TY - JOUR A1 - Pfennig, A. A1 - Simkin, Roman T1 - Identifying the initial corrosion fatigue failure based on dropping electrochemical potential N2 - The corrosion fatigue of duplex stainless-steel X2CrNiMoN22-5-3 can be determined by purely alternating axial cyclic load to failure using hour-glass shaped specimens. The experimental setup comprises a corrosion chamber allowing for the circulation of an aquifer electrolyte heated to 369 K simulating a carbon capture and storage as well as geothermal power plant environment. During engineering of a carbon storage site or geothermal power plant, it may be crucial to determine the failure onset of a component beforehand. Therefore, an algorithm with 93.3% reliability was established based on splitting the measured potential values into ten time series with a capacity of ten values. The failure of corrosion fatigue specimens in a geothermal environment correlates to the drop of the curves of the electrochemical potential which is measured simultaneously within the corrosion chamber. Crack initiation was, therefore, successfully derived from the electrochemical potential. KW - Corrosion fatigue KW - Surface corrosion KW - CO2 KW - Crack initiation KW - Geothermal energy production PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-629310 DO - https://doi.org/10.3390/app15010403 SN - 2076-3417 VL - 15 IS - 1 SP - 1 EP - 15 PB - MDPI CY - Basel AN - OPUS4-62931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Mohring, Wencke A1 - Wolf, Marcus T1 - The insignificant improvement of corrosion and corrosion fatigue behavior in geothermal environment applying Boehmit coatings on high alloyed steels N2 - The efficacy of alumina-sol based coatings in a water-free atmosphere at high temperatures suggests a potential solution for enhancing the corrosion resistance of high-alloyed steels in Carbon Capture and Storage (CCS) environments. In this study, coupons of X20Cr13, designed for use as injection pipes with 13% Chromium and 0.20% Carbon (1.4021, AISI 420), were sol-gel coated with water and ethanol-based alumina. These coated coupons were then exposed to CO2-saturated saline aquifer water, simulating conditions in the Northern German Basin, for 1000 h at ambient pressure and 60 °C. Corrosion fatigue experiments were also conducted using specimens of X5CrNiMoCuNb16-4 (1.4542, AISI 630), a suitable candidate for geothermal applications, to assess the impact of the ethanol-based coating on the number of cycles to failure at different stress amplitudes. Unfortunately, the coating exhibited early spallation, resulting in corrosion kinetics and corrosion fatigue data identical to those of uncoated specimens. Consequently, the initially promising Boehmit coating is deemed unsuitable for CCS applications and further research therefore not advisable. KW - Alumina coating KW - High alloyed steel KW - Pitting KW - Surface corrosion KW - CO2 KW - Pipeline KW - Corrosion KW - CCS KW - CO2-storage PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-623786 DO - https://doi.org/10.3390/app14041575 SN - 2076-3417 VL - 14 IS - 4 SP - 1 EP - 12 PB - MDPI CY - Basel AN - OPUS4-62378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bügel, Stefanie A1 - Hähnel, Malte A1 - Kunde, Tom A1 - de Sousa Amadeu, Nader A1 - Sun, Yangyang A1 - Spieß, Alex A1 - Beglau, Thi Hai Yen A1 - Schmidt, Bernd M. A1 - Janiak, Christoph T1 - Synthesis and Characterization of a Crystalline Imine-Based Covalent Organic Framework with Triazine Node and Biphenyl Linker and Its Fluorinated Derivate for CO2/CH4 Separation N2 - : A catalyst-free Schiff base reaction was applied to synthesize two imine-linked covalent organic frameworks (COFs). The condensation reaction of 1,3,5-tris-(4-aminophenyl)triazine (TAPT) with 4,40-biphenyldicarboxaldehyde led to the structure of HHU-COF-1 (HHU = Heinrich-Heine University). The fluorinated analog HHU-COF-2 was obtained with 2,20,3,30,5,50,6,60-octafluoro 4,40 -biphenyldicarboxaldehyde. Solid-state NMR, infrared spectroscopy, X-ray photoelectron spectroscopy, and elemental analysis confirmed the successful formation of the two network structures. The crystalline materials are characterized by high Brunauer–Emmett–Teller surface areas of 2352 m2/g for HHU-COF-1 and 1356 m2/g for HHU-COF-2. The products of a larger-scale synthesis were applied to prepare mixed-matrix membranes (MMMs) with the polymer Matrimid. CO2/CH4 permeation tests revealed a moderate increase in CO2 permeability at constant selectivity for HHU-COF-1 as a dispersed phase, whereas application of the fluorinated COF led to a CO2/CH4 selectivity increase from 42 for the pure Matrimid membrane to 51 for 8 wt% of HHU-COF-2 and a permeability increase from 6.8 to 13.0 Barrer for the 24 wt% MMM KW - Separation KW - COF KW - MMM KW - CO2 PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-618625 DO - https://doi.org/10.3390/ma15082807 VL - 15 IS - 8 SP - 2807 PB - MDPI AN - OPUS4-61862 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Arinchtein, A. A1 - Ye, M.-Y. A1 - Yang, Q. A1 - Kreyenschulte, C. A1 - Wagner, Andreas A1 - Frisch, M. A1 - Brückner, A. A1 - Kondratenko, E. A1 - Kraehnert, R. T1 - Dynamics of Reaction-Induced Changes of Model-Type Iron Oxide Phases in the CO2-Fischer-Tropsch-Synthesis N2 - Iron-based catalysts are employed in CO2-FTS due to their ability to convert CO2 into CO in a first step and their selectivity towards higher hydrocarbons in a second CO hydrogenation step. According to the literature, iron carbides represent the active phase for hydrocarbon formation and are claimed to emerge in the presence of CO. We propose nanostructured FeOx films as model systems to assess information about the complex phase transformations during CO2-FTS. Mesoporous hematite, ferrihydrite, maghemite, maghemite/magnetite films were exposed to CO2-FTS atmospheres at 20 bar and 300°C. Up to three distinct phases were observed depending on the timeon-stream (TOS): a sintered maghemite/magnetite phase, a carbidic core-shell structure, and a low-crystalline, needle-type oxide phase. Our findings indicate that the formation of an intermediary maghemite/magnetite phase, predominant after short TOS (30 h), precedes the evolution of the carbide phase. Yet, even after prolonged TOS (185 h), no full conversion into a bulk carbide is observed. KW - Nanostructured FeOx films KW - CO2 KW - Scanning Auger Spectroscopy PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-549709 DO - https://doi.org/10.1002/cctc.202200240 SN - 1867-3880 VL - 14 IS - 14 SP - 1 EP - 11 PB - Wiley-VCH AN - OPUS4-54970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Aristia, Gabriela A1 - Le, Quynh Hoa A1 - Bäßler, Ralph T1 - Corrosion of Carbon Steel in Artificial Geothermal Brine: Influence of Carbon Dioxide at 70 °C and 150 °C N2 - This study focuses on the corrosion mechanism of carbon steel exposed to an artificial geothermal brine influenced by carbon dioxide (CO2) gas. The tested brine simulates a geothermal source in Sibayak, Indonesia, containing 1500 mg/L of Cl-, 20 mg/L of SO4 2-, and 15 mg/L of HCO3-with pH 4. To reveal the temperature effect on the corrosion behavior of carbon steel, exposure and electrochemical tests were carried out at 70 °C and 150 °C. Surface analysis of corroded specimens showed localized corrosion at both temperatures, despite the formation of corrosion products on the surface. After 7 days at 150 °C, SEM images showed the formation of an adherent, dense, and crystalline FeCO3 layer. Whereas at 70 °C, the corrosion products consisted of chukanovite (Fe2(OH)2CO3) and siderite (FeCO3), which are less dense and less protective than that at 150 °C. Control experiments under Ar-environment were used to investigate the corrosive effect of CO2. Free corrosion potential (Ecorr) and electrochemical impedance spectroscopy (EIS) confirm that at both temperatures, the corrosive effect of CO2 was more significant compared to that measured in the Ar-containing solution. In terms of temperature effect, carbon steel remained active at 70 °C, while at 150 °C, it became passive due to the FeCO3 formation. These results suggest that carbon steel is more susceptible to corrosion at the near ground surface of a geothermal well, whereas at a deeper well with a higher temperature, there is a possible risk of scaling (FeCO3 layer). A longer exposure test at 150 °C with a stagnant solution for 28 days, however, showed the unstable FeCO3 layer and therefore a deeper localized corrosion compared to that of seven-day exposed specimens. KW - Carbon steel KW - CO2 KW - Corrosion KW - Electrochemical impedance spectroscopy KW - Geothermal PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-498168 DO - https://doi.org/10.3390/ma12223801 SN - 1996-1944 VL - 12 IS - 22 SP - 3801-1 EP - 20 PB - MDPI CY - Basel AN - OPUS4-49816 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lazik, D. A1 - Ebert, S. A1 - Neumann, Patrick P. A1 - Bartholmai, Matthias T1 - Characteristic length measurement of a subsurface gas anomaly - A monitoring approach for heterogeneous flow path distributions N2 - Geogenic gases from natural sources, carbon dioxide (CO2) from a geological repository (carbon capture and storage - CCS) or a leaking gas pipeline can present serious risks in industrial and urban areas. To extend the lead time for risk treatment in such critical regions, reliable detection of gases within the shallow subsurface is required to observe critical gas accumulations before degassing into the atmosphere. A near real-time monitoring approach is introduced to determine the volumetric expansion of a leakinggas in the subsurface. Considering the pressure relaxation with the ambient air pressure, the approach enables the forecasting of the final size of a pressurized gas body in terms of characteristic lengths. According to theoretical basics, such a characteristic length, which enables us to perform a gas (safety) measurement based on a purely geometrical measure, behaves independently of subsurface properties,i.e., it enables a reliable quantification of the escaping gas irrespective of its heterogeneous or changingflow path distribution. A field test for a 10 l/min pinhole leakage injected into a 10 m long, 0.4 m wide, 0.95 m deep soil-filled trench that was equipped with linear sensors shows the lateral-vertical volumetric gas expansion along these sensors, and demonstrates the applicability of the characteristic length approach. KW - Monitoring KW - Carbon capture and storage KW - Leakage KW - Quantification KW - Subsurface KW - CO2 PY - 2016 DO - https://doi.org/10.1016/j.ijggc.2016.02.008 SN - 1750-5836 VL - 2016 IS - 47 SP - 330 EP - 341 PB - Elsevier B.V. AN - OPUS4-35425 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yevtushenko, Oleksandra A1 - Bäßler, Ralph A1 - Carrillo-Salgado, I. T1 - Material challenges for stainless steel in carbon capture and storage N2 - Corrosion resistance of duplex stainless steel (SS) (UNS S32101) and super austenitic SS (UNS NO8031) (Alloy 31) was investigated in crevice conditions in a saline brine. Rubber was used to form a metal/non-metal-crevice confguration. UNS NO8031 did not exhibit any signs of pitting corrosion even by applying potentials much more positive than the corrosion potential. KW - Corrosion KW - CO2 KW - Saline aquifer fluids PY - 2014 SN - 0094-1492 VL - 53 IS - 5 SP - 2 EP - 5 CY - Houston, Tex. AN - OPUS4-30633 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -