TY - JOUR A1 - Popiela, Bartosz A1 - Günzel, Stephan A1 - Schukar, Marcus A1 - Mair, Georg W. A1 - Krebber, Katerina A1 - Seidlitz, Holger T1 - Impact of internal pressure control during manufacturing on residual stresses and safety performance of type 4 pressure vessels N2 - Composite pressure vessels are commonly manufactured using the wet filament winding process, where various process parameters can influence the performance of the finished component. In this study two designs of wet filament wound 6.8-liter type 4 composite pressure vessels were manufactured. Both differ only by the internal pressure used during the filament winding, which primarily influences the residual stress state in the composite structure. An extensive experimental study was carried out, including 10 slow burst tests and strain measurements with fiber optic sensors. Significant differences can be observed in the performance of the two designs even though the used stacking sequence, materials and other manufacturing parameters are the same for both designs. A discussion of the differences in the behavior of both cylinder types is provided, including the strain distribution in slow burst tests and failure mechanism. KW - Residual stresses KW - Slow burst tests KW - Filament winding KW - Type 4 composite pressure vessels KW - Hydrogen PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-626663 DO - https://doi.org/10.1016/j.jcomc.2025.100581 SN - 2666-6820 VL - 17 SP - 1 EP - 9 PB - Elsevier B.V. CY - Amsterdam, Netherlands AN - OPUS4-62666 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Schröder, Nina A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Hydrogen-assisted cracking in GMA welding of high-strength structural steel - A new look into this issue at narrow groove N2 - Modern arc processes, such as the modified spray arc (Mod. SA), have been developed for gas metal arc welding of high-strength structural steels with which even narrow weld seams can be welded. High-strength joints are subjected to increasingly stringent requirements in terms of welding processing and the resulting component performance. In the present work, this challenge is to be met by clarifying the influences on hydrogen-assisted cracking (HAC) in a high-strength structural steel S960QL. Adapted samples analogous to the self-restraint TEKKEN test are used and analyzed with respect to crack formation, microstructure, diffusible hydrogen concentration and residual stresses. The variation of the seam opening angle of the test seams is between 30° and 60°. To prevent HAC, the effectiveness of a dehydrogenation heat treatment (DHT) from the welding heat is investigated. As a result, the weld metals produced at reduced weld opening angle show slightly higher hydrogen concentrations on average. In addition, increased micro- as well as macro-crack formation can be observed on these weld metal samples. On all samples without DHT, cracks in the root notch occur due to HAC, which can be prevented by DHT immediately after welding. KW - High-strength structural steel KW - Gas metal arc welding KW - Diffusible hydrogen KW - Hydrogen-assisted cracking KW - TEKKEN KW - Residual stresses KW - Weld metal cracking PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527260 DO - https://doi.org/10.3390/met11060904 VL - 11 IS - 6 SP - 1 EP - 18 PB - MDPI CY - Basel AN - OPUS4-52726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -