TY - CONF A1 - Weber, Mike A1 - Zaghdoudi, Maha A1 - Brandt, Guido A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Coefficients of Friction in Dependence on Aging State of Elastomers – Experimental Identification and Numerical Simulation of the Experiment N2 - Elastomer seals are mounted as barrier seals in lid systems of containers designed for transport and disposal of negligible heat generating radioactive waste and as auxiliary seals in spent fuel storage and transportation casks (dual purpose casks (DPC)). When the behavior of mounted seals under normal and hypothetical accident conditions of disposal and transport is to be simulated, a comprehensive knowledge of their complex mechanical properties at every state of aging is necessary. In previous works, BAM’s efforts in experimental investigations on specimen artificially aged at different temperatures and times and the implementation of the found results in finite element material models were presented. Additionally, our approaches to reproduce the aging process itself and to extrapolate the results of artificially accelerated aging to longer times were presented. Numerical simulations have shown that the behavior of the seal during mounting and one-sided pressurizing and the resulting performance values such as leakage rate strongly depend on the coefficient of friction (COF) between flange and seal. The friction coefficient, in turn, depends on the aging state of the elastomer material as several publications suggest (see below). Dynamic COF between an exemplary ethylene propylene diene rubber (EPDM) material and a stainless steel ball were determined by using a self-designed linear oscillation tribometer. Unaged and artificially aged EPDM specimen stored for 30 days and 100 days at a temperature of 150 °C were tested. A stainless steel ball (d=10 mm) is brought in contact with the specimen’s surface und loaded by normal forces of 2.5 N, 5 N, 10 N and 20 N. During a reciprocating movement of the EPDM sheet, the horizontal force/friction force is continuously measured, and the COF can be derived. It is well known that friction is a complex phenomenon especially in soft materials. It cannot be excluded that the measured friction force is influenced by additional force components, resulting from the ball’s grooving through the elastomer’s surface. This force depends on the penetration depth of the ball and on the resistance of the elastomer in its different states of aging. The latter results from microstructural changes i.e., chain scission and additional crosslinking that occur during aging which in turn influence the softening or hardening of the material. A finite element (FE) ABAQUS® model was developed to reproduce the measurement process. It should help to better understand the physical mechanisms and to quantify the percentage of measured forces resulting from real friction on the one hand and forces resulting from unintended side effects that could falsify the result on the other hand. The behavior of the elastomer in its different states of aging is reproduced by a FE material model already presented in previous works of BAM. T2 - ASME 2022 Pressure Vessels & Piping Conference (PVP2022) CY - Las Vegas, NV, USA DA - 17.02.2022 KW - Numerical Simulation KW - Radioactive Waste KW - Elastomers KW - Aging KW - Seal Behavior KW - Leakage Rate KW - Coefficient of Friction KW - Experiment PY - 2022 SP - 1 EP - 8 PB - American Society of Mechanical Engineers (ASME) CY - New York, NY, USA AN - OPUS4-57093 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lozano, Daniel A1 - Bulling, Jannis A1 - Prager, Jens T1 - Quadtree decomposition as a meshing strategy for guided waves simulations using the scaled boundary finite element method N2 - Structural health monitoring techniques associate strongly with damage detection and characterization. Ultrasonic guided waves (UGW), for such scope, arise as one of the most promising methods for many reasons i.e. UGW are able to travel long distances and they have high sensitivity to damage. In this context, the necessity to model realistic wave-defect interaction occurs to be critical. Realistic damage scenarios can be modeled through the usage of image-based quadtree meshes. Images, such as the outcome from X-ray scans, C-scans, etc., can be converted into meshes for further integration in a computational domain. Quadtree meshes are created by converting the intensity of the pixels to quadrilateral cells. Homogeneous regions inside one image result in one quad, whereas fine features such as discontinuities can be described with smaller quads. This contribution proposes an efficient methodology to model wave defect interaction, using as a framework the scaled boundary finite element method (SBFEM) and quadtree meshes. Problems as non-conforming regions in the mesh due to the space tree decomposition can be easily avoided using SBFEM’s polygonal elements. Moreover, the semi-analytical nature of the SBFEM allows the modeling of arbitrarily long prismatic/undamaged regions of the waveguides without an increase in the computational burden. T2 - DAGA 2022 CY - Stuttgart, Germany DA - 21.03.2022 KW - Wave defect interaction KW - Scaled Boundary Finite Element Method KW - Quadtree meshes KW - Image-based models KW - Transient analysis PY - 2022 SP - 887 EP - 890 CY - Stuttgart AN - OPUS4-57153 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Hille, Falk A1 - Hofmann, Detlev A1 - Kind, Thomas ED - Isecke, B. ED - Krieger, J. T1 - Überwachung der Brücke Altstädter Bahnhof, Brandenburg./H. Begleituntersuchungen mit moderner Sensorik und zerstörungsfreier Prüfung N2 - Die B1 Brücke am Altstädter Bahnhof in Brandenburg an der Havel wurde im Dezember 2019 aufgrund von während einer turnusmäßigen Inspektion entdeckten Rissen und Hohlstellen entlang der vorgespannten Längsträger gesperrt und im Mai 2021 abgebrochen. In der Zwischenzeit wurde die Brücke detailliert überwacht. Vor dem Abriss wurden zudem umfangreiche Untersuchungen zur Bestandsaufnahme und Schadensanalyse sowie Tests moderner Sensorik vorgenommen. Dabei konnte sowohl die richtige, zuvor nicht sicher bekannte Anzahl von Spanngliedern in den Querträgern sicher ermittelt werden als auch durch moderne Varianten der Schwingungsmessungen und der faseroptischen Sensorik zusätzliche Kenntnisse püber das Bauwerksverhalten ermittelt werden . In dem Beitrag werden die Verfahren mit ihren Möglichkeiten und Grenzen vorgestellt, die Ergebnissee an der Brücke in Brandenburg erläutert und zukünftige Einsatzmöglichkeiten diskutiert. T2 - 5. Brückenkolloquium CY - Ostfildern, Germany DA - 06.09.2022 KW - Monitoring KW - Brücke KW - Radar KW - Vibration KW - Faseroptik PY - 2022 SN - 978-3-8169-3549-0 SP - 555 EP - 566 PB - Expert Verlag CY - Tübingen AN - OPUS4-55627 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feistkorn, S. A1 - Algernon, D. A1 - Arndt, R. A1 - Ebell, Gino A1 - Friese, M. A1 - Grosse, C. U. A1 - Holstein, R. A1 - Niederleithinger, Ernst A1 - Schickert, M. A1 - Schulze, S. A1 - Taffe, A. A1 - Walther, A. A1 - Wolf, J. A1 - Zoega, A. A1 - Zwanzig, M. T1 - Introduction to DIN 4871: Qualification of NDT Personnel in Civil Engineering (NDT-CE) N2 - Recently, non-destructive testing in civil engineering (NDT-CE), in particular of concrete components, has successfully mastered the leap from research to practice. Several methods have been established for field inspections to determine the concrete cover of reinforcement or to estimate the compressive strength as well as other parameters related to the concrete material. In addition, the application of nondestructive testing is indispensable, if information about the inner structure - such as the location of rebars and tendon ducts or the damage-related condition assessment to detect grouting defects, honeycombs, delamination, or corrosion - is required. Besides the selection of a suitable NDT method and an appropriate inspection system, the reliability of the results depends largely on the person who applies the non-destructive inspection technique and evaluates the inspection results. To ensure a high quality of non-destructive concrete evaluation as well as to keep the uncertainty caused by the inspection personnel to a minimum, structured, consistent and regulated theoretical as well as practical training of inspection personnel is essential. To close this gap, the subcommittee of education (UA-A) within the committee for NDT-CE of the German Society for Nondestructive Testing (DGZfP) has been reactivated in 2018 to establish uniform training standards for nondestructive concrete inspections in the long term. The subcommittee consists of scientists, practitioners, authorities, and clients. So far, the national standard DIN 4871 “Non-destructive testing - Qualification and Certification of NDT personnel in Civil Engineering (NDT-CE)” was developed and is currently under review. This standard considers the civil-industry-specifics, for example, that standards for NDT of concrete, as well as related product standards with a few exceptions, still do not exist at the moment. Within this presentation, the concept, the connection to ISO 9712 and other standards as well as an overview of the developed German standard DIN 4871 will be presented. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Non-destrucive testing KW - Civil engineering PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-555250 UR - https://www.ndt.net/article/ndtce2022/paper/66594_manuscript.pdf VL - 2022/09 SP - 1 EP - 12 PB - NDT.net CY - Bad Breisig AN - OPUS4-55525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska A1 - Hofmann, Detlef A1 - Johann, Sergej A1 - Tiebe, Carlo A1 - Basedau, Frank A1 - Sturm, Patrick A1 - Lay, Vera A1 - Niederleithinger, Ernst T1 - Multi-sensor conception for safe sealing structures in underground repositories N2 - The project "SealWasteSafe" of the Bundesanstalt für Materialforschung und -prüfung (BAM, Berlin) deals with sealing structures applied for underground disposal of nuclear waste from two perspectives: (1) material improvement for application in sealing constructions and (2) feasibility study regarding multi-sensor approaches to ensure quality assurance and long-term monitoring. One specimen of 150 l made of alkali-activated material, which was found innovative and suitable for sealing constructions based on preliminary laboratory studies, and, for comparison purpose, another one made of salt concrete, are manufactured with an integrated multi-sensory setup for quality assurance and long-term-monitoring. The specimens were left in their cast form and additionally thermally insulated to simulate the situation in the repository. The multi-sensory concept comprises RFID technology embedded in the specimens suppling material temperature and moisture measurements, integrated fibre optic sensing allowing strain measurement and acoustic emission testing for monitoring possible crack formation. Overall, the suitability and the functionality of the sensors embedded into and attached to strongly alkaline (pH > 13 for the AAM) and salt corrosive (NaCl) environment was proven for the first 672 h. First temperature measurement based on RFID succeeded after 626 h for the alkali-activated material and after 192 h for the conventional salt concrete. Strain measurement based on distributed fibre optic sensing turned out the alkali-activated material with > 1 mm m-1 undergoing approximately twice the compression strain as the salt concrete with strains < 0.5 mm m-1. In contrast, the acoustic emission first and single hits representing crack formation in numbers, was found for alkali-activated material half of that detected at the salt concrete. T2 - SMIRT 26 CY - Berlin/Potsdam, Germany DA - 10.07.2022 KW - SealWasteSafe KW - Monitoring KW - Acoustic emission KW - Fibre optic sensing KW - RFID technology KW - alkali-activated material PY - 2022 SP - 1 EP - 10 AN - OPUS4-55371 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Prabhakara, Prathik A1 - Mielentz, Frank A1 - Stolpe, Heiko A1 - Behrens, Matthias A1 - Lay, Vera A1 - Niederleithinger, Ernst T1 - Construction and validation of a novel phased array borehole probe for ultrasonic investigations at sealing structures in radioactive repositories N2 - A new type of ultrasonic borehole probe is currently under development for the quality assurance of sealing structures in radioactive waste repositories using existing research boreholes. The goal is to examine the sealing structures made of salt concrete for possible cracks, delamination, and embedded objects. Earlier prototype probes use 12 or 16 individual dry point contact (DPC) horizontal shear wave transducers grouped into a transmitter and a receiver array, each made up of six or eight individual transducers. They are operated with a commercially available portable ultrasonic flaw detector used in the civil engineering industry. To increase the generated sound pressure of the borehole probe, the number of transducers in the novel probe is increased to 32. In addition, timed excitation of each probe is used to direct a focused sound beam to a specific angle and distance based on calculated time delays. Hence, the sensitive test volume is limited, and the signal-to-noise ratio of the received signals is improved. This paper presents the validation of the newly developed phased array borehole probe by beam computation in CIVA software and experimental investigations on a semi-cylindrical test specimen to investigate the directional characteristics. In combination with geophysical reconstruction techniques, an optimised radiation pattern of the probe is expected to improve the signal quality and thus increase the reliability of the imaging results. This is of great importance for the construction of safe sealing structures needed for the disposal of radioactive or toxic waste. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Borehole probe KW - Phased array technique KW - SealWasteSafe KW - Monitoring KW - Engineered barrier; PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-568016 SN - 1435-4934 SP - 1 EP - 4 PB - NDT.net AN - OPUS4-56801 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strangfeld, Christoph A1 - Bühling, Benjamin A1 - Hauke, M. A1 - Schweitzer, T. A1 - Maack, Stefan T1 - Frequency modulated, air-coupled ultrasound generated by fluidic oscillators N2 - The majority of ultrasonic devices used for non-destructive testing in civil engineering require contact with the surface of the concrete (specimen), which significantly increases the time required for the measurement. This makes it impractical for extensive investigation of large-scale structures such as bridge decks, foundations, or tunnels. In a pioneering approach, fluidic oscillators are used as contact free ultrasonic sources to overcome the aforementioned limitations. These robust and cost-effective actuators require only pressurised air and are ideally suited for harsh environments. At a constant supply pressure, they generate a continuous mono-frequent actuation signal. Further, varying the supply pressure via a fast pressure regulator was found to generate a frequency modulated signal which enabled time-of-flight measurement with an added advantage of increased signal to noise ratio. To demonstrate the feasibility of this novel idea of non-contact ultrasound, the results of the initial tests are presented. T2 - IEEE International Ultrasound Symposium CY - Venice, Italy DA - 11.10.2022 KW - Air-coupled ultrasound KW - Frequency modulation KW - Non-destructive testing KW - Civil engineering KW - Building materials KW - Fluidic oscillators PY - 2022 DO - https://doi.org/10.1109/IUS54386.2022.9958740 SP - 1 EP - 4 AN - OPUS4-56073 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schumacher, T. A1 - Niederleithinger, Ernst T1 - Combining Passive and Active Ultrasonic Stress Wave Monitoring Techniques: Opportunities for Condition Evaluation of Concrete Structures N2 - Concrete structures are invaluable assets to a society and managing them efficiently and effectively can be supported by information gathered through structural health monitoring (SHM). In this paper, a combined approach based on passive, i.e., acoustic emission (AE), and active, i.e., ultrasonic stress wave (USW) monitoring techniques for application to concrete structures is proposed and evaluated. While AE and USW are based on the same underlying physics, i.e., wave motion in solids, they differ fundamentally with respect to the nature of the source. For the former, external stimuli such as mechanical loads or temperature cause the rapid release of energy from initially unknown locations. As a result, AE events are unique and cannot be repeated. For the latter, a known source at a known location is employed at a specified time. This approach is thus controlled and repeatable. It is argued that a combination of these two techniques has the potential to provide a more comprehensive picture of ongoing fracture processes, damage progression, as well as slowly occurring aging and degradation mechanisms. This combined approach does thus promise new opportunities to support condition assessment of concrete structures. After providing an overview and comparison of the two techniques, results, and observations from a full-scale laboratory experiment and an in-service bridge monitoring study are discussed to demonstrate the promise of the proposed combined monitoring approach. Finally, suggestions for further work are presented. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Ultrasound KW - Acoustic emission KW - Concrete structures KW - Monitoring PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563242 UR - https://www.ndt.net/article/ndtce2022/paper/61607_manuscript.pdf SP - 1 EP - 11 PB - NDT.net AN - OPUS4-56324 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Arndt, R.W. A1 - Grosse, C.U, A1 - Maehner, D. A1 - Niederleithinger, Ernst A1 - Taffe, A. A1 - Algernon, D. A1 - Berger, J. A1 - Kessler, S. A1 - Krueger, M. A1 - Kruschwitz, Sabine A1 - Ufermann-Wallmeier, D. A1 - Walther, A. T1 - Non-destructive testing in civil engineering: A memorandum for teaching at German-speaking universities N2 - This contribution summarizes actual developments and draft fundamental teaching topics in the field of nondestructive testing in civil engineering (NDT-CE). It is based on the first memorandum on teaching and research in the field of NDT-CE at German speaking universities and provides an overview of the academic education and highlights possible focuses, especially in teaching but also takes into account noteworthy developments and topics in research in the field of NDT-CE. Suggestions are given for the development and advancement of the teaching curricula in regards to a comprehensive and sound professional education of students in civil engineering and adjacent disciplines. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Curriculum KW - NDT-CE KW - University KW - Competencies PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563269 UR - https://www.ndt.net/article/ndtce2022/paper/61547_manuscript.pdf SP - 1 EP - 10 PB - NDT.net AN - OPUS4-56326 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Guangliang, Y. A1 - Mahon, D. A1 - Gardner, S. T1 - Muon tomography applied to assessment of concrete structures: First experiments and simulations. N2 - Non-destructive techniques for reinforced or prestressed concrete inspection such as ultrasound or radar have found regular, successful practical application but sometimes suffer from limited resolution and accuracy, imaging artefacts or restrictions in detecting certain features. Until the 1980s X-ray transmission was used in case of special demands and showed a much better resolution than other NDT techniques. However, due to safety concerns and cost issues, this method is almost never used anymore. Muon tomography has received much attention recently. Novel detectors for cosmic muons and tomographic imaging algorithms have opened new fields of application. As a first step towards practical application in civil engineering and as a proof of concept we used an existing system to image the interior of a reference reinforced 600 kg concrete block. Even with a yet not optimized setup for this kind of investigation, the muon imaging results are at least of similar quality compared to ultrasonic and radar imaging, potentially even better. In a second step, we have performed simulations to assess the potential for a set of important testing problems such as grouting defects in tendon ducts. The next steps include the development of mobile detectors and optimizing acquisition and imaging parameters. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Muon tomography KW - Concrete KW - Inspection KW - Simulation PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563224 UR - https://www.ndt.net/article/ndtce2022/paper/60943_manuscript.pdf SP - 1 EP - 8 PB - NDT.net AN - OPUS4-56322 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epple, Niklas A1 - Niederleithinger, Ernst A1 - Fontoura Barroso, Daniel T1 - Coda Wave Interferometry for Monitoring Bridges with Embedded Ultrasonic Transducers – Lessons Learned at the Gänstorbrücke Bridge Ulm, Germany N2 - Ultrasonic Coda Wave interferometry has the potential to detect minute changes in scattering materials like concrete. By permanently installing ultrasonic transducers in concrete, DFG Research unit CoDA aims to develop methods for concrete damage assessment in Germany's aging infrastructure. To test the methods developed in simulations and laboratory experiments on a large scale, we have implemented several ultrasonic transducers at the Gänstorbrücke Ulm, one of Germany's most monitored road bridges. Since fall 2020 we are monitoring parts of the center of the Bridge, as well as an abutment, and compare the results to the commercial monitoring system. All data is recorded with a self-made data collection device, the so-called W-Box, and analyzed with different coda wave-based algorithms to detect signal and volumetric velocity changes. The long-term measurements show that the influence of temperature changes on strains and therefore ultrasound velocity changes calculated with coda waves can be monitored. The capabilities and limitations of the coda wave-based monitoring system are tested in a controlled experiment. Static loading using a truck with varying loads at several positions allows the calibration of the system to improve the detectability of possibly damaging loads and changes induced by this loading. A map of velocity change analyzing data from this load experiment shows that the influence of load on the material and strain distribution can be detected with array measurements. T2 - NDT-CE 2022 - The International Symposium on Nondestructive Testing in Civil Engineering CY - Zurich, Switzerland DA - 16.08.2022 KW - Coda Wave Interferometry KW - Ultrasound KW - Embedded sensors KW - Bridge Monitoring KW - Load Experiment PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-564531 SP - 1 EP - 8 AN - OPUS4-56453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grohmann, Maria A1 - Niederleithinger, Ernst A1 - Buske, B. T1 - Application of Elastic Reverse Time Migration to Ultrasonic Echo Data in Civil Engineering N2 - To improve ultrasonic imaging of concrete structures, we transferred a seismic migration technique, the Reverse Time Migration (RTM), to non-destructive testing. A 2D elastic RTM algorithm was tested on synthetic ultrasonic echo data. Compared to the typically used synthetic aperture focusing technique (SAFT) as well as our acoustic RTM algorithm, the presented elastic RTM results show an enhancement in imaging vertical reflectors and complex features inside the 2D numerical concrete model. T2 - The International Symposium on Nondestructive Testing in Civil Engineering CY - Zurich, Switzerland DA - 16.08.2022 KW - Ultrasonic Echo Technique KW - Reverse Time Migration KW - Synthetic Aperture Focusing Technique PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-561147 UR - https://www.ndt.net/article/ndtce2022/paper/60699_manuscript.pdf SP - 1 EP - 6 AN - OPUS4-56114 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bühling, Benjamin A1 - Maack, Stefan A1 - Strangfeld, Christoph T1 - OsciCheck - A Novel Fluidic Transducer for Air-Coupled Ultrasonic Measurements N2 - Ultrasonic measurement technology has become indispensable in NDT-CE. Air-coupled ultrasonic (ACU) measurement techniques promise to reduce measurement time. However, the signal quality suffers from large specific impedance mismatch at the transducer-air and air-specimen interface. Additionally, large pressure amplitudes are necessary for the penetration depth required in NDT-CE applications. To address the specific requirements of ultrasonic testing in NDT-CE, a robust ACU transducer was developed, that generates ultrasound by quickly switching a pressurized air flow. The simple design of the fluidic transducer makes the device maintenance free and resilient against harsh environmental conditions. Since the signal is generated by aeroacoustics, there is no specific impedance mismatch between the transducer and the surrounding air. The ultrasonic signal exhibits frequencies in the 30-60 kHz range and is therefore well suited to penetrate heterogenous materials such as concrete. This contribution gives an introduction in the working principle and signal characteristics of the fluidic transducer. Its applicability to measurements in concrete is verified. A detailed outlook is given to discuss the future potential of fluidic ultrasonic actuators. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Air-coupled ultrasound KW - Nondestructive testing KW - Fluidics KW - Bistable amplifier KW - Aeroacoustics PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-555271 UR - https://www.ndt.net/search/docs.php3?id=27319 VL - 2022/09 SP - 1 EP - 9 PB - NDT.net CY - Bad Breisig AN - OPUS4-55527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liao, Chun-Man A1 - Bernauer, F. A1 - Igel, H. A1 - Hadziioannou, C. A1 - Niederleithinger, Ernst T1 - Real-time bridge monitoring using ultrasonic techniques combined with six-component (6-C) measurements N2 - This study aims to develop a real time structural health monitoring method by ultrasonic tests combined with advanced six component (6C) translation and rotation measurements. Conventionally, the investigation of the velocity and acceleration response in the translation direction is used to obtain the eigenfrequencies of structures. Recently the measurement of rotation has been considered to fully characterize the dynamic behavior of structures. This research undertakes the evaluation of a novel 6C sensor (IMU50-iXblue) with components originally developed for navigation for the purpose of bridge monitoring. However, as for all vibration recordings, there is a certain influence of environmental conditions (mainly temperature) which may affect evaluation and the results of structural assessment. We propose applying the cross-correlation function to the 6C ambient vibration signals to reconstruct wave propagation and using coda wave interferometry (CWI) to obtain internal velocity variation from waveforms. A field experiment on a large-scale prestressed concrete bridge model is presented. To verify that we are able to identify the pre-stress loss even in presence of temperature effects, we perform measurements in two different scales: the ultrasonic and output-only, vibration measurements. The change in the structural properties due to the pre-stress loss should be detected by the pulse velocity change. The results reveal both the performance and advantages of ultrasonic techniques and the capabilities of 6C sensors. To conclude, the application of CWI to wave signals contributes to a comprehensive assessment for bridge monitoring. T2 - NDT-CE 2022 CY - Zurich, Switzerland DA - 16.08.2022 KW - Structural health monitoring KW - Ultrasonic KW - Coda wave interferometry PY - 2022 SP - 1 EP - 10 AN - OPUS4-55660 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simbruner, Kai A1 - Billone, M. C. A1 - Zencker, Uwe A1 - Liu, Y. Y. A1 - Völzke, Holger T1 - Brittle Failure Analysis of High-Burnup PWR Fuel Cladding Alloys N2 - The general aim of this research is the development of methods for predicting mechanical behavior and identification of limiting conditions to prevent brittle failure of high-burnup (HBU) pressure water reactor (PWR) fuel cladding alloys. A finite element (FE) model of the ring compression test (RCT) was created to analyze the failure behavior of zirconium-based alloys with radial hydrides during the RCT. An elastic-plastic material model describes the zirconium alloy. The stress-strain curve needed for the elastic-plastic material model was derived by inverse finite element analyses. Cohesive zone modeling is used to reproduce sudden load drops during RCT loading. Based on the failure mechanism in non-irradiated ZIRLO® claddings, a micro-mechanical model was developed that distinguishes between brittle failure along hydrides and ductile failure of the zirconium matrix. Two different cohesive laws representing these types of failure are present in the same cohesive interface. The key differences between these constitutive laws are the cohesive strength, the stress at which damage initiates, and the cohesive energy, which is the damage energy dissipated by the cohesive zone. Statistically generated matrix-hydride distributions were mapped onto the cohesive elements and simulations with focus on the first load drop were performed. Computational results are in good agreement with the RCT results conducted on high-burnup M5® samples. It could be shown that crack initiation and propagation strongly depend on the specific configuration of hydrides and matrix material in the fracture area. T2 - 26th International Conference on Structural Mechanics in Reactor Technology - SMiRT 26 CY - Potsdam, Germany DA - 10.07.2022 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Spent Nuclear Fuel KW - Ring Compression Test PY - 2022 SP - 1 EP - 10 AN - OPUS4-55434 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Claudia A1 - Ladu, Luana A1 - Asna Ashari, Parsa A1 - Blind, K. A1 - Castka, P. ED - Jakobs, K. ED - Kim, D.-h. T1 - Digital maturity in the conformity assessment industry: An explorative study from Germany N2 - The services of Conformity Assessment Bodies (CABs) are essential to provide for trust in and safety of digital products and services by demonstrating that requirements from standards are met. Thus, it is vital that CABs are ready to fulfil their tasks also in the digital transformation, having the necessary capabilities and resources. Our study is the first to comprehensively assess the digital maturity in the CA industry and to provide some insights into the readiness of the industry to support and at the same time benefit from the digital age. To this end, we developed and implemented a digital maturity model tailored to the CA industry. In this paper, we present first results from our survey among 354 accredited CABs in Germany. With our research we contribute to better understand the digital transformation and maturation of CABs along distinctive stages. The findings suggest that the transformation process in the CA industry is just at the beginning, with the majority of CABs still in early stages of digital maturity. Also, only a few of them already exploit the latest digital technologies and applications like artificial intelligence, blockchain or big data analytics. Nevertheless, CABs regard digitalization as a big opportunity – for themselves and their industry. T2 - 26th EURAS Annual Standardisation Conference – Standards for Digital Transformation: Blockchain and Innovation CY - Glasgow, Great Britain DA - 08.06.2022 KW - Digital maturity KW - Digital transformation KW - Digitalization KW - Quality infrastructure KW - Conformity assessment KW - Conformity assessment body KW - Testing KW - Certification KW - Inspection KW - Laboratory PY - 2022 SN - 978-3-95886-446-7 SP - 253 EP - 272 PB - Verlag Mainz CY - Mainz AN - OPUS4-55065 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liu, Yung A1 - Völzke, Holger A1 - Zencker, Uwe A1 - Jaunich, Matthias T1 - Cooperation in Advanced Technologies Associated with the Back End of Nuclear Fuel Cycle N2 - A Memorandum of Understanding (MOU) between Argonne National Laboratory (Argonne) and the German Bundesanstalt für Materialforschung und -prüfung (BAM) was signed in October 2014. Its objectives are to promote cooperation among scientists and specialists at Argonne and BAM and establish a framework for collaboration in advanced technologies associated with the back end of the nuclear fuel cycle. Collaborative activities involving Argonne and BAM may be implemented through the promotion of joint research activities and scientific workshops and conferences; exchange of technical information; and visits by scientists, specialists, and graduate, postgraduate, and Ph.D. students. The MOU was renewed in January 2020 for another five years. Highlights of the progress and achievements are provided in identified topical areas for collaboration on ageing management guidance, storage, transportation and disposal R&D, joint conference activities, and conclude with the benefits of the MOU in fostering Argonne and BAM collaboration. T2 - 26th International Conference on Structural Mechanics in Reactor Technology - SMiRT 26 CY - Potsdam, Germany DA - 10.07.2022 KW - Nuclear fuel cycle KW - Back end KW - Spent fuel performance KW - Storage KW - Transportation PY - 2022 SP - 1 EP - 10 AN - OPUS4-55861 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zubia Aranburu, Judith A1 - Cappella, Brunero A1 - Zabala Eguren, A. A1 - Buruaga Lamarain, L. A1 - Aginagalde Lopez, A. A1 - Bonse, Jörn A1 - Schwibbert, Karin T1 - Quantification of the adhesion force of E. coli on Ti via single-cell force spectroscopy N2 - Antibiotic resistance is a growing global problem which poses a massive threat to human health. Although human activity contributes to the acceleration of the process, bacteria have a self-driven stabilisation mechanism to protect themselves from such and other external threats: biofilm formation. Nonetheless, it is the adhesion of a single bacterial cell to a surface that triggers the formation of such network of biomolecules and microorganisms, as well as its hazardous consequences. The main objective of this work was to quantify the adhesion force of a single E. coli cell on a Ti substrate via the AFM-related single-cell force spectroscopy, with both the cell and the substrate material being of high clinical relevance. A set of 25 x 25 force displacement curves was acquired with a maximum force of 3.2 nN without dwell time, yielding a topography map and an adhesion force map that showed to be correlated. A mean adhesion force of 0.85 ± 0.175 nN was measured and the presence of cell appendages on the bacterial cell wall was verified through individual force-displacement curves. Bacterial viability was assessed after the measurements via live/dead staining. T2 - XL Congreso Anual de la Sociedad Española de Ingeniería Biomédica CASEIB 2022 CY - Valladolid, Spain DA - 23.11.2022 KW - Bacteria KW - Atomic force microscopy KW - Force distance curve PY - 2022 SN - 978-84-09-45972-8 SP - 217 EP - 220 AN - OPUS4-57039 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ghafafian, Carineh A1 - Trappe, Volker ED - Vassilopoulos, A. P. ED - Michaud, V. T1 - Fully-reversed fatigue behavior of scarf joint repairs for wind turbine blade shell applications N2 - To enable a quick and cost-effective return to service for wind turbine blades, localized repairs can be executed by technicians in the field. Scarf repairs, shown to be highly efficient with a smooth load transition across angled joint walls and a restored aerodynamic profile, are the focus of this work. The failure mechanisms of these structures were examined under quasi-static tensile and fully-reversed cyclic loading. While the scarf ratio was held constant at 1:50, the repair layup was varied between large-to-small and small-to-large. The effect of the presence of resin pockets and the fiber orientation mismatch between parent and repair material on the restored strength of BIAX ±45° glass fiber reinforced polymer scarf joint structures was studied. T2 - 20th European Conference on Composite Materials CY - Lausanne, Switzerland DA - 26.06.2022 KW - Fatigue KW - Scarf repairs KW - Glass fiber reinforced polymers PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-569646 UR - https://infoscience.epfl.ch/record/298799 SN - 978-2-9701614-0-0 VL - Vol. 5 - Applications and structures SP - 195 EP - 201 PB - Composite Construction Laboratory (CCLab) CY - Lausanne AN - OPUS4-56964 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Trappe, Volker A1 - Sachs, Patrick ED - Vassilopoulos, A. P. ED - Michaud, V. T1 - Dynamic mechanical analysis of epoxy-matrix cross linking measured in-situ using an elastomer container N2 - A new patented dynamic mechanical analysis (DMA) is presented, where the tensile, bending- or torsional stiffness of a media can be characterized in-situ during the phase transition from liquid to solid. An epoxy system, e.g. Hexion L285/H287, is filled into an elastomer container, such as a silicone tube. This can be mounted into a conventional OMA and, based on a linear viscoelastic approach, the storage modulus (E';G'), the loss modulus (E'';G'') and the loss angle tan(δ) can be measured at constant temperature as a function of time in order to investigate the liquid to sol-gel to solid transition. With this new method, the stiffness increase as a result of the cure process can be directly measured more precisely than with a rheometer in a shear plate set-up, because using an elastomer container gives a defined cross section for calculating the Young's modulus. T2 - 20th European Conference on Composite Materials CY - Lausanne, Switzerland DA - 26.06.2022 KW - Cross linking KW - Dynamic mechanical analysis (DMA) KW - Thermoset polymers KW - Cure process PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-569651 UR - https://infoscience.epfl.ch/record/298799 SN - 978-2-9701614-0-0 VL - Vol. 5 - Applications and structures SP - 181 EP - 186 PB - Composite Construction Laboratory (CCLab) CY - Lausanne AN - OPUS4-56965 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -