TY - JOUR A1 - Durlo Tambara, Luís Urbano A1 - Nikoonasab, Ali A1 - Radtke, Martin A1 - de Oliveira Guilherme Buzanich, Ana A1 - Gluth, Gregor T1 - Determination of the oxidation depths of ground granulated blast furnace slag-containing cement pastes using Mn K-edge X-ray absorption near-edge structure spectroscopy N2 - The redox potential of the pore solution of hardened cements containing ground granulated blast furnace slag (GGBFS) affects reinforcement corrosion and immobilization of radioactive waste. Here, Mn K-edge X-ray absorption near-edge structure (XANES) spectroscopy was applied to determine the depth profile of the oxidation state of manganese in hardened GGBFS-containing cement pastes. Manganese was oxidized in the outer regions of some of the pastes, but the depth to which this occurred was not identical with the ‘blue-green/white color change front’, usually interpreted as indicating oxidation of sulfur species. For CEM III/B, the color change of the material was gradual and thus unsuitable for a precise determination of the oxidation depth, while for the alkali-activated slag, a distinct color change front was found, but full oxidation of manganese and sulfur had not occurred in the brighter region. Mn K-edge XANES spectroscopy is thus a more reliable method than the determination of the visual color change front to follow the ingress of the oxidation front. KW - Manganese KW - Oxidation KW - Sulfide KW - Alkali-activated materials KW - Redox conditions PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651469 DO - https://doi.org/10.1111/jace.70445 SN - 0002-7820 SN - 1551-2916 VL - 109 IS - 1 SP - 1 EP - 11 PB - Wiley CY - Oxford AN - OPUS4-65146 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nikoonasab, Ali A1 - Licht, M. A1 - Weiler, L. A1 - Achenbach, R. A1 - Raupach, M. A1 - Gluth, Gregor T1 - Pore solution compositions and redox potentials of ground granulated blast furnace slag-containing cement pastes N2 - The pore solutions of hardened ground granulated blast furnace slag (GGBFS)-containing cements differ from the pore solutions of other cements with effects on reinforcement corrosion, application of electrochemical methods and immobilisation of radioactive waste. In the present study, the pore solutions of seven different GGBFS-containing cements (alkali-activated slag, alkali-activated slag/fly ash blends, hybrid alkaline cement (HAC), CEM III/C and CEM III/B) were extracted and their elemental and sulfate concentration, pH, redox potential and conductivity were determined; a Portland cement (CEM I) pore solution was analysed analogously. The silicon and aluminium concentrations of the alkali-activated cements increased with fly ash fraction, reaching values up to 5 mM and 10 mM, respectively, and thus were considerably higher than those of the standard cements. The redox potentials of the pore solutions of the GGBFS-containing cements were in the range from −100 mV to –500 mV vs Ag/AgCl, that is considerably lower than that of the Portland cement (8–20 mV vs Ag/AgCl), with the value depending on the GGBFS fraction and whether the cements were alkali-activated or not. These results indicate that the effects of reduced sulfur species from GGBFS in cements are more pronounced in alkali-activated materials, including HAC, and increase with GGBFS fraction. KW - Alkali-activated materials KW - Ground granulated blast furnace slag KW - Sulfide KW - Redox potential KW - Pore solution PY - 2026 DO - https://doi.org/10.1680/jadcr.25.00041 SN - 1751-7605 SN - 0951-7197 VL - 38 IS - 4 SP - 238 EP - 249 PB - Emerald CY - Leeds AN - OPUS4-64619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Durlo Tambara, Luís Urbano A1 - Hirsch, A. A1 - Dehn, F. A1 - Gluth, Gregor T1 - Carbonation resistance of alkali-activated GGBFS/calcined clay concrete under natural and accelerated conditions N2 - The carbonation resistance of alkali-activated materials (AAMs) is a crucial parameter for their applicability in concrete construction, yet the parameters influencing it are insufficiently understood to date. In the present study, the carbonation resistance of alkali-activated concretes with varying fractions of ground granulated blast furnace slag (GGBFS) and calcined clay (i.e., high, intermediate, and low Ca contents) were assessed under natural and accelerated conditions. Corresponding hardened AAM pastes were studied using X-ray diffraction, thermogravimetry, Raman microscopy, and mercury intrusion porosimetry. The carbonation resistance of the concretes at natural CO2 concentration depended principally on their water/(CaO + MgOeq + Na2Oeq + K2Oeq) ratio. The remaining variability for similar ratios was caused by differences between the pore structures of the AAMs. For concrete with favorable water/(CaO + MgOeq + Na2Oeq + K2Oeq) ratio and pore structure, the carbonation resistance was comparable to that of Portland cement concrete. The relationship between carbonation coefficients obtained under accelerated and natural conditions differed for concretes with high and low fractions of calcined clay, indicating that accelerated carbonation testing is less suitable to study the carbonation of low-Ca AAMs. KW - Alkali-activated materials KW - Carbonation KW - Calcined clay PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-610747 DO - https://doi.org/10.1016/j.conbuildmat.2024.138351 SN - 1879-0526 VL - 449 SP - 1 EP - 14 PB - Elsevier CY - Amsterdam AN - OPUS4-61074 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Mundra, Shishir A1 - Henning, Ricky T1 - Chloride binding by layered double hydroxides (LDH/AFm phases) and alkali-activated slag pastes: an experimental study by RILEM TC 283-CAM N2 - Chloride binding by the hydrate phases of cementitious materials influences the rate of chloride ingress into these materials and, thus, the time at which chloride reaches the steel reinforcement in concrete structures. Chloride binding isotherms of individual hydrate phases would be required to model chloride ingress but are only scarcely available and partly conflicting. The present study by RILEM TC 283-CAM ‘Chloride transport in alkali-activated materials’ significantly extends the available database and resolves some of the apparent contradictions by determining the chloride binding isotherms of layered double hydroxides (LDH), including AFm phases (monosulfate, strätlingite, hydrotalcite, and meixnerite), and of alkali-activated slags (AAS) produced with four different activators (Na2SiO3, Na2O·1.87SiO2, Na2CO3, and Na2SO4), in NaOH/NaCl solutions at various liquid/solid ratios. Selected solids after chloride binding were analysed by X-ray diffraction, and thermodynamic modelling was applied to simulate the phase changes occurring during chloride binding by the AFm phases. The results of the present study show that the chloride binding isotherms of LDH/AFm phases depend strongly on the liquid/solid ratio during the experiments. This is attributed to kinetic restrictions, which are, however, currently poorly understood. Chloride binding by AAS pastes is only moderately influenced by the employed activator. A steep increase of the chloride binding by AAS occurs at free chloride concentrations above approx. 1.0 M, which is possibly related to chloride binding by the C–(N–)A–S–H gel in the AAS. KW - Chloride binding KW - Sorption isotherm KW - Layered double hydroxide KW - AFm phase KW - Alkali-activated materials PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599370 DO - https://doi.org/10.1617/s11527-024-02311-3 SN - 1359-5997 SN - 1871-6873 VL - 57 IS - 4 SP - 1 EP - 17 PB - Springer Nature AN - OPUS4-59937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rudić, O. A1 - Mittermayr, F. A1 - Gluth, Gregor A1 - Simon, Sebastian A1 - Ukrainczyk, N. A1 - Seyrek, Y. A1 - Freytag, B. A1 - Juhart, J. A1 - Grengg, C. T1 - On the benefits of vegetable oil addition for the pore structure and acid resistance of alkali-activated systems N2 - The impact of high additions of vegetable oil (12 vol%) on the mechanical and microstructural properties of metakaolin-slag-based alkali-activated materials (AAMs) was studied. The addition of oil resulted in a slight decrease in initial polymerization kinetics but did not affect the final degree of reaction. AAM-oil-composite-mortars exhibited approximately ∼30% lower compressive strength primarily due to the entrainment of air voids. Newly formed soap phases significantly reduced the volume of small capillary and gel pores (pore radii <15 nm), leading to a decrease in specific inner surface area by a factor of up to 15. The porosity modification induced by the oil addition greatly enhanced the resistance of AAMs against sulfuric acid attack, shifting the dominant processes from diffusion and cracks to framework-dissolution controlled by the inherent phase stabilities. Following the immersion in sulfuric acid (pHstat = 2) for 8 weeks, the depth of corroded layer decreased by 70% and no cracks due to expansive phases were observed. These promising findings suggest that the incorporation of vegetable oil in AAMs has the potential to address durability concerns associated with diffusion-based corrosion processes, thereby expanding the range of future applications. KW - Alkali-activated materials KW - Acid resistance KW - Pore structure PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-581719 DO - https://doi.org/10.1016/j.ceramint.2023.08.036 VL - 49 IS - 20 SP - 33275 EP - 33290 PB - Elsevier Ltd. AN - OPUS4-58171 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Henning, Ricky A1 - Sturm, Patrick A1 - Keßler, S. A1 - Gluth, Gregor T1 - Corrosion of hybrid alkaline cements in saline solution simulating evaporite rock – effect of the Portland clinker content N2 - Two hybrid alkaline cements (HAC) based on Portland clinker, ground granulated blast furnace slag (GGBFS), fly ash and sodium sulfate, as well as an alkali-activated GGBFS/fly ash blend and a Portland cement paste were exposed to a saturated saline solution for 70 days. The combined chemical attack of chloride, magnesium and sulfate ions and the associated changes of the phase assemblage of the materials were studied by X-ray diffraction, thermal analysis and spatially resolved X-ray fluorescence spectroscopy. The experimental results revealed dissolution of ettringite, C-N-A-S-H and calcite, and the formation of gypsum, Kuzel's salt and Friedel's salt; thermodynamic modeling indicated the formation of M-S-H. The resistance of the HAC against attack by the saline solution increased with Portland clinker fraction. The capacity of portlandite to maintain pH at values above 10 is found to be a major factor controlling the resistance of HAC against corrosion in the saline solution. KW - Hybrid cements KW - Alkali-activated materials KW - Magnesium chloride KW - Corrosion KW - Salt attack PY - 2023 DO - https://doi.org/10.1016/j.cemconres.2023.107215 SN - 0008-8846 SN - 1873-3948 VL - 172 SP - 1 EP - 14 PB - Elsevier Ltd. AN - OPUS4-57638 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mundra, S. A1 - Samson, G. A1 - Masi, G. A1 - Achenbach, R. A1 - Bastidas, D. M. A1 - Bernal, S. A. A1 - Bignozzi, M. C. A1 - Criado, M. A1 - Cyr, M. A1 - Gartner, N. A1 - von Greve-Dierfeld, S. A1 - Legat, A. A1 - Nikoonasab, Ali A1 - Provis, J. L. A1 - Raupach, M. A1 - Gluth, Gregor T1 - Application of electrochemical methods for studying steel corrosion in alkali-activated materials N2 - Alkali-activated materials (AAMs) are binders that can complement and partially substitute the current use of conventional cement. However, the present knowledge about how AAMs protect steel reinforcement in concrete elements is incomplete, and uncertainties exist regarding the application of electrochemical methods to investigate this issue. The present review by EFC WP11-Task Force ‘Corrosion of steel in alkali-activated materials’ demonstrates that important differences exist between AAMs and Portland cement, and between different classes of AAMs, which are mainly caused by differing pore solution compositions, and which affect the outcomes of electrochemical measurements. The high sulfide concentrations in blast furnace slag-based AAMs lead to distinct anodic polarisation curves, unusually low open circuit potentials, and low polarisation resistances, which might be incorrectly interpreted as indicating active corrosion of steel reinforcement. No systematic study of the influence of the steel–concrete interface on the susceptibility of steel to corrosion in AAMs is available. Less common electrochemical methods present an opportunity for future progress in the field. KW - Alkali-activated materials KW - Reinforcement corrosion KW - Steel corrrosion KW - Electrochemical methods KW - Concrete PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572241 DO - https://doi.org/10.1002/maco.202313743 SN - 1521-4176 VL - 74 IS - 7 SP - 988 EP - 1008 PB - Wiley-VCH CY - Weinheim AN - OPUS4-57224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Ke, X. A1 - Vollpracht, A. A1 - Weiler, L. A1 - Bernal, S. A. A1 - Cyr, M. A1 - Dombrowski-Daube, K. A1 - Geddes, D. A. A1 - Grengg, C. A1 - Le Galliard, C. A1 - Nedeljkovic, M. A1 - Provis, J. L. A1 - Valentini, L. A1 - Walkley, B. T1 - Carbonation rate of alkali-activated concretes and high-volume SCM concretes: a literature data analysis by RILEM TC 281-CCC N2 - The current understanding of the carbonation and the prediction of the carbonation rate of alkali-activated concretes is complicated inter alia by the wide range of binder chemistries used and testing conditions adopted. To overcome some of the limitations of individual studies and to identify general correlations between mix design parameters and carbonation resistance, the RILEM TC 281-CCC ‘Carbonation of Concrete with Supplementary Cementitious Materials’ Working Group 6 compiled and analysed carbonation data for alkali-activated concretes and mortars from the literature. For comparison purposes, data for blended Portland cement-based concretes with a high percentage of SCMs (≥ 66% of the binder) were also included in the database. The analysis indicates that water/CaO ratio and water/binder ratio exert an influence on the carbonation resistance of alkali-activated concretes; however, these parameters are not good indicators of the carbonation resistance when considered individually. A better indicator of the carbonation resistance of alkali-activated concretes under conditions approximating natural carbonation appears to be their water/(CaO + MgOeq + Na2Oeq + K2Oeq) ratio, where the subscript ‘eq’ indicates an equivalent amount based on molar masses. Nevertheless, this ratio can serve as approximate indicator at best, as other parameters also affect the carbonation resistance of alkali-activated concretes. In addition, the analysis of the database points to peculiarities of accelerated tests using elevated CO2 concentrations for low-Ca alkali-activated concretes, indicating that even at the relatively modest concentration of 1% CO2, accelerated testing may lead to inaccurate predictions of the carbonation resistance under natural exposure conditions. KW - Alkali-activated materials KW - Durability KW - Carbonation KW - Accelerated testing PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560037 DO - https://doi.org/10.1617/s11527-022-02041-4 VL - 55 IS - 8 SP - 1 EP - 15 PB - Springer Nature AN - OPUS4-56003 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Grengg, C. A1 - Ukrainczyk, N. A1 - Mittermayr, F. A1 - Dietzel, M. T1 - Acid resistance of alkali-activated materials: Recent advances and research needs N2 - Cementitious materials are frequently applied in environments in which they are exposed to acid attack, e.g., in sewer systems, biogas plants, and agricultural/food-related industries. Alkali-activated materials (AAMs) have repeatedly been shown to exhibit a remarkably high resistance against attack by organic and inorganic acids and, thus, are promising candidates for the construction and the repair of acid-exposed structures. However, the reaction mechanisms and processes affecting the acid resistance of AAMs have just recently begun to be understood in more detail. The present contribution synthesises these advances and outlines potentially fruitful avenues of research. The interaction between AAMs and acids proceeds in a multistep process wherein different aspects of deterioration extend to different depths, complicating the overall determination of acid resistance. Partly due to this indistinct definition of the ‘depth of corrosion’, the effects of the composition of AAMs on their acid resistance cannot be unambiguously identified to date. Important parallels exist between the deterioration of low-Ca AAMs and the weathering/corrosion of minerals and glasses (dissolution-reprecipitation mechanism). Additional research requirements relate to the deterioration mechanism of high-Ca AAMs; how the character of the corroded layer influences the rate of deterioration; the effects of shrinkage and the bond between AAMs and substrates. KW - Alkali-activated materials KW - Acid attack KW - Acid resistance KW - Concrete repair KW - MIC PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-557376 DO - https://doi.org/10.21809/rilemtechlett.2022.157 SN - 2518-0231 VL - 7 SP - 58 EP - 67 PB - RILEM Publications SARL CY - Paris AN - OPUS4-55737 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grengg, C. A1 - Koraimann, G. A1 - Ukrainczyk, N. A1 - Rudic, O. A1 - Luschnig, S. A1 - Gluth, Gregor A1 - Radtke, Martin A1 - Dietzel, M. A1 - Mittermayr, F. T1 - Cu- and Zn-doped alkali activated mortar – Properties and durability in (bio)chemically aggressive wastewater environments N2 - Metakaolin-based alkali activated mortars (AAM) - with and without CuSO4·5H2O and ZnO addition (mass ratio Mn+/solid binder 0.08% to 1.7%) - were casted and exposed within an extensive long-term field campaign over the period of 20 months to a sewer basin, strongly affected by biogenic acid corrosion. (Un-)exposed AAM were tested regarding their physicochemical and microstructural properties, bioreceptivity and overall durability. Metal addition led to a retarding effect during alkali-activation reaction, as well as to an increase in open porosity of up to 3.0% and corresponding lower compressive strength of up to 10.9%. Reduced microbial colonization and diversity were observed on AAM with Cu, while Zn addition led to increased biodiversity. We propose that the observed higher durability of Cu-doped AAM is due to antibacterial effects and associated reduction of biogenic acid production, superseding overall negative effects of metal-dosage on physical material properties. Observed lower durability of Zn-doped AAM was related to combined negative physicochemical and microbial effects. KW - Microbially induced corrosion KW - Alkali-activated materials KW - Biogenic acid corrosion KW - Biogene Schwefelsäurekorrosion KW - MIC PY - 2021 DO - https://doi.org/10.1016/j.cemconres.2021.106541 SN - 0008-8846 VL - 149 SP - 1 EP - 15 PB - Elsevier CY - Oxford AN - OPUS4-53070 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mundra, Shishir A1 - Provis, J. L. T1 - Mechanisms of passivation and chloride-induced corrosion of mild steel in sulfide-containing alkaline solutions N2 - The pore fluid within many concretes is highly alkaline and rich in reduced sulfur species, but the influence of such alkaline-sulfide solutions on the surface film formed on steel reinforcement is poorly understood. This study investigates the critical role of HS− in defining mild steel passivation chemistry. The surface film formed on the steel in alkaline-sulfide solutions contains Fe(OH)2 and Fe–S complexes, and the critical chloride concentration to induce corrosion increases at high sulfide concentration. However, this behavior is dependent on the duration of exposure of the steel to the electrolyte, and the nature of the sulfidic surface layer. KW - Alkali-activated materials KW - Steel corrosion KW - Sulfide KW - Chloride PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-528861 DO - https://doi.org/10.1007/s10853-021-06237-x VL - 56 IS - 26 SP - 14783 EP - 14802 PB - Springer Nature AN - OPUS4-52886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grengg, C. A1 - Gluth, Gregor A1 - Mittermayr, F. A1 - Ukrainczyk, N. A1 - Bertmer, M. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Radtke, Martin A1 - Leis, A. A1 - Dietzel, M. T1 - Deterioration mechanism of alkali-activated materials in sulfuric acid and the influence of Cu: A micro-to-nano structural, elemental and stable isotopic multi-proxy study N2 - In this study, a multi-proxy approach combining 29Si, 27Al and 1H MAS-NMR, FEG-EPMA, XANES at the Cu K-edge and XRD analytics with hydrochemical tools such as ICP-OES analyses, oxygen-isotope signatures, and thermodynamic modelling was applied to K-silicate-activated metakaolin specimens - with and without CuSO4·5H2O addition - exposed to sulfuric acid at pH = 2 for 35 days. The results revealed a multistage deterioration mechanism governed by (i) acid diffusion, (ii) leaching of K-A-S-H, (iii) microstructural damage related to precipitation of expansive (K,Ca,Al)-sulfate-hydrate phases (iv) complete dissolution of the K-A-S-H framework, (v) and formation of silica gel in the outermost corroded regions. Copper ions were mainly located in layered spertiniite-chrysocolla-like phases in the as-cured materials. The results demonstrate an overall negative effect of Cu addition on chemical material durability, implying that the reported higher durability of Cu-doped AAM in biocorrosion environments can be best explained by bacteriostatic effects. KW - Alkali-activated materials KW - Acid resistance KW - Microbially induced corrosion KW - MIC PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520567 DO - https://doi.org/10.1016/j.cemconres.2021.106373 SN - 0008-8846 VL - 142 SP - 1 EP - 15 PB - Elsevier CY - Oxford AN - OPUS4-52056 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Sebastian A1 - Gluth, Gregor ED - Rossignol, S. ED - Gluth, Gregor T1 - Unraveling the hardening mechanism during laser-induced slip casting of lithium aluminate-microsilica slurry N2 - Additive manufacturing (AM) of alkali-activated materials is a promising method for producing ceramic precursors, construction elements and other parts. A recently introduced AM process is laser-induced slip casting of lithium aluminate/microsilica slurries, which yields parts with excellent mechanical strengths. To clarify the underlying mechanisms, μ-Raman spectroscopy was applied to parts produced by the process, and the dissolution and hydration of lithium aluminate was studied inter alia using conventional and in-situ X-ray diffraction. The results show that significant dissolution of lithium aluminate occurs, particularly at increased temperatures during laser interaction, which leads to an increase of pH and precipitation of an akopovaite-like Li-Al-CO3 layered double hydroxide. The increase of the pH is likely to induce dissolution of the microsilica and possibly formation of a hydrous lithium aluminosilicate gel. These observations explain the strength evolution of the studied parts and can also aid the development and improvement of related AM methods. KW - Alkali-activated materials KW - Additive manufacturing KW - Laser-induced slip casting KW - Lithium KW - Layered double hydroxide PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520557 DO - https://doi.org/10.1016/j.oceram.2021.100060 SN - 2666-5395 VL - 5 IS - Special issue: Alkali-activated materials and geopolymers in ceramics and beyond SP - 1 EP - 7 PB - Elsevier CY - Amsterdam AN - OPUS4-52055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sturm, Patrick A1 - Moye, J. A1 - Gluth, Gregor A1 - Vogler, Nico A1 - Taffe, A. A1 - Kühne, Hans-Carsten ED - Rossignol, S. ED - Gluth, Gregor T1 - Properties of alkali-activated mortars with salt aggregate for sealing structures in evaporite rock N2 - Concrete structures for sealing of tunnels in the host rock are an essential part of systems for nuclear waste storage. However, concretes based on blended cements or magnesium oxychloride cements, which are commonly considered for this application, can deteriorate severely due to a significant heat of hydration and associated deformation and cracking. Alkali-activated materials (AAMs) offer a potential solution to this problem because of their low heat release during hardening. To explore their suitability for the construction of sealing structures in evaporite rock, various AAMs with salt aggregate were studied regarding fresh properties, heat release, mechanical properties and microstructure. The heat of reaction of the AAMs was up to 55% lower than that of a blended cement designed for sealing structures, indicating significant benefits for the intended application. Other relevant properties such as mechanical strength and permeability depended strongly on the mix-design of the AAMs and curing conditions. KW - Alkali-activated materials KW - Geopolymers KW - Nuclear waste storage KW - Sealing structures KW - Evaporite rock PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519422 DO - https://doi.org/10.1016/j.oceram.2020.100041 SN - 2666-5395 VL - 5 IS - Special issue: Alkali-activated materials and geopolymers in ceramics and beyond SP - 1 EP - 8 PB - Elsevier CY - Amsterdam AN - OPUS4-51942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Winnefeld, F. A1 - Gluth, Gregor A1 - Bernal, S. A. A1 - Bignozzi, M. C. A1 - Carabba, L. A1 - Chithiraputhiran, S. A1 - Dehghan, A. A1 - Dolenec, S. A1 - Dombrowski-Daube, K. A1 - Dubey, A. A1 - Ducman, V. A1 - Yu, J. A1 - Peterson, K. A1 - Stephan, D. A1 - Provis, J. L. T1 - RILEM TC 247-DTA round robin test: sulfate resistance, alkali-silica reaction and freeze–thaw resistance of alkali-activated concretes N2 - The RILEM technical committee TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ conducted a round robin testing programme to determine the validity of various durability testing methods, originally developed for Portland cement based-concretes, for the assessment of the durability of alkali-activated concretes. The outcomes of the round robin tests evaluating sulfate resistance, alkali-silica reaction (ASR) and freeze–thaw resistance are presented in this contribution. Five different alkali-activated concretes, based on ground granulated blast furnace slag, fly ash, or metakaolin were investigated. The extent of sulfate damage to concretes based on slag or fly ash seems to be limited when exposed to an Na2SO4 solution. The mixture based on metakaolin showed an excessive, very early expansion, followed by a dimensionally stable period, which cannot be explained at present. In the slag-based concretes, MgSO4 caused more expansion and visual damage than Na2SO4; however, the expansion limits defined in the respective standards were not exceeded. Both the ASTM C1293 and RILEM AAR-3.1 test methods for the determination of ASR expansion appear to give essentially reliable identification of expansion caused by highly reactive aggregates. Alkali-activated materials in combination with an unreactive or potentially expansive aggregate were in no case seen to cause larger expansions; only the aggregates of known very high reactivity were seen to be problematic. The results of freeze–thaw testing (with/without deicing salts) of alkali-activated concretes suggest an important influence of the curing conditions and experimental conditions on the test outcomes, which need to be understood before the tests can be reliably applied and interpreted. KW - Alkali-activated materials KW - Sulfate attack KW - Alkali silica reaction KW - Alkali aggregate reaction KW - Freeze-thaw attack PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-515527 DO - https://doi.org/10.1617/s11527-020-01562-0 VL - 53 IS - 6 SP - 140 PB - Springer Nature AN - OPUS4-51552 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Ebell, Gino A1 - Hlavacek, Petr A1 - Mietz, Jürgen T1 - Chloride‐induced steel corrosion in alkali‐activated fly ash mortar: Increased propensity for corrosion initiation at defects N2 - Chloride contents at the steel–mortar interface that initiate steel corrosion were determined for carbon steel in alkali‐activated fly ash mortar for three different exposure conditions: exposure to 1 M NaCl solution; leaching in deionized water and then exposure to 1 M NaCl solution; and leaching in deionized water, aging in air at 20°C and natural CO2 concentration, and then exposure to 1 M NaCl solution. For comparison, a Portland cement mortar, exposed to 1 M NaCl solution, was studied. The median values of the corrosion‐initiating chloride contents (average over the full length of the rebar) in the alkali‐activated fly ash mortar varied between 0.35 and 1.05 wt% Cl with respect to binder, consistently lower than what was obtained for the Portland cement mortar, but with no clear trend regarding the exposure conditions. For most of the alkali‐activated fly ash mortar specimens, preferential corrosion at the connection between the working electrode and the external measurement setup was observed, while preferential corrosion did not occur for the Portland cement mortar. Scanning electron microscopy and auxiliary experiments in synthetic solutions indicated that this behavior was caused by inhomogeneities at the steel–mortar interface in the alkali‐activated mortar, likely due to its peculiar rheological properties in the fresh state. KW - Alkali-activated materials KW - Steel corrosion KW - Critical chloride content KW - Steel-concrete interface PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-507268 DO - https://doi.org/10.1002/maco.202011541 VL - 71 IS - 5 SP - 749 EP - 758 PB - Wiley-VCH AN - OPUS4-50726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Arbi, K. A1 - Bernal, S. A. A1 - Bondar, D. A1 - Castel, A. A1 - Chithiraputhiran, S. A1 - Dehghan, A. A1 - Dombrowski-Daube, K. A1 - Dubey, A. A1 - Ducman, V. A1 - Peterson, K. A1 - Pipilikaki, P. A1 - Valcke, S. L. A. A1 - Ye, G. A1 - Zuo, Y. A1 - Provis, J. L. T1 - RILEM TC 247-DTA round robin test: carbonation and chloride penetration testing of alkali-activated concretes N2 - Many standardised durability testing methods have been developed for Portland cement-based concretes, but require validation to determine whether they are also applicable to alkali-activated materials. To address this question, RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ carried out round robin testing of carbonation and chloride penetration test methods, applied to five different alkali-activated concretes based on fly ash, blast furnace slag or metakaolin. The methods appeared overall to demonstrate an intrinsic precision comparable to their precision when applied to conventional concretes. The ranking of test outcomes for pairs of concretes of similar binder chemistry was satisfactory, but rankings were not always reliable when comparing alkali-activated concretes based on different precursors. Accelerated carbonation testing gave similar results for fly ash-based and blast furnace slag-based alkali-activated concretes, whereas natural carbonation testing did not. Carbonation of concrete specimens was observed to have occurred already during curing, which has implications for extrapolation of carbonation testing results to longer service life periods. Accelerated chloride penetration testing according to NT BUILD 443 ranked the tested concretes consistently, while this was not the case for the rapid chloride migration test. Both of these chloride penetration testing methods exhibited comparatively low precision when applied to blast furnace slag-based concretes which are more resistant to chloride ingress than the other materials tested. KW - Alkali-activated materials KW - Durability KW - Carbonation KW - Chloride penetration KW - Concrete PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-504045 DO - https://doi.org/10.1617/s11527-020-1449-3 SN - 1359-5997 SN - 1871-6873 VL - 53 IS - 1 SP - 21 PB - Springer Nature AN - OPUS4-50404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hlavacek, Petr A1 - Gluth, Gregor A1 - Lüchtenborg, Jörg A1 - Sturm, Patrick A1 - Mühler, T. A1 - Kühne, Hans-Carsten A1 - Günster, Jens T1 - A Novel Approach to Additive Manufacturing of Alkali-activated Materials: Laser-induced Slip Casting (LIS) of Lithium Aluminate/Silica Slurries N2 - Additive manufacturing of alkali-activated materials currently attracts a lot of attention, because of the possibility to produce customized high-performance elements for a range of applications, potentially being more resource-efficient than conventionally produced parts. Here, we describe a new additive manufacturing process for alkali-activated materials that is based on selective laser-heating of lithium aluminate/microsilica slurries. The new process-material combination allows to manufacture elements with complex geometries at high building rates and high accuracy. The process is versatile and transferrable to structures of sizes differing by orders of magnitude. The mechanical strength of the obtained materials was in the range of values reported for conventional metakaolin-based geopolymers, and superior to what has been hitherto reported for alkali-activated materials produced by additive manufacturing. This mechanical performance was obtained despite the fact that the degree of reaction of the lithium aluminate and the microsilica was low, suggesting that significant reactions took place only at the surface of the microsilica particles. KW - Laser-induced slip casting KW - Alkali-activated materials KW - Additive manufacturing PY - 2019 DO - https://doi.org/10.29272/cmt.2018.0011 SN - 2612-4882 VL - 1 IS - 2 SP - 138 EP - 144 PB - Techna Group AN - OPUS4-49142 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Provis, J. L. A1 - Arbi, K. A1 - Bernal, S. A. A1 - Bondar, D. A1 - Buchwald, A. A1 - Castel, A. A1 - Chithiraputhiran, S. A1 - Cyr, M. A1 - Dehghan, A. A1 - Dombrowski-Daube, K. A1 - Dubey, A. A1 - Ducman, V. A1 - Gluth, Gregor A1 - Nanukuttan, S. A1 - Peterson, K. A1 - Puertas, F. A1 - van Riessen, A. A1 - Torres-Carrasco, M. A1 - Ye, G. A1 - Zuo, Y. T1 - RILEM TC 247-DTA round robin test: mix design and reproducibility of compressive strength of alkali-activated concretes N2 - The aim of RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ is to identify and validate methodologies for testing the durability of alkali-activated concretes. To underpin the durability testing work of this committee, five alkali-activated concrete mixes were developed based on blast furnace slag, fly ash, and flash-calcined metakaolin. The concretes were designed with different intended performance levels, aiming to assess the capability of test methods to discriminate between concretes on this basis. A total of fifteen laboratories worldwide participated in this round robin test programme, where all concretes were produced with the same mix designs, from single-source aluminosilicate precursors and locally available aggregates. This paper reports the mix designs tested, and the compressive strength results obtained, including critical insight into reasons for the observed variability in strength within and between laboratories. KW - Alkali-activated materials KW - Alkali-activated slag KW - Compressive strength KW - Concrete KW - Mix-design PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-489131 DO - https://doi.org/10.1617/s11527-019-1396-z SN - 1359-5997 SN - 1871-6873 VL - 52 IS - 5 SP - Article Number 99 PB - Springer Nature AN - OPUS4-48913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Carabba, L. A1 - Pirskawetz, Stephan A1 - Krüger, Simone A1 - Gluth, Gregor A1 - Bignozzi, M.C. T1 - Acoustic emission study of heat-induced cracking in fly ash-based alkali-activated pastes and lightweight mortars N2 - Alkali-activated fly ashes have been proposed for various applications where resistance against high temperatures is required, yet several details regarding the response of these materials to heat-exposure need to be clarified. In the present study, heat-induced cracking in fly ash-based alkali-activated pastes and lightweight mortars was analyzed by in-situ acoustic emission (AE) detection during complete heating-cooling cycles (up to ∼1100 °C), augmented by thermogravimetry and ex-situ SEM and XRD analyses. The applicability of the lightweight mortars as passive fire protection coatings was assessed by recording temperature-time curves of mortar-coated steel plates. Cracking during heating was limited and associated exclusively with the dehydration of the materials in the temperature range ∼90–360 °C. However, samples heated to temperatures above ∼600 °C exhibited intense cracking on cooling. This was attributed to differential deformations caused by local sintering and partial melting at the glass transition temperature, and subsequent quenching on cooling. KW - Alkali-activated materials KW - Acoustic emission KW - Fire proofing KW - Heat resistance KW - Cracking PY - 2019 DO - https://doi.org/10.1016/j.cemconcomp.2019.04.013 SN - 0958-9465 SN - 1873-393X VL - 102 SP - 145 EP - 156 PB - Elsevier AN - OPUS4-47904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -