TY - JOUR A1 - Sanchez Olivares, G. A1 - Rockel, Daniel A1 - Calderas, F. A1 - Schartel, Bernhard T1 - Utilizing leather fibers from industrial wastes as bio-filler to improve flame retardancy in polypropylene JF - Journal of Industrial and Engineering Chemistry N2 - Combining buffing leather fibers from industrial waste streams with ammonium polyphosphate and bentonite clay is proposed as a flame-retardant additive for polypropylene. The paper addresses how they can be processed into attractive composites with the desired mechanical properties. Buffing leather fibers function as a multifunctional bio-filler and as a synergist for the flame retardant, resulting in fire retardancy successful enough to increase the oxygen index (LOI) by up to 7 vol.-% and to achieve a V0 UL 94 classification. Impressively reduced heat release rates are obtained in the cone calorimeter at 50 kW/m2 irradiation; for instance, the maximum average rate heat evolved (MARHE) drops from 765 to below 200 kW m􀀀 2. The synergistic effects are quantified and shown to be very strong for LOI and MARHE. This work opens the door to use waste buffing leather fibers as a promising multifunctional and synergistic bio-filler. KW - Polypropylene KW - Flame retardancy KW - Industrial waste KW - Leather fibers KW - Bio-filler PY - 2024 DO - https://doi.org/10.1016/j.jiec.2023.11.008 SN - 1226-086X SN - 1876-794X VL - 132 SP - 148 EP - 160 PB - Elsevier B.V. AN - OPUS4-59556 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Juds, Carmen A1 - Schmidt, J. A1 - Weller, Michael G. A1 - Lange, Thorid A1 - Beck, Uwe A1 - Conrad, T. A1 - Boerner, H. G. T1 - Combining phage display and next-generation sequencing for materials sciences: A case study on probing polypropylene surfaces JF - Journal of the American Chemical Society N2 - Phage display biopanning with Illumina next-generation sequencing (NGS) is applied to reveal insights into peptide-based adhesion domains for polypropylene (PP). One biopanning round followed by NGS selects robust PP-binding peptides that are not evident by Sanger sequencing. NGS provides a significant statistical base that enables motif analysis, statistics on positional residue depletion/enrichment, and data analysis to suppress false-positive sequences from amplification bias. The selected sequences are employed as water-based primers for PP-metal adhesion to condition PP surfaces and increase adhesive strength by 100% relative to nonprimed PP. KW - Polymers KW - Polypropylene KW - Glue KW - Plastics KW - Surface Activation KW - Primer KW - Peptide Library KW - Epoxy KW - Solid-binding Peptides KW - Functionalization KW - Polymer-binding Peptides KW - Adhesion KW - Material-binding Peptides KW - Adhesives PY - 2020 DO - https://doi.org/10.1021/jacs.0c03482 SN - 0002-7863 SN - 1520-5126 VL - 142 IS - 24 SP - 10624 EP - 10628 PB - ACS CY - Washington, DC, USA AN - OPUS4-51123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yin, Huajie A1 - Sypaseuth, Fanni D. A1 - Schubert, M. A1 - Schoch, R. A1 - Bastian, M. A1 - Schartel, Bernhard T1 - Routes to halogen‐free flame‐retardant polypropylene wood plastic composites JF - Polymers for Advanced Technologies N2 - Developing halogen‐free flame retardants with reasonably high efficiency, which thus function at limited loadings in polypropylene‐based wood/plastic composites (WPC), is still a challenge. Cost‐effective flame‐retarded WPC have been identified as a way to open the door to an interesting, broader spectrum of application in the building and transportation sectors. This work imparts a systematic comprehensive understanding and assessment of different basic routes to halogen‐free flame‐retarded WPC, taking into account economic and environmental considerations. Cheap, halogen‐free single‐component flame retardants and their multicomponent systems are investigated at reasonable filling grades of 20 wt%. The basic routes of promising synergistic multicomponent systems are discussed, and their potential and Limits assessed. Optimizing the consistency of fire residue; closing the surface of inorganic‐organic residual layers; the thermal stabilization and design of the residue, eg, synergistic combination of ammonium polyphosphate and expandable graphite; and the combination of different flame‐retardant mechanisms, eg, intumescence and flame inhibition, are proposed as promising routes to boost the flame‐retardant efficiency. KW - Flammability KW - Halogen‐free KW - Multicomponent systems KW - Polypropylene KW - Wood plastic composite (WPC) PY - 2019 DO - https://doi.org/10.1002/pat.4458 SN - 1099-1581 SN - 1042-7147 VL - 30 IS - 1 SP - 187 EP - 202 PB - Wiley AN - OPUS4-46909 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mueller, Axel A1 - Becker, Roland A1 - Dorgerloh, Ute A1 - Simon, Franz-Georg A1 - Braun, Ulrike T1 - The effect of polymer aging on the uptake of fuel aromatics and ethers by microplastics JF - Environmental Pollution N2 - Microplastics are increasingly entering marine, limnic and terrestrial ecosystems worldwide, where they sorb hydrophobic organic contaminants. Here, the sorption behavior of the fuel-related water contaminants benzene, toluene, ethyl benzene and xylene (BTEX) and four tertiary butyl ethers to virgin and via UV radiation aged polypropylene (PP) and polystyrene (PS) pellets was investigated. Changes in material properties due to aging were recorded using appropriate polymer characterization methods, such as differential scanning calorimetry, Fourier transform infrared spectroscopy, gel permeation chromatography, X-ray photoelectron spectroscopy, and microscopy. Pellets were exposed to water containing BTEX and the ethers at 130-190 mg/L for up to two weeks. Aqueous sorbate concentrations were determined by headspace gas chromatography. Sorption to the polymers was correlated with the sorbate's Kow and was significant for BTEX and marginal for the ethers. Due to substantially lower glass transition temperatures, PP showed higher sorption than PS. Aging had no effect on the sorption behavior of PP. PS sorbed less BTEX after aging due to an oxidized surface layer. KW - BTEX KW - Polypropylene KW - Polystyrene KW - Sorption KW - Degradation PY - 2018 DO - https://doi.org/10.1016/j.envpol.2018.04.127 SN - 0269-7491 VL - 240 SP - 639 EP - 646 PB - Elsevier CY - Amsterdam AN - OPUS4-44990 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pappalardo, Salvatore A1 - Russo, Pietro A1 - Acierno, Domenico A1 - Rabe, Sebastian A1 - Schartel, Bernhard T1 - The synergistic effect of organically modified sepiolite in intumescent flame retardant polypropylene JF - European Polymer Journal N2 - The pyrolysis, flammability and fire behavior of polypropylene (PP) containing an intumescent flame retardant and sepiolite nanoparticles were investigated by performing thermogravimetry, oxygen index (LOI), UL-94, and cone calorimeter tests. The combination of 0.5 wt% of premodified sepiolite (OSEP) with 12 wt% of a commercial intumescent flame retardant showed a clear synergy in LOI, UL-94 ranking and peak heat release rate. The ternary formulation achieved a V-0 classification and, consequently, allowed a reduction in the amount of flame retardant necessary to achieve this result. Whereas OSEP and pristine sepiolite nanoparticles (SEP) affect the performance in PP nanocomposites quite similarly, OSEP outperformed SEP in the combination with intumescent flame retardant. The cone calorimeter results and dynamic rheological measurements confirmed the synergistic effect between the nanofiller and the flame retardant resulting from the improved properties of the residual protective layer. KW - Polypropylene KW - Intumescent flame retardant KW - Sepiolite KW - Cone calorimetry KW - Low oxygen index PY - 2016 DO - https://doi.org/10.1016/j.eurpolymj.2016.01.041 SN - 0014-3057 VL - 76 SP - 196 EP - 207 PB - Elsevier AN - OPUS4-35854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mohamed, Zeinab A1 - Friedrich, Jörg Florian A1 - Krüger, Simone A1 - Farouk, M. A1 - Moustapha, M.E. T1 - Plasma deposition of adhesion-promoting polymer layers onto polypropylene for subsequent covering with thick fire retardant coatings JF - Journal of adhesion science and technology N2 - Melamine resins were used as 50-µm-thick fire retardant coatings for polypropylene (PP). Preceding deposition, low-pressure plasma polymer films of allyl alcohol were coated onto PP to improve the adhesion between PP and melamine resin coatings. The efficiency of such fire retardant coatings was confirmed by flame tests. The plasma-deposited polymer and the dip-coated melamine resin films were characterized by Fourier transform infrared-attenuated total reflectance spectroscopy and X-ray photoelectron spectroscopy (XPS). The adhesion of coatings was measured using a 90° peel test with a doubled-faced adhesive tape. To detect the locus of failure, the peeled layer surfaces were inspected using optical microscopy and XPS. Thermal properties of PP thick melamine resin-coated films were analyzed by thermogravimetric analysis. KW - Polymer KW - Plasma KW - Polypropylene KW - Fire retardant KW - Melamine precursors KW - Plasma polymerization KW - Allyl alcohol KW - Flame retardants KW - Curing PY - 2015 DO - https://doi.org/10.1080/01694243.2015.1033878 SN - 0169-4243 SN - 1568-5616 VL - 29 IS - 14 SP - 1522 EP - 1533 PB - VNU Science Press CY - Utrecht AN - OPUS4-33112 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bajer, Kamila A1 - Braun, Ulrike A1 - Hintersteiner, I. T1 - The memory effect in polyolefinic products: A tool for confirming the steam sterilization process JF - Materials testing N2 - DSC-Messungen von dampfsterilisierten medizinischen Produkten aus Polyolefinen zeigen beim ersten Heizvorgang als auffällige Besonderheit eine zusätzliche Stufe, bekannt als Temperpeak. Das Ziel dieser Untersuchungen ist, dieses Phänomen nachzuvollziehen und zu verstehen, um es als Nachweis für die Dampfsterilisation nutzen zu können. Dafür wurden PP- und PE-Proben unter verschiedenen Bedingungen dampfsterilisiert und im Ofen thermisch behandelt. Anschließend wurden die Proben mittels DSC untersucht und die Einflüsse der thermischen Behandlung und der mechanischen Beanspruchung analysiert. Um den Einfluss unterschiedlicher Materialspezifikationen zu prüfen, wurden zusätzlich verschiedene Referenzmaterialien (PE und PP) untersucht und GPC-Messungen durchgeführt. Des Weiteren wurde die Beständigkeit des Signals gegenüber der Zeit und der Temperatureinflüssen betrachtet. Die Untersuchungen zeigen, dass sich ein stabiler Memory-Effekt erzeugen lässt. KW - Memory effect KW - Steam sterilization KW - Polypropylene KW - Polyethylene KW - DSC PY - 2015 DO - https://doi.org/10.3139/120.110722 SN - 0025-5300 VL - 57 IS - 4 SP - 316 EP - 323 PB - Hanser CY - München AN - OPUS4-33104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dittrich, Bettina A1 - Wartig, K.-A. A1 - Mülhaupt, R. A1 - Schartel, Bernhard T1 - Flame-retardancy properties of intumescent ammonium poly(phosphate) and mineral filler magnesium hydroxide in combination with graphene JF - Polymers N2 - Thermally reduced graphite oxide (TRGO), containing only four single carbon layers on average, was combined with ammonium polyphosphate (APP) and magnesium hydroxide (MH), respectively, in polypropylene (PP). The nanoparticle's influence on different flame-retarding systems and possible synergisms in pyrolysis, reaction to small flame, fire behavior and mechanical properties were determined. TRGO has a positive effect on the yield stress, which is decreased by both flame-retardants and acts as a synergist with regard to Young's modulus. The applicability and effects of TRGO as an adjuvant in combination with conventional flame-retardants depends strongly on the particular flame-retardancy mechanism. In the intumescent system, even small concentrations of TRGO change the viscosity of the pyrolysing melt crucially. In case of oxygen index (OI) and UL 94 test, the addition of increasing amounts of TRGO to PP/APP had a negative impact on the oxygen index and the UL 94 classification. Nevertheless, systems with only low amounts (≤1 wt%) of TRGO achieved V-0 classification in the UL 94 test and high oxygen indices (>31 vol%). TRGO strengthens the residue structure of MH and therefore functions as a strong synergist in terms of OI and UL 94 classification (from HB to V-0). KW - Graphene KW - Intumescence KW - Ammonium polyphosphate KW - Magnesium hydroxide KW - Synergy KW - Polypropylene PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-320685 DO - https://doi.org/10.3390/polym6112875 SN - 2073-4360 VL - 6 IS - 11 SP - 2875 EP - 2895 PB - MDPI CY - Basel AN - OPUS4-32068 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bajer, Kamila A1 - Braun, Ulrike T1 - Different aspects of the accelerated oxidation of polypropylene at increased pressure in an autoclave with regard to temperature, pretreatment and exposure media JF - Polymer testing N2 - The aim of this study is to investigate and compare three different factors, temperature, pretreatment and exposure media, on the oxidation and aging behavior of polypropylene (PP) bulk samples in the autoclave test under increased oxygen pressure. The aging of polypropylene, in this case syringe material, was accelerated under different conditions. The samples were aged at 75°, 80° and 85 °C under pure oxygen and at 75 °C under ultrapure water. Further samples treated with 15 kGy (e-beam) were aged at 75 °C under pure oxygen. All experiments were carried out at an oxygen partial pressure of 50 bar. The different courses of aging were evaluated and compared. Color and transparency were used to assess the visual changes; weight, geometry and tensile test for the changes in technical properties; and DSC, FTIR and TDS-GC-MS to improve our physico-chemical understanding of the aging processes. The investigations showed that all factors tested influence oxidation/aging behaviour. Dry or wet exposure has no effect on aging during the induction time. However, after the point of maximum service time the degradation process of polymer changes significantly in the presence of water. The increase of aging temperature decreases the maximum service time; however a temperature higher than 80 °C changes the relative ratio of surface and bulk oxidation. The pretreatment with irradiation decreases the maximum service time further, because the irradiation partly damages the antioxidant, and the mobility of antioxidant fragments inside the polymer changes. These diffusion effects influence the relative ratio of bulk and surface oxidation of the polymer sample. KW - Autoclave test KW - Accelerated aging KW - Polypropylene KW - Electron radiation PY - 2014 DO - https://doi.org/10.1016/j.polymertesting.2014.05.006 SN - 0142-9418 VL - 37 SP - 102 EP - 111 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-30867 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Purohit, Purv A1 - Wang, D.-Y. A1 - Wurm, Andreas A1 - Schick, C. A1 - Schönhals, Andreas T1 - Comparison of thermal and dielectric spectroscopy for nanocomposites based on polypropylene and layered double hydroxide - proof of interfaces JF - European polymer journal N2 - Polymer based nanocomposites by melt blending of synthesized ZnAl-Layered Double Hydroxide (ZnAl-LDH) and polypropylene (PP) were investigated by temperature modulated differential scanning calorimetry (TMDSC). The LDH was organically modified by using a surfactant, sodium dodecylbenzene sulfonate (SDBS) to increase the interlayer spacing of the LDH, so that polymer segments can intercalate the inter layer galleries. The glass transition temperature (Tg) and the thermal relaxation strength (Δcp) were determined. The Tg remains constant for concentration till 12 wt% of LDH and a slight reduction of 3 K might be observed for 16 wt% LDH but within the experimental error. The thermal relaxation strength decreases indicating reduction in the amount of mobile polymer segments from amorphous fraction. This finding is supported by the increase in the rigid amorphous fraction (RAF) which is attributed to the polymer molecules which are in close proximity to the crystals and the LDH sheets, as they hinder their mobility. This is analyzed in detail and related to the dielectric relaxation spectroscopy (BDS) results. KW - Polypropylene KW - Layered double hydroxide KW - Nanocomposites KW - Temperature modulated differential scanning calorimetery KW - Dielectric spectroscopy KW - Rigid amorphous fraction PY - 2014 DO - https://doi.org/10.1016/j.eurpolymj.2014.03.005 SN - 0014-3057 SN - 1873-1945 VL - 55 SP - 48 EP - 56 PB - Elsevier CY - Oxford AN - OPUS4-30626 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hofmann, D. A1 - Wartig, K.-A. A1 - Thomann, R. A1 - Dittrich, Bettina A1 - Schartel, Bernhard A1 - Mülhaupt, R. T1 - Functionalized graphene and carbon materials as additives for melt-extruded flame retardant polypropylene JF - Macromolecular materials and engineering N2 - Functionalized graphene nanosheets TRGO and MLG 250, prepared from thermally reduced graphite oxide, represent attractive carbon additives for improving the performance of flame retardant polypropylene (PP-FR). The influence of carbon nanofiller type and content on morphology, thermal, mechanical, and electrical properties as well as the fire behavior of melt-extruded PP-FR is investigated. In contrast to conventional nano- and micron-sized carbon fillers such as expanded graphite (EG 40), nano-scaled carbon black (CB), and multiwall carbon nanotubes (CNT), only TRGO and MLG 250 afford uniform dispersion combined with simultaneously improved stiffness (+80%), electrical conductivity (3 × 10-5 S · cm-1) and enhanced flame retardancy of PP-FR, as expressed by lower peak heat release rate (-76%). KW - Extrusion KW - Flame retardance KW - Graphene KW - Nanocomposite KW - Polypropylene PY - 2013 DO - https://doi.org/10.1002/mame.201200433 SN - 1438-7492 SN - 1439-2054 VL - 298 IS - 12 SP - 1322 EP - 1334 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-29817 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Robertson, Daniela T1 - Test method for testing oxidative resistance of polyethylene based products JF - Polymers for advanced technologies KW - Oxidation KW - Degradation KW - Polyethylene KW - Polypropylene PY - 2013 SN - 1042-7147 SN - 1099-1581 VL - 24 IS - Suppl. 1 SP - 1 PB - John Wiley & Sons, Ltd. CY - Chichester AN - OPUS4-29406 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dittrich, Bettina A1 - Wartig, K.-A. A1 - Hofmann, D. A1 - Mülhaupt, R. A1 - Schartel, Bernhard T1 - Carbon black, multiwall carbon nanotubes, expanded graphite and functionalized graphene flame retarded polypropylene nanocomposites JF - Polymers for advanced technologies N2 - Herein, we examine the influence of adding functionalized graphene (FG), distinct expanded graphites and carbon nanofillers such as carbon black and multiwall carbon nanotubes on mechanical properties, morphology, pyrolysis, response to small flame and burning behavior of a V-2 classified flame-retarded polypropylene (PP). Among carbon fillers, FG and multilayer graphene (MLG) containing fewer than 10 layers are very effectively dispersed during twin-screw extrusion and account for enhanced matrix reinforcement. In contrast to the other fillers, no large agglomerates are detected for PP-FR/FG and PP-FR/MLG, as verified by electron microscopy. Adding FG to flame-retardant PP prevents dripping due to reduced flow at low shear rates and shifts the onset of thermal decomposition to temperatures 40°C higher. The increase in the onset temperature correlates with the increasing specific surface areas (BET) of the layered carbon fillers. The reduction of the peak heat release rate by 76% is attributed to the formation of effective protection layers during combustion. The addition of layered carbon nanoparticles lowers the time to ignition. The presence of carbon does not change the composition of the evolved pyrolysis gases, as determined by thermogravimetric analysis combined with online Fourier-transformed infrared measurements. FG and well-exfoliated MLG are superior additives with respect to spherical and tubular carbon nanomaterials. KW - Graphene KW - Flame retardancy KW - Nanocomposites KW - Polypropylene KW - Carbon nanoparticles PY - 2013 DO - https://doi.org/10.1002/pat.3165 SN - 1042-7147 SN - 1099-1581 VL - 24 IS - 10 SP - 916 EP - 926 PB - John Wiley & Sons, Ltd. CY - Chichester AN - OPUS4-29337 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dittrich, Bettina A1 - Wartig, K.-A. A1 - Hofmann, D. A1 - Mülhaupt, R. A1 - Schartel, Bernhard T1 - Flame retardancy through carbon nanomaterials: carbon black, multiwall nanotubes, expanded graphite, multi layer graphene and graphene in polypropylene JF - Polymer degradation and stability N2 - Herein we investigate the influence of carbon additives with different particle sizes and shapes on the flame retardancy and mechanical properties of isotactic polypropylene. Thermally reduced graphite oxide (TRGO) and multi-layer graphene (MLG250), consisting of few graphene layers, are compared with spherical, tubular and platelet-like carbon fillers such as carbon black (CB), multiwall nanotubes (MWNT) and expanded graphite (EG). The different morphologies control the dispersion of the carbon particles in PP and play a key role in structure–property relationships. Uniformly dispersed CB, MLG250 and TRGO shift the onset temperature of PP decomposition to temperatures around 30 °C higher, induce a flow limit in the composites' melt viscosity and change drastically their fire behaviour. The prevented dripping and significantly increased heat absorption result in decreased time to ignition and hardly any change in the reaction to a small flame. Under forced-flaming conditions reductions in the peak heat release rate of up to 74% are achieved due to the formation of a protective layer of residue during combustion. The described effects of carbon nanomaterials on the properties of PP composites are most pronounced for well-exfoliated graphenes, making them preferable to less exfoliated, micron-sized expanded graphite or conventional spherical and tubular carbon nanoparticles. KW - Polypropylene KW - Flame retardancy KW - Nanocomposites KW - Graphene KW - Carbon nanomaterials KW - Thermally reduced graphite oxide PY - 2013 DO - https://doi.org/10.1016/j.polymdegradstab.2013.04.009 SN - 0141-3910 SN - 1873-2321 VL - 98 IS - 8 SP - 1495 EP - 1505 PB - Applied Science Publ. CY - London AN - OPUS4-28638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yin, Huajie A1 - Mix, Renate A1 - Friedrich, Jörg Florian T1 - Influence of differently structured aluminium-polypropylene interfaces on adhesion JF - Journal of adhesion science and technology N2 - Polar groups were introduced on polypropylene surfaces for increasing the surface energy and the peel strength to evaporated aluminium layers. Three kinds of plasma processes were used for introducing such functional groups to polyolefin surfaces: low-pressure radio-frequency (RF) O2 plasma exposure, atmospheric-pressure dielectric-barrier discharge (DBD) treatment in air, and the deposition of allylamine plasma polymer. The amino groups of the allylamine plasma polymer were also used as anchoring points for chemical introduction of covalently bonded spacer molecules equipped with reactive endgroups. Thus, silanol endgroups of a covalently bonded spacer were able to interact with the evaporated metal layer. The Al-PP composites achieved a maximal peel strength of 470 N/m by exposing the polymer to the lowpressure O2 plasma and 500 N/m on exposure to the atmospheric DBD plasma. After allylamine plasma polymerization and grafting of spacers, the peel strength was usually higher than 1500 N/m and the composites could not be peeled. KW - Polypropylene KW - Low-pressure RF oxygen plasma KW - Dielectric barrier discharge (DBD) KW - Pulsed plasma polymerization KW - Surface wettability KW - Peel strength PY - 2011 DO - https://doi.org/10.1163/016942410X511132 SN - 0169-4243 SN - 1568-5616 VL - 25 IS - 8 SP - 799 EP - 818 PB - VNU Science Press CY - Utrecht AN - OPUS4-23990 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Purohit, Purv A1 - Huacuja Sánchez, Jesús A1 - Wang, D.-Y. A1 - Emmerling, Franziska A1 - Thünemann, Andreas A1 - Heinrich, G. A1 - Schönhals, Andreas T1 - Structure - property relationships of nanocomposites based on polypropylene and layered double hydroxides JF - Macromolecules N2 - Nanocomposites based on polypropylene (PP) and organically modified ZnAl layered double hydroxides (ZnAl-LDH) were prepared by melt blending and investigated by a combination of differential scanning calorimetry (DSC), small- and wide-angle X-ray scattering (SAXS and WAXS), and dielectric relaxation spectroscopy (DRS). An average number of stack size of LDH layers is calculated by analyzing the SAXS data which is close to that of pure organically modified ZnAl-LDH. Scanning microfocus SAXS investigations show that the ZnAl-LDH is homogeneously distributed in the PP matrix as stacks of 4–5 layers with an intercalated morphology. DSC and WAXS results show that the degree of crystallinity decreases linearly with the increasing content of LDH. The extrapolation of this dependence to zero estimates a limiting concentration of ca. 40% LDH where the crystallization of PP is completely suppressed by the nanofiller. The dielectric spectra of the nanocomposites show several relaxation processes which are discussed in detail. The intensity of the dynamic glass transition (β-relaxation) increases with the concentration of LDH. This is attributed to the increasing concentration of the exchanged anion dodecylbenzenesulfonate (SDBS) which is adsorbed at the LDH layers. Therefore, a detailed analysis of the β-relaxation provides information about the structure and the molecular dynamics in the interfacial region between the LDH layers and the polypropylene matrix which is otherwise dielectrically invisible (low dipole moment). As a main result, it is found that the glass transition temperature in this interfacial region is by 30 K lower than that of pure polypropylene. This is accompanied by a drastic change of the fragility parameter deduced from the relaxation map. KW - Nanocomposites KW - Layered double hydroxide KW - Dielectric spectroscopy KW - X-ray scattering KW - Polypropylene PY - 2011 DO - https://doi.org/10.1021/ma200323k SN - 0024-9297 SN - 1520-5835 VL - 44 IS - 11 SP - 4342 EP - 4354 PB - American Chemical Society CY - Washington, DC AN - OPUS4-23921 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ma, L. A1 - Feng, L. A1 - Hioki, A. A1 - Cho, K.H. A1 - Vogl, Jochen A1 - Berger, Achim A1 - Turk, G. A1 - Macleod, S. A1 - Labarraque, G. A1 - Tong, W.F. A1 - Schiel, D. A1 - Yafa, C. A1 - Valiente, L. A1 - Konopelko, L.A. A1 - Quetel, C. A1 - Vermaercke, P. A1 - Manzano, J.V.L. A1 - Linsky, M. A1 - Cortés, E. A1 - Tangpitayakul, S. A1 - Plangsangmas, L. A1 - Bergamaschi, L. A1 - Hearn, R. T1 - International comparison of the determination of the mass fraction of cadmium, chromium, mercury and lead in polypropylene: the Comité Consultatif pour la quantité de matière pilot study CCQM-P106 JF - Accreditation and quality assurance KW - Cadmium KW - Chromium KW - Mercury KW - Lead KW - Polypropylene KW - CCQM PY - 2010 DO - https://doi.org/10.1007/s00769-009-0574-z SN - 0949-1775 SN - 1432-0517 VL - 15 IS - 1 SP - 39 EP - 44 PB - Springer CY - Berlin AN - OPUS4-20787 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Werner A1 - Jakob, Ines A1 - Li, Chunshan A1 - Tatzky-Gerth, Renate T1 - Antioxidant depletion and OIT values of high impact PP strands JF - Chinese journal of polymer science KW - Polypropylene KW - Stabilizers KW - Oxidative resistance KW - Antioxidant depletion KW - Oxidative induction time PY - 2009 DO - https://doi.org/10.1142/S0256767909004102 SN - 0256-7679 VL - 27 IS - 3 SP - 435 EP - 445 PB - World Scientific CY - Singapore AN - OPUS4-19458 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg Florian A1 - Mix, Renate A1 - Kühn, Gerhard T1 - Adhesion of metals to plasma-induced functional groups at polymer surfaces JF - Surface and coatings technology N2 - The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 3–4 to 10–14 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral “monomers” like ethylene or butadiene the concentration of the functional groups was varied. A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2–CH2). KW - Peel strength KW - Aluminium KW - Polypropylene KW - Poly(tetrafluoroethylene) KW - Pulsed plasma KW - Allyl alcohol KW - Allylamine KW - Acrylic acid KW - Plasma surface treatment KW - Adhesion PY - 2005 SN - 0257-8972 VL - 200 IS - 1-4 SP - 565 EP - 568 PB - Elsevier Science CY - Lausanne AN - OPUS4-10897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -