TY - CONF A1 - Ebell, Gino T1 - Prestressed Concrete Structures with Concentrated Tendons - Structural Damage due to Hydrogen-Induced Stress Corrosion Cracking N2 - In the course of the deconstruction of the "Bridge of the 20th anniversary of the GDR" at the Altstädter Bahnhof in Brandenburg a. d. Havel, new information on the initiation of hydrogen-induced stress cracks was obtained. BAM was commissioned by the Brandenburg State Road Administration to participate in a corresponding joint project which is financed by the Federal Ministry for Digital and Transport. The added value of the new information gained in this project goes beyond the specific structure. It describes unexpected new damage patterns that can be transferred to other structures with concentrated tendons (tendon block method and Baur-Leonhardt method) and were previously unknown in this form. These should be made known to other developers to enable them to initiate any necessary actions. T2 - Eurocorr 2022 CY - Berlin, Gemany DA - 29.08.2022 KW - Korrosion KW - Corrosion KW - Hydrogen KW - Stress Cracking PY - 2022 AN - OPUS4-55613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Einfluss von Korrosionsprozessen auf die Verbundfestigkeit Feuerverzinkter Betonstähle in der Erstarrungsphase von Beton N2 - Die Wechselwirkung von hoher Alkalität und feuerverzinktem Betonstahl in der Frischbetonphase generiert einen Störung in der Verbundzone. diese Störung basiert sowohl auf der Wasserstoffentwicklung in der Frischbetonphase bis zur diffusionskontrollierten Decksschichtbildung als auch auf die erstarrungsverzögernde Wirkung von Zinkionen auf die CSH-Phasenbildung. Diese werden zwangsläufig infolge anfänglicher starker Korrosionsprozesse frei, und reichern sich in der Verbundzone an. Hier kann es beim normgerechten Ausschalen nach 24h zu weiteren Störungen des Haftverbundes kommen das davon Auszugehen ist das die Erstarrung der CSH-Phasen in der Verbundzone noch nicht begonnen hat. T2 - Forschungsbeiratssitzung der Forschungsvereinigung Feuerverzinkung CY - Darmstadt, Germany DA - 04.12.2025 KW - Korrosion KW - Verzinkter Betonstahl KW - Hydrogen PY - 2025 AN - OPUS4-65054 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Inhibition of hydrogen evolution on galvanized reinforcement in fresh concrete by addition of potassium permangante N2 - Due to the EUdirective53/2003/EEC,which has been in force since 17th January, 2005, restricts the soluble chromate content in cements to amaximum value of 2ppm. This ammount is to low to inhibit the hydrogen evolutuion by the cathodic partial reaction in fresh concrete. T2 - Eurocorr 2019 CY - Sevilla, Spain DA - 09.09.2019 KW - Corrosion KW - Galvanized reinforcement KW - Hydrogen PY - 2019 AN - OPUS4-48934 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Seifert, Lando A1 - Müller, Thoralf T1 - Stress corrosion test in thiocyanate solution with galvanostatic current N2 - Prüfung von Spannstählen hinsichtlich ihrer Anfälligkeit gegenüber wasserstoffinduzierter Spannungsrisskorrosion in kürzeren Zeiträumen. Gewährleistung der Dauerhaftigkeit mittels neuartiger elektrochemischer Prüfverfahren und galvanostatischer Kontrolle und Wasserstoffbeladung T2 - Meeting ISO TC17 SC16 WG8 CY - Online meeting DA - 11.01.2023 KW - Hydrogen KW - Corrosion PY - 2023 AN - OPUS4-56854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ekici, Nilsah T1 - Introduction of The SHIMMER Database for Safe Hydrogen Injection in The European Natural Gas Infrastructure N2 - An important step in the transportation strategy for hydrogen is its injection into the existing natural gas grid, which allows accelerating the transition to a low-carbon economy, in other words, hydrogen economy. The European Commission has established hydrogen roadmaps and strategies that emphasize the safe and efficient integration of hydrogen into the natural gas network to support this transition. In line with the objectives of the road map, several funded projects have been established, among others – the Safe Hydrogen Injection Modelling and Management for European Gas Network Resilience (SHIMMER) project. One of the main goals of this project is establishing a database containing a comprehensive repository of information regarding materials, standards, European pilot projects, and operational conditions parameters for the European gas network gathered from open sources as well as transmission and distribution system operators participating in the project. The SHIMMER database has an extensive structure consisting of 262 pipeline entries, each with details such as length, design pressure, inner diameter, and installation year and more. The following contribution elaborates on how the SHIMMER database was established as reliable source of information to be available for the public. The database allows consistent assessments of hydrogen compatibility across different countries, offering a structured framework to help overcome the challenges inherent to the assessments of the components for the injection of hydrogen across Europe. Further, the SHIMMER database provides a valuable information source for future research on the European gas networks. T2 - ICHS 2025 CY - Seoul, South Korea DA - 22.09.2025 KW - Database KW - Hydrogen KW - Gas Grid KW - Low-carbon KW - Pipeline Steel PY - 2025 AN - OPUS4-64288 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - El Harrab, Hayat A1 - Askar, Enis A1 - Franken, T. A1 - Mauss, F. T1 - Experimental and Reaction Kinetic Study of Hydrogen Ignition Behavior at Ignition Limits N2 - The paper presents the results of the experimental and reaction kinetic investigation of hydrogen ignition at different pressures, highlighting its non-linear behaviour and effects of radical wall termination. The reaction kinetic simulation predicts the three characteristic ignition limits caused by radical and thermal auto-ignition and is in close agreement with the experimental measurements. The introduction of radical wall termination in the reaction mechanism allowed us to investigate the effect of the autoclave wall and vessel size on the hydrogen ignition behaviour. The first ignition limit is determined by the chain initiation reaction H_2+O_2→2 OH and shows a strong sensitivity towards wall termination of O, H and OH radicals. The third ignition limit is dominated by the reaction paths HO_2+HO_2→H_2 O_2+O_2 and H_2 O_2+M→2 OH+M which is why it shows a strong sensitivity towards wall termination of HO₂ and H₂O₂ radicals. The second ignition limit is influenced by the wall termination of O, H, OH, HO2 and H2O2 radicals. Increasing the radical wall termination rate by increasing the adsorption rate of the radicals at the wall leads to an increase of the auto-ignition temperature at the same pressure. T2 - 13th Mediterranean Combustion Symposium CY - Corfu, Greece DA - 01.06.2025 KW - Hydrogen KW - Auto-ignition Temperature KW - Radical Wall Termination Reaction KW - Ignition Limit PY - 2025 AN - OPUS4-64762 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Component test for the assessment of in-service welding on/onto pressurized hydrogen pipelines N2 - Hydrogen is seen as the energy carrier of the future. Therefore a reliable infrastructure to transport hydrogen in a large scale is needed. A so called European hydrogen backbone out of long distance transmission pipelines is planned by European countries to create a hydrogen transport infrastructure. Due to economic reasons this will be achieved by new build pipelines such as repurposed natural Gas (NG) pipelines, converted to hydrogen useage. A general suitability for hydrogen service of low alloyed pipeline steel, as it is used for NG service today, is given. But in case of necessary in-service welding procedures in terms of e.g. hot-tapping and stoppling, the risk of a critical hydrogen uptake into the pipe materials due to much higher temeperatures while welding and the possibility of hydrogen embrittlement (HE) needs to be closely investigated. The presentation gives an overview of the current H2-SuD project, investigating the feasability of in-service welding on future hydrogen pipelines. Therefore, component-like demonstrators were developed to test (I) the additional hydrogen uptake due to in-service welding under hydrogen pressure and (II) to measure the temperature field due to different welding parameters and demonstrator geometries, especially on the inner pipe wall surface. Collected data will be used to validate a numerical simulation of the thermal field and additionally the hydrogen diffusion in the pipeline material. T2 - Presentation at The University of Manchester CY - Manchester, United Kingdom DA - 12.09.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Welding PY - 2025 AN - OPUS4-64129 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Hydrogen determination in welded metallic materials: Necessity and challenges N2 - In the course of tomorrow's hydrogen-based energy transition, the construction of the corresponding infrastructure will play a central role. The majority of materials used to date are typically welded for component fabrication. In that context, steels are widely applied and can be prone to hydrogen embrittlement. For the evaluation of any hydrogen effect on, for example, the mechanical properties of a welded metallic material, the hydrogen content must be precisely determined. According to ISO 3690, carrier gas hot extraction (CGHE) can be used. In addition to the pure quantification of hydrogen, thermal desorption analysis (TDA) with varied heating rates can be used to determine and evaluate the bonding state at microstructural defects in the material. For both techniques, experimental and measurement influences have to be considered, which have a great effect on the result. For CGHE, for example, ISO 3690 suggests different sample geometries as well as minimum extraction times. The present study summarizes results and experiences of numerous investigations with different sample temperatures and geometries (ISO 3690 type B and cylindrical TDA samples) regarding: the influence of the sample surface (polished/welded), measurement accuracies depending on the sample volume. In particular, a deviating extraction temperature to the set temperature, can significantly falsify the measurement results. Based on the results, methods are shown to quickly reach the desired extraction temperature without having to physically interfere with the measurement equipment. This serves to substantially improve the reliability of hydrogen measurement through increased signal stability and accelerated hydrogen desorption. In general, an independent temperature measurement with dummy samples for the selected heating procedure is advisable to exclude possible unwanted temperature influences already before the measurement. In addition (and way more important), the methods described can be transferred directly to industrial applications. T2 - Eurocorr 2023 - The European Corrosion Congress CY - Brussels, Belgium DA - 27.08.2023 KW - Hydrogen KW - Carrier gas hot extraction KW - Welding KW - ISO 3690 KW - Measurement PY - 2023 AN - OPUS4-58305 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Repair welding of in service hydrogen pipelines N2 - In the course of tomorrow's hydrogen-based energy transition, the construction of the corresponding infrastructure will play a central role. In that context, large diameter long-distance transmission pipelines for hydrogen will be the backbone in the European Union with service pressures from 70 to 90 bar (e.g., depending on national regulations). It is a major goal to rededicate the existing LNG infrastructure despite the necessity of new pipelines. From that point of view repairing of such transmissions pipelines via welding can be necessary. For the LNG infrastructure, it is state of the art that repair welding is conducted at pipelines under service, i.e., the LNG is still flowing as pressurized gas in the steel pipes. The reason is that a shut-down of large diameter pipelines is not so easy or sometimes impossible. In fact, as long no oxygen enters the pipeline, there would be any combustion or (in the worst case) explosion. At the moment, it is entirely open if current repair welding procedures for LNG pipelines can be transferred to pure hydrogen pipelines. In opposite to LNG, hydrogen can be way easier absorbed to the pipeline steels and diffuses through the material. If it accumulates in susceptible regions, i.e., in the welded joint, hydrogen assisted embrittlement could occur. The planned welding procedure requires a so-called preheating and maintenance of the weld joint of up to 300°C for several hours. This temperature is way higher compared to the typical service temperature of max. 40 to 50°C at operational pressures of 100 bar. In accordance to API 941, these low-alloyed pipeline steels are subjected to short-term service loads, which they are not designed for. For that reason, a collaborative project between BAM and DVGW (German Association for Gas and Water professions) was initiated in 2022 to answer the following questions by experiments and numerical simulation of: (1) How many hydrogen is additionally absorbed during the heating of the material to max. 300°C under remaining operational pressures? (2) Is the hydrogen concentration sufficient to reach a critical condition? (3) Which material and weld microstructure is the most susceptible? (4) Is there a significant difference in the repair welding behavior of LNG pipelines that had been already in use for long-term? (5) Which welding parameters and joint dimensions must be ensured for safe repair welding repair of typical pipelines? For that reason, the present study gives an overview on the current practice in repair welding of in-service pipelines, the industrial importance of this topic for the hydrogen-based energy transition and summarizes first results. T2 - Eurocorr 2023 - The European Corrosion Congress CY - Brussels, Belgium DA - 27.08.2023 KW - Hydrogen KW - Repair Welding KW - Pipeline KW - In-service KW - High-pressure PY - 2023 AN - OPUS4-58334 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Component test for safety assessment of in-service welding on / onto pressurized hydrogen pipelines N2 - Hydrogen is the energy carrier of tomorrow for a fossil-free future. This requires a reliable transport infrastructure capable of transporting large quantities of hydrogen, e.g. for the steel and chemical industries. In addition to the construction of new pipelines, the conversion of existing natural gas (NG) networks is an essential part of global hydrogen strategies. The transport of hydrogen is fundamentally different from that of NG, as hydrogen can be absorbed into the pipeline material. Given the known effects of hydrogen embrittlement, the compatibility of the materials for the proposed pipelines (typically low alloy steels in a wide range of strengths and thicknesses) must be investigated. However, pipelines require frequent maintenance, repair, or the need to install additional outlets. In some cases, it is necessary to perform welding on or to the pipelines while they are still in service, i.e. with active gas flow under high pressure, such as the well-known "hot tapping". This in-service welding poses challenges for hydrogen operations in terms of additional hydrogen absorption during welding and material compatibility. The challenge can be roughly divided into the possible austenitization of the inner pipe material exposed to hydrogen, which can lead to sufficient hydrogen absorption, and the welding itself, which causes an increased temperature range. Both lead to a significant increase in hydrogen solubility and diffusivity of the respective materials compared to room temperature. In this context, knowledge about hot tapping on hydrogen pipelines is scarce due to the lack of operational experience. Fundamental experimental investigations are required to investigate the transferability from natural gas to hydrogen pipeline networks. For this reason, the present study presents a specially designed mock-up / demonstrator concept for the realistic assessment of the welding process conditions. T2 - Materials Week 2025 CY - Frankfurt am Main, Germany DA - 02.04.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Repair welding PY - 2025 AN - OPUS4-62874 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Challenges in repair welding of in-service h2-pipelines N2 - Hydrogen will be one of the most important energy carriers of tomorrow. For the necessary large-scale and long-distance transportation, a reliable pipeline infrastructure is required. It is meanwhile in the most countries accepted to follow a two-way strategy by (I) repurposing the existing natural gas (NG) grid combined with (II) the installation of new pipelines. For example, in Europe a so-called European Hydrogen Backbone (EHB) is planned for 2040. Currently, 28 countries work together to establish a hydrogen pipeline grid of several thousands of kilometers. In that connection, a wide number of materials are used with different thicknesses, strength levels, chemical composition, surface conditions and so on. Worldwide research projects suggest the general compatibility of the currently applied pipeline steels e.g., in Germany the “SysWestH2” project. Nonetheless, the hydrogen gas grid will require regular inspections, repair, and maintenance. In addition, sometimes pipeline tees are required to connect new grids or pipelines the existing infrastructure. From that point of view, existing concepts from NG-grids must be investigated in terms of the transferability to hydrogen service. An overview on occurring challenges for this hydrogen transition, especially for in-service weld repair procedures is given in this presentation. T2 - AMPP 2024 - The Association for Materials Protection and Performance CY - Genoa, Italy DA - 09.06.2024 KW - In-service KW - Pipeline KW - Repair welding KW - High-pressure KW - Hydrogen PY - 2024 AN - OPUS4-60327 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Component test to simulate critical conditions of hydrogen assisted cracking in submerged arc welded offshore steel N2 - Offshore Wind Turbines (OWT) are a key factor in tomorrow's sustainable energy generation. The ever� increasing installation depth and weight of OWTs require suitable foundation concepts such as monopiles or tripods. Typically, mild steels such as S420ML are used with plate thicknesses of up to several hundred mm, resulting in high restraints in the welded joints. The large plate thickness requires high-efficiency welding processes such as submerged arc welding (SAW) with multiple wires. Due to the very high stiffness and plate thickness of the large-scale offshore structure, a susceptibility to time� delayed hydrogen assisted cracking (HAC) may occur. For this reason, a minimum waiting time (MWT) of up to 48 h must be considered before NDT is conducted. The evaluation of the crack susceptibility is complex due to the component size and stiffness of real offshore structures. For this purpose, a near-component test geometry has been developed to transfer the real stiffness conditions to laboratory (i.e. workshop) scale. The 350 kg mock-up consisted of heavy plates (thickness 50 mm, seam length 1,000 m) joined by a 22-pass submerged-arc weld. Additional stiffeners simulated the effect of high restraint or shrinkage restraint of the weld. Extreme scenarios of hydrogen absorption during welding were simulated by using flux in dry (HD < 5 ml/100g Fe) and wet (HD > 15 ml/100g Fe) conditions. Weld residual stresses were determined using a robotic X-ray diffractometer. Areas of critical tensile residual stress (at the yield strength level) were found in the weld metal and in the heat affected zone, suggesting that these weld subzones are the most critical in the case of hydrogen ingress. To identify possible delayed cracking, the welds were inspected by phased array ultrasonic testing (PAUT) after welding, 6 h, 12 h, 24 h, and a maximum of 48 h. Summarized, no significant occurrence of HAC was detected, indicating the high crack resistance of the welded joint, i.e., a suitable combination of base material, welding consumable and parameters. T2 - Materials Week/Steel Innovation CY - Frankfurt am Main, Germany DA - 02.04.2025 KW - Cold cracking KW - Component test KW - Hydrogen KW - Minimum waiting time KW - Offshore steel grade PY - 2025 AN - OPUS4-62873 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Component test concept for evaluation of in-service welding on pressurized hydrogen pipelines N2 - Hydrogen is set as the energy carrier of tomorrow and most countries will achieve large-scale hydrogen transport through the conversion of the natural gas (NG) grid and the construction of new pipelines. The interaction between hydrogen and the pipeline materials differs fundamentally from that of NG, as hydrogen is readily absorbed into the material. Considering the possible hydrogen embrittlement (HE), the compatibility of the pipeline materials (low-alloyed steels with a wide strength/thickness range) must be investigated. However, pipelines require intervention for maintenance, repair, or grid expansion with welding on/onto the pipelines while in service, i.e. the well-known "hot tapping" and "plugging" or “stoppling”. The challenges compared to NG can be broadly divided into the possible austenitization of the inner pipe material exposed to hydrogen and the welding itself. Both result in a significant increase in hydrogen solubility and could potentially pose challenges in terms of HE. Emphasis is placed on the word "could" because knowledge of "hot tapping" on hydrogen pipelines is scarce due a lack of service experience. To this end, this study proposes a concept for a component-like demonstrator with the objectives: (1) safe feasibility of "hot tapping" on pressurized model hydrogen pipeline sections, (2) facilitate ex-post sample extraction for the purpose of quantifying the absorbed hydrogen concentrations, and (3) ensure in-situ temperature measurement during welding to monitor the pipeline surface temperature. For safety reasons in the event of an unintentional "burn-through", a solid cylinder was inserted in the demonstrator to restrict the hydrogen gas volume to a small, pressurized layer. Reference pipeline surface temperature measurements were ensured on comparable, unpressurized geometries. The investigated range of welding conditions was investigated for representative material/thickness combinations (DN50 to DN200), suggesting the feasibility of the demonstrator for the determination of reliable in-service welding conditions for both installed and new pipelines for hydrogen service. T2 - 20th Pipeline Technology Conference ptc2025 CY - Berlin, Germany DA - 06.05.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Repair welding KW - Component test PY - 2025 AN - OPUS4-63170 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Quantification of hydrogen uptake during in-service hydrogen pipeline welding N2 - Hydrogen must be transported on a large scale from producers to consumers to ensure the energy transition. The necessary pipeline grid is achieved by conversion of the natural gas (NG) grid and building new pipelines. Welding during service as part e.g. of “hot-tapping” is unavoidable for maintenance/repair/expansion. Based on existing studies, the basic material compatibility of (low-alloyed) pipeline steels with hydrogen is postulated. However, this cannot be assumed for the case of in-service welding on pipelines in pressurized condition. The reason is the increased temperature e.g. by preheating and (in particular) during welding of the single passes. As a result, the inner pipeline surface undergoes multiple short-term heating but to high temperatures. In particular, the first passes can result in a temperature close to the austenitic transformation of the material for small wall thicknesses. Both increase the hydrogen uptake into the welded joint. If hydrogen embrittlement is likely to occur, depends on the hydrogen uptake, which must be quantified. For this purpose, welding experiments on pressurized demonstrators were conducted. The hydrogen uptake at 100 bar was compared to reference experiments with nitrogen. A new sample extraction routine for the quantification of the weld-zone specific hydrogen uptake was established. Comprehensive experiments with different steels (P235, L360, L485), wall thicknesses (4.1 mm to 7.8 mm) and diameters (DN50 and DN200) were conducted. In addition, the influence of the welding layer sequence on the hydrogen uptake between single- and multi-layer welds was investigated. Analytical approaches were used to approximate the hydrogen uptake in the respective weld zones. The main findings were that the layer sequence and especially the wall thickness have a large influence on the hydrogen uptake. T2 - 20th Pipeline Technology Conference ptc2025 CY - Berlin, Germany DA - 06.05.2025 KW - In-service KW - Hydrogen KW - Pipeline KW - Repair welding KW - Component test PY - 2025 AN - OPUS4-63165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erxleben, Kjell T1 - Challenges and difficulties in repair welding procedures on in-service hydrogen pipelines N2 - Hydrogen as an energy carrier plays a key role in tomorrow's energy transition. For effective use of hydro-gen as energy carrier the construction of the corresponding infrastructure is of utmost importance. In that context, large diameter long-distance transmission pipelines will form the so-called hydrogen backbone in the European Union with service pressures up to 100 bar (e.g., depending on national regulations). From an economically and ecologically point of view, a major goal is to repurpose the existing natural gas (NG) infra-structure to minimize the need to install new pipelines. To ensure the safety, reliability and integrity of this future hydrogen infrastructure repair welding or further welding of branch pipes etc. can be necessary at in-service conditions, meaning a permanent flow of pressurized hydrogen while executing the repair procedure. The reason is that a shut-down of large diameter pipelines is not easy or sometimes merely impossible. In fact, as long, as no oxygen enters the pipeline, there will neither be any combustion nor (in the worst-case scenario) explosion. The special techniques like hot tapping or stoppling are state-of-the-art for NG and oil pipeline grids. Currently, it is not finally clarified if repair welding procedures for NG pipelines can be trans-ferred to pure hydrogen pipelines. In opposite to NG, hydrogen can be way easier absorbed to the pipeline steels and diffuses through the material. If it accumulates in susceptible regions, i.e., in the welded joint or heat affected zone, hydrogen assisted embrittlement could occur and lead to loss of integrity or even cata-strophic failure of the pipeline. For example, requires the planned welding procedure a preheating and maintenance of the weld joint of up to 300°C for up to several hours at the outer. This temperature is way higher compared to the typical service temperature of max. 60°C at operational pressures of up to 100 bar. In accordance to API 941, these low-alloyed pipeline steels are subjected to short-term service loads, which they are not designed for. Another considerable fact is that if the weld seam is attached to the pipeline, the temperature especially for small wall thickness can be easily above the austenitization temperature. It is well known that austenite has a way higher hydrogen solubility compared e.g. to ferrite/bainite microstructure of the low-alloyed steel. Current studies indicate a remarkable increase of the hydrogen ingress dur-ing the austenitization from the inner pipe wall. It must be answered if a critical material degradation because of increased hydrogen uptake due to in-service welding procedures is likely to occur. T2 - MPA Seminar 2024 CY - Stuttgart, Germany DA - 08.10.2024 KW - In-service KW - Pipeline KW - Hydrogen KW - Welding KW - Repair PY - 2024 AN - OPUS4-61468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feldkamp, Martin T1 - R&D Activities by BAM Related to Transport Package Fire Testing N2 - Packages for the transport of radioactive material shall meet the mechanical and thermal test requirements of the International Atomic Energy Agency (IAEA) regulations for package design approval. Besides mechanical testing, the Federal Institute for Materials Research and Testing (BAM) performs thermal tests in accordance with the IAEA regulations. The thermal test includes a 30-minute 800°C fully engulfing fire. BAM continuously performs various thermal experiments for the investigation of the thermal response of packages with respect to the IAEA fire. The purpose of this paper is to give an overview of the already performed, ongoing and future physical tests and experiments of BAM in the field of thermal investigations. These research and development works shall support our competencies for the authority package design assessment. BAM operates a propane gas fire test facility. To be able to carry out comparative investigations and validity between the propane fire and the in detail prescribed pool fire test in the regulations, BAM carries out various calorimetric tests and investigates the boundary conditions of the fire with the help of fire reference packages. At the same time, we are conducting various fire scenarios with wood-filled impact limiters. Large-scale fire tests of impact limiters are carried out on a full scale as well as on a small scale. Influencing variables are investigated in particular by means of geometric changes and the consideration of artificial damages, in particular holes. In addition to propane fire as a heat source, thermal scenarios are also investigated with hydrogen as heat source and an infrared radiator system to ignite test specimens. For these numerous test arrangements, the transferability to existing and newly developed transport package designs is essential and fruitful within the review of design approvals, especially for Dual Purpose casks with a long-lasting operation time. T2 - 20th International Symposium on the Packaging and Transportation of Radioactive Materials (PATRAM 22) CY - Juan-les-Pins, France DA - 11.06.2023 KW - Fire Testing KW - Wood KW - Hydrogen KW - Fire Reference Test PY - 2023 AN - OPUS4-57722 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias T1 - Potential Effects of Battery and Hydrogen Fires regarding Regulatory Requirements N2 - Introduction and Necessity of the Investigation The IAEA regulations for the safe transport of radioactive material (IAEA SSR-6) define the safety requirements for different package types and consider different transport conditions. The accident conditions of transport specify different mechanical and thermal tests based on investigations of real accident scenarios. Considering the rapid development of new boundary conditions of transport such as electric mobility and the use of hydrogen as energy source for trucks and other kind of vehicles, potential effects of battery and hydrogen fires in transport accidents should be investigated. The aim is to evaluate the existing test requirements developed and derived decades ago, whether they are covering the current transport situation. This concept paper will briefly present the reasons for detailed investigations as bases for a coordinated research project under the roof of the IAEA. T2 - Technical Exchange IRSN – BAM Transport & Storage of Packages for Radioactive Material CY - Berlin, Germany DA - 04.06.2024 KW - Fire KW - Battery KW - Hydrogen KW - IAEA Regulations PY - 2024 AN - OPUS4-60338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gradt, Thomas T1 - Influence of cryogenic hydrogen environment on the tribological properties of materials N2 - The presentation gives an overview over the LH2-activities during 20 years of tribological research in cryogenic environments at BAM. T2 - 2019 Hydrogenius & I2CNER Tribology Symposium CY - Fukuoka, Japan DA - 30.01.2019 KW - Friction KW - Wear KW - Hydrogen KW - Cryogenic Engineering KW - Hydrogen Embrittlement PY - 2019 AN - OPUS4-47339 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Schaupp, Thomas T1 - Hydrogen in steel visualized by neutron imaging N2 - Neutron cameras allow visualizing hydrogen distributions with radiographic or tomographic imaging methods in iron and steel. The necessary contrast between hydrogen and iron stems from the high difference in the total neutron cross section of both elements. This allows e.g. the in situ measurement of hydrogen mass flow inside cm thick steel samples with a temporal resolution of 20 s using neutron radiography as well as the quantitative measurement of hydrogen accumulations at the crack’s inner surfaces in hydrogen embrittled iron samples with neutron tomography. We could detect directly gaseous hydrogen in the crack cavities and we measured the gas pressure. This new quality of the information on a micrometer scale allows new insights for the analysis of hydrogen-induced damage mechanisms. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20-30 μm. In this contribution, we show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography methods in order to visualize and quantify hydrogen accumulations at cracks. The measurements were performed at the research reactor BER II of the HZB in Berlin and at the FRM II reactor of the neutron source Heinz Maier-Leibnitz in Garching. T2 - 3rd international conference on metals & hydrogen CY - Ghent, Belgium DA - 29.05.2018 KW - Hydrogen KW - Neutron KW - Radiography KW - Tomography KW - Steel PY - 2018 AN - OPUS4-45074 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Utilization of the Tubular Specimen Technique for the Qualification of Metallic Materials for Hydrogen Technologies N2 - As the world shifts to a decarbonized economy, the demand for hydrogen-based technologies is rapidly increasing. In order to make optimal use of hydrogen as an energy carrier, the infrastructure for hydrogen storage and transport in particular, must meet high technical safety standards. The indispensable basis for such safety assessments are the material properties, which must be evaluated under operating conditions that are as real as possible. The conventional method for the assessment of the material properties in gaseous hydrogen is conducted by testing materials in high-pressure hydrogen gas in a pressure vessel (autoclave). It is an established method that allows to perform common standardized tests such as tensile, fatigue and crack growth tests under varying hydrogen conditions. However, this method is complex and entails high costs due to extensive safety regulations. The hollow specimen technique is a more efficient test method, which can be used to assess the mechanical properties of materials under high-pressure hydrogen gas. The procedure is conducted by enclosing high-pressure gas into a hole along the axis of the tensile test specimen. Recently, this method has been successfully performed at pressures up to 1000 bar and over a wide range of temperatures. Due to the low hydrogen volume needed, this method requires minimal safety regulation; therefore, the costs are reduced when compared to the conventional autoclave technique. This method is now in a standardization process, which has been initiated by Japan as a new working package in ISO (TC 164/SC 1/WG 9). The following contribution presents preliminary results obtained testing common grades of metastable austenitic stainless steel. For this purpose, the mechanical properties and fracture surface of solid and tubular specimens were assessed and compared using slow strain rate tensile (SSRT) test as part of the preliminary work at the Fraunhofer IWM. In a similar way, pipeline steels evaluated under hydrogen atmospheres using the geometry adapted by BAM will be presented. Within the framework of the TransHyDE flagship project, more results with the goal of supporting the standardization of the hollow specimen technique are expected to be obtained. T2 - ZwickRoell Forum for High-Temperature Testing CY - Fürstenfeld, Austria DA - 03.05.2023 KW - Hydrogen KW - H2Hohlzug KW - TransHyDE KW - Tubular specimen technique KW - Innovation PY - 2023 AN - OPUS4-57417 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -