TY - JOUR A1 - Greiser, Sebastian A1 - Gluth, Gregor A1 - Sturm, Patrick A1 - Jäger, Christian T1 - 29Si{27Al}, 27Al{29Si} and 27Al{1H} double-resonance NMR spectroscopy study of cementitious sodium aluminosilicate gels (geopolymers) and gel-zeolite composites N2 - The influence of starting materials and synthesis route on the properties and the structure of cementitious sodium aluminosilicate gels is not fully understood, partly due their amorphous nature and the fact that they often contain residual reactants, which can make the results of single-pulse NMR spectroscopy applied to these materials difficult to interpret or ambiguous. To overcome some of these limitations, 29Si{27Al} TRAPDOR NMR as well as 27Al{29Si} and 27Al{1H} REDOR NMR spectroscopy were applied to materials synthesized by the one-part alkali-activation route from three different amorphous silica starting materials, including rice husk ash. The latter led to formation of a fully amorphous sodium aluminosilicate gel (geopolymer), while the materials produced from the other silicas contained amorphous phase and crystalline zeolites. Application of the double-resonance NMR methods allowed to identify hydrous alumina gel domains in the rice husk ash-based material as well as significantly differing amounts of residual silica in the three cured materials. Four-coordinated Al existed not only in the aluminosilicate gel framework but also in a water-rich chemical environment with only a small amount of Si in proximity, likely in the alumina gel or possibly present as extra-framework Al in the aluminosilicate gel. The results demonstrate how the employment of different silica starting materials determines the phase assemblage of one-part alkali-activated materials, which in turn influences their engineering properties such as the resistance against chemically/biologically aggressive media. KW - Alkali-activated materials KW - Solid-state NMR KW - Aluminium hydroxide KW - Rice husk ash PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-469353 DO - https://doi.org/10.1039/C8RA09246J SN - 2046-2069 VL - 8 IS - 70 SP - 40164 EP - 40171 PB - Royal Society of Chemistry AN - OPUS4-46935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simoes, R. A1 - Bernades, C. A1 - Joseph, A. A1 - Piedade, F. A1 - Kraus, Werner A1 - Emmerling, Franziska A1 - Diogo, H. A1 - da Piedade, M. T1 - Polymorphism in simvastatin: Twinning, disorder, and enantiotropic phase transitions N2 - : Simvastatin is one of the most widely used active pharmaceutical ingredients for the treatment of hyperlipidemias. Because the compound is employed as a solid in drug formulations, particular attention should be given to the characterization of different polymorphs, their stability domains, and the nature of the phase transitions that relate them. In this work, the phase transitions delimiting the stability domains of three previously reported simvastatin forms were investigated from structural, energetics, and dynamical points of view based on single crystal X-ray diffraction (SCXRD), hot stage microscopy (HSM), and differential scanning calorimetry (DSC) experiments (conventional scans and heat capacity measurements), complemented with molecular dynamics (MD) simulations. Previous assignments of the crystal forms were confirmed by SCXRD: forms I and II were found to be orthorhombic (P212121, Z′/Z = 1/4) and form III was monoclinic (P21, Z′/Z = 2/4). The obtained results further indicated that (i) the transitions between different forms are observed at 235.9 ± 0.1 K (form III → form II) and at 275.2 ± 0.2 K (form II → form I) in DSC runs carried out at 10 K min−1 and close to these values when other types of techniques are used (e.g., HSM). (ii) They are enantiotropic (i.e., there is a transition temperature relating the two phases before fusion at which the stability order is reversed), fast, reversible, with very little hysteresis between heating and cooling modes, and occur under single crystal to single crystal conditions. (iii) A nucleation and growth mechanism seems to be followed since HSM experiments on single crystals evidenced the propagation of an interface, accompanied by a change of birefringence and crystal contraction or expansion (more subtle in the case of form III → form II), when the phase transitions are triggered. (iv) Consistent with the reversible and small hysteresis nature of the phase transitions, the SCXRD results indicated that the molecular packing is very similar in all forms and the main structural differences are associated with conformational changes of the “ester tail”. (v) The MD simulations further suggested that the tail is essentially “frozen” in two conformations below the III → II transition temperature, becomes progressively less hindered throughout the stability domain of form II, and acquires a large conformational freedom above the II → I transition. Finally, the fact that these transitions were found to be fast and reversible suggests that polymorphism is unlikely to be a problem for pharmaceutical formulations employing crystalline simvastatin because, if present, the III and II forms will readily convert to form I at ambient temperature. KW - Polymorphism KW - Twinning KW - Disorder KW - Simvastatine PY - 2018 DO - https://doi.org/10.1021/acs.molpharmaceut.8b00818 SN - 1543-8384 SN - 1543-8392 VL - 15 IS - 11 SP - 5349 EP - 5360 PB - American Chemical Society CY - Washington, DC AN - OPUS4-46927 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas T1 - Broadband dielectric spectroscopy to study soft matter systems N2 - The basics of broadband dielectric spectroscopy were introduced in detail. The analysis of the data was discussed. As application of broadband dielectric spectroscopy the alpha-relaxation (dynamic glass transition) and the chain dynamics of polymers were ilustrated. Further the application of dielectric spectroscopy to polymerbased nanocomposites and high preformance polymers was discussed in detail. T2 - Kolloquiumsvotrag am Karlsruher Instiut of Technology CY - Karlsruhe, Germany DA - 05.12.2018 KW - Broadband dielectric spectroscopy PY - 2018 AN - OPUS4-46910 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breitfeld, Steffen A1 - Scholz, Gudrun A1 - Emmerling, Franziska A1 - Kemnitz, Erhard T1 - BaF-Coordination polymers: Mechanochemical syntheses of new coordination polymers with a direct Ba-F bond N2 - Metal organic frameworks (MOFs) and coordination polymers (CPs) Play an important role in different fields of applications like e.g. catalysis, separations, gas storages, sensors or optoelectronics. Moreover, particularly fluorinated metal-organic frameworks (FMOFs) are in the focus of interest during the last years. Due to the strong electronegativity of fluorine the FMOFs show beside an enhanced thermal stability excellent optical and electrical properties compared to non-fluorinated frameworks. In most cases fluorine is implemented using perfluorinated organic linkers at the synthesis, usually performed by solvothermal synthesis. However, only few examples are known so far where fluorine is coordinated directly to the metal cation. Recently we reported about successful mechanochemical syntheses and characterization of fluorine-containing coordination polymers of alkaline earth metals by milling M(OH)2 (M: Ca, Sr, Ba) with fluorinated benzene dicarboxylic acids. In the present study, it was shown that it is possible to connect fluorine directly to Barium using a mechanochemical synthesis route. A new phase pure barium coordination polymer, BaF-benzene-dicarboxylate (BaF(p-BDC)0.5), was synthesized by milling starting either from barium hydroxide or from barium acetate as sources for barium cations. In both cases the second reactant was 1,4-benzenedicarboxylic acid (H2(p-BDC)). Ammonium fluoride was used as fluorinating agent directly at milling. Although single crystals are not accessible so far and the structure was not solved yet, both the 19F MAS NMR spectrum and the FT IR spectrum give strong evidence that fluorine as well as 1,4-benzenedicarboxylate are connected to barium. This is the first mechanochemical synthesis of coordination polymers where fluorine is directly coordinated to the metal cation. The new compound BaF(p-BDC)0.5 was characterized by X-ray powder diffraction, FT IR- and 19F, 1H-13C CP MAS NMR spectroscopies, DTA-TG and elemental analysis. T2 - Konferenz CY - Oberjoch, Germany DA - 22.07.20108 KW - Mechanochemical syntheses KW - Coordination polymers KW - Direct fluorine-metal bond KW - Alkaline earth metal PY - 2018 AN - OPUS4-46897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Emmerling, Franziska A1 - Tumanov, N. A1 - Tumanova, N. A1 - Fischer, Franziska A1 - Morelle, F. A1 - Ban, V. A1 - Robeyns, K. A1 - Filinchuk, Y. A1 - Wouters, J. A1 - Leyssens, T. T1 - Exploring polymorphism and stoichiometric diversity in naproxen/proline cocrystals N2 - We present naproxen/proline cocrystals discovered when combining enantiopure and racemic naproxen and proline. Using liquid-assisted grinding as the main method to explore the variety of crystal forms in this system, we found 17 cocrystals, of which the structures of only four of them were previously known. The naproxen/proline system exhibited multiple polymorphs of 1 : 1 stoichiometry as well as more rare cocrystals with 1 : 2 and 2 : 3 stoichiometries, two cocrystal hydrates and one cocrystal solvate. In situ ballmilling, used to monitor liquid-assisted grinding reactions, revealed that the solvent dictates the reaction intermediates even if the final reaction product stays the same. Synchrotron X-ray diffraction data collected in situ upon heating allowed us to monitor directly the phase changes upon heating and gave access to pure diffraction patterns of several cocrystals, thus enabling their structure determination from powder X-ray diffraction data; this method also confirmed the formation of a conglomerate in the RS-naproxen/DL-proline system. Proline in cocrystals kept its ability to form charge-assisted head-to-tail N-H⋯O hydrogen bonds, typical of pure crystalline amino acids, thus increasing the percentage of strong chargeassisted interactions in the structure and consequently providing some of the cocrystals with higher melting points as compared to pure naproxen. The majority of drugs are chiral, and hence, these data are of importance to the pharmaceutical industry as they provide insight into the challenges of chiral cocrystallization. KW - In situ KW - Mechanochemistry KW - XRD PY - 2018 UR - https://pubs.rsc.org/en/Content/ArticleLanding/CE/2018/C8CE01338A#!divAbstract DO - https://doi.org/10.1039/c8ce01338a SN - 1466-8033 VL - 20 IS - 45 SP - 7308 EP - 7321 PB - Royal Society of Chemistry CY - London AN - OPUS4-46913 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Chapartegui, Ander A1 - Emmerling, Franziska A1 - Schneider, Rudolf T1 - MOFs as optical sensor elements against endocrine disrupting phthalates N2 - The development of optical sensing technologies for Endocrine Disrupting Chemicals (EDCs) was urgently needed to facilitate currently unmet demands on comprehensive monitoring of These substances, thus ensuring consumer safety. T2 - SALSA CY - Berlin, Germany DA - 01.05.2018 KW - MOF KW - Short chained phthalates PY - 2018 AN - OPUS4-46889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Chapartegui, Ander A1 - Emmerling, Franziska A1 - Schneider, Rudolf T1 - Metal-Organic Frameworks as turn on fluorescent optical sensors against endocrine disrupting phthalate plasticizers N2 - The development of quick and simple optical sensing technologies for Endocrine Disrupting Chemicals (EDCs) is needed to facilitate monitoring of these substances to ensure consumer safety. Optical sensing was achieved against phthalates acting as EDC that have host guest interaction with an intercalated Metal-organic framework (MOF), resulting in a fluorescence emission upon excitation. The fluorescent turn-on signal was generated by using a fluorophore with a structural component that has little fluorescence unless excimers are formed. Strategies to engineer functional MOF structures suitable for sensing EDC phthalates were developed, and the characterization of the MOFs with and without present phthalates was done by single crystal XRD, PXRD, RAMAN and Thermogravimetry. Extensive photo-physical characterization of host-guest complexes of different phthalates and the MOF as well as the resulting exciplex fluorescence was performed. Photo physical characterization revealed an analyte specific fluorescence fingerprint that allows discerning even minute changes in chemical structures of the analyte and therefore paving the way for sensing tools in real world analytical applications. The presented capability of MOFs to sense EDCs is envisioned to complement established methods from analytical chemistry such as mass spectrometry based methods which can’t be used on site and are often associated with infrastructural capacity constraints T2 - EURoptrode CY - Naples, Italy DA - 25.03.2018 KW - MOF KW - Short chained Phthalates PY - 2018 AN - OPUS4-46890 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sobol, Oded A1 - Böllinghaus, Thomas T1 - BAM’s role in materials science and hydrogen in metals: TOF-SIMS imaging N2 - Due to its low mass and high diffusivity in presence of compositional, thermal and mechanical gradients, hydrogen within a metallic microstructure can result in severe loss in ductility even at low concentrations and might lead eventually to a catastrophic and unpredictable failure of structural components during service. In this context, hydrogen mapping at the microscale is still considered among the most important challenges on the pathway towards a better understanding of the hydrogen transport and assisted cracking phenomena in metals, specifically in structural components, e.g. steels. Among the very few available techniques to localize hydrogen at the microscale, Time-of-flight secondary ion mass spectrometry (ToF-SIMS) was proven to be a reliable tool. Based on the assumption that deuterium influence the microstructure similarly to hydrogen, in the following contribution ToF-SIMS was applied as the main technique to detect and locally map the deuterium distribution in several alloys: lean 2101 and standard 2205 duplex stainless steel (DSS), AISI 304L austenitic stainless steel and titanium 6Al-4V alloy. These alloys were selected as case studies in this work due to the wide use of them in many applications and environments which frequently provide critical conditions for hydrogen absorption and assisted degradation. The innovative design of in-situ and ex-situ experiments enabled us to elucidate the permeation, transport and trapping of deuterium in the microstructure in sub-micron resolution for the first time. In addition to the novel experimental setups, further progress was gained by applying computational multivariate data analysis (MVA) on the raw data and data fusion with high resolution structural characterization methods (scanning electron microscopy and electron back-scattered diffraction – SEM/EBSD). This combination allowed us to correlate the deuterium distribution and the influence on the microstructure. T2 - 4th Symposium on Innovative Measurement and Analysis for Structural Materials CY - Tokyo, Japan DA - 13.11.2018 KW - ToF-SIMS KW - Duplex stainless steel KW - Austenitic stainless steel KW - Principal Component Analysis KW - Data-fusion PY - 2018 UR - https://unit.aist.go.jp/tia-co/project/SIP-IMASM/sympo/2018/index.html AN - OPUS4-46867 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sobol, Oded T1 - Hydrogen assisted cracking phenomena in duplex stainless steels elucidated by in- and ex-situ ToF-SIMS experiments N2 - In the presented research, the high potential and abilities of secondary ion mass spectrometry (ToF-SIMS) to detect and locally map the hydrogen distribution in two types of duplex stainless steels are shown. The research validates certain proposed mechanisms by combining ToF-SIMS with high-resolution scanning electron microscopy and electron-backscattered diffraction. The combination of data from several techniques on the same region was conducted in this field for the first time by applying data treatment of the ToF-SIMS raw data and data fusion approach. This powerful combination of methods allows reviewing of the occurring processes related to hydrogen assisted cracking. The step beyond the state of the art in this field was gained here by developing permeation and mechanical loading experiments within the ToF-SIMS during chemometric imaging of the hydrogen distribution in the microstructure. The research presents the necessary correlation between the hydrogen distribution and the resulted structural changes, the diffusion behavior in a duplex microstructure and stress induced diffusion of hydrogen by applying external load at the microscale. T2 - 6th WMRIF Early Career Scientist Summit CY - NPL Teddington UK DA - 18.06.2018 KW - ToF-SIMS KW - Duplex stainless steel KW - LDX KW - EBSD KW - Data-fusion PY - 2018 AN - OPUS4-46865 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Jörg T1 - Sekundärstrahlungsemission bei der UKP-Laser-Anwendung: Herausforderung für die Arbeitssicherheit N2 - Im Vortrag werden die Risiken, insbesondere die unerwünschte Erzeugung von Röntgenstrahlung, bei der Nutzung ultrakurzer Laserimpulse in der Materialbearbeitung beschrieben. Neue Anforderungen an den Arbeitsschutz werden dargestellt. T2 - SPECTARIS, Deutscher Industrieverband für optische, medizinische und mechatronische Technologien e.V., Veranstaltung Technische Kommission Photonik CY - Berlin, Germany DA - 27.11.2018 KW - Ultrakurze Laserimpulse KW - Materialbearbeitung KW - Röntgenstrahlung KW - Arbeitsschutz PY - 2018 AN - OPUS4-46859 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krüger, Jörg T1 - Femtosecond laser-assisted photovoltaic bottom-up strategies N2 - A promising technology in photovoltaics is based on micro-concentrator solar cells, where the photovoltaic active area is realized as an array of sub-millimeter sized thin-film solar cells. Different approaches to produce micro-sized precursors of CIGSe absorbers on molybdenum are presented using 30-fs laser pulses at 790 nm wavelength. On the one hand, a multi pulse surface structuring of the molybdenum or the underlying glass substrate and a subsequent physical vapor deposition (PVD) process were used for a site-selective aggregation of indium droplets. On the other hand, a single pulse laser-induced forward transfer (LIFT) was utilized to selectively deposit combined copper/indium/gallium precursor pixels on the molybdenum back contact of the solar cell. It was demonstrated that a postprocessing of the laser-generated micro-sized precursors results in an array of working CIGSe solar cells with an efficiency of 2.9% for 1 sun Illumination. T2 - Leibniz-Institut für Oberflächenmodifizierung (IOM), Institutskolloquium CY - Leipzig, Germany DA - 29.11.2018 KW - Femtosecond laser patterning KW - Laser-induced forward transfer KW - CIGSe KW - Micro solar cell KW - Light concentration PY - 2018 AN - OPUS4-46831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Abad Andrade, Carlos Enrique A1 - Florek, S. A1 - Becker-Ross, H. A1 - Huang, M.-D. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Radtke, Martin A1 - Lippitz, Andreas A1 - Hodoroaba, Vasile-Dan A1 - Schmid, Thomas A1 - Heinrich, Hans-Joachim A1 - Recknagel, Sebastian A1 - Jakubowski, Norbert A1 - Panne, Ulrich T1 - Zirconium permanent modifiers for graphite furnaces used in absorption spectrometry: understanding their structure and mechanism of action N2 - The mechanism of action of zirconium permanent modifiers on graphite surfaces was investigated in order to understand its influence on the analytical signal in atomic and molecular absorption spectrometry (AAS/MAS). For this, the molecule formation of CaF was studied, which is used for the indirect analytical determination of fluorine in high-resolution continuum source graphite furnace molecular absorption spectrometry (HR-CS-GFMAS). The kinetics of this reaction was established by monitoring its molecular spectrum at different atomisation temperatures. An Arrhenius plot showed a pseudo-first order reaction with respect to fluorine (n = 1). An intermediate state was isolated, and its structure was elucidated by spectroscopic methods: scanning electron microscopy with energy dispersive X-ray spectroscopy (SEMEDX), X-ray photoelectron spectroscopy (XPS), X-ray absorption spectroscopy (XANES and EXAFS), and Raman microspectroscopy. We propose here a mechanism, where ZrO2 acts as a heterogeneous catalyst: after a pyrolytic step, an intermediate state of ZrO(OCaF) is activated, and at higher temperatures, CaF(g) is released from the zirconium-coated graphite surface. No evidence of the formation of zirconium carbide was found. Consequently, as the CaF formation is catalysed by a heterogeneous catalyst, surface modifications with ZrO2 nanoparticles and ZrO xerogels were investigated in order to increase the surface area. Their influence was evaluated in the molecule formation of CaF, CaCl, CaBr, and CaI. Graphite furnace modification with zirconium oxide nanoparticles proves to be the best choice for fluorine analysis with a signal enhancement of more than eleven times with respect a non-coated graphite furnace. However, the influence of zirconium modifications in the analytical signals of Cl, and I is lower than the F signals or even negative in case of the Br. Understanding zirconium modifiers as heterogeneous catalysts offers a new perspective to AAS and MAS, and reveals the potential of surface analytical methods for development of improved permanent modifiers and graphite furnace coatings. KW - Zirconium KW - HR-CS-MAS KW - Graphite furnace KW - Nanoparticles KW - Xerogel KW - Calcium monofluoride KW - Absorption spectrometry PY - 2018 UR - https://pubs.rsc.org/en/content/articlelanding/2018/ja/c8ja00190a DO - https://doi.org/10.1039/C8JA00190A SN - 0267-9477 VL - 33 IS - 12 SP - 2034 EP - 2042 PB - Royal Society of Chemistry AN - OPUS4-46775 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Emmerling, Franziska T1 - Mechanistic investigations of mechanosyntheses N2 - Mechanochemistry is a fast and efficient method applicable for the synthesis of new organic, metal-organic, and inorganic compounds. The direct monitoring of milling reactions is still challenging. The underlying reaction mechanisms often remain unclear. In the last years, we have established a tandem in situ approach for investigating mechanochemical reactions using time-resolved in situ XRD coupled with Raman spectroscopy. A further development is the in situ coupling of synchrotron XRD, Raman spectroscopy, and thermography allowing the observation of mechanochemical reactions in real time. [5] Information on the crystalline, molecular, and temperature state of the materials during grinding could be collected. The chemical composition of the reaction mixture was found to be directly correlated with changes in the temperature profile of the reaction. Furthermore, the presented setup allows the detection of crystalline, amorphous, eutectic as well as liquid intermediates. Based on these data, metastable polymorphs of cocrystals and coordination polymorphs could be isolated and struc-turally characterized. A multi-step diffusion mechanism was identified for most systems. Crystalline phases were obtained intermediately, suggesting that the synthesis is following Ostwald’s rules of stages. The resulting deeper kinetic and thermodynamic understanding of milling processes is the key for future optimization of mechanochemical syntheses. T2 - Beilstein Symposium MECHANOCHEMISTRY: MICROSCOPIC AND MACROSCOPIC ASPECTS CY - Rüdesheim, Germany DA - 13.11.2018 KW - Mechanochemistry KW - Phosphonates KW - In situ PY - 2018 AN - OPUS4-46758 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinrich, Thomas T1 - BAM and Division 6.1 N2 - This is a short overview of BAM and Division 6.1. We have insight into BAM's roles and responsibilities and the work we are doing in Division 6.1. T2 - Visit at CSEM Landquart CY - Landquart, Switzerland DA - 13.08.2018 KW - ToF-SIMS KW - AES KW - XPS KW - SEM PY - 2018 AN - OPUS4-46765 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kunz, Valentin A1 - Kjaervik, Marit A1 - Müller, Anja A1 - Hodoroaba, Vasile-Dan A1 - Unger, Wolfgang T1 - How to meet new challenges in advanced nanoparticle analytics N2 - Three current research projects performed at BAM’s Division for Surface Analysis and Interfacial Chemistry are presented that tackle important challenges with regard to the characterization of nanomaterials: 1) The characterization at ambient pressure, 2) the investigation of core-shell nanoparticles, and 3) the characterization of non-spherical particles by electron microscopy. 1) Surface analytical techniques such as Photoelectron Spectroscopy (XPS) or Secondary Ion Mass Spectrometry (SIMS) typically require measurements in ultra-high vacuum. However, for many applications (e.g. catalysis and nanotoxicology) it is important to know the surface chemical properties of nanomaterials at ambient conditions. Therefore, near-ambient pressure X-ray photoelectron spectroscopy (NAP-XPS) was used to investigate nanoparticles in suspension. The used instrumental set-up allows to directly insert nanoparticle suspensions into the analysis chamber and to measure without prior sample preparation. Compared to dry reference samples measured under high-vacuum, a shift towards higher binding energies was observed for silver nanoparticles in water, indicating a change of surface potential at the water-nanoparticle interface. 2) To determine the dimensions of core-shell nanoparticles (shell thickness, core and total diameter), scanning transmission X-ray microscopy (STXM) was used. The analyzed model system consists of a polytetrafluorethylene (PTFE) core surrounded by a polystyrene (PS) shell, providing a strong X-ray absorption contrast at the C K-edge and a well-defined interface. The introduced STXM‐based methodology yields particle dimensions in agreement with scanning electron microscopy (SEM) results and provides additional information such as the position of the particle core, which cannot be extracted from a SEM micrograph. 3) The accurate measurement of size distributions of non-spherically shaped nanoparticles (representing most of the industrial nanoparticulate materials) is a challenging analytical task. High-resolution electron microscopy (TEM and SEM) is best suited to access the shape of individual nanoparticles. To fill the gap between ideal, monodisperse particles of spherical shape and complex real-world samples, BAM has started the work to develop reference nanoparticles of controlled shape, such as TiO2 platelets, bipyramids, and elongated particles. Results of a recent ISO inter-laboratory comparison will be shown with emphasis on the measurement parameters, descriptors and data analysis. T2 - NanoSafe Conference 2018 CY - Grenoble, France DA - 5.11.2018 KW - Nanoparticles PY - 2018 AN - OPUS4-46730 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sachse, René A1 - Hertwig, Andreas A1 - Hodoroaba, Vasile-Dan A1 - Krähnert, R. T1 - Multi-method analysis of pore-controlled mesoporous oxide materials N2 - Determining the porosity of catalytic layers is crucial for quality assurance. We present results of a multi-method study to determine thickness, porosity, dielectric function and other properties of pure and mixed iridium and titanium oxide layers used in electrocatalytic water splitting. T2 - European Optical Society Biennial Meeting (EOSAM) 2018 CY - Delft, The Netherlands DA - 08.10.2018 KW - Multi-method analysis KW - Mesoporous oxide materials KW - Electro catalytic water splitting KW - Electron probe X-ray microanalysis (EPMA) KW - Spectroscopic ellipsometry (SE) KW - Optical porosimetry PY - 2018 AN - OPUS4-46740 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altmann, Korinna A1 - Eisentraut, Paul A1 - Goedecke, Caroline A1 - Ricking, Mathias A1 - Bannick, Claus-Gerhard A1 - Braun, Ulrike T1 - Freshwater compartments: Screening method for polymer identification and mass contents of microplastic particles using TED-GC-MS N2 - The pathways of plastics, especially of microplastic (MP), in environmental compartments, particularly in aquatic systems, are not well understood. The critical point is the lack of fast, harmonised methods for sampling, sample preparation and sample analysis. These three analytical steps are dependent on one another and must be optimised. In recent years, we developed a method for representative sampling and fast detection of MP in aqueous systems. The sampling in different freshwater bodies is performed in the field with a fractionated filtration system using mesh sizes of 500, 100 and 50 µm. For water with an intermediate or high content of suspended particular matter a minimum of 1000 L has to be filtered. In the lab, mesh sizes of 10 and 5 µm are used for further filtration. Subsequently, the water filtrates of the different particle size classes are sterilised, dried, weighed and homogenised, if necessary. Conventional methods for MP analysis are infrared and raman spectroscopy, giving information on the shapes and numbers of individually identified MP particles. Our focus is on the determination of mass contents of various polymers potentially contained in environmental samples. For qualitative and quantitative MP detection TED-GC-MS is used, a two-step method based on gas chromatography-mass spectrometry (GC-MS) with previous thermal extraction. This method not only enables us to screen the samples for characteristic marker-molecules, thus identifying single polymers, but furthermore allows the calculation of mass contents of individual polymers. In the present work, different freshwater compartments were exemplarily studied to identify containing polymers and calculate their mass content in MP particles. T2 - MICRO2018 CY - Lanzarote, Spain DA - 19.11.2018 KW - Microplastic KW - TED-GC-MS KW - Mass contents PY - 2018 AN - OPUS4-46739 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sobol, Oded A1 - Röhsler, Andreas A1 - Nolze, Gert A1 - Unger, Wolfgang A1 - Böllinghaus, Thomas T1 - Sputtering derived artefacts in austenitic steel during Time-of-Flight Secondary Ion Mass Spectrometry analyses N2 - Among the very few techniques to localize hydrogen (H) at the microscale in steels, Time-of-flight secondary ion mass spectrometry (ToF-SIMS) was proven to be a reliable tool. The necessity to detect hydrogen stems from its deleterious effects in metals, that are often used as structural components and to obtain better understanding of the underlying metallurgical mechanisms of hydrogen embrittlement (HE) which are still unclear. Austenitic stainless steels are nowadays commonly used in a wide variety of application, from hydrogen transport and storage facilities to petrochemical and offshore applications where they are exposed to aggressive environments and therefore prone to HE. One of the greater risks in the austenitic class is the embrittlement of the material due to the instability of the γ austenite and its transformation into a brittle α martensitic phase. This transformation takes place due to the local stresses that are induced by the uptake of hydrogen during service. Nonetheless, it was shown that this transformation can occur as an artefact during SIMS analysis itself where Cs-sputtering is necessary not only to remove surface contaminations but mainly to enhance H/D secondary ion yield. In the following contribution we show the influence of different sputtering conditions on AISI 304L austenitic stainless steel in order to distinguish the artefact from the hydrogen induced transformation. The material was charged electrochemically in a deuterium based electrolyte. Deuterium (D) must be in these experiments as a replacement for hydrogen which cannot be used because adsorbed hydrogen superimposes hydrogen originating from charging the sample in the SIMS images. ToF-SIMS analyses were conducted by ToF SIMS IV (IONTOF GmbH, Münster, Germany). The experiments were carried out on deuterium charged and non-charged samples. The structural characterization was carried out by SEM and EBSD examinations before and after charging, both with a Leo Gemeni 1530VP field-emission scanning electron microscope and a Zeiss Supra 40 instrument (Carl Zeiss Microscopy GmbH, Oberkochen, Germany). The results showed that the use of 1keV Cs+ beam induces stacking faults while higher sputter beam energies results in γ→α transformation. T2 - SIMS Europe 2018 CY - Münster, Germany DA - 16.09.2018 KW - Austenitic steel KW - Hydrogen KW - ToF-SIMS KW - Artefact PY - 2018 AN - OPUS4-46701 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kricheldorf, H. T1 - Transesterification in alcohol-initiated ROPs of l- and meso-lactide catalyzed by Sn(II) and Sn(IV) compounds at low temperatures N2 - The purpose of this study is to shed more light on the transesterification processes in alcohol-initiated and tin(II) 2-ethylhexanoate (SnOct2)-catalyzed polymerizations of lactides at low or moderate temperatures. Ethanol-initiated polymerizations are conducted in concentrated solutions at 80 °C and a strong dependence of even/odd equilibration on the alcohol/Sn ratio. Around or above 120 °C cyclization of poly(l-lactide) via “backbiting” occurs as a third mechanism. However, poly(m-lactide) shows a higher cyclization tendency and yields cyclics even at 100 °C. Combinations of ethanol and certain cyclic dibutyltin(IV) catalysts also yield cyclic oligomers of l-lactide at 80 °C. Reaction conditions allowing for a total suppression of all transesterification reactions are not found, but even-numbered poly(m-lactide)s with a purity >95% are obtained at 70 or 60 °C. KW - Cyclization KW - MALDI-TOF MS KW - Polyester KW - Polylactide KW - Transesterification PY - 2018 DO - https://doi.org/10.1002/macp.201800445 SN - 1022-1352 SN - 1521-3935 VL - 219 IS - 24 SP - 1800445, 1 EP - 10 PB - Wiley-VCH CY - Weinheim AN - OPUS4-46705 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schönhals, Andreas T1 - Thin polymer films as model systems for polymer nanocomposites N2 - Polymers at interfaces play a major role in a broad variety of applications ranging from engineering purposes (for instance polymer based nanocomposites) to high tech implications (for instance light emitting diodes). Here, thin films with thicknesses down to few nanometers are prepared on different substrates as model systems for polymer composites. The thin films are investigated by a combination of surface analytical and volume sensitive methods. As surface analytical methods atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), and contact angle measurements (CAM) are employed. As volume sensitive broadband dielectric spectroscopy (BDS), specific heat spectroscopy (SHS), and ellipsometry are used. Especially attention is paid to understand the glass transition behavior of thin films because the glass transition is the key phenomenon determines the application of polymers also in thin films. To understand the glass transition behavior of thin films, which is controversially discussed in literature, a three layer model is discussed. Firstly, a mobile surface layer is assumed at polymer air interface of the film due to missing of segment/segment interactions. Secondly, in the middle of the film a bulk-like layer should be expected. Thirdly, for polymers having non-repulsive interactions with the substrate an irreversibly adsorbed layer is expected to be formed. Due the adsorption the molecular mobility of the segments in this layer is slowed down. What is measured for the glass transition of thin films is a complicated average of all of these effects. The different layers are hardly to address separately. Therefore, in the presentation especially model systems are selected and investigated to verify the layer model. T2 - Kolloquiumsvortrag and der Universität des Saarlandes CY - Saarbrücken, Gemany DA - 20.11.2018 KW - Thin polymer films PY - 2018 AN - OPUS4-46692 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schönhals, Andreas A1 - Zorn, R. T1 - Quasi-elastic scattering of high free volume polymers by neutron time-of-flight spectroscopy N2 - Experimental report to proposal 13562 Quasi-elastic scattering of the polymer with intrinsic microporoasity PIM-1 is measured by neutron time-of-flight spectroscopy and discussed. KW - Neutron scattering KW - PIM-1 PY - 2018 SP - 1 EP - 2 CY - Garching AN - OPUS4-46693 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Anja A1 - Radnik, Jörg A1 - Lippitz, Andreas A1 - Unger, Wolfgang T1 - Progress Talk 3 / Non-destructive depth profiling of core-shell nanoparticles by ER-XPS N2 - This presentation deals with the progress between month twenty and twenty-nine of my PhD thesis. I prepared it, in order to update my supervisor Prof. Kemnitz and my colleagues from the department of chemistry at the Humboldt-Universität zu Berlin (HU). T2 - Working Group Meeting of Prof. Erhard Kemnitz CY - Humboldt-Universität zu Berlin (HU), Germany DA - 20.11.2018 KW - ER-XPS KW - Synchrotron KW - Core-shell nanoparticles KW - Depth-profiling PY - 2018 AN - OPUS4-46676 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Goedecke, Caroline A1 - Altmann, Korinna A1 - Eisentraut, Paul A1 - Bannick, C. G. A1 - Braun, Ulrike T1 - Mikroplastik - Suchen und Finden N2 - Der Vortrag stellt spektroskopische und neue thermoanalytische Verfahren zum Nachweis von Mikroplastik in Umweltproben vor. Ein spezieller Fokus liegt auf dem neu entwickelten Verfahren der TED-GC-MS. Zusätzlich wird gezeigt, wie die TED-GC-MS eingesetzt werden kann, um Reifen in der Umwelt zu bestimmen. T2 - Fachforum Ressourcen - Kunststoffe und Nachhaltigkeit CY - Leverkusen, Germany DA - 06.11.2018 KW - Mikroplastik KW - TED-GC-MS KW - Thermoanalytische Verfahren KW - Spektroskopische Verfahren PY - 2018 AN - OPUS4-46652 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brandl, F. A1 - Thünemann, Andreas A1 - Beuermann, S. T1 - Poly(meth)acrylate-PVDF core–shell particles from emulsion polymerization: preferential formation of the PVDF β crystal phase N2 - A facile and convenient approach for the synthesis of core–shell particles via emulsion polymerization is presented. The shell consists of poly(vinylidene fluoride) (PVDF) and the core of poly(methyl methacrylate) (PMMA), poly(glycidyl methacrylate) (PGMA) or poly(methyl acrylate) (PMA). In a first step, a non-fluorinated (meth)acrylate monomer is polymerized in the emulsion to produce poly(meth)acrylate core particles. Secondly, vinylidene fluoride (VDF) is directly added to the reactor and polymerized for shell formation. Small-angle X-ray scattering (SAXS) was employed to characterize the structure of the core–shell particles. Interestingly, the particles’ core contains fluorinated and non-fluorinated polymers, whereas the shell of the particles consists only of PVDF. The resulting particles with a diameter of around 40 nm show a significantly higher PVDF β phase content than the PVDF homopolymer obtained by emulsion polymerization KW - Small-angle x-ray scattering KW - SAXS KW - Nanopatricle KW - Polymer PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-465910 DO - https://doi.org/10.1039/C8PY01236A SN - 1759-9954 SN - 1759-9962 VL - 9 IS - 44 SP - 5359 EP - 5369 PB - The Royal Society of Chemistry AN - OPUS4-46591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schütter, Jan T1 - Tailored Micro- and Nanostructured Surfaces for Bacterial Attachment Studies N2 - To investigate the attachment behavior of bacteria, tailored surfaces are needed. Differences in the chemical charge of the substrate are varied by -COO-, -CH3, -OH, -NH3 terminated functional groups. Regular patterns of them on the surfaces enable bacteria to choose their preferred attachment sides. Tools to tailor the samples are µ-contact printing, self-assembled monolayers and physical vapor deposition. The same concept of preferred sides in patterned surfaces is transferred to the nano- and microroughness which is accomplished by using zinc oxide nanorods synthesis. T2 - PhD Retreat CY - Warnemünde, Germany DA - 28.09.2018 KW - ZnO nanorods KW - µ-contact printing KW - Surface modification KW - Microbial induced corrosion PY - 2018 AN - OPUS4-46577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Nanoanalytik-Aktivitäten @ BAM N2 - In dieser Präsentation werden Aktivitäten im Bereich der 'nano'-Charakterisierung bei der BAM vorgestellt. Beispiele von F&E-Projekten und -Kooperationen im nano-Analytik-Bereich bei der BAM werden genannt. Thematische Kooperations-Möglichkeiten zwischen BAM und dem Netzwerk NanoAnalytik und -Messtechnik in der Produktion werden diskutiert. T2 - Treffen des Netzwerkes NanoAnalytik und -Messtechnik CY - Berlin, Germany DA - 06.11.2018 KW - Nanoanalytik KW - Nano-Projekte KW - Nano-Kompetenzzentrum KW - Nano-Charakterisierung PY - 2018 UR - https://www.nanoinitiative-bayern.de/nanoanalytik/ AN - OPUS4-46563 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Anja A1 - Unger, Wolfgang A1 - Wirth, Thomas A1 - Kjaervik, Marit A1 - Cant, D. A1 - Shard, A. A1 - Clifford, C. T1 - Measurement of the thickness and nature of nanoparticle coatings - ISO/PWI TR 23173 N2 - This presentation explains the outline and scientific content of the ISO technical report 23173 "Measurement of the thickness and nature of nanoparticle coatings using electron spectroscopies". This technical report deals with those electron spectroscopy methods that are able to determine the coating thickness of nanoparticles. This specifically includes X-ray photoelectron spectroscopy (XPS), energy-resolved X-Ray photoelectron spectroscopy (ERXPS) using synchrotron radiation, near abient pressure photoelectron spectroscopy (NAPXPS) and Auger electron spectroscopy (AES). T2 - 18. Sitzung des DIN-Normenausschusses 062-08-16 AA CY - Berlin, Germany DA - 08.11.2018 KW - Core-shell nanoparticles KW - Electron spectroscopy KW - XPS KW - Synchrotron radiation KW - AES PY - 2018 AN - OPUS4-46550 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kjaervik, Marit A1 - Unger, Wolfgang T1 - New work item proposal for a technical report for ISO/TC 201 WG4 “Surface characterization of biomaterials”: Surface chemical analysis – Surface chemical analysis of cells and biofilms N2 - The proposed ISO Technical Report provides a description of a variety of physical methods of analytical chemistry by which bacteria and biofilms can be analysed. The state of the art, sample requirements and strengths associated with each method are identified. Presented at the DIN-meeting for NA 062-08-16 AA „Chemische Oberflächenanalyse und Rastersondenmikroskopie“ T2 - 18. Sitzung des DIN-meeting NA 062-08-16 AA "Chemische Oberflächenanalyse und Rastersondenmikroskopie“ CY - Berlin, Germany DA - 08.11.2018 KW - 3D nano SIMS KW - Fourier transform infrared spectroscopy KW - Raman-spectroscopy KW - Biofilms KW - XPS PY - 2018 AN - OPUS4-46548 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Diehn, Sabrina A1 - Zimmermann, B. A1 - Bagcioglu, M. A1 - Seifert, Stephan A1 - Kohler, A. A1 - Ohlson, M. A1 - Fjellheim, S. A1 - Weidner, Steffen A1 - Kneipp, Janina T1 - Matrix-assisted laser desorption/ionization time-of-flight mass spectrometry (MALDI-TOF MS) shows adaption of grass pollen composition N2 - MALDI time-of-flight mass spectrometry (MALDI-TOF MS) has become a widely used tool for the classification of biological samples. The complex chemical composition of pollen grains leads to highly specific, fingerprint-like mass spectra, with respect to the pollen species. Beyond the species-specific composition, the variances in pollen chemistry can be hierarchically structured, including the level of different populations, of environmental conditions or different genotypes. We demonstrate here the sensitivity of MALDI-TOF MS regarding the adaption of the chemical composition of three Poaceae (grass) pollen for different populations of parent plants by analyzing the mass spectra with partial least squares discriminant analysis (PLS-DA) and principal component analysis (PCA). Thereby, variances in species, population and specific growth conditions of the plants were observed simultaneously. In particular, the chemical pattern revealed by the MALDI spectra enabled discrimination of the different populations of one species. Specifically, the role of environmental changes and their effect on the pollen chemistry of three different grass species is discussed. Analysis of the Group formation within the respective populations showed a varying influence of plant genotype on the classification, depending on the species, and permits conclusions regarding the respective rigidity or plasticity towards environmental changes. KW - Pollen KW - MALDI-TOF MS KW - Classification KW - Partial least square discriminant analysis (PLS-DA) KW - Principal component analysis (PCA) PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-465294 DO - https://doi.org/10.1038/s41598-018-34800-1 SN - 2045-2322 VL - 8 IS - 1 SP - 16591, 1 EP - 11 PB - Nature AN - OPUS4-46529 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fortini Moustafa Osman, Renata A1 - Kehren, D. A1 - Meyer-Plath, A. A1 - Sturm, Heinz T1 - Development of a method for measuring the rigidity of nanofibers N2 - Over the past decades, the growing industry working for lightweight constructions has demanded materials exhibiting improved properties such as higher mechanical modulus and strength, better chemical resistance and lower costs of production. It is known that especially nanofibers tend to enhance the mechanical, thermal and electrical properties of polymers. Therefore, some types of nanofibers are already being used embedded in polymeric matrix of sports equipment, aircraft parts and automobile components. However, nanofibers are a relatively new material category, the consequences of which for mankind are not yet fully known. Nanofibers detached from polymeric materials can be released into the environment during, e.g., processing and aging. The risks in dealing with such nanofibers are generally unknown, even if further studies of health aspects are being carried out. Problems always arise when the fibers can penetrate the cells, thus the mechanical rigidity of nanofibers is a key factor in assessing the risks. Common methods describe the geometry of nanofibers. These methods are necessary, but not sufficient to describe the mechanical properties, as for during manufacture and aging these properties may change; the modulus and strength values may differ from those of the original fibers. Different experimental techniques for nanomechanical testing have been studied using the atomic force microscope, the scanning electron microscope and transmission electron microscope, showing promising results. This project aims to evaluate the bending stiffness of CNTs with an experimental setup within the Dynamic Scanning Electron Microscope. Based on the Euller-Bernoulli beam theory, the Young’s modulus of CNTs can be obtained using the resonance frequency of mechanically excited nanofibers, its dimensions and density. The resonance frequency is acquired by extracting the signals of the secondary electrons when the nanofibers show significant vibration movement, also possible to be seen on the microscope images. The electronic signals of the secondary electrons are filtered and treated by a lock-in amplifier, so the corresponding amplitude and phase values can be evaluated. This method could be applied to any nanofiber that has the shape similar to a symmetric beam. T2 - Workshop on Reference Nanomaterials Current situation and needs: development, measurement, standarization CY - Berlin, Germany DA - 14.05.2018 KW - Nanofiber KW - Rigidity KW - Resonance KW - DySEM PY - 2018 AN - OPUS4-46527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Smales, Glen Jacob A1 - Pauw, Brian Richard A1 - Thünemann, Andreas T1 - THE MAUS: A GI-/ULTRA-/W/SAXS Instrument of the future N2 - The Multi-scale Analyzer for Ultrafine Structures or the “MAUS” for short, is a SAXS instrument that combines a multitude of features that make it both unique, and one of the most adaptable instruments around. T2 - SAS2018 CY - Traverse City, MI, USA DA - 07.10.2018 KW - SAXS KW - MAUS KW - Small-angle scattering KW - DAWN KW - Grazing incidence PY - 2018 AN - OPUS4-46523 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Julia A1 - Almalla, Ahed A1 - Özcan Sandikcioglu, Özlem T1 - AFM-Untersuchungen von funktionellen Beschichtungen und Strukturänderungen unter mechanischer Beanspruchung N2 - Die Rasterkraftmikroskopie (AFM) hat sich in den letzten Jahren als eine vielseitige Abbildungstechnik von Oberflächen mit einer sehr hohen Ortsauflösung etabliert. Über die Untersuchung der reinen Oberflächentopographie sind erweiterte Modi in der Lage, gleichzeitig Informationen über die elektrischen und magnetischen Eigenschaften sowie Adhäsionsprozesse auf Oberflächen zu liefern. Interessanter wird es, wenn das AFM mit geeigneten Messzellen für in-situ-Untersuchungen in kontrollierten Atmosphären oder in Elektrolyten unter elektrochemischer Kontrolle ausgestattet ist. Dies ermöglicht die Untersuchung von Korrosions- und Adhäsionsprozessen unter Bedingungen, die die Betriebsumgebung repräsentieren. Ein aktueller Forschungsschwerpunkt unseres Fachbereiches liegt in den Untersuchungen der Deformationseigenschaften von Funktionsschichten auf Leichtmetalllegierungen, sowie in situ Untersuchungen des Korrosionsverhaltens unter kombinierter korrosiver und mechanischer Beanspruchung mittels AFM. Durch die Integrierung eines Zug-Druckmoduls in den Probentisch des Rasterkraftmikroskops haben wir jetzt die Möglichkeit, verschiedene Materialien uniaxialen Umformversuchen mit bis zu 5 kN Kraft zu unterziehen. Dabei können unter anderem auch zyklische Belastungen genutzt werden, um Ermüdungsprozesse zu simulieren. Da die Messungen in situ ohne die De- und Remontage der Probe durchgeführt werden, ermöglicht der Aufbau nicht nur Messungen mit präziser Positionssteuerung, sondern auch die Untersuchung von Prozessen im elastischen Bereich, die für die Aufklärung der Mechanismen, die zu Ermüdungsversagen führen, entscheidend sind. Die Posterpräsentation wird detaillierte Informationen zum neuen AFM-Setup liefern und unsere aktuellen Ergebnisse zur Verformung dünner Schutzschichten auf AA2024-T3 zusammenfassen. T2 - Hybrid, Materials and Structures CY - Bremen, Germany DA - 18.04.2018 KW - Kelvinsondenkraftmikroskopie KW - Funktionelle Beschichtungen KW - Kombinierete korrosive und mechanische Beanspruchung KW - Lokale Korrosion KW - Delamination KW - Deformation PY - 2018 AN - OPUS4-46522 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jemian, P. A1 - Jackson, A. A1 - Richter, T. A1 - Butler, P. A1 - King, S. A1 - Rennie, A. A1 - Pauw, Brian Richard T1 - NXcanSAS: standard to store reduced SAS data of any dimension N2 - A SAS-specific extension of the NeXus file standard has been put together for the community to interchangably store measurement data, accompanied by all possible metadata. T2 - XVII International Small Angle Scattering Conference - SAS2018 CY - Traverse City, Michigan, USA DA - 07.10.2018 KW - Small-angle scattering KW - Data standard KW - NeXus KW - Archival format KW - Quality PY - 2018 AN - OPUS4-46521 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Snow, T. A1 - Pauw, Brian Richard A1 - Smith, A. A1 - Terrill, N. A1 - Thuenemann, Andreas T1 - Modular SAXS data corrections N2 - A standardized methodology for the correction of scattering patterns, the calculation of uncertainties, the subtraction of backgrounds and solvents, optionally followed by the azimuthal averaging/reduction step, is presented. T2 - XVII International Small Angle Scattering Conference - SAS2018 CY - Traverse City, Michigan, USA DA - 07.10.2018 KW - Small-angle scattering KW - Software KW - Sata corrections KW - Quality PY - 2018 AN - OPUS4-46520 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pauw, Brian Richard A1 - Smith, A. A1 - Snow, T. A1 - Shebanova, O. A1 - Hermida Merino, D. A1 - Smales, Glen Jacob A1 - Sutter, J. A1 - Ilavsky, J. A1 - Terrill, N. A1 - Thuenemann, Andreas A1 - Bras, W. T1 - Enhancing your SAXS with interleaved USAXS for less than 50 k€ N2 - A portable, inexpensive module is presented that can enhance good existing SAXS instruments by offering an extension on the angular range to include the ultra-small-angles. The instrument has been shown to work for interleaved SAXS/USAXS experiments. T2 - XVII International Small Angle Scattering Conference - SAS2018 CY - Traverse City, Michigan, USA DA - 07.10.2018 KW - Small-angle scattering KW - USAXS KW - Bonse Hart KW - Instrumentation KW - Data analysis PY - 2018 AN - OPUS4-46519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pauw, Brian Richard A1 - Kaestner, Claudia A1 - Thuenemann, Andreas T1 - How good is SAXS? Results from a large Round Robin on an easy sample N2 - 22 laboratories returned 45 small-angle scattering datasets on a suspension of silver nanoparticles. The variance of the results has been analyzed in order to estimate the expected accuracy and precision of the small-angle scattering technique. T2 - XVII International Small Angle Scattering Conference - SAS2018 CY - Traverse City, Michigan, USA DA - 07.10.2018 KW - Small-angle scattering KW - Round Robin KW - Silver nanoparticles KW - Quality KW - McSAS PY - 2018 AN - OPUS4-46518 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pauw, Brian Richard A1 - Breßler, Ingo T1 - McSAS for SAS analysis: Usage, Benefits and Potential Pitfalls N2 - An introductory lecture for users at the Diamond Light Source, on how to use the McSAS software to analyze their data. T2 - Small Angle Scattering Training School CY - Diamond Light Source, Didcot, United Kingdom DA - 04.06.2018 KW - Small-angle scattering KW - Software KW - Analysis PY - 2018 AN - OPUS4-46517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witt, Julia A1 - Almalla, Ahed A1 - Stepien, Daniel A1 - Özcan Sandikcioglu, Özlem T1 - Multilayer thin coatings for corrosion protection of AA2024-T3 aluminium alloy N2 - The performance of adhesively joined hybrid components relies strongly on the stability of the adhesive-material interface. With the increasing utilization of multi-material structures in the automotive and aerospace industry, it is of great scientific and technical interest to understand the processes leading to adhesive failure and to develop novel strategies to increase corrosion and delamination resistance of adhesive joints. The aim of this study is to develop thin epoxy based films and their carbon nanofiller loaded composites on aluminium alloy AA2024-T3 and to investigate their interfacial stability under corrosive and coupled corrosive-mechanical load. Spin coating was used for the layer-by-layer deposition of poly[(o-cresyl glycidyl ether)-co-formaldehyde] and poly-(ethylenimine) bi-layers. Carbon nanofillers are introduced either by mixing into the coating components or in between individual layers. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) analysis was performed to investigate the porosity and water uptake of the model films, respectively. Atomic force microscopy (AFM) results indicated a very homogeneous and dense film with low surface roughness. The bi-layer thickness ranged between 30 to 40 nm. Electrochemical measurements show a higher corrosion resistance with the increase of the bi-layer number. The main novelty of this contribution is the in-situ AFM investigations under coupled corrosive-mechanical load. For this purpose, a tensile module capable of uniaxial stretching and compression with up to 5 kN force was integrated into the AFM stage. Stretching experiments were performed to investigate the mechanical properties and adhesion of the films, as well as structural changes of the film morphology during uniaxial deformation. The contribution will provide detailed information on the new AFM setup and summarize our results on the stability of model epoxy and nanocomposite films on AA2024-T3. T2 - EURADH 2018 CY - Lisbon, Portugal DA - 05.09.2018 KW - Electrochemical Empedance Spectroscopy (EIS) KW - Scanning Kelvin Probe Force Microscopy (SKPFM) KW - Corrosion KW - Delamination KW - Aluminium KW - Epoxide PY - 2018 AN - OPUS4-46513 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Sachse, René A1 - Hertwig, Andreas A1 - Kraehnert, R. T1 - Analysis of Mesoporous Iridium Oxide Thin Films by the Combined Methodical Approach SEM/EDS/STRATAGem N2 - For the determination of porosity of Ir oxide thin films, electron probe microanalysis (EPMA) can be used as part of a combined SEM/EDS/STRATAGem analysis. The mass deposition (in μg cm-2) of films was calculated with the analysis software STRATAGem via k-values measured with EDS. The average density of coated films was obtained from the mass deposition and the film thickness as measured by the cross-section SEM. The porosity was calculated by dividing the average film density by the bulk (theoretical) density of the film material. Film porosities were counterchecked by spectroscopic ellipsometry (SE) using the Bruggeman effective medium approximation (BEMA). The results obtained by both analytical approaches/methods used, SEM/EDS/STRATAGem and SE were in good agreement. T2 - Microscopy & Microanalysis 2018 CY - Baltimore, MD, USA DA - 05.08.2018 KW - Electron probe microanalysis (EPMA) KW - Iridium oxide KW - Porous thin films KW - Spectroscopic ellipsometry PY - 2018 AN - OPUS4-46509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dittmann, Daniel A1 - Eisentraut, Paul A1 - Kittner, Maria A1 - Ruhl, A. S. A1 - Jekel, M. A1 - Braun, Ulrike T1 - Wasseranalytik oberhalb des Siedepunktes N2 - Das Poster fasst die Möglichkeiten gekoppelter thermischer Analyseverfahren mit Zersetzungsgasanalyse (TGA, TGA-FTIR, TGA-MS, TED-GC-MS) zusammen und stellt ihre Anwendungen für Wasserproben an ausgewählten Beispielen vor. T2 - 3. Mülheimer Wasseranalytisches Seminar (MWAS2018) CY - Mülheim an der Ruhr, Germany DA - 12.09.2018 KW - Thermogravimetrie KW - Zersetzungsgasanalyse KW - Wasseranalytik PY - 2018 AN - OPUS4-46508 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Kim, K. J. T1 - Measurement of Elemental Composition of FeNi and SiGe Thin Films by Electron Probe Microanalysis with Stratagem Software N2 - The present study repeats electron probe microanalysis (EPMA) measurements with the thin film analysis software Stratagem on an Fe-Ni thin films on silicon and reports - for the first-time – results of analysis on Si-Ge thin films deposited on a non-conductive aluminium oxide substrate. If the very good EPMA/Stratagem results for the FeNi system were expected due to previous studies, the data obtained for the SiGe films are particularly valuable, because of the challenging insulator substrate of Al2O3. The conductivity of the Si1-xGex surface necessary for charging-free analysis was ensured by applying conductive copper tape onto film surface down to sample stage. Four accelerating voltages, 15, 20, 25 and 30 kV, have been applied, so that the Ge Kα X-ray line at 9.87 keV could be excited. T2 - Microscopy & Microanalysis 2018 CY - Baltimore, MD, USA DA - 05.08.2018 KW - Electron probe microanalysis (EPMA) KW - Fe-Ni KW - Si-Ge KW - Stratagem KW - X-ray spectroscopy KW - thin film analysis PY - 2018 AN - OPUS4-46506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Donėlienė1, J. A1 - Rudzikas, M. A1 - Rades, Steffi A1 - Dörfel, Ilona A1 - Peplinski, Burkhard A1 - Sahre, Mario A1 - Pellegrino, F. A1 - Maurino, V. A1 - Ulbikas, J. A1 - Galdikas, A. T1 - Electron Microscopy and X-Ray Diffraction Analysis of Titanium Oxide Nanoparticles Synthesized by Pulsed Laser Ablation in Liquid N2 - A femto-second pulsed laser ablation in liquid (PLAL) procedure for the generation of titanium oxide nanoparticles (NP) is reported with the purpose of understanding morphology and structure of the newly generated NPs. Ablation duration was varied for optimization of NP generation processes between 10 and 90 min. Surface morphology of NPs as well as their size and shape (distribution) were analysed by various complementary electron microscopy techniques, i.e. SEM, TSEM and TEM. The crystalline structure of titanium oxide particles was investigated by XRD and HR-TEM. Concentration of generated titanium oxide NPs in liquid was analysed by ICP-MS. A mix of crystalline (mainly anatase), partly crystalline and amorphous spherical titanium oxide NPs can be reported having a mean size between 10 and 20 nm, which is rather independent of the laser ablation (LA) duration. A second component consisting of irregularly shaped, but crystalline titanium oxide nanostructures is co-generated in the LA water, with more pronounced occurrence at longer LA times. The provenance of this component is assigned to those spherical particles generated in suspension and passing through the converging laser beam, being hence subject to secondary irradiation effects, e. g. fragmentation. T2 - Microscopy & Microanalysis 2018 CY - Baltimore, MD, USA DA - 05.08.2018 KW - Nanoparticles KW - Titanium oxide KW - Laser ablation in liquid KW - Electron microscopy KW - XRD PY - 2018 AN - OPUS4-46502 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kricheldorf, H. R. T1 - Spirocyclic bisphenoxides of Ge, Zr, and Sn as catalysts for ring-expansion polymerizations of L- and meso-lactide N2 - Spirocyclic phenoxides of germanium, zirconium, and tin were prepared from 2,20-dihydroxybiphenyl and 2,20-dihydroxy-1,10-binaphthyl. Ring-expansion polymerizations of L-lactide are mainly studied at 160 or 180 °C. The reactivity of the catalysts increases in the order: Zr < Ge < Sn. Regardless of catalyst, the weight-average molecular weights (Mw) never exceed 50,000 g mol−1. The resulting poly(L-lactide)s are optically pure and have a cyclic architecture. Decreasing temperature and time favor Formation of even-numbered cycles, and at 102 ° cyclics, almost free of odd-numbered rings are obtained. Analogous polymerizations of meso-lactide give similar results >120 °C, but different results at 100 or 80 °C. Surprisingly, bell-shaped narrow molecular weight distributions are obtained <140 °C, resembling the pattern of living polymerizations found for alcohol-initiated polymerizations. An unusual transesterification mechanism yielding narrow distributions of odd-numbered cycles is discovered too. KW - Cyclization KW - Polylactides KW - MALDI-TOF MS KW - Ring-opening polymerization KW - Spirocyclic PY - 2018 DO - https://doi.org/10.1002/pola.29259 SN - 0887-624X SN - 1099-0518 VL - 56 IS - 24 SP - 2730 EP - 2738 PB - Wiley Periodicals AN - OPUS4-46498 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wurzler, Nina A1 - Kleinbub, Sherin A1 - Koerdt, Andrea A1 - Özcan Sandikcioglu, Özlem T1 - Effect of conditioning layers on the attachment and biofilm formation of electroactive bacteria on stainless steel N2 - The characteristics of different molecules chosen as representatives for specific functionalities in conditioning layers play an important role on attachment behavior and later biofilm formation of bacteria. The chemical composition is a major component influencing the attachment but there is a conglomerate of influences. T2 - Eurocorr2018 CY - Krakow, Poland DA - 09.09.2018 KW - Conditioning layer KW - Stainless steel KW - Bacterial attachment PY - 2018 AN - OPUS4-46487 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang A1 - Ehlert, Christopher A1 - Donskyi, Ievgen A1 - Girard-Lauriault, P.-L. A1 - Lippitz, Andreas A1 - Illgen, Rene A1 - Haag, R. A1 - Adeli, M. T1 - Chemical modification of graphene and carbon nano tubes as viewed by xps and nexafs spectroscopies with dft spectra simulation N2 - Graphene is a two-dimensional carbon network with unique properties. However, its low solubility, poor reactivity and the limited accessibility of a well-defined basal plane are major challenges for applications. An ideal method to overcome these problems is the covalent attachment of functional molecules to its surface which enable further reactive modifications for specific applications. There are several technologies for surface functionalization of graphene and related CNT materials. To get control on the functionalization process and to optimize the performance of the modified surfaces analytical tools for surface chemical characterization are required. X-ray absorption (NEXAFS) and photoelectron spectroscopy (XPS) have been identified to be rather powerful here [1-3]. Specifically, NEXAFS spectroscopy underpinned by quantum chemical spectrum simulations [4] is unique in a way to address changes of aromaticity and defect formation at the graphene surface during functionalization. For relevant surface modification technologies, we present examples on how NEXAFS and XPS can do a good job. All presented modifications aim on the production of platforms for defined functional 2D nanomaterials, as for example multifunctional hybrid architectures. In detail, we investigated: • A wet chemical method for covalent functionalization of graphene sheets by a one-pot nitrene [2+1] cycloaddition reaction under mild conditions. Here a reaction between 2,4,6-trichloro-1,3,5-triazine and sodium azide with thermally reduced graphene oxide (TRGO) results in defined dichlorotriazine-functionalized graphene sheets. • Graphene and carbon nanotube functionalized by Vacuum-Ultraviolet (VUV) induced photochemical or r.f. cw low pressure plasma processes to introduce amino, hydroxy or brominated functionalities. To underpin finger-print information delivered by C K-edge NEXAFS we studied the effects of selected point and line defects as well as chemical modifications for a single graphene layer model by density functional theory based spectrum simulations. References [1] P.-L. Girard-Lauriault et al., Appl. Surf. Sci., 258 2012 8448-8454, DOI: 10.1016/j.apsusc.2012.03.012 [2] A. Lippitz et al., Surf. Sci., 611 2013 L1-L7, DOI: 10.1016/j.susc.2013.01.020 [3] A. Faghani et al., Angew. Chemie (International ed.), 56 2017 2675-2679, DOI:10.1002/anie.201612422 [4] C. Ehlert, et al., Phys.Chem.Chem.Phys., 16 2014 14083-14095, DOI: 10.1039/c4cp01106f T2 - AVS 65th INTERNATIONAL SYMPOSIUM CY - Long Beach, CA, USA DA - 21.10.2018 KW - Graphene KW - Plasma KW - Nitrene [2+1] cycloaddition KW - XPS KW - NEXAFS PY - 2018 AN - OPUS4-46468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang T1 - Acquiring and Documenting Reproducible Spectra, Depth Profiles and Images: XPS, AES and SIMS N2 - In this talk sample prep/handling, instrument calibration and data acquisition methods with examples from XPS, Auger and SIMS will be addressed in terms of their contributions to the reproducibility of data delivered by the methods. Active parties in the field are VAMAS TWA 2 “Surface chemical analysis” (http://www.vamas.org/twa2/index.html), ISO/TC 201 “Surface chemical analysis” (https://www.iso.org/committee/54618.html) and the Surface Analysis Working Group (SAWG) at the International Meter Convention (https://www.bipm.org/en/ committees/cc/wg/sawg.html). The tools to improve the reproducibility of spectra, depth profiles and images at these international platforms are inter-laboratory comparisons, validated SOPs, standards and certified reference materials (CRM) as well as uncertainty budgets and establishment of traceability chains. The last point is of specific importance because all the methods, XPS, Auger and SIMS, are not primary methods. To address quantitative XPS, AES and SIMS results of relevant inter-laboratory comparisons organized by SAWG considering measurands as alloy surface composition and thickness of thin films will be introduced. These comparisons delivered results which are viewed to be benchmarking, some of them resulted in ISO/TC 201 standards. For quantitative XPS and AES the principal outline of an uncertainty budget will be discussed together with the audience. Another issue of quantitative XPS which definitely needs consideration are valid methods for a determination of the transmission function of the instruments and even for the emission angle in the respective experiments. Concerning the field of depth profiling it has to be investigated together with the audience whether the ISO (or ASTM) standards we have are sufficient to guarantee comparable results. Having in mind the number of different sputter ion species available today and range of samples of interest (metals, semiconductors, organic films) this might be questionable. And, how do depth profiling by AR-XPS and variable excitation energy XPS compete here? For imaging surface chemical analysis, the characterization of the imaging system is an issue to be investigated. Here the determination of lateral resolution is a relevant topic. Finally, the future needs to develop metrology for new applications e.g., ambient-pressure XPS, bio samples, and core-shell nanoparticles, will be issues raised for a discussion with the audience. T2 - 17th Topical Conference on Quantitative Surface Analysis (QSA 17) CY - Long Beach, CA, USA DA - 21.10.2018 KW - Depth Profiles and Images KW - X-ray Photoelectron Spectroscopy (XPS) KW - Auger Electron Spectroscopy (AES) KW - SIMS KW - Reproducible Spectra PY - 2018 AN - OPUS4-46470 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Park, J. A1 - Kim, G. B. A1 - Lippitz, Andreas A1 - Kim, Y. M. A1 - Jung, D. A1 - Unger, Wolfgang A1 - Kim, Y.-P. A1 - Lee, T. G. T1 - Plasma-polymerized antifouling biochips for label-free measurement of protease activity in cell culture media N2 - We report polyethylene glycol (PEG)-grafting antifouling surfaces using a plasma copolymerized (PcP) technique to monitor protease activity in complex media. By varying the mixing ratio of the PEG and ethylenediamine (EDA) precursors, the PcP-PEG-EDA (PcP-PE) film was able to easily control surface amine density with good preservation of the internal PEG structure. We found that nonspecific protein adsorption was dramatically reduced in serum-containing media on the PcP-PE films, as opposed to that on plasma polymerized-EDA (PP-E) films without PEG. When SPR sensor chips coated with PcP-PE film were employed to detect protease activity, biotinylated luciferase probes (luciferase-peptide-biotin) on streptavidin-conjugated SPR chips enabled real-time and label-free measurement of matrix metalloproteinase activity in cell culture media. Owing to its excellent antifouling ability, this newly developed method boasts minimal nonspecific binding and can serve as a biochip platform to promote a wide range of applications in the biological field. KW - Polyethylene glycol (PEG)-grafting antifouling surface KW - Biochip KW - ATR-FTIR spectroscopy KW - XPS KW - NEXAFS KW - Plasma PY - 2019 DO - https://doi.org/10.1016/j.snb.2018.10.123 SN - 0925-4005 VL - 281 SP - 527 EP - 534 PB - Elsevier B.V. AN - OPUS4-46463 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eitzen, L. A1 - Paul, S. A1 - Braun, Ulrike A1 - Altmann, Korinna A1 - Jekel, M. A1 - Ruhl, A. T1 - The challenge in preparing particle suspensions for aquatic microplastic research N2 - The occurrence of small particles consisting of organic polymers, so-called microplastic (MP), in aquatic Environments attracts increasing interest in both public and science. Recent sampling campaigns in surface Waters revealed substantial numbers of particles in the size range from a few micrometers to a few millimeters. In order to validate sample preparation, identification and quantification and to investigate the behavior of MP particles and potential toxic effects on organisms, defined MP model particles are needed. Many studies use spherical compounds that probably behave differently compared to irregularly shaped MP found in environmental samples. However, preparation and handling of MP particles are challenging tasks and have been systematically investigated in the present study. Polystyrene (PS) as a commonly found polymer with a density slightly above that of water was selected as polymer type for milling and fractionation studies. A cryogenic ball mill proved to be practical and effective to produce particles in the size range from 1 to 200 μm. The yield of small particles increased with increasing pre-cooling and milling durations. Depending on the concentration and the size, PS particles do not completely disperse in water and particles partly creep vertically up along glass walls. Stabilized MP suspensions without use of surfactants that might harm organisms are needed for toxicological studies. The stabilization of PS particle suspensions with ozone treatment reduced the wall effect and increased the number of dispersed PS particles but increased the dissolved organic carbon concentration and changed the size Distribution of the particles. KW - Reference material KW - Microplastic PY - 2018 DO - https://doi.org/10.1016/j.envres.2018.09.008 SN - 0013-9351 SN - 1096-0953 VL - 168 SP - 490 EP - 495 PB - Elsevier AN - OPUS4-46462 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eisentraut, Paul A1 - Dümichen, Erik A1 - Ruhl, A. A1 - Jekel, M. A1 - Albrecht, M. A1 - Gehde, M. A1 - Braun, Ulrike T1 - Two Birds with One Stone-Fast and Simultaneous Analysis of Microplastics: Microparticles Derived from Thermoplastics and Tire Wear N2 - Analysis of microplastic particles (MP) in environmental samples needs sophisticated techniques and is time intensive due to sample preparation and detection. An alternative to the most common (micro ) spectroscopic techniques, FTIR or Raman spectroscopy, are the thermoanalytical methods, where specific decomposition products can be analyzed as marker compounds for different kind of plastics types and mass contents. Thermal extraction desorption gas chromatography mass spectrometry (TED-GC-MS) allows the fast identification and quantification of MP in environmental samples without sample preparation. Whereas up to now only the analysis of thermoplastic polymers was realized, this is the first time that even the analysis of tire wear (TW) content in environmental samples is possible. Various marker compounds for TW were identified. They include characteristic decomposition products of elastomers, antioxidants and vulcanization agents. Advantages and drawbacks of these marker substances were evaluated. Environmental samples from street run off were exemplarily investigated and presented. KW - TED-GC-MS KW - Microplastic KW - Tire wear PY - 2018 DO - https://doi.org/10.1021/acs.estlett.8b00446 VL - 5 IS - 10 SP - 608 EP - 613 PB - American Chemical Society AN - OPUS4-46460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Principles for the development of standards for investigation procedures of plastics in environmental media and materials N2 - An overview about the current status of microplastic analysis is given with scope on hamonisation and standarisation. T2 - Annual ISO/TC 61 Meeting CY - Saitama, Japan DA - 24.09.2018 KW - Standardisation KW - Microplastic KW - Analysis PY - 2018 AN - OPUS4-46457 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Entwicklung einer schnellen und robusten Methode für die Analytik von Mikroplastik in Wasser N2 - Vortrag im Rahmen der Preisverleihung zum Mülheimer Wasser Award 2018, Vorstellung der TED-GC-MS als Methode für Mikroplastik Analyse T2 - 3. Wasseranalytisches Seminar (MWAS 2018) CY - Mülheim a.d. Ruhr, Germany DA - 12.09.2018 KW - Mikroplastik KW - Analytik PY - 2018 AN - OPUS4-46459 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radtke, Martin T1 - Von Ägypten bis Hiddensee – Analyse von Gold mit Synchrotronstrahlung - Update 2018 N2 - Gold ist eines der sieben schon im Altertum bekannten Metalle und wurde wg. seines Glanzes und seiner Seltenheit von alters her als Tauschmittel und zur Herstellung von Schmuck benutzt. Außerdem ist es einfach bearbeitbar und weitestgehend gegen chemische Einflüsse resistent. Die Untersuchungen von Gold mit synchrotronstrahlungsangeregter Röntgenfluoreszenzanalyse sind zerstörungsfrei und geben Auskunft über die in der untersuchten Probe vorhandenen chemischen Elemente. Bei den hier vorgestellten Untersuchungen an der BAMline stehen Fragestellungen wie Herkunft, Herstellungsverfahren und Zusammengehörigkeit von Goldfunden im Vordergrund. Die verschiedenen Fragestellungen werden an einer Reihe von Beispielen erläutert die vom Wikingerschatz aus Hiddensee über die Himmelsscheibe von Nebra bis hin zu Funden aus Ägypten langen. Zusätzlich werden die modernen Messmethoden vorgestellt, die am Synchrotron heutzutage zur Verfügung stehen. T2 - Vorlesung FU Berlin Einführung in die Archäometrie CY - Berlin, Germany DA - 01.11.2018 KW - Gold KW - Synchrotron KW - XRF KW - BAMline PY - 2018 AN - OPUS4-46451 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Saadeh, Qais A1 - Pauw, Brian Richard A1 - Thünemann, Andreas A1 - Günster, Jens T1 - In-Situ SAXS Techniques N2 - Our project's aim is to enhance the capabilities of additive manufacturing techniques, where enabling a Two-Photon-Polymerization (TPP) 3D printer of producing arrays of precisely aligned nanoparticles is of an enormous value. As heterogeneous functional nanostructures with arrays of oriented nanoparticles are very promising in many fields; electrochemistry, energy storage, nanoelectronics among other vital fields. The feasibility and the convenience of orienting nanoparticles using magnetic, electric fields and ultrasonic vibrations will be systematically investigated, using Small Angle X-ray Scattering (SAXS), since SAXS can provide detailed information about the orientation characteristics of nano-Ensembles. Corresponding to our prerequisites, a set ad hoc functional sample holders, sample stages and other In-Situ SAXS solutions were developed, and incorporated to be compatible with a state-of-the-arts SAXS machine, called Multi-scale Analyzer for Ultrafine Structures (MAUS). The MAUS has been customized and engineered to serve as a miniaturized synchrotron, and that is exactly what we need. Experiments attempting to orient superparamagnetic nanoparticles will be discussed, where the outcomes will not only help in understanding the mechanics of field-particle interactions, it will also help in further developing the adequate needed set of corrections to the SAXS data, that is especially regards oriented samples. T2 - XVII International Small Angle Scattering Conference – SAS 2018 CY - Traverse City, Michigan, USA DA - 07.10.2018 KW - In-Situ Techniques KW - SAXS KW - Magnetic nano-particles PY - 2018 AN - OPUS4-46443 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gollwitzer, Christian A1 - Ulbricht, Alexander A1 - Scholz, Philipp A1 - Joshi, Yogita A1 - Weidner, Steffen T1 - 3D printing material filled with metal organic frameworks analyzed by synchrotron based absorption edge tomography N2 - Absorption edge tomography, also known as differential tomography at absorption edges, is a method which exploits the sudden change of the attenuation coefficient, when the photon energy crosses the absorption edge of an element. Synchrotron radiation is the best source for absorption edge tomography, because of its small bandwidth, high intensity and easily adjustable photon energy. The synchrotron beamline BAMline at the synchrotron radiation facility BESSY II in Berlin, which is operated by the Bundesanstalt für Materialforschung und -prüfung (BAM), provides a monochromatized beam in a photon energy range from 5 keV up to 80 keV with a bandwidth of 2%, when the double multilayer monochromator is used. Together with the microtomography setup, this enables differential tomography with submicron resolution at the K edge of the elements from chromium up to the lanthanides, and up to uranium, when the L edges are used as well. In this work, metal organic frameworks (MOFs) embedded in polymer are characterized using differential tomography. MOFs are microporous structures of metal ions, coordinated by organic linker molecules, that can be used in a broad field of applications, especially in gas storage and catalysis. In this work, polymer embedded MOFs were extruded into filaments, which could be used for 3d-printing to profit from the specific properties of the MOFs in polymeric materials combined with the arbitrary shapes provided by 3d-printing. For the extrusion, different polymer classes like ABS, polyester- and polyetherurethanes, as well as different MOFs (ZIF-8, ZIF-67, HKUST-1) were used to create MOF containing filaments with a nominal diameter of 3.0 mm. Differential tomography at the edges of the Zn, Co, and Cu was then used to find the distribution of the corresponding MOF in the filament and to analyze the shape of the inclusions. T2 - MSE 2018 CY - Darmstadt, Germany DA - 26.09.2018 KW - Absorption edge KW - Tomography KW - Metal organic framework KW - Synchrotron PY - 2018 AN - OPUS4-46429 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rades, Steffi A1 - Borghetti, P. A1 - Ortel, Erik A1 - Wirth, Thomas A1 - Blanco, M. A1 - Gómez, E. A1 - Martinez, A. A1 - Jupille, J. A1 - Martra, G. A1 - Hodoroaba, Vasile-Dan T1 - Control of functionalization of supports for subsequent assembly of titania nanoparticle films N2 - For self‐assembling of TiO2 nanoparticles in multiple layers by layer‐by‐layer deposition to be applied to TiO2 thin films with defined and homogeneous thickness for large‐scale applications, the proper functionalization of substrate surface is a prerequisite to guarantee sufficient adhesion. The substrates selected and tested in the present paper were conductive, fluorine‐doped tin oxide (FTO) glass, nonconductive silica glass, and titanium alloy. The current study focusses on the analytical control of the stepwise functionalization of the substrates with 3‐aminopropyltriethoxysilane and glutaraldehyde (GA) for both the FTO glass and silica glass and with 3‐aminepropyl phosphonic acid and GA for Ti alloy. The analyses have been conducted by means of surface sensitive methods, X‐ray photoelectron spectroscopy, Auger electron spectroscopy, and time‐of‐flight secondary ions mass spectrometry. Chemical composition of surface of functionalized substrates shows differences in the degree and type of modification in dependence on substrate. It could be demonstrated that the best functionalized substrates were the conductive FTO glasses. The analysis of the functionalized Ti substrates has revealed that the surface coverage with 3‐aminepropyl phosphonic acid and GA molecules is an inhomogeneous one, and further optimization of the two‐step functionalization on the Ti alloy substrate is necessary. KW - Nanoparticles KW - Surface functionalization KW - TiO2 KW - SEM/EDX KW - Auger Electron Spectroscopy KW - ToF-SIMS KW - Thin films PY - 2018 DO - https://doi.org/10.1002/sia.6398 SN - 0142-2421 SN - 1096-9918 VL - 50 IS - 11 SP - 1200 EP - 1206 PB - John Wiley & Sons, Ltd. AN - OPUS4-46406 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rades, Steffi A1 - Oswald, F. A1 - Narbey, S. A1 - Radnik, Jörg A1 - Hodoroaba, Vasile-Dan T1 - Analytical approach for characterization of morphology and chemistry of a CH3NH3PbI3/TiO2 solar cell layered system N2 - Manufacturing of new perovskite layered solar cells with constant high light conversion Efficiency over time may be hampered by the loss of efficiency caused by structural and/or chemical alterations of the complex layered system. SEM/EDX combined with XPS were chosen as an appropriate methodical approach to characterize perovskite laboratory cells in depth and at surface, before and after light exposure. The layered perovskite system investigated here is based on glass covered with fluorine doped tin oxide, followed by thin films of TiO2, ZrO2, and a thick monolithic carbon. TiO2 film is subdivided into a dense layer covered by porous one constituted of nanoparticles of truncated bipyramidal shape. This layered system serves as the matrix for the perovskite. EDX spectral maps on cross sections of specimen have shown that Pb and I are distributed homogeneously throughout the porous layers C, ZrO2, and TiO2. SEM/EDX data show that 20 weeks of ambient daylight did not change significantly the in‐depth distribution of the elemental composition of Pb and I throughout the entire solar cell system. It was confirmed with EDX that nanoparticles identified in high‐resolution SEM micrographs contain mainly Pb and I, indicating these to be the perovskite crystals. However, a compositional and chemical altering began in the near‐surface region of the outermost ~10 nm after 2 months of illumination which was observed with XPS. T2 - ECASIA 2017 CY - Montpellier, France DA - 24.09.2017 KW - Solar Cell KW - SEM KW - EDX KW - XPS KW - layered system PY - 2018 DO - https://doi.org/10.1002/sia.6410 SN - 0142-2421 SN - 1096-9918 VL - 50 IS - 11 SP - 1234 EP - 1238 PB - John Wiley & Sons, Ltd. AN - OPUS4-46394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea A1 - An, Biwen Annie A1 - Özcan Sandikcioglu, Özlem A1 - Widdel, F. T1 - Microbial corrosion of iron coupled to methanogenesis by strains from different environments N2 - Microbially influenced corrosion (MIC) of iron is usually attributed to sulfate-reducing microorganisms (SRM) which act upon the metal by the reactiveness of hydrogen sulfide, and by withdrawal of the available electrons in electrical contact with the metal. Methanogenic archaea are supposed to cause MIC. Because they do not produce hydrogen sulfide, withdrawal of electrons may be their main corrosive mechanism; however, mechanistic details and kinetics of the overall process are poorly understood. Precipitation of siderite (4Fe + 5HCO3 + 5H+  4FeCO3 + CH4 + 3H2O) can lead to an insulating layer on the metal surface and lower the corrosion rate. Still, the extent of FeCO3 precipitation may be significantly influenced by environmental conditions such as pH and advective processes. T2 - ISME CY - Leipzig, Germany DA - 12.08.2018 KW - Methanogens KW - MIC KW - Corrosion KW - Environmental Simulation PY - 2018 AN - OPUS4-46397 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea A1 - An, Biwen Annie A1 - Özcan Sandikcioglu, Özlem A1 - Widdel, F. T1 - Microbial corrosion of iron coupled to methanogenesis by strains from different environments N2 - Microbially influenced corrosion (MIC) of iron is usually attributed to sulfate-reducing microorganisms (SRM) which act upon the metal by the reactiveness of hydrogen sulfide, and by withdrawal of the available electrons in electrical contact with the metal. Methanogenic archaea are supposed to cause MIC. Because they do not produce hydrogen sulfide, withdrawal of electrons may be their main corrosive mechanism; however, mechanistic details and kinetics of the overall process are poorly understood. Precipitation of siderite (4Fe + 5HCO3 + 5H+  4FeCO3 + CH4 + 3H2O) can lead to an insulating layer on the metal surface and lower the corrosion rate. Still, the extent of FeCO3 precipitation may be significantly influenced by environmental conditions such as pH and advective processes. T2 - EMBO-Workshop CY - Vienna, Austria DA - 02.08.2018 KW - Methanogens KW - MIC KW - Corrosion KW - Environmental Simulation PY - 2018 AN - OPUS4-46396 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Hertwig, Andreas A1 - Kormunda, M. A1 - Ryšánek, P. A1 - Ivanov, L. T1 - Characterisation of magnetron sputtered SnZnOx by means of spectroscopic ellipsometry - how can we analyse TCO materials optically? N2 - Transparent conductive oxide (TCO) films are a vital part of a large part of modern technology. The production of TCO materials has sparked much development in plasma coating technology. Quality control measurements of these layers are therefore important in many fields of optics and electronics such as high efficiency thin film photovoltaics. In this presentation, we report on optical measurements of ZnSnOx layers generated by DC/RF magnetron plasma co-sputtering. By changing the respective power on two different targets, the overall power, the gas composition and post-treatment, the properties of this type of layers can be varied in a number of parameters. The optical, electrical, and chemical properties of TCO layers are the technically most important properties together with the layer thickness. The dielectric function of layers is accessible by means of spectroscopic ellipsometry, which also yields the very important value for the layer thickness at the same time. It would be a significant step forward in quality control to use this non-destructive method also as a fast test for electrical properties. Therefore, we report on the optical properties connected to the production parameters, and also on our preliminary results connecting the optical dielectric function (in the visible and near infrared) to the electrical conductivity of the layers. We discuss the effect of deposition parameters on the optical properties of the layers and present an approach for correlating optical and electrical properties. Further, we discuss the question of accuracy of optical properties gained from model-fit-based optical methods and the use of different parameterised models for the dielectric function to achieve this. T2 - PSE 2018 - 16th Conference on Plasma Surface Engineering CY - Garmisch-Partenkirchen, Germany DA - 17.09.2018 KW - Mixed Oxides KW - TCO KW - Quality Control KW - Ellipsometry KW - Optical Constants PY - 2018 AN - OPUS4-46388 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hahn, Marc Benjamin A1 - Solomun, Tihomir A1 - Sturm, Heinz T1 - Determination of the Microscopic Dose-Damage Relation for Radiation of different Linear Energy Transfer N2 - The determination of the microscopic dose-damage relationship for DNA in an aqueous environment is of a fundamental interest for dosimetry and applications in radiation therapy and protection. We combine geant4 particle-scattering simulations in water with calculations concerning the movement of biomolecules to obtain the energy deposit in the biologically relevant nanoscopic volume.[1] We juxtaposition these results to the experimentally determined damage to obtain the microscopic dose-damage relationship at a molecular level. This approach is tested for an experimentally challenging system concerning the direct irradiation of plasmid DNA (pUC19) in water with electrons as primary particles.[2] Here a microscopic target model for the plasmid DNA based on the relation of lineal energy and radiation quality is used to calculate the effective target volume. It was found that on average fewer than two ionizations within a 7.5-nm radius around the sugar-phosphate backbone are sufficient to cause a single strand break, with a corresponding median lethal energy deposit being E1/2=6±4 eV.[1] The presented method is applicable for ionizing radiation (e.g., γ rays, x rays, and electrons) and a variety of targets, such as DNA, proteins, or cells. [1] Hahn, M. B., Meyer, S., Kunte, H.-J., Solomun, T. & Sturm, H. Measurements and simulations of microscopic damage to DNA in water by 30 keV electrons: A general approach applicable to other radiation sources and biological targets. Phys. Rev. E 95, 052419 (2017). [2] Hahn, M. B. et al. Direct electron irradiation of DNA in a fully aqueous environment. Damage determination in combination with Monte Carlo simulations. Phys. Chem. Chem. Phys. 19, 1798–1805 (2017). T2 - DYSON 2018 CY - Potsdam, Germany DA - 08.10.2018 KW - DNA KW - Dosimetry KW - Electron irradiation KW - Geant4 KW - Hydroxyl radical KW - LET KW - Linear energy transfer KW - Low energy electrons KW - MCS KW - Microdosimetry KW - Monte-Carlo simulations KW - Radiation damage KW - Radiation therapy KW - SEM KW - Electron Microscope KW - LEE KW - Protein PY - 2018 AN - OPUS4-46383 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Emmerling, Franziska T1 - Mechanochemical Syntheses of Metal Phosphonates N2 - Mechanochemistry is a suitable method for synthesizing a variety of metal phosphonates. By varying the ratio of the reactants, it is possible to control the reaction pathway. With this approach targeted synthesis of a certain composition is possible. Several new metal phosphonate structures were solved from the powder X-ray diffraction data including molecular metal phosphonates. The results demonstrate a new fast, facile, and environmental friendly alternative for the preparation of metal phosphonates. In situ investigations of the milling processes provided insights into the formation process of metal phosphonates. A multi-step diffusion mechanism was identified for most systems. Crystalline phases were obtained intermediately, suggesting that the synthesis is following Ostwald’s rules of stages. T2 - 1st European Workshop on Metalphophantes CY - Swanse, UK DA - 18.09.2018 KW - Mechanochemistry PY - 2018 AN - OPUS4-46382 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Riedel, Jens A1 - You, Yi A1 - Bierstedt, Andreas A1 - van Wasen, Sebastian A1 - Bosc-Bierne, Gaby A1 - Weller, Michael G. T1 - Airborne Laser-Induced Plasma as an Ambient Desorption/Ionization Source for Mass Spectrometry and its Characterization N2 - Laser-induced plasma (LIP) has drawn significant amount of attentions in the past decades, particular in elemental analyses for solid or liquid samples. Through proper focusing of the highly energetic laser beam, the plasma can also be ignited in the ambient air, where airborne analytes can be ionized. Such an effect enabled the use of airborne LIP as an ambient ionization source for mass spectrometric analyses. In contrast to other ambient desorption/ionization sources, airborne LIP does not require a specific discharge medium or expensive gas stream. Meanwhile, the airborne LIP produces reagent ion species for both proton-transfer and charge-transfer reactions in addition to the vacuum ultraviolent photons that are capable of promoting single photon ionization, which can be utilized to ionize polar and non-polar analytes. In order to gauge the analytical performance of airborne LIP, it is critical to understand the undergoing chemistry and physics during and after the plasma formation. Due to the ambient nature of airborne LIP, the variations of air composition and flow strongly affect the plasma behaviors. Preliminary result suggested the addition of a laminar flow of nitrogen gas favored the formation of protonated species (MH+) against the molecular ones (M+). Although the gas addition approach cannot fully tune the ionization process towards the specific production of pseudo-molecular species versus molecular ones, the alternation of molecular ion formation can be used for analyte recognitions through post processing of the ion patterns. The pulsed character of the used lasers makes the reagent ion equilibrium both transient- and highly fluid-dynamically controlled. The acoustic shock-waves induced by the airborne LIP get affected by an applied gas streams towards the plasma center, influencing the molecular-ion and ion-ion interactions in the near proximity of the plasma. To understand the airborne LIP formation, the temporally and spatially resolved optical emission spectra were recorded. The results will be correlated to time-resolved mass-spectrometric investigations of the ion profile during different stages of the plasma formation. As one example, the formation of pyrylium ion originating from aromatic compounds will be highlighted. T2 - SciX 2018 CY - Atlanta, GA, USA DA - 21.10.2018 KW - Laser-Induced Plasma KW - Ambient Desorption/Ionization KW - Mass Spectrometry KW - Characterization PY - 2018 AN - OPUS4-46376 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kneipp, Janina A1 - Zhang, Zhiyang T1 - Mapping the Inhomogeneity in Plasmonic Catalysis on Supported Gold Nanoparticles Using Surface-Enhanced Raman Scattering Microspectroscopy N2 - The characterization of a catalyst often occurs by averaging over large areas of the catalyst material. On the other hand, optical probing is easily achieved at a resolution at the micrometer scale, specifically in microspectroscopy. Here, using surface-enhanced Raman scattering (SERS) mapping of larger areas with micrometer-sized spots that contain tens to hundreds of supported gold nanoparticles each, the photoinduced dimerization of p-aminothiophenol (PATP) to 4,4′-dimercaptoazobenzene (DMAB) was monitored. The mapping data reveal an inhomogeneous distribution of catalytic activity in the plasmon-catalyzed reaction in spite of a very homogeneous plasmonic enhancement of the optical signals in SERS. The results lead to the conclusion that only a fraction of the nanostructures may be responsible for a high catalytic activity. The high spot-to-spot variation in catalytic activity is also demonstrated for DMAB formation by the plasmon-catalyzed reduction from p-nitrothiophenol (PNTP) and confirms that an improvement of the accuracy and reproducibility in the characterization of catalytic reactions can be achieved by microspectroscopic probing of many positions. Using SERS micromapping during the incubation of PATP, we demonstrate that the reaction occurs during the incubation process and is influenced by different parameters, leading to the conclusion of dimerization in a gold-catalyzed, nonphotochemical reaction as an alternative to the plasmon-catalyzed process. The results have implications for the future characterization of new catalyst materials as well as for optical sensing using plasmonic materials. KW - P-aminothiophenol KW - Silver nanoparticles KW - Chemical transformation KW - Metal nanoparticles KW - Coupling reactions KW - AU nanoparticle KW - AG nanoparticle KW - Spectroscopy KW - Sers KW - Molecule PY - 2018 DO - https://doi.org/10.1021/acs.analchem.8b01701 VL - 90 IS - 15 SP - 9199 EP - 9205 PB - American Chemical Society AN - OPUS4-46372 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radtke, Martin A1 - Berger, Achim T1 - Tragbare RFA an Gläsern: Ergebnisse und Grenzen N2 - Vorstellung der Ergebnisse der Messungen an Gläsern von Goethes Prismen. T2 - 3. Goethe/Ritter-Workshop CY - Berlin, Germany DA - 25.05.2018 KW - Goethe KW - Farbenlehre KW - Prisma KW - Handheld KW - XRF PY - 2018 AN - OPUS4-46369 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radtke, Martin A1 - de Oliveira Guilherme Buzanich, Ana A1 - Reinholz, Uwe A1 - Riesemeier, Heinrich A1 - Scharf, o T1 - The colour X-ray camera – Basics and applications of a 2D X-ray detector N2 - The Color X-ray Camera CXC or SLcam® is an energy-resolving X-ray camera capable of energy- and space-resolved measurements. It consists of a high-speed CCD detector coupled to a polycapil-lary optic that conducts the X-ray photons from the probe to distinct pixels onto the detector. The camera is capable of fast acquisition of spatially and energy resolved fluorescence images. A dedicated software enables the acquisition and the online processing of the spectral data for all 69696 pixels, leading to a real-time visualization of the elements distribution in a sample. It was developed in a joint project with BAM, IFG Berlin and PN Sensors. In this contribution we will mainly discuss the use of the CXC at our beamline, the BAMline at BESSY II and imaging applications of the CXC from different areas, like biology and archaeometry. Additionally new developments for the use of the detector without optics, like wavelength dispersive detection or 1shot-XANES, will be presented. T2 - Seminar Strahlenphysikalische Anwendungen in Technik und Medizin CY - ATi Wien, Austria DA - 24.01.2018 KW - XRF KW - Synchrotron KW - BAMline PY - 2018 AN - OPUS4-46365 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mueller, Axel A1 - Eisentraut, Paul A1 - Braun, Ulrike T1 - Nachweis von Mikroplastik in terrestrischen Umweltproben mittels TED-GC-MS N2 - Das Auftreten von Mikroplastik (MP) in aquatischen Ökosystemen ist bereits vielfältig dokumentiert. MP sind Kunststoffpartikel mit einer Größe kleiner als 5000 µm. Sie gelangen entweder als primäres MP (bspw. Zusätze in Kosmetikartikeln) oder als sekundäres MP (Fragmentierung größerer Kunststoffteile) in die Umwelt. Über die Existenz von Kunststoffpartikeln und deren Verbleib in terrestrischen Systemen ist wenig bekannt. Bis heute ist es unklar, ob MP im Boden durch Bodenerosion in die aquatische Umwelt transportiert wird und Boden somit als MP-Quelle für Gewässer fungiert, oder ob Partikel im Boden zurückgehalten werden und Boden eine MP-Senke darstellt. Hierzu sind aussagekräftige Messungen von Proben notwendig. Das Fehlen harmonisierter Verfahren für die Probenahme, Probenaufbereitung und Detektion erschwert die aktuelle Diskussion. In den wenigen bisher veröffentlichten Studien fanden hauptsächlich spektroskopische Methoden wie FTIR- oder Raman-Mikroskopie als Detektionsverfahren Anwendung. Diese liefern in der Regel Aussagen über Partikelanzahlen. Im vorliegenden Projekt soll als Analysemethode die von uns entwickelte ThermoExtraktionDesorption-GasChromatograpie-MassenSpektrometrie (TED-GC-MS) genutzt werden. Bei dieser Methode wird die Probe bis 600 °C erhitzt; die Zersetzungsgase werden auf einer Festphase sorbiert, anschließend in ein GS-MS-System überführt und dort desorbiert, getrennt und identifiziert. Die Methode erlaubt auf schnellem Wege über den Nachweis von spezifischen Zersetzungsprodukten die Identifikation einzelner Polymere, aber auch die quantitative Bestimmung des MP-Massegehaltes in einer Bodenprobe. Ziel des vorliegenden Projektes ist die Entwicklung eines systematischen Protokolls zur Probenahme, Probenaufarbeitung und anschließenden Analyse mittels TED-GC-MS von MP in terrestrischen Proben. Neben der Erstellung einer systematischen Probenahmestrategie sind Probenaufarbeitungsschritte wie die Reduktion der anorganischen Matrix mittels Dichteseparation sowie die oxidative Zersetzung organischer Matrixbestandteile notwendig. Im vorliegenden Tagungsbeitrag präsentieren wir die Anwendung der TED-GC-MS für die Bestimmung von MP in verschiedenen terrestrischen Umweltmatrizen. T2 - Umwelt 2018 CY - Münster, Germany DA - 09.09.2018 KW - TED-GC-MS KW - Mikroplastik KW - Analytik PY - 2018 AN - OPUS4-46364 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witte, Steffen A1 - de Oliveira Guilherme Buzanich, Ana A1 - Fittschen, U.E.A. A1 - Radtke, Martin A1 - Reinholz, Uwe A1 - Wobrauschek, P. A1 - Streli, C. T1 - TXRF-XANES: a unique experimental setup for chemical speciation of traces down to pg range N2 - Description of the set-up and first results for TXRF-XANES at BAMline T2 - XAFS 2018 CY - Cracow, Poland DA - 22.07.2018 KW - TXRF KW - XANES KW - Synchrotron KW - BAMline PY - 2018 AN - OPUS4-46363 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witte, Steffen A1 - Kulow, Anicó A1 - Seeberg, D. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Radtke, Martin A1 - Reinholz, Uwe A1 - Grunewald, Christian A1 - Riesemeier, Heinrich A1 - Wohlrab, S. T1 - S2XAFS@work: Customization for the Characterization of VOx based Catalysts N2 - X-ray absorption fine structure spectroscopy (XAFS) is a frequently employed technique in order to investigate structural composition and change of chemical compounds such as catalytic species. These structural properties are essential (i) to understand underlying reaction mechanism and (ii) to further improve the design of efficient catalysts. This investigation is based on a newly developed XAFS setup comprising both time- and lateral-resolved XAFS information simultaneously in a single-shot (S2XAFS). The primary broadband beam is generated by a filter/X-ray-mirror combination (bandpass). The transmitted beam through the sample is diffracted by a convexly bent Si (111) crystal, producing a divergent beam. This, in turn, is collected by an area sensitive detector with a theta to 2 theta geometry. This facile, stable and scanningless setup was tested at the BAMline @ BESSY-II (Berlin, Germany). This contribution focuses on further experimental optimizations allowing the characterization of supported vanadium oxide (VOx) based catalysts at the lower hard X-ray regime (5 to 6 keV). First S2XAFS measurements of these catalysts are presented herein. Supported VOx catalysts show promising results in the oxidation of methane to formaldehyde. S2XAFS allows determining the structural composition of the metal (i.e. vanadium) based on a fast and smart setup. It is therefore an ideal tool to identify crucial roles of chemical compounds in catalytic reactions. T2 - XAFS 2018 CY - Cracow, Poland DA - 22.07.2018 KW - XANES KW - XAFS KW - BAMline KW - Synchrotron PY - 2018 AN - OPUS4-46362 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witte, Steffen A1 - Radtke, Martin A1 - de Oliveira Guilherme Buzanich, Ana A1 - Grunewald, Christian A1 - Reinholz, Uwe A1 - Riesemeier, Heinrich A1 - Emmerling, Franziska T1 - XAFS@BAMline N2 - X-ray Absorption fine structure spectroscopy (XAFS) is a frequently employed technique in order to investigate structural composition and Change of chemical compounds such as catalytic species or corrosion processes. These structural properties are essential (i) to understand underlying reaction mechanism and (ii) to further improve the design of materials. While XAFS measurements are usually performed with ionization Chambers or simple fluorescence detectors, we at BAMline specialize in measurements with innovative set-ups that meet Specialrequirements such as time resolution, (3D-) spatial Resolution or demanding sample environments. This contribution presents various available XAFS configurations with their corresponding applications. In particular, these comprise single -shot XAFS for time- resolved measurements, grazing-exit XAFS with energy and a spatially resolved detector for the characterization of thin films and an in situ grazing incidence Setup for the characterization of corrosion layers. Additionally,the possibility of analyzing Minute samples in total-reflection geometry is demonstrated. T2 - EXRS 2018 CY - Ljubljana, Slovenia DA - 24.06.2018 KW - XANES KW - XAFS KW - BAMline KW - Synchrotron KW - TXRF PY - 2018 AN - OPUS4-46361 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breßler, Ingo T1 - SASfit, McSAS and beyond: Prospect of complementary tools for SAS data analysis N2 - Data analysis of SAS measurements has been dominated by the classical curve fitting approach. This method finds optimal parameters of a scattering model composed of analytical expressions. SASfit represents such a classical curve fitting toolbox: it is one of the mature programs for small-angle scattering data analysis and has been available and used for many years. The latest developments [1] will be extended by improving the interoperability of the extensive data base of models with third-party analysis software. An updated format of model definitions is also presented, which allows model function plug-ins to be used with the Python language. To complement the classical curve fitting method, the user-friendly opensource Monte Carlo regression package McSAS was developed. Most importantly, the form-free Monte Carlo approach of McSAS means that it is not necessary to provide any further mathematical restrictions to the Parameter distribution. Future developments include separating the core optimization from the GUI (allowing 'headless' integration), as well as parallel computing which reduces the computing time proportional to the number of available computing cores. The headless mode is presented by an example of Operation within interactive programming environments such as a Jupyter notebook. The promising results of Monte Carlo based data analysis for determining form-free Parameter distributions motivated the evaluation of the method with dynamic light scattering (DLS) data. For this purpose, the method was adapted for analyzing correlation curves such as those from multi-angle dynamic light scattering (DLS) data. The development of McDLS intends to overcome limitations of existing methods at reliably determining the modality of size distributions. An example of Monte Carlo based data analysis of multimodal DLS measurements will be presented. T2 - XVII International Small Angle Scattering Conference - SAS2018 CY - Traverse City, MI, USA DA - 07.10.2018 KW - Data analysis KW - Small angle scattering KW - Dynamic light scattering PY - 2018 AN - OPUS4-46308 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Saloga, Patrick E. J. T1 - SAXS in Analysis of Ultra-small Size-adjustable Zinc Oxide Nanoparticles for Controlled Band Gap Engineering N2 - Zinc oxide (ZnO) as a wide-bandgap II-VI semiconductor finds application in areas like optoelectronics, photocatalysis as well as in detection systems. While band-gap engineering in macroscopic ZnO can be performed by alloying, the band-gap of ZnO nanoparticles is also dependent on their size. Since small-angle X-ray scattering (SAXS) provides a much higher resolution in terms of ultra-small nanoparticle size analysis compared to other techniques, it allows for a careful examination of the correlation between particle size and band-gap. We report on the microwave-assisted synthesis of oleate-capped, photoluminescent zinc oxide nanoparticles with adjustable size as dispersions in organic solvents. The spherical particles were obtained by hydrolysis of the metal precursor in presence of a strong base at temperatures above the solvent’s boiling point. Hence, the reaction is dramatically accelerated and within seconds – instead of hours at lower temperatures –, narrowly dispersed particle systems are yielded. The particles’ sizes as derived from SAXS strongly depend on the reaction temperature and time. Choosing the right reaction conditions, the particle size and thus their band gap can be finely tuned. A size increase can be achieved both by increasing the reaction temperature and the reaction time. See Figure 1 for an exemplary comparison of five-minute syntheses at different temperatures. Here, the yielded particles display diameters between 5.0 and 7.6 nm and corresponding band-gaps of 3.32 up to 3.41 eV. The size increase is accompanied by a red-shift of the UV/Vis absorption edges and fluorescence emission. Furthermore, these particles can be transferred into water by coating with polysorbates. T2 - SAS2018 XVII International Small Angle Scattering Conference CY - Traverse City, Michigan, USA DA - 07.10.2018 KW - SAXS KW - Zinc oxide nanoparticles KW - Microwave synthesis PY - 2018 AN - OPUS4-46348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kormunda, M. A1 - Hertwig, Andreas A1 - Rysanek, P. A1 - Ivanov, L. T1 - Optical and Electrical Properties of reactive/nonreactive Magnetron Deposited SnZnOxCoatings Annealed at Various Temperatures N2 - ZnSnOx coatings were deposited from two 2in magnetron targets made of ZnO and SnO2 connected to DC pulsed and RF power supplies, respectively. The pure Ar and reactive gas mixture Ar/O2 were used. DC pulsed power applied on ZnO target was kept constant 50W 50kHz, 20% d.c. and the RF power applied on SnO2 target was set to values from 0W (pure ZnO deposited) up to 150W (up to 8 at.% of Sn in films). The deposited films were investigated by multiple techniques as deposited at RT as well as after annealing at temperatures 200o C and 450o C. The lower annealing temperature is still compatible with many of common polymeric substrates. The amount of Sn in the films is proportional to applied RF power on SnO2 target. But there is also significant influence of the post Deposition annealing on the film compositions. The ratio Zn/Sn is reduced by the annealing process. Therefore the annealing is promoting the migration of Sn toward the surface and Zn to inside. Moreover the films deposited in oxygen rich reactive gas mixture does not reduces the resistivity with added Sn in contrary to films deposited in Ar where the resistivity was reduced by 5 orders of magnitudes. The plasma parameters were investigated and mean energies of dominant species were in DC pulsed only about 3eV and DC + RF powered plasma up to 15eV. The expected higher energetic particles in the RF influenced plasma deliver an additional energy to the growing film. Therefore, we observed systematic differences between refractive indexes in the films deposited with low RF powered SnO2 magnetron at RT and post-annealed at 200 ° and practically no difference between RT and post-annealed film at higher RF power above 50 W. The XRD results proved the transitions from an amorphous to more crystalline structure by post-annealing of the films. T2 - PSE 2018 - 16th Conference on Plasma Surface Engineering CY - Garmisch-Partenkirchen, Germany DA - 17.09.2018 KW - Reactive sputtering KW - Plasma diagnostics KW - Optical films KW - TCO PY - 2018 AN - OPUS4-46347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kricheldorf, H. R. A1 - Scheliga, F. A1 - Weidner, Steffen T1 - Cyclic Polyesters via ROPPOC or REP N2 - Various catalysts and polycondensation mechanisms (ROPPOC/REP/ROP)were presented and discussed with regard to the Formation of cyclic and linear polylactides. It could be shown that depending on the structure of the catalyst even- and od numbered cyclics were selectively formed. These data were supported by various analytical techniques like MALDI-TOF mass spectrometry and Size Exclusion Chromatography. T2 - Polycondensation 2018 CY - Alexandria, VA, USA DA - 14.10.2018 KW - Polycondensation KW - MALDI-TOF MS KW - Ring-opening polymerization PY - 2018 AN - OPUS4-46340 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beck, Uwe A1 - Hielscher, Stefan A1 - Lange, Thorid A1 - Rietz, U. A1 - Lerche, D. T1 - State-of-the-Art in Multiple-Sample Evaluation of Adhesive and Bonding Strength N2 - The paper addresses the “State-of-the-Art in Multiple-Sample Evaluation of Adhesive and Bonding Strength” and the following points are discussed in more detail: 1. Motivation (coatings, varnishes, tapes, laminates, CFRP, adhesive-bonded joints) 2. Conventional single-sample testing (evaluation of adhesive and bonding strength; failure pattern) 3. Multiple-sample handling (MSH), bonding (MSB), and testing: centrifugal adhesion testing (CAT) (multiple-sample approach, tensile test within a centrifuge) 4. Application examples of CAT-Technology™ (laminates, optical coatings, CFRP joints) Finally, a summary is given regarding status quo and benefits of CAT-technology under tensile stress conditions whereas examples of testing in a centrifuge under compressive stress conditions are mentioned in the outlook. T2 - The 5th International Conference Competitive Materials and Technology Processes CY - Miskolc-Lillafüred, Hungary DA - 08.10.2018 KW - Centrifugal Adhesion Testing KW - CAT KW - Multiple-sample handling (MSH) KW - Multiple-sample bonding (MSB) KW - Tensile strength of laminates KW - Tensile strength of coatings KW - Adhesive strength KW - Bonding strength PY - 2018 AN - OPUS4-46336 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Haferkamp, Sebastian A1 - Emmerling, Franziska T1 - Mechanochemie N2 - In 3 Minuten sollte das Thema der Dissertation ohne zusätzliche Materialien vorgestellt werden. T2 - FameLab Germany 2018 CY - Potsdam, Germany DA - 15.03.2018 KW - Mechanochemie PY - 2018 AN - OPUS4-46319 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Haferkamp, Sebastian A1 - Akhmetova, Irina A1 - Kulla, Hannes A1 - Rademann, K. A1 - Emmerling, Franziska T1 - Mechanochemical Knoevenagel condensations of benzaldehyde derivates investigated in situ N2 - Mechanochemistry is widely applicable for the synthesis of inorganic, metal-organic, and organic compounds. It is known for short reaction times, nearly quantitative conversions, and decreasing amount of solvents, which opens the field to more environmentally friendly syntheses routes. Among organic syntheses, the Knoevenagel condensation is an important C-C bond forming reaction leading to α,β-unsaturated compounds. To gain more information on the underlying processes, we investigated the syntheses by a combination of different in situ investigation techniques, including synchrotron X-ray diffraction, Raman spectroscopy and thermography. This combination provides information on the structural changes and temperature influences during milling. Benzaldehyde derivates (nitro- and fluoro-derivates) reacted with malononitrile to the respective benzylidenemalononitriles. The in situ investigations show direct and quantitative conversions. In the case of the fluorinated benzaldehyde derivates we showed the possibility of using liquid substrates in mechanochemical organic synthesis. Surprisingly, after crystallization from a viscous state, the material was suitable for single-crystal X-ray analysis. T2 - Powder Diffraction School 2018 CY - Villigen, Switzerland DA - 24.09.2018 KW - C-C coupling KW - Mechanochemistry KW - In situ KW - Knoevenagel PY - 2018 AN - OPUS4-46320 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thünemann, Andreas T1 - Self-healing materials: structure elucidation with SAXS N2 - Healable materials could play an important role in reducing the environmental footprint of our modern technological society through extending the life cycles of consumer products and constructions. Future technologies require smart materials with advanced properties including responsiveness to external stimuli and particularly the ability to autonomously repair inflicted damage. The introduction of reversible connections in the polymer architecture, either in a non-covalent fashion, such as in supramolecular polymers, or by using dynamic covalent chemistry. One facile approach involves the implementation of reversible polymer networks as they offer high mechanical strength and thermal properties that are readily modified by the nature of the connecting dynamic bonds and the crosslinking density. In this context, small-angle scattering allows a detailed insight into the network structure of self-healing polymers either in bulk materials or in form of hydrogels. Here we report on how small-angle scattering can contribute to reveal the network structure. A first example is the conditional repair by locally switching the thermal healing capability of dynamic covalent polymers with light. Typical experimental SAXS curves of a photo- and thermal switchable polymer are shown. The scattering pattern show three characteristics. Region 1 is dominated by a forward scattering interpreted as resultant from large scale inhomogeneities of the bulk polymers (characterized by a first correlation length). The second scattering contribution can be interpreted as resultant from the network and is characterized by its entanglement distance. The mesh size of this network can be described by a second correlation length. Region 3 of the scattering pattern is dominated by a broad peak. Taking all effects into account, we approximate the total scattering as a sum of the three scattering contributions. In particular, the Debye-Büche function is used for I1 the Ornstein-Zernike function for the crosslinking contribution I2 and a Lorentzian peak function. We discussed this simple and more sophisticated approaches for revealing network structures. Examples of studies from hydrogel networks are provided as important materials with polymeric networks in life science applications. Finally, the determination of mesh size distributions as a function of temperature, time and healing efficiency is discussed in detail. T2 - XVII International Small Angle Scattering Conference - SAS2018 CY - Traverse City, Michigan, USA DA - 7.10.2018 KW - Small-angle x-ray scattering KW - Nanomaterial KW - Saxs PY - 2018 AN - OPUS4-46317 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vlajića, M. A1 - Unger, Wolfgang A1 - Bruns, J. A1 - Rueck-Braun, K. T1 - Photoswitching of fulgimides in different environments on silicon surfaces N2 - Reversible light-modulation of fulgimide based monolayers on Si(1 1 1) and Si(1 0 0) was investigated using ATR-FTIR spectroscopy. Fulgimide monolayers were prepared from neat COOH-terminated SAMs on Si(1 1 1) obtained from methyl undec-10-enoate, (1:1)-diluted COOH-terminated monolayers on Si(1 1 1), and GPTMS monolayers on Si(1 0 0). The epoxy-terminated monolayer on oxidized Si(1 0 0) was characterized with ellipsometry, XPS, as well as contact angle measurements, and ATR-FTIR spectroscopy revealed a strong influence of toluene water content on reproducible high-quality monolayer formation. The results of this study show that environmental polarity has a strong influence on fulgimide imide IR band locations and read-out options for the two photostationary states PSS(365 nm), containing E/Z- and C-isomers, and PSS(545 nm), with solely the E/Zisomers. Neat COOH-terminated monolayers on flat Si(1 1 1) have the Advantage of high functional Group concentration, orientation and stability, and an upright arrangement of fulgimide head groups. KW - Surface functionalization KW - Photoswitchable monolayers KW - ATR-FTIR spectroscopy KW - XPS PY - 2019 DO - https://doi.org/10.1016/j.apsusc.2018.09.159 SN - 0169-4332 SN - 1873-5584 VL - 465 SP - 686 EP - 692 PB - Elsevier B.V. AN - OPUS4-46276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Anja A1 - Saleh, Maysoon I. A1 - Unger, Wolfgang T1 - Investigation of core-shell nanoparticles using a combination of scanning Auger microscopy (SAM) and scanning electron microscopy (SEM) N2 - Products containing engineered nanoparticles already encounter us in most areas of our daily life including cosmetics, clothing, detergents, paints, batteries and displays. In most cases the particles exhibit a core-shell morphology either voluntarily or involuntarily. The properties of the nanoparticle shell determine the interaction with their environment and, thus, reliable control over these properties means reliable control over the particles performance and their toxicity. Therefore, sophisticated techniques to measure thickness and elemental composition of the nanoparticle shell are urgently required. Scanning Auger microscopy (SAM) is a powerful technique with a lateral resolution below 10 nm and a chemical contrast based on the characteristic kinetic energy of Auger electrons related to specific atomic levels and, thus, to a specific element. This work explores the potential of SAM for characterizing the core-shell structure of nanoparticles. A sample system of upconversion NaYF4:Yb,Er cores coated with SiO2 is investigated. Auger spectra, line scans and elemental maps of single nanoparticles will be presented. Challenges encountered will be highlighted, such as damage to the sample by electron beam irradiation. Scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX) are performed on the same samples, in order to verify the SAM results. T2 - BAM PhD Retreat CY - Warnemünde, Germany DA - 28.09.2018 KW - Core-shell nanoparticles KW - SAM KW - SEM KW - Surface analysis PY - 2018 AN - OPUS4-46270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - Cyclic poly(L-lactide)s via simultaneous ROP and polycondensation (ROPPOC) catalyzed by dibutyltin phenoxides N2 - Starting from dibutyltin oxide, four catalysts were synthesized, namely the dibutyltin bisphenoxides of Phenol (SnPh), 4-chlorophenol (SnCP), 4-hydroxybenzonitrile (SnCN) and pentafluorophenol (SnOPF). With the first three catalysts polymerizations of L-lactide at 160 °C in bulk yielded large fraction of linear chains having phenylester end groups at short reaction times. At longer times the fraction of cycles considerably increased at the expense of the linear chains, when SnCN was used as catalyst. With SnOPF only cyclic polylactides were obtained at low Lac/Cat ratios (< 400) with weight average molecular weights (Mw) up to 90 000 Da, whereas for high Lac/Cat ratios mixtures of cyclic and linear chains were found. Polymerizations in solution enabled variation of the molecular weight. Polymerizations of meso-lactide at temperatures down to 60 °C mainly yielded even-numbered linear chains supporting the postulated ROPPOC mechanism. KW - Cyclization KW - MALDI-TOF MS KW - Polycondensation KW - Ring-opening Polymerization KW - Polylactide PY - 2018 DO - https://doi.org/10.1016/j.eurpolymj.2018.10.005 SN - 0014-3057 IS - 109 SP - 360 EP - 366 PB - Elsevier AN - OPUS4-46263 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cant, D. A1 - Shard, A. A1 - Müller, Anja A1 - Clifford, C. A1 - Wirth, Thomas A1 - Unger, Wolfgang T1 - Surface chemical analysis – Electron spectroscopies – Measurement of the thickness and nature of nanoparticle coatings N2 - Recent years have seen increasing development of nanoparticles for applications in a wide range of fields, including but not limited to areas of great impact such as catalysis, medicine, energy, optoelectronics, cosmetics, and many others. In particular, nanoparticles bearing some form of coating layer, whether by design or due to incidental processes such as contamination or oxidation, are among the most commonly studied and utilised. In the characterisation of nanoparticles, the surface properties are of great importance, because a large proportion of the particle forms a part of the surface or interface. In the case of coated nanoparticles, the thickness of the coating is significant in determining the properties of the nanoparticle, and defines its interactions with its environment. Measurement of surface chemistry and coating thickness of nanoparticles is a challenge to which electron spectroscopies are well suited, due to high surface sensitivity, well-understood physical principles and accessibility. T2 - Annual Meeting of ISO/TC 201/SC7 CY - Cancun, Mexico DA - 21.09.2018 KW - Nanoparticle characterization KW - X-ray Photoelectron Spectroscopy (XPS) KW - Auger Electron Spectroscopy (AES) KW - Core-shell nanoparticles PY - 2018 AN - OPUS4-46259 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Prinz, Carsten A1 - Zimathies, Annett A1 - Emmerling, Franziska T1 - Importance of stability studies on porous certified reference materials N2 - In the development of certified reference materials (CRM), it is necessary to examine appropriate materials in advance for homogeneity and stability to meet the criteria of a CRM. In this case, the materials properties are characterized at the actual time without being possible to give a prognosis for suitability in the following years. It is, therefore, necessary to follow the certified material parameters via a monitoring system over the years on sale. For the current development of CRMs, the gained experience from long-term stability studies about the first generation of porous CRMs is significant. This experience is useful to better assess the suitability of candidate materials and thus develop higher quality CRMs in the future. A comparison between the gas sorption CRM materials silica, activated carbons, alpha alumina and anatase titanium oxides will illustrate the importance of long-term stability studies on porous CRMs. T2 - BERM 2018 - 15th International Symposium on Biological and Environmental Reference Materials CY - Berlin, Germany DA - 23.09.2018 KW - Reference material KW - Monitoring KW - Long-term stability PY - 2018 AN - OPUS4-46257 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan A1 - Procop, Mathias T1 - Check of the energy-dispersive X-ray spectrometers (EDS) performance with the BAM test material EDS-TM001/2 and BAM software EDS spectrometer test N2 - The test material EDS-TM001 together with an accompanying software package, “EDX spectrometer check”, have been made available in 2009 by BAM to be employed by EDS (energy dispersive spectrometer) users to check the performance of an EDS attached to the SEM. Particularly for test laboratories operating under accreditation schemes like ISO/IEC 17025, a periodical control of the critical instrumental parameters in end-user laboratories is required. With EDS-TM001 or EDS-TM002 (second generation) test material, this periodical check is reduced to the acquisition of only one 10 kV spectrum. The software “EDX spectrometer check” is destined to evaluate automatically this spectrum and determine the performance of the EDS in terms of energy resolution and calibration as well as possible alteration of low-energy efficiency due to detector contamination. Energy resolution can be compared with the specified values according to the international ISO standard ISO 15632:2012. EDS-TM is a synthetic material consisting of a thick layer of C, Al, Mn, Cu and Zr in a well-defined composition, deposited on a steel (in case of EDS-TM001) or silicon (in case of EDS-TM002) substrate. Meanwhile, more than one hundred laboratories (most of them located in Germany) use the EDS-TM001 or EDS-TM002 test material for the periodical check of their EDS. A detailed description of the test material and software together with examples of application was published recently. New results and gained experiences will be presented as well. T2 - BERM-15: International Symposium on Biological and Environmental Reference Materials CY - Berlin, Germany DA - 24.09.2018 KW - EDS KW - SEM/EDX KW - Test material KW - EDS-TM001 KW - EDS-TM002 KW - EDS Spectrometer Test KW - X-rays PY - 2018 AN - OPUS4-46253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - EMPIR nPSize - improved traceability chain of nanoparticle size measurements - Is a liaison to CEN/TC 352 nanotechnologies useful? N2 - The main objectives of the new EMPIR project nPSize are to establish EU capability of traceable measurement of NP size and shape, lower uncertainties of NP size measurement by developement of new nano-CRMs, new models (physical and machine learning), 3D method combination, and also by new ISO and CEN standards on accurate NP size measurement and guidance and knowledge transfer. The envisaged outcomes of the project will be presented and their suitability will be discussed to be taken over as pertinent contributions to normative projects within CEN/TC 352 Nanotechnologies. T2 - Joint Working Groups and 24th CEN/TC 352 Nanotechnologies Meetings CY - DIN, Berlin, Germany DA - 09.10.2018 KW - Nanoparticles KW - Size KW - Particle size distribution KW - Particle shape KW - Traceability KW - Standardisation KW - CEN/TC 352 Nanotechnologies PY - 2018 AN - OPUS4-46252 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Overview on the most advanced and suitable NanoDefine measurement methods N2 - The EC Recommendation on the definition of nanomaterial, based solely on size of the constituent particles, foresees development of harmonised measurement methods ensuring ‘consistent results across materials and over time’. The EU/FP7 research project NanoDefine has been exclusively dedicated to support the implementation of this EC Recommendation for the European Union’s legislation. For the first time, measurement techniques able to determine the size of nanoparticles have been evaluated systematically on a well-defined set of quality control materials (spherical, monodisperse) as well as industrial materials of complex shapes and considerable polydispersity. Particularly based on the analytical performance of the measurement techniques as tested on the challenging real-world particulate materials, it was possible to formulate recommendations for use of a new tiered approach consisting of screening and confirmatory techniques. Thus, a consistent framework of guidance for nanomaterial identification according to the EC Definition has been issued in form of the NanoDefiner e-tool, with a transparent decision flow scheme and an extensive user manual. Selected examples of analysis and classification as nano-/non-nanomaterials will be given, highlighting the limits of applicability of the available measurement techniques in dependence on sample properties. On some recent relevant developments in sample preparation – as a crucial part for an accurate analysis - will be also reported. T2 - VCI-NanoDefine Follow-up Meeting CY - VCI, Frankfurt am Main, Germany DA - 25.09.2018 KW - Nanoparticles KW - Nanomaterial KW - EC definition of nanomaterial KW - Nanoparticle size distribution PY - 2018 AN - OPUS4-46251 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinrich, Thomas A1 - Schneider, Markus A1 - Schäpe, Kaija A1 - Unger, Wolfgang A1 - Stockmann, Jörg M. T1 - Classification of engineered Titania nanomaterials via surface analysis using principal component analysis (PCA) assisted Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS) N2 - Due to the growing number of engineered nanomaterials (NM) the need for a reliable risk assessment for these materials is today bigger than ever before. Especially the nanomaterial’s surface or shell directly interacts with its environment and therefore is a crucial factor for NM’ toxicity or functionality. Especially, titania is one of the NM with the greatest technological importance. It is used for a large number of applications and can be found in food, cosmetics, glasses, mirrors, paints to mention only a few. In 2012, experts estimate[d] the annual European nano-titania production or utilization at an amount of more than 10,000 t. Great progress has been achieved in the area of NM investigation and characterization during the past decade. A variety of publications provide information about technological innovation as well as hazard potential, which means the potential risk on human health and ecosystems. However, enhanced data harmonization and well-defined standards for nanomaterial analysis, could significantly improve the reliability of such studies which often suffers from varying methods, parameters and sample preparations. To develop a suitable approach for the NM’s risk assessment, the ACEnano project aims at establishing a toolbox of verified methods. The size of this well-structured European project allows to handle even those big challenges like data harmonization and standardization. Due to its powerful combination of superior surface sensitivity and lateral resolution down to the Nano regime, ToF-SIMS could become one of these toolbox methods. Supported by multivariate data analysis such as principal component analysis (PCA), the method can be used for sub-classification of nanomaterial families using slight differences in surface chemistry. Here, we show a PCA supported classification of titania nanoparticles from various sources (NIST, JRC, BAM) with ToF-SIMS. Parameters like size, shell, pre-preparation and crystal system cause variance in the data and allow us to distinguish the species from each other. Moreover, this variance in the data also occurs and can be used for investigation when we compare our measurements of particle ensembles with those of grown titania films. The carefully selected and refined peaks allow a reasonable particle categorization and further a reliable allocation of blank feeds, which introduces a promising approach for NM characterization in the context of NM risk assessment. T2 - SIMS-Europe CY - Münster, Germany DA - 16.09.2018 KW - Nanoparticles KW - ToF-SIMS KW - XPS KW - PCA KW - Titania PY - 2018 AN - OPUS4-46250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinrich, Thomas A1 - Müller, Anja A1 - Schneider, Markus A1 - Sparnacci, Katja A1 - Unger, Wolfgang T1 - Chemical characterisation and classification of (Core-Shell) nanoparticles using PCA assisted ToF-SIMS N2 - The analysis of nanomaterials is currently an important task - especially in case of risk assessment – as the properties of these material class are not well understood and their growing use in everyday life. The rather high surface area of these objects renders their interactions significantly different to their corresponding bulk. Thus, the surface’s chemical composition must be investigated to get a better understanding and prediction of the nanomaterials’ behaviour. ToF-SIMS and XPS have proven to be powerful tools to determine the general chemical composition. The superior surface sensitivity of ToF-SIMS furthermore allows us to study mainly the utmost atomic layers and thus gives us an idea of possible interactions involved. Supported by multivariate data analysis such as principal component analysis (PCA), the method can also be used for sub-classification of different materials using slight differences in surface chemistry. Here, we present data of the analysis of Hyflon®-polystyrene core-shell nanoparticles which can be used as a model system due to the known preparation and a rather good chemical as well as physical separation of core and shell. Principle component analysis (PCA) will be used to detect the influence of sample preparation and for a better separation of different samples. This is achieved by measurement of a statistically relevant set of samples for every particle sample. We acquired surface spectra under static SIMS conditions with Bi32+ and analysed the resulting spectra by PCA. The carefully selected and refined peaks allow a reasonable categorization and further a reliable allocation of blank feeds. In detail, the fluorine containing, organic fragments are an indication for a heterogeneous shell that has errors. Furthermore, results on Au nanoparticles with and without an antibody shell are presented. ToF-SIMS imaging is desired to be implemented for single particle detection as well. T2 - SIMS-Europe CY - Münster, Germany DA - 16.09.2018 KW - Nanoparticles KW - ToF-SIMS KW - XPS KW - PCA KW - Titania KW - Core-Shell PY - 2018 AN - OPUS4-46249 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinrich, Thomas A1 - Müller, Anja A1 - Unger, Wolfgang T1 - Chemical characterisation of (core-shell) nanoparticles using PCA assisted ToF-SIMS and XPS N2 - The analysis of nanomaterials is currently an important task - especially in case of risk assessment – as the properties of these material class are not well understood. The rather high surface area of these objects renders their interactions significantly different to their corresponding bulk. Thus, the surface’s chemical composition must be investigated to get a better understanding and prediction of the nanomaterials’ behavior. ToF-SIMS and XPS have proven to be powerful tools to determine the general chemical composition. The superior surface sensitivity of ToF-SIMS furthermore allows us to study mainly the utmost atomic layers and thus gives us an idea of the interactions involved. Here, we present initial data on the analysis of Hyflon®-polystyrene core-shell nanoparticles which can be used as a model system due to the known preparation and a rather good chemical as well as physical separation of core and shell. Furthermore, results on Au nanoparticles with and without an antibody shell are presented. Principle component analysis (PCA) will be used to detect the influence of sample preparation and for a better separation of different samples. ToF-SIMS imaging is desired to be implemented for single particle detection as well. T2 - 3rd NanoSafety Forum for Young Scientists CY - Valetta, Malta DA - 08.09.2018 KW - Nanoparticles KW - ToF-SIMS KW - XPS PY - 2018 AN - OPUS4-46248 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grunert, B. A1 - Saatz, Jessica A1 - Hoffmann, Katrin A1 - Appler, F. A1 - Lubjuhn, Dominik A1 - Jakubowski, Norbert A1 - Resch-Genger, Ute A1 - Emmerling, Franziska A1 - Briel, A. T1 - Multifunctional rare-earth element nanocrystals for cell labeling and multimodal imaging N2 - In this work, we describe a simple solvothermal route for the synthesis of Eu3+-doped gadolinium orthovanadate nanocrystals (Eu:GdVO4−PAA) functionalized with poly(acrylic)acid (PAA), that are applicable as cell labeling probes for multimodal cellular imaging. The Eu3+ doping of the vanadate matrix provides optical functionality, due to red photoluminescence after illumination with UV light. The Gd3+ ions of the nanocrystals reduce the T1 relaxation time of surrounding water protons, allowing these nanocrystals to act as a positive MRI contrast agent with a r1 relaxivity of 1.97 mM−1 s−1. Low background levels of Eu3+, Gd3+, and V5+ in biological systems make them an excellent label for elemental microscopy by Laser Ablation (LA)-ICP-MS. Synthesis resulted in polycrystalline nanocrystals with a hydrodynamic diameter of 55 nm and a crystal size of 36.7 nm, which were further characterized by X-ray diffraction (XRD), photoluminescence spectroscopy (PL) and transmission electron microscopy (TEM). The multifunctional nanocrystals were subsequently used for intracellular labeling of both human adipose-derived stem cells (MSCs) and A549 (adenocarcinomic human alveolar basal epithelial) cells. KW - Bioimaging KW - Nanoparticle KW - Multimodal KW - Lanthanide PY - 2018 DO - https://doi.org/10.1021/acsbiomaterials.8b00495 SN - 2373-9878 VL - 4 IS - 10 SP - 3578 EP - 3587 PB - ACS Publications CY - Washington, USA AN - OPUS4-46244 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Unger, Wolfgang A1 - Kjaervik, Marit T1 - New work item proposal for a technical report for ISO/TC 201 WG 4 “Surface characterization of biomaterials”: Surface chemical analysis – Surface chemical analysis of cells and biofilms N2 - The proposed ISO Technical Report provides a description of a variety of physical methods of analytical chemistry by which bacteria and biofilms can be analysed. The state of the art, sample requirements and strengths associated with each method are identified. T2 - 27th Plenary Meeting of ISO/TC 201 CY - Cancun, Mexico DA - 2018-09-20 KW - Surface chemical analysis of biofilms KW - XPS KW - Fourier-Transform Infrared Spectroscopy KW - 3D nano SIMS KW - Raman-spectroscopy PY - 2018 AN - OPUS4-46214 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nietzold, Carolin A1 - Dietrich, Paul A1 - Holzweber, M. A1 - Lippitz, Andreas A1 - Kamalakumar, A. A1 - Blanchard, V. A1 - Ivanov-Pankov, S. A1 - Weigel, W. A1 - Panne, Ulrich A1 - Unger, Wolfgang T1 - Surface chemical characterization of model glycan surfaces and shelf life studies of glycan microarrays using XPS, NEXAFS spectroscopy, ToF-SIMS and fluorescence scanning N2 - Biomedical applications, including functional biomaterials, carbohydrate-arrays, and glycan-based biosensors. The chemistry of glycan immobilization plays an essential role in the bioavailability and function of surface bound carbohydrate moieties. For biomedical applications the stability over time (shelf life) of glycan arrays is a crucial factor. Herein we report on approaches for surface and interface characterization relevant to the needs of production of glycan microarrays which were tested using model carbohydrate surfaces. For detailed characterization of glycan model surfaces we used a combination of X-ray photoelectron spectroscopy (XPS), near edge X-ray absorption fine structure spectroscopy (NEXAFS) and ToF SIMS which are complementary techniques of surface chemical analysis. Links to fluorescence spectroscopy often used for characterization in the microarray community were established as well. In detail, amine-reactive silicon oxide and glass surfaces were used for anchoring oligosaccharides with an amino linker. The amount of surface bound carbohydrates was estimated by X-ray photoelectron spectroscopy (XPS). Glycan immobilization was investigated using lectins, which are glycan-binding molecules. A shelf life study of model glycan microarrays on epoxy-coated glass surfaces was done over a period of 160 days under different storage conditions utilizing fluorescence, ToF-SIMS and XPS analysis. It was shown that glycan activity of the models used can be maintained at least for half a year of storage at 4 °C. KW - Glycan microarray KW - XPS KW - NEXAFS KW - ToF-SIMS KW - Fluorescence PY - 2018 UR - https://www.sciencedirect.com/science/article/pii/S0169433218320300?via%3Dihub DO - https://doi.org/10.1016/j.apsusc.2018.07.133 SN - 0169-4332 SN - 1873-5584 VL - 459 SP - 860 EP - 873 PB - Elsevier B.V. AN - OPUS4-46212 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Roland A1 - Altmann, Korinna A1 - Braun, Ulrike T1 - Reference materials for microplastics in environmental matrices N2 - The pollution of marine, limnic and terrestrial environments with plastic waste and the potential impact especially on biota and humans has received increasing attention in recent years. Special focus is on particles smaller than 5 mm, the so-called microplastics. Consequently, possible regulations of emission and remediation efforts require sound information on the occurrence and fate of microplastics in the respective environmental compartments. Microplastics (MP) differ from classical organic pollutants in biota or the environment in that they do not consist of clearly defined low-molecular weight compounds but of polymer particulates with varying sizes and chemical compositions. This leads to specific challenges regarding the analytical techniques to be employed for their identification and quantification. Microplastics are defined as polymer particle in the size range between 1 µm and 5 mm and cover a wide range of polymers such as polyethylene, polypropylene, polystyrene and polyethylene terephthalate in variable geometric shapes. Properties relevant for environmental microplastics are polymer type, particle form and size distribution, surface morphology (aging status) and total mass fraction contained in a given sample. Polymer identification and particle size estimation using optical methods (IR and Raman spectroscopy) are time consuming and complicated by surface characteristics as a result of weathering, soiling, and microbial colonisation. Total mass fractions of MP in environmental samples can be determined by thermo-analytical methods. There are currently no standardised methods for sampling, sampling preparation, or detection of MP in environmental samples. So far, qualitative and quantitative investigations are done by research institutes and have not reached the routine laboratory community. The near future will see harmonisation efforts of MP mass fraction determination in environmental matrices by thermo-analytical procedures. The immediate need for reference materials during method development and comparison is outlined with regard to relevant matrix/polymer compositions, existing regulations and currently achievable detection limits. Examples for solid environmental matrix reference materials are discussed regarding the challenges encountered with matrices and polymer types as well as homogeneity testing and property value characterisation. T2 - BERM 2018 15th International Symposium on Biological and Environmental Reference Materials CY - Berlin, Germany DA - 23 September 2018 KW - Referenzmaterialien KW - Schwebstoffe KW - Sediment KW - Polymer PY - 2018 AN - OPUS4-46209 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wanner, C. A1 - Poethig, R. A1 - Carrero, S. A1 - Fernandez-Martinez, A. A1 - Jäger, Christian A1 - Furrer, G. T1 - Natural occurrence of nanocrystalline Al-hydroxysulfates: Insights on formation, Al solubility control and As retention N2 - Nanocrystalline basaluminite [Al4OH10(SO4)(H2O)3–5] and Aggregation of the e-Keggin polyoxocation [Al12(AlO4)(OH)24(H2O)12]7+, referred to as Al13, have both been described to form in acid mine Drainage environments. Although the chemical composition is quite similar, their crystalline varieties significantly differ, demonstrating that various types of Al-hydroxysulfates can form under similar conditions and that their respective formation is not fully understood yet. Here, we report the occurrence of nanocrystalline precipitates that form naturally in a small alpine catchment in Switzerland where an acidic mountainous stream (pH 4) is neutralized successively after mixing with several neutral tributaries. The stepwise neutralization in conjunction with the large amount of precipitates provide an ideal setting for obtaining new insights into (i) the structure of naturally forming Al-hydroxysulfates, (ii) their formation mechanism, (iii) their role in controlling the solubility of Al, and (iv) their ability to lower the mobility of As. Synchrotron-based high-energy X-ray diffraction and subsequent pair distribution function analyses demonstrate that these precipitates are structurally identical to basaluminite samples obtained from acid mine drainage sites. In contrast, only minor amounts of tetrahedrally coordinated Al, as present in Al13, were identified by nuclear magnetic resonance spectroscopy. The precipitates are further characterized by elevated As concentrations up to 600 lg/g, whereas other heavy metals are at background concentrations only. Given the low As concentrations in the stream from which precipitation occurs (<0.03 mg/L), high As concentrations confirm that basaluminite serves as a highly efficient As sink, which is attributed to its high anion-exchange capacity. Chemical analysis of streamwater samples in combination with geochemical modeling show that precipitation occurs instantaneously upon mixing with neutral streams. Moreover, our data reveal that the precipitation of basaluminite exerts a strong solubility control on dissolved Al concentrations as manifested by the quasi-constant basaluminite ion activity product observed during neutralization from pH 5 to pH 5.9. We hypothesize that in our field system, high fluoride and sulfate concentrations on the order of 100 and 1–2 mg/L, KW - Basaluminite KW - Al13 KW - Acid rock drainage KW - Arsenic retention KW - Aluminum KW - Anion exchange PY - 2018 DO - https://doi.org/10.1016/j.gca.2018.06.031 SN - 0016-7037 SN - 1872-9533 VL - 238 SP - 252 EP - 269 PB - Elsevier Ltd. AN - OPUS4-46164 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mino, L. A1 - Pellegrino, F. A1 - Rades, Steffi A1 - Radnik, Jörg A1 - Hodoroaba, Vasile-Dan A1 - Spotto, G. A1 - Maurino, V. A1 - Martra, G. T1 - Beyond shape engineering of TiO2 nanoparticles: Post-synthesis treatment dependence of surface hydration, hydroxylation, Lewis acidity and photocatalytic activity of TiO2 anatase nanoparticles with dominant {001} or {101} facets N2 - TiO2 anatase nanoparticles are among the relevant players in the field of light-responsive semiconductor nanomaterials used to face environmental and energy issues. In particular, shape-engineered TiO2 anatase nanosheets with dominant {001} basal facets gained momentum because of the possibility to exploit different and/or improved functional behaviors with respect to usual bipyramidal TiO2 anatase nanoparticles, mainly exposing {101} facets. Nevertheless, such behavior depends in a significant extent on the physicochemical features of surfaces exposed by nanosheets. They can vary in dependence on the presence or removal degree of capping agents, namely, fluorides, used for shape-engineering, and experimental investigations in this respect are still a few. Here we report on the evolution of interfacial/ surface features of TiO2 anatase nanosheets with dominant {001} facets from pristine nanoparticles fluorinated both in the bulk and at their surface to nanoparticles with F− free surfaces by treatment in a basic solution and to totally F− free nanoparticles by calcination at 873 K. The nanoparticles fluorine content and its subsequent evolution is determined by complementary techniques (ion chromatography, TOF-SIMS, XPS, AES, SEM-EDX), probing different depths. In parallel, the evolution of the electronic properties and the Ti valence state is monitored by UV−vis spectroscopy and XPS. The calcination treatment results in {001} facets poorly hydroxylated, hydrated, and hydrophilic, which appear as surface features consequent to the expected (1 × 4) reconstruction. Moreover, IR spectroscopy of CO adsorbed as probe molecule indicates that the Lewis acidity of Ti4+ sites exposed on (1 × 4) reconstructed {001} facets of calcined TiO2 nanosheets is weaker than that of cationic centers on {101} facets of bipyramidal TiO2 anatase nanoparticles. The samples have also been tested in phenol photodegradation highlighting that differences in surface hydration, hydroxylation, and Lewis acidity between TiO2 nanoparticles with nanosheet (freed by F− by calcination at 873 K) and bipyramidal shape have a strong impact on the photocatalytic activity that is found to be quite limited for the nanoparticles mainly exposing (1 × 4) reconstructed {001} facets. KW - Nanoparticles KW - TiO2 KW - F- doping KW - Shape-controlled nanoparticles KW - Nanosheets PY - 2018 DO - https://doi.org/10.1021/acsanm.8b01477 SN - 2574-0970 VL - 1 IS - 9 SP - 5355 EP - 5365 PB - ACS Publications CY - Washington, DC, U.S.A. AN - OPUS4-46157 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kjaervik, Marit A1 - Dietrich, P. A1 - Thissen, A. A1 - Schwibbert, Karin A1 - Unger, Wolfgang T1 - Investigations of biofilms in various conditions by near-ambient pressure XPS N2 - X-ray photoelectron spectroscopy (XPS) provides elemental and chemical information from the outermost ~10 nm of the sample surface. This is in the same order of magnitude as the thickness of the outer bacterial membrane of gram-negative bacteria, as well as outer membrane molecules as exopolysaccharides and lipopolysaccharides, commonly attached to the cell surface. With the development of near-ambient pressure (NAP)-XPS, bacteria can be analysed with minimal sample preparation. EnviroESCA is a laboratory based NAP-XPS instrument, equipped with a monochromated Al Kα radiation source and a differentially pumped energy analyser connected to an exchangeable sample environment. It allows for measurements in various gas-atmospheres, including water vapor, which makes it possible to characterise bacteria and other biological samples close to their natural, hydrated state. Artificial model-biofilms of exopolysaccharides, planktonic Pseudomonas Fluorescens and biofilms of Escherichia Coli have been characterised in hydrated and dried state. High-resolution XPS-spectra from carbon, oxygen, nitrogen and phosphorous can be assigned to carbohydrates, lipids and proteins in general agreement with literature. Especially the carbon 1s peak is of interest. A series of measurements of an E. coli biofilm from 11 mbar in humid environment to 1 mbar air reveal changes in the C1s peak, which suggests that the bacterial surface undergo substantial Change. T2 - BAM PhD-retreat CY - Warnemünde, Germany DA - 28.09.2018 KW - Biofilms KW - E. coli KW - NAP-XPS PY - 2018 AN - OPUS4-46132 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maiwald, Michael A1 - Emmerling, Franziska A1 - Villajos Collado, José Antonio A1 - Maierhofer, Christiane A1 - Thiel, Erik A1 - Altenburg, Simon T1 - Already producing or still assembling? – Perspectives towards modular production and quality control in a digitized process industry N2 - The CLEAN ENERGY Flagship is an initiative designed to utilize recent game changing developments in digital, materials and manufacturing technologies to catalyze a radical paradigm shift towards clean, reliable, efficient and cost-optimal energy. Unifying and drastically accelerating radically new energy material design, processing and integration across the entire value chain addressing energy production, conversion, storage and systems. CLEAN ENERGY participants are all distinguished research organisations that each benefit from their own industry networks and contacts with regions and state-level activities and have a long history of collaborating with each other (for 10 years now under the umbrella of EERA) within a European collaborative framework. Through EERA, CLEAN ENERGY aims to become a crucial partner in the SET-Plan, supporting long-lasting approaches through its established networks and internal collaborations. T2 - Clean Energy Workshop on Autonomous Materials Development Platforms CY - Brussels, Belgium DA - 02.10.2018 KW - Digitization KW - Energy production KW - Energy storage KW - Energy systems KW - Clean energy technology PY - 2018 AN - OPUS4-46135 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pauw, Brian Richard A1 - Breßler, Ingo A1 - Snow, T. A1 - Thünemann, Andreas T1 - Software- and instrument development for characterization of nano-(C)RMs N2 - This poster deals with improvements and characteriztion of small-angle scattering limitations, by looking at the trifecta of Data collection and uncertainty propagation, data analysis methodologies, and real-world tests. It is found that - with appropriate care and instrumentation - accuracies of 1% on mean nanomaterial sizes, and 10% on the size distribution width as well as the volume fraction can be achieved. T2 - BAM-PTB Workshop on Reference Nanomaterials CY - Berlin, Germany DA - 14.05.2018 KW - Small-angle scattering KW - Instrumentation KW - Methodology KW - MAUS KW - Data analysis KW - Data correction PY - 2018 AN - OPUS4-46107 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn A1 - Kirner, Sabrina V. A1 - Wirth, Thomas A1 - Spaltmann, Dirk A1 - Krüger, Jörg T1 - Chemical effects in the formation of fs-laser-induced periodic surface structures N2 - The processing of laser-induced periodic surface structures (LIPSS, ripples) on metals and semiconductors in ambient air is usually accompanied by superficial oxidation effects - widely neglected in the current literature. In this contribution, chemical, structural, and mechanical alterations in the formation of femtosecond LIPSS are characterized by a variety of surface analytical techniques, including energy dispersive X-ray analyses (EDX), X-ray photoelectron spectroscopy (XPS), micro Raman spectroscopy (µ-RS), and depth-profiling Auger electron microscopy (AEM). Alternative routes of electrochemical and thermal oxidation allow to qualify the relevance of superficial oxidation effects on the tribological performance in oil lubricated reciprocating sliding tribological tests (RSTT). It is revealed that the fs-laser processing of near-wavelength sized LIPSS on metals leads to the formation of a few hundreds of nanometer thick graded oxide layer, consisting mainly of amorphous oxides. Regardless of its reduced hardness and limited thickness, this nanostructured surface layer can effciently prevent a direct metal-metal contact in the RSTT and may also act as an anchor layer for specific wear-reducing additives contained in the engine oil involved T2 - 8th International LIPSS Workshop CY - Bochum, Germany DA - 27.09.2018 KW - Laser-induced periodic surface structures, LIPSS KW - Femtosecond KW - Oxidation KW - Tribology PY - 2018 AN - OPUS4-46106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn A1 - Legall, Herbert A1 - Schwanke, Christoph A1 - Pentzien, Simone A1 - Krüger, Jörg T1 - X-ray emission during processing of metals with ultrashort laser pulses N2 - Ultrashort laser pulse micromachining features a high precision. By increasing the repetition rate of the applied laser to several 100 kHz, laser processing becomes quick and cost-effective and make this method attractive for industrial applications. Upon exceeding a critical laser intensity, hard X-ray radiation is generated as a side effect. Even if the emitted X-ray dose per pulse is low, the accumulated X-ray dose becomes significant for high-repetition-rate laser systems so that radiation safety must be considered. T2 - 8th International LIPSS Workshop CY - Bochum, Germany DA - 27.09.2018 KW - X-ray KW - Laser processing KW - Ultrashort KW - Metals PY - 2018 AN - OPUS4-46104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hollamby, M. J. A1 - Holmes, A. T. A1 - Blackburn, E. A1 - Danks, A. A1 - Jellyman, E. A1 - Pauw, Brian Richard A1 - Rogers, S. A1 - Grillo, I. A1 - Saeki, A. A1 - Nakanishi, T. T1 - Formation and magnetic alignment of a photoconductive organogel formed by an alkyl-C60 hydrophobic amphiphile N2 - The formation and alignment of gel fibres in alkanes (solvents) was investigated. The gel fibres consist of small amphiphilic molecules containing a C60 molecule and a small ligand chain. Under the right conditions, these self-assemble in core-shell micelles, which themselves pack into micron-sized fibre-like structures. These can be aligned using a strong magnetic field, as investigated using SANS with a 17T superconducting magnet at a range of field strengths. T2 - 7th EuCheMS Chemistry Congress CY - Liverpool, UK DA - 26.08.2018 KW - Small-angle scattering KW - Alignment KW - SANS KW - SAXS PY - 2018 AN - OPUS4-46101 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -