbeitsausschuss NAS/NMP: Zerstörende Prüfung von Schweißverbindungen (DVS AG Q 4/Q 4.1)" CY - Online meeting DA - 10.03.2022 KW - Schweißen KW - Erstarrungsrisse KW - hochfester Stahl PY - 2022 AN - OPUS4-54579 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Einfluss spanender Bearbeitungsschritte auf die Eigenspannungen additiv gefertigter Komponenten aus hochfestem Stahl N2 - Diese Studie konzentriert sich auf den Einfluss der Bearbeitung auf die Eigenspannungen und den Verzug von WAAM-Proben. Definierte Proben wurden vollautomatisch mit einem speziellen WAAM-Massivdraht (Streckgrenze >820 MPa) mit unterschiedlichen geometrischen Designs geschweißt. Der Eigenspannungszustand vor und nach dem Abtrennen der AM-Struktur von der Substratplatte wurde mittels Röntgenbeugung an der Probenoberfläche analysiert und durch 3D-Verformungsanalysen mittels Photogrammetrie ergänzt. Die Ergebnisse zeigen einen signifikanten Einfluss der Geometrie auf die Relaxation und Umverteilung der Eigenspannungen. T2 - NA 092-00-05 GA "Gemeinschaftsarbeitsausschuss NAS/NMP: Zerstörende Prüfung von Schweißverbindungen (DVS AG Q 4/Q 4.1) CY - Berlin, Germany DA - 20.03.2024 KW - DED-arc KW - Eigenspannungen KW - Hochfester Stahl PY - 2024 AN - OPUS4-59753 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Increasing the Significance of Varestraint Tests through Improved Crack Evaluation N2 - It was found that there is a systematic dependence of the crack growth on the welding parameters as well as on the load. Decreasing welding speeds with simultaneously higher heat input promote crack formation with increasing strain rate. Based on the results, a new crack criterion was finally selected which allows an extended assessment of the material behavior during the MVT-test. The threshold introduced can quantify the dependencies of the crack formation on the welding and testing parameters, which could not be comprehensively described with the conventional evaluation. In principle, the evaluation routine can also be transferred to other Varestraint or externally loaded hot cracking tests. T2 - IIW Intermediate Meeting Comission II-c CY - Garching, Germany DA - 06.03.2023 KW - Solidification cracking KW - Varestraint-Test PY - 2023 AN - OPUS4-57131 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of residual stresses and heat control on stress relief cracking in a CrMoV steel mockup N2 - Preventing failures in the manufacture or operation of petrochemical reactors made from creep-resistant, low-alloy steels such as 13CrMoV9-10 still requires research, despite over 60 years of investigation into the field of stress relief cracking. Welding this steel grade requires care. This is due to its low toughness and high strength in the welded condition if not heat treated after welding, combined with an increased susceptibility to cracking during stress relaxation. Previous research on cracking in creep resistant steels has focused on thermal and metallurgical factors; however, little knowledge has been gained on cracking under real-life restraint conditions. In this work, the influence of welding heat control on cracking was investigated by simulating the manufacturing conditions prevailing in the construction of petrochemical reactors using a special weld mockup. The application of acoustic emission analysis showed that cracks formed during post-weld heat treatment in a temperature range between 300 °C and 500 °C. Compared to small scale samples, the toughness of the restrained welds was significantly lower. SEM and TEM analyses of all samples revealed early ageing due to early precipitation of special carbides during post-weld heat treatment under restraint. Neutron diffraction experiments showed that the residual stresses in the weld seam reach the yield point of the material. The presentation provides an overview of how a comprehensive assessment of the integrity of submerged arc welded CrMoV steels can be achieved in the laboratory. T2 - Cracking Phenomena in Welding and Additive Manufacturing 2025 CY - Trollhättan, Sweden DA - 12.03.2025 KW - CrMoV KW - Stress Relief Cracking KW - Sub-merged arc welding PY - 2025 AN - OPUS4-62783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Investigation of restraint intensity influence on solidification cracking of high-strength filler materials in fillet welds via CTS testing N2 - Next to chemical composition, metallurgy and welding parameters, the intensity of restraint is one of the variables influencing solidification cracking. Tests like the Houldcroft Test, rate the hot cracking susceptibility indirectly on the amount of restraint the welding can endure without cracking. Modern lightweight steel construction welds can be subject to a larger amount of restraint due to their high-strength nature compared to classical use cases. By varying the plate thickness of Controlled Thermal Severity (CTS) tests produced out of S1100 QL, it was possible to vary the intensity of restraint on fillet welds at a high level. Testing was conducted with four different filler wires for Metal Active Gas (MAG) welding, including three solid and one metal-cored wire. In addition, two sets of welding parameters were tested. The first set with high heat input and high welding speed was shown to be more prone to solidification cracking compared to the second set with lower heat input and welding speed. The results show an increase in solidification cracking with increasing restraint severity. T2 - IIW Intermediate Meeting Comission II-A CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Solidification cracking KW - High strength steel KW - Weldability PY - 2024 AN - OPUS4-59748 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of Residual Stresses on Stress Relief Cracking of Thick Walled Creep Resistant Steel Welds N2 - Controlling the residual stress level during welding of creep-resistant Cr-Mo-V steels is crucial to avoid so called stress relief cracking (SRC) during post weld heat treatment (PWHT) of large-scale components. In the present study, a laboratory scale test specimen (400 mm x 400 mm x 25 mm) was used to simulate thick-walled component welds made of 13CrMoV9-10. The aim was to identify the level and distribution of residual stresses to evaluate the suitability of the specimen for laboratory based SRC testing. High restraint was ensured by the specimen geometry with a narrow welding gap in the center. This gap was filled by submerged arc welding in a multi-layer technique. Two specimens were welded with identical parameters and compared in the as-welded state and after PWHT (705 °C for 10 h). Neutron diffraction was used to determine the residual stresses in the weld metal, the heat-affected zone (HAZ) and the base material at different depths longitudinal, transverse, and normal to the welding direction. The experiments were performed on the instrument E3 of the research reactor BERII of HZB Berlin, Germany. Complementarily, laboratory X-ray diffraction was applied to characterize the surface residual stresses. In the welded state, especially in the weld metal and the adjacent HAZ, the residual stress can reach the yield strength of the untreated material. The highest levels occur in the longitudinal direction. The transverse and normal directions are characterized by residual stress of lower magnitude. As expected, the residual stress is almost completely relieved after PWHT. T2 - International Conference on Residual Stresses ICRS-11 CY - Nancy, France DA - 27.03.2022 KW - Welding KW - Creep-resistant steel KW - Stress relief cracking KW - Residual stress KW - Post weld heat treatment PY - 2022 AN - OPUS4-54577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Assessing ferrite content in duplex stainless steel weld metals: WRC '92 predictions vs. practical measurements N2 - The weldability of stainless steels is largely controlled by the chemical composition, and alloys with ferritic or ferritic-austenitic solidification show the highest resistance to hot cracking. As the resulting phase balance also affects the final properties, it may be beneficial to both foresee and measure the weld metal ferrite content. The WRC ’92 constitution diagram is currently the most accurate prediction tool available, but it does not take the cooling rate into consideration and the precision may be less accurate for stainless steels with high ferrite numbers (FN). This study aims to validate the reliability of the WRC ’92 diagram for weld metals with FN > 50. The chemical composition was altered through gas tungsten arc welding (GTAW) of UNS S32205 with ER347 filler wire that had been PVD-coated with either niobium (Nb), copper (Cu), nickel (Ni), manganese (Mn), carbon (C), or silicon (Si). The actual ferrite content was assessed using image analysis, FERITSCOPE® and X-ray diffraction (XRD). While the WRC ’92 diagram predictions were deemed accurate to acceptable for Ni, Si, and Mn, notable deviations were observed for Nb, Cu, and C. The FeriteScope exhibited a consistent trend with image analysis, though the values were higher, and scatter was wider, and the conversion factor is open for discussion. The lowest accuracy and largest spread were obtained using non-contact XRD, rendering it unsuitable for ferrite measurements of welds. T2 - IIW Intermediate Meeting Comission IX-H CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Duplex Stainless Steel KW - Ferrite KW - WRC 92 PY - 2024 AN - OPUS4-59750 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of Residual Stresses on Stress Relief Cracking of Thick-Walled Creep-Resistant Steel Welds N2 - Controlling the residual stress level during welding of creep-resistant Cr-Mo-V steels is crucial to avoid so called stress relief cracking (SRC) during post weld heat treatment (PWHT) of large-scale components. In the present study, a laboratory scale test specimen (400 mm x 400 mm x 25 mm) was used to simulate thick-walled component welds made of 13CrMoV9-10. The aim was to identify the level and distribution of residual stresses to evaluate the suitability of the specimen for laboratory based SRC testing. High restraint was ensured by the specimen geometry with a narrow welding gap in the center. This gap was filled by submerged arc welding in a multi-layer technique. Two specimens were welded with identical parameters and compared in the as-welded state and after PWHT (705 °C for 10 h). Neutron diffraction was used to determine the residual stresses in the weld metal, the heat-affected zone (HAZ) and the base material at different depths longitudinal, transverse, and normal to the welding direction. The experiments were performed on the instrument E3 of the research reactor BERII of HZB Berlin, Germany. Complementarily, laboratory X-ray diffraction was applied to characterize the surface residual stresses. In the welded state, especially in the weld metal and the adjacent HAZ, the residual stress can reach the yield strength of the untreated material. The highest levels occur in the longitudinal direction. The transverse and normal directions are characterized by residual stress of lower magnitude. As expected, the residual stress is almost completely relieved after PWHT. T2 - AJP 2023 3rd International Conference on Advanced Joining Processes CY - Braga, Portugal DA - 19.10.2023 KW - Residual stress KW - Creep-resistant steel KW - Stress relief cracking KW - Neutron diffraction PY - 2023 AN - OPUS4-58646 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Observation of martensite formation by combined use of synchrotron diffraction and dilatometry N2 - Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material. T2 - Material Science & Technology (MS&T16) 3rd International Workshop of In-situ Studies with Photons, Neutrons and Electrons Scattering CY - Salt Lake City, UT, USA DA - 23.10.2016 KW - Residual stress KW - Martensite KW - Dilatometry KW - Synchrotron diffraction KW - Neutron diffraction PY - 2016 AN - OPUS4-37999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Optimierung schweißbedingter Beanspruchungen an Bauteilen aus hochfesten feinkornbaustählen beim Einsatz modifizierter Sprühlichtbogenprozesse N2 - Im Forschungsprojekt wurden unter gezielter definierter Schrumpfbehinderung Schweißexperimente an hochfesten Feinkornbaustählen durchgeführt, um den Einfluss der Wärmeführung sowie den Einsatz modifizierter Sprühlichtbogenprozesse verbunden mit schmaleren Nahtfugen auf die lokalen Eigenspannungen und die Gesamteigenbeanspruchungen an geschweißten Bauteilen zu analysieren. In dem Vortrag wurden für das IGF-Vorhaben 17978 N "Bauteilbeanspruchung modifizierter Sprühlichtbögen" die wesentlichen Zusammenhänge zu schweißbedingten Beanspruchungen an hochfesten Schweißverbindungen sowie einige der erarbeiteten Erkenntnisse und erreichten Ziele des Forschungsprojektes in Bezug auf die wasserstoffunterstützte Kaltrissbildung vorgestellt. T2 - Sitzung AG Q4.1 Wasserstoffunterstützte Rissbildung CY - Duisburg, Germany DA - 15.03.2016 KW - Modifizierter Sprühlichtbogen KW - Eigenspannungen KW - MAG-Schweißen KW - Hochfeste Feinkornbaustähle KW - Einspannung KW - Röntgendiffraktometrie KW - Schweißprozessparameter PY - 2016 AN - OPUS4-38791 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Influence of machining on residual stresses in additive manufactured high-strength steel components N2 - This study focuses on the effect of machining on the residual stresses and distortion of WAAM specimens. Defined specimens were welded fully automatically with a special WAAM solid wire (yield strength >820 MPa) with different geometric designs. The residual stresses state before and after cutting of the AM structure from the substrate plate were analyzed by means of X-ray diffraction on the specimen surface and complementary by 3d deformation analyses using photogrammetry. The results reveal significant influences of the geometry on the relaxation and redistribution of residual stresses. T2 - IIW Intermediate Meeting Comission IX-AM CY - Incheon, South Korea DA - 12.03.2024 KW - Residual stress KW - DED-arc KW - High strength steel PY - 2024 AN - OPUS4-59751 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Einfluss der Schweiß- und Prüfparameter bei der Heißrissbewertung hochfester Schweißzusatzwerkstoffe N2 - Die Heißrissneigung beim Schweißen kann mittels einer ganzen Reihe von Prüfverfahren ermittelt werden. Eine etablierte Methode ist die sogenannte Varestraint-Prüfung, welche auch an der Bundesanstalt für Materialforschung und -prüfung (BAM) als modifizierter Varestraint/Transvarestraint-Test (MVT) zum Einsatz kommt. Die Ergebnisse von Varestraint-Prüfungen hängen jedoch stets in unterschiedlichem Maße von der individuellen Prüfmaschinenauslegung und den verwendeten Prüfparametern ab. Dies kann zu einer uneinheitlichen Bewertung des Rissverhaltens führen, wenn die Risslänge konventionell als Kriterium für die Rissneigung herangezogen wird. Scheinbare Abhängigkeiten von Prozessparametern erschweren dann die Interpretation der Ergebnisse. Eine neuartige Bewertungsmethodik entkoppelt den Maschineneinfluss vom Materialverhalten und verwendet die Dehnrate als Risskriterium in Analogie zu Prokhorovs Heißrissmodell. Die neue Auswertung wird anhand einer Studie hochfester Schweißzusatzwerkstoffe vorgestellt, deren Rissverhalten in Abhängigkeit der chemischen Zusammensetzung und der Schweißparameter bewertet wird. T2 - 5. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - Heißrisse KW - Varestraint-Test KW - Materialprüfung PY - 2023 AN - OPUS4-57070 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Optimierung schweißbedingter Beanspruchungen an Bauteilen aus hochfesten Feinkornbaustählen durch Wärmeführung N2 - Höherfeste Feinkornbaustähle werden zunehmend in modernen Schweißkonstruktionen bspw. dem Mobilkranbau eingesetzt. Während der schweißtechnischen Verarbeitung sind für diese Stahlgüten aufgrund ihres speziellen Gefüges und relativ hohen Streckgrenzenverhältnisses engere Verfahrensgrenzen einzuhalten als bei Stählen mit niedrigerer Festigkeit. Zudem erfordert die Sicherheit höherfester Schweißverbindungen präzise Kenntnisse über die Höhe und Verteilung schweißbedingter Beanspruchungen, da diese die erreichbare Tragfähigkeit und Bauteilperformance sowie den wirtschaftlichen Einsatz beeinflussen. Geltende Fertigungsrichtlinien für Schweißkonstruktionen wurden vorrangig für niedrigfeste Güten erarbeitet und vernachlässigen reale Steifigkeits- und Wärmeableitungsbedingungen. In dieser Arbeit wird deshalb der Einfluss der Wärmeführung auf die Eigenspannungsausbildung und Gesamtbeanspruchung in Schweißverbindungen typischer Vertreter höherfester Feinkornbaustähle (z.B. S960QL) systematisch untersucht. Zur Berücksichtigung äußerer Bauteilsteifigkeiten wurden die Proben in Nahtquerrichtung unter definierten realitätsnahen Einspanngraden in speziellen dreidimensional wirkenden Prüfanlagen mehrlagig geschweißt. Dabei ließen sich die resultierenden Kräfte und Spannungen multiaxial in-situ analysieren und ein deutlicher Einfluss der Wärmeführung auf den Kräfte- und Momentenhaushalt aufzeigen. Mittels statistischer Auswertung wurden wesentliche Aussagen für adaptierte Wärmeführungs- und Schweißparameter zur Beanspruchungsoptimierung entwickelt. Die Bewertung der Effekte und Interaktionen der Einflussfaktoren nach Wirkungsart und -ort gestattete zudem, Ansätze zur Berücksichtigung schweißbedingter Beanspruchungen bei der Auslegung höherfester Schweißkonstruktionen zu erarbeiten. T2 - AG Q4.1 Wasserstoffunterstützte Rissbildung CY - Berlin, Germany DA - 07.03.2017 KW - Höherfester Feinkornbaustahl KW - MAG-Schweißen KW - Wärmeführung KW - Schweißprozessparameter KW - Eigenspannungen KW - Bauteilversuch KW - Einspanngrad KW - Beanspruchungen PY - 2017 AN - OPUS4-41067 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Mehraxiale schweißbedingte Beanspruchungen und Werkstoffverhalten bei der Bauteilmontage höherfester Feinkornbaustähle N2 - Der zunehmende Bedarf an hochfesten Feinkornbaustählen in modernen Schweißkonstruktionen, in einer deutlich wachsenden Anzahl von Branchen wie dem Hoch-, Anlagen- und Kranbau, führte in den letzten Jahren zur Entwicklung zahlreicher Grund- und Zusatzwerkstoffe. Neben der Erreichung anforderungsgerechter mechanischer Eigenschaften wird die wirtschaftliche Verarbeitung dieser Güten durch hohe Sicherheitsanforderungen an die Schweißnaht bestimmt. Hohe Zugeigenspannungen in der Schweißverbindung können die Beanspruchbarkeit und Sicherheit eines geschweißten Bauteils wesentlich reduzieren. Insbesondere bei einer hohen konstruktiven Schrumpfbehinderung können die Beanspruchungen auch schon während der Fertigung ein risskritisches Niveau erreichen. Mittels geeigneten Wärmeführungen beim Schweißen und der adäquaten Auswahl von Schweißprozess und Zusatzwerkstoffen ist sowohl eine Minimierung der sich lokal in der Naht bildenden Zugeigenspannungen als auch der globalen infolge von Abstützeffekten auftretenden Reaktionsspannungen und -momente erzielbar. Im Rahmen zweier AiF-Forschungsvorhaben IGF.-Nr. 17267 N und 17978 N wurden verschiedene experimentelle Beanspruchungsanalysen durchgeführt, um den Schweißprozess hinsichtlich der resultierenden schweißbedingten Beanspruchungen zu untersuchen. Hierfür war es erforderlich, die Steifigkeitsverhältnisse so wie sie beim Schweißen realer Bauteilstrukturen auftreten, auf Schweißexperimente im Labor zu übertragen. Dazu wurde bspw. eine an der BAM eigens entwickelte Prüfanlage eingesetzt, mit der die mehraxialen Belastungen analysiert wurden, die mit bis zu 2 MN beim Vorwärmen, Schweißen und Abkühlen auftreten. Die Schweißeigenspannungen wurden mittels Röntgendiffraktometrie bestimmt. Zwar zeigten sich für niedrige Arbeitstemperaturen beim Schweißen ein signifikant reduziertes Gesamtbeanspruchungsniveau nach der Abkühlung der gesamten Schweißnaht. Die langen Abkühlphasen während der mehrlagigen schweißtechnischen Fertigung führen jedoch speziell bei den ersten Schweißraupen zu sehr hohen Reaktionsspannungen. Dabei erwiesen sich schmalere Nahtfugen verbunden mit dem Einsatz modifizierter Schweißprozesse und der Einsatz dehnfähiger Schweißzusätze für das Wurzelschweißen als geeignete Mittel, um eine deutliche Absenkung des Beanspruchungsniveaus beim Schweißen unter Schrumpfbehinderung zu erreichen. Ferner ist damit eine weitere wesentliche Reduzierung der Gesamtbeanspruchung und insbesondere der Zugeigenspannungen in der WEZ möglich. Mithilfe dieser Erkenntnisse ist die Optimierung der schweißbedingten Beanspruchungen unter Nutzung einer adaptierten Wärmeführung zur verbesserten Ausnutzung des Festigkeitspotentials höherfester Feinkornbaustähle erreichbar. T2 - Sitzung AG Q4.1 Wasserstoffunterstützte Rissbildung CY - Halle, Germany DA - 14.03.2018 KW - Bauteilprüfung KW - Eigenspannungen KW - MAG-Schweißen KW - Hochfeste Feinkornbaustähle PY - 2018 AN - OPUS4-45501 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Untersuchungen zur Kaltrissvermeidung in geschweißten Bauteilen aus hochfestem Stahl T2 - 39. VDI-Jahrestagung Schadensanalyse - Wasserstoff in metallischen Bauteilen CY - Würzburg, Germany DA - 2013-10-08 PY - 2013 AN - OPUS4-29215 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Residual Stress Engineering by Low Transformation Temperature Alloys - State of the Art and Recent Developments T2 - 66th IIW Annual Assembly 2013 CY - Essen, Germany DA - 2013-09-11 PY - 2013 AN - OPUS4-29109 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Capabilities of Diffraction Techniques in Welding Research T2 - International Workshop on Industrial Research using Synchrotron and Neutron Methods CY - Berlin, Germany DA - 2013-12-03 PY - 2013 AN - OPUS4-29705 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Properties and Weldability of Modified Low Transformation Temperature (LTT) Filler Wires T2 - IIW Intermediate Meeting - SC II-A CY - Berlin, Germany DA - 2014-04-01 PY - 2014 AN - OPUS4-30537 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Properties and Weldability of Modified Low Transformation Temperature (LTT) Filler Wires T2 - IIW Annual Assembly - SC II-A CY - Seoul, South Korea DA - 2014-07-14 PY - 2014 AN - OPUS4-31093 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - In-situ observation of stress accumulation during sub-merged arc welding T2 - European Conference on Residual Stresses ECRS 9 CY - Troyes, France DA - 2014-07-07 PY - 2014 AN - OPUS4-31096 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Capabilities of Diffraction Techniques in Welding Research T2 - ESS Science Symposium - Future Engineering Diffraction Research in Materials Processing and Testing CY - Prague, Czech Republic DA - 2014-11-17 PY - 2014 AN - OPUS4-32042 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Transformation Plasticity during Martensite Formation analyzed by Synchrotron Diffraction T2 - MSE 2014: Materials Science and Engineering CY - Darmstadt, Germany DA - 2014-09-23 PY - 2014 AN - OPUS4-32017 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Comparison and capabilities of different Methods N2 - X-ray and Neutron diffraction as well as the contour method were used to determine residual stresses in a additively manufactured sample. The results are compared. Capabilites and limitations are shown. T2 - European Conference on Residual Stresses 11 - Tutorial 1: Residual stresses in additive manufacturing CY - Prague, Czech Republic DA - 03.06.2024 KW - Residual stress KW - X-ray diffraction KW - Neutron diffraction KW - Contour method PY - 2024 AN - OPUS4-60286 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -